WO2012087016A2 - 자성이 우수한 방향성 전기강판 및 이의 제조방법 - Google Patents
자성이 우수한 방향성 전기강판 및 이의 제조방법 Download PDFInfo
- Publication number
- WO2012087016A2 WO2012087016A2 PCT/KR2011/009913 KR2011009913W WO2012087016A2 WO 2012087016 A2 WO2012087016 A2 WO 2012087016A2 KR 2011009913 W KR2011009913 W KR 2011009913W WO 2012087016 A2 WO2012087016 A2 WO 2012087016A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- steel sheet
- grain
- oriented electrical
- electrical steel
- less
- Prior art date
Abstract
Description
Claims (13)
- 중량%로, Si: 2.0∼4.5%, C: 0.001∼0.10%, Al: 0.010%이하, Mn: 0.08%이하, N: 0.005%이하, S: 0.002~0.050%, 잔부 Fe 및 기타 불가피하게 혼입되는 불순물로 이루어지는 슬라브를 가열한 후, 열간압연하고, 1회의 냉간압연 혹은 중간소둔을 포함하는 2회 이상의 냉간압연을 실시한 후, 탈탄 및 재결정소둔을 실시한 다음, 2차재결정 소둔을 실시하도록 하는 자성이 우수한 방향성 전기강판의 제조방법.
- 청구항 1에 있어서,상기 슬라브는 S가 0.005%이상으로 함유되는 자성이 우수한 방향성 전기강판의 제조방법.
- 청구항 1에 있어서,상기 슬라브는 Mn이 0.05%이하로 함유되는 자성이 우수한 방향성 전기강판의 제조방법.
- 청구항 1 내지 청구항 3중 어느 한 항에 있어서,2차재결정 소둔시 단독으로 입계에 편석되는 S 혹은 FeS 석출물중의 적어도 어느 하나에 의하여 결정립 성장을 억제함에 의하여 2차재결정을 일으키도록 하는 자성이 우수한 방향성 전기강판의 제조방법.
- 청구항 1 내지 청구항 3중 어느 한 항에 있어서,2차재결정된 강판의 두께방향 단면에서의 Al 산화물의 밀도를 0.1~500개/mm2로 하는 자성이 우수한 방향성 전기강판의 제조방법.
- 청구항 1 내지 청구항 3중 어느 한 항에 있어서,50Hz, 1.7테슬라의 교류 자장을 인가한 조건에서의 보자력 값을 30A/m이하로 하는 자성이 우수한 방향성 전기강판의 제조방법.
- 청구항 1 내지 청구항 3중 어느 한 항에 있어서, 상기 2차재결정 소둔은,탈탄 및 재결정된 강판을 1000℃이상의 온도로 승온하여 2차재결정을 일으킨 후, 1000℃이상의 온도에서 10시간 이내로 균열처리하고 냉각시키도록 하는 자성이 우수한 방향성 전기강판의 제조방법.
- 청구항 7에 있어서,균열처리하는 시간을 1시간 이내로 하는 자성이 우수한 방향성 전기강판의 제조방법.
- 청구항 1 내지 청구항 3중 어느 한 항에 있어서,열간압연 후, 냉간압연 전에 열연판 소둔을 실시하도록 하는 자성이 우수한 방향성 전기강판의 제조방법.
- 중량%로, Si: 2.0∼4.5%, C: 0.003%이하, Al: 0.010%이하, Mn: 0.08%이하, N: 0.005%이하, 잔부 Fe 및 기타 불가피하게 혼입되는 불순물로 이루어지고, 단독으로 입계에 편석된 S 혹은 FeS 석출물중의 적어도 어느 하나가 결정립성장 억제제로 작용하여 2차재결정되어진 자성이 우수한 방향성 전기강판.
- 청구항 10에 있어서, 상기 방향성 전기강판은,두께방향 단면에서의 Al 산화물 밀도가 0.1~500개/mm2인 자성이 우수한 방향성 전기강판.
- 청구항 10 또는 청구항 11에 있어서, 상기 방향성 전기강판은,Mn이 0.05%이하로 함유되고, S가 0.0005% 이상 함유되어 있는 자성이 우수한 방향성 전기강판.
- 청구항 10 또는 청구항 11에 있어서, 상기 방향성 전기강판은,50Hz, 1.7테슬라의 교류 자장을 인가한 조건에서의 보자력 값이 30A/m이하인 자성이 우수한 방향성 전기강판.