WO2010042196A1 - Catalytic materials, photoanodes, and photoelectrochemical cells for water electrolysis and other electrochemical techniques - Google Patents
Catalytic materials, photoanodes, and photoelectrochemical cells for water electrolysis and other electrochemical techniques Download PDFInfo
- Publication number
- WO2010042196A1 WO2010042196A1 PCT/US2009/005521 US2009005521W WO2010042196A1 WO 2010042196 A1 WO2010042196 A1 WO 2010042196A1 US 2009005521 W US2009005521 W US 2009005521W WO 2010042196 A1 WO2010042196 A1 WO 2010042196A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- photoanode
- photoactive
- electrode
- catalytic material
- species
- Prior art date
Abstract
Description
Claims