WO2009145284A1 - Inkjet recording ink and image forming method - Google Patents
Inkjet recording ink and image forming method Download PDFInfo
- Publication number
- WO2009145284A1 WO2009145284A1 PCT/JP2009/059831 JP2009059831W WO2009145284A1 WO 2009145284 A1 WO2009145284 A1 WO 2009145284A1 JP 2009059831 W JP2009059831 W JP 2009059831W WO 2009145284 A1 WO2009145284 A1 WO 2009145284A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- ink
- resin
- carbon black
- inkjet recording
- mass
- Prior art date
Abstract
Description
Claims