WO2009129051A2 - Panels including renewable components and methods for manufacturing - Google Patents
Panels including renewable components and methods for manufacturing Download PDFInfo
- Publication number
- WO2009129051A2 WO2009129051A2 PCT/US2009/039128 US2009039128W WO2009129051A2 WO 2009129051 A2 WO2009129051 A2 WO 2009129051A2 US 2009039128 W US2009039128 W US 2009039128W WO 2009129051 A2 WO2009129051 A2 WO 2009129051A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- panel
- weight
- base mat
- slurry
- mesh
- Prior art date
Links
- 238000000034 method Methods 0.000 title claims abstract description 27
- 238000004519 manufacturing process Methods 0.000 title claims abstract description 10
- 230000000717 retained effect Effects 0.000 claims abstract description 54
- 239000000835 fiber Substances 0.000 claims abstract description 34
- 239000002245 particle Substances 0.000 claims abstract description 31
- 239000011230 binding agent Substances 0.000 claims abstract description 11
- 239000002002 slurry Substances 0.000 claims description 87
- XLYOFNOQVPJJNP-UHFFFAOYSA-N water Substances O XLYOFNOQVPJJNP-UHFFFAOYSA-N 0.000 claims description 84
- 240000007594 Oryza sativa Species 0.000 claims description 55
- 235000007164 Oryza sativa Nutrition 0.000 claims description 55
- 235000009566 rice Nutrition 0.000 claims description 55
- 239000010902 straw Substances 0.000 claims description 25
- 239000002023 wood Substances 0.000 claims description 18
- 241000209140 Triticum Species 0.000 claims description 15
- 235000021307 Triticum Nutrition 0.000 claims description 15
- 235000002017 Zea mays subsp mays Nutrition 0.000 claims description 14
- 240000008042 Zea mays Species 0.000 claims description 13
- 235000005824 Zea mays ssp. parviglumis Nutrition 0.000 claims description 13
- 235000005822 corn Nutrition 0.000 claims description 13
- 235000009419 Fagopyrum esculentum Nutrition 0.000 claims description 11
- 240000007049 Juglans regia Species 0.000 claims description 10
- 235000009496 Juglans regia Nutrition 0.000 claims description 10
- 235000020238 sunflower seed Nutrition 0.000 claims description 10
- 235000020234 walnut Nutrition 0.000 claims description 10
- 239000004566 building material Substances 0.000 claims description 9
- 235000017060 Arachis glabrata Nutrition 0.000 claims description 8
- 244000105624 Arachis hypogaea Species 0.000 claims description 8
- 235000010777 Arachis hypogaea Nutrition 0.000 claims description 8
- 235000018262 Arachis monticola Nutrition 0.000 claims description 8
- 235000020232 peanut Nutrition 0.000 claims description 8
- 239000010903 husk Substances 0.000 claims description 6
- 235000017166 Bambusa arundinacea Nutrition 0.000 claims description 4
- 235000017491 Bambusa tulda Nutrition 0.000 claims description 4
- 235000015334 Phyllostachys viridis Nutrition 0.000 claims description 4
- 244000198134 Agave sisalana Species 0.000 claims description 3
- 241000609240 Ambelania acida Species 0.000 claims description 3
- 241000209128 Bambusa Species 0.000 claims description 3
- 240000008564 Boehmeria nivea Species 0.000 claims description 3
- 244000025254 Cannabis sativa Species 0.000 claims description 3
- 235000012766 Cannabis sativa ssp. sativa var. sativa Nutrition 0.000 claims description 3
- 235000012765 Cannabis sativa ssp. sativa var. spontanea Nutrition 0.000 claims description 3
- 244000060011 Cocos nucifera Species 0.000 claims description 3
- 235000013162 Cocos nucifera Nutrition 0.000 claims description 3
- 240000000491 Corchorus aestuans Species 0.000 claims description 3
- 235000011777 Corchorus aestuans Nutrition 0.000 claims description 3
- 235000010862 Corchorus capsularis Nutrition 0.000 claims description 3
- 229920000742 Cotton Polymers 0.000 claims description 3
- 240000008620 Fagopyrum esculentum Species 0.000 claims description 3
- 240000000797 Hibiscus cannabinus Species 0.000 claims description 3
- 240000005979 Hordeum vulgare Species 0.000 claims description 3
- 235000007340 Hordeum vulgare Nutrition 0.000 claims description 3
- 240000006240 Linum usitatissimum Species 0.000 claims description 3
- 235000004431 Linum usitatissimum Nutrition 0.000 claims description 3
- 240000000907 Musa textilis Species 0.000 claims description 3
- 244000273256 Phragmites communis Species 0.000 claims description 3
- 235000014676 Phragmites communis Nutrition 0.000 claims description 3
- 240000006394 Sorghum bicolor Species 0.000 claims description 3
- 235000011684 Sorghum saccharatum Nutrition 0.000 claims description 3
- 239000010905 bagasse Substances 0.000 claims description 3
- 235000009120 camo Nutrition 0.000 claims description 3
- 235000005607 chanvre indien Nutrition 0.000 claims description 3
- 239000000428 dust Substances 0.000 claims description 3
- 239000011487 hemp Substances 0.000 claims description 3
- 235000014571 nuts Nutrition 0.000 claims description 3
- 238000004513 sizing Methods 0.000 claims 1
- 238000009826 distribution Methods 0.000 abstract description 17
- VTYYLEPIZMXCLO-UHFFFAOYSA-L Calcium carbonate Chemical compound [Ca+2].[O-]C([O-])=O VTYYLEPIZMXCLO-UHFFFAOYSA-L 0.000 description 56
- 239000010451 perlite Substances 0.000 description 56
- 235000019362 perlite Nutrition 0.000 description 56
- 239000004615 ingredient Substances 0.000 description 37
- 229920002472 Starch Polymers 0.000 description 35
- 239000011490 mineral wool Substances 0.000 description 35
- 235000019698 starch Nutrition 0.000 description 35
- 239000008107 starch Substances 0.000 description 31
- 229910000019 calcium carbonate Inorganic materials 0.000 description 28
- 239000000463 material Substances 0.000 description 28
- 239000000945 filler Substances 0.000 description 21
- 238000002156 mixing Methods 0.000 description 16
- 239000011152 fibreglass Substances 0.000 description 13
- 230000002745 absorbent Effects 0.000 description 12
- 239000002250 absorbent Substances 0.000 description 12
- 229910052751 metal Inorganic materials 0.000 description 12
- 239000002184 metal Substances 0.000 description 12
- 239000007787 solid Substances 0.000 description 12
- 238000010521 absorption reaction Methods 0.000 description 11
- 238000013019 agitation Methods 0.000 description 11
- 230000008569 process Effects 0.000 description 9
- 238000012360 testing method Methods 0.000 description 9
- 241000219051 Fagopyrum Species 0.000 description 8
- 239000004927 clay Substances 0.000 description 8
- 229910052570 clay Inorganic materials 0.000 description 8
- 239000012784 inorganic fiber Substances 0.000 description 8
- 239000000203 mixture Substances 0.000 description 8
- 241000196324 Embryophyta Species 0.000 description 7
- 230000005540 biological transmission Effects 0.000 description 6
- 239000000047 product Substances 0.000 description 6
- 230000009467 reduction Effects 0.000 description 6
- 239000002028 Biomass Substances 0.000 description 5
- 239000008187 granular material Substances 0.000 description 5
- 230000005484 gravity Effects 0.000 description 5
- 238000003801 milling Methods 0.000 description 5
- 238000003825 pressing Methods 0.000 description 5
- 240000002470 Amphicarpaea bracteata Species 0.000 description 4
- 235000000073 Amphicarpaea bracteata Nutrition 0.000 description 4
- 229920005610 lignin Polymers 0.000 description 4
- 230000000704 physical effect Effects 0.000 description 4
- 238000004537 pulping Methods 0.000 description 4
- 239000002994 raw material Substances 0.000 description 4
- 238000007873 sieving Methods 0.000 description 4
- 239000002699 waste material Substances 0.000 description 4
- HEMHJVSKTPXQMS-UHFFFAOYSA-M Sodium hydroxide Chemical compound [OH-].[Na+] HEMHJVSKTPXQMS-UHFFFAOYSA-M 0.000 description 3
- 230000015572 biosynthetic process Effects 0.000 description 3
- 238000000227 grinding Methods 0.000 description 3
- 239000011148 porous material Substances 0.000 description 3
- 239000000126 substance Substances 0.000 description 3
- 210000002268 wool Anatomy 0.000 description 3
- 230000008901 benefit Effects 0.000 description 2
- 239000006227 byproduct Substances 0.000 description 2
- 235000010216 calcium carbonate Nutrition 0.000 description 2
- 238000005520 cutting process Methods 0.000 description 2
- 238000011161 development Methods 0.000 description 2
- 238000001035 drying Methods 0.000 description 2
- 238000009950 felting Methods 0.000 description 2
- 239000010440 gypsum Substances 0.000 description 2
- 229910052602 gypsum Inorganic materials 0.000 description 2
- 239000001257 hydrogen Substances 0.000 description 2
- 229910052739 hydrogen Inorganic materials 0.000 description 2
- 229910010272 inorganic material Inorganic materials 0.000 description 2
- 239000011147 inorganic material Substances 0.000 description 2
- 239000012978 lignocellulosic material Substances 0.000 description 2
- 239000000779 smoke Substances 0.000 description 2
- GEHJYWRUCIMESM-UHFFFAOYSA-L sodium sulfite Chemical compound [Na+].[Na+].[O-]S([O-])=O GEHJYWRUCIMESM-UHFFFAOYSA-L 0.000 description 2
- 239000004575 stone Substances 0.000 description 2
- VZSRBBMJRBPUNF-UHFFFAOYSA-N 2-(2,3-dihydro-1H-inden-2-ylamino)-N-[3-oxo-3-(2,4,6,7-tetrahydrotriazolo[4,5-c]pyridin-5-yl)propyl]pyrimidine-5-carboxamide Chemical compound C1C(CC2=CC=CC=C12)NC1=NC=C(C=N1)C(=O)NCCC(N1CC2=C(CC1)NN=N2)=O VZSRBBMJRBPUNF-UHFFFAOYSA-N 0.000 description 1
- 229910021578 Iron(III) chloride Inorganic materials 0.000 description 1
- 244000082204 Phyllostachys viridis Species 0.000 description 1
- 235000008331 Pinus X rigitaeda Nutrition 0.000 description 1
- 235000011613 Pinus brutia Nutrition 0.000 description 1
- 241000018646 Pinus brutia Species 0.000 description 1
- 239000004115 Sodium Silicate Substances 0.000 description 1
- 229920002522 Wood fibre Polymers 0.000 description 1
- 241000482268 Zea mays subsp. mays Species 0.000 description 1
- 239000001240 acylated distarch phosphate Substances 0.000 description 1
- 239000002154 agricultural waste Substances 0.000 description 1
- DIZPMCHEQGEION-UHFFFAOYSA-H aluminium sulfate (anhydrous) Chemical compound [Al+3].[Al+3].[O-]S([O-])(=O)=O.[O-]S([O-])(=O)=O.[O-]S([O-])(=O)=O DIZPMCHEQGEION-UHFFFAOYSA-H 0.000 description 1
- ANBBXQWFNXMHLD-UHFFFAOYSA-N aluminum;sodium;oxygen(2-) Chemical compound [O-2].[O-2].[Na+].[Al+3] ANBBXQWFNXMHLD-UHFFFAOYSA-N 0.000 description 1
- QVGXLLKOCUKJST-UHFFFAOYSA-N atomic oxygen Chemical compound [O] QVGXLLKOCUKJST-UHFFFAOYSA-N 0.000 description 1
- 239000011425 bamboo Substances 0.000 description 1
- BRPQOXSCLDDYGP-UHFFFAOYSA-N calcium oxide Chemical compound [O-2].[Ca+2] BRPQOXSCLDDYGP-UHFFFAOYSA-N 0.000 description 1
- 239000000292 calcium oxide Substances 0.000 description 1
- ODINCKMPIJJUCX-UHFFFAOYSA-N calcium oxide Inorganic materials [Ca]=O ODINCKMPIJJUCX-UHFFFAOYSA-N 0.000 description 1
- 239000001913 cellulose Substances 0.000 description 1
- 229920002678 cellulose Polymers 0.000 description 1
- 239000004568 cement Substances 0.000 description 1
- 238000007385 chemical modification Methods 0.000 description 1
- 239000011248 coating agent Substances 0.000 description 1
- 238000000576 coating method Methods 0.000 description 1
- 239000002131 composite material Substances 0.000 description 1
- 238000010411 cooking Methods 0.000 description 1
- 230000002950 deficient Effects 0.000 description 1
- LVYZJEPLMYTTGH-UHFFFAOYSA-H dialuminum chloride pentahydroxide dihydrate Chemical compound [Cl-].[Al+3].[OH-].[OH-].[Al+3].[OH-].[OH-].[OH-].O.O LVYZJEPLMYTTGH-UHFFFAOYSA-H 0.000 description 1
- 239000006185 dispersion Substances 0.000 description 1
- 238000005265 energy consumption Methods 0.000 description 1
- 238000012851 eutrophication Methods 0.000 description 1
- 238000009313 farming Methods 0.000 description 1
- 239000011790 ferrous sulphate Substances 0.000 description 1
- 235000003891 ferrous sulphate Nutrition 0.000 description 1
- 238000001914 filtration Methods 0.000 description 1
- 239000008394 flocculating agent Substances 0.000 description 1
- 238000007373 indentation Methods 0.000 description 1
- 229910052500 inorganic mineral Inorganic materials 0.000 description 1
- 238000009413 insulation Methods 0.000 description 1
- RBTARNINKXHZNM-UHFFFAOYSA-K iron trichloride Chemical compound Cl[Fe](Cl)Cl RBTARNINKXHZNM-UHFFFAOYSA-K 0.000 description 1
- BAUYGSIQEAFULO-UHFFFAOYSA-L iron(2+) sulfate (anhydrous) Chemical compound [Fe+2].[O-]S([O-])(=O)=O BAUYGSIQEAFULO-UHFFFAOYSA-L 0.000 description 1
- 229910000359 iron(II) sulfate Inorganic materials 0.000 description 1
- 238000010030 laminating Methods 0.000 description 1
- 239000004816 latex Substances 0.000 description 1
- 229920000126 latex Polymers 0.000 description 1
- 230000014759 maintenance of location Effects 0.000 description 1
- 238000005259 measurement Methods 0.000 description 1
- 238000010297 mechanical methods and process Methods 0.000 description 1
- 230000005226 mechanical processes and functions Effects 0.000 description 1
- 238000002844 melting Methods 0.000 description 1
- 230000008018 melting Effects 0.000 description 1
- 239000011707 mineral Substances 0.000 description 1
- 235000010755 mineral Nutrition 0.000 description 1
- 230000004048 modification Effects 0.000 description 1
- 238000012986 modification Methods 0.000 description 1
- 239000001301 oxygen Substances 0.000 description 1
- 229910052760 oxygen Inorganic materials 0.000 description 1
- 230000020477 pH reduction Effects 0.000 description 1
- 238000004806 packaging method and process Methods 0.000 description 1
- 229920002401 polyacrylamide Polymers 0.000 description 1
- 238000002360 preparation method Methods 0.000 description 1
- -1 sawdust Substances 0.000 description 1
- 238000005549 size reduction Methods 0.000 description 1
- 229910001388 sodium aluminate Inorganic materials 0.000 description 1
- NTHWMYGWWRZVTN-UHFFFAOYSA-N sodium silicate Chemical compound [Na+].[Na+].[O-][Si]([O-])=O NTHWMYGWWRZVTN-UHFFFAOYSA-N 0.000 description 1
- 229910052911 sodium silicate Inorganic materials 0.000 description 1
- 229910052979 sodium sulfide Inorganic materials 0.000 description 1
- GRVFOGOEDUUMBP-UHFFFAOYSA-N sodium sulfide (anhydrous) Chemical compound [Na+].[Na+].[S-2] GRVFOGOEDUUMBP-UHFFFAOYSA-N 0.000 description 1
- 235000010265 sodium sulphite Nutrition 0.000 description 1
- 239000002910 solid waste Substances 0.000 description 1
- 238000005507 spraying Methods 0.000 description 1
- 239000000725 suspension Substances 0.000 description 1
- 238000010408 sweeping Methods 0.000 description 1
- 238000010998 test method Methods 0.000 description 1
- 239000000196 tragacanth Substances 0.000 description 1
- 238000010792 warming Methods 0.000 description 1
- 239000002025 wood fiber Substances 0.000 description 1
Classifications
-
- E—FIXED CONSTRUCTIONS
- E04—BUILDING
- E04B—GENERAL BUILDING CONSTRUCTIONS; WALLS, e.g. PARTITIONS; ROOFS; FLOORS; CEILINGS; INSULATION OR OTHER PROTECTION OF BUILDINGS
- E04B1/00—Constructions in general; Structures which are not restricted either to walls, e.g. partitions, or floors or ceilings or roofs
- E04B1/62—Insulation or other protection; Elements or use of specified material therefor
- E04B1/74—Heat, sound or noise insulation, absorption, or reflection; Other building methods affording favourable thermal or acoustical conditions, e.g. accumulating of heat within walls
- E04B1/82—Heat, sound or noise insulation, absorption, or reflection; Other building methods affording favourable thermal or acoustical conditions, e.g. accumulating of heat within walls specifically with respect to sound only
- E04B1/84—Sound-absorbing elements
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B28/00—Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements
- C04B28/24—Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements containing alkyl, ammonium or metal silicates; containing silica sols
- C04B28/26—Silicates of the alkali metals
-
- E—FIXED CONSTRUCTIONS
- E04—BUILDING
- E04B—GENERAL BUILDING CONSTRUCTIONS; WALLS, e.g. PARTITIONS; ROOFS; FLOORS; CEILINGS; INSULATION OR OTHER PROTECTION OF BUILDINGS
- E04B1/00—Constructions in general; Structures which are not restricted either to walls, e.g. partitions, or floors or ceilings or roofs
- E04B1/62—Insulation or other protection; Elements or use of specified material therefor
- E04B1/74—Heat, sound or noise insulation, absorption, or reflection; Other building methods affording favourable thermal or acoustical conditions, e.g. accumulating of heat within walls
- E04B1/82—Heat, sound or noise insulation, absorption, or reflection; Other building methods affording favourable thermal or acoustical conditions, e.g. accumulating of heat within walls specifically with respect to sound only
- E04B1/84—Sound-absorbing elements
- E04B1/86—Sound-absorbing elements slab-shaped
-
- E—FIXED CONSTRUCTIONS
- E04—BUILDING
- E04B—GENERAL BUILDING CONSTRUCTIONS; WALLS, e.g. PARTITIONS; ROOFS; FLOORS; CEILINGS; INSULATION OR OTHER PROTECTION OF BUILDINGS
- E04B9/00—Ceilings; Construction of ceilings, e.g. false ceilings; Ceiling construction with regard to insulation
- E04B9/04—Ceilings; Construction of ceilings, e.g. false ceilings; Ceiling construction with regard to insulation comprising slabs, panels, sheets or the like
-
- E—FIXED CONSTRUCTIONS
- E04—BUILDING
- E04C—STRUCTURAL ELEMENTS; BUILDING MATERIALS
- E04C2/00—Building elements of relatively thin form for the construction of parts of buildings, e.g. sheet materials, slabs, or panels
- E04C2/02—Building elements of relatively thin form for the construction of parts of buildings, e.g. sheet materials, slabs, or panels characterised by specified materials
-
- E—FIXED CONSTRUCTIONS
- E04—BUILDING
- E04C—STRUCTURAL ELEMENTS; BUILDING MATERIALS
- E04C2/00—Building elements of relatively thin form for the construction of parts of buildings, e.g. sheet materials, slabs, or panels
- E04C2/02—Building elements of relatively thin form for the construction of parts of buildings, e.g. sheet materials, slabs, or panels characterised by specified materials
- E04C2/26—Building elements of relatively thin form for the construction of parts of buildings, e.g. sheet materials, slabs, or panels characterised by specified materials composed of materials covered by two or more of groups E04C2/04, E04C2/08, E04C2/10 or of materials covered by one of these groups with a material not specified in one of the groups
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2111/00—Mortars, concrete or artificial stone or mixtures to prepare them, characterised by specific function, property or use
- C04B2111/52—Sound-insulating materials
-
- E—FIXED CONSTRUCTIONS
- E04—BUILDING
- E04B—GENERAL BUILDING CONSTRUCTIONS; WALLS, e.g. PARTITIONS; ROOFS; FLOORS; CEILINGS; INSULATION OR OTHER PROTECTION OF BUILDINGS
- E04B1/00—Constructions in general; Structures which are not restricted either to walls, e.g. partitions, or floors or ceilings or roofs
- E04B1/62—Insulation or other protection; Elements or use of specified material therefor
- E04B1/74—Heat, sound or noise insulation, absorption, or reflection; Other building methods affording favourable thermal or acoustical conditions, e.g. accumulating of heat within walls
- E04B2001/742—Use of special materials; Materials having special structures or shape
- E04B2001/745—Vegetal products, e.g. plant stems, barks
-
- E—FIXED CONSTRUCTIONS
- E04—BUILDING
- E04B—GENERAL BUILDING CONSTRUCTIONS; WALLS, e.g. PARTITIONS; ROOFS; FLOORS; CEILINGS; INSULATION OR OTHER PROTECTION OF BUILDINGS
- E04B1/00—Constructions in general; Structures which are not restricted either to walls, e.g. partitions, or floors or ceilings or roofs
- E04B1/62—Insulation or other protection; Elements or use of specified material therefor
- E04B1/74—Heat, sound or noise insulation, absorption, or reflection; Other building methods affording favourable thermal or acoustical conditions, e.g. accumulating of heat within walls
- E04B2001/742—Use of special materials; Materials having special structures or shape
- E04B2001/746—Recycled materials, e.g. made of used tires, bumpers or newspapers
-
- E—FIXED CONSTRUCTIONS
- E04—BUILDING
- E04B—GENERAL BUILDING CONSTRUCTIONS; WALLS, e.g. PARTITIONS; ROOFS; FLOORS; CEILINGS; INSULATION OR OTHER PROTECTION OF BUILDINGS
- E04B1/00—Constructions in general; Structures which are not restricted either to walls, e.g. partitions, or floors or ceilings or roofs
- E04B1/62—Insulation or other protection; Elements or use of specified material therefor
- E04B1/74—Heat, sound or noise insulation, absorption, or reflection; Other building methods affording favourable thermal or acoustical conditions, e.g. accumulating of heat within walls
- E04B1/82—Heat, sound or noise insulation, absorption, or reflection; Other building methods affording favourable thermal or acoustical conditions, e.g. accumulating of heat within walls specifically with respect to sound only
- E04B2001/8245—Machines for manufacturing, shaping, piercing or filling sound insulating elements
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
- Y02A—TECHNOLOGIES FOR ADAPTATION TO CLIMATE CHANGE
- Y02A30/00—Adapting or protecting infrastructure or their operation
- Y02A30/24—Structural elements or technologies for improving thermal insulation
- Y02A30/244—Structural elements or technologies for improving thermal insulation using natural or recycled building materials, e.g. straw, wool, clay or used tires
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
- Y02W—CLIMATE CHANGE MITIGATION TECHNOLOGIES RELATED TO WASTEWATER TREATMENT OR WASTE MANAGEMENT
- Y02W30/00—Technologies for solid waste management
- Y02W30/50—Reuse, recycling or recovery technologies
- Y02W30/91—Use of waste materials as fillers for mortars or concrete
Definitions
- PANELS INCLUDING RENEWABLE COMPONENTS AND METHODS FOR MANUFACTURING
- the present invention relates to panels for the building industry that include a renewable component to improve acoustic and physical properties of the panel. Methods of making such panels are also provided.
- BACKGROUND Panels used as tiles or walls fall into the category of building products and provide architectural value, acoustical absorbency, acoustical attenuation and utility functions to building interiors.
- panels such as acoustical panels, are used in areas that require noise control. Examples of these areas are office buildings, department stores, hospitals, hotels, auditoriums, airports, restaurants, libraries, classrooms, theaters, and cinemas, as well as residential buildings.
- an acoustical panel for example, is substantially flat and self-supporting for suspension in a typical ceiling grid system or similar structure.
- acoustical panels possess a certain level of hardness and rigidity, which is often measured by its modulus of rupture (“MOR").
- MOR modulus of rupture
- an acoustical panel also possesses sound absorption, as well as transmission reduction properties. Sound absorption is typically measured by its Noise Reduction Coefficient ("NRC”) as described in ASTM C423.
- NRC Noise Reduction Coefficient
- An acoustical panel with an NRC value of 0.60 absorbs 60% of the sound that strikes it and deflects 40% of the sound.
- Another test method is estimated NRC (“eNRC”), which uses an impedance tube as described in ASTM C384.
- CAC Ceiling Attenuation Class
- STC Sound Transmission Class
- Acoustical panels made in accordance with various industry standards and building codes have a Class A fire rating. According to ASTM E84, a flame spread index less than 25 and a smoke development index less than 50 are required. Airflow resistivity, a measurement of the porosity of a mat, is tested according to modified ASTM C423 and C386 standards. In addition, MOR, hardness and sag of acoustical panels are tested according to ASTM C367. Increased porosity of a base mat improves acoustical absorbency, but it is not measured by any specific industry standard or building code. Currently, most acoustical panels or tiles are made using a water-felting process preferred in the art due to its speed and efficiency.
- the base mat is formed utilizing a method similar to papermaking.
- aqueous slurry including a dilute aqueous dispersion of mineral wool and a lightweight aggregate, is delivered onto a moving foraminous wire of a Fourdrinier-type mat forming machine. Water is drained by gravity from the slurry and then optionally further dewatered by means of vacuum suction and/or by pressing. Next, the dewatered base mat, which may still hold some water, is dried in a heated oven or kiln to remove the residual moisture.
- Panels of acceptable size, appearance and acoustic properties are obtained by finishing the dried base mat. Finishing includes surface grinding, cutting, perforation/fissuring, roll/spray coating, edge cutting and/or laminating the panel onto a scrim or screen.
- a typical acoustical panel base mat composition includes inorganic fibers, cellulosic fibers, binders and fillers.
- inorganic fibers can be either mineral wool (which is interchangeable with slag wool, rock wool and stone wool) or fiberglass.
- Mineral wool is formed by first melting slag or rock wool at 1300°C (2372°F) to 1650 0 C (3002 0 F). The molten mineral is then spun into wool in a fiberizing spinner via a continuous air stream.
- Inorganic fibers are stiff, giving the base mat bulk and porosity.
- cellulosic fibers act as structural elements, providing both wet and dry base mat strength. The strength is due to the formation of countless hydrogen bonds with various ingredients in the base mat, which is a result of the hydrophilic nature of the cellulosic fibers.
- a typical base mat binder used is starch.
- Typical starches used in acoustical panels are unmodified, uncooked starch granules that are dispersed in the aqueous panel slurry and distributed generally uniformly in the base mat. Once heated, the starch granules become cooked and dissolve, providing binding ability to the panel ingredients. Starches not only assist in the flexural strength of the acoustical panels, but also for hardness and rigidity of the panel. In certain panel compositions having a high concentration of inorganic fibers, a latex binder is used as the primary binding agent.
- Typical base mat fillers include both heavyweight and lightweight inorganic materials.
- a primary function of the filler is to provide flexural strength and contribute to hardness of the panel.
- filler is used throughout this disclosure, it is to be understood that each filler has unique properties and/or characteristics that can influence the rigidity, hardness, sag, sound absorption and reduction in the sound transmission in panels.
- heavyweight fillers include calcium carbonate, clay or gypsum.
- An example of a lightweight filler includes expanded perlite. As a filler, expanded perlite has the advantage of being bulky, thereby reducing the amount of filler required in the base mat.
- expanded perlite is relatively fragile and frangible during the manufacturing process. In general, the greater the amount of expanded perlite used, the poorer the panel acoustic absorption properties.
- the expansion of perlite consumes a significant amount of energy. Expanded perlite is formed when perlite ore is introduced into an expanding tower that is heated to about 950 0 C (1750 0 F). Water in the perlite structure turns to steam and the resulting expansion causes the perlite to "pop" like popcorn to reduce the density to about one-tenth of the unexpanded material.
- the lower bulk density of expanded perlite enables it to flow upward in the expanding tower and be collected by a filtering device. This process uses a relatively large amount of energy to heat all of the perlite to a temperature sufficient to vaporize the water within it.
- a common chemical pulping method uses sodium sulfide, sodium hydroxide or sodium sulfite to dissolve the lignin at about 150°C (302°F) to about 180 0 C (356°F), reducing the fiber's biomass by about 40-60%.
- a thermal-mechanical pulping method subjects wood chips to high temperatures (about 130°C (266°F)) and high pressure (about 3-4 atmospheres (304-405 kPa)), causing the lignin to soften and allowing fiber cells to be mechanically torn apart. Disruption of the lignin bond causes the defiberization of the raw material with a resulting loss in its biomass of about 5-10%. Both chemical and thermal-mechanical pulping processes require significant amounts of energy to reduce the ligno- cellulosic material to its individual fibers. Further, the loss of such a large fraction of the biomass increases the cost of raw materials.
- U.S. Patent No. 6,322,731 discloses a method for forming a structural panel of indefinite length, comprising an organic particulate base material consisting predominately of rice hulls and a binder. Due to the requirements for structural integrity, the process requires a combination of high temperature and high pressure to form a panel of sufficient strength. The resultant panel has relatively low sound absorption value, due to its high density and low porosity. The thermal and acoustic insulation characteristics are achieved through the encased cavities.
- U.S. Patent No. 5,851 ,281 discloses a process for manufacturing a cement-waste material composite where the waste material is rice husks. The rice husks are heated to approximately 600°C (1112°F) in the absence of oxygen to produce micro-granules.
- U.S. Patent No. 6,443,258 discloses an acoustically absorbent porous panel formed from a cured, aqueous, foamed, cementitious material. The panel provides good acoustical performance with enhanced durability and moisture resistance. Rice hull ash is added to enhance the overall hardness of the foamed cement panel.
- a panel is provided for use as a building material having improved acoustic and physical properties.
- the present panels include a renewable component, such as rice hulls and have improved acoustic properties, including maintaining a relatively constant CAC or STC.
- an improved NRC is achieved while maintaining or improving other physical properties of the panel, including the MOR, hardness, airflow resistivity and sag.
- the present panel includes about 0.1 % to about 95% by weight of a renewable component.
- the panel has at least one of a CAC value of at least about 25, an NRC value of at least about 0.25 and an STC value of at least about 25.
- Some other embodiments of the present panel include a panel core including from about 0.1 % to about 95% by weight of a ground renewable component; from about 0.1 % to about 95% by weight of one or more fibers; from about 1 % to about 30% by weight of one or more binders; and from about 3% to about 80% by weight of one or more fillers, all based on the dry panel weight.
- the ground renewable component has a particle size distribution whereby less than 5% of the particles are retained by a mesh screen with openings of about 0.312 inches and less than 5% of the particles pass through a mesh screen with openings of about 0.059 inches.
- a method for the production of a panel for use as a building material includes the steps of forming an aqueous slurry that includes from about 0.1 % to about 95% of the renewable component and water. A base mat is then formed from the slurry using a foraminous wire. The water from the base mat is removed and the base mat is finished to form a panel for use as a building material.
- the panel made by this method has at least one of a CAC value of at least about 25 and an NRC value of at least about 0.25.
- At least one other embodiment is a method for the production of a panel for use as a building material includes the steps of selecting a ground renewable component; combining water with from about 0.1 % to about 95% by weight of the renewable component; from about 1 % to about 50% by weight of a fiber; from about 1 % to about 30% by weight of a binder; and from about 3% to about 80% by weight of a filler to form an aqueous slurry; forming a base mat on a foraminous wire from the aqueous slurry; removing water from the base mat and finishing the base mat.
- the renewable component is separated to obtain the particle size distribution described above.
- the panel made by this method has at least one of a CAC value of at least about 25 and an NRC value of at least about 0.25.
- a ground or milled renewable component is advantageous since preparation of the renewable component requires less energy than other filler materials. It is preferred that the renewable component is ground or directly incorporated into acoustical panels. Energy is consumed in this process only if the renewable component is ground and/or sieved, using less energy compared to expanding perlite.
- renewable material Another advantage of using a renewable material is that it is prepared without significant loss in biomass.
- the ground or milled renewable material maintains its bulk structure and is not subjected to chemical modification or changes in chemical structure, such as defiberizing. Retention of the biomass results in more efficient use of the purchased raw materials, thereby reducing its cost.
- the product, method and composition described herein are intended to apply to panels for use as building materials. More specifically, the panels can also be used as ceiling panel products, acoustical panels or tiles.
- the following discussion is directed to an acoustical panel as one embodiment of the invention; however this is not intended to limit the invention in any way.
- Fibers are present in the acoustical panel as inorganic fibers, organic fibers or combinations thereof.
- Inorganic fibers can be mineral wool, slag wool, rock wool, stone wool, fiberglass or mixtures thereof.
- the inorganic fibers are stiff, giving the base mat bulk and porosity.
- Inorganic fibers are present in the acoustical panel in amounts of about 0.1 % to about 95%, based on the weight of the panel. At least one embodiment of the acoustical panel uses mineral wool as the preferred fiber.
- Cellulosic fibers, an example of an organic fiber act as structural elements providing both wet and dry base mat strength.
- Cellulosic fibers in the base mat range from about 1 % to about 50% by weight of the panel, preferably about 5% to about 40% and most preferably from about 10% to about 30%.
- One preferred cellulosic fiber is derived from recycled newsprint.
- the panels include at least one ingredient that is a renewable component.
- Renewable components are defined as wood or non-wood plants, or a portion of wood or non-wood plants. These renewable components are preferably ligno-cellulosic, which include cellulose and lignin. Potential sources of these materials are waste materials or byproducts from the farming industry, the agricultural industry, the forestry industry and/or the building industry.
- Rice hulls or husks are examples of the renewable component.
- examples of other renewable components include, but are not limited to: wheat chaff, oak husk, rye whisk, cotton seed hull, coconut shells, corn bran, corn cobs, rice straw stalk, wheat straw stalk, barley straw stalk, oat straw stalk, rye straw stalk, bagasse, reeds, Esparto, Sabai, flax, kenaf, jute, hemp, ramie, abaca, sisal, saw dust, bamboos, wood chips, sorghum stalks, sunflower seeds, buckwheat hulls, nut shells, including peanut and walnut shells, other similar materials and mixtures thereof.
- the renewable components are preferably reduced in size prior to mixing with other panel ingredients.
- the renewable materials preferably have a particle size that passes through a mesh screen with 0.312 inch openings (2.5 mesh as defined by the ASTM sieve chart) and is retained on a mesh screen with 0.0059 inch openings (100 mesh as defined by the ASTM sieve chart).
- the renewable component is used whole or as received from a supplier.
- Use of the term "renewable component” is intended to include particles that are whole or reduced in size by any method as is known in the art, including particles that are comminuted, shredded, ground, milled, sieved or combinations thereof. Size reduction is optionally achieved by mechanical processes, such as grinding or milling, to obtain the desired sizes. At least one embodiment uses hammer mill-type equipment.
- renewable components can be sieved with screens of particular mesh sizes to obtain a desired particle size distribution.
- the coarse fraction that is too large to pass through the largest desired screen is optionally removed and re-processed until the resulting material passes through the screen.
- the ground rice hulls are first sieved with a #30 mesh screen to remove large particles, followed by sieving through a #80 mesh screen to remove particles that are too fine.
- the processed hulls that pass the #30 mesh screen and are retained on the #80 mesh screen are used to make the acoustical panels.
- the materials that pass through the #80 mesh screen are not used in the panels.
- the #30 mesh screen has an opening of 0.022 inches or 0.55 mm.
- the #80 mesh screen has an opening of 0.007 inches or 180 ⁇ m.
- the processed hulls obtained directly from a rice milling plant are used to make acoustical panels.
- the particle distribution of the comminuted renewable material optionally has at least about 95% of the particles that pass through a #30 mesh screen and no more than about 5% of the particles pass through a #80 mesh screen of a U.S. Sieve Set.
- expanded perlite is a material that is often used in building panels. When used in ceiling panels, expanded perlite tends to form a structure that lacks interconnected pores. Introducing a ground or milled renewable component into acoustical panels helps to interrupt the expanded perlite structure and thereby increases interconnected pores. Panels including ground renewable components in addition to perlite are more porous and yield higher acoustical absorbency than panels having perlite without any ground or milled renewable components. It has been observed that the larger the particle size of the renewable component, the higher the acoustical absorption value. The optimum particle size distribution for any one embodiment depends on the desired acoustical absorption value.
- the renewable component particle size distribution is desirably compatible with other ingredients, such as fiber, expanded perlite and the like, to form a homogeneous and uniform slurry. Formation of a uniform slurry leads to production of homogeneous and uniform base mat.
- the particle size distribution is preferably chosen so as to maintain or improve the physical integrity of the panel.
- the renewable components include less than about 5% by weight of particles that are retained by a #6 mesh screen. In other embodiments, the renewable components used include less than about 5% of particles that are retained by a #20 mesh screen. In still other embodiments, the ground or milled renewable components used include less than about 5% of particles that are retained by a #30 mesh screen.
- the renewable components have a bulk density between about 5 to about 50 lbs/ft 3 (80 to 800 kg/m 3 ), with a more preferred bulk density of about 10 to 40 lbs/ft 3 (160 to 640 kg/m 3 ) and a most preferred range of about 20 to about 35 lbs/ft 3 (320 to 560 kg/m 3 ).
- the #6 mesh screen has an opening of 0.132 inches or 3.35 mm
- the #20 screen mesh has an opening of 0.0312 inches or 800 ⁇ m
- the #30 screen mesh has an opening of 0.022 inches or 0.55 mm.
- Starch is optionally included in the base mat as a binder. Typical starches are unmodified, uncooked starch granules that are dispersed in an aqueous slurry and become distributed generally uniformly through the base mat. The base mat is heated, cooking and dissolving the starch granules to bind the panel ingredients together. Starch not only assists in the flexural strength of the acoustical panels, but also improves the hardness and rigidity of the panel. In addition, the base mat optionally includes starches in the range of about 1 % to about 30% by weight of the panel, more preferably from about 3% to about 15% and most preferably from about 5% to about 10%.
- Typical base mat fillers include both lightweight and heavyweight inorganic materials.
- heavyweight fillers include calcium carbonate, clay or gypsum.
- Other fillers are also contemplated for use in the acoustical panels.
- calcium carbonate in the range from about 0.5% to about 10% by weight of the panel is utilized.
- the calcium carbonate can also be used in the range of about 3% to about 8% by weight of the panel.
- An example of a lightweight filler is expanded perlite.
- Expanded perlite is bulky, reducing the amount of filler used in the base mat. Primary functions of the filler are improved flexural strength and hardness of the panel. Even though the term "filler" is used throughout this discussion, it is to be understood that each filler has unique properties and/or characteristics that can influence the rigidity, hardness, sag, sound absorption and reduction in the sound transmission in panels.
- the expanded perlite in the base mat of this embodiment is present in amounts ranging from about 5% to about 80% by weight of the panel, more preferably about 10% to about 60% by weight of the panel and most preferably from about 20% to about 40% by weight of the panel.
- the base mat includes a renewable component, mineral wool, expanded perlite, starch, calcium carbonate and/or clay.
- a renewable component mineral wool, expanded perlite, starch, calcium carbonate and/or clay.
- One of the preferred renewable components is ground rice hulls.
- the percentage of renewable component is in the range of about 0.1 % to about 95% by weight of the panel, more preferably about 5% to about 60% and most preferably from about 7% to about 40%.
- acoustical panel Another optional ingredient in the acoustical panel is clay, which is typically included to improve fire resistance. When exposed to fire, the clay does not burn; instead, it sinters.
- Acoustical panels optionally include from about 0% to about 10% clay by weight of the panel, with a preferred range of about 1 % to about 5%.
- clay many types of clay are used including but not limited to Spinks Clay and Ball Clay from Gleason, TN. and Old Hickory Clay from Hickory, KY.
- a flocculant is also optionally added to the acoustical panels.
- the flocculant is preferably used in the range of about 0.1 % to about 3% by weight of the panel and more preferably from about 0.1 % to about 2%.
- Useful flocculants include, but are not limited to, aluminum chlorohydrate, aluminum sulfate, calcium oxide, ferric chloride, ferrous sulfate, polyacrylamide, sodium aluminate and sodium silicate.
- an aqueous slurry is preferably created by mixing water with the renewable component, mineral wool, expanded perlite, cellulosic fibers, starch, calcium carbonate, clay and flocculant.
- Mixing operations are preferably carried out in a stock chest, either in batch modes or in continuous modes.
- the amount of added water is such that the resultant total solid content or consistency is in the range of about 1 % to about 8% consistency, preferably from about 2% to about 6% and more preferably from about 3% to about 5%.
- the slurry is transported to a headbox, which provides a steady flow of the slurry material.
- the slurry flowing out of the headbox is distributed onto a moving foraminous wire to form the wet base mat.
- Water is first drained from the wire by gravity. It is contemplated that in certain embodiments, a low vacuum pressure may be used in combination with, or after draining water from the slurry by gravity. Additional water is then optionally removed by pressing and/or using vacuum-assisted water removal, as would be appreciated by those having ordinary skill in the art. The remainder of the water is typically evaporated in an oven or kiln to form the formed base mat.
- the base mats preferably have a bulk density between about 7 to about 30 lbs/ft 3 (112 to 480 kg/m 3 ), more preferably between about 8 to about 25 lbs/ft 3 (128 to 400 kg/m 3 ) and most preferably from about 9 to about 20 lbs/ft 3 (144 to 320 kg/m 3 ).
- the formed base mat is then cut and converted into the acoustical panel through finishing operations well known by those having ordinary skill in the art.
- finishing operations include, among others, surface grinding, coating, perforating, fissuring, edge detailing and/or packaging.
- Perforating and fissuring contribute significantly to improving acoustical absorption value from the above-described base mats.
- Perforating operations provide multiple perforations on the surface of a base mat at a controlled depth and density (number of perforations per unit area). Perforating is carried out by pressing a plate equipped with a predetermined number of needles onto a base mat.
- Fissuring provides indentation of unique shapes onto the surface of a formed base mat with, for example, a roll equipped with a patterned metal plate. Both perforating and fissuring steps open the base mat surface and its internal structure, thereby allowing air to move in and out of the panel. Openings in the base mat also allow sound to enter and be absorbed by the base mat core.
- the acoustical panels are optionally laminated with a scrim or veil. It is also contemplated that the present acoustical panels can be manually cut with a utility knife.
- the present acoustical panels preferably have a bulk density between about 9 to about 32 lbs/ft 3 (144 to 513 kg/m 3 ), more preferably between about 10 to about 27 lbs/ft 3 (160 to 433 kg/m 3 ) and most preferably from about 11 to about 22 lbs/ft 3 (176 to 352 kg/m 3 ).
- the panels preferably have a thickness between about 0.2 inches to 1.5 inches (5 to 38 mm), more preferably between about 0.3 inches to 1.0 inch (8 to 25 mm) and most preferably from about 0.5 inches to about 0.75 inches (13 to 19 mm).
- Acoustical panels including at least one renewable component preferably achieve an NRC value of at least about 0.25 and a CAC value of at least about 25. Moreover, the acoustical panels achieve an eNRC value of least about 0.15. In addition, the acoustical panels achieve an MOR value of at least about 80 psi and a hardness value of at least about 100 Ibf, while achieving a maximum sag value in a 90% RH humidity chamber of 1.5 inch (38 mm). Still further, the acoustical panels achieve a flame spread index of less than about 25 and a smoke development index of less than about 50. The acoustical panels also have an STC of at least about 25.
- Rice hulls were obtained from Riceland Industries,
- Rice hulls were classified according to sieve sizes, with sieves of #6 mesh screen, #10 mesh screen (having an opening of 0.066 inches or 1.7 mm), #16 mesh screen (having an opening of 0.039 inches or 1 mm) and #30 mesh screen.
- the size distribution of the rice hull included about 18.3% retained on the #10 mesh screen, about 58.0% retained on the #16 mesh screen, about 20.1 % retained on the #30 mesh screen, while about 3.6% passed through the #30 mesh screen.
- the bulk density of the rice hull was about 8.51 lbs/ft 3 (136 kg/m 3 ).
- a slurry having about 4.5% consistency was formed by mixing water with panel ingredients and varying amounts of perlite and rice hulls as described in Table 1. With the water being constantly stirred, the ingredients were added in the following order: newsprint pulp, starch, calcium carbonate, ground rice hull, mineral wool and expanded perlite. The slurry was agitated for about 2 minutes. At the end of agitation, flocculent was added to the slurry in a concentration of about 0.1 % by weight of the slurry. The slurry was then poured into a forming box having the dimensions 14"x14"x30" (0.36 m x 0.36 m x 0.76 m).
- a fiberglass scrim supported by a metal grid allowed the slurry water to drain freely, while retaining most of the solids. Additional water was removed by applying a low pressure vacuum (1" Hg (25 mm Hg)) to the forming box. The wet base mat was then pressed to a constant wet thickness to remove additional water and also to consolidate the base mat structure. Finally, the wet base mat was further dewatered by applying a higher pressure vacuum (5-9" Hg (127 - 229 mmHg). The formed base mat was then dried in an oven or kiln at 315°C (600 0 F) for 30 minutes and 149°C (300°F) for 3 hours to remove remaining moisture.
- base mats having a higher percent by weight of rice hulls also have a lower airflow resistivity value, demonstrating that the base mats are more porous. Consequently, base mats including more rice hulls are more acoustically absorbent, which is reflected in the unperforated eNRC value.
- Example 2
- Rice hulls were obtained from Riceland Industries, Jonesborough, AR, where the rough rice was milled to separate the rice kernel from its hull.
- the rice hull was further ground with a Fritz mill equipped with a 0.109" (0.028 m) diameter perforated screen size.
- the rice hulls were ground until all of the materials passed through the screen. Additional rice hulls were ground and separated using screens with openings of 0.079" and 0.050" (0.002 m and 0.0013 m, respectively).
- the bulk densities of the above samples were about 14.62 lbs/ft 3 (234 kg/m 3 ), 16.31 lbs/ft 3 (261 kg/m 3 ) and 21.77 lbs/ft 3 (349 kg/m 3 ) for the screen openings of 0.109" (0.028 m), 0.079" (0.002 m) and 0.050" (0.0013 m), respectively.
- a slurry having about 4.5% consistency was formed by mixing water with panel ingredients and varying amounts of perlite and rice hulls as described in Table 2. With water being constantly stirred, the ingredients were added in the following order: newsprint pulp, starch, calcium carbonate, ground rice hull, mineral wool and expanded perlite. The slurry was agitated for about 2 minutes. At the end of agitation, flocculent in an amount about 0.1 % by weight was added to the slurry. The slurry was then poured into a forming box having the dimensions 14"x14"x30" (0.36 m x 0.36 m x 0.76 m).
- a fiberglass scrim supported by a metal grid allowed the slurry water to drain freely, while retaining most of the solids. Additional water was removed by applying a low pressure vacuum (1" Hg (25 mm)) to the forming box. The wet base mat was then pressed to a constant wet thickness to remove additional water and also to consolidate the base mat structure. Finally, the wet base mat was further dewatered by applying a higher pressure vacuum (5-9" Hg (127 - 229 mmHg). The formed base mat was then dried in an oven or kiln at 315°C (600 0 F) for 30 minutes and 149°C (300 0 F) for 3 hours to remove remaining moisture.
- base mats having rice hulls that were able to pass through larger screen openings are more acoustically absorbent, which is reflected in a higher eNRC value.
- Rice hulls were obtained from Rice Hull Specialties, Stuttgart, AR, where rice hulls from a rice milling plant were ground.
- the ground rice hulls were first sieved with a #20 mesh screen to remove larger particles, followed by sieving through a #80 mesh screen to remove smaller particles.
- the ground rice hulls that passed through the #20 mesh screen and were retained on the #80 mesh screen were used to make the base mats.
- the bulk density was about 22.96 lbs/ft 3 (368 kg/m 3 ).
- a slurry having about 4.5% consistency was formed by mixing water with panel ingredients and varying amounts of perlite and rice hulls as described in Table 3. With water being constantly stirred, the ingredients were added in the following order: newsprint pulp, starch, calcium carbonate, ground rice hull, mineral wool and expanded perlite. The slurry was agitated for about 2 minutes. At the end of agitation, about 0.1 % by weight of the slurry of flocculent was added to the slurry. The slurry was then poured into a forming box having the dimensions 14"x14"x30" (0.36 m x 0.36 m x 0.76 m).
- a fiberglass scrim supported by a metal grid allowed the slurry water to drain freely, while retaining most of the solids. Additional water was removed by applying a low pressure vacuum (1" Hg (25 mmHg)) to the forming box. The wet base mat was then pressed to a constant wet thickness to remove additional water and also to consolidate the base mat structure. Finally, the wet base mat was further dewatered by applying a higher pressure vacuum (5-9" Hg (127 - 229 mmHg). The formed base mat was then dried in an oven or kiln at 315°C (600 0 F) for 30 minutes and 149°C (300°F) for 3 hours to remove remaining moisture.
- Example 4 All three samples in the example were significantly more porous and acoustically more absorbent than the controls of test numbers 1 and 2 in Example 1.
- Example 4 All three samples in the example were significantly more porous and acoustically more absorbent than the controls of test numbers 1 and 2 in Example 1.
- Rice hulls were obtained from Rice Hull Specialties, Stuttgart, AR, where rice hulls from a rice milling plant were ground. The ground rice hulls were first sieved with a #30 mesh screen to remove larger particles, followed by sieving through a #80 mesh screen to remove smaller particles. The ground rice hulls that passed through the #30 mesh screen and were retained on the #80 mesh screen were used to make the base mats. The bulk density was about 28.56 lbs/ft 3 (457 kg/m 3 ). A slurry was prepared in a stock chest by mixing water with panel ingredients according to the composition of Table 4:
- Re-claimed acoustical panels are those panels that are defective, off-quality or ground finished products.
- the re-claimed acoustical panels may or may not be of the same composition.
- the consistency of the slurry was about 3.0%.
- a homogeneous slurry including the ingredients of Table 4 was transported to the head box, which provides a steady flow of slurry material.
- the slurry flowing out of the head box was then distributed on a foraminous wire to form a wet base mat.
- Water was first drained from the wire by gravity. Additional water was removed by applying a low vacuum pressure under the wire (4" Hg (100 mm Hg)). After pressing the base mats between two rollers, additional water was removed by applying a relatively high vacuum pressure under the wire (7-15" Hg (178 - 381 mmHg). The remaining water and moisture in the wet base mat was evaporated in a kiln.
- Table 6 shows the finished acoustical panel properties: Table 6
- Rice hulls were obtained from Rice Hull Specialties, Stuttgart, AR, where rice hulls from a rice milling plant were ground. The ground rice hulls were first sieved with a #20 mesh screen to remove large particles, followed by sieving through a #80 mesh screen to remove small particles. The ground rice hulls that passed through the #20 mesh screen and were retained on the #80 mesh screen were used to make the base mats. The bulk density was about 24.37 lbs/ft 3 (390 kg/m 3 ). A slurry was prepared in a stock chest by mixing water with panel ingredients approximately according to the composition of Table 7:
- the consistency of the slurry was about 3.0%.
- a homogeneous slurry including the ingredients of Table 7 was transported to head box, which provides a steady flow of slurry material. The slurry flowing out of the head box was then distributed on a foraminous wire to form a wet base mat. Water was first drained from the wire by gravity. Additional water was removed by applying a low vacuum pressure under the wire (1" Hg (25 mm Hg)). After pressing the base mats between two rollers, additional water was removed by applying a relatively high vacuum pressure under the wire (5-9" Hg (127 - 229 mm Hg). The remaining water and moisture in the wet base mat was evaporated in a kiln.
- Table 9 shows the finished acoustical panel properties:
- Buckwheat hulls were obtained from Zafu Store, Houston, TX.
- the buckwheat hull was further ground with a Fritz mill equipped with a 0.05" (1.27 mm) diameter perforated screen size.
- the buckwheat hulls were ground until all of the materials passed through the screen.
- the bulk density of the ground buckwheat hull was about 24.5 lbs/ft 3 (392 kg/m 3 ).
- the size distribution of the ground buckwheat hull was: 21.0% retained on the 20 mesh, 47.4% retained on the 30 mesh, 21.0% retained on the 40 mesh, and 5.6% retained on the 50 mesh, 2.8% retained on the 100 mesh, and 2.3% passed through 100 mesh.
- a slurry having about 4.5% consistency was formed by mixing water with panel ingredients and varying amounts of perlite and buckwheat hulls as described in Table 10. With water being constantly stirred, the ingredients were added in the following order: newsprint pulp, starch, calcium carbonate, ground buckwheat hull, mineral wool and expanded perlite. The slurry was agitated for about 2 minutes. At the end of agitation, about 0.1 % by weight of flocculent was added to the slurry. The slurry was then poured into a forming box having the dimensions 14"x14"x30" (0.36 m x 0.36 m x 0.76 m).
- a fiberglass scrim supported by a metal grid allowed the slurry water to drain freely, while retaining most of the solids. Additional water was removed by applying a low pressure vacuum (1" Hg (25 mm)) to the forming box. The wet base mat was then pressed to remove additional water and also to consolidate the base mat structure. Finally, the wet base mat was further dewatered by applying a higher pressure vacuum (5-9" Hg (127mmHg - 229mmHg)). The formed base mat was then dried in an oven or kiln at 315°C (600 0 F) for 30 minutes and 149°C (300 0 F) for 3 hours to remove the remaining moisture.
- base mats containing buckwheat hulls are more acoustically absorbent, which is indicated by a higher eNRC value than the control (test #1 ).
- a slurry having about 4.5% consistency was formed by mixing water with panel ingredients and varying amounts of perlite and wood shavings as described in Table 11. With water being constantly stirred, the ingredients were added in the following order: newsprint pulp, starch, calcium carbonate, ground wood shavings, mineral wool and expanded perlite. The slurry was agitated for about 2 minutes. At the end of agitation, about 0.1 % by weight of the slurry of flocculent was added to the slurry. The slurry was then poured into a forming box having the dimensions 14"x14"x30" (0.36 m x 0.36 m x 0.76 m).
- a fiberglass scrim supported by a metal grid allowed the slurry water to drain freely, while retaining most of the solids. Additional water was removed by applying a low pressure vacuum (1" Hg (25 mm)) to the forming box. The wet base mat was then pressed to a constant wet thickness to remove additional water and also to consolidate the base mat structure. Finally, the wet base mat was further dewatered by applying a higher pressure vacuum (5-9" Hg (127mmHg - 229mmHg)). The formed base mat was then dried in an oven or kiln at 315°C (600 0 F) for 30 minutes and 149°C (300 0 F) for 3 hours to remove remaining moisture.
- base mats containing ground wood shavings are more acoustically absorbent, which is indicated in a higher eNRC value than the control (test #1 ).
- the wheat straw was further ground with a Fritz mill equipped with a 0.050" (1.27 mm) diameter perforated screen size. The wheat straw was ground until most of the materials passed through the screen. The bulk density of the ground wheat straw was about 7.7 lbs/ft 3
- the size distribution of ground wheat straw was: 3.6% retained on 20 mesh, 25.3% retained on 30 mesh, 25.4% retained on 40 mesh, 19.8% retained on 50 mesh, 17.1 % retained on 100 mesh, and 8.9% passed through 100 mesh.
- a slurry having about 4.5% consistency was formed by
- a fiberglass scrim supported by a metal grid allowed the slurry water to drain freely, while retaining most of the solids. Additional water was removed by applying a low pressure vacuum (1" Hg (25 mm)) to the forming box. The wet base mat was then pressed to a constant wet thickness to remove additional water and also to consolidate the base mat structure. Finally, the wet base mat was further dewatered by applying a higher pressure vacuum (5-9" Hg (127mmHg - 229mmHg). The formed base mat was then dried in an oven or kiln at 315°C (600 0 F) for 30 minutes and 149°C (300 0 F) for 3 hours to remove remaining moisture.
- base mats containing ground wheat straw are more acoustically absorbent, which is indicated in a higher eNRC value than the control (test #1 ).
- Sawdust was obtained from ZEP, Carterville, GA., as a floor sweeping material.
- the bulk density of the sawdust was about 24.0 lbs/ft 3 (384 kg/m 3 ).
- the size distribution of the sawdust was: 9.0% retained on the 20 mesh, 24.3% retained on the 30 mesh, 22.7% retained on the 40 mesh, and 19.1 % retained on the 50 mesh, 21.4% retained on the 100 mesh, and 3.6% passed through 100 mesh.
- a slurry having about 4.5% consistency was formed by mixing water with panel ingredients and varying amounts of perlite and sawdust as described in Table 13. With water being constantly stirred, the ingredients were added in the following order: newsprint pulp, starch, calcium carbonate, sawdust, mineral wool and expanded perlite. The slurry was agitated for about 2 minutes. At the end of agitation, about 0.1 % by weight of flocculent was added to the slurry. The slurry was then poured into a forming box having the dimensions 14"x14"x30" (0.36 m x 0.36 m x 0.76 m).
- a fiberglass scrim supported by a metal grid allowed the slurry water to drain freely, while retaining most of the solids. Additional water was removed by applying a low pressure vacuum (1" Hg (25 mm)) to the forming box. The wet base mat was then pressed to remove additional water and also to consolidate the base mat structure. Finally, the wet base mat was further dewatered by applying a higher pressure vacuum (5-9" Hg (127mmHg -
- the formed base mat was then dried in an oven or kiln at 315°C (600 0 F) for 30 minutes and 149°C (300 0 F) for 3 hours to remove the remaining moisture.
- base mats containing sawdust are more acoustically absorbent, which is indicated by a higher eNRC value than the control (test #1 ).
- the bulk density of the ground corn cob was about 18.5 lbs/ft 3 (296 kg/m 3 ).
- the size distribution of the ground corn cobs was: 0.0% retained on the 20 mesh, 0.1 % retained on the 30 mesh, 1.6% retained on the 40 mesh, and 94.1 % retained on the 50 mesh, 4.1 %
- a slurry having about 4.5% consistency was formed by mixing water with panel ingredients and varying amounts of perlite and ground corn cobs as described in Table 14. With water being constantly stirred, the ingredients were added in the following order: newsprint pulp,
- the slurry was agitated for about 2 minutes. At the end of agitation, about 0.1 % by weight of flocculent was added to the slurry. The slurry was then poured into a forming box having the dimensions 14"x14"x30" (0.36 m x 0.36 m x 0.76 m).
- a fiberglass scrim supported by a metal grid allowed the slurry water to drain freely, while retaining most of the solids. Additional water was removed by applying a low pressure vacuum (1" Hg (25 mm)) to the forming box. The wet base mat was then pressed to remove additional water and also to consolidate the base mat structure. Finally, the wet base mat was further dewatered by applying a higher pressure vacuum (5-9" Hg (127mmHg -
- the formed base mat was then dried in an oven or kiln at 315°C (600 0 F) for 30 minutes and 149°C (300 0 F) for 3 hours to remove the remaining moisture.
- base mats containing ground corn cobs are acoustically more absorbent, which is indicated by a higher eNRC value than the control (test #1 ).
- the bulk density of the ground walnut shell was about 44.2 lbs/ft 3 (708 kg/m 3 ).
- the size distribution of the ground walnut shell was: 0.0% retained on the 20 mesh, 0.0% retained on the 30 mesh, 3.9% retained on the 40 mesh, and 72.5% retained on the 50 mesh, 23.2% retained on the 100 mesh, and 0.3% passed through 100 mesh.
- a slurry having about 4.5% consistency was formed by mixing water with panel ingredients and varying amounts of perlite and walnut shell as described in Table 15. With water being constantly stirred, the ingredients were added in the following order: newsprint pulp, starch, calcium carbonate, ground walnut shells, mineral wool and expanded perlite. The slurry was agitated for about 2 minutes. At the end of agitation, about 0.1 % by weight of flocculant was added to the slurry. The slurry was then poured into a forming box having the dimensions 14"x14"x30" (0.36 m x 0.36 m x 0.76 m).
- a fiberglass scrim supported by a metal grid allowed the slurry water to drain freely, while retaining most of the solids. Additional water was removed by applying a low pressure vacuum (1" Hg (25 mm)) to the forming box. The wet base mat was then pressed to remove additional water and also to consolidate the base mat structure. Finally, the wet base mat was further dewatered by applying a higher pressure vacuum (5-9" Hg (127mmHg - 229mmHg)). The formed base mat was then dried in an oven or kiln at 315°C (600 0 F) for 30 minutes and 149°C (300 0 F) for 3 hours to remove the remaining moisture.
- base mats containing ground walnut shells are acoustically more absorbent, which is indicated by a higher eNRC value than the control (test #1 ).
- Peanut Shells were obtained from a local grocery store. The peanut shells were further ground with a Fritz mill equipped with a 0.05" (1.27 mm) diameter perforated screen size. The peanut shells were ground until all of the materials passed through the screen. The bulk density of the ground peanut shells was 15.2 lbs/ft 3 (243 kg/m 3 ). The size distribution of the ground peanut shells was: 0.2% retained on the 20 mesh, 13.1 % retained on the 30 mesh, 31.5% retained on the 40 mesh, and 19.8% retained on the 50 mesh, 29.2% retained on the 100 mesh, and 6.1 % passed through 100 mesh. A slurry having about 4.5% consistency was formed by mixing water with panel ingredients and varying amounts of perlite and peanut shells as described in Table 16.
- the ingredients were added in the following order: newsprint pulp, starch, calcium carbonate, ground peanut shells, mineral wool and expanded perlite.
- the slurry was agitated for about 2 minutes. At the end of agitation, about 0.1 % by weight of flocculent was added to the slurry.
- the slurry was then poured into a forming box having the dimensions 14"x14"x30" (0.36 m x 0.36 m x 0.76 m).
- a fiberglass scrim supported by a metal grid allowed the slurry water to drain freely, while retaining most of the solids. Additional water was removed by applying a low pressure vacuum (1" Hg (25 mm)) to the forming box.
- the wet base mat was then pressed to remove additional water and also to consolidate the base mat structure. Finally, the wet base mat was further dewatered by applying a higher pressure vacuum (5-9" Hg (127mmHg - 229mmHg)). The formed base mat was then dried in an oven or kiln at 315°C (600 0 F) for 30 minutes and 149°C (300 0 F) for 3 hours to remove the remaining moisture.
- base mats containing ground peanut shells are acoustically more absorbent, which is indicated by a higher eNRC value than the control (test #1 ).
- Sunflower seed hulls were obtained from Archer Deniels Midland, ND.
- the bulk density of the ground sunflower seed hulls was about 12.4 lbs/ft 3 (199 kg/m 3 ).
- the size distribution of the ground sunflower seed hulls was: 0.1 % retained on the 20 mesh, 8.9% retained on the 30 mesh, 30.3% retained on the 40 mesh, and 29.3% retained on the 50 mesh, 23.9% retained on the 100 mesh, and 7.5% passed through 100 mesh.
- a slurry having about 4.5% consistency was formed by mixing water with panel ingredients and varying amounts of perlite and ground sunflower seed hulls as described in Table 17. With water being constantly stirred, the ingredients were added in the following order: newsprint pulp, starch, calcium carbonate, ground sunflower seed hulls, mineral wool and expanded perlite.
- the slurry was agitated for about 2 minutes. At the end of agitation, about 0.1 % by weight of flocculent was added to the slurry. The slurry was then poured into a forming box having the dimensions 14"x14"x30" (0.36 m x 0.36 m x 0.76 m).
- a fiberglass scrim supported by a metal grid allowed the slurry water to drain freely, while retaining most of the solids. Additional water was removed by applying a low pressure vacuum (1" Hg (25 mm)) to the forming box. The wet base mat was then pressed to remove additional water and also to consolidate the base mat structure. Finally, the wet base mat was further dewatered by applying a higher pressure vacuum (5-9" Hg (127mmHg -
- the formed base mat was then dried in an oven or kiln at 315°C (600 0 F) for 30 minutes and 149°C (300 0 F) for 3 hours to remove the remaining moisture.
- base mats containing ground sunflower seed hulls are acoustically more absorbent, which is indicated by a higher eNRC value than the control (test #1 ).
Landscapes
- Engineering & Computer Science (AREA)
- Physics & Mathematics (AREA)
- Architecture (AREA)
- Acoustics & Sound (AREA)
- Structural Engineering (AREA)
- Civil Engineering (AREA)
- Electromagnetism (AREA)
- Chemical & Material Sciences (AREA)
- Ceramic Engineering (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Inorganic Chemistry (AREA)
- Materials Engineering (AREA)
- Organic Chemistry (AREA)
- Building Environments (AREA)
- Laminated Bodies (AREA)
- Paper (AREA)
- Panels For Use In Building Construction (AREA)
- Dry Formation Of Fiberboard And The Like (AREA)
Priority Applications (8)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
EP09732899.1A EP2310588A4 (en) | 2008-04-18 | 2009-04-01 | RENEWABLE COMPONENTS CONTAINING PLATES AND MANUFACTURING METHOD |
BRPI0907357-4A BRPI0907357B1 (pt) | 2008-04-18 | 2009-04-01 | Painéis incluindo componentes ronováveis e métodos para fabricação |
CA2721574A CA2721574C (en) | 2008-04-18 | 2009-04-01 | Panels including renewable components and methods for manufacturing |
JP2011505074A JP5691097B2 (ja) | 2008-04-18 | 2009-04-01 | 再生可能成分を含むパネル、および製造方法 |
RU2010143122/03A RU2507349C2 (ru) | 2008-04-18 | 2009-04-01 | Панели, содержащие возобновляемые компоненты, и способ их изготовления |
CN2009801136519A CN102007255A (zh) | 2008-04-18 | 2009-04-01 | 包含可再生组分的板及其制造方法 |
MX2010011031A MX2010011031A (es) | 2008-04-18 | 2009-04-01 | Paneles que incluyen componentes renovables y metodos para su manufactura. |
ZA2010/07103A ZA201007103B (en) | 2008-04-18 | 2010-10-06 | Panels including renewable components and methods for manufacturing |
Applications Claiming Priority (4)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US12/106,077 US7935223B2 (en) | 2008-04-18 | 2008-04-18 | Panels including renewable components and methods for manufacturing |
US12/106,077 | 2008-04-18 | ||
US12/414,313 | 2009-03-30 | ||
US12/414,313 US8133357B2 (en) | 2008-04-18 | 2009-03-30 | Panels including renewable components and methods for manufacturing same |
Publications (2)
Publication Number | Publication Date |
---|---|
WO2009129051A2 true WO2009129051A2 (en) | 2009-10-22 |
WO2009129051A3 WO2009129051A3 (en) | 2009-12-17 |
Family
ID=43332969
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/US2009/039128 WO2009129051A2 (en) | 2008-04-18 | 2009-04-01 | Panels including renewable components and methods for manufacturing |
Country Status (13)
Country | Link |
---|---|
EP (1) | EP2310588A4 (ja) |
JP (1) | JP5691097B2 (ja) |
KR (1) | KR101633779B1 (ja) |
CN (2) | CN102007255A (ja) |
BR (1) | BRPI0907357B1 (ja) |
CA (1) | CA2721574C (ja) |
CO (1) | CO6311022A2 (ja) |
MX (1) | MX2010011031A (ja) |
MY (1) | MY157316A (ja) |
RU (1) | RU2507349C2 (ja) |
TW (1) | TWI460339B (ja) |
WO (1) | WO2009129051A2 (ja) |
ZA (1) | ZA201007103B (ja) |
Cited By (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
ES2344884A1 (es) * | 2010-04-07 | 2010-09-08 | Alejandro Barreras Perez | Procedimiento para la fabricacion de placas aislantes y placa aislante obtenida. |
US10173353B2 (en) | 2011-11-14 | 2019-01-08 | Spc Sunflower Plastic Compound Gmbh | Biocomposite and/or biomaterial with sunflower seed shells/husks |
US10399899B2 (en) | 2012-10-23 | 2019-09-03 | United States Gypsum Company | Pregelatinized starch with mid-range viscosity, and product, slurry and methods related thereto |
US10464847B2 (en) | 2012-10-23 | 2019-11-05 | United States Gypsum Company | Pregelatinized starch with mid-range viscosity, and product, slurry and methods related thereto |
US10875935B2 (en) | 2012-10-23 | 2020-12-29 | United States Gypsum Company | Method of preparing pregelatinized, partially hydrolyzed starch and related methods and products |
Families Citing this family (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN103103892B (zh) * | 2012-12-27 | 2015-05-13 | 山东轻工业学院 | 一种纳米TiO2吸音纸板的制备方法 |
CA3026440A1 (en) * | 2016-06-17 | 2017-12-21 | Armstrong World Industries, Inc. | Pelletization of recycled ceiling materials |
US10696594B2 (en) * | 2017-08-11 | 2020-06-30 | Usg Interiors, Llc | High noise reduction coefficient, low density acoustical tiles |
CN108687928A (zh) * | 2018-05-25 | 2018-10-23 | 柳州市林道科技有限公司 | 一种环保人造板及其制造工艺 |
CN110757917B (zh) * | 2019-11-08 | 2022-02-11 | 中南林业科技大学 | 一种桉木单板贴面木基复合板材及其制备方法 |
Family Cites Families (23)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US7004A (en) * | 1850-01-08 | Connecting ctjttees to shafts of boeing instetjments | ||
JPS5463514A (en) * | 1977-10-29 | 1979-05-22 | Hideo Fukuda | Sounddproof panel having composite front plate |
JPS5872441A (ja) * | 1981-10-28 | 1983-04-30 | 松下電工株式会社 | 吸音パネル |
CA1330291C (en) * | 1987-01-12 | 1994-06-21 | David Graham Izard | Low density frothed mineral wool panel and method |
EP0347810B1 (en) * | 1988-06-23 | 1993-03-10 | The Celotex Corporation | Acoustical mineral fiberboard and method of manufacturing same |
RU2034965C1 (ru) * | 1992-04-23 | 1995-05-10 | Масленников Борис Иванович | Теплозвукоизоляционная панель |
CN1024342C (zh) * | 1992-06-12 | 1994-04-27 | 山东建筑材料工业学院 | 一年生植物纤维水泥复合板的制备方法 |
KR960007958B1 (ko) * | 1993-12-10 | 1996-06-17 | 재단법인 한국전자통신연구소 | 신호망 관리 시스템의 루팅제원 관리 방법 |
US5558710A (en) * | 1994-08-08 | 1996-09-24 | Usg Interiors, Inc. | Gypsum/cellulosic fiber acoustical tile composition |
JP2815542B2 (ja) * | 1994-08-31 | 1998-10-27 | 三菱電機ホーム機器株式会社 | 多孔質構造体を用いた吸音機構 |
US5656129A (en) * | 1995-05-31 | 1997-08-12 | Masonite Corporation | Method of producing fibers from a straw and board products made therefrom |
ATE213040T1 (de) * | 1996-05-22 | 2002-02-15 | Erb Gottfried | Dämmaterial aus naturprodukten und herstellungsverfahren dafür |
US20020096278A1 (en) * | 2000-05-24 | 2002-07-25 | Armstrong World Industries, Inc. | Durable acoustical panel and method of making the same |
KR20020009249A (ko) * | 2000-07-25 | 2002-02-01 | 조송준 | 건축 내외장재용 조성물 및 그 제조방법 |
KR200238704Y1 (ko) * | 2001-01-04 | 2001-09-26 | (주)남산건설 | 코코넛 섬유 (Fiber)를 이용한 흡음재 |
JP5512062B2 (ja) * | 2001-04-03 | 2014-06-04 | アームストロング ワールド インダストリーズ インコーポレーテッド | 耐久性の多孔性物品およびその製造プロセス |
US20030134553A1 (en) * | 2002-01-14 | 2003-07-17 | L.S.I. (420) Import Export And Marketing Ltd. | Sound absorbing article |
DE10260922A1 (de) * | 2002-12-20 | 2004-07-15 | Schmidt, Axel H. | Dämpfungsmaterial und Grundstoff zu dessen Herstellung |
DE102004024251A1 (de) * | 2004-05-11 | 2005-12-08 | Igv Institut Für Getreideverarbeitung Gmbh | Verfahren und Anlage zur Herstellung von geformten Schaummaterialien auf der Basis von proteinhaltigen Bipolymeren |
DE102004056131B4 (de) * | 2004-11-16 | 2006-08-31 | Kronotec Ag | Schalldämmplatte |
US20070042658A1 (en) * | 2005-02-14 | 2007-02-22 | Hni Technologies Inc. | Fiber-containing article and method of manufacture |
CN200989028Y (zh) * | 2006-01-13 | 2007-12-12 | 张晓会 | 高效保温节能绿色多功能复合墙板 |
US7503430B2 (en) * | 2006-09-07 | 2009-03-17 | Usg Interiors, Inc. | Reduced dust acoustic panel |
-
2009
- 2009-04-01 CN CN2009801136519A patent/CN102007255A/zh active Pending
- 2009-04-01 JP JP2011505074A patent/JP5691097B2/ja not_active Expired - Fee Related
- 2009-04-01 MY MYPI2010004698A patent/MY157316A/en unknown
- 2009-04-01 RU RU2010143122/03A patent/RU2507349C2/ru not_active IP Right Cessation
- 2009-04-01 WO PCT/US2009/039128 patent/WO2009129051A2/en active Application Filing
- 2009-04-01 MX MX2010011031A patent/MX2010011031A/es active IP Right Grant
- 2009-04-01 KR KR1020107025828A patent/KR101633779B1/ko active IP Right Grant
- 2009-04-01 EP EP09732899.1A patent/EP2310588A4/en not_active Withdrawn
- 2009-04-01 BR BRPI0907357-4A patent/BRPI0907357B1/pt not_active IP Right Cessation
- 2009-04-01 CN CN201510532756.5A patent/CN105178462A/zh active Pending
- 2009-04-01 CA CA2721574A patent/CA2721574C/en not_active Expired - Fee Related
- 2009-04-13 TW TW098112160A patent/TWI460339B/zh not_active IP Right Cessation
-
2010
- 2010-10-06 ZA ZA2010/07103A patent/ZA201007103B/en unknown
- 2010-11-18 CO CO10144677A patent/CO6311022A2/es not_active Application Discontinuation
Non-Patent Citations (2)
Title |
---|
None |
See also references of EP2310588A4 |
Cited By (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
ES2344884A1 (es) * | 2010-04-07 | 2010-09-08 | Alejandro Barreras Perez | Procedimiento para la fabricacion de placas aislantes y placa aislante obtenida. |
US10173353B2 (en) | 2011-11-14 | 2019-01-08 | Spc Sunflower Plastic Compound Gmbh | Biocomposite and/or biomaterial with sunflower seed shells/husks |
US10919189B2 (en) | 2011-11-14 | 2021-02-16 | Spc Sunflower Plastic Compound Gmbh | Biocomposite and/or biomaterial with sunflower seed shells/husks |
US10399899B2 (en) | 2012-10-23 | 2019-09-03 | United States Gypsum Company | Pregelatinized starch with mid-range viscosity, and product, slurry and methods related thereto |
US10464847B2 (en) | 2012-10-23 | 2019-11-05 | United States Gypsum Company | Pregelatinized starch with mid-range viscosity, and product, slurry and methods related thereto |
US10875935B2 (en) | 2012-10-23 | 2020-12-29 | United States Gypsum Company | Method of preparing pregelatinized, partially hydrolyzed starch and related methods and products |
US11135818B2 (en) | 2012-10-23 | 2021-10-05 | United States Gypsum Company | Pregelatinized starch with mid-range viscosity, and product, slurry and methods related thereto |
US11168030B2 (en) | 2012-10-23 | 2021-11-09 | United States Gypsum Company | Pregelatinized starch with mid-range viscosity, and product, slurry and methods related thereto |
Also Published As
Publication number | Publication date |
---|---|
BRPI0907357B1 (pt) | 2019-04-09 |
KR20110021785A (ko) | 2011-03-04 |
RU2507349C2 (ru) | 2014-02-20 |
CO6311022A2 (es) | 2011-08-22 |
MX2010011031A (es) | 2010-11-05 |
JP5691097B2 (ja) | 2015-04-01 |
CN102007255A (zh) | 2011-04-06 |
KR101633779B1 (ko) | 2016-06-27 |
JP2011518266A (ja) | 2011-06-23 |
EP2310588A2 (en) | 2011-04-20 |
CA2721574A1 (en) | 2009-10-22 |
BRPI0907357A2 (pt) | 2015-10-13 |
CN105178462A (zh) | 2015-12-23 |
WO2009129051A3 (en) | 2009-12-17 |
EP2310588A4 (en) | 2014-10-29 |
CA2721574C (en) | 2018-05-01 |
ZA201007103B (en) | 2011-07-27 |
MY157316A (en) | 2016-05-31 |
TW201006992A (en) | 2010-02-16 |
RU2010143122A (ru) | 2012-05-27 |
TWI460339B (zh) | 2014-11-11 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
CA2757316C (en) | Panels including renewable components and methods for manufacturing same | |
US7935223B2 (en) | Panels including renewable components and methods for manufacturing | |
CA2721574C (en) | Panels including renewable components and methods for manufacturing | |
CN107949550B (zh) | 吸声天花板砖 | |
JP7297218B2 (ja) | 高ノイズ低減係数、低密度音響タイル |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
WWE | Wipo information: entry into national phase |
Ref document number: 200980113651.9 Country of ref document: CN |
|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 09732899 Country of ref document: EP Kind code of ref document: A2 |
|
WWE | Wipo information: entry into national phase |
Ref document number: MX/A/2010/011031 Country of ref document: MX |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2011505074 Country of ref document: JP Ref document number: 2721574 Country of ref document: CA |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2009732899 Country of ref document: EP |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2432/MUMNP/2010 Country of ref document: IN |
|
ENP | Entry into the national phase |
Ref document number: 20107025828 Country of ref document: KR Kind code of ref document: A |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2010143122 Country of ref document: RU Ref document number: 10144677 Country of ref document: CO |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
ENP | Entry into the national phase |
Ref document number: PI0907357 Country of ref document: BR Kind code of ref document: A2 Effective date: 20101018 |