WO2009081543A1 - 積層シート及びその製造方法 - Google Patents

積層シート及びその製造方法 Download PDF

Info

Publication number
WO2009081543A1
WO2009081543A1 PCT/JP2008/003805 JP2008003805W WO2009081543A1 WO 2009081543 A1 WO2009081543 A1 WO 2009081543A1 JP 2008003805 W JP2008003805 W JP 2008003805W WO 2009081543 A1 WO2009081543 A1 WO 2009081543A1
Authority
WO
WIPO (PCT)
Prior art keywords
sheet
release sheet
adhesive layer
base material
product
Prior art date
Application number
PCT/JP2008/003805
Other languages
English (en)
French (fr)
Inventor
Masahiko Kawano
Original Assignee
Mitsubishi Plastics, Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mitsubishi Plastics, Inc. filed Critical Mitsubishi Plastics, Inc.
Publication of WO2009081543A1 publication Critical patent/WO2009081543A1/ja

Abstract

　本発明は、打ち抜き及びハーフカットをする長さを極力短くしつつ、巻圧による痕や傷などの発生を防止した積層シートを提供する。 　本発明の積層シート１は、長尺の剥離シート２上に粘着層３と基材４とからなる所定形状の製品部５を剥離シートの長さ方向に適宜間隔で複数形成した構成を備え、剥離シート２の幅方向両端部側に、賦型加工して製品部５の厚みよりも高さのある保護部６を表面側又は裏面側に形成したことを特徴とする。

Description

積層シート及びその製造方法
　本発明は、長尺の剥離シート上に粘着層及び基材からなる製品部を積層した積層シート及びその製造方法に関する。
　従来、光ディスクには、受光面を保護するためカバーシートを設けてあることがある。
　このようなカバーシートは、例えば、剥離シート上に適宜間隔で複数作成した積層シートの状態で提供される。この積層シートは、ロール状に巻き取られていくため、巻圧によりカバーシートに痕がついたり、粘着層の粘着剤がはみ出してカバーシートに汚れが付着したりすることがあった。また、巻取り時に異物等が挟み込まれ、カバーシートに押し痕や傷などが発生したりするなどの問題があった。
　近年、開発されてきたブルーレイディスクでは、このような痕や傷などがあると、データの読み書きに支障が生じるおそれがある。
　そこで、巻き取りした際、粘着剤をはみ出させず、カバーシートに痕や傷などが付かなくするため、下記特許文献１～３に示すように、ハーフカットにより縁部を残したり、縁部にテープ状の保護材を貼り付けたりした積層シートや、特許文献４に示すように、ハーフカットにより縁部を***させた積層シートや、特許文献５に示すように、剥離シートの縁部を折り返した積層シートなどが開発されている。
特開２００４－３５８３６号公報 特開２００４－９５０１３号公報 特開２００５－２１６４４０号公報 特開２００６－２２４５８１号公報 特開２００７－１２２３０号公報
　積層シートに、打ち抜き又はハーフカットを施すことは、打ち抜きカスが発生するおそれがある。特に、基材にＵＶ硬化樹脂を設けた積層シートに打ち抜き又はハーフカットを施す場合はカスが発生しやすく、このカスがカバーシートに付着して汚したり、傷つけたりするおそれがある。
　上記特許文献１～４に記載の積層シートは、カバーシートを切り抜く以外にも縁部を残すため、或いは縁部に***部を設けるためにハーフカットを施すので、カスが発生しやすいものである。
　また、上記特許文献１に記載の積層シートは、縁部にテープ状の保護材を設けものも開示されているが、別部材を付加する必要があるため、経済的観点から好ましくなく、上記特許文献５に記載の積層シートは、縁部を折り返すため、必要とする剥離シートの面積が広くなり、これも経済的観点から好ましくない。
　また、これらに使用する剥離シートは、カバーシート剥離後、巻き取られて廃棄処分とされる。この際、資源の再利用化の観点より、剥離シートと別材料となる縁部を残したり、保護材を付加することは、再利用を困難にさせる為、好ましくない。
　そこで、本発明の目的は、打ち抜き及びハーフカットをする長さを極力短くしつつ、巻圧による痕や傷などの発生を防止した積層シート及びその製造方法を提供することにある。
　本発明は、下記（１）～（７）の構成を採用するものである。
（１）長尺の剥離シート上に粘着層と基材とからなる所定形状の製品部を剥離シートの長さ方向に適宜間隔で複数形成した構成を備えた積層シートであって、剥離シートの幅方向両端部側に賦型加工して製品部の厚みよりも高さのある保護部を表面側又は裏面側に形成した積層シート。
（２）保護部は、凹凸が連続する凹凸構造とした（１）に記載の積層シート。
（３）保護部は、超音波溶着装置により設けた（１）又は（２）に記載の積層シート。
（４）長尺の剥離シート上に粘着層を介して基材を積層し、基材及び粘着層にハーフカットして製品部を形成し、基材及び粘着層の製品部以外の部分である不要部を剥離除去した後、剥離シートの幅方向両端部側に賦型加工して製品部の厚みよりも高さのある保護部を表面側又は裏面側に形成する積層シートの製造方法。
（５）長尺の剥離シート上に粘着層を介して基材を積層し、剥離シートの幅方向中間付近を円形状に打ち抜くとともに、基材及び粘着層に打ち抜き部分と同心円状にハーフカットして製品部を剥離シートの長さ方向に適宜間隔で複数形成し、基材及び粘着層の製品部以外の部分である不要部を剥離除去した後、剥離シートの幅方向両端部側に賦型加工して製品部の厚みよりも高さのある保護部を表面側又は裏面側に形成する積層シートの製造方法。
（６）保護部は、凹凸が連続する凹凸構造とした（４）又は（５）に記載の積層シートの製造方法。
（７）保護部は、超音波溶着装置により設けた（４）～（６）のいずれかに記載の積層シートの製造方法。
　なお、本発明でいう「保護部の高さ」は、保護部を剥離シートの表面側に形成した場合は剥離シートの表面からの高さをいい、保護部を剥離シートの裏面側に形成した場合は剥離シートの裏面からの高さをいう。
　本発明の積層シートは、剥離シートの幅方向両端部側に賦型により製品部の厚みを超える高さの保護部を形成してあり、巻取りした際、保護部が巻圧を受けるので、製品部に痕や傷などが付くことを防止することができ、また、従来のように、他部材を用いることや剥離シートの面積を広くせずとも製品部に痕や傷などが付くことを防止でき、経済的観点から好ましいものである。
　また、本発明の積層シートの製造方法は、製品部となる部分のみをハーフカット或いは打ち抜きするので、カスが発生するおそれが少なく、カスにより傷がついたり、汚れたりするおそれが少ないものである。
本発明の積層シートの一実施形態を示した概略斜視図である。 図１の積層シートの横断面図である。 本発明の積層シートの他の実施形態を示した横断面図である。 本発明の積層シートの他の実施形態を示した概略斜視図である。 本発明の積層シートの製造方法の一例を示した図である。
　以下、本発明を実施形態に基づいて説明するが、本発明の範囲が下記実施形態に限定されるものではない。
　図１は本発明の一実施形態の積層シートを模式的に示した概略斜視図であり、図２は図１の積層シートの横断面図である。
　本発明の一実施形態の積層シート１は、図１又は２に示すように、長尺の剥離シート２上に、粘着層３及び基材４からなる円盤状の製品部５を剥離シート２の長さ方向に適宜間隔で複数形成してあり、剥離シート２の幅方向両端部側に、表面側に***する保護部６を賦型加工して形成してあるものである。
　なお、本実施形態では、製品部５をブルーレイディスクなどの光学ディスクに用いる円盤状のカバーシートとしてあるが、これに限定するものではなく、種々の形状とすることができる
（剥離シート２）
　剥離シート２としては、熱可塑性樹脂フィルムを使用することができ、例えば、ポリエチレンテレフタレートフィルム、ポリエステルフィルム、ポリプロピレンフィルムなどの樹脂フィルムを用いることができる。
　これら樹脂フィルム表面には、シリコン系などの剥離剤を塗布し、剥離処理してあるのが好ましい。なかでも、ポリエチレンテレフタレートフィルムの表面にシリコン系剥離剤を塗布したものが好ましい。
　剥離シート２の厚みは、３８μｍ～２００μｍ、特に５０μｍ～１００μｍとするのが好ましい。
（粘着層３）
　粘着層３は、粘着剤又は接着剤から形成することができ、この粘着剤又は接着剤としては、例えば、アクリル系、ゴム系、シリコン系、ウレタン系、ポリエステル系などを用いることができる。なかでも、アクリル系粘着剤を用いるのが好ましい。
　粘着層３の厚みは、製品部５を積層する被積層体によるが、５μｍ～５０μｍ、特に１０μｍ～３０μｍとするのが好ましい。
（基材４）
　基材４は、例えば、ポリエチレンテレフタレート、ポリカーボネート、ポリスチレン、ポリエチレン、ポリプロピレン、塩化ビニル、ポリイミド、ウレタンアクリレートとエポキシアクリレートを主成分とするＵＶ硬化樹脂などからなる樹脂フィルム又はこれらの積層体を用いることができる。なかでも、ウレタンアクリレートとエポキシアクリレートを主成分とするＵＶ硬化樹脂が好ましい。
　基材４の厚みは、用途にもよるが、２５μｍ～２５０μｍ、特に５０μｍ～１００μｍとするのが好ましい。
（保護部６）
　保護部６は、剥離シート２の幅方向両端部側に、剥離シート２の長さ方向に凹凸の連続する凹凸構造として形成してある。保護部６の高さは、製品部５の厚みを超えるように形成してあり、製品部５の厚みよりも２０μｍ～５０μｍ高く形成するのが好ましい。保護部６の幅は、１０ｍｍ～４ｍｍ、特に８ｍｍ～６ｍｍとするのが好ましい。
　保護部６は、プレス装置や超音波溶着装置などで賦型加工して形成することができる。なかでも、超音波溶着装置を用いるのが好ましく、これにより、剥離シート２に適宜高さの賦型を施すことが容易にできる。
　なお、超音波溶着装置とは、剥離シート２を工具ホーンと呼ばれる振動部の超音波振動により溶融させ、工具ホーン自体の形状や工具ホーンと相対する加圧部の形状により任意の形状に加工するものである。
　中でも加圧部にローラー状の加工部を用いるタイプ（一般に超音波ミシンと呼ばれている）のものは、剥離シート２を連続的に送りながら、賦型加工することができるため、より好適である。
　超音波ミシンは具体的には、株式会社プロコ製ＰＵＳ－２１５０などがある。
　図１又は２に示した実施形態では、保護部６は、剥離シート２の表面側に***させているが、図３に示すように、裏面側に***させた保護部６ａとすることができる。この際、保護部６ａの高さは、製品部５の厚みよりも２０μｍ～５０μｍ高く形成するのが好ましい。
　図１又は２に示した実施形態では、保護部６を、略矩形状の凸部を適宜間隔で***させて形成してあるが、これに限定するものではなく、略円状の凸部を適宜間隔で***させて形成することや凸部が連なるように***させて形成することもできる。また、保護部６を、剥離シート２の片側端部に一列形成してあるが、図４に示すように、直線状に配して形成し、その内側にも、製品部５の外周に沿うように円弧状に配して形成した二列の保護部６ｂとすることもできる。
（製造方法）
　以下、積層シート１の製造方法の一例を説明する。
　長尺の剥離シート２の片面に粘着剤又は接着剤を塗布して粘着層３を形成する。この塗布は、リップコーターで行うのが好ましい。形成した粘着層３上に基材４を積層する。この際、圧着しながら積層するのが好ましい。
　この積層体の基材４側から、図５（ａ）に示すように、剥離シート２の幅方向中間付近を所定の間隔で円形状に打ち抜くとともに基材４及び粘着層３をハーフカットして打ち抜き部分と同心円状の切れ込みを形成し、円盤状の製品部５を形成する。
　次に、図５（ｂ）に示すように、基材４及び粘着層３の製品部５部分以外の不要部８を剥離除去する。
　そして、図５（ｃ）に示すように、剥離シート２の幅方向両端部側に、賦型加工して保護部６を形成し、積層シート１を製造することができる。
　保護部６は、前述したとおり、プレス装置や超音波溶着装置などで賦型加工して形成することができ、なかでも、超音波溶着装置を用いるのが好ましい。
　超音波溶着装置を用いた際は、例えば、２０ｋＨｚの超音波を発信させ、２～２０ｍ／ｍｉｎ、好ましくは５～１５ｍ／ｍｉｎの速さで賦型加工をするのが好ましい。
　この積層シート１は、剥離シート２に製品部５の厚みを越える高さの保護部６を賦型してあるため、ロール状に巻取りしても、製品部５が圧迫されることがないので、製品部５に痕や傷が付いたり、粘着剤がはみ出したりすることがない。
　また、上記製造方法は、ハーフカット或いは打ち抜くのは製品部５の箇所のみなので、カスが出にくく、製品部５を汚すおそれが少ない。
　以下、実施例を示すが、本発明の範囲が下記実施例に限定されるものではない。
（実施例１）
　ポリエチレンテレフタレートフィルムの片面にシリコン系剥離剤を塗布した剥離シート（厚さ：７５μｍ）の剥離処理面上に、アクリル系粘着剤をリップコーターにより塗布してＤＲＹ厚２０μｍの粘着層を形成した。
　粘着層に、ウレタンアクリレートとエポキシアクリレートを主成分とするＵＶ硬化樹脂からなる厚さ８０μｍの基材を圧着し、幅１５０ｍｍ、長さ１５０ｍの積層体を作製した。
　次に、連続打抜き装置（富士商工マシナリー株式会社製：UDP-3000）を用いて、積層体の幅方向中間付近を円形状に打ち抜くとともに、基材及び粘着層をハーフカットして円形状に切れ込みを入れ、外径１２０ｍｍ、内径２３ｍｍの円盤状の製品部を一定間隔で複数形成した後、製品部以外の部分の不要部を剥離除去した。
　続いて、工具ホーン回転式超音波溶着装置（別名：超音波ミシン、株式会社プロコ製：PUS-2150）を用いて、剥離シートの幅方向両端部側に、連続して送りながらローラーにより、速度９ｍ／ｍｉｎ、加圧０．１５ＭＰａ、出力５００Ｗの条件で連続凹凸賦型を行い、保護部を形成して積層シートを形成した。
　この積層シートを、直径６インチのプラスチック製巻芯に巻取り、ロール巻取体とした。
　このロール巻取体を１週間放置し、製品部に痕、傷、汚れなどが付いていないかを目視で確認したところ、そのようなものは見られなかった。

Claims (7)

  1. 　長尺の剥離シート上に粘着層と基材とからなる所定形状の製品部を剥離シートの長さ方向に適宜間隔で複数形成した構成を備えた積層シートであって、剥離シートの幅方向両端部側に、賦型加工して製品部の厚みよりも高さのある保護部を表面側又は裏面側に形成した積層シート。
  2. 　保護部は、凹凸が連続する凹凸構造とした請求項１に記載の積層シート。
  3. 　保護部は、超音波溶着装置により設けた請求項１又は２に記載の積層シート。
  4. 　長尺の剥離シート上に粘着層を介して基材を積層し、基材及び粘着層をハーフカットして製品部を形成し、基材及び粘着層の製品部以外の部分である不要部を剥離除去した後、剥離シートの幅方向両端部側に、賦型加工して製品部の厚みよりも高さのある保護部を表面側又は裏面側に形成する積層シートの製造方法。
  5. 　長尺の剥離シート上に粘着層を介して基材を積層し、剥離シートの幅方向中間付近を円形状に打ち抜くとともに基材及び粘着層を打ち抜き部分と同心円状にハーフカットして製品部を剥離シートの長さ方向に適宜間隔で複数形成し、基材及び粘着層の製品部以外の部分である不要部を剥離除去した後、剥離シートの幅方向両端部側に賦型加工して製品部の厚みよりも高さのある保護部を表面側又は裏面側に形成する積層シートの製造方法。
  6. 　保護部は、凹凸が連続する凹凸構造とした請求項４又は５に記載の積層シートの製造方法。
  7. 　保護部は、超音波溶着装置により設けた請求項４～６のいずれかに記載の積層シートの製造方法。

     
PCT/JP2008/003805 2007-12-25 2008-12-17 積層シート及びその製造方法 WO2009081543A1 (ja)