WO2007082498A1 - Verfahren zur beschichtung eines hartmetall- oder cermetsubstratkörpers und beschichteter hartmetall- oder cermetkörper - Google Patents
Verfahren zur beschichtung eines hartmetall- oder cermetsubstratkörpers und beschichteter hartmetall- oder cermetkörper Download PDFInfo
- Publication number
- WO2007082498A1 WO2007082498A1 PCT/DE2006/001943 DE2006001943W WO2007082498A1 WO 2007082498 A1 WO2007082498 A1 WO 2007082498A1 DE 2006001943 W DE2006001943 W DE 2006001943W WO 2007082498 A1 WO2007082498 A1 WO 2007082498A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- substrate body
- coating
- cermet
- pvd
- blasting agent
- Prior art date
Abstract
Description
Claims