WO2007063995A1 - 記録材料および印刷物の製造方法 - Google Patents
記録材料および印刷物の製造方法 Download PDFInfo
- Publication number
- WO2007063995A1 WO2007063995A1 PCT/JP2006/324116 JP2006324116W WO2007063995A1 WO 2007063995 A1 WO2007063995 A1 WO 2007063995A1 JP 2006324116 W JP2006324116 W JP 2006324116W WO 2007063995 A1 WO2007063995 A1 WO 2007063995A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- recording material
- ink receiving
- plastic layer
- layer
- receiving layer
- Prior art date
Abstract
Description
Claims