WO2006106701A1 - Mg含有チタン酸リチウムからなるリチウムイオン電池用活物質及びリチウムイオン電池 - Google Patents
Mg含有チタン酸リチウムからなるリチウムイオン電池用活物質及びリチウムイオン電池 Download PDFInfo
- Publication number
- WO2006106701A1 WO2006106701A1 PCT/JP2006/306390 JP2006306390W WO2006106701A1 WO 2006106701 A1 WO2006106701 A1 WO 2006106701A1 JP 2006306390 W JP2006306390 W JP 2006306390W WO 2006106701 A1 WO2006106701 A1 WO 2006106701A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- active material
- ion battery
- lithium ion
- lithium
- negative electrode
- Prior art date
Abstract
Description
Claims