WO2006010736A1 - Kühlmittelleitung - Google Patents
Kühlmittelleitung Download PDFInfo
- Publication number
- WO2006010736A1 WO2006010736A1 PCT/EP2005/053547 EP2005053547W WO2006010736A1 WO 2006010736 A1 WO2006010736 A1 WO 2006010736A1 EP 2005053547 W EP2005053547 W EP 2005053547W WO 2006010736 A1 WO2006010736 A1 WO 2006010736A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- coolant line
- layer
- line according
- inner layer
- polypropylene
- Prior art date
Abstract
Description
Claims