WO2006001340A1 - 両面研磨用キャリアおよびその製造方法 - Google Patents
両面研磨用キャリアおよびその製造方法 Download PDFInfo
- Publication number
- WO2006001340A1 WO2006001340A1 PCT/JP2005/011548 JP2005011548W WO2006001340A1 WO 2006001340 A1 WO2006001340 A1 WO 2006001340A1 JP 2005011548 W JP2005011548 W JP 2005011548W WO 2006001340 A1 WO2006001340 A1 WO 2006001340A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- double
- carrier
- side polishing
- polishing
- base material
- Prior art date
Abstract
Description
Claims