WO2005118499A1 - ディスプレイ装置用基板ガラス - Google Patents
ディスプレイ装置用基板ガラス Download PDFInfo
- Publication number
- WO2005118499A1 WO2005118499A1 PCT/JP2005/009355 JP2005009355W WO2005118499A1 WO 2005118499 A1 WO2005118499 A1 WO 2005118499A1 JP 2005009355 W JP2005009355 W JP 2005009355W WO 2005118499 A1 WO2005118499 A1 WO 2005118499A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- glass
- substrate glass
- panel display
- strain point
- display device
- Prior art date
Abstract
Description
Claims