WO2003064085A1 - Element d'outil de coupe revetu a couche de revetement dure et procede de formation de la couche de revetement dure sur l'outil de coupe - Google Patents
Element d'outil de coupe revetu a couche de revetement dure et procede de formation de la couche de revetement dure sur l'outil de coupe Download PDFInfo
- Publication number
- WO2003064085A1 WO2003064085A1 PCT/JP2003/000903 JP0300903W WO03064085A1 WO 2003064085 A1 WO2003064085 A1 WO 2003064085A1 JP 0300903 W JP0300903 W JP 0300903W WO 03064085 A1 WO03064085 A1 WO 03064085A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- component
- content point
- point
- hard coating
- coating layer
- Prior art date
Description
Claims