WO2002098819A1 - Procede de production d'un materiau composite au carbure de silicium sic renforce de fibres sic - Google Patents
Procede de production d'un materiau composite au carbure de silicium sic renforce de fibres sic Download PDFInfo
- Publication number
- WO2002098819A1 WO2002098819A1 PCT/JP2001/009365 JP0109365W WO02098819A1 WO 2002098819 A1 WO2002098819 A1 WO 2002098819A1 JP 0109365 W JP0109365 W JP 0109365W WO 02098819 A1 WO02098819 A1 WO 02098819A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- sic
- sic fiber
- composite material
- fiber
- slurry
- Prior art date
Description
Claims