WO2002047616A2 - Prothese dentaire entierement ceramique comportant une structure en oxyde de zircon a stabilisation cerique - Google Patents
Prothese dentaire entierement ceramique comportant une structure en oxyde de zircon a stabilisation cerique Download PDFInfo
- Publication number
- WO2002047616A2 WO2002047616A2 PCT/EP2001/014502 EP0114502W WO0247616A2 WO 2002047616 A2 WO2002047616 A2 WO 2002047616A2 EP 0114502 W EP0114502 W EP 0114502W WO 0247616 A2 WO0247616 A2 WO 0247616A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- framework
- zro
- weight
- proportion
- infiltration
- Prior art date
Abstract
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
AU2002219170A AU2002219170A1 (en) | 2000-12-11 | 2001-12-11 | Fully ceramic tooth replacement with a frame made of cer-stabilised zircon oxide |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
DE10061630.5 | 2000-12-11 | ||
DE10061630A DE10061630B4 (de) | 2000-12-11 | 2000-12-11 | Vollkeramischer Zahnersatz mit einem Gerüst aus einem Cerstabillisierten Zirkonoxid |
Publications (2)
Publication Number | Publication Date |
---|---|
WO2002047616A2 true WO2002047616A2 (fr) | 2002-06-20 |
WO2002047616A3 WO2002047616A3 (fr) | 2002-09-19 |
Family
ID=7666673
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/EP2001/014502 WO2002047616A2 (fr) | 2000-12-11 | 2001-12-11 | Prothese dentaire entierement ceramique comportant une structure en oxyde de zircon a stabilisation cerique |
Country Status (3)
Country | Link |
---|---|
AU (1) | AU2002219170A1 (fr) |
DE (1) | DE10061630B4 (fr) |
WO (1) | WO2002047616A2 (fr) |
Cited By (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2003035014A1 (fr) * | 2001-10-25 | 2003-05-01 | Vita Zahnfabrik H. Rauter Gmbh & Co. Kg | Systeme pour produire une ceramique de recouvrement |
WO2008040780A1 (fr) * | 2006-10-05 | 2008-04-10 | Vita Zahnfabrik H. Rauter Gmbh & Co. Kg | Procédé de fabrication d'une pièce moulée en céramique |
WO2008106958A2 (fr) * | 2007-03-06 | 2008-09-12 | Hermsdorfer Institut Für Technische Keramik E.V. | Céramique pour incrustations vestibulaires pour des restaurations dentaires en dioxyde de zirconium stabilisé à l'yttrium et procédé de fixation d'incrustations vestibulaires sur des restaurations dentaires en dioxyde de zirconium stabilisé à l'yttrium |
CN108395246A (zh) * | 2018-05-15 | 2018-08-14 | 钱兴 | 一种高韧性口腔用纳米瓷粉材料的制备方法 |
US10214443B2 (en) | 2005-02-08 | 2019-02-26 | Ivoclar Vivadent Ag | Lithium silicate materials |
Families Citing this family (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20050164045A1 (en) | 2004-01-27 | 2005-07-28 | Ivoclar Vivadent Ag | Method for the production of an oxide ceramic shaped part and a part produced by such method |
DE102004021424A1 (de) * | 2004-04-30 | 2005-11-24 | Institut für Neue Materialien Gemeinnützige GmbH | Füge- oder Abdichtelement aus einem glasinfiltrierten Keramik- oder Metallkomposit und Verfahren zu seiner Anwendung |
EP1972320A1 (fr) | 2007-03-22 | 2008-09-24 | Vita Zahnfabrik H. Rauter GmbH & Co. KG | Verre d'infiltration contenant du niobium |
DE102010028693A1 (de) | 2010-05-06 | 2011-11-10 | Sirona Dental Systems Gmbh | Verfahren zur Herstellung eines Zahnersatzteils und Zahnersatzteil |
Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE4020893A1 (de) * | 1989-06-30 | 1991-01-03 | Hoya Corp | Verfahren zur herstellung eines anorganischen, biologisch vertraeglichen materials |
EP0690031A1 (fr) * | 1994-07-01 | 1996-01-03 | Ivoclar Ag | Vitrocéramiques contenant Zro2 |
US5695337A (en) * | 1994-10-05 | 1997-12-09 | Tyszblat Sadoun; Michele | Process for producing a dental prosthesis secured on an implant and an intermediate piece useable for implementing this process |
Family Cites Families (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP0240643A1 (fr) * | 1986-04-11 | 1987-10-14 | Tyszblat Sadoun, Michèle | Procédé de fabrication de prothèses dentaires |
JPH05306141A (ja) * | 1991-03-07 | 1993-11-19 | Hoya Corp | ガラスセラミックス及びそれを用いた人工歯冠 |
US5775912A (en) * | 1996-08-16 | 1998-07-07 | American Thermocraft Corporation | Method of producing a dental restoration using CAD/CAM |
-
2000
- 2000-12-11 DE DE10061630A patent/DE10061630B4/de not_active Expired - Fee Related
-
2001
- 2001-12-11 AU AU2002219170A patent/AU2002219170A1/en not_active Abandoned
- 2001-12-11 WO PCT/EP2001/014502 patent/WO2002047616A2/fr not_active Application Discontinuation
Patent Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE4020893A1 (de) * | 1989-06-30 | 1991-01-03 | Hoya Corp | Verfahren zur herstellung eines anorganischen, biologisch vertraeglichen materials |
EP0690031A1 (fr) * | 1994-07-01 | 1996-01-03 | Ivoclar Ag | Vitrocéramiques contenant Zro2 |
US5695337A (en) * | 1994-10-05 | 1997-12-09 | Tyszblat Sadoun; Michele | Process for producing a dental prosthesis secured on an implant and an intermediate piece useable for implementing this process |
Cited By (12)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2003035014A1 (fr) * | 2001-10-25 | 2003-05-01 | Vita Zahnfabrik H. Rauter Gmbh & Co. Kg | Systeme pour produire une ceramique de recouvrement |
US10214443B2 (en) | 2005-02-08 | 2019-02-26 | Ivoclar Vivadent Ag | Lithium silicate materials |
US10981823B2 (en) | 2005-02-08 | 2021-04-20 | Ivoclar Vivadent Ag | Lithium silicate materials |
WO2008040780A1 (fr) * | 2006-10-05 | 2008-04-10 | Vita Zahnfabrik H. Rauter Gmbh & Co. Kg | Procédé de fabrication d'une pièce moulée en céramique |
US8168113B2 (en) | 2006-10-05 | 2012-05-01 | Vita Zahnfabrik H. Rauter Gmbh & Co. Kg | Method for the production of a ceramic molded part |
WO2008106958A2 (fr) * | 2007-03-06 | 2008-09-12 | Hermsdorfer Institut Für Technische Keramik E.V. | Céramique pour incrustations vestibulaires pour des restaurations dentaires en dioxyde de zirconium stabilisé à l'yttrium et procédé de fixation d'incrustations vestibulaires sur des restaurations dentaires en dioxyde de zirconium stabilisé à l'yttrium |
WO2008106958A3 (fr) * | 2007-03-06 | 2009-11-05 | Hermsdorfer Institut Für Technische Keramik E.V. | Céramique pour incrustations vestibulaires pour des restaurations dentaires en dioxyde de zirconium stabilisé à l'yttrium et procédé de fixation d'incrustations vestibulaires sur des restaurations dentaires en dioxyde de zirconium stabilisé à l'yttrium |
JP2010519986A (ja) * | 2007-03-06 | 2010-06-10 | イフォクレール ヴィヴァデント アクチェンゲゼルシャフト | イットリウム安定化二酸化ジルコニウム製歯科修復物用ベニアセラミック、およびイットリウム安定化二酸化ジルコニウム製歯科修復物のベニア形成方法 |
US8592330B2 (en) | 2007-03-06 | 2013-11-26 | Ivoclar Vivadent Ag | Veneer ceramic for dental restorations and method for veneering dental restorations |
US8987153B2 (en) | 2007-03-06 | 2015-03-24 | Ivoclar Vivadent Ag | Veneer ceramic for dental restorations and method for veneering dental restorations |
US9359245B2 (en) | 2007-03-06 | 2016-06-07 | Ivoclar Vivadent Ag | Veneer ceramic for dental restorations and method for veneering dental restorations |
CN108395246A (zh) * | 2018-05-15 | 2018-08-14 | 钱兴 | 一种高韧性口腔用纳米瓷粉材料的制备方法 |
Also Published As
Publication number | Publication date |
---|---|
AU2002219170A1 (en) | 2002-06-24 |
WO2002047616A3 (fr) | 2002-09-19 |
DE10061630B4 (de) | 2004-02-12 |
DE10061630A1 (de) | 2002-06-27 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
EP2885259B1 (fr) | Matériau composite à base d'oxyde de zirconium | |
EP3558671B1 (fr) | L'utilisation de corps multicouche en céramique oxydée présentant un comportement au frittage adapté | |
DE60303964T2 (de) | Verstärkte keramikrestauration | |
EP2956427B1 (fr) | Matériaux polyphases à base d'oxyde de zirconium | |
EP2287122B1 (fr) | Vitrocéramique de phosphosilicate | |
EP3453686A1 (fr) | Vitroceramique et verre au lithium-silice ayant une teneur en zro2 | |
WO2013167723A1 (fr) | Ébauche préfrittée à usage dentaire | |
DE102015122861A1 (de) | Verfahren zur Herstellung eines Rohlings, Rohling sowie eine dentale Restauration | |
EP1568667A2 (fr) | Compositions de vitrocéramiques dentaires compressibles et renforcées | |
WO2002047616A2 (fr) | Prothese dentaire entierement ceramique comportant une structure en oxyde de zircon a stabilisation cerique | |
DE19610300C2 (de) | Hochfeste transluzente Glimmer-Glaskeramiken, Verfahren zu ihrer Herstellung und Verwendung | |
EP1167311B1 (fr) | Vitrocéramique en apatite à basse température de frittage | |
EP3366260A1 (fr) | Procédé de fabrication d'une prothèse dentaire | |
EP2146678B1 (fr) | Verre d'infiltration contenant du niobium | |
EP2045218B1 (fr) | Glaçure destinée au revêtement de surfaces | |
WO2003035014A1 (fr) | Systeme pour produire une ceramique de recouvrement | |
EP1959912B1 (fr) | Alliage dentaire et son utilisation | |
DE102020103720A1 (de) | Verwendung eines Rohlings mit Halter zur Herstellung von dentalen Restaurationen | |
JP2008006268A (ja) | 歯科用セラミックス焼結体およびその製造方法 | |
DD245360B1 (de) | Dentalmaterial fuer kuenstlichen zahnersatz und verfahren zur seiner herstellung | |
DD235557A1 (de) | Opakermasse fuer eine duenne keramikverblendschale |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AK | Designated states |
Kind code of ref document: A2 Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NO NZ OM PH PL PT RO RU SD SE SG SI SK SL TJ TM TN TR TT TZ UA UG US UZ VN YU ZA ZM ZW |
|
AL | Designated countries for regional patents |
Kind code of ref document: A2 Designated state(s): GH GM KE LS MW MZ SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG |
|
AK | Designated states |
Kind code of ref document: A3 Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NO NZ OM PH PL PT RO RU SD SE SG SI SK SL TJ TM TN TR TT TZ UA UG US UZ VN YU ZA ZM ZW |
|
AL | Designated countries for regional patents |
Kind code of ref document: A3 Designated state(s): GH GM KE LS MW MZ SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG |
|
121 | Ep: the epo has been informed by wipo that ep was designated in this application | ||
DFPE | Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101) | ||
REG | Reference to national code |
Ref country code: DE Ref legal event code: 8642 |
|
122 | Ep: pct application non-entry in european phase | ||
NENP | Non-entry into the national phase |
Ref country code: JP |
|
WWW | Wipo information: withdrawn in national office |
Country of ref document: JP |