WO2001038024A1 - Procede de production de poudre fine de nickel metallique comprenant des particules spheriques fines - Google Patents
Procede de production de poudre fine de nickel metallique comprenant des particules spheriques fines Download PDFInfo
- Publication number
- WO2001038024A1 WO2001038024A1 PCT/JP2000/007986 JP0007986W WO0138024A1 WO 2001038024 A1 WO2001038024 A1 WO 2001038024A1 JP 0007986 W JP0007986 W JP 0007986W WO 0138024 A1 WO0138024 A1 WO 0138024A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- nickel
- slurry
- nickel oxide
- carbonate
- particles
- Prior art date
Description
Claims