WO2000066646A2 - Oil-free oxidatively curable polyester compositions - Google Patents
Oil-free oxidatively curable polyester compositions Download PDFInfo
- Publication number
- WO2000066646A2 WO2000066646A2 PCT/US2000/012044 US0012044W WO0066646A2 WO 2000066646 A2 WO2000066646 A2 WO 2000066646A2 US 0012044 W US0012044 W US 0012044W WO 0066646 A2 WO0066646 A2 WO 0066646A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- oxidatively curable
- amount
- present
- weight
- oxidatively
- Prior art date
Abstract
Description
Claims