WO1999041322A1 - Matiere de revetement pour former une pellicule photocatalytique hydrophile, procede de fabrication d'une pellicule photocatalytique hydrophile, et element photocatalytique hydrophile - Google Patents

Matiere de revetement pour former une pellicule photocatalytique hydrophile, procede de fabrication d'une pellicule photocatalytique hydrophile, et element photocatalytique hydrophile Download PDF

Info

Publication number
WO1999041322A1
WO1999041322A1 PCT/JP1999/000582 JP9900582W WO9941322A1 WO 1999041322 A1 WO1999041322 A1 WO 1999041322A1 JP 9900582 W JP9900582 W JP 9900582W WO 9941322 A1 WO9941322 A1 WO 9941322A1
Authority
WO
WIPO (PCT)
Prior art keywords
coating agent
precursor
group
titania
acid
Prior art date
Application number
PCT/JP1999/000582
Other languages
English (en)
Japanese (ja)
Inventor
Eiichi Kojima
Original Assignee
Toto Ltd.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Toto Ltd. filed Critical Toto Ltd.
Priority to AU25465/99A priority Critical patent/AU2546599A/en
Publication of WO1999041322A1 publication Critical patent/WO1999041322A1/fr

Abstract

L'invention concerne une matière de revêtement capable de former une pellicule photocatalytique hydrophile avec une ténacité, une dureté, une transparence, et une transmittance de la lumière visible satisfaisantes, cette pellicule présentant en outre l'avantage de rester hydrophile même cachée de la lumière. Cette matière de revêtement renferme un précurseur de titane amorphe, un oxyde de titane cristallin, et un précurseur capable d'être converti en un composé pourvu d'une liaison siloxane.
PCT/JP1999/000582 1998-02-10 1999-02-10 Matiere de revetement pour former une pellicule photocatalytique hydrophile, procede de fabrication d'une pellicule photocatalytique hydrophile, et element photocatalytique hydrophile WO1999041322A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
AU25465/99A AU2546599A (en) 1998-02-10 1999-02-10 Coating material for forming photocatalytic hydrophilic film, method of forming photocatalytic hydrophilic film, and photocatalytic hydrophilic member

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP4452998 1998-02-10
JP10/44529 1998-02-10

Publications (1)

Publication Number Publication Date
WO1999041322A1 true WO1999041322A1 (fr) 1999-08-19

Family

ID=12694052

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP1999/000582 WO1999041322A1 (fr) 1998-02-10 1999-02-10 Matiere de revetement pour former une pellicule photocatalytique hydrophile, procede de fabrication d'une pellicule photocatalytique hydrophile, et element photocatalytique hydrophile

Country Status (2)

Country Link
AU (1) AU2546599A (fr)
WO (1) WO1999041322A1 (fr)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2004018579A1 (fr) * 2002-08-21 2004-03-04 Jsr Corporation Composition de revetement
WO2004096935A1 (fr) * 2003-04-30 2004-11-11 Ube Nitto Kasei Co., Ltd. Liquide de revetement photocatalytique, pellicule photocatalytique et element photocatalytique
JP2005336334A (ja) * 2004-05-27 2005-12-08 Ube Nitto Kasei Co Ltd 非晶質酸化チタン複合塗膜形成用コーティング組成物、それを用いた塗膜およびその用途
WO2007131474A1 (fr) 2006-05-17 2007-11-22 Nano-X Gmbh Matériau de revêtement

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH09227831A (ja) * 1995-12-22 1997-09-02 Toto Ltd 光触媒性親水性コ−ティング組成物
JPH09227829A (ja) * 1995-12-22 1997-09-02 Toto Ltd 光触媒性親水性コーティング組成物、親水性被膜の形成方法および被覆物品
JPH10183062A (ja) * 1996-10-30 1998-07-07 Jsr Corp コーティング用組成物
JPH10195379A (ja) * 1997-01-08 1998-07-28 Toto Ltd 光触媒性親水性コ−ティング液
JPH10279886A (ja) * 1997-02-06 1998-10-20 Shin Etsu Chem Co Ltd コーティング組成物、親水性膜、及び親水性膜を有する被覆物品
JPH1161652A (ja) * 1997-08-07 1999-03-05 Jsr Corp 繊 維

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH09227831A (ja) * 1995-12-22 1997-09-02 Toto Ltd 光触媒性親水性コ−ティング組成物
JPH09227829A (ja) * 1995-12-22 1997-09-02 Toto Ltd 光触媒性親水性コーティング組成物、親水性被膜の形成方法および被覆物品
JPH10183062A (ja) * 1996-10-30 1998-07-07 Jsr Corp コーティング用組成物
JPH10195379A (ja) * 1997-01-08 1998-07-28 Toto Ltd 光触媒性親水性コ−ティング液
JPH10279886A (ja) * 1997-02-06 1998-10-20 Shin Etsu Chem Co Ltd コーティング組成物、親水性膜、及び親水性膜を有する被覆物品
JPH1161652A (ja) * 1997-08-07 1999-03-05 Jsr Corp 繊 維

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2004018579A1 (fr) * 2002-08-21 2004-03-04 Jsr Corporation Composition de revetement
CN100376646C (zh) * 2002-08-21 2008-03-26 捷时雅株式会社 涂料组合物
WO2004096935A1 (fr) * 2003-04-30 2004-11-11 Ube Nitto Kasei Co., Ltd. Liquide de revetement photocatalytique, pellicule photocatalytique et element photocatalytique
JPWO2004096935A1 (ja) * 2003-04-30 2006-07-13 宇部日東化成株式会社 光触媒塗工液、光触媒膜および光触媒部材
CN100381527C (zh) * 2003-04-30 2008-04-16 宇部日东化成株式会社 光催化剂涂布液、光催化剂膜和光催化剂构件
JP2005336334A (ja) * 2004-05-27 2005-12-08 Ube Nitto Kasei Co Ltd 非晶質酸化チタン複合塗膜形成用コーティング組成物、それを用いた塗膜およびその用途
WO2007131474A1 (fr) 2006-05-17 2007-11-22 Nano-X Gmbh Matériau de revêtement

Also Published As

Publication number Publication date
AU2546599A (en) 1999-08-30

Similar Documents

Publication Publication Date Title
JP3077199B2 (ja) 光触媒性親水性コーテイング組成物
JP3303696B2 (ja) 光触媒性親水性コ−ティング組成物
WO2000018504A1 (fr) Article photocatalyseur, article protege contre l'encrassement et le voilement, et procede de production d'un article protege contre l'encrassement et le voilement
WO1997045502A1 (fr) Element anti-encrassement et composition pour revetement anti-encrassement
JP5761346B2 (ja) 無機親水性コート液、それから得られる親水性被膜及びこれを用いた部材
JPH10231146A (ja) 防曇防汚ガラス物品
KR20150028979A (ko) 코팅 조성물 및 그의 용도
EP2749608B1 (fr) Revêtements antireflets ayant des propriétés autonettoyantes, substrats comprenant de tels revêtements et procédés associés
WO1998055573A1 (fr) Procede de traitement prealable de surface avant formation d'une pellicule hydrophile photocatalytique, detergent et composition de sous-couche mis en application dans ce procede
JP3797037B2 (ja) 光触媒性親水性コーティング組成物
JP4665221B2 (ja) 二酸化チタン光触媒担持体とその製造方法
WO2001068786A1 (fr) Element hydrophile et son procede de fabrication
JPH11309379A (ja) 光触媒性親水性部材、及び光触媒性親水性コ−ティング組成物
JP2002346393A (ja) 光触媒体およびその製造方法
JP2006131917A (ja) 光触媒性親水性コーティング組成物
JPH11228865A (ja) 光触媒性親水被膜形成用のコ−ティング剤および光触媒性親水部材
WO1999041322A1 (fr) Matiere de revetement pour former une pellicule photocatalytique hydrophile, procede de fabrication d'une pellicule photocatalytique hydrophile, et element photocatalytique hydrophile
JPH11181339A (ja) 親水性コ−ティング組成物
JP2002320917A (ja) 光触媒性塗膜の製造方法、および光触媒性部材
JPH11100526A (ja) 光触媒性親水性部材、及び光触媒性親水性コ−ティング組成物
JP2000086933A (ja) 光触媒性親水性部材、及び、光触媒性親水性コ−ティング組成物
JP2002356650A (ja) 光触媒性塗膜形成組成物およびそれを成膜した光触媒性部材
JP2000144057A (ja) コーティング組成物
JP2006136758A (ja) 光触媒組成物、および光触媒部材
JP2004154779A (ja) 光触媒皮膜を塗布した基材および光触媒皮膜を基材上に形成する方法

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AL AM AT AU AZ BA BB BG BR BY CA CH CN CU CZ DE DK EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MD MG MK MN MW MX NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT UA UG US UZ VN YU ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GH GM KE LS MW SD SZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE BF BJ CF CG CI CM GA GN GW ML MR NE SN TD TG

DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
121 Ep: the epo has been informed by wipo that ep was designated in this application
REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

WWE Wipo information: entry into national phase

Ref document number: 09634826

Country of ref document: US

NENP Non-entry into the national phase

Ref country code: KR

122 Ep: pct application non-entry in european phase