WO1996020828A1 - Feuille metallique revetue de resine, d'une grande nettete d'image et dont le revetement presente une grande adhesivite apres travail - Google Patents

Feuille metallique revetue de resine, d'une grande nettete d'image et dont le revetement presente une grande adhesivite apres travail Download PDF

Info

Publication number
WO1996020828A1
WO1996020828A1 PCT/JP1995/002639 JP9502639W WO9620828A1 WO 1996020828 A1 WO1996020828 A1 WO 1996020828A1 JP 9502639 W JP9502639 W JP 9502639W WO 9620828 A1 WO9620828 A1 WO 9620828A1
Authority
WO
WIPO (PCT)
Prior art keywords
resin
layer
metal plate
coated
coated metal
Prior art date
Application number
PCT/JP1995/002639
Other languages
English (en)
French (fr)
Inventor
Yoshiyuki Sugimoto
Takashi Minamigi
Tetsuo Nakamoto
Original Assignee
Toyo Kohan Co., Ltd.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Toyo Kohan Co., Ltd. filed Critical Toyo Kohan Co., Ltd.
Priority to CA002209137A priority Critical patent/CA2209137C/en
Priority to AU43151/96A priority patent/AU694600B2/en
Priority to EP95941850A priority patent/EP0816063B1/en
Priority to JP52083896A priority patent/JP3691068B2/ja
Priority to DE69526680T priority patent/DE69526680T2/de
Priority to US08/860,526 priority patent/US6235399B1/en
Publication of WO1996020828A1 publication Critical patent/WO1996020828A1/ja

Description

明 細 害 加工密着性に優れた高鲜映性樹脂被覆金属板 技術分野
本発明は、 優れた鲜映性を有する樹脂被覆金属板に関し、 特に張り出し加工、 深絞り加工等の厳し t、加工にお L、ても被 δ樹脂層の剥離を生じず、 かつ加工密着 性に優れた高鲜映性樹脂被覆金属板に関する。 背景技術
近年、 家電機器、 音饗機器、 厨房器具、 内装建材などの高級化に伴い、 意匠の 高級化が追求されている。 意匠の高級化は材料表面の意匠性とりわけ高鲜映性で 表現するとともに、 更に張出し加工、 深絞り加工等の加工形状により表現するこ とができる。 そのため、 張出し加工、 深絞り加工等の成形加工密着性に優れた高 鲜映性化粧鋼板の要求が高まってきた。
これらの要求に応えるため、 種々研究が為され、 特開平 2 - 5 5 1 2 6号公報 にあるように、 5〜 1 0 0 mの熱可塑性あるいは熱硬化性樹脂の透明フィルム と、 鉛筆硬度が H〜 7 Bの熱可塑性樹脂 （5〜5 0 ^ m) を、 着色された金属板 に積層する方法が提案されている。
この方法では、 鲜映性は得られるが、 張出し加工、 絞り加工等の厳しい加工を 行うと、 積層される樹脂の構成層界面又は積層される樹脂と着色された金属板と の界面での剥讎を生ずるため、 加工形状が限定されている。
即ち、 従来技術では、 張出し加工、 絞り加工等の加工性に優れ、 かつ鲜映性を 併せ持った積層金属板を得ることが極めて困難であった。
本発明の課題は、 前記従来技術上の問題点に鑑み、 張出し加工、 絞り加工等の 加工密着性に優れ、 かつ鲜映性に優れた樹脂被覆金属板を提供することにある。 発明の開示
本発明の樹脂被覆金属板は、 金属板を基板とし、 少なくとも基板の片面に、 基 板側から順次、 塗料層、 5〜： I 0 0 m厚の変性ォレフィン樹脂層、 柄または Z およびベタ印刷層、 接着剤層、 5〜1 0 0 ;u m厚の透明ポリエステル系樹脂フィ ルムが積層されている。
また、 本発明の樹脂被現金厲板は、 金属板を基板とし、 少なくとも基板の片面 に、 基板側から順次、 塗料層、 柄または Zおよびベタ印刷層、 5〜 1 0 0 m厚 の変性ォレフィン樹脂層、 接着剤層、 5〜 1 0 0 m厚の透明ポリエステル系樹 脂フィルムが積層されている。
さらに、 本発明の樹脂被覆金属板は、 金属板を基板とし、 少なくとも基板の片 面に、 基板側から順次、 塗料層、 5〜1 0 O i^ mの変性ォレフィン樹脂層、 接着 剤層、 5〜1 0 0 厚の透明ポリエステル系樹脂フィルムが積層されている。 これらの樹脂被覆金属板は、 透明ポリエステル系樹脂フィルムの上層に塗料層が 形成されていることが好ましい。 そして、 上記樹脂被覆金属板は、 接着剤層中や 印刷層中には、 アルミニウム顔料や雲母顔料が混入されていることが望ましい。 作用
積層された樹脂の中間に設けられた変性ォレフィン樹脂層が、 印刷層、 塗料層 、 ポリエステル系樹脂フィルムなどとの接着性に優れるため、 深絞り等の厳しい 加工によっても、 構成層 （樹脂層） 界面での剥離が生ぜず、 優れた加工密着性を 示す。 また、 金属板の表面粗さや各構成層 （樹脂層） の凸凹を、 変性ォレフィン 樹脂層が吸収するので、 樹脂被覆金属板として優れた鲜映性を得ることができる ο
さらに、 最外層である透明ポリエステル系樹脂フィルムの上層に塗料層 （いわ ゆるトップコ一ト） が形成されているので、 樹脂被覆金属板を成形加工するとき や取扱い時の傷付き性が改善される。 図面の簡単な説明
図 1〜図 3は、 この発明に係る樹脂被覆金属板の片面側の構成を示す断面図で める。 発明を実施するための最良の形態
以下、 本発明の実施例について詳細に説明する。
図 1〜 3は、 樹脂被覆層を設けた場合の樹脂被覆金属板の片面側の構成を示す。 本発明の樹脂被覆金属板は、 金属板の両側に樹脂被覆層力、'設けられていてもよい し、 片面のみに設けられていてもよい。
以下、 金属板の片側に樹脂被覆層が設けられている場合を例にとって説明する 。 図 1は、 請求項 1の発明に対応し、 Aは透明ポリエステル系樹脂フィルム、 B は接着剤層、 Cは柄または Zおよびベタ印刷層、 Dは変性ォレフィン樹脂層、 E は塗料層、 1 0は金属板である。
図 1において、 Aは厚み 5〜1 0 0〃mの透明ポリエステル系樹脂フィルムで あり、 樹脂被覆金属板の最外層を構成している。
好ましい下限厚みは 1 5 mであり、 好ましい上限厚みは 8 0 /i mである。 樹脂フィルムの厚みが 5 m未満の場合は、 樹脂被覆金属板全体としての鲜映性 に劣り、 しかもフィルム被覆時のフィルム取り扱いが困難である。 1 0 0 / ΙΏを 超えると樹脂被覆金属板の加工密着性が劣る。
樹脂被覆金属板を成形加工するときや取扱い時の傷付き性を改善するために、 最外層である透明ポリエステル系樹脂フィルム Aの上層にシリコン系、 フッ素系 、 アクリル系、 メラミン系またはウレタン系の焼き付型あるいは紫外線照射型塗 料層 （いわゆるトップコ一ト） を 0. 2〜5 0 m形成させることが好ましい。 さらに好ましい下限厚みは 0 . 5〃mであり、 好ましい上限厚みは 3 0 mであ る。 0 . 2 m未満であると干渉色が目立ち、 耐傷付き性も劣る。 一方 5 0 /z m を超えると加工性が低下し経済性にも劣る。 透明性ポリエステル系樹脂フィルム Aには、 ポリエチレンテレフタート樹脂お よびその共重合体が含まれる。
Bは接着剤層であり、 ポリエステル系、 ェポキン系、 アクリル系、 メラミン系 またはウレタン系等の樹脂を含む。
また、 上記樹脂の他、 ァーグリシドキシプロピル · トリメ トキシシラン （例え ば日本ュニカー社製シランカップリング剤） などの接着効果を有する接着助剤を 使用することもできる。 上記接着剤層の厚みは、 0, l〜50^m形成するが好 ましい。 さらに好ましい下限厚みは 0. 5 /mであり、 好ましい上限厚みは 30 ； t mである。 接着剤層の厚みが 0. 1 t m未満であると、 耐沸水性、 加工密着性 に劣る。 一方 50 /zmを超えると、 接着剤に含まれる残留溶剤の影饗で加熱時に 表面外観が悪くなる。 このため鲜映性が劣ることとなる。
接着剤層には、 アルミニゥム金厲粉末ある L、は雲母粉末などの顔料を混入させ ることもできる。
この場合、 アルミニウム顔料の混入割合は、 接着剤の固形分に対して重量比で 約 0. 1〜30%で好適である。 さらに望ましい下限は 1 %、 上限は 20%であ る。 混入割合が 0. 1未満では金属光沢がでず、 30%を超えると接着剤層がも ろくなり鲜映性も劣るからである。
アルミニウム顔料の粒子の形状は、 球状 ·鱗片状があるが、 その大きさは両者 とも平均粒径で 0. 1〜10 のものが好適である。 さらに望ましい下限は 1 m、 上限は 80 である。 平均粒径が 0. 1 m未満では意匠性が悪く、 100 ^zmを超えると鲜映性が劣ることとなるからである。
雪母顔料の混入割合は、 接着剤の固形分に対して重量比で約 0. 1〜 30 %で 好適である。 さらに望ましい下限は 1%、 上限は 20%である。 混入割合が 0. 1未満では金属光沢がでず、 30 %を超えると接着剤層がもろくなるからである o
雲母顔料の粒子の形状は、 球状 ·鱗片状があるが、 その大きさは両者とも平均粒 径で 0 . 1〜 1 0 0 /z mのものが好適である。 さらに望ましい下限は 1 u m、 上 限は 8 0 mである。 平均粒径が 0. 1未満では意匠性が悪く、 1 0 0 を超 えると鲜映性が劣ることとなるからである。
次に、 Cは意匠性を付与するために形成される柄印刷層あるいはベタ印刷層で あり、 その両者を含む場合もある。 これらの両印刷層を構成する樹脂としては、 ポリエステル系、 ェポキン系、 アクリル系、 メラミン系またはウレタン系等の樹 脂を含むが、 ポリエステル系樹脂を用いると加工密着性が極めて優れるのでより 好ましい。
その厚みは、 柄印刷層の場合は、 l〜5 w m形成するが好ましく、 未満 であると印刷柄が明瞭にでず、 5 mを超えると溶剤が残留し、 鲜映性にばらつ きを生ずるからである。
ベタ印刷層の場合は、 l〜5 w m形成するのが好ましい。 1 m未満であると 色調にばらつきを生じ、 5 mを超えると溶剤が残留し、 鲜映性にばらつきを生 ずるからである。 また経済的でない。
印刷層には、 アルミニウム顔料や雲母顔料を混入させることもできる。 この場 合、 顔料の混入割合は、 上記接着剤層において述べた場合と同様である。
Dは、 厚み 5〜 1 0 0 mを示す変性ォレフィン樹脂層であり、 本発明の優れ た加工密着性と高鲜映性を付与するために主要な構成要素である。
変性ォレフィン樹脂は、 カルボキシル基を分子内に有するポリプロピレン共重 合体とポリプロピレンとを次の割合で混合することにより製造する。
ポリプロピレン共重合体： 1 0 0〜2 0 (重量部）
ポリプロピレン： 1 0 0〜0 (重量部）
変性ォレフィン樹脂層の好ましい下限厚みは 1 0 mであり、 好ましい上限厚 みは 8 0 mである。 さらに好ましい下限厚みは 2 0 mであり、 さらに好まし い上限厚みは 7 0 t/ mである。 変性ォレフィン樹脂層の厚みが、 5 未満にな ると被覆金属板全体としての鲜映性が低下し、 1 0 O mを超えると被覆金属板 全体としての表面硬度や加工密着性が低下する。
変性ォレフィン樹脂としては、 水酸基、 加水分解性基、 カルボキシル基、 およ び酸無水基から選ばれる少なくとも 1種の官能基を分子内に有するォレフィン重 合体、 もしくはォレフィン重合体と他のポリオレフィン重合体の混合物などが含 まれる。
変性ォレフィン樹脂層中には、 1種または 2種以上の顔料を含んでいてもさし つかえない。
なお、 変性ォレフィン樹脂層の上層または下層 （あるいは両層） に、 シラン力 ックリング剤等でアンカー処理を施すことも、 積層樹脂間の接着力を向上させる ために好ましい。
上記、 透明ポリエステル系樹脂フィルム A、 接着剤層 B、 印刷層 Cおよび変性 ォレフィン樹脂層 Dを総称して被覆樹脂フイルムという。
図 1の Eは、 金属板の上に直接形成される意匠としての着色層を構成する塗料 層である。 塗料用樹脂としては、 ポリエステル系、 ァクリノレ系、 ウレタン系、 ェ ポキン系またはメラミン樹脂を主成分とするものを含むが、 特にポリエステル系 樹脂を主成分とすると、 加工密着性が極めて優れたものとなるので好ましい。 塗 料層の厚みは、 1〜5 0〃mが好適であり、 さらに望ましくは 5〜3 0 i mであ る。
また、 塗料層 Eは 2層以上で構成されるものを含む。 即ち、 基板の耐食性を向上 するために、 防锖顔料を含む下塗り層を持つ複層として形成されたものを含む。 例えば下地に塗る 1層が着色塗料で、 その上に塗る 2層めはクリァ一塗料でもよ い。
図 1の 1 0は、 基板としての金属板である。 金属板には、 スチール板ゃステン レス鋼板などの鋼板をはじめとして、 亜鉛めつき網板、 複合亜鉛めつき鋼板、 二 ッケルめっき鋼板、 ティンフリースチールなどの表面処理鋼板を含む。 また、 ァ ルミ二ゥム板や銅板などの非鉄金属板なども含む。 厚みは 0. 2 mn！〜 1 . 2 m mのものが好ましい。
金属板の片側のみに樹脂を被覆する場合には、 金属板の下層 （樹脂被覆をしな い側） には、 防锖塗料層を 0 . 1〜5 0 m形成させるのが好適であり、 さらに 塩化ビニルフィルムなどを被覆するのも防鐯上好ましい。 塗料用樹脂としては、 ポリエステル系、 アクリル系、 ウレタン系、 ェポキン系またはメラミン樹脂を主 成分とするものが好適である。
図 2は、 請求項 3の発明に対応し、 Aは透明ポリエステル系樹脂フィルム、 B は接着剤層、 Cは柄またはノおよびベタ印刷層、 Dは変性ォレフィン樹脂層、 E は塗料層、 1 0は金属板である。 図 1で説明した被覆樹脂の構成層との位置関係 において、 柄または/およびベタ印刷層 Cと、 変性ォレフィン樹脂層 Dとが入れ 替わった構成となっている。
すなわち請求項 3の被覆金属板は、 印刷層 Cが、 塗料層 Eと変性ォレフィン樹 脂層 Dとの間に形成されている。 この場合、 変性ォレフィン樹脂層 Dは、 下層に 形成されている印刷層 Cの意匠性を活かすために透明なものを用い、 印刷層 Cに 形成された模様を外部より見えるようにする。
図 3は、 請求項 4の発明に対応し、 Aは透明ポリエステル系樹脂フィルム、 B は接着剤層、 Cは変性ォレフィン樹脂層、 Dは塗料層、 1 0は金属板である。 図 2の構成層との位置関係において、 印刷層 Cがな 、構成となっている。
この場合、 塗料層 Dの外観が透明ポリエステル系樹脂フィルム Aの上部より観察 できる。
(製造方法）
( 1 ) 塗装鋼板の作成
電気亜鈴めつき鋼板等の表面にロールコートによる塗装を 1回あるいは 2回塗り する。 また塗料層を厚くしたい場合は、 さらに塗り回数を増やす。
( 2 ) 被覆樹脂フィルムの作成
図 1に示した （請求項 2記載） 被覆樹脂フィルムの作成を例にとって説明する。 まず、 ポリエステル系樹脂フィルム上に、 接着剤層をロールコートし、 乾燥後柄 印刷をする。 さらに必要がある場合はその上にベタ印刷を行う。 あるいは柄印刷 を省略してベタ印刷のみを行う場合もある。 そして上記印刷層の上に、 変性ポリ プロピレン樹脂を押し出し法により形成する。
( 3 ) 被覆
前記の塗装鋼板を加熱した後、 前記被覆樹脂フィルムをラミネートロールで被覆 し、 更に加熱を行い镜面ロールで加圧し冷却する。 このときのラミネートロール のロール圧は 1〜 80 k g/cm2 が好適である。 さらに望ましい下限は 5 k g /cm2 であり、 上限は G O k gZcm2 である。 ロール圧が 1 k gZcm2 未 満では、 被覆樹脂が金属板の幅方向に対して均一に圧着されず、 表面外観 （鲜映 性） にばらつきを生ずる。 一方、 80 k g/cm2 を超えるとロールの摩耗が激 しく、 ロール組み替えを頻繁に行わなければならず生産性を損なう。
(実施例 1 )
(塗装鋼板の作成）
板厚 =0. 5 mm, めっき量 l O g/m2, クロメート皮膜層 （クロムとし て） =0. 05mg/dm2, 平均表面粗さ R a = 0. 3〃mの電気亜鉛めつき 鋼板に、 白色顔料を有する共重合ポリエステル系の塗料を 1 5 m塗布、 焼付け した塗装鑭板を作成した。
(被覆樹脂フィルムの作成）
5 m厚のポリエステル系の樹脂を予めトップコートした （フィルム保護膜） 25 m厚の透明なポリエチレンテレフタレートフイルムに、 ポリエステル系樹 脂の接着剤を 1 m塗布し、 ポリエステル系インキで木目柄印刷を行い （厚み 1 fim) . 2 O m厚の透明変性プロピレン樹脂 （ポリプロピレン共重合体： 1 0 0重量部とポリプロピレン： 1 00重量部を混合） を、 押し出し法により積層し た多層フィルムを作成して、 被覆樹脂フィルムとした。
(積層） 前記の塗装鋼板に、 前記被覆樹脂フィルムを 2 0 0 の雰囲気中でロール圧 2 O k g / c m2 で上記塗装鐧板上に被覆した。 その結果、 本願発明のものは鲜映 性を示す数値は 0. 8を示し、 加工密着性も優れていた。
(比較例 1 )
実施例 1と同様な方法で塗装鋼板を作成し、 これに次のフィルムを被覆した。 すなわち、 透明な 2 5〃m厚のポリエチレンテレフタレートフィルムに、 ポリエ ステル系樹脂の接着剤を 1 m塗布し、 ポリエステル系インキで木目柄印刷を行 い ( 1 ^ m) 、 被覆樹脂フィルムとした。
そして実施例 1と同様な方法で積層し樹脂被覆金属板を作成した。 その結果、 加工密着性は良かったが、 鲜映性を示す数値は 0 . 1と悪く、 劣っていた。 (実施例 2 )
実施例 1と同様に塗装銅板を作成した。 そして、 これに次のフィルムを被覆し た。 すなわち、 1 0 0〃m厚の透明なポリエチレンテレフタレートフィルムの片 面上にポリエステル系樹脂の接着剤を 5〃m塗布し、 さらにその上に 1 0 0 / m 厚の透明な変性プロピレン樹脂を押し出し法により積層した。
さらにその上にポリエステル系インキで木目柄印刷 （厚み 5 / m) を行い、 続 いてベタ印刷 （厚み 5 m) を行って多層フィルムを作成して、 被覆樹脂フィル ムとした。 そして、 実施例 1で用いた塗装鋼板に、 2 0 0ての雰囲気で、 ロール 圧が 2 0 k g Z c m2で積層し、 鲜映性を有する樹脂被覆金属板を作成した。 こ の金属板の鲜映性を示す値は 1 . 0を示し、 加工密着性も優れたものであった。 (比較例 2 )
実施例 1と同様な方法で塗装鋼板を作成し、 これに次のフィルムを被覆した。 すなわち、 透明な 1 0 0 厚のポリエチレンテレフ夕レートフイルムに、 ポリ エステル系樹脂の接着剤を 5 u m塗布した。
さらにその上に 1 0 0〃m厚の透明なプロピレン樹脂を押し出し法により積層 した。 さらにその上にポリエステル系インキで木目柄印刷 （厚み 5〃m) を行い 続いてベタ印刷 （厚み 5 ^ m) を行って多層フィルムを作成して、 被覆樹脂フィ ルムとした。 そして実施例 1と同様な方法で積層し樹脂被 δ金属板を作成した。 その結果、 鲜映性を示す数値は 0 . 8と良かったが、 加工密着性は悪く、 劣って いた。
(実施例 3 )
実施例 1と同様に塗装鑭板を作成した。 そして、 これに次のフィルムを被覆し た。 すなわち、 1 2 ju m厚の透明なポリエチレンテレフタレートフィルムの片面 上にシランカップリング剤を 0 . 5 m塗布し、 さらにその上に雲母顔料を混入 したポリエステル系ィンキで 4 m厚のベタ印刷を行った。 さらにその上に 5 m厚の透明な変性プロピレン樹脂を押し出し法により積層した多層フィルムを作 成して、 被覆樹脂フィルムとした。 そして、 実施例 1で用いた塗装鋼板に、 2 0 0 の雰囲気で、 ロール圧が 2 O k g Z c m2 で積層し、 鲜映性を有する樹脂被 覆金属板を作成した。 この金属板の鲜映性を示す値は 0. 7を示し、 加工密着性 も優れたものであった。
(比較例 3 )
実施例 1と同様な方法で塗装鋼板を作成し、 これに次のフィルムを被覆した。 すなわち、 透明な 1 2 m厚のポリエチレンテレフタレートフィルムの片面上に シランカップリング剤を 0 . 5〃m塗布し、 さらにその上に雲母顔料を混入した ポリエステル系ィンキで 4 m厚のベタ印刷を行った。 さらにその上に 5 m厚 の透明なプロピレン樹脂を押し出し法により積層した多層フィルムを作成して、 被覆樹脂フィルムとした。 そして ^例 1と同様な方法で積層し樹脂被覆金属板 を作成した。 その結果、 鲜映性を示す数値は 0 . 7と良かったが、 加工密着性は 悪く、 劣っていた。
(実施例 4 )
実施例 1と同様に塗料鋼板を作成した。 そして、 これに次のフィルムを被覆し た。 すなわち、 5 0〃m厚の透明なポリエチレンテレフタレートフィルムの片面 上に A 1顔料を混入させたポリエステル系樹脂の接着剤を 5 0 m塗布した。 さらにその上に 5 0 m厚の透明な変性プロピレン樹脂を押し出し法により積層 した多層フィルムを作成して、 被覆樹脂フィルムとした。 そして、 実施例 1で用 いた塗装鋼板に、 2 0 0ての雰囲気で、 ロール圧が 2 0 k g Z c m 2 で積層し、 鲜映性を有する樹脂被覆金属板を作成した。 この金属板の鲜映性を示す値は 0 . 7を示し、 加工密着性も優れたものであった。
(比較例 4 )
実施例 1と同様な方法で塗装鋼板を作成し、 これに次のフィルムを被覆した。 すなわち、 透明な 5 0〃m厚のポリエチレンテレフタレートフィルムの片面上に A】顔料を混入させたポリエステル系樹脂の接着剤を 5 0 m塗布した。 さらに その上に 5 0 m厚の透明なプロピレン樹脂を押し出し法により積層した多層フ イルムを作成して、 被覆樹脂フィルムとした。 そして実施例 1と同様な方法で積 層し樹脂被覆金属板を作成した。 その結果、 鲜映性を示す数値は 0 . 7と良かつ たが、 加工密着性は悪く、 劣っていた。
(評価方法）
(鲜映性）
本発明における鲜映性は次の方法により測定した。 すなわち、 携帯用鲜明度光沢 計 P G D - 4型 （財団法人日本色彩研究所製） を用い、 写像鲜映性、 すなわち、 化粧面に写した正反射像の鲜映度を測定した。 この測定値が高 L、ものほど鲜映性 が優れている。
測定方法はつぎの様にした。 すなわち、 1 0 c m x 1 0 c mの樹脂被覆金属板の 上に光沢計を水平に押し当て、 肉眼で目盛りを読み取り、 その値を鲜映性を示す 値とした。
(加工密着性）
本発明における加工密着性の評価は、 次の 2テストを行い両測定結果を総合的に 判断して評価した。 ( 1 ) エリクセン張り出しテスト
樹脂被覆金属板の被覆樹脂面にカッターナイフで原板に達するまでの碁盤目状の きずを入れて、 裏面よりエリクセンテスト試験機にて 8 mm張り出しを行う。 そ の後、 1 0 0 で 1時間の継続加熱を行い、 樹脂雇の剥餱程度を評価した。 表 1および表 2中で、 ◎印を「剥離なし」 とし、 X印を「剥雜あり」 として表示 した。
( 2 ) カップ深絞りテスト
樹脂被覆金属板を、 絞り比 r = 2 . 2で山田式深絞り試験機にてカップ絞りを行 う。 カップ円筒部を形成している樹脂面に、 カッターナイフで原板に達するまで 5 mm間隔の碁盤目状のきずを入れた後、 1 0 0 で 1時間の継続加熱を行い、 樹脂層の剥離程度を評価した。
表 1および表 2中で、 ◎印を「剥餱なし」 とし、 X印を 「剥雜あり」 として表示 した。 産業上の利用可能性
表 1および表 2にまとめて示すように、 本発明は、 積層された樹脂の中間に設 けられた変性ォレフィン樹脂層力、'、 印刷層、 塗料層、 ポリエステル系樹脂フィル ムなどとの接着性に優れるため、 深絞り等の厳しい加工によっても、 構成層界面 での剥雠が生ぜず、 優れた加工密着性を示す。
また、 金属板の表面粗さや各構成層 （樹脂層） の凸凹を、 変性ォレフィン樹脂 層が吸収するので、 樹脂被覆金属板として優れた鲜映性を得ることができる。 表 1
Figure imgf000015_0001
表 2 塗装鎖板 被 ¾ 樹 脂 フ ィ ル ム の 構 成 加 工 密 着 性 醉？ ft往
変性れフィン 印刷層 C 接着剤層 透明ホ。リエステル系 の値 エリクセン 力，フ' 金 厲 板 着色塗料層 E 樹脂層 D B 榭脂 ルム A 張り出しテスト 深絞りテスト 実施例 4 ステンレス鎮板 茶色顔料配^ 変性フ Πピレン 水" エステル 透明 * リエチレン 0. 7
0. 5 mm¾L ェ キシ系 50 m m テレ 7タレ-トフイルム ◎ ◎
30 μπ\ (Al顔料 50 /i m
入り）
50 μπ\ 比較例 4 ステンレス網板 茶色顔料配合 透明 リ; Tnt。レン 透明 *°リエチレンテレフ 0. 7 X X
0. 5mm厚 ェ *。キン系 50 /z m 系樹 β旨 タレ-トフ Λ
30 ^ m ( 顔料 50 βπι
入り）
50 μπ

Claims

請 求 の 範 囲
1 . 金属板を基板とし、 基板の片面又は両面に、 少なくとも、 5〜 1 0 0 m 厚の変性ォレフィン樹脂層、 その上に 5〜 1 0 O m厚のポリエステル系樹脂フ ィルムが積層された樹脂被覆金属板。
2 . 金属板を基板とし、 少なくとも基板の片面に、 基板側から順次、 塗料層、 5〜 1 0 0 m厚の変性ォレフィン樹脂層、 柄または およびベタ印刷層、 接着 剤層、 5〜 1 0 0 m厚の透明ポリエステル系樹脂フィルムが積層された樹脂被 覆金属板。
3 . 金属板を基板とし、 少なくとも基板の片面に、 基板側から順次、 塗料層、 柄または およびベタ印刷層、 5〜1 0 0 / m厚の変性ォレフィン樹脂層、 接着 剤層、 5〜 1 0 0 厚の透明ポリエステル系樹脂フィルムが積層された樹脂被 覆金属板。
4 . 金属板を基板とし、 少なくとも基板の片面に、 基板側から順次、 塗料層、 5〜 1 0 0 mの変性ォレフィン樹脂層、 接着剤層、 5〜 1 0 0 tz m厚の透明ポ リエステル系樹脂フィルムが積層された樹脂被覆金属板。
5 . 前記透明ポリエステル系樹脂フィルムの上層に塗料層が形成層された請求 項 1〜 4のいずれかに記載の樹脂被覆金属板。
6 . 前記接着剤層中にアルミニゥム金属顔料が混入されている請求項 2〜 5の t、ずれかに記載の樹脂被覆金属板。
7. 前記印刷層中にアルミニゥム金属顔料が混入されている請求項 2〜 5のい ずれかに記載の樹脂被覆金属板。
8 . 前記接着剤層中に雲母顔料が混入されている請求項 1〜 6のいずれかに記 載の樹脂被覆金属板。
9 . 前記印刷層中に雲母顔料が混入されている請求項 2〜 7のし、ずれかに記載 の樹脂被覆金属板。
PCT/JP1995/002639 1994-12-29 1995-12-22 Feuille metallique revetue de resine, d'une grande nettete d'image et dont le revetement presente une grande adhesivite apres travail WO1996020828A1 (fr)