WO1996020522A1 - Element de laser a semi-conducteur - Google Patents
Element de laser a semi-conducteur Download PDFInfo
- Publication number
- WO1996020522A1 WO1996020522A1 PCT/JP1995/002677 JP9502677W WO9620522A1 WO 1996020522 A1 WO1996020522 A1 WO 1996020522A1 JP 9502677 W JP9502677 W JP 9502677W WO 9620522 A1 WO9620522 A1 WO 9620522A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- type
- carrier block
- semiconductor laser
- laser device
- Prior art date
Description
Claims