WO1996002870A1 - Resine polyester pour un toner, procede de preparation de la resine et toner obtenu - Google Patents

Resine polyester pour un toner, procede de preparation de la resine et toner obtenu Download PDF

Info

Publication number
WO1996002870A1
WO1996002870A1 PCT/JP1995/001395 JP9501395W WO9602870A1 WO 1996002870 A1 WO1996002870 A1 WO 1996002870A1 JP 9501395 W JP9501395 W JP 9501395W WO 9602870 A1 WO9602870 A1 WO 9602870A1
Authority
WO
WIPO (PCT)
Prior art keywords
toner
polyester resin
product
less
toner according
Prior art date
Application number
PCT/JP1995/001395
Other languages
English (en)
French (fr)
Inventor
Shinji Kubo
Noriyuki Tajiri
Hitoshi Iwasaki
Yoichi Nagai
Original Assignee
Mitsubishi Rayon Co., Ltd.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP6183060A external-priority patent/JPH0830025A/ja
Priority claimed from JP08089695A external-priority patent/JP3296678B2/ja
Application filed by Mitsubishi Rayon Co., Ltd. filed Critical Mitsubishi Rayon Co., Ltd.
Priority to EP95925115A priority Critical patent/EP0720064B1/en
Priority to US08/605,074 priority patent/US5807654A/en
Priority to DE69533186T priority patent/DE69533186T2/de
Priority to KR1019960701240A priority patent/KR100236511B1/ko
Publication of WO1996002870A1 publication Critical patent/WO1996002870A1/ja
Priority to US09/019,147 priority patent/US6103438A/en

Description

明 細 書 トナー用ポリ エステル樹脂、 その製造方法およびトナー 技術分野
本発明は、 電子写真法、 静電記録法ゃ静電印刷法などにおいて静 電荷像または磁気潜像の現像に用いる乾式トナー用樹脂として有用 なポリエステル樹脂、 その製造および使用に関する。 さらに詳しく は、 本発明は、 色合い、 画像の鮮明性および画像精度が要求される フルカラー用として有用な トナー用ボリエステル樹脂、 その製造方 法およびそれを用いた トナーに関する。
背景技術
静電荷像より恒久的な顕像を得る方法においては、 光導電性感光 体または静電記録体上に形成された静電荷像をあらかじめ摩擦によ り帯電させた トナーによって現像した後、 定着を行う。 磁気潜像の 場合は、 磁気ドラム上の潜像を磁性体を含むトナーによって現像し た後、 定着を行う。
定着は、 光導電性感光体または静電記録体上に現像によって得ら れた トナー像を、 直接融着させるか、 紙やフ ィ ルム上に トナー像を 転写した後、 これを転写シー ト上に融着させることによって行われ る。 トナーの融着は、 溶剤蒸気との接触もしく は加圧や加熱によつ て行われる。 加熱方式には、 電気オーブンによる無接触加熱方式と 加圧ローラーによる圧着加熱方式があるが、 定着工程の高速化が要 請される最近では主として後者が用いられている。
乾式現像方法で使用される トナーには、 1 成分系 トナーと 2成分 系 トナーがある。 2成分系 トナーは、 先ず樹脂、 着色剤、 荷電制御 剤およびその他必要な添加剤を溶融混練して十分に分散させた後、 粗粉砕し、 次いで微粉砕して、 所定の粒度範囲に分級して製造され る。 1 成分系 トナーは、 上記の 2成分系の トナーの各成分の他に磁 性鉄粉を添加して同様に製造される。
樹脂は、 トナー配合中の主成分であるため、 トナーに要求される 性能の大部分を支配する。 このため トナー用樹脂には、 トナー製造 においては溶融混練工程での着色剤の分散性、 粉砕工程での粉碎性 の良いこ となどが要求され、 また トナーの使用においては定着性、 耐オフセッ ト性、 耐ブロ ッキング性および電気的性質が良いこ とな どの多様な性能が要求される。
トナーの製造に用いられる樹脂と しては、 エポキシ樹脂、 ポリエ ステル樹脂、 ボリ スチレ ン樹脂、 メ 夕ク リ ル系樹脂などが公知であ るが、 圧着加熱定着方式用には、 主にスチレンと (メ タ) アク リ ル 酸エステルの共重合体が用いられてきた。 しかし、 最近では、 より 低温で定着が可能であるこ とや定着された トナー像の耐塩ビ可塑剤 性が優れているこ とから、 ポリエステル樹脂が注目されている。
さ らに、 カラ一画像を得るためには、 上述の現像工程において 3 〜 4色の トナーを転写紙に付着させ、 次いで定着工程において各種 成分を溶融混合しながら発色させ、 定着させなければならない。 フ ルカラ一 トナー用バイ ンダー樹脂には、 上述のごと く 定着工程での 混合性の良い樹脂、 換言すれば、 溶融流動性の良い樹脂が強く望ま れている。 しかし、 溶融流動性の良好なバイ ンダー樹脂を用いた場 合、 定着工程でのオフセ ッ ト現象が生じる問題がある。
一方、 オフセッ ト現象を防止するため、 バイ ンダー樹脂を架橋化 させたり、 高分子化させたりすると、 溶融流動性が低下するため、 フルカラー トナー用のバイ ンダー樹脂と しては適さない。 従って、 フルカラー用複写機の場合、 オフセッ トを防止するため、 定着口一 ラー表面にシリ コーンオイル等を塗布している。
また、 最近では、 画像特性のみならず、 環境的な要素が重要視さ れてきており、 トナー製造時または複写時に刺激臭が発生し、 オペ レ一夕一やオフィ ス内で問題が多発している。 また、 フルカラー用 トナーは O H P用シー トへ複写するケースが多いことにより、 バイ ンダ一樹脂が着色していると複写物の透過性が低下し、 0 H Pで写 し出す時に画像が曇るという問題がある。 また、 バイ ンダー樹脂が 着色していると、 シアン、 マゼン夕およびイェローの 3原色を混合 して使用するフルカラー用 トナーでは、 色調の再現幅が狭く、 複写 印刷物の画像精度が低下する。 このため、 より高い画像精度が要求 されるようになった現在、 バイ ンダー樹脂においても、 より性能の 高い、 つま り臭気がなく、 着色も少ないバイ ンダー樹脂が要求され るようになってきている。 発明の開示
本発明は、 上記の如き状況に鑑みてなされたものであり、 その目 的とするところは、 トナーの製造時や使用時に刺激臭が発生せず、 また複写物の透過性の低下による画像の暴りのない鲜明な画像が得 られ、 色調の再現幅が広く なり、 複写印刷物の画像精度に優れた ト ナー用ボリエステル樹脂を提供することにある。
本発明者らは、 前記の目的を達成すべく鋭意検討を進めた結果、 アルデヒ ド化合物、 その分解生成物および副生物の含有量が特定数 値以下であるポリエステル樹脂によりその目的を達成できるこ とを 見い出し、 本発明を完成した。
すなわち、 本発明は、 芳香族ジカルボン酸およびその低級アルキ ルエステルからなる群から選ばれる少なく とも 1種を含む酸成分と 、 ビスフエノ ール A誘導体ジオールからなる群から選ばれる少なく と も 1 種を含むアルコール成分とからなるポリエステル樹脂であつ て、 前記ボリ エステル樹脂中のアルデヒ ド化合物、 その分解生成物 および副生物の含有量が 200 p pm以下であるこ とを特徴とする トナー 用ポリエステル樹脂にある。
本発明のこのボリエステル樹脂は、 電子写真法、 静電記録法ゃ静 電印刷法などにおける静電荷像または磁気潜像の現像に用いる乾式 トナーのバイ ンダー樹脂と して有用である。 発明を実施するための最良の形態
本発明でいうアルデヒ ド化合物、 その分解生成物および副生物と は、 ァセ トアルデヒ ド、 プロ ピオンアルデヒ ドなどのアルデヒ ド基 を有する、 沸点が 1 80 °C以下の化合物、 その分解生成物および副生 物をいう。
上記のアルデヒ ド化合物、 その分解生成物および副生物は、 トナ 一用ポリエステル樹脂において使用されている ビスフ エノ ール A誘 導体成分が加熱によ り分解して生成したり、 あるいはポリエステル には不可欠なカルボン酸の還元反応などによって生成する。 アルデ ヒ ド化合物、 その分解生成物および副生物は、 このようにポリ エス テル樹脂系の トナーにおいてさまざまなプロセスを経て生成する可 能性を有する。 また、 これらのアルデヒ ド化合物およびその分解生 成物は、 ボリ エステルの原料であるエチレ ングリ コールなどと反応 して、 ジォキソラ ン化合物を生成する。
このようなアルデヒ ド化合物、 その分解生成物および副生物は、 上記のようなボリ エステル樹脂の着色に悪影響を及ぼすとともに、 トナーと しての刺激臭の原因と もなる。 特に、 ァセ トアルデヒ ドや プロ ピオンアルデヒ ドのような低沸点のものは、 トナー化時の溶融 混練や複写時の加熱で容易に大気中に拡散し、 刺激臭の原因となる したがって、 トナーに供せられるボリエステル樹脂または トナ一 中のアルデヒ ド化合物、 その分解生成物および副生物の含有量は、
200 p pm以下であるこ とが重要であり、 好ま しく は l OO ppnu より好ま しく は 50 p pm 以下、 特に好ま しく は l Oppm 以下の範囲である。 これ は、 ボリエステル樹脂またはトナー中のアルデヒ ド化合物、 その分 解生成物および副生物の含有量が 200 p pmを超えると、 ボリエステル 樹脂の着色に悪影響を及ぼす傾向にあるとともに、 トナーとしての 刺激臭が認められるようになる傾向にあるためである。
本発明の トナー用ボリエステル樹脂は、 波長 440nm における吸光 度が 0. 05以下であるのが好ま しい。 これは、 吸光度の値が 0. 05を超 えると、 例えば、 フルカラー トナー用のバイ ンダー樹脂として〇 H P シー ト等に複写して使用する場合に、 光の透過性が低下し、 鲜明 な画像が得られなくなり、 また色調の再現性が低下するためである 。 さらに好ま しく は、 波長 440nm での吸光度が 0. 03以下、 特に好ま しく は 0. 01以下の範囲である。
本発明における吸光度は、 ポリエステル樹脂 2 gを 1 00m l のメチ ルクロライ ドに溶解し、 分光光度計を用いて波長 440nm における吸 光度を測定して求めた値である。
ボリエステル樹脂の吸光度に影饗を及ぼす原因としては、 ボリエ ステル樹脂の重合の間に生成する分解物が主な原因として考えられ 、 分解し難い単量体を選定したり、 分解物の生成を抑制する重合条 件を選定すること等によって、 吸光度を低下させることができる。 特に、 ボリエステル樹脂中に含有されるアルデヒ ド化合物、 その分 解生成物および副生物を抑制することが重要であり、 ボリエステル 樹脂あるいは トナー中のアルデヒ ド化合物、 その分解生成物および 副生物の含有量を 200ppm以下にすることが重要であり、 好ま しく は l OOp pm以下、 より好ま し く は 50 p pm 以下の範囲である。
かかる本発明の トナー用ボリエステル樹脂を得る方法については 特に限定されないが、 例えば下記に示す方法、 すなわち、
( 1 ) 先ず、 重合成分である酸成分 ( a ) およびアルコール成分 ( b ) を反応釜に仕込み、 窒素気流下で加熱昇温してエステル化反 応、 またはエステル化交換反応を行い、
( 2 ) 次いで、 常法に従って前記反応で生じた水またはアルコ一 ルを除去し、 引続いて 30mniHg以下の高真空下でアルデヒ ド化合物、 その分解生成物および副生物およびアルコール成分を留出させなが ら、 240 eC以下の低温で縮合反応を行う、
などの方法により得るこ とができる。
本発明の トナー用ボリエステル樹脂を得るのに用いられる酸成分 ( a ) は、 テレフタル酸、 イ ソフタル酸などの芳香族ジカルボン酸 およびその低級アルキルエステルからなる群から選ばれる少なく と も 1 種を含むものからなる。
酸成分 ( a ) と して使用されるテレフタル酸およびイ ソフタル酸 などの低級アルキルエステルの例と しては、 例えば、 テレフタル酸 ジメチル、 イ ソフタル酸ジメチル、 テレフタル酸ジェチル、 イ ソフ タル酸ジェチル、 テレフタル酸ジブチル、 イ ソフタル酸ジブチルな どが挙げられるが、 コス トおよびハン ドリ ング性の点でテレフタル 酸ジメチルゃイ ソフタル酸ジメチルが好ま しい。 上記の芳香族ジカ ルボン酸およびその低級アルキルエステルは、 それぞれ単独で、 ま たは 2種以上を混合して使用される。
芳香族ジカルボン酸は、 疎水性が強いベンゼン環からなり、 トナ 一の耐湿性を高めるこ とができるとともに、 得られる樹脂のガラス 転移温度 (以下、 単に Tgという。 ) を上げ、 トナーの耐ブロ ッキン グ性の向上に寄与する効果がある。 したがって、 芳香族ジカルボン 酸は、 全酸成分に対して 60モル%以上含有させるこ とが好ま し く 、 さ らに好ま し く は 70モル%以上である。 なかでも、 テレフタル酸系 のものは、 樹脂の夕フネスおよび Tgをァ ッブさせるのに効果があり 、 全酸成分に対して 50モル%以上含有させるこ とが好ま しく 、 さ ら に好ま しく は 60モル%以上の範囲である。 また、 イ ソ フ タル酸系の ものは、 反応性を高める効果があり、 目的によってその使用バラ ン スを変えて用いるこ とが好ま しい。
本発明において、 酸成分(a) と して必要に応じて使用するこ との できるその他のジカルボン酸の例と して、 フタル酸、 セバシン酸、 イ ソデシル琥珀酸、 マレイ ン酸、 フマル酸、 アジピン酸、 およびそ れらのモノ メチル、 モノェチル、 ジメチル、 ジメチルエステルなど 、 ならびにそれらの酸無水物が挙げられる。 これらの 2価カルボン 酸成分は、 トナーの定着性や耐ブロ ッキング性に大き く影響を与え るので、 樹脂の要求性能に応じて、 本発明の目的を阻害しない範囲 で、 好ま しく は全酸成分に対して 30モル%以下程度で含有させるこ とができる。
また、 本発明においては、 酸成分 ( a ) として、 必要に応じて 3 価以上の多価カルボン酸を使用するこ とができる。 3価以上の多価 カルボン酸の例と しては、 ト リ メ リ ッ ト酸、 ピロメ リ ッ ト酸、 1 , 2 , 4 — シクロへキサン ト リ カルボン酸、 2 , 5 , 7 —ナフ夕 レ ン ト リ カルボン酸、 1 , 2 , 4 —ナフタ レ ン ト リ カルボン酸、 1 , 2 , 5 —へキサン ト リ カルボン酸、 1 , 2 , 7 , 8 —オクタ ンテ トラ カルボン酸およびこれらの酸無水物などを挙げるこ とができる。
これらの 3価以上の多価カルボン酸は、 それぞれ単独で、 または 2種以上を混合して用いられ、 得られる樹脂の Tgを高める効果があ ると と もに、 樹脂に凝集性を付与し、 トナーの耐オフセッ ト性を高 める効果があり、 全酸成分に対して 0. 5 〜30モル の範囲で用いる こ とが好ま し く、 さ らに好ま しく は 1 25モル%の範囲である。 こ れは、 0.5 モル%未満では上記の効果が十分に得られないためであ り、 30モル%を超える とボリエステル樹脂の製造時のゲル化の制御 が困難となり、 所望の樹脂が得られ難い傾向にあるためである。 な お、 後述する 3価以上の多価アルコールを併用する場合には、 両者 の合計量を上記の範囲とするこ とが好ま しい。
本発明の トナー用のボリエステル樹脂を得るのに用いられるアル コール成分 ( b ) は、 ビスフヱノ ール A誘導体からなる芳香族ジォ ールを含有する ものである。 ビスフ ヱノ ール A誘導体からなる芳香 族ジオールは、 アルデヒ ド化合物等の生成の原因となるものである が、 一方で樹脂の Tgを上げ、 トナーと しての耐ブロ ッキング性を向 上させる効果を有するので、 トナー用ポリエステル樹脂においてァ ルコール成分と して好適に使用されるものである。
本発明において使用される芳香族ジオールの例としては、 ビスフ ェノ ール A誘導体であるポリオキシエチレン一 ( 2. 0 ) — 2 , 2 一 ビス ( 4 — ヒ ドロキシフ ヱニル) プ ン、 ボリ ォキシプロ ピレ ンー ( 2. 0 ) — 2 2 — ビス ( 4 — ヒ ドロキシフエニル) プロパ ン、 ポリ オキシプロ ピレ ン ( 2. 2 ) 一ポリオキンエチレ ン一 ( 2 . 0 ) — 2 , 2 — ビス ( 4 ー ヒ ドロキンフ エニル) ブ 'ン、 ボリ ォキシエチ レ ン一 ( 2. 3 ) — 2 2 — ビス ( 4 ー ヒ ドロキシフエ ニル) プロパン、 ポリ オキシプロ ピレン一 ( 6 ) - 2 , 2 — ビス ( 4 ー ヒ ドロキシフヱニル) プロハ 'ン、 ボリォキシプロ ピレン ( 2. 3 ) 一 2 , 2 — ビス ( 4 ー ヒ ドロキシフ エニル) プ 'ン、 ポリ オ キシプロ ピレ ン一 ( 2. 4 ) — 2 , 2 — ビス ( 4 ー ヒ ドロキシフ エ ニル) ブ ·ン、 ボリ ォキシプロ ピレ ン ( 3. 3 ) — 2 , 2 — ビス ( 4 ー ヒ ドロキンフエニル) プロパン、 ポリ オキシエチレ ン一 ( 3 . 0 ) - 2 , 2 — ビス ( 4 — ヒ ドロキシフエニル) プロバン、 ボリ ォキシエチレ ン一 ( 6 ) — 2 , 2 — ビス ( 4 ー ヒ ドロキシフ エニル ) プロパンなどが挙げられる。
これらの芳香族ジオールは、 それぞれ単独で、 または 2種以上を 混合して使用される。 しかし、 芳香族ジオールは、 反応性が鈍く分 解を促すため、 アルデヒ ド化合物、 その分解生成物および副生物の 生成の原因となるものであり、 樹脂が着色して吸光度に悪影饗を及 ぼすことを考えた場合、 その使用量は限られてく る。 好ま しい使用 量は、 全酸成分に対して 90モル%以下であり、 さらに好ま しく は 80 モル%以下である。 しかしながら、 芳香族ジオールは、 Tgを上げ、 トナーの耐ブロ ッキング性を向上させる効果があるため、 全酸成分 に対して少なく とも 20モル の量で使用されるのが好ま しいけれど も、 ボリエステル樹脂の着色とのバランスを考慮してその使用量を 設定する必要がある。
また、 本発明において、 アルコール成分 ( b ) には、 脂肪族ジォ ールが適宜に含有される。 有用な脂肪族ジオールの例としては、 ェ チレングリ コール、 ジエチレングリ コール、 ネオペンチルダリ コー ル、 プロピレングリ コール、 ブタンジオールなどを挙げることがで き、 これらはそれぞれ単独で、 または 2種以上を混合して用いられ る。 これらの脂肪族ジオールは、 縮重合反応速度を向上せしめる作 用を有する。 これらの中でも定着性の点からエチレングリ コール、 ネオペンチルグリ コールおよびブタンジオールが好ま しい。
脂肪族ジオールは、 得られる樹脂に可撓性を付与し、 定着性に寄 与するが、 Tgが低下し、 耐ブロッキング性に悪影響を及ぼすため、 これらの使用量は、 使用機種にあわせて適宜に設定すればよい。 脂 肪族ジオールの使用量は、 全酸分に対して 20〜80モル%とするのが 好ま しく、 さらに好ま しく は 40〜80モル%の範囲である。
また、 本発明においては、 アルコール成分 ( b ) として、 必要に 応じて 3価以上の多価アルコールを使用するこ とができる。 多価ァ ルコールの例と しては、 ソルビ トール、 1 , 2 , 3 , 6—へキサテ トラロール、 1 , 4 ーソルビタ ン、 ペン夕エリ ス リ トール、 ジペン 夕エリ ス リ トール、 ト リペン夕エリ ス リ トール、 蔗糖、 1 , 2 , 4 一ブタ ン ト リオール、 し 2 , 5—ペン夕 ト リオール、 グリセロ ー ル、 2—メチルプロパン ト リ オール、 2—メチルー 1 , 2 、 4 ーブ タ ン ト リ オール、 ト リ メチロールェタ ン、 ト リ メチロールプロハ'ン 、 1 , 3 , 5— ト リ ヒ ドロキシメチルベンゼンなどが挙げられる。 これらの多価アルコールは、 それぞれ単独で、 または 2種以上を混 合して用いられる。 これらの 3価以上の多価アルコールは、 得られ る樹脂の Tgを高める効果を有する とと もに、 樹脂に凝集性を付与し 、 トナーの耐オフセッ ト性を高める効果がある。 その使用量は、 全 酸成分に対して 0. 5 〜50モル%の範囲であるのが好ま しく 、 さ らに 好ま しく は 1 〜25モル%の範囲である。 これは、 0. 5 モル%未満で は上記の効果が十分に得られないためであり、 30モル%を超えると ボリ エステル樹脂の製造時のゲル化の制御が困難となり、 所望の樹 脂が得られ難い傾向にあるためである。 なお、 前述の 3価以上の多 価アルコールを併用する場合には、 両者の合計量を上記の範囲とす るのが好ま しい。
本発明の トナー用ポリエステル樹脂は、 上記の酸成分 ( a ) と上 記のアルコール成分 ( b ) を重合するこ とにより得るこ とができる が、 本発明の目的を達成するためには、 ボリエステル樹脂の着色に 悪影饗を及ぼし、 また トナーと しての刺激臭の原因ともなる分解生 成物の発生を抑える重合プロセスを用いる必要がある。
本発明では、 前記のモノマーを反応釜に仕込み、 加熱昇温するこ とによ り、 エステル化反応またはエステル交換反応を行う。 この時 必要に応じて硫酸、 チタ ンブ トキサイ ド、 ジブチルスズオキサイ ド 、 酢酸マグネシウム、 酢酸マンガン等の通常公知のエステル化反応 またはエステル交換反応で使用されるエステル化触媒またはエステ ル交換触媒が使用される。 次いで常法に従って該反応で生じた水ま たはアルコールを除去する。 重合に際しては、 通常公知の重合触媒 、 例えばチタンブトキサイ ド、 ジブチルスズオキサイ ド、 酢酸スズ 、 酢酸亜鉛、 二硫化スズ、 三酸化アンチモン、 二酸化ゲルマンニゥ ムなどが用いられる。
本発明においては引き続き重合反応を行うが、 このとき l OOmmHg 以下の真空下でジオール成分を留出除去させながら重合を行うのが よい。 重合プロセスの第一段階のエステル化反応では、 窒素気流下 で行う こ とが好ま しい。 また、 第二段階の縮合反応時においては、 240 で以下の低温で、 かつ 30龍 Hg以下の高真空度で反応を行う こと が好ま しい。 240 てを超える高温で縮合するとアルデヒ ド化合物等 の分解物の発生が激しく、 それを用いた樹脂は トナー化時に刺激臭 の発生が激しく、 それを O H Pで複写した時、 光の透過性が低下す る。 縮合反応の温度は、 さらに好ま しく は 230 て以下、 より好ま し く は 220 'C以下である。 また、 高真空で反応を行う という ことは、 反応速度を高めるだけでなく、 生成した低沸点のアルデヒ ド化合物 を系外に除去する効果をももたらす。 また、 この縮合反応は、 さら に好ま しく は l OmmHg以下、 より好ま しく は 5 關 Hg以下の真空下で行 われる。
このようにして得られる本発明の トナー用ボリエステル樹脂は、 アルデヒ ド化合物、 その分解生成物および副生物の含有量が 200p pm 以下で、 かつ着色がなく、 吸光度 (440 nm) も低いものであり、 ト ナー化時の溶融混練や複写時の加熱においても刺激臭を発散させる ことがなく、 特に トナー像の色合いが問題となるフルカラー トナー 用のバイ ンダー樹脂として好ま しい。 本発明においては、 このようなアルデヒ ド化合物、 その分解生成 物および副生物の含有量が 200 p pm以下であるボリエステル樹脂を主 成分とするバイ ンダー樹脂を用いた トナーにおいても、 トナー中の アルデヒ ド化合物、 その分解生成物および副生物に基づく トナーと しての刺激臭の発生を抑止するこ とができる。 トナー中のアルデヒ ド化合物、 その分解生成物および副生物の含有量は、 200 Ρ ΡΠ1以下で あるこ とが好ま しく、 さ らに好ま し く は l O O p pm以下、 よ り好ま し く は 50 p pm 以下の範囲である。
また、 本発明のポリエステル樹脂においては、 波長 440nm におけ る吸光度が 0. 5 以下となるような光透過性の高い色調に優れた樹脂 であるため、 このボリエステル樹脂をフルカラ一用 トナーのバイ ン ダー樹脂と して用いても複写印刷物の画像精度の低下をな くすこ と ができる。 特に O H P用シー トへ複写するフルカラー トナー用のバ イ ンダ一樹脂と して使用する場合には、 複写物の透過性の低下によ る画像の Sりのない鲜明な画像が得られる とともに、 色調の再現幅 が広く なり、 複写印刷物の画像精度に優れたものとなる。
本発明において、 上記のようなボリエステル樹脂は、 トナーのバ イ ンダ一樹脂の主成分と して用いられるが、 このバイ ンダ一樹脂に は必要によりスチレ ン系樹脂、 スチレン一ァク リ ル系樹脂などの他 の樹脂を併用するこ ともできる。
また、 本発明の トナーは、 上記のようなボリエステル樹脂を主成 分とするバイ ンダー樹脂と着色剤を含有してなる ものであり、 バイ ンダ一樹脂は トナー中に 70〜 97重量%の範囲で含有されるこ とが好 ま しく 、 さ らに好ま しく は 80〜95重量%の範囲である。 これは、 バ ィ ンダ一樹脂の含有量が 70重量%未満であると、 トナーと しての非 オフセッ 卜性が低下する傾向にあり、 逆に 97重量%を超えると トナ 一の帯電安定性に劣る傾向にあるためである。 使用される着色剤と しては、 通常使用されている ものでよ く 、 例えば、 力一ボンブラ ッ ク、 ニグ口シン染料、 ラ ンプ黒、 ス一ダンブラ ッ ク S M、 ネーブル イエロ一、 ミ ネラノレフ ア ース トイエロー、 リ ソーノレレ ッ ド、 ノヽ '—マ ネ ン トオ レ ン ジ 4 R等の着色剤あるいは顔料等が挙げられる。
本発明の トナーにおいては、 荷電制御剤、 オフセッ ト防止剤、 磁 性粉等の添加剤を使用 してもよい。 これらの添加剤は、 通常使用さ れている ものでよ く、 例えば、 ニグ口シン、 アルキル基含有アジン 系染料、 塩基性染料、 モノアブ染料またはその金属錯体、 サリチル 酸またはその金属錯体、 アルキルサリ チル酸またはその金厲錯体、 ナフ トェ酸またはその金属錯体等の荷電制御剤、 ボリエチレ ン、 ボ リ ブロ ビレ ン、 エチ レ ン一ボリ プロ ピレ ン共重合体等のオフセ ッ ト 防止剤、 フユライ ト、 マグネタイ ト等の磁性粉が挙げられる。
本発明の トナーは、 バイ ンダー樹脂、 着色剤および添加剤等を、 例えば、 二軸押出機やミ キサー等の混練機を用いて、 バイ ンダー樹 脂の軟化温度より も 15〜30eC程度高い温度で混練した後、 微粉碎し 、 分級して、 トナー化される。 得られた トナー粒子は、 平均粒径が 5〜20〃 m程度であるこ とが好ま しく 、 さ らに好ま しく は 8〜 m程度である。 また、 粒径が 5 m以下の微粒子が 3重量%未満で あるこ とが好ま しい。
以下、 実施例および比較例により本発明を具体的に説明する。 なお、 実施例および比較例における性能評価は以下の方法を用い て行った。
( 1 ) Tg (ガラス転移温度) (て)
(株) 島津製作所製、 示差走査熱量計を用い、 試料をメ ル ト クェ ンチした後、 昇温 5 eC Z分で測定した。 吸熱カーブ近辺のベースラ イ ンと、 接線の交点 (ショルダー値) を Tgと した。
( 2 ) 軟化温度 ('C ) (株) 島津製作所製、 フ ローテスター ( C F T— 5 0 0 ) を用い て、 ノズル 1.0 mm0 X lOmml 、 荷重 30kgf 、 昇温 3 °C/分、 サンプ ル量 1.0 gの条件下でサンプルが半分流出 した時の温度を軟化温度 C ) と した。
( 3 ) 組成分析
樹脂をヒ ドラジンで加水分解し、 液体ク ロマ ト グラフィ ーで定量 した。
( 4 ) 酸価 (mgKOH / g )
樹脂をべン ジルアルコールで加熱溶解した後、 冷却し、 1 ノ50規 定の K0H ベンジルアルコール溶液にて滴定した。
( 5 ) アルデヒ ド化合物、 その分解生成物および副生物の含有量 試料 2.0 gをへッ ドスペースガスク ロマ ト グラ フ ィ ー ( (株) 島 津製作所製、 H S S— 2 B ) により定量した。
( 6 ) 官能試験
試料 10gを強化ガラス製のサンプル瓶に入れ、 150 'Cで 30分加熱 後、 臭気の有無をチェ ッ ク した。
( 7 ) 吸光度
樹脂 2 gを 100ml のメ チ レ ンクロライ ドに溶解し、 分光光度計 ( (株) 日立製作所製、 モデル 1 5 0 - 2 0 ) にて光長 lOmtnLの標準 石英セルを用いて、 440nm の波長における吸光度を測定した。
( 8 ) トナー面像評価
シ リ コー ンオイルを塗布したヒ一 トロ一ラーを有し、 温度が自由 に変更可能で、 7枚 Z分の印刷速度のフルカラ一複写機を用いて、 0 H Pフ ィ ルムに複写した際の画像の暴りおよび画像精度を目視に て、 以下の基準で評価した。
© : 画像の暴りがな く極めて鲜明で、 画像精度も優れたもの
〇 : 画像の暴りが殆どな く 鲜明で、 画像精度も良好なもの X : 画像の暴りが目立ち、 画像精度も不良なもの
また、 実施例および比較例中で用いた略記号は、 次のものを表わ す。
ジオール A : ボリォキシプロ ピレン一 ( 2 . 3 ) — 2 , 2 — ビス ( 4 ー ヒ ドロキシフ エニル) プロパン
ジオール B : ポリオキシエチレ ン一 ( 2 . 3 ) — 2 , 2 — ビス ( 4 ー ヒ ドロキシフ エニル) プロパン
実施例 1
テレフタル酸 1 00 モル部、 ジオール A 50モル部、 ジオール B 1 0モ ル部およびエチレングリ コール 55モル部を蒸留塔を備えた反応容器 に投入した。 触媒である三酸化ァンチモンを全酸成分に対して 0. 05 重量部添加し、 内温を 260 、 攪拌回転数を 120rpmに保ち、 常圧下 の窒素気流下でエステル化反応させた。 その後、 反応系内を 30分か けて l . OmmHg まで減圧し、 内温を 220 eCに保持して、 エチレングリ コールを留出せしめながら縮合反応を 5時間行い、 Tgが 62'C、 軟化 温度が 1 80 'Cおよび酸価が ^ SmgKOHZ gの特性値を有する樹脂 R - 1 を得た。 表 1 に得られた樹脂 R— 1 の組成分折結果、 アルデヒ ド 化合物含有量の定量結果ならびに官能試験結果を示す。
次に、 上記樹脂 R — 1 の 94重量部に対して、 カーボンブラ ッ ク ( 三菱化成 (株) 製、 # 40) 4重量部および電荷制御剤 (オリエン ト 化学 (株) 製、 ボン ト ロ ン S— 34 ) 1 重量部をプレ ミ キシングした 。 その後、 イ ンタ一ナルミキサー (栗本鉄工 (株) 製) を用いて、 内温 1 50 。C、 65 r pm の条件下で 30分間混練した。 得られた混練物を 粗粉碎した後、 微粉砕および分极を行って粒径 5 〜 1 8 mの トナー を得た。
得られた トナーについてアルデヒ ド化合物の含有量の定量および 官能試験を行った。 結果を表 1 に示す。 比較例 1
実施例 1 と同じ重合仕込み組成および操作でエステル化および縮 合を行い、 樹脂 R - 2を得た。 但し、 エステル化時には窒素導入を 行わず、 縮合温度 270 て、 真空度 l OOmmHg で 6時間縮合した。
得られた樹脂 R — 2 は、 64 eCの T gと 1 1 0 での軟化温度を有してい た。 また、 樹脂 R - 2 について、 アルデヒ ド化合物の含有量を測定 したところ、 プロ ピオンアルデヒ ドが 350 p pm含有されていた。 また 、 官能試験においても非常に強い刺激臭があつた。
次に、 得られた樹脂 R — 2 を用いて実施例 1 と同様の方法で調製 した トナーについて、 アルデヒ ド化合物の含有量を定量したところ 、 320 Ρ ΡΠ1のプロ ピオンアルデヒ ドが含有されていた。 また、 官能試 験においても強い刺激臭があった。
また、 上記の混練において、 ベン ト孔を有する二軸の押出機を用 いた場合、 トナー中のブロ ピオンアルデヒ ドの含有量は 220 p pmまで 減少したが、 官能試験において刺激臭が認められた。
実施例 2 〜 7
エステル化雰囲気、 縮合条件および樹脂組成を表 1 の如く に変更 した以外は、 実施例 1 と同様な操作を行い、 樹脂 R — 3 〜 R— 8 を 得た。
次いで、 この得られた樹脂 R — 3 〜 R — 8、 およびこれらの樹脂 R — 3 〜 R — 8 を用いて実施例 1 と同様の方法で調製して得た トナ 一についてアルデヒ ド化合物の定量および官能試験を行った。 結果 を表 1 に示す。
樹脂 R — 3 〜 R — 8 のいずれもアルデヒ ド化合物の含有量は低く 、 官能試験においても刺激臭はなかった。 また、 トナー化した場合 でもアルデヒ ド化合物の含有量は少な く、 官能試験においても刺激 ¾は 7よ力ヽ っ こ。 比較例 2〜 5
エステル化雰囲気、 縮合条件および樹脂組成を表 3の如く に変更 した以外は実施例 1 と同様な操作を行い、 樹脂 R — 9〜R — 12を得 た。
次いで、 この得られた樹脂 R — 9〜R — 12、 およびこれらの樹脂 R — 9〜R— 12を用いて実施例 1 と同様の方法で調製して得た トナ 一についてアルデヒ ド化合物の定量および官能試験を行った。 結果 を表 1 に示す。
樹脂 R — 9〜R — 12のいずれにおいても、 アルデヒ ド化合物の含 有量が多く、 官能試験においても刺激臭があった。 また、 トナー化 後においてもアルデヒ ドの含有量は高く、 トナーの官能試験におい ても刺激臭を有していた。
実施例 8〜 9
エステル化雰囲気、 縮合条件および樹脂組成を表 4に示す如く に 変更した以外は実施例 1 と同様な操作を行って、 架橋樹脂 R — 13〜 R - 14を得た。
次いで、 この得られた架橋樹脂 R — 13〜R — 14、 およびこれらの 樹脂 R — 13~R — 14を用いて実施例 1 と同様な方法で調製して得た トナーについてアルデヒ ド化合物の定量および官能試験を行った。 結果を表 1 に示す。
架橋樹脂 R — 13〜R— 14のいずれにおいてアルデヒ ド化合物の含 有量は低く、 官能試験においても刺激臭はなかった。 また、 トナー 化した場合でもアルデヒ ド化合物の含有量は少なく、 官能試験にお いても刺激臭はなかった。 表 1
Figure imgf000020_0001
TPA : テレフタル酸 【PA : イソフタル酸 TMA :無水トリメリ ッ ト酸
NPG : ネオペンチルグリコール EG :エチレングリコール
* ' : アルデヒド化合物 (プロピオンアルデヒド) 含有量 (ppm)
* 2 : トナー調製後のアルデヒ ド化合物 (プロビオンアルデヒ ド) 含有量 (ppm)
表 1 (つづき)
Figure imgf000021_0001
実施例 10
テ レ フ タル酸 100 モル部、 ジオール A60モル部およびエチ レ ング リ コール 65モル部を蒸留塔を備えた反応容器に投入した。 触媒であ る三酸化アンチモ ンを全酸成分に対して 0.05重量部添加し、 内温を 260 て、 攪拌回転数を 120rpmに保ち、 常圧の窒素気流下でエステル 化反応させた。 その後、 反応系内を 30分かけて l. OmmHg まで減圧し 、 内温を 220 eCに保持して、 エチレ ングリ コールを留出せしめなが ら縮合反応を 5 時間行い、 Tgが 64 、 軟化温度が 109 °Cおよび酸価 が 7. lmgKOH/ gの特性値を有する樹脂 R - 15を得た。 表 2 に得られ た樹脂 R - 15の組成分折結果、 アルデヒ ド化合物含有量の定量結果 、 官能試験結果および吸光度測定結果を示す。
次に、 上記樹脂 R— 15の 94重量部に対して、 カーボンブラ ッ ク ( 三菱化成 (株) 製、 #40) 5重量部および荷電制御剤 (オ リエン ト 化学 (株) 製、 ボン トロ ン S — 34) 1 重量部をプレ ミ キシングした 。 その後、 イ ンターナル ミ キサー (栗本鉄工 (株) 製) を用いて、 内温 150 'C、 65rpm の条件下で 30分間混練した。 得られた混練物を 粗粉砕した後、 微粉砕および分級を行って粒径 5〜18 i mの トナー を得た。
得られた トナーについてアルデヒ ド化合物含有量の定量および官 能試験を行った。 結果を表 2 に示す。
比較例 6
実施例 10と同じ重合仕込み組成および操作でエステル化および縮 合を行い、 樹脂 R— 16を得た。 但し、 エステル化時には窒素導入を 行わず、 縮合温度 270 。C、 真空度 lOOmmHg で 7時間縮合した。
得られた樹脂 R - 16は、 63ての Tgと 106 ての軟化温度を有してい た。 また、 樹脂 R— 16について、 アルデヒ ド化合物の含有量を測定 したところ、 プロ ピオンアルデヒ ド 330ppmと 2 —ェチル一 1 , 3 — ジォキソラン 40ppm が含有されており、 官能試験においても非常に 強い刺激臭があった。 また、 着色を示す吸光度は 0.076 であった。 次に、 得られた樹脂 R — 16を用いて実施例 10と同様の方法で調製 した トナーについて、 アルデヒ ド化合物の含有量を定量したところ 、 プロ ピオンアルデヒ ド 315ppmと 2 —ェチル一 1 , 3 —ジォキフシ ラン 37ppm が含有されており、 官能試験においても強い刺激臭があ つた。
また、 上記の混練において、 ベン ト孔を有する二軸の押出機を用 いた場合、 トナー中のプロ ピオンアルデヒ ドの含有量は 220ppmまで 減少したが、 官能試験において刺激臭が認められた。
実施例 Π〜 14
エステル化雰囲気、 縮合条件および樹脂組成を表 2の如く に変更 した以外は実施例 10と同様な操作を行い、 樹脂 R — 17〜R — 20を得 た。 得られた樹脂の組成分析結果、 アルデヒ ド化合物含有量の定量 結果、 官能試験結果および吸光度则定結果を表 2 に示す。
次いで、 この得られた樹脂 R — 17〜R — 20を用い、 フルカラー ト ナー用着色剤を用いた以外は実施例 10と同様にしてフルカラー トナ 一を調製した。 得られた トナーについて、 アルデヒ ド化合物の定量 、 官能試験、 吸光度測定および画像評価を行い、 その結果を表 2 に 示す。
樹脂 R - 17〜R - 20は、 いずれも波長 440nm での吸光度が低く、 トナー化した際にも優れた画像特性を示していた。 特に、 樹脂 R — 19および R - 20では、 極めて優れた画像特性を有していた。 また、 樹脂 R — 17〜R - 20は、 いずれもアルデヒ ド化合物の含有量が低く 、 官能試験においても刺激臭はなかった。 これらを トナー化した際 にも、 同様に刺激臭はなかった。
比較例 7〜 10 エステル化雰囲気、 縮合条件および樹脂組成を表 2の如く に変更 した以外は実施例 1 0と同様な操作を行い、 樹脂 R - 21〜R - 24を得 た。 得られた樹脂の組成分折結果、 アルデヒ ド化合物含有量の定量 結果、 官能試験結果および吸光度測定結果を表 2 に示す。
次いで、 この得られた樹脂 R — 21〜R — 24を用い、 フルカラー ト ナー用着色剤を用いた以外は実施例 1 0と同様にしてフルカラ一 トナ —を調製した。 得られた トナーについて、 アルデヒ ド化合物含有量 の定量、 官能試験および画像評価を行い、 その結果を表 2に示す。 樹脂 R - 21〜R — 24は、 いずれも波長 440 nm での吸光度が高く、 光透過性に劣っており、 トナー化した際にも画像の曇りや画像精度 に劣っていた。 また、 いずれの樹脂もアルデヒ ド化合物の含有量が 高く、 官能試験においても刺激臭を有し、 トナー化した際にも同様 に刺激臭を有していた。
表 2
Figure imgf000025_0001
TPA : テレフタル酸 ίΡΑ : イソフタル酸 ΤΜΑ :無水トリメリ ッ ト酸
NPG : ネオペンチルグリコール EG :エチレングリコール
* ' : アルデヒ ド化合物 (プロピオンアルデヒド) 含有量 (ppm)
* 2 : トナー調製後のアルデヒ ド化合物 (プロビオンアルデヒ ド) 含有量 (ppm)
表 2 (つづき)
Figure imgf000026_0001
産業上の利用可能性
本発明の トナー用ボリエステル樹脂は、 吸光度が低く、 光透過性 および色調の優れたものであり、 トナーとしての画像の鲜明性およ び画像精度に優れ、 特に トナー像の色合いが問題となるフルカラー トナー用として好適なものである。 また、 本発明のボリエステル樹 脂およびトナーは、 トナー化時の溶融混練および複写時などの加熱 においても刺激臭の発生がなく、 電子写真法、 静電記録法および静 電印刷法などにおいて静電荷像または磁気潜像に用いる乾式トナー 用樹脂およびトナーとしてきわめて有用である。

Claims

請 求 の 範 囲
1. 芳香族ジカルボン酸およびその低极アルキルエステルからな る群から選ばれる少な く とも 1 種を含む酸成分と、 ビスフエノ ール A誘導体ジオールからなる群から選ばれる少なく と も 1 種を含むァ ルコール成分とからなるボリエステル樹脂であって、 前記ボリエス テル樹脂中の了ルデヒ ド化合物、 その分解生成物および副成物の含 有量が 200 Ρ ΡΠ1以下である トナ一用ボリエステル樹脂。
2. 波長 440nm における吸光度が 0. 05以下である請求項 1 記載の トナー用ボリ エステル樹脂。
3. アルデヒ ド化合物、 その分解生成物および副成物の含有量が l OOp pm以下である請求項 1 記載の トナー用ボリエステル樹脂。
4. アルデヒ ド化合物、 その分解生成物および副成物の含有量が 50ppm 以下である請求項 1 記載の トナー用ボリエステル樹脂。
5. アルデヒ ド化合物、 その分解生成物および副成物の含有量が l Oppm 以下である請求項 1 記載の トナー用ボリエステル樹脂。
6. アルデヒ ド化合物、 その分解物または副成物の沸点が 1 80 'C 以下である請求項 1 記載の トナー用ボリエステル樹脂。
7. アルデヒ ド化合物、 その分解物または副成物の沸点が 1 00 'C 以下である請求項 1 記載の トナー用ボリエステル樹脂。
8. アルデヒ ド化合物、 その分解物または副成物の沸点が 50 'C以 下である請求項 1 記載の トナー用ボリエステル樹脂。
9. アルデヒ ド化合物、 その分解物または副成物が、 プロ ビオン アルデヒ ド、 ァセ トアルデヒ ドまたはジォキフラ ン化合物である請 求項 1 記載の トナー用ボリ エステル樹脂。
1 0. ボリエステル樹脂が、 芳香族ジカルボン酸およびその低級ァ ルキルエステルからなる群から選ばれる少な く とも 1 種を含む酸成 分と、 ビスフヱノ ール A誘導体ジオールからなる群から選ばれる少 なく とも 1 種と脂肪族ジオールからなる群から選ばれる少な く とも 1 種とを含むアルコール成分からなる請求項 1 記載の トナー用ボリ エステル樹脂。
1 1 . ビスフエノール A誘導体ジオールが、 ビスフエ ノ ール Aのァ ルキレンォキサイ ド付加物である請求項 1 記載の トナー用ボリ エス テル樹脂。
12. ビスフ エノ ール A誘導体ジオールが、 ビスフ エノ ール Aのプ ロ ピレ ンォキサイ ド付加物である請求項 1 1記載の トナー用ポリエス テル樹脂。
1 3. ビスフ エ ノ ール A誘導体ジオールと して、 ビスフ エノ ール A のプロ ピレンオキサイ ド付加物およびビスフ ヱノ ール Aのエチレ ン ォキサイ ド付加物を含有する請求項 1 1記載の トナー用ボリエステル 樹脂。
14. ビスフヱノ ール A誘導体ジオールが、 全酸成分に対して 30〜 90モル%の量で含有されている請求項 1 0記載の トナー用ボリエステ ル樹脂。
1 5. ビスフヱ ノ ール A誘導体ジオールが、 全酸成分に対して 50〜 80モル%の量で含有されている請求項 1 0記載の トナー用ボリエステ ル樹脂。
1 6. ボリエステル樹脂が、 3価以上の多価カルボン酸および ま たは 3価以上の多価アルコールを構成成分と して含む非線状ボリエ ステル樹脂である請求項 1 記載の トナー用ボリエステル樹脂。
17. 3価以上の多価カルボン酸および/または 3価以上の多価ァ ルコールが、 全酸成分に対して 0. 5 〜30モル の量で含有されてい る請求項 1 4記載の トナー用ボリエステル樹脂。
1 8. 3価以上の多価カルボン酸およびノまたは 3価以上の多価ァ ルコールが、 全酸成分に対して 1 〜25モル%の量で含有されている 請求項 1 4記載の トナー用ボリエステル樹脂。
1 9. 芳香族ジカルボン酸およびその低級アルキルエステルからな る群から選ばれる少なく とも 1 種を含む酸成分と、 ビスフ Xノール
A誘導体ジオールからなる群から選ばれる少なく とも 1 種を含むァ ルコール成分を、 エステル化反応またはエステル交換反応に付した 後、 30匪 Hg以下の真空下で、 240 'C以下の反応温度で縮合反応を行 う こ とを含む、 アルデヒ ド化合物、 その分解生成物および副成物の 含有量が 200 p pm以下である トナー用ボリエステル樹脂の製造方法。
20. 縮合反応が、 l OmmHg以下の真空下で行われる請求項 1 9記載の 法。
21 . 縮合反応が、 5 匪 Hg以下の真空下で行われる請求項 1 9記載の 方法。
22. 縮合反応が、 230 て以下の反応温度で行われる請求項 1 9記載 の方法。
23. 縮合反応が、 220 eC以下の反応温度で行われる請求項 1 9記載 の方法。
24. ボリエステル樹脂を主成分とする結着樹脂を含むトナーにお いて、 前記トナー中のアルデヒ ド化合物、 その分解生成物および副 成物の含有量が 200ρρπι以下であることを特徴とする トナー。
25. アルデヒ ド化合物、 その分解生成物および副成物の含有量が l OOppm以下である請求項 24記載の トナー。
26. アルデヒ ド化合物、 その分解生成物および副成物の含有量が 50 p pm 以下である請求項 24記載の トナー。
27. アルデヒ ド化合物、 その分解生成物および副成物の含有量が l O p pm 以下である請求項 24記載の トナー。
28. アルデヒ ド化合物、 その分解物または副成物の沸点が 1 80 °C 以下である請求項 24記載の トナー。
29. アルデヒ ド化合物、 その分解物または副成物の沸点が 1 00 て 以下である請求項 24記載の トナー。
30. アルデヒ ド化合物、 その分解物または副成物の沸点が 50て以 下である請求項 24記載の トナー。
31 . アルデヒ ド化合物、 その分解物または副成物が、 プロ ビオン アルデヒ ド、 ァセ トアルデヒ ドまたはジォキソラ ン化合物である請 求項 24記載の トナー。
PCT/JP1995/001395 1994-03-14 1995-07-12 Resine polyester pour un toner, procede de preparation de la resine et toner obtenu WO1996002870A1 (fr)