Classifications

• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F18/00—Homopolymers and copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by an acyloxy radical of a saturated carboxylic acid, of carbonic acid or of a haloformic acid
  • C08F18/02—Esters of monocarboxylic acids
  • C08F18/04—Vinyl esters
  • C08F18/10—Vinyl esters of monocarboxylic acids containing three or more carbon atoms
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F18/00—Homopolymers and copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by an acyloxy radical of a saturated carboxylic acid, of carbonic acid or of a haloformic acid
  • C08F18/02—Esters of monocarboxylic acids
  • C08F18/12—Esters of monocarboxylic acids with unsaturated alcohols containing three or more carbon atoms
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
  • C09J131/00—Adhesives based on homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by an acyloxy radical of a saturated carboxylic acid, of carbonic acid, or of a haloformic acid; Adhesives based on derivatives of such polymers
  • C09J131/02—Homopolymers or copolymers of esters of monocarboxylic acids
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
  • C09J133/00—Adhesives based on homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides, or nitriles thereof; Adhesives based on derivatives of such polymers
  • C09J133/04—Homopolymers or copolymers of esters
  • C09J133/06—Homopolymers or copolymers of esters of esters containing only carbon, hydrogen and oxygen, the oxygen atom being present only as part of the carboxyl radical
  • C09J133/08—Homopolymers or copolymers of acrylic acid esters
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L2205/00—Polymer mixtures characterised by other features
  • C08L2205/14—Polymer mixtures characterised by other features containing polymeric additives characterised by shape
  • C08L2205/18—Spheres
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L2205/00—Polymer mixtures characterised by other features
  • C08L2205/14—Polymer mixtures characterised by other features containing polymeric additives characterised by shape
  • C08L2205/18—Spheres
  • C08L2205/20—Hollow spheres
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
  • C09J2301/00—Additional features of adhesives in the form of films or foils
  • C09J2301/30—Additional features of adhesives in the form of films or foils characterized by the chemical, physicochemical or physical properties of the adhesive or the carrier
  • C09J2301/302—Additional features of adhesives in the form of films or foils characterized by the chemical, physicochemical or physical properties of the adhesive or the carrier the adhesive being pressure-sensitive, i.e. tacky at temperatures inferior to 30°C

Definitions

• This invention relates to tacky, polymeric, organic solvent-insoluble, elastomeric, pressure-sensitive adhesive microspheres, prepared from vinyl ester monomers, to processes for their preparation, and to their use as pressure-sensitive adhesives.
• Tacky, elastomeric microspheres are known to be useful in repositionable pressure-sensitive adhesive applications.
• the term "repositionable” refers to the ability to be repeatedly adhered to and removed from a substrate without substantial loss of adhesion capability.
• Microsphere-based adhesives are thought to perform well in such applications at least in part due to their "self-cleaning" character, wherein substrate contaminants tend to be pushed aside and trapped between the microspheres as the adhesive is applied. Upon removal, the adhesive can then still present a relatively uncontaminated surface for reapp cation to the substrate.
• Such solid, acrylate tacky microspheres are typically the suspension polymerization products of acrylate or methacrylate esters and free radically copolymerizable polar monomers. These polymerizations are performed in the presence of a variety of emulsifiers, surfactants, stabilizers and/or under particular process conditions which induce the formation and prevent the agglomeration of the spheres.
• Hollow, polymeric, acrylate, inherently tacky, infusible, solvent- insoluble, solvent-dispersible, elastomeric pressure-sensitive adhesive microspheres having diameters of at least about one micrometer have been described in U.S. Patent Nos. 5,045,569 (Delgado) and 4,988,567 (Delgado). Delgado teaches that small amounts of a high Tg vinyl ester such as vinyl acetate can be used in the composition provided that the resultant polymer has a Tg below -20 C.
• Preferred hollow microspheres contain one or more interior voids having diameters at least 10% of the hollow microspheres.
• the pressure-sensitive adhesives based on the hollow microspheres show reduced or even eliminated adhesive transfer in comparison with repositionable pressure-sensitive adhesives which are based on solid microspheres.
• the disclosed microspheres are useful as repositionable pressure-sensitive adhesives and in repositionable spray pressure-sensitive adhesive compositions.
• vinyl esters have found limited use in pressure- sensitive adhesive formulations.
• Examples of non-mi crosphere pressure-sensitive adhesives containing vinyl esters include U.S. Patent Nos. 3,751,449 (Gobran et al.); 4,296,017 (Eichelseder et al); and 3,519,587 (Bergmeister et al.).
• vinyl esters are not used due to their lack of availability, high cost and poor rate of reactivity and slow polymerization under free radical conditions when compared to acrylate, methacrylate and maleate esters.
• the polymers prepared therefrom are hydrolytically less stable than acrylic polymers. For these reasons vinyl esters have not been specifically utilized as major components in tacky, elastomeric microsphere compositions. Summary of the Invention
• tacky microspheres based upon different monomer systems.
• This invention provides tacky, polymeric, organic solvent- insoluble, elastomeric, vinyl ester containing pressure-sensitive adhesive microspheres typically having diameters of at least about one micrometer.
• the microspheres of the invention are organic solvent swellable. These microspheres are useful as repositionable pressure-sensitive adhesives.
• the present invention also provides pressure-sensitive adhesives comprising these microspheres. More specifically, these inherently tacky, polymeric, organic solvent-insoluble, elastomeric, pressure sensitive adhesive microspheres comprise: a (co)polymer having a Tg of less than about -IO C comprising the polymerization product of:
• the copolymer referred to above consists essentially of (a), (b), (c) and (d), and most preferably consists of (a), (b), (c), and (d).
• the pressure sensitive adhesive micropheres consist essentially of said aforementioned copolymers, most preferably consists of said aforementioned copolymers.
• microspheres of this invention which are hollow, microspheres of this invention which are solid, methods of making these microspheres, aqueous suspensions and solvent dispersions of these microspheres, spray repositionable pressure-sensitive adhesive compositions, and microsphere coated sheet materials.
• hollow, preferred hollow microspheres contain one or more interior voids having diameters at least 10% of the hollow microspheres.
• the microspheres of the invention have a glass transition temperature (Tg) of less than about -10°C, preferably about -100°C to about -20°C. If the glass transition temperature of the microspheres rises above -10°C, then the microspheres will have reduced tack and elasticity.
• Aqueous suspensions of hollow microspheres may be prepared by a two-step emulsification process comprising the steps of:
• Aqueous suspensions of hollow microspheres which may contain polar monomer(s) may also be prepared by a simpler ("one-step") emulsification process comprising the steps of:
• At least one emulsifier which is capable of forming a water-in-oil emulsion inside the droplets, the emulsion being substantially stable during emulsification and polymerization;
• Aqueous suspensions of hollow microspheres may also be prepared by a modification of the "one-step" emulsification process comprising the steps of: (a) forming droplets by mixing together
• At least one emulsifier which is capable of forming a water-in-oil emulsion inside the droplets, the emulsion being substantially stable during emulsification and polymerization, and
• Aqueous suspensions of solid microspheres may be prepared by an analogous "one-step” emulsification process comprising the steps of: (a) forming droplets by mixing together:
• Aqueous suspensions of solid microspheres may be prepared by a "one- step” emulsification process comprising the steps of: (a) forming droplets by mixing together:
• droplet means the liquid stage of the microspheres prior to the completion of polymerization.
• cavity means a space within the walls of a droplet or microsphere when still in the suspension or dispersion medium prior to drying, and thus containing whatever medium was used. 3.
• void means an empty space completely within the walls of a polymerized microsphere.
• the term "hollow” means containing at least one void or cavity.
• solid means not hollow; that is, void-free or cavity- free.
• elastomeric has been described, for example, as, “... applying to amorphous or non-crystalline materials that can be stretched to at least twice their original length and which will retract rapidly and forcibly to substantially their original dimensions upon release of the force.” [S.L. Rosen, Fundamental Principles of Polymeric materials. Wilev: New York, p. 314 (1982 ]
• organic solvent-insoluble in reference to a polymeric material refers to a polymeric material which is not totally dissolved on a molecular level in common organic solvents.
• solvent swellable in reference to a polymeric material refers to a polymeric material that swells in solvent to an extent larger than its original dimension and forms a dispersion consisting, substantially, of individual particles.
• Useful ester monomers are oleophilic, water emulsifiable, have restricted water solubility (less than about lg/per lOOg of water at 25°C), and as homopolymers, generally have glass transition temperatures below about - 10°C.
• Vinyl ester monomers useful according to the invention are those of the general formula:
• R s selected from the group consisting of linear or branched alkyl groups having 1 to 12 carbon atoms.
• vinyl esters include but are not limited to those selected from the group consisting of vinyl 2-ethylhexanoate, vinyl caprate, vinyl laurate, vinyl pelargonate, vinyl hexanoate, vinyl propionate, vinyl decanoate, vinyl octanoate, and other monofunctional unsaturated vinyl esters of linear or branched carboxylic acids comprising 3 to 14 carbon atoms which as homopolymers have glass transition temperatures below about -10°C.
• Preferred vinyl ester monomers include those selected from the group consisting of vinyl laurate, vinyl caprate, vinyl-2-ethylhexanoate, and mixtures thereof.
• cycloaliphatic- and phenyalkyl-substituted vinyl esters such as those described in U.S. Patent No. 3,751,449 (Gobran et al.) having the formula set forth immediately below, can also be used in the microspheres of the present invention.
• CH 2 CH-O-C-CH-R 3 where R 2 is a cycloaliphatic or aromatic group (e.g., phenyl), and
• R3 is a hydrogen atom or lower alkyl (e.g., with 1 to 6 carbon atoms).
• the free radically polymerizable polar monomers useful in the present invention are both somewhat oil-soluble and water-soluble, resulting in a distribution of the polar monomer between the aqueous and the oil phases.
• Suitable polar monomers include but are not limited to those selected from the group consisting of acrylic acid, methacrylic acid, itaconic acid, crotonic acid, maleic acid, fumaric acid, sulfoethyl methacrylate, N-vinyl pyrrolidone, N-vinyl caprolactam, 2-vinyl-4,4-dimethyl-2-oxazolidinone, t-butyl acrylamide, dimethyl amino ethyl acrylamide, N-octyl acrylamide, and ionic monomers such as sodium methacrylate, ammonium acrylate, sodium acrylate, trimethylamine p-vinyl benzimide, 4,4,9-trimethyl-4-azonia-7-oxo-8-oxa-dec-9-ene-l-sulphonate, N,N-dimethyl-N-(beta-methacryloxy-ethyl) ammonium propionate betaine, trimethylamine meth
• Preferred polar monomers include those selected from the group consisting of monoolefinic monocarboxylic acids, monoolefinic dicarboxylic acids, acrylamides, N-substituted acrylamides, salts thereof, and mixtures thereof.
• Examples of such preferred polar monomers include but are not limited to those selected from the group consisting of acrylic acid, sodium acrylate, N-vinyl pyrrolidone, and mixtures thereof.
• Free radically polymerizable nonpolar vinyl monomers which, as homopolymers, have glass transition temperatures higher than about -10°C, e.g., tert-butyl acrylate, isobornyl acrylate, butyl methacrylate, vinyl acetate, acrylonitrile, mixtures thereof, and the like, may optionally be utilized in conjunction with one or more of the vinyl ester monomers provided that the glass transition temperature of the resultant copolymer is below about -10°C.
• alkyl acrylate and methacrylate monomers are useful in preparing the microspheres and pressure-sensitive adhesives of this invention.
• alkyl acrylate and methacrylate monomers are those monofunctional unsaturated acrylate and methacrylate esters of non-tertiary alkyl alcohols, the alkyl groups of which preferably have from about 4 to about 14 carbon atoms.
• Such monomers include but are not limited to those selected from the group consisting of isooctyl acrylate, 4-methyl-2-pentyl acrylate, 2-methylbutyl acrylate, isoamyl acrylate, sec-butyl acrylate, n-butyl acrylate, 2-ethylhexyl acrylate, isodecyl methacrylate, isononyl acrylate, isodecyl acrylate, and mixtures thereof.
• Prefe ⁇ ed acrylate monomers include those selected from the group consisting of isooctyl acrylate, isononyl acrylate, isoamyl acrylate, isodecyl acrylate, 2-ethylhexyl acrylate, n-butyl acrylate, sec-butyl acrylate, and mixtures thereof.
• microspheres of this invention and the pressure-sensitive adhesives made therefrom comprise a copolymer comprising about 50 to about 100 percent by weight of at least one free radically polymerizable vinyl ester monomer; optionally, about 0 to about 20 percent by weight of one or more polar monomers, (typically about 0.1 to about 20 percent, if included); and optionally about 0 to about 50 weight percent of a nonpolar free radically copolymerizable vinyl monomer (typically about 0.1 to about 50 percent by weight, if included), based upon the total weight of the copolymer.
• the pressure-sensitive adhesive microspheres comprise a copolymer comprising about 60 to about 100 percent by weight of free radically polymerizable vinyl ester monomer; optionally, about 0 to about 15 percent by weight of at least one polar monomer (typically about 0.1 to about 15 percent, if included); and optionally about 0 to about 30 weight of nonpolar free radically copolymerizable vinyl monomer (typically about 0.1 to about 30 percent, if included) based upon the total weight of the copolymer.
• polar monomer typically about 0.1 to about 15 percent, if included
• nonpolar free radically copolymerizable vinyl monomer typically about 0.1 to about 30 percent, if included
• the pressure-sensitive adhesive microspheres comprise a copolymer comprising about 70 to about 100 percent by weight of free radically polymerizable vinyl ester monomer; optionally about 0 to about 10 percent by weight of polar monomer (typically about 0.1 to about 10 percent by weight, if included), and optionally about 0 to about 20 percent (typically about 0.1 to about 20 percent by weight, if included) by weight of nonpolar free radically copolymerizable vinyl monomer, based upon the total weight of the copolymer.
• polar monomer typically about 0.1 to about 10 percent by weight, if included
• nonpolar free radically copolymerizable vinyl monomer typically about 0.1 to about 20 percent by weight, if included
• microspheres may also be prepared using free radically polymerizable vinyl ester monomer(s) alone or without a polar monomer in combination only with other free radically polymerizable nonpolar vinyl monomers, such as isooctyl acrylate, vinyl acetate, etc. Most preferably, at least about 1 percent to about 10 percent by weight polar monomer is included as this ratio provides microspheres with balanced pressure-sensitive adhesive properties.
• Aqueous suspensions of the hollow microspheres of the invention may be prepared by a "two-step" emulsification process which first involves forming a water-in-oil emulsion of an aqueous solution of water and, if used, polar monomer(s), in the oil phase monomer (i.e., at least vinyl ester monomer and optional nonpolar monomer), using an emulsifier having a low hydrophilic-lipophilic balance (HLB) value. Where it is desirable not to include a polar monomer, an aqueous phase may be mixed directly with the oil phase monomer (i.e., vinyl ester monomer and optional nonpolar monomer), and emulsifier to form the water-in-oil emulsion.
• polar monomer(s) i.e., at least vinyl ester monomer and optional nonpolar monomer
• HLB hydrophilic-lipophilic balance
• the hollow morphology of the microspheres of the invention can be determined through the choice of emulsifiers used in this "two-step" process.
• Suitable emulsifiers for the use in the first step of the two step preparation of hollow microspheres are those having HLB values below about 7, preferably in the range of about 2 to about 7.
• examples of such emulsifiers include but are not limited to those selected from the group consisting of sorbitan monooleate, sorbitan trioleate, ethoxylated oleyl alcohol (such as Brij 93, available from Atlas Chemical Industries, Inc.), and mixtures thereof.
• oil phase monomer(s), emulsifier, a free radical initiator, and optional crosslinking monomer or monomers as defined below are combined, and an aqueous solution comprising water and, if used, polar monomer(s) is agitated and poured into the oil phase mixture to form a water-in-oil emulsion.
• a thickening agent, such as methyl cellulose, may also be included in the aqueous phase of the water-in-oil emulsion.
• a water-in-oil-in-water emulsion is formed by dispersing the water-in-oil emulsion of the first step into an aqueous phase containing an emulsifier having an HLB value above about 6.
• emulsifiers include but are not limited to those selected from the group consisting of ethoxylated sorbitan monooleate, ethoxylated lauryl alcohol, alkyl sulfates, and mixtures thereof.
• critical micelle concentration which is herein defined as the minimum concentration of emulsifier necessary for the formation of micelles, i.e., submicroscopic aggregations of emulsifier molecules.
• Critical micelle concentration is slightly different for each emulsifier, usable concentrations ranging from about 1.0 x 10" ⁇ to about 3.0 moles/liter.
• the final process step of the method of the invention involves the application of heat or radiation (such as ultraviolet radiation, etc.) to initiate polymerization of the monomers.
• heat or radiation such as ultraviolet radiation, etc.
• Aqueous suspensions of hollow microspheres which may contain polar monomer(s) may also be prepared by a "one-step" emulsification process comprising aqueous suspension polymerization of at least one vinyl ester monomer and optional nonpolar monomer and, optionally, at least one polar monomer in the presence of at least one emulsifier capable of producing a water-in-oil emulsion inside the droplets which is substantially stable during emulsification and polymerization.
• the emulsifier is utilized in concentrations greater than its critical micelle concentration.
• emulsifiers formulated at this concentration will produce stable cavity-containing droplets during the polymerization, and are suitable for use in this one-step process.
• emulsifiers include but are not limited to those selected from the group consisting of alkylarylether sulfates such as sodium alkylarylether sulfate, e.g., Triton W/30, available from Rohm and Haas; alkylarylpolyether sulfates such as alkylarylpoly(ethylene oxide) sulfates; alkyl sulfates such as sodium lauryl sulfate, ammonium lauryl sulfate, triethanolamine lauryl sulfate, and sodium hexadecyl sulfate; alkyl ether sulfates such as ammonium lauryl ether sulfate, and alkylpolyether sulfates such as alkyl poly(ethylene oxide) sulfates; alkylarylether
• Emulsifiers selected from the group consisting of alkyl sulfates, alkyl ether sulfates, alkylarylether sulfates, and mixtures thereof are preferred as they provide a maximum void volume per microsphere for a minimum amount of surfactant.
• Nonionic emulsifiers e.g. Siponic Y-500-70 (ethoxylated oleyl alcohol, commercially available from Alcolac, Inc.) and Pluronic PI 03 (block copolymer of polypropylene oxide and polyethylene oxide commercially available form BASF Corporation), can also be utilized alone or in conjunction with anionic emulsifiers, and mixtures thereof.
• Polymeric stabilizers may also be present but are not necessary.
• Aqueous suspensions of solid microspheres may be prepared by a
• one-step emulsification process comprising an aqueous suspension polymerization of at least one vinyl ester monomer; at least one polymeric stabilizer, such as poly(vinyl alcohol); optionally, at least one polar monomer; optionally, at least one nonpolar monomer, and/or optionally a crosslinking monomer. It is believed that other polymeric stabilizers, such as those described in U.S. Patent No.
• 4,166,152 (Baker et al.) (e.g., carboxy-modified polyacrylamides, carboxy-modified celluloses, quaternary amine-substituted celluloses, etc.), and other steric or electrosteric polymeric stabilizers, including but not limited to those selected from the group consisting of polyoxyethylene, polyacrylic acid, polymethacrylic acid, polyacrylamide, polyvinyl pyrrolidone, polyethylene imine, polyvinyl methyl ether, salts thereof, and mixtures thereof, would also be useful according to the present invention.
• steric or electrosteric polymeric stabilizers including but not limited to those selected from the group consisting of polyoxyethylene, polyacrylic acid, polymethacrylic acid, polyacrylamide, polyvinyl pyrrolidone, polyethylene imine, polyvinyl methyl ether, salts thereof, and mixtures thereof, would also be useful according to the present invention.
• aqueous suspension of solid microspheres not incorporating any polar monomer may be prepared by a similar "one-step" emulsification process which incorporates emulsifiers having HLB values lower than about 25 rather than polymeric stabilizers in the formation of these microspheres.
• emulsifiers having HLB values lower than 25 include but are not limited to those selected from the group consisting of alkylarylpolyether sulfonates such as alkylarylpoly (ethylene oxide) sodium sulfonate ⁇ -200, commericially available from the Rohm and Haas Co.); alkyl benzene sulfonates such as sodium p- dodecylbenzene sulfonate (e.g., PolystepTM Biosoft LAS-50, commericially available from Alcolac, Inc.); alkyl sulfosuccinates, such as Aerosol ⁇ M OT, a dioctyl ester of sodium sulfosuccinic acid commercially available from American Cyanamid Process Chemicals Dep ; and mixtures thereof.
• alkylarylpolyether sulfonates such as alkylarylpoly (ethylene oxide) sodium sulfonate ⁇ -200, commericially available from the Rohm and
• All of these preparative methods may be modified by withholding the addition of all or part, if used, of the polar monomer(s) and/or nonpolar monomer(s), if used, and/or multifunctional crosslinking agent, if used, until after polymerization of the water-in-oil-in-water emulsion is initiated. This may be done provided that the withheld components are added to the polymerizing mixture prior to its 100% conversion of monomers to polymer in the emulsion.
• This processing flexibility allows the formulator to add any portion of the optional polar monomer(s) and/or optional free radically polymerizable vinyl monomers and/or any portion of the multifunctional crosslinking agent at any convenient point in preparing the pressure-sensitive adhesive microspheres of this invention.
• Suitable initiators are those which are normally suitable for free radical polymerization of free radically polymerizable monomers and which are oil-soluble and of very low solubility in water (i.e., typically less than about 1 g per lOOg of water at 20°C).
• examples of such initiators include but are not limited to those selected from the group consisting of thermally-activated initiators such as azo compounds, hydroperoxides, peroxides, and the like, and photoinitiators such as benzophenone, benzoin ethyl ether, and 2,2-dimethoxy-2-phenyl acetophenone, and the like, and mixtures thereof.
• Use of a water-soluble polymerization initiator causes formation of substantial amounts of latex.
• the initiator is generally used in an amount ranging from about 0.01 percent up to about 10 percent by weight of the total polymerizable composition (i.e., monomers, and optional crosslinking agent), preferably up to about 5 percent.
• composition from which the microspheres of the invention are made may also contain a multifunctional crosslinking agent.
• multifunctional refers to crosslinking agents which possess two or more free radically polymerizable ethylenically unsaturated groups.
• Useful multifunctional crosslinking agents include but are not limited to those selected from the group consisting of acrylic or methacrylic esters of diols such as butanediol diacrylate, triols such as glycerol, and tetrols such as pentaerythritol.
• crosslinking agents include but are not limited to those selected from the group consisting of polyvinylic crosslinking agents, such as substituted and unsubstituted divinylbenzene; and difunctional urethane acrylates, such as Ebecryl 270 and Ebecryl 230 (1500 weight average molecular weight and 5000 weight average molecular weight acrylated urethanes, respectively - both available from Radcure Specialties), and mixtures thereof.
• crosslinker(s) is (are) added at a level of up to about 0.15 equivalent weight %, preferably up to about 0.1 equivalent weight %, of the total polymerizable composition (i.e. monomers plus optional crosslinking agent).
• the "equivalent weight %" of a given compound is defined as the number of equivalents of that compound divided by the total number of equivalents in the total composition, wherein an equivalent is the number of grams divided by the equivalent weight.
• the equivalent weight is defined as the molecular weight divided by the number of polymerizable groups in the monomer (in the case of those monomers with only one polymerizable group, equivalent weight - molecular weight).
• the crosslinker can be added to any phase at any time before 100% conversion. Preferably it is added before initiation occurs. Crosslinking can alternatively occur via exposure to an appropriate radiation source, such as gamma or electron beam radiation.
• microsphere Diameter The microspheres of the invention are normally tacky, elastomeric, organic solvent-insoluble but swellable in organic solvents, and small, typically having diameters of at least about 1 micrometer, preferably in the range of about 1 to about 300 micrometers.
• the voids typically range in size up to about 100 micrometers or larger.
• an aqueous suspension of the hollow or solid microspheres is obtained which is stable to agglomeration or coagulation under room temperature conditions (i.e., about 20 to about 25°C).
• the suspension may have a non-volatile solids contents of from about 10 to about 50 percent by weight.
• the suspension Upon prolonged standing, the suspension separates into two phases, one phase being aqueous and substantially free of polymer, the other phase being an aqueous suspension of microspheres. Both phases may contain a minor portion of submicron latex particles. Decantation of the microsphere-rich phase provides an aqueous suspension having a non-volatile solids content on the order of about 40 to about 50 percent which, if shaken with water, will readily redisperse.
• the aqueous suspension of microspheres may be utilized immediately following polymerization to provide inherently tacky pressure-sensitive adhesive coatings.
• the suspension may be coated on suitable flexible or inflexible backing materials by conventional coating techniques such as knife coating or Meyer bar coating or use of an extrusion die.
• Solvent dispersions of the microspheres may also be coated on suitable backing materials by conventional coating techniques, as described above for aqueous suspensions.
• suitable backing materials for the aqueous or solvent based coatings include but are not limited to those selected from the group consisting of paper, plastic films, cellulose acetate, ethyl cellulose, woven or nonwoven fabric formed of synthetic or natural materials, metal, metallized polymeric film, ceramic sheet material, and the like. Primers or binders may be used thereon.
• Suspensions or dispersions of the microspheres in a liquid medium may be sprayed by conventional techniques without cobwebbing or may be incorporated in aerosol containers with suitable propellants including but not limited to those selected from the groups consisting of alkanes, alkenes, chlorofluorocarbons, e.g., Freon halocarbon propellents (commercially available from E.I. du Pont de Nemours & Co., Inc.), and mixtures thereof.
• suitable propellants including but not limited to those selected from the groups consisting of alkanes, alkenes, chlorofluorocarbons, e.g., Freon halocarbon propellents (commercially available from E.I. du Pont de Nemours & Co., Inc.), and mixtures thereof.
• Useful aerosol formulae have a solids content of from about 5% to about 20%, preferably from about 10% to about 16%.
• the pressure-sensitive adhesive properties of the microspheres may be altered by addition of tackifying resin and/or plasticizer. It is also within the scope of this invention to include various other components, such as pigments, neutralizing agents such as sodium hydroxide, etc., fillers, stabilizers, or various polymeric additives.
• the pressure-sensitive adhesive of the invention consists essentially of the microspheres of the invention, more preferably consists of the microspheres of the invention. Test Methods Tack
• the tack of sheets coated with the microspheres of the invention was measured with a Polyken Probe Tack tester (available from Kendall Company) according to American Society for Testing and Materials Test Method ASTM
• Microspheres of the current invention were coated onto 1.5 mil primed polyester film, yielding a dried adhesive coating thickness of 1 to 2 mils. After cleaning the probe with ethyl acetate using a lint-free cloth, a 2 cm x 2 cm sample of the adhesive coated sheet was placed on the annular ring weight of the Polyken apparatus. The tack was then measured and recorded using a 10 mm stainless steel probe having a diameter of 0.4975 cm with a speed of 0.5 cm/second and dwell time of 1 second.
• Glass Transition Temperature (Tg) Glass transition temperatures were measured using Differential Scanning
• Biosoft Polystep Biosoft LAS-50 sodium dodecyl benzene sulfonate available from Stepan Co.
• Siponate Siponate DS 10 sodium p-dodecylbenzene sulfonate available from Alcolac, Inc.
• Vinol 205 VinolTM 205, polyvinyl alcohol available from
• Microspheres consisting of a predominance (i.e. at least about 50 percent by weight) of at least one free radically polymerizable vinyl ester were prepared and examined for tack, diameter, Tg and morphology.
• Example 1 In a one-liter resin reactor equipped with mechanical sti ⁇ er and inlet- outlet lines for vacuum and argon, 450 grams of distilled and deionized water and 6.0 grams of Standapol ⁇ M A (Ammonium lauryl sulfate from Henkel AG) were charged and heated to 65°C. Next, 0.71 gram of LucidolTM-70 (70% benzoyl peroxide commercially available from Atochem North America, Inc.) was dissolved in a mixture of 144 grams of vinyl laurate, 6.0 grams of acrylic acid, and 0.04 gram of 1-4 butanediol diacrylate. When the Lucidol -70 was dissolved, the monomer mixture was added to the reactor while stirring at 400 RPM.
• Standapol ⁇ M A Ammonium lauryl sulfate from Henkel AG
• Example 3 The following example illustrates the preparation of hollow tacky microspheres using a two step emulsification method:
• Standapol *- A 0.75 gram of Standapol *- A was dissolved in 150 grams of distilled and deionized water and charged into a one-liter glass reactor equipped with a mechanical stirrer and inlet-outlet lines for vacuum and argon.
• a water-in-oil emulsion was prepared in an Omni mixer by stirring 75 grams of distilled and deionized water with
• Example 4 a polymeric stabilizer was used.
• Example 5 a solid microsphere which did not incorporate polar monomer was made using a surfactant with an HLB less than 25.
• Example 4 In a one-liter glass reactor equipped with a mechanical sti ⁇ er and inlet- outlet lines for vacuum and argon, 3 grams of Vinol ⁇ M 350 (polyvinyl alcohol available from Air Products) were dissolved in 225 grams of distilled and deionized water. The reactor was heated to 75 °C, its atmosphere evacuated by applying vacuum and refilling with argon. When the temperature of the reactor reached 75°C, a mixture of 75 grams of VynateTM-2EH and 0.36 grams of LucidoH- ⁇ 70 were added. The agitation was set at 400 RPM.
• the reactor temperature was maintained at 75 °C for 22 hours. An argon purge was maintained during the polymerization. After this time period the suspension was allowed to cool down to room temperature. The reactor was emptied and the suspension filtered. Optical microscopy showed solid microspheres of about 90 microns in diameter.
• Examples 6 to 10 The following examples, made in accordance with Example 1 and in the proportions stated in Table 1, illustrate the preparation of different tacky microspheres. In all cases 225.0 grams of distilled and deionized water was used in the recipe. All polymerizations were carried out at 75°C.
• Example 12 illustrates the preparation of solid tacky microspheres using an alternative polymeric stabilizer (Example 12) and a polar monomer and an alternative polymeric stablilizer (Example 11).
• Vinol 350 and Vinol 205 are polymeric stabilizers.

Landscapes

• Chemical & Material Sciences (AREA)
• Organic Chemistry (AREA)
• Health & Medical Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Medicinal Chemistry (AREA)
• Polymers & Plastics (AREA)
• Adhesives Or Adhesive Processes (AREA)
• Manufacturing Of Micro-Capsules (AREA)
• Addition Polymer Or Copolymer, Post-Treatments, Or Chemical Modifications (AREA)

Applications Claiming Priority (2)

Publications (1)

Family

ID=23029564

Family Applications (2)

Family Applications After (1)

Country Status (4)

Cited By (6)

Families Citing this family (3)

Citations (4)

• 1995
  • 1995-06-29 WO PCT/US1995/008139 patent/WO1996001280A1/en active Application Filing
  • 1995-06-30 CA CA002191752A patent/CA2191752A1/en not_active Abandoned
  • 1995-06-30 JP JP8503923A patent/JPH10502410A/ja active Pending
  • 1995-06-30 WO PCT/US1995/008215 patent/WO1996001281A1/en not_active Application Discontinuation
  • 1995-06-30 EP EP95925382A patent/EP0769029A1/en not_active Withdrawn

Patent Citations (4)

Non-Patent Citations (1)

Also Published As

Similar Documents

Legal Events