US20240071661A1 - Low-Magnetostrictive Oriented Silicon Steel and Manufacturing Method Therefor - Google Patents
Low-Magnetostrictive Oriented Silicon Steel and Manufacturing Method Therefor Download PDFInfo
- Publication number
- US20240071661A1 US20240071661A1 US18/259,898 US202218259898A US2024071661A1 US 20240071661 A1 US20240071661 A1 US 20240071661A1 US 202218259898 A US202218259898 A US 202218259898A US 2024071661 A1 US2024071661 A1 US 2024071661A1
- Authority
- US
- United States
- Prior art keywords
- silicon steel
- manufacturing
- difference
- amount
- steel substrate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Links
- 229910000976 Electrical steel Inorganic materials 0.000 title claims abstract description 115
- 238000004519 manufacturing process Methods 0.000 title claims abstract description 35
- 238000000576 coating method Methods 0.000 claims abstract description 93
- 239000000758 substrate Substances 0.000 claims abstract description 54
- 239000011248 coating agent Substances 0.000 claims abstract description 46
- 238000010329 laser etching Methods 0.000 claims abstract description 37
- 238000000137 annealing Methods 0.000 claims description 27
- 238000001816 cooling Methods 0.000 claims description 24
- 238000010438 heat treatment Methods 0.000 claims description 11
- 238000000034 method Methods 0.000 claims description 11
- 238000005097 cold rolling Methods 0.000 claims description 10
- WGLPBDUCMAPZCE-UHFFFAOYSA-N Trioxochromium Chemical compound O=[Cr](=O)=O WGLPBDUCMAPZCE-UHFFFAOYSA-N 0.000 claims description 8
- VYPSYNLAJGMNEJ-UHFFFAOYSA-N Silicium dioxide Chemical compound O=[Si]=O VYPSYNLAJGMNEJ-UHFFFAOYSA-N 0.000 claims description 5
- 239000012535 impurity Substances 0.000 claims description 5
- GNFTZDOKVXKIBK-UHFFFAOYSA-N 3-(2-methoxyethoxy)benzohydrazide Chemical compound COCCOC1=CC=CC(C(=O)NN)=C1 GNFTZDOKVXKIBK-UHFFFAOYSA-N 0.000 claims description 4
- FGUUSXIOTUKUDN-IBGZPJMESA-N C1(=CC=CC=C1)N1C2=C(NC([C@H](C1)NC=1OC(=NN=1)C1=CC=CC=C1)=O)C=CC=C2 Chemical compound C1(=CC=CC=C1)N1C2=C(NC([C@H](C1)NC=1OC(=NN=1)C1=CC=CC=C1)=O)C=CC=C2 FGUUSXIOTUKUDN-IBGZPJMESA-N 0.000 claims description 4
- 238000003723 Smelting Methods 0.000 claims description 4
- 238000005266 casting Methods 0.000 claims description 4
- 239000003795 chemical substances by application Substances 0.000 claims description 4
- 238000005261 decarburization Methods 0.000 claims description 4
- 238000002955 isolation Methods 0.000 claims description 4
- XLYOFNOQVPJJNP-UHFFFAOYSA-N water Substances O XLYOFNOQVPJJNP-UHFFFAOYSA-N 0.000 claims description 4
- 229940075614 colloidal silicon dioxide Drugs 0.000 claims description 3
- RGPUVZXXZFNFBF-UHFFFAOYSA-K diphosphonooxyalumanyl dihydrogen phosphate Chemical compound [Al+3].OP(O)([O-])=O.OP(O)([O-])=O.OP(O)([O-])=O RGPUVZXXZFNFBF-UHFFFAOYSA-K 0.000 claims description 3
- QQFLQYOOQVLGTQ-UHFFFAOYSA-L magnesium;dihydrogen phosphate Chemical compound [Mg+2].OP(O)([O-])=O.OP(O)([O-])=O QQFLQYOOQVLGTQ-UHFFFAOYSA-L 0.000 claims description 3
- 229910000401 monomagnesium phosphate Inorganic materials 0.000 claims description 3
- 235000019785 monomagnesium phosphate Nutrition 0.000 claims description 3
- 238000001953 recrystallisation Methods 0.000 claims description 3
- 238000005245 sintering Methods 0.000 claims description 3
- XEEYBQQBJWHFJM-UHFFFAOYSA-N Iron Chemical group [Fe] XEEYBQQBJWHFJM-UHFFFAOYSA-N 0.000 abstract description 18
- 230000000052 comparative effect Effects 0.000 description 55
- 229910000831 Steel Inorganic materials 0.000 description 34
- 239000010959 steel Substances 0.000 description 34
- 239000000243 solution Substances 0.000 description 13
- 230000005381 magnetic domain Effects 0.000 description 7
- 238000005530 etching Methods 0.000 description 4
- 229910052839 forsterite Inorganic materials 0.000 description 4
- 229910052742 iron Inorganic materials 0.000 description 4
- HCWCAKKEBCNQJP-UHFFFAOYSA-N magnesium orthosilicate Chemical compound [Mg+2].[Mg+2].[O-][Si]([O-])([O-])[O-] HCWCAKKEBCNQJP-UHFFFAOYSA-N 0.000 description 4
- 230000005415 magnetization Effects 0.000 description 4
- 239000000126 substance Substances 0.000 description 4
- 229910001224 Grain-oriented electrical steel Inorganic materials 0.000 description 3
- 230000008859 change Effects 0.000 description 3
- 238000009826 distribution Methods 0.000 description 3
- 230000005284 excitation Effects 0.000 description 3
- 239000000463 material Substances 0.000 description 3
- 239000000203 mixture Substances 0.000 description 3
- 230000009467 reduction Effects 0.000 description 3
- 238000005096 rolling process Methods 0.000 description 3
- 238000012360 testing method Methods 0.000 description 3
- UFHFLCQGNIYNRP-UHFFFAOYSA-N Hydrogen Chemical compound [H][H] UFHFLCQGNIYNRP-UHFFFAOYSA-N 0.000 description 2
- 230000001133 acceleration Effects 0.000 description 2
- 239000013078 crystal Substances 0.000 description 2
- 230000007423 decrease Effects 0.000 description 2
- 230000007547 defect Effects 0.000 description 2
- 238000013461 design Methods 0.000 description 2
- 238000010894 electron beam technology Methods 0.000 description 2
- 230000001678 irradiating effect Effects 0.000 description 2
- 238000005457 optimization Methods 0.000 description 2
- 230000008569 process Effects 0.000 description 2
- 238000007670 refining Methods 0.000 description 2
- OHVLMTFVQDZYHP-UHFFFAOYSA-N 1-(2,4,6,7-tetrahydrotriazolo[4,5-c]pyridin-5-yl)-2-[4-[2-[[3-(trifluoromethoxy)phenyl]methylamino]pyrimidin-5-yl]piperazin-1-yl]ethanone Chemical compound N1N=NC=2CN(CCC=21)C(CN1CCN(CC1)C=1C=NC(=NC=1)NCC1=CC(=CC=C1)OC(F)(F)F)=O OHVLMTFVQDZYHP-UHFFFAOYSA-N 0.000 description 1
- AFCARXCZXQIEQB-UHFFFAOYSA-N N-[3-oxo-3-(2,4,6,7-tetrahydrotriazolo[4,5-c]pyridin-5-yl)propyl]-2-[[3-(trifluoromethoxy)phenyl]methylamino]pyrimidine-5-carboxamide Chemical compound O=C(CCNC(=O)C=1C=NC(=NC=1)NCC1=CC(=CC=C1)OC(F)(F)F)N1CC2=C(CC1)NN=N2 AFCARXCZXQIEQB-UHFFFAOYSA-N 0.000 description 1
- 229910019142 PO4 Inorganic materials 0.000 description 1
- XUIMIQQOPSSXEZ-UHFFFAOYSA-N Silicon Chemical compound [Si] XUIMIQQOPSSXEZ-UHFFFAOYSA-N 0.000 description 1
- 229910052782 aluminium Inorganic materials 0.000 description 1
- SNAAJJQQZSMGQD-UHFFFAOYSA-N aluminum magnesium Chemical compound [Mg].[Al] SNAAJJQQZSMGQD-UHFFFAOYSA-N 0.000 description 1
- 150000008064 anhydrides Chemical class 0.000 description 1
- 239000007864 aqueous solution Substances 0.000 description 1
- 238000005452 bending Methods 0.000 description 1
- 230000009286 beneficial effect Effects 0.000 description 1
- 229910052729 chemical element Inorganic materials 0.000 description 1
- 239000008199 coating composition Substances 0.000 description 1
- 229910052681 coesite Inorganic materials 0.000 description 1
- 229910052906 cristobalite Inorganic materials 0.000 description 1
- 238000001514 detection method Methods 0.000 description 1
- 230000000694 effects Effects 0.000 description 1
- 238000005098 hot rolling Methods 0.000 description 1
- 230000006872 improvement Effects 0.000 description 1
- 238000009413 insulation Methods 0.000 description 1
- 229910052749 magnesium Inorganic materials 0.000 description 1
- 239000011777 magnesium Substances 0.000 description 1
- 239000000395 magnesium oxide Substances 0.000 description 1
- CPLXHLVBOLITMK-UHFFFAOYSA-N magnesium oxide Inorganic materials [Mg]=O CPLXHLVBOLITMK-UHFFFAOYSA-N 0.000 description 1
- AXZKOIWUVFPNLO-UHFFFAOYSA-N magnesium;oxygen(2-) Chemical compound [O-2].[Mg+2] AXZKOIWUVFPNLO-UHFFFAOYSA-N 0.000 description 1
- 238000000691 measurement method Methods 0.000 description 1
- 230000007246 mechanism Effects 0.000 description 1
- 238000012986 modification Methods 0.000 description 1
- 230000004048 modification Effects 0.000 description 1
- 238000011056 performance test Methods 0.000 description 1
- 230000000737 periodic effect Effects 0.000 description 1
- 235000021317 phosphate Nutrition 0.000 description 1
- 150000003013 phosphoric acid derivatives Chemical class 0.000 description 1
- 238000005554 pickling Methods 0.000 description 1
- QVLTXCYWHPZMCA-UHFFFAOYSA-N po4-po4 Chemical compound OP(O)(O)=O.OP(O)(O)=O QVLTXCYWHPZMCA-UHFFFAOYSA-N 0.000 description 1
- 239000000843 powder Substances 0.000 description 1
- 238000002360 preparation method Methods 0.000 description 1
- 238000012545 processing Methods 0.000 description 1
- 230000035945 sensitivity Effects 0.000 description 1
- 238000010008 shearing Methods 0.000 description 1
- 229910052710 silicon Inorganic materials 0.000 description 1
- 239000010703 silicon Substances 0.000 description 1
- 239000000377 silicon dioxide Substances 0.000 description 1
- 229910052682 stishovite Inorganic materials 0.000 description 1
- 238000006467 substitution reaction Methods 0.000 description 1
- 229910052905 tridymite Inorganic materials 0.000 description 1
Images
Classifications
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01F—MAGNETS; INDUCTANCES; TRANSFORMERS; SELECTION OF MATERIALS FOR THEIR MAGNETIC PROPERTIES
- H01F1/00—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties
- H01F1/01—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials
- H01F1/03—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity
- H01F1/12—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity of soft-magnetic materials
- H01F1/14—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity of soft-magnetic materials metals or alloys
- H01F1/16—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity of soft-magnetic materials metals or alloys in the form of sheets
- H01F1/18—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity of soft-magnetic materials metals or alloys in the form of sheets with insulating coating
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
- C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
- C21D1/26—Methods of annealing
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
- B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
- B23K26/00—Working by laser beam, e.g. welding, cutting or boring
- B23K26/0093—Working by laser beam, e.g. welding, cutting or boring combined with mechanical machining or metal-working covered by other subclasses than B23K
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
- B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
- B23K26/00—Working by laser beam, e.g. welding, cutting or boring
- B23K26/70—Auxiliary operations or equipment
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
- C21D1/18—Hardening; Quenching with or without subsequent tempering
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
- C21D1/26—Methods of annealing
- C21D1/28—Normalising
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
- C21D1/68—Temporary coatings or embedding materials applied before or during heat treatment
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
- C21D1/84—Controlled slow cooling
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D6/00—Heat treatment of ferrous alloys
- C21D6/005—Heat treatment of ferrous alloys containing Mn
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D6/00—Heat treatment of ferrous alloys
- C21D6/008—Heat treatment of ferrous alloys containing Si
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/12—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties
- C21D8/1216—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties the working step(s) being of interest
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/12—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties
- C21D8/1216—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties the working step(s) being of interest
- C21D8/1222—Hot rolling
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/12—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties
- C21D8/1216—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties the working step(s) being of interest
- C21D8/1233—Cold rolling
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/12—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties
- C21D8/1244—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties the heat treatment(s) being of interest
- C21D8/125—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties the heat treatment(s) being of interest with application of tension
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/12—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties
- C21D8/1244—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties the heat treatment(s) being of interest
- C21D8/1255—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties the heat treatment(s) being of interest with diffusion of elements, e.g. decarburising, nitriding
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/12—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties
- C21D8/1244—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties the heat treatment(s) being of interest
- C21D8/1261—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties the heat treatment(s) being of interest following hot rolling
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/12—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties
- C21D8/1244—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties the heat treatment(s) being of interest
- C21D8/1266—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties the heat treatment(s) being of interest between cold rolling steps
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/12—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties
- C21D8/1244—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties the heat treatment(s) being of interest
- C21D8/1272—Final recrystallisation annealing
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/12—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties
- C21D8/1277—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties involving a particular surface treatment
- C21D8/1283—Application of a separating or insulating coating
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/12—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties
- C21D8/1294—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties involving a localized treatment
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
- C21D9/0081—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for slabs; for billets
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
- C21D9/52—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for wires; for strips ; for rods of unlimited length
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/001—Ferrous alloys, e.g. steel alloys containing N
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
- B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
- B23K2103/00—Materials to be soldered, welded or cut
- B23K2103/02—Iron or ferrous alloys
- B23K2103/04—Steel or steel alloys
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
- B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
- B23K26/00—Working by laser beam, e.g. welding, cutting or boring
- B23K26/36—Removing material
- B23K26/362—Laser etching
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D2201/00—Treatment for obtaining particular effects
- C21D2201/05—Grain orientation
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C2202/00—Physical properties
- C22C2202/02—Magnetic
Definitions
- the present invention relates to a type of steel material and its manufacturing method, in particular to low-magnetostrictive oriented silicon steel and its manufacturing method.
- transformer cores are commonly laminated or wound with oriented silicon steel.
- Transformer manufacturers primarily focus on two performance indicators: no-load loss characteristics and no-load excitation current characteristics, which correspond to the loss and the excitation power characteristics of the oriented silicon steel, respectively.
- the noise performance of the transformers has become an equally important indicator as the no-load loss, which corresponds to the magnetostrictive characteristics of the oriented silicon steel. It should be noted that during alternating current excitation, the dimensional change of the oriented silicon steel plates due to magnetization are known as magnetostriction, which is one of the main sources of the transformer noise.
- the magnetostriction of the oriented silicon steel has become the main source of the transformer noise.
- the mechanism behind the magnetostriction of the oriented silicon steel is the variation and rotation of 90° magnetic domains that deviate from the easy magnetization direction during the magnetization process.
- the ideal state of the oriented silicon steel products is to have only 180° magnetic domains.
- small additional domains called lancet domains (90° domains) appear among the 180° magnetic domains to reduce the magnetostatic energy. Therefore, the magnetostriction can be effectively reduced by reducing 90° domains (closed domains).
- the main methods used to reduce magnetostriction include: (1) improving the orientation degree of crystal planes of the ⁇ 001> crystal plane of the finished product; (2) reducing the thickness of the finished products; and (3) increasing the tension of coatings.
- the reduction of the magnetostriction of the finished oriented silicon steel plate can be achieved by implementing these three technical solutions, thereby achieving a reduction in the transformer noise levels.
- the magnetostrictive characteristics can be reduced.
- this method in which the tension difference between the forsterite coatings and the total tension difference between the forsterite coatings and the insulating coatings are adjusted, has limitations in improving the magnetostrictive difference between two surfaces of single-sided laser-etched oriented silicon steel substrates, and it is difficult to control and produce oriented electromagnetic steel plates with excellent noise characteristics and minimal magnetostrictive deviations between upper and lower surfaces in a batch, stable, and cost-effective manner.
- the oriented electromagnetic steel plate of the invention includes a steel plate base material, a primary coating formed on surfaces of the steel plate base material, and a tension insulating coating formed on the surfaces of the primary coating, wherein the coating satisfies the following conditions: the ratio of the thickness of the tension insulating coating to the thickness of the primary coating is ⁇ (0.1, 3), the thickness of the tension insulating coating is ⁇ (0.5, 4.5) ⁇ m, and the total tension of the primary coating and the tension insulating coating is ⁇ (1,10) MPa.
- Magnetic domain control is achieved by irradiating the surface of the tension insulating coating with a laser from above.
- a strip-like sample having a length of 300 mm in a direction parallel to a rolling direction of the grain-oriented electrical steel sheet and a length of 60 mm in a direction parallel to a transverse direction is extracted from the grain-oriented electrical steel sheet, a range from a surface of the tension insulating coating to a depth position of 5 ⁇ m toward the base steel sheet side from an interface between the base steel sheet and the primary film is removed by pickling at least one surface of the sample, and a warpage amount of the sample is thereafter measured. In this case, the warpage amount satisfies specified conditions.
- Chinese patent document CN106029917A published on Oct. 12, 2016, titled “Grain-Oriented Electrical Steel Sheet for Low-Noise Transformer, and Method for Manufacturing Said Sheet”, discloses an oriented electromagnetic steel plate, which is obtained by irradiating a steel sheet surface with an electron beam having a beam diameter d of 0.40 mm or less in a line region extending in a direction intersecting a rolling direction, wherein the modulated irradiation line region is formed with repeating units connected to each other in the line region direction, a periodic distance of the repeating units in the modulated irradiation line region is 2 ⁇ 3 ⁇ d mm to 2.5 ⁇ d mm, a repeating interval of the modulated irradiation line region in the rolling direction is 4.0 mm to 12.5 mm.
- the intensity of the electron beam is not lower than an intensity with which long and narrow divided magnetic domains extending in the modulated irradiation line region direction are formed at least on an irradiated side, and not higher than an intensity with which coating damage does not occur and a plastic strain region is not formed on the irradiated side.
- the present invention aims to solve the problem of uneven stress distribution in existing oriented silicon steel due to single-sided laser etching, which causes the bending of the steel plate toward the etched surface and leads to a significant magnetostrictive deviation between the etched surface and non-etched surface of the oriented silicon steel.
- the present invention provides a manufacturing method for a low-magnetostrictive oriented silicon steel.
- the oriented silicon steel comprises a silicon steel substrate and insulating coatings on surfaces of the silicon steel substrate.
- the manufacturing method comprises: performing single-sided laser etching on the silicon steel substrate, wherein the side of the silicon steel substrate, on which single-sided laser etching is performed, is a first surface, and the side arranged opposite to the first surface is a second surface; determining a deflection difference between the first surface and the second surface based on the power of laser etching, and determining the difference in the amount of the insulating coatings on the first surface and the second surface based on the deflection difference; and forming insulating coatings on the first surface and the second surface, wherein the amount of the insulating coating on the second surface is greater than that on the first surface, and the amount of the insulating coating on the first surface and that on the second surface satisfy the difference in the amount of the insulating coatings.
- the deflection (representing a distance from the center of the surface after the steel plate is bent to the original plate axis) difference between the first surface and the second surface of the silicon steel substrate can be determined according to the power of laser etching. Then the difference in the amount of the insulating coatings applied to the first surface and the second surface is obtained according to the deflection difference. The insulating coatings are applied to the first surface and the second surface based on the difference in the amount of the insulating coatings.
- the deflection difference between the first surface and the second surface of a finished product of oriented silicon steel caused by single-sided laser etching is reduced by adjusting the tension difference between the insulating coatings on the first surface and the second surface, thereby reducing the magnetostrictive deviation between the first surface and the second surface.
- Single-sided laser etching is a commonly used method in the prior art for refining the magnetic domains of the oriented silicon steel and reducing losses.
- a method for forming insulating coatings comprises: coating the first surface and the second surface with insulating coating solution, and baking and sintering the insulating coating solution to form the insulating coatings on the first surface and the second surface.
- the steps of baking and sintering the insulating coating solution can be carried out according to the prior art.
- the power of laser etching is controlled to enable the obtained oriented silicon steel to exhibit an A-weighted magnetostriction velocity level of smaller than or equal to 55 db(A).
- the power of laser etching in the present invention is set at 0.5-2.5 mJ/mm 2 to achieve the purpose of reducing the noise of a transformer iron core made from the oriented silicon steel during operation.
- the power of laser etching is set at 1-2 mJ/mm 2 to further reduce the noise generated during the operation of the transformer iron core prepared from the oriented silicon steel of the present invention.
- the deflection difference is determined based on the following formula:
- the formulas for calculating the deflection difference and the difference in the amount of the insulating coatings are an empirical formula derived by inventors using experimental data obtained by changing the parameters such as the thickness of the silicon steel substrate, the power of laser etching, the coating formulation, the coating thickness or the like, under the condition of specific etching equipment, and performing fitting according to the obtained data.
- the difference in the amount of the insulating coatings is determined based on the following formula:
- the amount of the insulating coating on the first surface is 4.0-4.5 g/m 2 .
- the thickness of the insulating coating is too small, the tension imparted to the substrate by the insulating coating is low, resulting in insufficient magnetic optimization. If the thickness of the insulating coating is too large, it affects the stacking factor of the finished products, and meanwhile, it is easy to cause defects such as powder loss and white edges during the shearing process.
- the thickness H of the silicon steel substrate is: 0.18 mm ⁇ H ⁇ 0.23 mm.
- the thickness of the silicon steel substrate is greater than or equal to 0.18 mm.
- the thickness of the substrate is greater than 0.23 mm, due to the increased thickness and increased rigidity, the sensitivity to the uneven stress distribution caused by laser etching decreases after the insulating coatings are formed on the surfaces. As a result, the deflection difference caused by uneven stress distribution from laser etching becomes smaller, making it unsuitable for the above-mentioned empirical formula.
- the components of the insulating coating solution are as follows: at least one of aluminum dihydrogen phosphate and magnesium dihydrogen phosphate: 2%-25%, colloidal silicon dioxide: 4%-16%, chromic anhydride: 0.15%-4.50%, and the balance being water and other inevitable impurities.
- the insulating coating is used to improve the insulation performance of the surfaces of the silicon steel substrate.
- the insulating coating solution widely used in the prior art is an aqueous solution mainly composed of chromic anhydride, colloidal SiO 2 and phosphates of Mg and Al.
- the silicon steel substrate in the present invention is prepared by the following steps according to the prior art: step a, smelting and casting; step b, heating; step c, normalizing; step d, cold rolling; step e, decarburization annealing; step f, final annealing; and step g, hot stretch annealing.
- step c a two-stage normalizing treatment is performed on the silicon steel substrate: firstly, heating the silicon steel substrate to 1100-1200° C., then cooling it to 900-1000° C. at a cooling rate of 1° C./s-10° C./s, and finally cooling it to room temperature at the cooling rate of 10° C./s to 70° C./s.
- step d cold rolling either a primary cold rolling or a secondary cold rolling with an intermediate annealing step is performed.
- step e a primary recrystallization annealing is performed at 800-900° C., followed by the application of the annealing isolation agent on the surface of the silicon steel substrate.
- an annealing isolation agent such as magnesium oxide, needs to be applied to the surface of the silicon steel substrate before a high-temperature final annealing to prevent adhesion between steel plates at high temperature.
- the annealing temperature is controlled at 1100-1200° C., with a holding time of 20-30 hours.
- step g firstly, the silicon steel substrate is heated to 800-900° C., then held for 10-30 seconds, and finally cooled to room temperature at the cooling rate of 5° C./s-50° C./s.
- the present invention provides a low-magnetostrictive oriented silicon steel, which exhibits a minimal magnetostriction deviation between the etched surface and non-etched surface of the oriented silicon steel and has a good average magnetostriction.
- Vibration generated by the iron core prepared from the low-magnetostrictive oriented silicon steel of the present invention is small, so that the overall noise level of transformers with such iron core is low.
- the present invention provides a low-magnetostrictive oriented silicon steel, which is prepared by the manufacturing method for a low-magnetostrictive oriented silicon steel, wherein the magnetostrictive deviation between the first surface and the second surface of the oriented silicon steel is smaller than or equal to 2 db(A), and the average magnetostriction of the oriented silicon steel is smaller than or equal to 55 db(A).
- the low-magnetostrictive oriented silicon steel and the manufacturing method therefor of the present invention have the following advantages and beneficial effects:
- the difference in the amount of the insulating coatings on the first surface and the second surface can be obtained according to the deflection difference between the etched surface and the non-etched surface of the steel substrate, so as to adjust the tension of insulating coatings on the etched surface (the first surface) and the non-etched surface (the second surface), thereby reducing the magnetostrictive deviation between the etched surface and the non-etched surface.
- the prepared low-magnetostrictive oriented silicon steel achieves a magnetostrictive deviation between the etched surface and the non-etched surface of the oriented silicon steel of ⁇ 2 db (A) and an average magnetostriction of ⁇ 55 db (A).
- the vibration generated by the iron core prepared from the low-magnetostrictive oriented silicon steel is small, so that the overall noise level of the transformer with such iron core is low.
- FIG. 1 shows a curve of the magnetostriction of the etched surface of the oriented silicon steel in the present invention with varying energy density of laser etching.
- FIG. 2 shows a curve of the deflection difference between the first surface and the second surface of the silicon steel substrate of the present invention with varying energy density of laser etching, after single-sided laser etching is performed on the silicon steel substrate.
- FIG. 3 shows the difference in the amount of the insulating coatings on the first surface and the second surface required for maintaining the straightness of silicon steel substrate of the present invention under different deflection differences.
- Silicon steel substrates in Examples 1-6 and comparative steel plates in Comparative Examples 1 ⁇ 4 are prepared by the following steps:
- the related operations and specific manufacturing process parameters of the oriented silicon steel in Examples 1-6 of the present invention satisfy preferred design specifications of technical solutions of the present invention.
- the comparative steel plates in Comparative Examples 1 ⁇ 4 do not control the difference in the amount of the insulating coatings corresponding to the deflection difference between two surfaces caused by laser etching.
- Table 1 lists the mass percentages of various chemical elements of the silicon steel substrates and the thicknesses of finished products of the oriented silicon steel in the low-noise oriented silicon steel in Examples 1-6 and the comparative steel plates in Comparative Examples 1-4. In the following Examples and Comparative Examples, the balance of chemical components of the silicon steel substrate/plate is Fe and other inevitable impurities.
- Example 1 0.061 3.25 0.011 0.026 0.0083 0.23
- Example 2 0.060 3.24 0.020 0.027 0.009 0.2
- Example 3 0.065 3.12 0.017 0.0288 0.0087 0.18
- Example 4 0.055 3.19 0.012 0.029 0.0079 0.23
- Example 5 0.058 3.15 0.022 0.0296 0.0089 0.2
- Example 6 0.067 3.30 0.025 0.0292 0.0092 0.18 Comparative 0.061 3.33 0.009 0.0274 0.0088 0.23
- Example 1 Comparative 0.063 3.28 0.022 0.0281 0.0080 0.23
- Example 2 Comparative 0.066 3.21 0.015 0.0291 0.0084 0.2
- Example 3 Comparative 0.058 3.29 0.018 0.0268 0.0078 0.18
- Example 4 Comparative 0.063 3.28 0.022 0.0281 0.0080 0.23
- Example 3 Comparative 0.066 3.21 0.015 0.0291 0.0084 0.2
- Example 3 Comparative 0.05
- the present invention in order to obtain the oriented silicon steel with desired performance, single-sided laser etching is performed on the silicon steel substrate.
- the power of laser etching determines the deflection difference between the first surface and the second surface, and based on this deflection difference, the difference in the amount of the insulating coatings is determined.
- the insulating coatings are formed on the first surface and the second surface to obtain the oriented silicon steel.
- the amount of coatings on the surfaces of the silicon steel substrate needs to satisfy the following conditions: the amount of the insulating coating on the second surface is greater than that on the first surface, and the amount of insulating coating on the first surface and that on the second surface satisfy the difference in the amount of the insulating coatings.
- the specific chemical compositions of the insulating coating solution applied to the silicon steel substrates of Examples 1-6 and the comparative steel plates of Comparative Examples 1-4, in mass percentage, can be expressed as follows: at least one of aluminum dihydrogen phosphate or magnesium dihydrogen phosphate: 2%-25%; colloidal silicon dioxide: 4%-16%, chromic anhydride: 0.15%-4.50%, and the balance of water and other inevitable impurities.
- Table 2 lists specific chemical compositions of the insulating coating solution applied to the surfaces of the silicon steel substrates in Examples 1-6 and the comparative steel plates in Comparative Examples 1-4.
- Table 3-1 lists the specific parameters of the manufacturing processes of the silicon steel substrates in Examples 1-6 and comparative steel plates in Comparative Examples 1-4.
- Table 3-2 lists the power of single-sided laser etching performed on the silicon steel substrates in Examples 1-6 and the comparative steel plates in Comparative Examples 1-4, and deflection differences, the amount of insulating coatings on surfaces, and the difference in the amount of the insulating coatings between the two surfaces of finally obtained oriented silicon steel.
- the prepared oriented silicon steel in Examples 1-6 and comparative steel plates in Comparative Examples 1-4 were sampled respectively.
- the specific measurement method can be found in the international electrotechnical commission (IEC) technical report-IEC/TP 62581.
- the obtained test results of the magnetostrictive performance of each example and comparative examples are listed in Table 4.
- Table 4 lists the performance test results of the oriented silicon steel with low noise characteristics in Examples 1-6 and the comparative steel plates in Comparative Examples 1-4.
- 240KVA three-phase transformers were further prepared using the oriented silicon steel in Examples 1-6 and the comparative steel plates in Comparative Examples 1-4.
- the noise detection was carried out on each three-phase transformer prepared in the examples and comparative examples under the magnetization condition of 50 Hz and 1.7 T (GB/T 1094.10-2003).
- Table 5 lists the noise test results of the 240KVA three-phase transformers prepared using low-noise oriented silicon steel in Examples 1-6 and the comparative steel plates in Comparative Examples 1-4.
- the magnetostrictive deviation between the first surfaces and the second surfaces of the oriented silicon steel in Examples 1-6 is ⁇ 2 db (A), and the average magnetostriction is ⁇ 55 db (A).
- the overall noise level of the 240KVA three-phase transformers prepared using the low-noise oriented silicon steel in Examples 1-6 is significantly lower.
- FIG. 1 shows the curve of magnetostriction of the etched surface of oriented silicon steel of the present invention as a function of the energy density of laser etching, with the shaded area corresponding to the performance of the oriented silicon steel in Examples 2-4. It can be seen that with the increase of energy density of laser etchning, an improvement rate of magnetic performance (iron loss reduction) initially increases and then stablizes, and the magnetostrictive performance initially decreases and then increases.
- an improvement rate of magnetic performance iron loss reduction
- FIG. 2 shows the curve of the deflection difference between the first surface and the second surface of the silicon steel substrate in the present invention after the single-sided laser etching, as a function of the energy density of laser etching, with the shaded area corresponding to the performance of the silicon steel substrate in Examples 2-4. It can be seen that with the increase of energy density of laser etching, the deflection difference between the first surface and the second surface of the silicon steel substrate initially increases exponentially and then stabilizes.
- FIG. 3 shows the difference in the amount of the insulating coatings on the first surface and the second surface required for the silicon steel substrate of the present invention to maintain straightness under the condition of different deflection differences.
- the shaded area corresponds to the performance of the silicon steel substrate in Examples 2-4. It can be seen that in order to maintain the straightness of the finished oriented silicon steel and reduce the magnetostrictive deviation between the two surfaces, and it is necessary to adjust the difference in the amount of the insulating coatings on the first surface and the second surface based on the deflection difference caused by laser etching.
- the manufacturing method for the low-magnetostrictive oriented silicon steel of the present invention can adjust the tension difference of the insulating coatings between the etched surface and the non-etched surface of the silicon steel substrate based on the deflection difference between the etched surface and the non-etched surface of the silicon steel substrate after single-sided laser etching, thereby reducing the magnetostrictive deviation between the etched surface and the non-etched surface of the oriented silicon steel.
- the low-magnetostrictive oriented silicon steel prepared using the manufacturing method can achieve a magnetostrictive deviation between the etched surface and the non-etched surface of the oriented silicon steel ⁇ 2 db(A) and an average magnetostriction ⁇ 55 db(A).
- the vibrations generated by the iron core made of the low-magnetostrictive oriented silicon steel are small, resulting in a low overall noise level of transformers with such iron cores.
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Physics & Mathematics (AREA)
- Mechanical Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Materials Engineering (AREA)
- Crystallography & Structural Chemistry (AREA)
- Thermal Sciences (AREA)
- Electromagnetism (AREA)
- Manufacturing & Machinery (AREA)
- Optics & Photonics (AREA)
- Plasma & Fusion (AREA)
- Dispersion Chemistry (AREA)
- Power Engineering (AREA)
- Manufacturing Of Steel Electrode Plates (AREA)
- Soft Magnetic Materials (AREA)
- Chemical Treatment Of Metals (AREA)
Applications Claiming Priority (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
CN202110031202.2 | 2021-01-11 | ||
CN202110031202.2A CN114762911B (zh) | 2021-01-11 | 2021-01-11 | 一种低磁致伸缩取向硅钢及其制造方法 |
PCT/CN2022/071200 WO2022148468A1 (zh) | 2021-01-11 | 2022-01-11 | 一种低磁致伸缩取向硅钢及其制造方法 |
Publications (1)
Publication Number | Publication Date |
---|---|
US20240071661A1 true US20240071661A1 (en) | 2024-02-29 |
Family
ID=82357974
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US18/259,898 Pending US20240071661A1 (en) | 2021-01-11 | 2022-01-11 | Low-Magnetostrictive Oriented Silicon Steel and Manufacturing Method Therefor |
Country Status (5)
Country | Link |
---|---|
US (1) | US20240071661A1 (zh) |
EP (1) | EP4261853A4 (zh) |
JP (1) | JP2024502594A (zh) |
CN (1) | CN114762911B (zh) |
WO (1) | WO2022148468A1 (zh) |
Families Citing this family (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN117265361A (zh) * | 2022-06-13 | 2023-12-22 | 宝山钢铁股份有限公司 | 一种低磁致伸缩取向硅钢板的制造方法及取向硅钢板 |
Family Cites Families (20)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4363677A (en) * | 1980-01-25 | 1982-12-14 | Nippon Steel Corporation | Method for treating an electromagnetic steel sheet and an electromagnetic steel sheet having marks of laser-beam irradiation on its surface |
US4964922A (en) * | 1989-07-19 | 1990-10-23 | Allegheny Ludlum Corporation | Method for domain refinement of oriented silicon steel by low pressure abrasion scribing |
JPH0387314A (ja) * | 1989-08-29 | 1991-04-12 | Babcock Hitachi Kk | 低鉄損方向性珪素鋼板の製造方法 |
JP5446377B2 (ja) * | 2008-03-31 | 2014-03-19 | Jfeスチール株式会社 | 方向性電磁鋼板およびその製造方法 |
JP5923882B2 (ja) * | 2010-06-30 | 2016-05-25 | Jfeスチール株式会社 | 方向性電磁鋼板およびその製造方法 |
JP5594252B2 (ja) * | 2010-08-05 | 2014-09-24 | Jfeスチール株式会社 | 方向性電磁鋼板の製造方法 |
KR101530450B1 (ko) * | 2010-08-06 | 2015-06-22 | 제이에프이 스틸 가부시키가이샤 | 방향성 전기 강판 |
KR101551781B1 (ko) * | 2011-12-26 | 2015-09-09 | 제이에프이 스틸 가부시키가이샤 | 방향성 전자 강판 |
PL2843062T3 (pl) * | 2012-04-27 | 2020-12-14 | Nippon Steel Corporation | Blacha cienka ze stali elektrotechnicznej o ziarnach zorientowanych oraz sposób jej wytwarzania |
JP5668795B2 (ja) * | 2013-06-19 | 2015-02-12 | Jfeスチール株式会社 | 方向性電磁鋼板およびそれを用いた変圧器鉄心 |
JP2015161024A (ja) | 2014-02-28 | 2015-09-07 | Jfeスチール株式会社 | 低騒音変圧器用の方向性電磁鋼板およびその製造方法 |
EP3141626B1 (en) * | 2014-05-09 | 2020-02-26 | Nippon Steel Corporation | Low magnetorestriction oriented electromagnetic steel sheet with low iron loss |
CN104018068B (zh) * | 2014-06-12 | 2017-01-11 | 国家电网公司 | 一种厚度为0.18mm的高磁感取向硅钢的制备方法 |
EP3255640B1 (en) | 2015-02-05 | 2022-11-02 | JFE Steel Corporation | Method for predicting transformer noise property |
CN106282512B (zh) * | 2015-05-11 | 2018-03-30 | 宝山钢铁股份有限公司 | 低噪音变压器用取向硅钢片制造方法 |
CN107881411B (zh) * | 2016-09-29 | 2019-12-31 | 宝山钢铁股份有限公司 | 一种低噪音变压器用低铁损取向硅钢产品及其制造方法 |
CN108660295A (zh) * | 2017-03-27 | 2018-10-16 | 宝山钢铁股份有限公司 | 一种低铁损取向硅钢及其制造方法 |
KR102009834B1 (ko) * | 2017-12-26 | 2019-08-12 | 주식회사 포스코 | 이방향성 전기강판 및 그의 제조방법 |
CN111748731A (zh) * | 2019-03-28 | 2020-10-09 | 宝山钢铁股份有限公司 | 低磁致伸缩取向硅钢及其制造方法 |
CN110306030B (zh) * | 2019-08-07 | 2021-09-24 | 包头市威丰稀土电磁材料股份有限公司 | 一种激光刻痕机在纵剪线上的应用 |
-
2021
- 2021-01-11 CN CN202110031202.2A patent/CN114762911B/zh active Active
-
2022
- 2022-01-11 US US18/259,898 patent/US20240071661A1/en active Pending
- 2022-01-11 WO PCT/CN2022/071200 patent/WO2022148468A1/zh active Application Filing
- 2022-01-11 JP JP2023541062A patent/JP2024502594A/ja active Pending
- 2022-01-11 EP EP22736629.1A patent/EP4261853A4/en active Pending
Also Published As
Publication number | Publication date |
---|---|
WO2022148468A1 (zh) | 2022-07-14 |
JP2024502594A (ja) | 2024-01-22 |
CN114762911A (zh) | 2022-07-19 |
EP4261853A4 (en) | 2024-06-12 |
EP4261853A1 (en) | 2023-10-18 |
CN114762911B (zh) | 2023-05-09 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
JP5077470B2 (ja) | 方向性電磁鋼板 | |
US11459634B2 (en) | Method for manufacturing stress-relief-annealing-resistant, low-iron-loss grain-oriented silicon steel | |
WO2013099160A1 (ja) | 方向性電磁鋼板 | |
JPWO2013099272A1 (ja) | 方向性電磁鋼板およびその製造方法 | |
KR20180073306A (ko) | 방향성 전기강판 및 그 자구미세화 방법 | |
WO2012001953A1 (ja) | 方向性電磁鋼板およびその製造方法 | |
JPS59197520A (ja) | 鉄損の低い一方向性電磁鋼板の製造方法 | |
JPH02259020A (ja) | 磁気特性の優れた一方向性電磁鋼板の製造方法 | |
CN114561512B (zh) | 用激光刻痕脱碳板以改善取向硅钢片磁致伸缩的方法 | |
WO2018150791A1 (ja) | 方向性電磁鋼板 | |
US20240071661A1 (en) | Low-Magnetostrictive Oriented Silicon Steel and Manufacturing Method Therefor | |
JP2012172191A (ja) | 方向性電磁鋼板の製造方法 | |
RU2547377C2 (ru) | Способ изготовления текстурированного листового стального изделия | |
JP2012031516A (ja) | 方向性電磁鋼板の製造方法 | |
US20230307160A1 (en) | Method for manufacturing grain-oriented electrical steel sheet | |
JP2012031518A (ja) | 方向性電磁鋼板およびその製造方法 | |
CN112159935B (zh) | 一种具有低噪声特性的高磁感取向硅钢及生产方法 | |
JP5565307B2 (ja) | 方向性電磁鋼板の製造方法 | |
WO2023241574A1 (zh) | 一种低磁致伸缩取向硅钢板的制造方法及取向硅钢板 | |
KR102221606B1 (ko) | 방향성 전기강판 및 그의 제조 방법 | |
JP3492965B2 (ja) | 磁気特性が優れた一方向性電磁鋼板を得る冷間圧延方法 | |
WO2022255172A1 (ja) | 方向性電磁鋼板 | |
WO2024063163A1 (ja) | 方向性電磁鋼板 | |
JP3311021B2 (ja) | 鉄損の低い高磁束密度一方向性電磁鋼板の製造方法 | |
CN117344210A (zh) | 取向硅钢及其制造方法 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: BAOSHAN IRON & STEEL CO., LTD., CHINA Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:WU, MEIHONG;LI, GUOBAO;CHU, SHUANGJIE;AND OTHERS;REEL/FRAME:064114/0464 Effective date: 20230626 |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION |