US20180209007A1 - High strength hot rolled steel sheet - Google Patents
High strength hot rolled steel sheet Download PDFInfo
- Publication number
- US20180209007A1 US20180209007A1 US15/744,690 US201515744690A US2018209007A1 US 20180209007 A1 US20180209007 A1 US 20180209007A1 US 201515744690 A US201515744690 A US 201515744690A US 2018209007 A1 US2018209007 A1 US 2018209007A1
- Authority
- US
- United States
- Prior art keywords
- steel sheet
- less
- rolled steel
- hot rolled
- high strength
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
- 229910000831 Steel Inorganic materials 0.000 title claims abstract description 137
- 239000010959 steel Substances 0.000 title claims abstract description 137
- 229910001568 polygonal ferrite Inorganic materials 0.000 claims abstract description 61
- 229910000859 α-Fe Inorganic materials 0.000 claims abstract description 36
- 239000000126 substance Substances 0.000 claims abstract description 23
- 229910001566 austenite Inorganic materials 0.000 claims abstract description 22
- 239000000203 mixture Substances 0.000 claims abstract description 22
- 229910001567 cementite Inorganic materials 0.000 claims abstract description 15
- KSOKAHYVTMZFBJ-UHFFFAOYSA-N iron;methane Chemical compound C.[Fe].[Fe].[Fe] KSOKAHYVTMZFBJ-UHFFFAOYSA-N 0.000 claims abstract description 15
- 229910001563 bainite Inorganic materials 0.000 claims abstract description 14
- 229910000734 martensite Inorganic materials 0.000 claims abstract description 12
- 229910001562 pearlite Inorganic materials 0.000 claims abstract description 12
- 229910052758 niobium Inorganic materials 0.000 claims description 14
- 229910052720 vanadium Inorganic materials 0.000 claims description 14
- 229910052719 titanium Inorganic materials 0.000 claims description 13
- 239000012535 impurity Substances 0.000 claims description 10
- 229910052802 copper Inorganic materials 0.000 claims description 9
- 229910052750 molybdenum Inorganic materials 0.000 claims description 9
- 229910052759 nickel Inorganic materials 0.000 claims description 9
- 229910052796 boron Inorganic materials 0.000 claims description 8
- 229910052791 calcium Inorganic materials 0.000 claims description 8
- 229910052749 magnesium Inorganic materials 0.000 claims description 8
- 229910052748 manganese Inorganic materials 0.000 claims description 8
- 229910052804 chromium Inorganic materials 0.000 claims description 7
- 229910052797 bismuth Inorganic materials 0.000 claims description 6
- 229910052799 carbon Inorganic materials 0.000 claims description 3
- 229910052757 nitrogen Inorganic materials 0.000 claims description 3
- 229910052698 phosphorus Inorganic materials 0.000 claims description 3
- 238000005096 rolling process Methods 0.000 description 63
- 238000001816 cooling Methods 0.000 description 48
- 230000000052 comparative effect Effects 0.000 description 25
- 230000009467 reduction Effects 0.000 description 22
- 238000000034 method Methods 0.000 description 19
- 230000000694 effects Effects 0.000 description 16
- 238000005728 strengthening Methods 0.000 description 15
- 230000001186 cumulative effect Effects 0.000 description 14
- 230000001105 regulatory effect Effects 0.000 description 14
- 238000005098 hot rolling Methods 0.000 description 12
- 230000008569 process Effects 0.000 description 11
- 238000010438 heat treatment Methods 0.000 description 10
- XEEYBQQBJWHFJM-UHFFFAOYSA-N iron Substances [Fe] XEEYBQQBJWHFJM-UHFFFAOYSA-N 0.000 description 10
- 238000001556 precipitation Methods 0.000 description 10
- 230000006866 deterioration Effects 0.000 description 9
- 239000010410 layer Substances 0.000 description 8
- 238000012360 testing method Methods 0.000 description 8
- 238000005516 engineering process Methods 0.000 description 7
- 238000005246 galvanizing Methods 0.000 description 7
- 230000001976 improved effect Effects 0.000 description 6
- 238000004519 manufacturing process Methods 0.000 description 6
- 238000007747 plating Methods 0.000 description 6
- 239000006104 solid solution Substances 0.000 description 6
- 230000009466 transformation Effects 0.000 description 6
- 230000001276 controlling effect Effects 0.000 description 5
- 238000005275 alloying Methods 0.000 description 4
- 230000005540 biological transmission Effects 0.000 description 4
- 239000000470 constituent Substances 0.000 description 4
- 238000005244 galvannealing Methods 0.000 description 4
- 230000003287 optical effect Effects 0.000 description 4
- 238000005554 pickling Methods 0.000 description 4
- 238000009864 tensile test Methods 0.000 description 4
- 238000009825 accumulation Methods 0.000 description 3
- 238000005530 etching Methods 0.000 description 3
- 238000012545 processing Methods 0.000 description 3
- 239000000047 product Substances 0.000 description 3
- 238000011282 treatment Methods 0.000 description 3
- CURLTUGMZLYLDI-UHFFFAOYSA-N Carbon dioxide Chemical compound O=C=O CURLTUGMZLYLDI-UHFFFAOYSA-N 0.000 description 2
- FAPWRFPIFSIZLT-UHFFFAOYSA-M Sodium chloride Chemical group [Na+].[Cl-] FAPWRFPIFSIZLT-UHFFFAOYSA-M 0.000 description 2
- 230000008859 change Effects 0.000 description 2
- 238000005260 corrosion Methods 0.000 description 2
- 230000007797 corrosion Effects 0.000 description 2
- 239000013078 crystal Substances 0.000 description 2
- 238000009826 distribution Methods 0.000 description 2
- 238000010191 image analysis Methods 0.000 description 2
- 238000007373 indentation Methods 0.000 description 2
- 229910052742 iron Inorganic materials 0.000 description 2
- 230000000670 limiting effect Effects 0.000 description 2
- 239000011159 matrix material Substances 0.000 description 2
- 230000007246 mechanism Effects 0.000 description 2
- 238000005498 polishing Methods 0.000 description 2
- 238000010998 test method Methods 0.000 description 2
- VYPSYNLAJGMNEJ-UHFFFAOYSA-N Silicium dioxide Chemical compound O=[Si]=O VYPSYNLAJGMNEJ-UHFFFAOYSA-N 0.000 description 1
- 230000002411 adverse Effects 0.000 description 1
- 238000000137 annealing Methods 0.000 description 1
- 229910002092 carbon dioxide Inorganic materials 0.000 description 1
- 239000001569 carbon dioxide Substances 0.000 description 1
- 230000015556 catabolic process Effects 0.000 description 1
- 239000011247 coating layer Substances 0.000 description 1
- 238000005097 cold rolling Methods 0.000 description 1
- 239000008119 colloidal silica Substances 0.000 description 1
- 238000012937 correction Methods 0.000 description 1
- 230000007812 deficiency Effects 0.000 description 1
- 238000006731 degradation reaction Methods 0.000 description 1
- 230000003111 delayed effect Effects 0.000 description 1
- 238000009792 diffusion process Methods 0.000 description 1
- 238000007598 dipping method Methods 0.000 description 1
- 239000006185 dispersion Substances 0.000 description 1
- 238000010894 electron beam technology Methods 0.000 description 1
- 239000012467 final product Substances 0.000 description 1
- 239000000446 fuel Substances 0.000 description 1
- 230000006872 improvement Effects 0.000 description 1
- 230000001939 inductive effect Effects 0.000 description 1
- 230000002401 inhibitory effect Effects 0.000 description 1
- JEIPFZHSYJVQDO-UHFFFAOYSA-N iron(III) oxide Inorganic materials O=[Fe]O[Fe]=O JEIPFZHSYJVQDO-UHFFFAOYSA-N 0.000 description 1
- 230000014759 maintenance of location Effects 0.000 description 1
- 238000005259 measurement Methods 0.000 description 1
- 230000000116 mitigating effect Effects 0.000 description 1
- 150000004767 nitrides Chemical class 0.000 description 1
- 239000002244 precipitate Substances 0.000 description 1
- 238000003825 pressing Methods 0.000 description 1
- 230000001737 promoting effect Effects 0.000 description 1
- 230000000644 propagated effect Effects 0.000 description 1
- 239000002994 raw material Substances 0.000 description 1
- 238000001953 recrystallisation Methods 0.000 description 1
- 230000000452 restraining effect Effects 0.000 description 1
- 229920006395 saturated elastomer Polymers 0.000 description 1
- 238000005204 segregation Methods 0.000 description 1
- 239000011780 sodium chloride Substances 0.000 description 1
- 239000000243 solution Substances 0.000 description 1
- 239000002344 surface layer Substances 0.000 description 1
- 238000011269 treatment regimen Methods 0.000 description 1
- 230000000007 visual effect Effects 0.000 description 1
- 238000010792 warming Methods 0.000 description 1
Images
Classifications
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
- C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
- C21D8/0226—Hot rolling
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/34—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of silicon
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
- C22C38/42—Ferrous alloys, e.g. steel alloys containing chromium with nickel with copper
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
- C22C38/44—Ferrous alloys, e.g. steel alloys containing chromium with nickel with molybdenum or tungsten
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
- C22C38/46—Ferrous alloys, e.g. steel alloys containing chromium with nickel with vanadium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
- C22C38/48—Ferrous alloys, e.g. steel alloys containing chromium with nickel with niobium or tantalum
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
- C22C38/50—Ferrous alloys, e.g. steel alloys containing chromium with nickel with titanium or zirconium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
- C22C38/54—Ferrous alloys, e.g. steel alloys containing chromium with nickel with boron
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
- C23C2/36—Elongated material
- C23C2/40—Plates; Strips
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D2211/00—Microstructure comprising significant phases
- C21D2211/005—Ferrite
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
- C23C2/06—Zinc or cadmium or alloys based thereon
Definitions
- the present invention relates to a hot rolled steel sheet, and particularly relates to a high strength hot rolled steel sheet which has excellent hole expansibility and is suitable for chassis components and the like of automobiles formed into various forms through pressing or the like.
- Hot rolled steel sheets are manufactured at relatively low cost and are widely used for various types of industrial equipment including automobiles. Recently, from a viewpoint on the restriction on carbon dioxide emission entailing the measures against global warming, fuel efficiency of automobiles has been required to be improved. Moreover, for the purpose of reducing weight and ensuring collision safety of vehicle bodies, high strength hot rolled steel sheets have been widely applied to automobile components.
- steel sheets for automobile components have to satisfy not only the strength but also various types of workability such as press formability and weldability required at the time of forming the components.
- press formability and weldability required at the time of forming the components.
- the frequency of use of stretch flange forming and burring forming is extremely high. Therefore, high strength hot rolled steel sheets for the chassis components are required to have excellent hole expansibility.
- the chassis components from a viewpoint on ensuring safety, many components are required to avoid plastic deformation even in a case where a large load is applied. Therefore, steel sheets for the chassis components are required to have a high yield ratio.
- the structure is uniformly strengthened by controlling the steel structure to be a single phase structure containing any one of ferrite, bainitic ferrite, bainite, and the like, through solid solution strengthening of Mn, Si, and the like, and/or carbide of Ti, Nb, V, and the like or precipitation strengthening due to Cu.
- Patent Document 1 discloses a technology that relates to a high strength hot rolled steel sheet having excellent hole expansibility, in which Ti carbide including Mo is dispersed in a substantially single phase structure of ferrite in a uniform and fine manner.
- Mo which is a very expensive alloying element. Therefore, from an economic viewpoint, the configuration is not suitable for mass production.
- Patent Document 2 discloses a technology in which elongation and stretch flangeability of a high strength hot rolled steel sheet are improved by appropriately controlling cooling of Ti-added steel containing predetermined amounts of Mn and Si during a period from hot rolling to coiling such that a structure having ferrite and bainite is achieved, and causing TiC to be finely precipitated.
- the yield ratio which is one of characteristics necessary for a hot rolled steel sheet applied to chassis components.
- bainite has a low yield ratio compared to ferrite after precipitation strengthening, the technology of Patent Document 2 allows bainite to be included up to 50%, and it is analogized that a high yield ratio cannot be maintained.
- ferrite includes so-called bainitic ferrite or pseudo-polygonal ferrite which is not polygonal ferrite.
- a temperature range of 720° C. or lower at which polygonal ferrite is not sufficiently formed is also allowed as a first cooling stop temperature.
- Bainitic ferrite and pseudo-polygonal ferrite have a structure indicating a yield ratio lower than that of polygonal ferrite.
- Patent Document 3 discloses a Ti-added high strength hot rolled steel sheet of which toughness and hole expansibility are improved by reducing the Mn content and controlling the percentage of C which is precipitated as cementite.
- a high yield ratio of 75% or more is not obtained in high strength steel of 540 MPa or higher.
- Patent Document 4 discloses a technology that relates to a high strength hot rolled steel sheet having excellent hole expansibility, in which corsening of TiC is suppressed by reducing the Mn content and the Si content and adding certain amounts of Ti and B.
- B has an effect of suppressing the recrystallization of austenite from being recrystallized, in a case of being subjected to multiple addition together with Ti having a similar effect, a rolling load during hot rolling increases remarkably, resulting in an increase of a load to a hot rolling mill. Therefore, there is concern that the technology of Patent Document 4 causes operational trouble.
- the strength of a final product considerably varies when the B content fluctuates only by several ppm, steel essentially containing B is not suitable for mass production.
- Patent Document 5 discloses a high strength hot rolled steel sheet which has a high yield ratio and excellent hole expansibility and is obtained by cooling steel containing large amounts of Si, Mn, and Ti under an appropriate cooling condition and causing the structure to be a single phase structure of granular bainitic ferrite.
- Patent Document 5 in order to obtain the granular bainitic ferrite structure, large amounts of Si and Mn need to be contained, thereby leading to a problem of an increase in alloying cost.
- Patent Document 1 Japanese Unexamined Patent Application, First Publication No. 2002-322540
- Patent Document 2 Japanese Unexamined Patent Application, First Publication No. 2007-009322
- Patent Document 3 Japanese Unexamined Patent Application, First Publication No. H10-287949
- Patent Document 4 Japanese Unexamined Patent Application, First Publication No. 2012-026032
- Patent Document 5 Japanese Unexamined Patent Application, First Publication No. 2004-307919
- An object of the present invention is to provide a high strength hot rolled steel sheet having a high yield ratio and excellent hole expansibility.
- the high strength in the present invention indicates that tensile strength (TS) is 540 MPa or higher.
- Ti is relatively inexpensive and exhibits remarkable precipitation strengthening with a minute amount of Ti content.
- the inventors have examined structures of hot rolled steel sheets on the premise that polygonal ferrite is employed as a main constituent.
- the inventors have examined utilization of precipitation strengthening of Ti.
- the inventors have also intensively examined a technique of improving the hole expansibility in a Ti-containing high strength hot rolled steel sheet in which Ti precipitates are precipitated in polygonal ferrite as a main constituent of the structures. As a result, the following knowledge has been acquired.
- the inventors have measured micro-hardness of each ferrite grain in steel having polygonal ferrite as a main constituent of the structure. As a result, it has been found that the hardness significantly varies depending on each of the measured grains. Furthermore, it has been found that hole expansibility can be remarkably improved by reducing unevenness in the hardness of ferrite grains.
- the inventors have observed the intragranular state of polygonal ferrite of a sample having inferior hole expansibility, using a transmission electron microscope. As a result, it has been found that a large amount of Ti-based anisometric carbide stretched in a particular orientation of the ferrite is precipitated and this exerts an adverse influence on the hole expansibility. In the related art, there have been few reports on the shape of Ti carbide affecting hole expansibility, and the mechanism of the shape of Ti-based carbide affecting hole expansibility is obscure. However, compared to Ti-based isometric carbide, Ti-based anisometric carbide is highly consistent with matrix phase ferrite, and it is estimated that considerable consistency distortion is accumulated around the Ti-based anisometric carbide. Therefore, it is estimated that this consistency distortion incites cracks to be propagated during hole expanding resulting in deterioration of the hole expansibility.
- the present invention has been made based on the knowledge described above.
- the gist is as follows.
- a hot rolled steel sheet including, as a chemical composition, by mass %, C: 0.010% to 0.200%, Si: 0.001% to 2.50%, Mn: 0.001% to 1.50%, P: 0.050% or less, S: 0.010% or less, N: 0.0070% or less, Al: 0.001% to 0.50%, Ti: 0.050% to 0.30%, V: 0% to 0.50%, Nb: 0% to 0.090%, Cr: 0% to 0.50%, Ni: 0% to 0.50%, Cu: 0% to 0.50%, Mo: 0% to 0.50%, B: 0% to 0.0050%, Ca: 0% to 0.01%, Mg: 0% to 0.01%, Bi: 0% to 0.01%, and a remainder of Fe and impurities.
- the structure includes, by area ratio, 80% or more of a polygonal ferrite, a total of 5% or less of a martensite and an austenite, and a total of 5% or less of a pearlite and a cementite, and the remainder is at least one selected from a bainitic ferrite and a bainite.
- a standard deviation of micro-hardness of 50 arbitrary pieces of the polygonal ferrite present within a range of ⁇ 100 ⁇ m from a central plane in a sheet thickness direction is ⁇ HV
- the ⁇ HV is 30 or smaller.
- a grain of the polygonal ferrite contains 5 ⁇ 10 7 pieces/mm 2 or more of Ti-containing carbide, and in 50% or more of the Ti-containing carbide, the aspect ratio which is a ratio of a length of a long side to a length of a short side is less than 3.
- the tensile strength is 540 MPa or higher.
- the chemical composition may include, by mass %, at least one selected from the group consisting of V: 0.010% to 0.50%, Nb: 0.001% to 0.090%, Cr: 0.001% to 0.50%, Ni: 0.001% to 0.50%, Cu: 0.001% to 0.50%, Mo: 0.001% to 0.50%, and B: 0.0001% to 0.0050%.
- the chemical composition may include, by mass %, at least one selected from the group consisting of Ca: 0.0001% to 0.01%, Mg: 0.0001% to 0.01%, and Bi: 0.0001% to 0.01%.
- the hot rolled steel sheet according to any one of (1) to (3) may further include a hot-dip galvanized layer on a surface.
- the steel sheet according to the aspect of the present invention it is possible to inexpensively manufacture a high strength hot rolled steel sheet having a high yield ratio and excellent hole expansibility.
- the steel sheet according to the aspect of the present invention also has excellent hole expansibility even during stretch flanges forming frequently employed for automobile components, particularly chassis components and the like. Therefore, the steel sheet particularly contributes to reducing weight and ensuring collision safety of vehicle bodies in automobile fields.
- FIG. 1 is a schematic view showing an example of a treatment pattern of hot rolling.
- FIG. 2 is a schematic view showing an example of a heat treatment pattern in a galvannealing line employed in Example 2.
- FIG. 3A is a view showing an example of micro-hardness distribution of polygonal ferrite measured in Example 1.
- FIG. 3B is a view showing another example of micro-hardness distribution of polygonal ferrite measured in Example 1.
- a high strength hot rolled steel sheet according to an embodiment of the present invention (hereinafter, will be sometimes referred to as a hot rolled steel sheet according to the present embodiment) will be described in detail.
- the hot rolled steel sheet according to the present embodiment includes, as a chemical composition, by mass %, C: 0.010% to 0.200%, Si: 0.001% to 2.50%, Mn: 0.001% to 1.50%, P: 0.050% or less, S: 0.010% or less, N: 0.0070% or less, Al: 0.001% to 0.50%, and Ti: 0.050% to 0.30%.
- the hot rolled steel sheet includes at least one selected from the group consisting of V: 0.50% or less, Nb: 0.090% or less, Cr: 0.50% or less, Ni: 0.50% or less, Cu: 0.50% or less, Mo: 0.50% or less, B: 0.0050% or less, Ca: 0.01% or less, Mg: 0.01% or less, and Bi: 0.01% or less; and a remainder of Fe and impurities.
- a structure includes, by area ratio, 80% or more of polygonal ferrite, a total of 5% or less of martensite and austenite, and a total of 5% or less of pearlite and cementite, and the remainder is at least one selected from bainitic ferrite and bainite.
- a grain of the polygonal ferrite contains 5 ⁇ 10 7 pieces/mm 2 or more of Ti-containing carbide, and in 50% or more of the Ti-containing carbide, an aspect ratio which is a ratio of the length of a long side to the length of a short side is less than 3.
- the C content is an element essential to high-strengthening of a steel sheet performed through precipitation strengthening or solid solution strengthening.
- the C content is set to 0.010% or more, is preferably set to 0.020% or more, and is more preferably set to 0.040% or more.
- the C content is set to 0.200% or less, is preferably set to 0.130% or less, and is more preferably set to 0.110% or less.
- Si is a solid solution strengthening element and is an element effective in high-strengthening of a steel sheet.
- the Si content is set to 0.001% or more, is preferably set to 0.01% or more, and is more preferably set to 0.04% or more. Meanwhile, if there is an excessive amount of Si, island-shaped scale is generated, and surface quality deteriorates. Therefore, the Si content is set to 2.50% or less, is preferably set to 1.30% or less, and is more preferably set to 0.80% or less.
- Mn is an element effective in improving strength of a steel sheet.
- Mn is an element which fixes S in steel as MnS and suppresses hot embrittlement caused by a solid solution S.
- the Mn content is set to 0.001% or more, is preferably set to 0.10% or more, and is more preferably set to 0.45% or more.
- the Mn content is set to 1.50% or less, is preferably set to 1.00% or less, and is more preferably set to 0.80% or less.
- P is an element contained as impurities, which cause weldability and toughness of a steel sheet to deteriorate. Therefore, it is preferable to have a small amount of P. However, in a case where the P content exceeds 0.050%, the influence described above becomes prominent. Accordingly, as a range in which deterioration of weldability and toughness is not prominent, the P content is set to 0.050% or less, is preferably set to 0.020% or less, and is more preferably set to 0.010% or less.
- S is an element contained as impurities, forming MnS in steel and causing hole expansibility of a steel sheet to deteriorate. Therefore, it is preferable to have a small amount of S.
- the S content exceeds 0.010%, the influence described above becomes prominent. Accordingly, as a range in which deterioration of hole expansibility is not prominent, the S content is set to 0.010% or less, is preferably set to 0.0050% or less, and is more preferably set to 0.0020% or less.
- N is an element contained as impurities, forming coarse nitride in steel and causing hole expansibility of a steel sheet to deteriorate remarkably. Therefore, it is preferable to have a small amount of N. However, in a case where the N content exceeds 0.0070%, the influence described above becomes prominent. Accordingly, as a range in which deterioration of hole expansibility is not prominent, the N content is set to 0.0070% or less and is preferably set to 0.0050% or less.
- Al is an element effective in deoxidation of steel.
- the Al content is set to 0.001% or more.
- the Al content is set to 0.50% or less, is preferably set to 0.20% or less, and is more preferably set to 0.10% or less.
- Ti is an element forming carbide in steel and inducing uniform precipitation strengthening of ferrite.
- Ti is also an element having effects of reducing the amount of a solid solution C by being precipitated as TiC and inhibiting precipitation of cementite which causes deterioration of hole expansibility. Therefore, in the hot rolled steel sheet according to the present embodiment, Ti is a particularly important element.
- the Ti content is set to 0.050% or more, is preferably set to 0.100% or more, and is more preferably set to 0.130% or more. Meanwhile, if the Ti content exceeds 0.30%, toughness deteriorates remarkably and an unnecessary cost increase is caused. Therefore, the Ti content is set to 0.30% or less, is preferably set to 0.25% or less, and is more preferably set to 0.20% or less.
- the hot rolled steel sheet according to the present embodiment contains the chemical composition described above and the remainder of Fe and impurities.
- the hot rolled steel sheet may further include at least one selected from the group consisting of V, Nb, Cr, Ni, Cu, Mo, B, Ca, Mg, and Bi.
- impurities denote components incorporated due to raw materials such as ores and scraps, or other factors when steel is industrially manufactured.
- V is an element forming carbide in steel.
- V is an element of which the solubility product in austenite is greater than that of Ti and which is effective in high-strengthening of a steel sheet. Therefore, although it is expensive compared to Ti, V may be contained as necessary.
- the V content is set to 0.010% or more, is preferably set to 0.070% or more, and is more preferably set to 0.140% or more. Meanwhile, when there is an excessive amount of V, a cost rise is caused. Therefore, even in a case where V is contained, the V content is set to 0.50% or less.
- Nb is an element which forms carbide in steel and is effective in high-strengthening of a steel sheet. Therefore, although it is expensive compared to Ti, Nb may be contained as necessary. When the Nb content is less than 0.001%, the effect described above cannot be sufficiently obtained. Accordingly, in a case of obtaining the effect described above, the Nb content is set to 0.001% or more. Meanwhile, when there is an excessive amount of Nb, plastic anisotropy of a steel sheet increases, and hole expansibility deteriorates. Therefore, even in a case where Nb is contained, the Nb content is set to 0.090% or less.
- All of Cr, Ni, Cu, Mo, and B are elements effective in high-strengthening of a steel sheet. Therefore, as necessary, the elements may be contained independently, or two or more thereof may be contained multiply. In order to achieve the effect described above, there is a need to include Cr: 0.001% or more, Ni: 0.001% or more, Cu: 0.001% or more, Mo: 0.001% or more, and B: 0.0001% or more. Meanwhile, similar to Mn, these elements delay ferritic transformation after hot rolling. Therefore, when there are excessive amounts of the elements, it becomes difficult to obtain, by area ratio, 80% or more of polygonal ferrite in the structure of a hot rolled steel sheet, and hole expansibility of a hot rolled steel sheet deteriorates.
- the amounts thereof are set to Cr: 0.50% or less, Ni: 0.50% or less, Cu: 0.50% or less, Mo: 0.50% or less, and B: 0.0050% or less respectively; and are preferably set to Cr: 0.20% or less, Ni: 0.20% or less, Cu: 0.20% or less, Mo: 0.09% or less, and B: 0.0040% or less, respectively.
- Ca and Mg are elements contributing to fine dispersion of inclusions in steel.
- Bi is an element mitigating micro-segregation of substitutional type alloying elements such as Mn and Si in steel. All of the elements contribute to improvement of hole expansibility of a steel sheet. Therefore, as necessary, the elements may be contained independently, or two or more thereof may be contained multiply. In order to achieve the effect described above, each of the elements needs to be contained 0.0001% or more. Meanwhile, when there are excessive amounts of these elements, ductility deteriorates. Therefore, even in a case where the elements are contained, the amounts of the elements are set to 0.01% or less.
- Polygonal ferrite has a structure effective in improving hole expansibility.
- the area ratio of polygonal ferrite is set to 80% or more, is preferably set to 90% or more, and is more preferably set to 95% or more.
- the area ratio of polygonal ferrite may be 100%. That is, the hot rolled steel sheet according to the present embodiment may be constituted of single phase polygonal ferrite.
- the total area ratio of the martensite and austenite is set to 5% or less and is preferably set to 2% or less.
- the total area ratio may be 0% (that is, none of martensite and austenite are contained).
- the austenite mentioned herein is so-called residual austenite.
- the total area ratio of the pearlite and cementite is set to 5% or less, is preferably set to 3% or less, and is more preferably set to 1% or less.
- the total area ratio may be 0% (that is, none of the pearlite and cementite are contained).
- the structure of the remainder other than those described above includes at least one selected from bainitic ferrite and bainite. However, in a case where the total area ratio of the structure described above is 100%, none of bainitic ferrite and bainite are included.
- Polygonal ferrite formed by a diffusion mechanism has no internal structures in grains, and its grain boundary is linear or forms an arc.
- bainitic ferrite and bainite have an internal structure, have an acicular intergranular shape, and have a structure distinctly different from that of polygonal ferrite. Therefore, polygonal ferrite, bainite, and bainitic ferrite can be determined based on the intergranular shape and the presence or absence of the internal structure from a photograph of the structure obtained by using an optical microscope after etching performed with nital. In a case where the internal structure is not distinctly revealed and a structure having an acicular intergranular shape (pseudo-polygonal ferrite) is present, it is counted as bainitic ferrite.
- cementite and pearlite are etched in black, their structures can be distinctly discriminated.
- an image analysis is performed with respect to a photograph of the structure obtained by means of an optical microscope employing a Le Pera-etched sample, so that the total area ratio of residual austenite and martensite can be calculated.
- a structure of a steel sheet is observed at 1 ⁇ 4 position of the depth in a sheet thickness, in which a representative structure of the steel sheet is shown.
- hole expansibility of a hot rolled steel sheet can be remarkably improved by reducing unevenness in hardness of ferrite grains.
- a hardness (micro-hardness) of 50 arbitrary pieces of polygonal ferrite present within a range of ⁇ 100 ⁇ m from a central plane (a face which includes a central portion of the sheet thickness of a steel sheet and is perpendicularly orthogonal to the sheet thickness direction) in the sheet thickness direction is measured, and when a standard deviation of the micro-hardness is the ⁇ HV, excellent hole expansibility can be obtained by setting the ⁇ HV to 30 or smaller. Therefore, the ⁇ HV is set to 30 or smaller. Since the standard deviation is preferred to be small, the lower limit of the ⁇ HV is zero.
- a specific method of measuring the ⁇ HV will be described below.
- a steel sheet of which a cross section in a rolling direction is subjected to mirror polishing and in which chemical polishing is performed using colloidal silica in order to remove a worked layer on a surface layer and then the grain boundary is revealed through nital-etching is used.
- the micro-hardness is measured using a micro-hardness measuring apparatus (brand name: FISCHERSCOPE HM 2000 XYp) by pushing a pyramidal Vickers indenter having an apex angle of 136° into a grain such that its indentation does not overlap the grain boundary of ferrite with respect to randomly selected 50 pieces of polygonal ferrite (grains) which are present within a range of ⁇ 100 ⁇ m from the central plane in the sheet thickness direction.
- the indentation load is set to 20 N.
- the standard deviation ⁇ HV of the micro-hardness is obtained from the 50 pieces of obtained data.
- 5 ⁇ 10 7 pieces/mm 2 or more of Ti-containing carbide are included in a grain of polygonal ferrite.
- precipitation strengthening is insufficient, thereby resulting in strength deficiency. Meanwhile, there is no need to regulate the upper limit.
- the number is within the component range described above, the number does not exceed 1 ⁇ 10 11 pieces/mm 2 .
- the pieces of Ti-containing carbide present in a grain of polygonal ferrite when 50% or more of the carbide, by the number percentage, has the ratio of the length of the short side to the length of the long side (aspect ratio expressed as long side/short side) less than 3, excellent hole expansibility can be obtained. It is preferable to include 2 ⁇ 3 or more of Ti-containing carbide having the aspect ratio of long side/short side less than 3 among the Ti-containing carbide present in a grain of polygonal ferrite. The percentage of the Ti-containing carbide having the aspect ratio less than 3 may be 100%.
- the percentage of the Ti-containing carbide having the aspect ratio less than 3 is obtained by setting orientation of an electron beam to be parallel to ⁇ 001> of matrix phase ferrite and obtaining carbide having the aspect ratio of long side/short side less than 3 with respect to the total number of pieces of observed Ti-containing carbide when 100 or more pieces of Ti-containing carbide are observed using a transmission electron microscope (magnification: 200,000-fold).
- the Ti-containing carbide is carbide containing Ti, and the Ti-containing carbide may further contain at least one of V and Nb. That is, the Ti-containing carbide also includes a state where carbide has a crystal structure (NaCl structure) of Ti-containing carbide and some locations of Ti are substituted with V or Nb.
- the hot rolled steel sheet according to the present embodiment may have a known hot-dip galvanized layer on its surface.
- the hot-dip galvanized layer may be a galvannealed layer which is alloyed. In a case where a steel sheet has a hot-dip galvanized layer, rust is restrained from being generated, and the corrosion resistance of the hot rolled steel sheet is improved.
- tensile strength TS is 540 MPa or higher
- the ratio (yield ratio (YR)) of the tensile strength TS and 0.2% proof stress YS is 75% or more
- the product (TS ⁇ ) of the tensile strength TS and a hole expanding rate ⁇ regulated by JFST 1001 is 50,000 MPa ⁇ % or higher.
- the hot rolled steel sheet according to the present embodiment aims to be provided with all the high tensile strength, the high yield ratio, and the high balance between the tensile strength and the hole expansibility (TS ⁇ ) by controlling the chemical composition and the structure.
- the tensile strength is preferably set to 590 MPa or higher. In addition, if the tensile strength exceeds 1,180 MPa, fatigue properties of a weld portion deteriorate. Accordingly, it is preferable to be 1,180 MPa or lower.
- the hot rolled steel sheet according to the present embodiment can be stably manufactured in accordance with a manufacturing method including the following processes (A) to (D), and it is preferable.
- the heated slab is subjected to rough rolling such that the cumulative rolling reduction within a range from 1,050° C. to 1,150° C. becomes 50% or larger.
- cooling is performed under the condition that the average cooling rate within the temperature range from Tx to CT (450° C. ⁇ CT ⁇ 650° C.) which is a secondary cooling end temperature becomes 30° C./s or faster. Then, after being cooled to CT, the hot rolled steel sheet is coiled.
- a slab having a chemical composition as described above is heated to approximately 1,200° C.
- the heating temperature is within the temperature range from 1,150° C. to 1,250° C.
- the heated slab becomes a hot rolled steel sheet via the hot rolling process including the rough rolling process and the finish rolling process.
- the hot rolled steel sheet according to the present embodiment is manufactured, in each process of rough rolling and finish rolling, it is preferable to control the temperature, the rolling reduction, and the like.
- the cumulative rolling reduction within the range from 1,050° C. to 1,150° C. is set to 50% or larger.
- the cumulative rolling reduction in the present invention is the percentage of the cumulative rolling reduction amount (difference between the inlet sheet thickness before the first pass in rolling and an outlet sheet thickness after the last pass in rolling) with respect to a reference, while the reference is an inlet sheet thickness before a first pass.
- the cumulative rolling reduction is calculated in each of rough rolling and finish rolling.
- the cumulative rolling reduction in rough rolling is the percentage of the difference between the inlet sheet thickness before the first pass in rough rolling and the outlet sheet thickness after the last pass in rough rolling.
- the cumulative rolling reduction in finish rolling is the percentage of the difference between the inlet sheet thickness before the first pass in finish rolling and the outlet sheet thickness after the last pass in finish rolling.
- the cumulative rolling reduction at 1,050° C. or lower ranges from 20% to 80%. if the cumulative rolling reduction at 1,050° C. or lower exceeds 80%, the anisotropy of the finally obtained structure of the hot rolled steel sheet is revealed. In this case, there are cases where the ⁇ HV increases and hole expansibility is degraded. The reason is presumed to be the hardness difference which is incited by deviation of the crystal orientation of ferrite grains. Meanwhile, if the cumulative rolling reduction at 1,050° C. or lower falls short of 20%, the austenite grain size is coarsened and accumulation of distortion in austenite becomes insufficient. Accordingly, ferritic transformation after finish rolling is suppressed, and the finally obtained polygonal ferrite fraction and standard deviation of micro-hardness of polygonal ferrite deviate from the desired range, and the possibility of deterioration of hole expansibility increases.
- the rolling reduction of the last pass is from 15% to 35%. If the rolling reduction of the last pass exceeds 35%, the anisotropy of the structure is revealed. As a result, there are cases where the ⁇ Hv increases and hole expansibility is degraded. Therefore, the rolling reduction of the last pass is set to 35% or smaller and is more preferably set to 25% or smaller. Meanwhile, if the rolling reduction of the last pass falls short of 15%, accumulation of distortion in austenite becomes insufficient. Accordingly, ferritic transformation after finish rolling is suppressed, and the finally obtained polygonal ferrite fraction and standard deviation of micro-hardness of polygonal ferrite deviate from the desired range, and the possibility of deterioration of hole expansibility increases.
- the finishing temperature (temperature of the steel sheet after the last pass of finish rolling) is set to 930° C. or higher. If the finishing temperature falls short of 930° C., the anisotropy of the structure is likely to be revealed in the finally obtained hot rolled steel sheet. As a result, the ⁇ Hv increases, and the possibility of deterioration of hole expansibility increases. Meanwhile, in accordance with an increase of the finishing temperature, the austenite grain size is coarsened and accumulation of distortion in austenite becomes insufficient. Accordingly, ferritic transformation after finish rolling is suppressed, and the finally obtained polygonal ferrite fraction and standard deviation of micro-hardness of polygonal ferrite grow, so that the possibility of deterioration of hole expansibility increases. Therefore, it is preferable that the upper limit of the finishing temperature is set to approximately 1,000° C.
- the hot rolled steel sheet is subjected to cooling.
- the average cooling rate within the temperature range from the finish rolling last pass temperature to 720° C. is set to 30° C./s.
- cooling of the hot rolled steel sheet at a low average cooling rate for a desired time which is determined in accordance with the Mn content is effective in promoting ferritic transformation and precipitation of the Ti-containing carbide, and having the finally obtained polygonal ferrite fraction and standard deviation of micro-hardness of polygonal ferrite within the desired range.
- the hot rolled steel sheet is coiled.
- the cooling rate is slower than 30° C./s or the coiling temperature exceeds 650° C.
- Ti-containing carbide in the hot rolled steel sheet is excessively coarsened during the cooling or after the coiling, and there are cases where it becomes difficult to ensure the desired strength.
- the coiling temperature is set to less than 450° C., accuracy of controlling the coiling temperature is degraded, and it is not preferable. Therefore, in order to be effective, the coiling temperature is set to range from 450° C. to 650° C., and cooling is performed until the temperature reaches the coiling temperature at a predetermined average cooling rate or faster.
- cooling is performed under the condition that the average cooling rate within the temperature range from a finish rolling last pass temperature to MT (720° C. ⁇ MT ⁇ 830° C.) becomes 30° C./s or faster.
- ii) as secondary cooling cooling is performed for t seconds which is regulated by the following Expression 1 under the cooling condition that the average cooling rate within the temperature range from MT to Tx (720° C. ⁇ Tx ⁇ MT) becomes 10° C./s or slower.
- cooling is performed under the cooling condition that the average cooling rate becomes 30° C./s or faster within the temperature range from the secondary cooling end temperature (Tx) to CT (450° C. ⁇ CT ⁇ 650° C.). Then, coiling is performed within the temperature range from the 450° C. to 650° C.
- (Mn) is the Mn content by unit mass %.
- the hot rolled steel sheet according to the present embodiment is manufactured, as necessary, the following processes may be further provided.
- a hot-dip galvanizing process for hot-dip galvanizing a hot rolled steel sheet may be provided. It is possible to form a coating layer on a surface of the steel sheet and to improve corrosion resistance of the steel sheet by performing hot-dip galvanizing.
- a galvannealed layer may be formed on a surface of the steel sheet by performing alloying.
- the maximum heating temperature during annealing before hot-dip galvanizing dipping is preferably set to 800° C. or lower.
- Other hot-dip galvanizing conditions may comply with routine procedures.
- pickling may be performed after the hot rolling process.
- skin pass rolling may be performed for flatness correction or promotion of scale peeling.
- the elongation rate in a case of performing skin pass rolling is not particularly regulated. However, it is preferable to set to range from 0.1% to less than 3.0%.
- Pieces of steel respectively having the chemical compositions indicated in Table 1 were each formed into ingot at a laboratory and were cast into slabs. Then, the slabs were subjected to heating, hot rolling, cooling, and coiling in the pattern as shown in FIG. 1 . In this case, the conditions in each process were as indicated in Table 2.
- SRT, R1, R2, R3, FT, MT, t, and CT indicate the following, respectively.
- R1 cumulative rolling reduction within range from 1,050° C. to 1,150° C.
- R2 cumulative rolling reduction at 1,050° C. or lower
- Hot rolled steel sheets obtained as described above were subjected to pickling.
- JIS No. 5 tensile test pieces were respectively collected from the hot rolled steel sheets in a direction perpendicular to the rolling direction.
- a tensile test was performed using these test pieces, and the yield strength (YS), the tensile strength (TS), the yield ratio (YR), and the total elongation (EL) were measured.
- samples each including a cross section of the hot rolled steel sheet in the rolling direction were collected.
- a surface corresponding to the cross section of each sample in the rolling direction was etched using a nital solution.
- a photograph of the structure obtained in the visual field of 300 ⁇ m ⁇ 300 ⁇ m at 1 ⁇ 4 position of the depth in the sheet thickness was captured using an optical microscope or an electronic scanning microscope, and the structure was identified.
- the area ratio of each structure was calculated through a point counting method.
- Polygonal ferrite, bainite, and bainitic ferrite were determined based on the intergranular shape and the presence or absence of the internal structure.
- the structure etched in black was discriminated from cementite and pearlite.
- an image analysis was performed with respect to the photograph of the structure obtained using the optical microscope, and the total area ratio of residual austenite and martensite was thereby calculated.
- a pellicle sample was collected from each of the hot rolled steel sheets. Then, carbide containing at least one of Ti, V, and Nb precipitated in a grain of ferrite was observed using the transmission electron microscope (magnification: 200,000-fold), and the number density and the percentage of the precipitated element having the aspect ratio of 3 or less were obtained.
- FIGS. 3A and 3B respectively show the measurement results of micro-hardness of the sample number 14 and the sample number 15, as examples.
- Tables 3 and 4 show the obtained results.
- V ⁇ , VP ⁇ , VMA, B, BF, and ⁇ HV indicate the following, respectively.
- the blank spaces for the structures denote that no observation was performed.
- V ⁇ area ratio of ferrite
- VMA total area ratio of martensite and austenite
- ⁇ HV standard deviation of micro-hardness of ferrite
- JIS No. 5 tensile test pieces were respectively collected in a direction perpendicular to the rolling direction.
- a tensile test was performed using these test pieces, and the yield strength (YS), the tensile strength (TS), the yield ratio (YR), and the total elongation (EL) were measured.
- a hole expanding test was performed based on “JFS T 1001 the hole expanding test method” of the Japan Iron and Steel Federation Standard, and the hole expanding rate (2) was measured.
- a pellicle sample was collected from each of the hot rolled steel sheets. Then, carbide containing at least one of Ti, V, and Nb precipitated in a grain of ferrite was observed using the transmission electron microscope (magnification: 200,000-fold), and the number density and the percentage of the precipitated element having the aspect ratio of 3 or less were obtained. The standard deviation of micro-hardness of the steel from which 80 area % or more polygonal ferrite could be obtained was measured through the method described above.
- Table 6 shows the obtained results.
- the sample numbers 39 to 42, and 44 to 47 since all the chemical compositions and the structures were within the range regulated by the present invention, desired mechanical characteristics were obtained.
- the sample number 43 the ⁇ HV exceeded the upper limit regulated by the present invention.
- desired mechanical characteristics could not be obtained.
- the sample number 48 the area ratio of polygonal ferrite fell short of the lower limit regulated by the present invention. As a result, desired mechanical characteristics could not be obtained.
- the steel sheet according to the present invention it is possible to inexpensively manufacture a high strength hot rolled steel sheet having a high yield ratio and excellent hole expansibility.
- the steel sheet according to the present invention also has excellent hole expansibility even during stretch flanges forming frequently employed for automobile components, particularly chassis components and the like. Therefore, the steel sheet industrially contributes to reducing weight and ensuring collision safety of vehicle bodies particularly in automobile fields.
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Mechanical Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Physics & Mathematics (AREA)
- Thermal Sciences (AREA)
- Crystallography & Structural Chemistry (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Heat Treatment Of Sheet Steel (AREA)
- Heat Treatment Of Steel (AREA)
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
PCT/JP2015/071845 WO2017022025A1 (ja) | 2015-07-31 | 2015-07-31 | 高強度熱延鋼板 |
Publications (1)
Publication Number | Publication Date |
---|---|
US20180209007A1 true US20180209007A1 (en) | 2018-07-26 |
Family
ID=57942560
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US15/744,690 Abandoned US20180209007A1 (en) | 2015-07-31 | 2015-07-31 | High strength hot rolled steel sheet |
Country Status (8)
Country | Link |
---|---|
US (1) | US20180209007A1 (zh) |
EP (1) | EP3330394B1 (zh) |
JP (1) | JP6485549B2 (zh) |
KR (1) | KR102079968B1 (zh) |
CN (1) | CN107849651B (zh) |
BR (1) | BR112018000633A2 (zh) |
MX (1) | MX2018001140A (zh) |
WO (1) | WO2017022025A1 (zh) |
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN113005352A (zh) * | 2021-02-08 | 2021-06-22 | 大连理工大学 | 一种外加纳米TiC强韧化马氏体钢的方法 |
US11242579B2 (en) * | 2016-09-22 | 2022-02-08 | Tata Steel Ijmuiden B.V. | Method of producing a hot-rolled high-strength steel with excellent stretch-flange formability and edge fatigue performance |
Families Citing this family (9)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN110656292A (zh) * | 2018-06-28 | 2020-01-07 | 上海梅山钢铁股份有限公司 | 一种抗拉强度440MPa级低屈强比高扩孔性热轧钢板 |
CN109047692B (zh) * | 2018-08-22 | 2021-01-26 | 江阴兴澄特种钢铁有限公司 | 一种能够在-60℃条件下使用的超薄规格高强钢板及其制造方法 |
KR102643337B1 (ko) * | 2019-07-10 | 2024-03-08 | 닛폰세이테츠 가부시키가이샤 | 고강도 강판 |
CN112522568A (zh) * | 2019-09-19 | 2021-03-19 | 宝山钢铁股份有限公司 | 一种耐火耐候钢板/带及其制造方法 |
BR112022008897A2 (pt) * | 2020-01-17 | 2022-08-23 | Nippon Steel Corp | Placa de aço e tubo de aço |
US20230140358A1 (en) * | 2020-03-19 | 2023-05-04 | Nippon Steel Corporation | Steel sheet |
MX2022012725A (es) * | 2020-04-17 | 2022-11-07 | Nippon Steel Corp | Lamina de acero laminada en caliente de alta resistencia. |
EP3925771A1 (en) | 2020-06-16 | 2021-12-22 | SSAB Technology AB | High strength steel product and method of manufacturing the same |
KR20240096056A (ko) * | 2022-12-19 | 2024-06-26 | 주식회사 포스코 | 강판 및 그 제조방법 |
Citations (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2013150669A1 (ja) * | 2012-04-06 | 2013-10-10 | 新日鐵住金株式会社 | 合金化溶融亜鉛めっき熱延鋼板およびその製造方法 |
Family Cites Families (15)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP3426465B2 (ja) | 1997-04-15 | 2003-07-14 | 新日本製鐵株式会社 | 靱性と加工性に優れた400〜800N/mm2級高強度熱延鋼板及びその製造方法 |
JP3882577B2 (ja) | 2000-10-31 | 2007-02-21 | Jfeスチール株式会社 | 伸びおよび伸びフランジ性に優れた高張力熱延鋼板ならびにその製造方法および加工方法 |
JP4411005B2 (ja) | 2003-04-04 | 2010-02-10 | 株式会社神戸製鋼所 | 成形性に優れた高強度熱延鋼板 |
CN100360698C (zh) * | 2003-04-21 | 2008-01-09 | 杰富意钢铁株式会社 | 高强度热轧钢板及其制造方法 |
JP4649868B2 (ja) * | 2003-04-21 | 2011-03-16 | Jfeスチール株式会社 | 高強度熱延鋼板およびその製造方法 |
JP5070732B2 (ja) | 2005-05-30 | 2012-11-14 | Jfeスチール株式会社 | 伸び特性、伸びフランジ特性および引張疲労特性に優れた高強度熱延鋼板およびその製造方法 |
JP4998755B2 (ja) * | 2009-05-12 | 2012-08-15 | Jfeスチール株式会社 | 高強度熱延鋼板およびその製造方法 |
JP5765080B2 (ja) | 2010-06-25 | 2015-08-19 | Jfeスチール株式会社 | 伸びフランジ性に優れた高強度熱延鋼板およびその製造方法 |
CN103038383B (zh) * | 2010-07-28 | 2014-12-24 | 新日铁住金株式会社 | 热轧钢板、冷轧钢板、镀锌钢板及这些钢板的制造方法 |
EP2746417B1 (en) * | 2011-08-17 | 2016-07-06 | Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd.) | High-strength hot-rolled steel plate |
JP5838796B2 (ja) * | 2011-12-27 | 2016-01-06 | Jfeスチール株式会社 | 伸びフランジ性に優れた高強度熱延鋼板およびその製造方法 |
PL2896715T3 (pl) * | 2012-09-26 | 2017-12-29 | Nippon Steel & Sumitomo Metal Corporation | Dwufazowa blacha stalowa cienka i sposób jej wytwarzania |
JP6058439B2 (ja) * | 2013-01-10 | 2017-01-11 | 株式会社神戸製鋼所 | 冷間加工性と加工後の表面硬さに優れる熱延鋼板 |
JP6177551B2 (ja) * | 2013-03-15 | 2017-08-09 | 株式会社神戸製鋼所 | 絞り加工性と加工後の表面硬さに優れる熱延鋼板 |
JP5892147B2 (ja) * | 2013-03-29 | 2016-03-23 | Jfeスチール株式会社 | 高強度熱延鋼板およびその製造方法 |
-
2015
- 2015-07-31 BR BR112018000633-5A patent/BR112018000633A2/pt not_active Application Discontinuation
- 2015-07-31 EP EP15900339.1A patent/EP3330394B1/en active Active
- 2015-07-31 MX MX2018001140A patent/MX2018001140A/es unknown
- 2015-07-31 JP JP2017532259A patent/JP6485549B2/ja active Active
- 2015-07-31 US US15/744,690 patent/US20180209007A1/en not_active Abandoned
- 2015-07-31 WO PCT/JP2015/071845 patent/WO2017022025A1/ja active Application Filing
- 2015-07-31 KR KR1020187002148A patent/KR102079968B1/ko active IP Right Grant
- 2015-07-31 CN CN201580082015.XA patent/CN107849651B/zh not_active Expired - Fee Related
Patent Citations (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2013150669A1 (ja) * | 2012-04-06 | 2013-10-10 | 新日鐵住金株式会社 | 合金化溶融亜鉛めっき熱延鋼板およびその製造方法 |
US20150140358A1 (en) * | 2012-04-06 | 2015-05-21 | Nippon Steel & Sumitomo Metal Corporation | Hot-dip galvannealed hot-rolled steel sheet and process for producing same |
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US11242579B2 (en) * | 2016-09-22 | 2022-02-08 | Tata Steel Ijmuiden B.V. | Method of producing a hot-rolled high-strength steel with excellent stretch-flange formability and edge fatigue performance |
CN113005352A (zh) * | 2021-02-08 | 2021-06-22 | 大连理工大学 | 一种外加纳米TiC强韧化马氏体钢的方法 |
Also Published As
Publication number | Publication date |
---|---|
BR112018000633A2 (pt) | 2018-09-18 |
EP3330394A1 (en) | 2018-06-06 |
EP3330394B1 (en) | 2020-08-26 |
KR20180019736A (ko) | 2018-02-26 |
MX2018001140A (es) | 2018-04-20 |
JP6485549B2 (ja) | 2019-03-20 |
CN107849651A (zh) | 2018-03-27 |
EP3330394A4 (en) | 2018-12-19 |
CN107849651B (zh) | 2019-09-03 |
WO2017022025A1 (ja) | 2017-02-09 |
JPWO2017022025A1 (ja) | 2018-05-31 |
KR102079968B1 (ko) | 2020-02-21 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
EP3330394B1 (en) | High_strength_ hot_rolled steel sheet | |
US10351936B2 (en) | High-strength hot-dip galvanized steel sheet and process for producing the same | |
KR102407357B1 (ko) | 고강도 냉연 강판 및 그의 제조 방법 | |
KR101988148B1 (ko) | 냉연 강판 및 그 제조 방법 | |
KR102186320B1 (ko) | 강판 및 도금 강판 | |
CN109563586B (zh) | 钢板及镀覆钢板 | |
RU2551726C1 (ru) | Высокопрочный холоднокатаный стальной лист с улучшенной способностью к локальной деформации и способ его получения | |
US10385431B2 (en) | High strength steel sheet having high young's modulus and method for manufacturing the same | |
US20220333221A1 (en) | Cold-rolled steel sheet and method for producing same | |
US10472697B2 (en) | High-strength steel sheet and production method therefor | |
US20180023160A1 (en) | High-strength steel sheet and production method therefor | |
US11035019B2 (en) | High-strength steel sheet and production method therefor | |
EP3757242A1 (en) | High-strength steel sheet and manufacturing method therefor | |
US20180237881A1 (en) | Steel sheet | |
JP2014031538A (ja) | 熱延鋼板およびその製造方法 | |
KR20210134967A (ko) | 고강도 강판 | |
US10266906B2 (en) | High-strength galvanized steel sheet and method for manufacturing the same | |
US12031203B2 (en) | Galvannealed steel sheet | |
TWI554618B (zh) | 高強度熱軋鋼板 | |
WO2023037878A1 (ja) | 冷延鋼板およびその製造方法 | |
WO2023063347A1 (ja) | 熱間圧延鋼板 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: NIPPON STEEL & SUMITOMO METAL CORPORATION, JAPAN Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:SUGIURA, NATSUKO;TANAKA, YASUAKI;YOKOYAMA, TAKAFUMI;REEL/FRAME:044630/0346 Effective date: 20171229 |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION |
|
AS | Assignment |
Owner name: NIPPON STEEL CORPORATION, JAPAN Free format text: CHANGE OF NAME;ASSIGNOR:NIPPON STEEL & SUMITOMO METAL CORPORATION;REEL/FRAME:049257/0828 Effective date: 20190401 |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: NON FINAL ACTION MAILED |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: FINAL REJECTION MAILED |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: FINAL REJECTION MAILED |
|
STCB | Information on status: application discontinuation |