US20130209748A1

US20130209748A1 - Electronic component packaging sheet, and formed article thereof

Info

Publication number: US20130209748A1
Application number: US13/877,742
Authority: US
Inventors: Junpei Fujiwara; Tomohiro Osawa; Masatoshi Kawata
Original assignee: Denki Kagaku Kogyo KK
Current assignee: Denka Co Ltd
Priority date: 2010-10-07
Filing date: 2011-10-06
Publication date: 2013-08-15
Also published as: SG10201508314RA; WO2012046806A1; WO2012046815A1; SG189310A1; JPWO2012046815A1; JPWO2012046806A1; CN103153807B; KR101859788B1; CN103167993B; JP6022938B2; KR20140017495A; KR20140044765A; JP6022939B2; MY168734A; KR101868178B1; US20130189496A1; SG189854A1; CN103167993A; MY163532A; CN103153807A

Abstract

Disclosed is an electronic component packaging sheet including a surface conductive layer formed on the surface of at least one side of a substrate sheet. The substrate sheet includes 80,000 to 220,000 Mw of a styrene-conjugated diene block copolymer; 200,000 to 400,000 Mw of a polystyrene resin; and 150,000 to 210,000 Mw of an impact resistant polystyrene resin. The surface conductive layer includes an acrylic copolymer resin; and carbon nanotubes. The electronic component packaging sheet is a transparent conductive sheet having excellent thermoforming properties, good transparency after thermoforming, and sufficient electrostatic diffusion performance to maintain a low surface resistance value. The electronic component packaging sheet is particularly suited for the manufacture of embossed carrier tape.

Description

TECHNICAL FIELD

The present invention relates to a sheet for packaging electronic components such as IC's, LED's, connectors and capacitors, a method for production thereof, and a formed article formed from said sheet.

BACKGROUND ART

Generally, carrier tapes are used to store and transport compact electronic components such as IC's. In particular, polystyrene (PS) sheets are excellent in transparency and have good thermoforming properties, so they are widely used for being able to provide carrier tapes of good pocket shape (see, e.g., Patent Documents 1 and 2).
On the other hand, when transporting IC's, the buildup of static electricity due to friction between the carrier tape and the content, or generated when peeling cover tape adhered to the top surface of the carrier tape, can result in destruction of the IC circuits. Additionally, in the case of very small components, the components can adhere to the cover tape, causing problems when mounting them to electronic devices. In order to prevent such trouble, the surface of the carrier tape is often subjected to an anti-static treatment (see, e.g., Patent Documents 3 and 4). However, when treated with a normal anti-static agent, the surface resistance can become higher, and the anti-static effect can be insufficient. Therefore, methods of preventing the buildup of static electricity by providing a conductive layer comprising a conductive material such as carbon black or a metallic powder are known (e.g., Patent Document 5), but in that case, it is difficult to obtain sufficient transparency to read letters inscribed on the compact electronic components that are contained inside through the tape or to inspect the products as to whether or not they are acceptable.
Additionally, as anti-static treatments for the surface of films in general, processes of coating the surface of a substrate film consisting of polycarbonate (PC), polyethylene terephthalate (PET), polypropylene (PP) or the like and forming a conductive layer having a certain degree of transparency have been proposed for various applications (see, e.g., Patent Documents 6 and 7).
However, sheets and films coated with various types of conductive agents and conductive compositions on their surfaces as disclosed in Patent Documents 6 and 7 are such that the materials of the substrate films are mainly composed of PC, PET and PP substrates, and no specific examples have been disclosed in the technical field of the present invention of a favorable arrangement wherein the surface of a PS sheet is coated. Additionally, when forming pockets in carrier tape using a sheet having the surface of the substrate sheet of the material coated with a conductive agent, the surface resistance of the conductive layer can rise, reducing the effect of preventing the buildup of electrostatic charge. Furthermore, when a raw sheet is stored in a wound state, particularly in a high-temperature high-humidity environment, blocking and separation of the conductive layer due to blocking may occur.

Patent Document 1: JP 2003-55526 A
Patent Document 2: JP 2005-23268 A
Patent Document 3: JP 2003-253069 A
Patent Document 4: JP 2003-320605 A
Patent Document 5: JP H9-76424 A
Patent Document 6: JP 2003-308733 A
Patent Document 7: JP 2007-157440 A

SUMMARY OF THE INVENTION

The present invention was achieved in view of the above-described circumstances, and has the primary purpose of offering an electronic component packaging sheet capable of retaining good thermoforming ability due to use of a polystyrene (PS) type substrate sheet, wherein the transparency does not deteriorate after forming even when providing a surface conductive layer, and the surface resistance can be maintained at a satisfactory level.
Additionally, the present invention has another purpose of offering an electronic component packaging sheet with almost no blocking of sheets and almost no separation of the conductive layer due to blocking.
Furthermore, the present invention also has the purpose of offering a method suitable for producing the aforementioned electronic component packaging sheet and a formed article produced using the aforementioned electronic component packaging sheet.
The antistatic effect is achieved in a carrier tape having a conductive layer on the surface by dispersing static electricity, generated by friction with the contents during transport or the like as described above, through a conductive layer with sufficiently low surface resistance. Therefore, the present inventors performed diligent research into compositions wherein the surface resistance measured at standard intervals is held to a standard level or less and the transparency is retained even after pocket formation, whereupon they discovered that an electronic component packaging sheet capable of solving these problems, and with almost no blocking of the sheet resulting in separation of the conductive layer, can be obtained by applying carbon nanotubes to a substrate sheet using a polystyrene (PS) type resin composition, wherein each resin has a molecular weight in a specific range.
In other words, according to a first aspect, the present invention offers an electronic component packaging sheet having a surface conductive layer formed on a surface on at least one side of a substrate sheet, wherein the substrate sheet comprises a styrene-conjugated diene block copolymer (A), a polystyrene resin (B), and a high impact polystyrene resin (C), the components having the following weight-average molecular weights (Mw):
component (A): Mw=80,000 to 220,000;
component (8): Mw=200,000 to 400,000;
component (C): Mw=150,000 to 210,000; and
the surface conductive layer comprising an acrylic copolymer resin (D) and carbon nanotubes (E).
Regarding the above, according to one embodiment, the peak molecular weight by GPC of polymer blocks of styrenic monomers in component (A) is in the range of 30,000 to 120,000; and a half-width of a molecular weight distribution curve of the polymer blocks of the styrenic monomers is in the range of 0.8 to 1.25. The rubber component in a graft rubber in component (C) is preferably a diene rubber monomer chosen from the group consisting of 1,3-butadiene (butadiene), 2-methyl-1,3-butadiene (isoprene), 2,3-dimethyl-1,3-butadiene, 1,3-pentadiene, 1,3-hexadiene and 2-methylpentadiene, or a thermoplastic elastomer of a styrene-conjugated diene block copolymer wherein the diene component is at least 50 mass %. In one example, the particle size of the graft rubber in component (C) is φ 2.0 to 3.0 μm, and the proportion of rubber in the graft rubber in the substrate sheet is 0.75 to 1.90 mass %.
In another embodiment, the substrate sheet is formed of a resin composition comprising 29 to 65 mass % component (A), 51 to 15 mass % component (B) and 20 to 9 mass % component (C), and the melt tension of the substrate sheet at 220° C. is 10 to 30 mN.
In yet another embodiment of the present invention, the carbon nanotubes in the surface conductive layer are multiwall carbon nanotubes of diameter 3 to 15 nm and length 0.5 to 3 μm, and the amount of the multiwall carbon nanotubes contained in the surface conductive layer is 3 to 10 mass %.
The particle size in an aqueous dispersion of the acrylic copolymer resin (D) in the surface conductive layer is 80 to 350 nm and the glass transition temperature Tg the acrylic copolymer resin (D) in the surface conductive layer is 25 to 80° C. Additionally, in a preferred embodiment, the surface resistance of a formed article with a draw ratio for thermoforming of 1.5 to 3 times is on the order of 10⁵Ω to 10⁷Ω. Additionally, the coefficient of static friction of the conductive layer formed on the surface of the substrate sheet is preferably at least 0.85 and at most 2.50, and the coefficient of kinetic friction is preferably at least 0.85 and at most 2.50.
In another embodiment, the present invention offers a method for producing the aforementioned electronic component packaging sheet, comprising steps of preparing a mixed dispersion by mixing the aqueous dispersion of an acrylic copolymer with a dispersion of carbon nanotubes obtained by primary dispersion in a bead mill of carbon nanotubes in an aqueous solution of a sulfonic acid dispersant having aromatics in the molecule, and secondary dispersion in an ultrasonic dispersion; and applying the mixed dispersion onto at least one surface of the substrate sheet.
In yet another embodiment, the present invention offers a formed article formed by thermoforming the aforementioned electronic component packaging sheet, and this formed article may, for example, be an embossed carrier tape.
According to the present invention, by using a polystyrene (PS) type substrate sheet, it is possible to obtain an electronic component packaging sheet that maintains good thermoforming properties, wherein the transparency after forming does not deteriorate even when providing a surface conductive layer, and the surface resistance can be retained at a satisfactory level. Additionally, the sheet almost never undergoes blocking or separation of the conductive layer.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows a formed article formed by thermoforming an electronic component packaging sheet in a pressure-forming machine according to an example of the present invention.

FIG. 2 shows standards for evaluation of thermoforming properties of an electronic component packaging sheet according to examples of the present invention.

FIG. 3 shows a method of measurement of surface resistance of a carrier tape formed article according to an example of the present invention.

MODES FOR CARRYING OUT THE INVENTION

Herebelow, modes for carrying out the present invention will be described in detail.
The electronic component packaging sheet according to an embodiment of the present invention has a surface conductive layer formed on the surface on at least one side of the substrate sheet. The substrate sheet is formed from a resin composition containing the respective components, i.e. a styrene-conjugated diene block copolymer (A), a polystyrene resin (B), and a high impact polystyrene resin (C), respectively having specific weight-average molecular weights, and the surface conductive layer comprises an acrylic copolymer resin (D), and carbon nanotubes (E).
The styrene-conjugated diene block copolymer (A) is a polymer including, in its structure, polymer blocks mainly comprising styrenic monomers and polymer blocks mainly comprising conjugated diene monomers. Examples of styrenic monomers include styrene, o-methylstyrene, p-methylstyrene, p-tert-butylstyrene, 1,3-dimethylstyrene, α-methylstyrene, vinylnapththalene, vinylanthracene and 1,1-diphenylethylene. In a particularly preferred embodiment of the invention, the monomers are mainly styrene, but one or more other components may be included as trace components.
Conjugated diene monomers are compounds having conjugated double bonds in their structure. Examples include 1,3-butadiene (butadiene), 2-methyl-1,3-butadiene (isoprene), 2,3-dimethyl-1,3-butadiene, 1,3-pentadiene, 1,3-hexadiene and 2-methylpentadiene, among which butadiene and isoprene are preferred. One or more types of conjugated diene monomers may be used. The polymer blocks mainly comprising styrenic monomers refer to both polymer blocks consisting of only structures derived from styrenic monomers and polymer blocks comprising structures derived from styrenic monomers in an amount of at least 50 mass %. The polymer blocks mainly comprising conjugated diene monomers refer to both polymer blocks consisting of only structures derived from conjugated diene monomers and polymer blocks comprising structures derived from conjugated diene monomers in an amount of at least 50 mass %. The conjugated diene content in the styrene-conjugated diene block copolymer (A), for every 100 parts by mass of component (A), should preferably be 10 to 25 mass % in view of the mechanical properties of the substrate sheet. Here, the conjugated diene content refers to the proportional mass of structures derived from conjugated diene monomers in the entire copolymer.
One or more types of the styrene-conjugated diene block copolymer (A) may be used. In the present invention, when the conjugated diene is butadiene, for example, the styrene-conjugated diene block copolymer may be either a styrene-butadiene (SB) bipolymer or a styrene-butadiene-styrene (SBS) terpolymer, and may be a resin composed of a plurality of blocks, with three or more styrene blocks and two or more butadiene blocks. Furthermore, it may have a so-called tapered block structure wherein the component ratio of styrene and butadiene blocks continuously changes between respective blocks. Additionally, the styrene-conjugated diene block copolymer may be one that is commercially available used as is.
In the styrene-conjugated diene block copolymer (A) used in the present invention, the polymer blocks of styrenic monomers in the component preferably have a peak molecular weight as measured by GPC in the range of 30,000 to 120,000, and the molecular weight distribution curve of the styrenic monomer blocks preferably has a half-width in the range of 0.8 to 1.25, more preferably 1.05 to 1.25. Use of those in this range enables good formability to be achieved. The molecular weight distribution curve of the styrene blocks in component (A) can be determined by the following method. First, component (A) is subjected to oxidative cleavage by chloroform using osmium tetroxide as a catalyst, in accordance with the method described in I. M. Kolthoff, et al., J. Polym. Sci., 1, 429 (1946), then the resulting styrene blocks are dissolved in a tetrahydrofuran solvent and measured by GPC. The molecular weight curve can then be used to determine the styrene-converted peak molecular weight using standard polystyrene (monodisperse). The GPC measurements may be in accordance with conventional techniques, with the main measurement conditions being as follows:
Column temperature: 40° C.
Detection method: differential refractometry
Mobile phase: tetrahydrofuran
Sample concentration: 2 mass %
Calibration curve: from standard polystyrene (monodisperse)
The half-width can be determined using this molecular weight distribution curve for the styrene blocks. Specifically, when the molecular weight is placed on the horizontal axis using a logarithmic scale with the range of 1000 to 1,000,000 being 15 cm, and the concentration (mass ratio) is placed on the vertical axis at an arbitrary height, the width of the peak on the horizontal axis at a height of 50% of the peak top is the half-width. In this case, the height of the peak top should be that perpendicular to the horizontal axis, and the width of the peak at 50% of the height should be parallel to the horizontal axis. The half-width of the molecular weight distribution curve of the styrene blocks correlates with the molecular weight distribution of the block copolymer. While the method of adjusting the molecular weight distribution is not particularly restricted, block copolymers of different molecular weights can be obtained by methods such as adjusting the time of addition of the initiator during the polymerization of styrene block parts in component (A).
The polystyrene resin (B) is a resin generally known as a GPPS, mainly comprising styrenic monomers, but may contain one or more aromatic vinyl compounds such as o-methylstyrene, p-methylstyrene, p-tert-butylstyrene, 1,3-dimethylstyrene, α-methylstyrene, vinylnaphthalene, vinylanthracene and 1,1-diphenylethylene as a trace component, and a commercially available resin may be used.
The high impact polystyrene resin (C) is a resin generally known as a HIPS, and is a polystyrene resin comprising microparticulate graft rubber to which styrenic monomers have been grafted. Graft rubber is a type of rubber wherein styrenic monomers have been graft-copolymerized to a rubber component as described below to form graft branches. The graft rubber content in component (C) can be determined by dissolving in a mixed solvent of MEK and acetone at a mass ratio of 50/50, recovering the undissolved portion by centrifugation, and calculating from the mass thereof. Examples of the rubber components in the graft rubber include, for example, diene rubbers with 1,3-butadiene (butadiene), 2-methyl-1,3-butadiene (isoprene), 2,3-dimethyl-1,3-butadiene, 1,3-pentadiene, 1,3-hexadiene and 2-methylpentadiene as monomers. Additionally, a thermoplastic elastomer which is a styrene-conjugated diene block copolymer wherein the diene component takes up at least 50 mass % may be used. Among these, polybutadiene and styrene-butadiene block copolymers are preferred.
With the graft rubber in component (C), having a particle size in the range of at least φ 2.0 μm and at most φ 3.0 μm, preferably at least φ 2.3 μm and at most φ 2.7 μm, the substrate sheet excels in transparency and strength properties. The graft rubber particle size here refers to the average particle size of the graft rubber component measured by a laser diffraction type particle analyzer. Additionally, in the substrate sheet of the present invention, the graft rubber content derived from component (C) in the substrate sheet when the substrate sheet is defined as 100 mass % should be 0.75 to 1.90 mass % in order to achieve balance between impact resistance and transparency of the substrate sheet. The graft rubber content in component (C) and the proportional content of component (C) in the substrate sheet should be adjusted to put the graft rubber content of the substrate sheet in the above-indicated ranges.
The substrate sheet of the present invention is formed of a resin composition containing 29 to 65 mass % of component (A), 51 to 15 mass % of component (B), and 20 to 9 mass % of component (C), with (A) to (C) totaling 100 mass %. By setting the composition in these ranges, a substrate sheet that is satisfactory in strength properties, impact resistance and transparency can be obtained.
The substrate sheet for an electronic component packaging sheet according to one embodiment of the present invention is preferably a resin wherein the weight-average molecular weights (Mw) of the respective components (A) to (C) are in the following ranges:
Component (A): Mw=80,000 to 220,000
Component (B): Mw=200,000 to 400,000
Component (C): Mw=130,000 to 210,000
Here, the weight-average molecular weight (Mw) can be determined from a standard polystyrene-converted molecular weight distribution curve determined by conventional methods using GPC.
By using resins in such ranges of weight-average molecular weight, not only does it become possible to adjust the appropriate range of melt tension for this resin composition as described below, but also a sheet with a good balance of strength properties and transparency can be obtained, with very good formability when thermoforming the resulting substrate sheets into carrier tape or the like, enabling good pocket formation even for deep draw forming.
Here, the melt tension is a value (mN) measured using a melt tension measuring apparatus with an orifice diameter of 1.0 mm φ, and orifice length of 10 mm and winding speeds of 10, 30 and 50 m/min. By using components (A) to (C) with weight-average molecular weights in the above-described ranges, and adjusting the blending ratio of the components (A) to (C) as needed, the melt tension at 220° C. of the resulting resin composition can be adjusted, preferably to the range of 10 to 30 mN. When the melt tension is in this range, a substrate sheet with particularly good forming properties can be obtained when thermoforming the substrate sheet to obtain a container. When the melt tension is less than 10 mN, holes may form when thermoforming the substrate sheet, and when exceeding 30 mN, the formativeness (sharpness) of the pockets of the formed articles may be deficient.
The method of producing the substrate sheet of the present invention using the resin composition comprising the above components (A) to (C) is not particularly limited and the sheet may be produced by a common method. For example, the components (A) to (C) can be blended in a predetermined ratio and mixed using a commonly used mixer such as a tumbler, then kneaded in an extruder to form pellet-shaped compounds. These pellet-shaped compounds can then be extruded using a φ 65 mm extruder with a T-die to produce substrate sheets. Additionally, so-called “ear” portions formed during the substrate sheet extrusion process can be pulverized and returned to the substrate sheet within a range not greatly affecting the strength of the substrate sheet and the formed article after forming.
While the thickness of the substrate sheet is not particularly limited, when considering the application, it should be from 50 μm to 3 mm, preferably 100 μm to 1 mm, and more preferably 150 to 600 μm.
The surface conductive layer formed on the surface of at least one side of the substrate sheet comprises carbon nanotubes and an acrylic copolymer resin. The carbon nanotubes are preferably multiwall carbon nanotubes (MWCNT). MWCNT is composed of tubes consisting of a plurality of tubular carbon walls of different diameter bundled into multiple layers around a central axis, the carbon walls being formed from a hexagonal mesh structure of carbon. The MWCNT may be formed with the carbon walls in a multilayered helical structure. The MWCNT is preferably of a type wherein the carbon walls are in 2 to 30 layers, more preferably 2 to 15 layers. Use of such a MWCNT greatly improves the transparency of the resulting conductive transparent film. More specifically, a MWCNT of diameter φ 3 to 15 nm and length 0.5 to 3 μm should preferably be used. The MWCNT may be dispersed in the aqueous composition such as to be individually separated, or they may be dispersed with a plurality being bundled together.
The acrylic copolymer resin should preferably be used as a binder in the form of an aqueous dispersion, and should preferably have a particle size (the average particle size here is the median diameter value) of 80 to 350 nm, more preferably 100 to 250 nm. By using those with a particle size in the range of 80 to 350 nm, the coefficient of static friction and the coefficient of kinetic friction can be adjusted to at least 0.85 and at most 2.50. While the transparency after coating could be increased by using an acrylic copolymer resin with a particle size of less than 80 nm, there is a risk of the coefficient of static friction and the coefficient of kinetic friction becoming less than 0.85, resulting in blocking and separation of the conductive layer due to blocking. On the other hand, the coefficient of static friction and the coefficient of kinetic friction could be raised by setting the particle size of the acrylic copolymer resin to at least 350 nm, but that may reduce the transparency and make it insufficient. Additionally, the glass transition temperature Tg of the acrylic copolymer resin should preferably be 25 to 80° C. in order to adequately retain the conductivity after thermoforming the sheet of the present invention.
The surface conductive layer comprising carbon nanotubes and an acrylic copolymer resin can be formed on the substrate sheet surface using a known method such as those described in the above-mentioned Patent Document 4 and JP 2005-290045 A.
In a preferred embodiment of the present invention, a mixed dispersion of carbon nanotubes and acrylic copolymer resin is obtained by preparing a carbon nanotube dispersion by primary dispersion in a bead mill of carbon nanotubes in an aqueous solution of a sulfonic acid type dispersant having aromatics in the molecule, and secondary dispersion in an ultrasonic dispersion, and mixing therewith an aqueous dispersion of an acrylic copolymer as a binder. Next, this mixed dispersion is applied to the surface on at least one side of the substrate sheet by a gravure coater or the like, then dried to form a surface conductive layer.
By forming the substrate sheet from a resin composition comprising resin components (A) to (C) of specific weight-average molecular weights and forming a surface conductive layer comprising carbon nanotubes (E) and an acrylic copolymer resin (D) on the surface thereof, it is possible to obtain a sheet for packaging electronic components such as an embossed carrier tape, with excellent thermoforming properties, wherein the transparency will not be reduced after forming, and the surface resistance is maintained at a satisfactory level. In particular, when a carrier tape or the like is thermoformed from a substrate sheet having formed thereon a surface conductive layer comprising preferably 3 to 10 mass % of carbon nanotubes, particularly MWCNT, preferably of diameter φ 3 to 15 nm and length 0.5 to 3 μm, in the surface conductive layer, the formability of the surface conductive layer is very good and the surface conductive layer will exhibit good transparency even after forming.

EXAMPLES

Herebelow, Examples 1 to 18 and Comparative Examples 1 to 7 of the sheet for packaging electronic components of the present invention shall be explained with reference to Tables 1 to 6 and FIGS. 1 to 3.
Table 1-1 to Table 1-3 show the specifications for each component (A), (B) and (C) in the resin composition of the substrate sheet used in the examples and comparative examples.
Table 1-1 shows the weight-average molecular weight (Mw) and butadiene/styrene mass % ratio of the compositions of the styrene-conjugated diene block copolymer (A), and the peak molecular weight of the styrene blocks and peak half-width of the styrene blocks in component (A). Table 1-2 shows the weight-average molecular weight (Mw) of the compositions of the polystyrene resin (B). Table 1-3 shows the weight-average molecular weight (Mw), graft rubber part (mass %) and graft rubber average particle size (μm) of the compositions of the high impact polystyrene resin (C).

TABLE 1-1

		Styrene	Styrene
Weight		Block	Block
Average	Butadiene/	Peak	Peak
Molecular	Styrene	Molecular	Half-width
Weight (Mw)	(Mass %)	Weight	(cm)

Styrene-	A-1	150,000	20/80	40,000	1.11
Conjugated	A-2	140,000	24/76	109,000	0.94
Diene	A-3	80,000	16/84	34,000	0.98
Copolymer	A-4	220,000	17/83	77,000	1.09
(A)	A-5	280,000	18/82	140,000	0.70
	A-6	70,000	40/60	15,000	1.30

	TABLE 1-2

	Weight
	Average
	Molecular
	Weight (Mw)

Polystyrene (B)	B-1	330,000
	B-2	290,000
	B-3	210,000
	B-4	370,000
	B-5	470,000
	B-6	120,000

TABLE 1-3

Weight		Graft Rubber
Average		Average
Molecular	Graft Rubber	Particle Size
Weight (Mw)	Part (mass %)	(μm)

High-Impact	C-1	180,000	8.6	2.5
Polystyrene (C)	C-2	190,000	7.9	2.0
	C-3	150,000	8.8	2.3
	C-4	200,000	7.4	2.3
	C-5	100,000	6.1	1.8
	C-6	250,000	7.3	2.8

Table 24 and Table 2-2 show the specs for components (D) and (E) in the surface conductive layer used for the examples and the comparative examples.
Table 2-1 shows the compositions (mass %) of the acrylic copolymer resin (D) as well as the glass transition point (° C.) and average particle size (nm) of the resins, and Table 2-2 shows the shapes of the carbon nanotubes (CNT) (E), among which NC 7000 in E-1 is an MWCNT produced by Nanocyl, and Graphistrength C100 in E-2 is an MWCNT produced by Arkema.

TABLE 2-1

Composition in Resin (mass %)	Glass	Average

	Methyl	Butyl	Butyl	Cyclohexyl	Transition	Particle
No	Methacrylate	Acrylate	Methacrylate	Methacrylate	Point (° C.)	Size (nm)

Acrylic	D-1	40	41	8	11	40	130
Copolymer	D-2	73	8	8	11	75	210
Resin (D)	D-3	75	7	7	11	85	870
	D-4	81	4	4	11	90	230
	D-5	40	35	14	11	70	70

	TABLE 2-2

	Shape

	diameter (nm)	length (μm)	Note

CNT (E)	E-1	9.5	1.5	NC-7000 (Nanocyl)
	E-2	12.0	5.0	Graphistrength C100
				(Arkema)

Table 3 shows the component ratios by mass % of the components (A), (13) and (C) used in Examples 1 to 18 and Comparative Example 1 to 7, and the graft rubber content in the substrate sheet, and Table 4 shows the melt tension measured at winding speeds of 10, 30 and 50 mm/min for the resin composition of the substrate sheet. The method of measuring melt tension will be discussed below.

	TABLE 3

	Styrene-Conjugated
	Diene Block	Polystyrene
	Copolymer (A) (mass %)	(B) (mass %)

	A-1	A-2	A-3	A-4	A-5	A-6	B-1	B-2	B-3	B-4	B-5	B-6

Example 1	58						33
Example 2		55						25
Example 3			58				33
Example 4				58			33
Example 5	58								33
Example 6	58									33
Example 7	58						33
Example 8	40						51
Example 9	35						45
Example 10	58						33
Example 11	58						33
Example 12	58						33
Example 13	58						33
Example 14	58						33
Example 15	58						33
Example 16	58						33
Example 17	58						33
Example 18	58						33
Comp. Example 1	58						33
Comp. Example 2	58						33
Comp. Example 3					58						33
Comp. Example 4						58						33
Comp. Example 5	100
Comp. Example 6	58
Comp. Example 7	58						33

	High Impact	GraftRubber
	Polystyrene (C) (mass %)	Content

	C-1	C-2	C-3	C-4	C-5	C-6	(mass %)

Example 1	9						0.77
Example 2		20					1.58
Example 3	9						0.77
Example 4	9						0.77
Example 5	9						0.77
Example 6				9			0.66
Example 7			9				0.79
Example 8	9						0.77
Example 9	20						1.72
Example 10	9						0.77
Example 11	9						0.77
Example 12	9						0.77
Example 13	9						0.77
Example 14	9						0.77
Example 15	9						0.77
Example 16	9						0.77
Example 17	9						0.77
Example 18	9						0.77
Comp. Example 1	9						0.77
Comp. Example 2	9						0.77
Comp. Example 3						9	0.65
Comp. Example 4					9		0.54
Comp. Example 5							0.00
Comp. Example 6	42						3.61
Comp. Example 7	9						0.77

TABLE 4

Melt
Tension	Melt Tension	Melt Tension
(10 m/	(30 m/min)	(50 m/min)
min) mN	mN	mN

Example 1	18	20	21
Example 2	15	17	18
Example 3	14	15	16
Example 4	19	21	22
Example 5	19	20	22
Example 6	20	21	22
Example 7	17	18	19
Example 8	26	30	31
Example 9	22	26	27
Example 10	18	20	21
Example 11	18	20	21
Example 12	18	20	21
Example 13	18	20	21
Example 14	18	20	21
Example 15	18	20	21
Example 16	18	20	21
Example 17	18	20	21
Example 18	18	20	21
Comp. Example 1	18	20	21
Comp. Example 2	18	20	21
Comp. Example 3	31	33	34
Comp. Example 4	8	10	11
Comp. Example 5	10	11	13
Comp. Example 6	14	15	15
Comp. Example 7	18	20	21

Table 5 shows the component ratios by mass % of the acrylic copolymer resin (D) and the carbon nanotubes (E) in the surface conductive layer formed on the substrate sheets of Examples 1 to 18 and Comparative Examples 1 to 7. In Comparative Example 2, tin oxide with a particle size of φ 10 nm was used instead of the carbon nanotubes. Additionally, in Comparative Example 7, an aqueous dispersion of a water-soluble epoxy resin (bisphenol A) was used as a binder instead of an aqueous dispersion of an acrylic copolymer resin.

	TABLE 5

	Acrylic Copolymer	CNT (E)
	Resin (D) mass %	mass %

	D-1	D-2	D-3	D-4	D-5	E-1	E-2

Example 1	95					5
Example 2	95					5
Example 3	95					5
Example 4	95					5
Example 5	95					5
Example 6	95					5
Example 7	95					5
Example 8	95					5
Example 9	95					5
Example 10	95						5
Example 11	97					3
Example 12	90					10
Example 13		95				5
Example 14			95			5
Example 15				95		5
Example 16					95	5
Example 17		95				5
Example 18		95				5
Comp. Example 1	100

Comp. Example 2

85

15 (*¹)

Comp. Example 3	95	5
Comp. Example 4	95	5
Comp. Example 5	95	5
Comp. Example 6	95	5

Comp. Example 7	95 (*²)	5

Note:
(*¹) Tin oxide, particle size 10 nm
(*²) Epoxy binder

Example 1

As shown in Table 3, 58 mass % of the styrene-butadiene block copolymer (A) of A-1 in Table 1-1 (Mw: 150,000; butadiene content 20 mass %), 33 mass % of the polystyrene resin (B) of B-1 in Table 1-2 (Mw: 330,000) and 9 mass % of the high impact polystyrene resin (C) of C-1 in Table 1-3 (Mw: 180,000; rubber particle size 25 μm) were dry-blended and formed into a film by a φ 40 mm extruder (L/D=26) and 600 mm wide T-dice, resulting in a substrate sheet of thickness 250 μm. Additionally, 5 parts by mass of an aqueous dispersion of the multiwall carbon nanotubes (MWCNT) (E) of E-1 shown in Table 2-2 (fiber diameter 95 nm, fiber length 1.5 μm) and 95 parts by mass of an aqueous dispersion of the acrylic copolymer (D) of D-1 shown in Table 2-1 (glass transition point: 40° C.) were mixed together to obtain a mixed dispersion wherein the component ratios in a conductive layer formed on the surface of a substrate sheet is 5 mass %195 mass % as shown in Table 5. Next, this mixed dispersion was coated onto the surface of a corona-treated substrate sheet in a gravure coater using a gravure roll, then dried at 90° C. to form a surface conductive layer of average thickness 3 μm after drying. The results of evaluation tests of a substrate sheet on which this surface conductive layer was formed are shown in Table 6.

Examples 2 to 18 and Comparative Examples 1 to 7

Substrate sheets having surface conductive layers formed thereon were obtained in the same manner as Example 1, aside from the fact that as the resin components (A) to (C), resins chosen from A-1 to A-6 in Table 1-1, B-1 to B-6 in Table 1-2 and C-1 to C-6 in Table 1-3 were used and blended at the mass ratios shown in Table 3 to prepare the substrate sheet, and a mixed aqueous dispersion of components (D) and (E) chosen from D-1 to D-5 shown in Table 2-1 and E-1 and E-2 shown in Table 2-2 as shown in Table 5.
Of Examples 1 to 18, only Example 10 used E-2 shown in Table 2-2 as the MWCNT. Example 15 used D-4 as the acrylic copolymer and Example 16 used D-5 as the acrylic copolymer.
Of Comparative Examples 1 to 7, Comparative Example 1 does not contain a MWCNT. In Comparative Example 2, tin oxide of particle size φ 10 nm was used instead of a MWCNT. In Comparative Example 3, the polystyrene of B-5 shown in Table 1-2 (weight-average molecular weight Mw: 470,000) was used as component (B), and in Comparative Example 4, B-6 (Mw: 120,000) shown in Table 1-2 was used as component (B) and the high impact polystyrene of C-5 shown in Table 1-3 (weight-average molecular weight Mw: 100,000) was used as component (C). Comparative Example 5 contained neither component (B) nor component (C), and Comparative Example 6 did not contain component (B). In Comparative Example 7, an aqueous dispersion of a water-soluble epoxy resin (bisphenol A) was used as a binder instead of the aqueous dispersion of an acrylic copolymer resin.
The evaluation results for the examples and comparative examples are shown together in Table 6.

TABLE 6

	Surface		Cond		Buckle	Coefficient		Surf Res
Formability	Resistance (Ω)	Draw	Crack	Haze (%)	Str (N)	Friction	Blk	after Blk

Ftiv

Hol

Sheet

Article

Ratio

Y/N

Sheet

Bottm

Article

Stat

Kin

Y/N

Eval. (Ω)

Example 1	5	N	5.0 × 10⁴	7.8 × 10⁶	2.8	N	24	8	20	1.51	1.50	N	5.1 × 10⁴
Example 2	5	N	4.3 × 10⁴	7.1 × 10⁶	2.8	N	29	13	18	1.51	1.50	N	4.3 × 10⁴
Example 3	5	N	7.0 × 10⁴	4.5 × 10⁵	1.8	N	23	7	27	1.52	1.51	N	7.5 × 10⁴
Example 4	5	N	6.2 × 10⁴	5.4 × 10⁵	1.8	N	23	8	31	1.51	1.50	N	6.3 × 10⁴
Example 5	5	N	7.9 × 10⁴	5.3 × 10⁵	1.8	N	24	8	31	1.52	1.50	N	8.1 × 10⁴
Example 6	5	N	8.7 × 10⁴	6.8 × 10⁶	2.8	N	23	8	21	1.52	1.50	N	8.9 × 10⁴
Example 7	5	N	6.6 × 10⁴	7.1 × 10⁶	2.8	N	23	7	19	1.52	1.51	N	6.9 × 10⁴
Example 8	5	N	8.8 × 10⁴	7.6 × 10⁶	2.8	N	24	8	24	1.51	1.50	N	9.1 × 10⁴
Example 9	5	N	8.9 × 10⁴	7.7 × 10⁶	2.8	N	29	13	22	1.51	1.50	N	9.1 × 10⁴
Example 10	5	N	9.4 × 10⁴	1.8 × 10⁸	2.8	N	24	8	20	1.52	1.51	N	9.5 × 10⁴
Example 11	5	N	8.9 × 10⁴	3.1 × 10⁷	1.8	N	23	7	30	1.50	1.49	N	8.7 × 10⁵
Example 12	5	N	<1.0 × 10⁴	2.3 × 10⁵	1.8	N	24	8	30	1.54	1.52	N	<1.0 × 10⁴
Example 13	5	N	5.4 × 10⁴	3.6 × 10⁶	2.8	N	24	8	20	1.55	1.53	N	5.3 × 10⁴
Example 14	5	N	5.7 × 10⁵	2.1 × 10⁶	2.8	N	45	25	20	1.64	1.62	N	5.9 × 10⁵
Example 15	5	N	7.6 × 10⁴	5.2 × 10¹⁰	2.8	Y (*²)	26	10	20	1.51	1.50	N	7.9 × 10⁴
Example 16	5	N	5.2 × 10⁴	6.8 × 10⁶	2.8	N	24	8	20	0.75	0.73	Y	>1.0 × 10¹⁴
Example 17	5	N	6.1 × 10⁴	5.6 × 10⁷	3.2	N	24	8	17	1.52	1.51	N	6.3 × 10⁴
Example 18	5	N	5.9 × 10⁴	5.1 × 10¹¹	4.0	Y (*²)	26	11	16	1.51	1.50	N	5.7 × 10⁴
Comp.	5	N	>1.0 × 10¹⁴	>1.0 × 10¹⁴	2.8	N	24	7	20	1.40	1.38	N	>1.0 × 10¹⁴
Example 1
Comp.	5	N	8.5 × 10⁷	>1.0 × 10¹⁴	2.8	Y (*²)	23	8	20	1.55	1.54	N	8.8 × 10⁷
Example 2
Comp.	2 (*¹)	N	7.8 × 10⁴	5.2 × 10⁶	2.8	N	24	9	35	1.52	1.51	N	7.5 × 10⁴
Example 3
Comp.	5	N	7.5 × 10⁴	6.5 × 10⁶	2.8	N	23	8	10	1.51	1.50	N	7.8 × 10⁴
Example 4
Comp.	5	N	8.5 × 10⁴	5.4 × 10⁶	2.8	N	7	6	8	1.52	1.50	N	8.7 × 10⁴
Example 5
Comp.	5	N	8.0 × 10⁴	5.8 × 10⁶	2.8	N	40	19	10	1.52	1.50	N	8.1 × 10⁴
Example 6
Comp.	5	N	4.8 × 10⁵	>1.0 × 10¹⁴	2.8	Y (*²)	24	8	20	1.91	1.89	N	4.8 × 10⁵
Example 7

Note
(*¹) The shape of the corner portions was poor.
(*²) Cracks occurred in the conductive layer during formation.

The raw material resins used in Examples 1 to 18 and Comparative Examples 1 to 7, and formed articles obtained by forming a surface conductive film on the surfaces of substrate sheets prepared from these raw material resins, then embossing, were evaluated by the below-described measurement methods.

(Molecular Weight of Raw Material Resin)

The molecular weights of the resin raw materials of (A) to (C) were determined as a standard polystyrene-converted weight-average molecular weight (Mw) using GPC (gel permeation chromatography). Tetrahydrofuran was used as the measuring solvent.

(Melt Tension of Raw Material Resin)

The melt tension (mN) was measured using a melt tension measuring apparatus (Toyo Seiki) with an orifice diameter of φ 1.0 mm, an orifice length of 10 mm, windup speeds of 10, 30 and 50 m/min and a cylinder temperature of 220° C.

(Glass Transition Temperature of Raw Material Resin)

A dispersion comprising an aqueous dispersion of an acrylic copolymer resin was dried at 90° C.×1 min and formed into a thin film to create samples for use as measuring samples, which were measured using a DSC (differential scanning calorimeter manufactured by SII).

(Particle Size of Acrylic Copolymer Resin)

A Horiba laser diffraction/scattering type particle size distribution measurer LA-920 (the average particle size here was the median diameter) was used to take measurements.

(Coefficient of Friction Measurement)

The coefficient of static friction and the coefficient of kinetic friction were measured in accordance with JIS-7125 using a friction measurer (Toyo Seiki). The measurements were made with a sample size of 63 mm×63 mm, a load of 200 g and a speed of 500 mm/min. Additionally, the coefficient of static friction and the coefficient of kinetic friction were the coefficients of friction between conductive layers.

(Blocking)

Substrate sheets coated on both sides were slit into sheet samples 44 mm wide to produce 200 m wound slit raw sheets (winding tension 1.0 kgf). The slit raw sheets were stored for one week at 52° C.×95% RH. After one week, the slit raw sheets were extracted and the sheets were wound out. After unwinding, they were inspected for the presence or absence of blocking between the conductive layers on the surfaces of overlapping substrate sheets, and separation of the conductive layer due to blocking was evaluated by measuring the surface resistance between overlapping conductive layers at 23° C.×50% RH in accordance with JIS K6911, and observing whether the surface resistance increased.

(Formability of Sheets)

Using a pressure-forming machine on substrate sheets having a surface conductive layer formed on each example and comparative example, pockets were formed of draw ratio 1.8 (pocket depth 3.0 mm), draw ratio 2.8 (pocket depth 6.0 mm), draw ratio 3.2 (pocket depth 9.0 mm) and draw ratio 4.0 (pocket depth 12.0 mm) and their formativeness was evaluated by evaluating the “sharpness” of the formed articles into five grades. Additionally, the pockets were visually inspected for the presence or absence of holes due to formation. The surface conductive layers were visually inspected for the presence or absence of cracks in the bottom surfaces of the pockets. FIG. 1 shows a formed article obtained by molding with a pressure-forming machine.
The draw ratio was calculated using the below-given formula based on the dimensions of the formed article. Additionally, in these formed articles, the area of the bottom surface of the pockets was roughly equal to the area of the mouth portions of the pockets (areas enclosed by the solid lines).

Method of Calculating Draw Ratio:

$\begin{matrix} Draw Ratio = pocket area \\ (bottom area + four side areas) / \\ pocket mouth area \\ = (X \times Y) + 2 \times (X \times Z) + 2 \times (X \times Y) / (X \times Y) \end{matrix}$
(where X is the formed article advancement direction, Y is the direction perpendicular to the formed article advancement direction and Z is the pocket depth).

Pressure forming: heater temperature 220° C.

As shown in FIG. 2, the pocket corners 11 of the formed articles 10 having pockets 20 formed therein were inspected, and their “sharpness” was visually evaluated into five grades in accordance with the samples 1 to 5 shown in FIG. 2.

(Transparency of Formed Articles)

The pocket side surfaces of the formed articles obtained by forming in a pressure-forming machine were cut out, clamped between black plates with holes of φ 6 mm (2826 mm²), and the bottom surfaces of the formed articles were measured for their haze and total light transmittance in accordance with the ASTM D1044 standard using a Haze-gard plus from BYK Gardner of Germany. The standard haze value was such that the haze was 15% or less at the bottom surface of the formed article in order to provide transparency enabling components placed in the formed articles to be visually confirmed.

(Surface Resistance of Formed Article)

Measurements were made at 23° C.×50% RH. The surface resistance was measured using a Mitsubishi Chemical Hiresta with a two-terminal probe (UA) as the probe. Additionally, the surface resistance of the entire pocket of the formed article was measured by a method as shown in FIG. 3. Additionally, the conductive layers on the pocket bottom surfaces and side surfaces were inspected by eye for the presence or absence of cracks during formation. Measurements were made by bringing a two-terminal probe into contact with the probe terminal contact positions 50 a and 50 b on the flanges 12 a and 12 b on both ends of the pocket. At this time, if the seal portions 13 a and 13 b of the carrier tape formed article 10 remain, then the conductive circuit 40 is formed on the seal portions 13 a, 13 b, so the entire pocket 20 cannot be measured. Therefore, as shown in FIG. 3, the seal portions 13 a, 13 b were cut along the dashed lines at cut positions 30 a, 30 b, the pocket side surfaces 60 a, 60 b were further cut away, and measurements were made while clamped in a jig of insulating material. The standard surface resistance value was on the order of 10⁵or less in a formed body with a draw ratio of 1.5 to 3 when thermoforming, and on the order of 10⁷or less for the formed article.

(Buckle Strength of Formed Article)

A Strograph (Toyo Seiki) was used to measure the strength of the pocket bottom surface portion of a formed article obtained by molding in a pressure-forming machine with the pocket mouth portion facing down, when compressed by 1.5 mm in the depth direction for a formed article of draw ratio 1.8 (pocket depth 3.0 mm), 3.0 mm for a formed article of draw ratio 2.8 (pocket depth 6.0 mm), 4.5 mm for a formed article of draw ratio 3.2 (pocket depth 9.0 mm) and 6.0 mm for a formed article of draw ratio 4.0 (pocket depth 12.0 mm), and this was recorded as the buckle strength. In the event of a buckle strength of 15 N or more, the formed article is viable for use as a container.
The results shown in Table 6 revealed the following.
(i) Examples 1 to 18 using polystyrene type resin compositions of weight-average molecular weights in the predetermined ranges for the substrate sheet exhibited excellent formability, formativeness and sufficient buckle strength. In contrast, Comparative Example 3 using B-5 having a weight-average molecular weight of 470,000 Mw for the polystyrene resin (B) of the substrate sheet and C-6 having a weight-average molecular weight of 250,000 Mw as the high impact polystyrene resin (C) had problems in the formativeness. Additionally, Comparative Example 4 using A-6 having a weight-average molecular weight of 70,000 Mw as the styrene-conjugated diene copolymer (A) in the substrate sheet and C-5 having a weight-average molecular weight of 100,000 Mw as the high impact polystyrene (C), Comparative Example 5 having a substrate sheet consisting only of the styrene-conjugated diene copolymer (A), and Comparative Example 6 not containing the polystyrene resin (B) all exhibited low buckle strength.
(ii) Examples 1 to 18 using polystyrene type resin compositions of weight-average molecular weights in the predetermined ranges for the substrate sheet and an acrylic copolymer resin (D) together with the carbon nanotubes (E) for the surface conductive layer exhibited relatively low surface resistances as both sheets and formed articles. In contrast, the surface resistance of Comparative Example 1 not containing a MWCNT in the surface conductive layer was high, on the order of 10¹⁴Ω for both sheet and formed article, and Comparative Example 2 using tin oxide instead of a MWCNT in the surface conductive layer and Comparative Example 7 using an epoxy as the binder in the surface conductive layer both had high surface resistances on the order of 10¹⁴Ω for the formed article, and resulted in cracking of the conductive layer in the formed article.
While the present invention has been explained by referring to embodiments above, the technical scope of the present invention is naturally not limited to the scope described by the above embodiments. Those skilled in the art will recognize that various modifications and improvements could be made to the above-described embodiments. Additionally, the fact that embodiments including such modifications or improvements can still be contained within the technical scope of the present invention will be readily apparent from the recitations of the claims.

INDUSTRIAL APPLICABILITY

By making use of known methods for forming (thermoforming) sheets such as vacuum forming, pressure forming and press forming on the sheets for packaging electronic components of the present invention, it is possible to obtain electronic component packaging containers of any shape such as carrier tapes (embossed carrier tapes) and trays. Using the sheets for packaging electronic components of the present invention, it is possible to form packaging containers of large container depth, and packaging containers of excellent strength can be obtained. In particular, they are very useful for embossment of carrier tape. After placing electronic components in the receptacle portions, the embossed carrier tape is covered by cover tape and wound into reels to form carrier tape bodies, which can then be used to store and transport electronic components. Carrier tape bodies contain electronic components inside a carrier tape. There are no particular limitations on the electronic components to be packaged, and examples include IC's, LED's (light emitting diodes), resistors and capacitors. Additionally, they can be used for packaging intermediary products or final products using such electronic components.

DESCRIPTION OF REFERENCE NUMBERS

10 formed article
11 pocket corner
12 a, 12 b flange
13 a, 13 b seal portion
20 pocket
30 a, 30 b cut position
40 conductive circuit
50 a, 50 b probe terminal contact position
60 a, 60 b pocket side surface

Claims

1. An electronic component packaging sheet having a surface conductive layer formed on a surface on at least one side of a substrate sheet, wherein

the substrate sheet comprises a styrene-conjugated diene block copolymer (A), a polystyrene resin (B), and a high impact polystyrene resin (C), the components having the following weight-average molecular weights (Mw):

component (A): Mw=80,000 to 220,000;

component (B): Mw=200,000 to 400,000;

component (C): Mw=150,000 to 210,000; and

the surface conductive layer comprising an acrylic copolymer resin (D) and carbon nanotubes (E).

2. The electronic component packaging sheet of claim 1, wherein the peak molecular weight by GPC of polymer blocks of styrenic monomers in component (A) is in the range of 30,000 to 120,000; and a half-width of a molecular weight distribution curve of the polymer blocks of the styrenic monomers is in the range of 0.8 to 1.25.

3. The electronic component packaging sheet of claim 1, wherein the rubber component in a graft rubber in component (C) is a diene rubber monomer chosen from the group consisting of 1,3-butadiene (butadiene), 2-methyl-1,3-butadiene (isoprene), 2,3-dimethyl-1,3-butadiene, 1,3-pentadiene, 1,3-hexadiene and 2-methylpentadiene, or a thermoplastic elastomer of a styrene-conjugated diene block copolymer wherein the diene component is at least 50 mass %.

4. The electronic component packaging sheet of claim 1, wherein the particle size of the graft rubber in component (C) is φ 2.0 to 3.0 μm, and the proportion of rubber in the graft rubber in the substrate sheet is 0.75 to 1.90 mass %.

5. The electronic component packaging sheet of claim 1, wherein the substrate sheet is formed of a resin composition comprising 29 to 65 mass % component (A), 51 to 15 mass % component (B) and 20 to 9 mass % component (C).

6. The electronic component packaging sheet of claim 1, wherein the melt tension of the substrate sheet at 220° C. is 10 to 30 mN.

7. The electronic component packaging sheet of claim 1, wherein the carbon nanotubes in the surface conductive layer are multiwall carbon nanotubes of diameter 3 to 15 nm and length 0.5 to 3 μm, wherein the amount of the multiwall carbon nanotubes contained in the surface conductive layer is 3 to 10 mass %.

8. The electronic component packaging sheet of claim 1, wherein the particle size in an aqueous dispersion of the acrylic copolymer resin (D) in the surface conductive layer is 80 to 350 nm.

9. The electronic component packaging sheet of claim 1, wherein the glass transition temperature Tg of the acrylic copolymer resin (D) in the surface conductive layer is 25 to 80° C.

10. The electronic component packaging sheet of claim 1, wherein the surface resistance of a formed article with a draw ratio for thermoforming of 1.5 to 3 times is on the order of 10⁵Ω to 10⁷Ω.

11. The electronic component packaging sheet of claim 1, wherein the coefficient of static friction of the conductive layer formed on the surface of the substrate sheet is at least 0.85 and at most 2.50, and the coefficient of kinetic friction is at least 0.85 and at most 2.50.

12. A method for producing the electronic component packaging sheet of claim 1 comprising steps of:

preparing a mixed dispersion by mixing the aqueous dispersion of an acrylic copolymer with a dispersion of carbon nanotubes obtained by primary dispersion in a bead mill of carbon nanotubes in an aqueous solution of a sulfonic acid type dispersant having aromatics in the molecule, and secondary dispersion in an ultrasonic dispersion; and

applying the mixed dispersion onto at least one surface of the substrate sheet.

13. A formed article obtained by thermoforming the electronic component packaging sheet of claim 1.

14. The formed article of claim 13, which is an embossed carrier tape.