US20110253947A1 - Aqueous dispersions containing of electrically conducting polymers containing high boiling solvent and additives - Google Patents
Aqueous dispersions containing of electrically conducting polymers containing high boiling solvent and additives Download PDFInfo
- Publication number
- US20110253947A1 US20110253947A1 US13/156,433 US201113156433A US2011253947A1 US 20110253947 A1 US20110253947 A1 US 20110253947A1 US 201113156433 A US201113156433 A US 201113156433A US 2011253947 A1 US2011253947 A1 US 2011253947A1
- Authority
- US
- United States
- Prior art keywords
- dispersion
- group
- layer
- electrically conductive
- conductive polymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
The present invention relates to electrically conductive polymer compositions, and their use in electronic devices. The compositions are an aqueous dispersion of at least one electrically conductive polymer doped with a non-fluorinated polymeric acid, at least one high-boiling polar organic solvent, and an additive selected from the group consisting of fullerenes, carbon nanotubes, and combinations thereof.
Description
- This application is a division of U.S. application Ser. No. 12/121,121, now allowed, which claims priority under 35 U.S.C. §119(e) from U.S. Provisional Application No. 60/938,786 filed on May 18, 2007, which is incorporated by reference herein in its entirety.
- 1. Field of the Disclosure
- This disclosure relates in general to aqueous dispersions of electrically conductive polymers containing solvent and additives, and their use in electronic devices.
- 2. Description of the Related Art
- Electronic devices define a category of products that include an active layer. Organic electronic devices have at least one organic active layer. Such devices convert electrical energy into radiation such as light emitting diodes, detect signals through electronic processes, convert radiation into electrical energy, such as photovoltaic cells, or include one or more organic semiconductor layers.
- Organic light-emitting diodes (OLEDs) are an organic electronic device comprising an organic layer capable of electroluminescence. OLEDs containing conducting polymers can have the following configuration:
-
- anode/buffer layer/EL material/cathode
with additional layers between the electrodes. The anode is typically any material that has the ability to inject holes into the EL material, such as, for example, indium/tin oxide (ITO). The anode is optionally supported on a glass or plastic substrate. EL materials include fluorescent compounds, fluorescent and phosphorescent metal complexes, conjugated polymers, and mixtures thereof. The cathode is typically any material (such as, e.g., Ca or Ba) that has the ability to inject electrons into the EL material. Electrically conducting polymers having low conductivity in the range of 10−3 to 10−7S/cm are commonly used as the buffer layer in direct contact with an electrically conductive, inorganic oxide anode such as ITO.
- anode/buffer layer/EL material/cathode
- Electrically conducting polymers which have the ability to carry a high current when subjected to a low electrical voltage, may have utility as electrodes for electronic devices. However, many conductive polymers have conductivities which are too low for use as electrodes. Furthermore, the mechanical strength of films made from the polymers, either self-standing or on a substrate, may not be sufficient for the electrode applications.
- Accordingly, there is a continuing need for improved conducting polymer compositions.
- There is provided an aqueous dispersion comprising at least one electrically conductive polymer doped with at least one non-fluorinated polymeric acid polymer, a high-boiling polar solvent, and an additive selected from the group consisting of carbon fullerenes, nanotubes, and combinations thereof.
- In another embodiment, there is provided a film formed from the above dispersion.
- In another embodiment, electronic devices comprising at least one layer comprising the above film are provided.
- The invention is illustrated by way of example and not limitation in the accompanying figures.
-
FIG. 1 is a schematic diagram of an organic electronic device. - Skilled artisans will appreciate that objects in the figures are illustrated for simplicity and clarity and have not necessarily been drawn to scale. For example, the dimensions of some of the objects in the figures may be exaggerated relative to other objects to help to improve understanding of embodiments.
- There is provided an aqueous dispersion of at least one electrically conductive polymer doped with at least one non-fluorinated polymeric acid, at least one high-boiling polar organic solvent, and an additive selected from the group consisting of carbon fullerenes, nanotubes, and combinations thereof. The above dispersion is referred to herein as the “new composition” and the “composite dispersion”.
- Many aspects and embodiments are described herein and are merely exemplary and not limiting. After reading this specification, skilled artisans will appreciate that other aspects and embodiments are possible without departing from the scope of the invention.
- Other features and benefits of any one or more of the embodiments will be apparent from the following detailed description, and from the claims. The detailed description first addresses Definitions and Clarification of Terms followed by the Doped Electrically Conductive Polymer, the Solvent, the Additive, Preparation of the Doped Electrically Conductive Polymer Composition, Buffer Layers, Electronic Devices, and finally, Examples.
- Before addressing details of embodiments described below, some terms are defined or clarified.
- The term “conductor” and its variants are intended to refer to a layer material, member, or structure having an electrical property such that current flows through such layer material, member, or structure without a substantial drop in potential. The term is intended to include semiconductors. In some embodiments, a conductor will form a layer having a conductivity of at least 10−7 S/cm.
- The term “electrically conductive” as it refers to a material, is intended to mean a material which is inherently or intrinsically capable of electrical conductivity without the addition of carbon black or conductive metal particles.
- The term “polymer” is intended to mean a material having at least one repeating monomeric unit. The term includes homopolymers having only one kind, or species, of monomeric unit, and copolymers having two or more different monomeric units, including copolymers formed from monomeric units of different species.
- The term “acid polymer” refers to a polymer having acidic groups.
- The term “acidic group” refers to a group capable of ionizing to donate a hydrogen ion to a Brønsted base.
- The term “highly-fluorinated” refers to a compound in which at least 90% of the available hydrogens bonded to carbon have been replaced by fluorine.
- The terms “fully-fluorinated” and “perfluorinated” are used interchangeably and refer to a compound where all of the available hydrogens bonded to carbon have been replaced by fluorine.
- The term “polar” refers to a molecule that has a permanent electric dipole.
- The term “high-boiling solvent” refers to an organic compound which is a liquid at room temperature and has a boiling point of greater than 100° C.
- The term “doped” as it refers to an electrically conductive polymer, is intended to mean that the electrically conductive polymer has a polymeric counterion to balance the charge on the conductive polymer.
- The term “doped conductive polymer” is intended to mean the conductive polymer and the polymeric counterion that is associated with it.
- The term “layer” is used interchangeably with the term “film” and refers to a coating covering a desired area. The term is not limited by size. The area can be as large as an entire device or as small as a specific functional area such as the actual visual display, or as small as a single sub-pixel. Layers and films can be formed by any conventional deposition technique, including vapor deposition, liquid deposition (continuous and discontinuous techniques), and thermal transfer.
- The term “carbon nanotube” refers to an allotrope of carbon having a nanostructure where the length-to-diameter ratio exceeds one million.
- The term “fullerene” refers to cage-like, hollow molecules composed of hexagonal and pentagonal groups of carbon atoms. In some embodiments, there are at least 60 carbon atoms present in the molecule.
- The term “nanoparticle” refers to a material having a particle size less than 100 nm. In some embodiments, the particle size is less than 10 nm. In some embodiments, the particle size is less than 5 nm.
- The term “aqueous” refers to a liquid that has a significant portion of water, and in one embodiment it is at least about 40% by weight water; in some embodiments, at least about 60% by weight water.
- The term “hole transport” when referring to a layer, material, member, or structure, is intended to mean such layer, material, member, or structure facilitates migration of positive charges through the thickness of such layer, material, member, or structure with relative efficiency and small loss of charge.
- The term “electron transport” means when referring to a layer, material, member or structure, such a layer, material, member or structure that promotes or facilitates migration of negative charges through such a layer, material, member or structure into another layer, material, member or structure.
- Although light-emitting materials may also have some charge transport properties, the terms “hole transport layer, material, member, or structure” and “electron transport layer, material, member, or structure” are not intended to include a layer, material, member, or structure whose primary function is light emission.
- The term “organic electronic device” is intended to mean a device including one or more semiconductor layers or materials. Organic electronic devices include, but are not limited to: (1) devices that convert electrical energy into radiation (e.g., a light-emitting diode, light emitting diode display, diode laser, or lighting panel), (2) devices that detect signals through electronic processes (e.g., photodetectors photoconductive cells, photoresistors, photoswitches, phototransistors, phototubes, infrared (“IR”) detectors, or biosensors), (3) devices that convert radiation into electrical energy (e.g., a photovoltaic device or solar cell), and (4) devices that include one or more electronic components that include one or more organic semiconductor layers (e.g., a transistor or diode).
- As used herein, the terms “comprises,” “comprising,” “includes,” “including,” “has,” “having” or any other variation thereof, are intended to cover a non-exclusive inclusion. For example, a process, method, article, or apparatus that comprises a list of elements is not necessarily limited to only those elements but may include other elements not expressly listed or inherent to such process, method, article, or apparatus. Further, unless expressly stated to the contrary, “or” refers to an inclusive or and not to an exclusive or. For example, a condition A or B is satisfied by any one of the following: A is true (or present) and B is false (or not present), A is false (or not present) and B is true (or present), and both A and B are true (or present).
- Also, use of “a” or “an” are employed to describe elements and components described herein. This is done merely for convenience and to give a general sense of the scope of the invention. This description should be read to include one or at least one and the singular also includes the plural unless it is obvious that it is meant otherwise.
- Group numbers corresponding to columns within the Periodic Table of the elements use the “New Notation” convention as seen in the CRC Handbook of Chemistry and Physics, 81st Edition (2000-2001).
- Unless otherwise defined, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs. In the Formulae, the letters Q, R, T, W, X, Y, and Z are used to designate atoms or groups which are defined within. All other letters are used to designate conventional atomic symbols. Group numbers corresponding to columns within the Periodic Table of the elements use the “New Notation” convention as seen in the CRC Handbook of Chemistry and Physics, 81st Edition (2000).
- To the extent not described herein, many details regarding specific materials, processing acts, and circuits are conventional and may be found in textbooks and other sources within the organic light-emitting diode display, lighting source, photodetector, photovoltaic, and semiconductive member arts.
- The doped electrically conductive polymer has a polymeric counterion derived from a polymeric acid to balance the charge on the conductive polymer.
- a. Electrically Conductive Polymer
- Any electrically conductive polymer can be used in the new composition. In some embodiments, the electrically conductive polymer will form a film which has a conductivity greater than 0.1 S/cm. In some embodiments, the new compositions described herein can be used to form films having a conductivity greater than 100 S/cm.
- The conductive polymers suitable for the new composition are made from at least one monomer which, when polymerized alone, forms an electrically conductive homopolymer. Such monomers are referred to herein as “conductive precursor monomers.” Monomers which, when polymerized alone form homopolymers which are not electrically conductive, are referred to as “non-conductive precursor monomers.” The conductive polymer can be a homopolymer or a copolymer. Conductive copolymers suitable for the new composition can be made from two or more conductive precursor monomers or from a combination of one or more conductive precursor monomers and one or more non-conductive precursor monomers.
- In some embodiments, the conductive polymer is made from at least one conductive precursor monomer selected from thiophenes, pyrroles, anilines, and polycyclic aromatics. The term “polycyclic aromatic” refers to compounds having more than one aromatic ring. The rings may be joined by one or more bonds, or they may be fused together. The term “aromatic ring” is intended to include heteroaromatic rings. A “polycyclic heteroaromatic” compound has at least one heteroaromatic ring.
- In some embodiments, the conductive polymer is made from at least one precursor monomer selected from thiophenes, selenophenes, tellurophenes, pyrroles, anilines, and polycyclic aromatics. The polymers made from these monomers are referred to herein as polythiophenes, poly(selenophenes), poly(tellurophenes), polypyrroles, polyanilines, and polycyclic aromatic polymers, respectively. The term “polycyclic aromatic” refers to compounds having more than one aromatic ring. The rings may be joined by one or more bonds, or they may be fused together. The term “aromatic ring” is intended to include heteroaromatic rings. A “polycyclic heteroaromatic” compound has at least one heteroaromatic ring. In some embodiments, the polycyclic aromatic polymers are poly(thienothiophenes).
- In some embodiments, monomers contemplated for use to form the electrically conductive polymer in the new composition comprise Formula I below:
- wherein:
-
- Q is selected from the group consisting of S, Se, and Te;
- R1 is independently selected so as to be the same or different at each occurrence and is selected from hydrogen, alkyl, alkenyl, alkoxy, alkanoyl, alkythio, aryloxy, alkylthioalkyl, alkylaryl, arylalkyl, amino, alkylamino, dialkylamino, aryl, alkylsulfinyl, alkoxyalkyl, alkylsulfonyl, arylthio, arylsulfinyl, alkoxycarbonyl, arylsulfonyl, acrylic acid, phosphoric acid, phosphonic acid, halogen, nitro, cyano, hydroxyl, epoxy, silane, siloxane, alcohol, benzyl, carboxylate, ether, ether carboxylate, amidosulfonate, ether sulfonate, ester sulfonate, and urethane; or both R1 groups together may form an alkylene or alkenylene chain completing a 3, 4, 5, 6, or 7-membered aromatic or alicyclic ring, which ring may optionally include one or more divalent nitrogen, selenium, tellurium, sulfur or oxygen atoms.
- As used herein, the term “alkyl” refers to a group derived from an aliphatic hydrocarbon and includes linear, branched and cyclic groups which may be unsubstituted or substituted. The term “heteroalkyl” is intended to mean an alkyl group, wherein one or more of the carbon atoms within the alkyl group has been replaced by another atom, such as nitrogen, oxygen, sulfur, and the like. The term “alkylene” refers to an alkyl group having two points of attachment.
- As used herein, the term “alkenyl” refers to a group derived from an aliphatic hydrocarbon having at least one carbon-carbon double bond, and includes linear, branched and cyclic groups which may be unsubstituted or substituted. The term “heteroalkenyl” is intended to mean an alkenyl group, wherein one or more of the carbon atoms within the alkenyl group has been replaced by another atom, such as nitrogen, oxygen, sulfur, and the like. The term “alkenylene” refers to an alkenyl group having two points of attachment.
- As used herein, the following terms for substituent groups refer to the formulae given below:
-
“alcohol” —R3—OH -
“amido” —R3—C(O)N(R6)R6 -
“amidosulfonate” —R3—C(O)N(R6)R4—SO3Z -
“benzyl” —CH2—C6H5 -
“carboxylate” —R3—C(O)O—Z or —R3—O—C(O)—Z -
“ether” —R3—(O—R5)p—O—R5 -
“ether carboxylate” —R3—O—R4—C(O)O—Z or —R3—O—R4—O—C(O)—Z -
“ether sulfonate” —R3—O—R4—SO3Z -
“ester sulfonate” —R3—O—C(O)—R4—SO3Z -
“sulfonimide” 13 R3—SO2—NH—SO2—R5 -
“urethane” —R3—O—C(O)—N(R6)2 -
- where all “R” groups are the same or different at each occurrence and:
- R3 is a single bond or an alkylene group
- R4 is an alkylene group
- R5 is an alkyl group
- R6 is hydrogen or an alkyl group
- p is 0 or an integer from 1 to 20
- Z is H, alkali metal, alkaline earth metal, N(R5)4 or R5
Any of the above groups may further be unsubstituted or substituted, and any group may have F substituted for one or more hydrogens, including perfluorinated groups. In some embodiments, the alkyl and alkylene groups have from 1-20 carbon atoms.
- where all “R” groups are the same or different at each occurrence and:
- In some embodiments, in the monomer, both R1 together form —W—(CY1Y2)m—W—, where m is 2 or 3, W is O, S, Se, PO, NR6, Y1 is the same or different at each occurrence and is hydrogen or fluorine, and Y2 is the same or different at each occurrence and is selected from hydrogen, halogen, alkyl, alcohol, amidosulfonate, benzyl, carboxylate, ether, ether carboxylate, ether sulfonate, ester sulfonate, and urethane, where the Y groups may be partially or fully fluorinated. In some embodiments, all Y are hydrogen. In some embodiments, the polymer is poly(3,4-ethylenedioxythiophene). In some embodiments, at least one Y group is not hydrogen. In some embodiments, at least one Y group is a substituent having F substituted for at least one hydrogen. In some embodiments, at least one Y group is perfluorinated.
- In some embodiments, the monomer has Formula I(a):
- wherein:
-
- Q is selected from the group consisting of S, Se, and Te;
- R7 is the same or different at each occurrence and is selected from hydrogen, alkyl, heteroalkyl, alkenyl, heteroalkenyl, alcohol, amidosulfonate, benzyl, carboxylate, ether, ether carboxylate, ether sulfonate, ester sulfonate, and urethane, with the proviso that at least one R7 is not hydrogen, and
- m is 2 or 3.
- In some embodiments of Formula I(a), m is two, one R7 is an alkyl group of more than 5 carbon atoms, and all other R7 are hydrogen. In some embodiments of Formula I(a), at least one R7 group is fluorinated. In some embodiments, at least one R7 group has at least one fluorine substituent. In some embodiments, the R7 group is fully fluorinated.
- In some embodiments of Formula I(a), the R7 substituents on the fused alicyclic ring on the monomer offer improved solubility of the monomers in water and facilitate polymerization in the presence of the fluorinated acid polymer.
- In some embodiments of Formula I(a), m is 2, one R7 is sulfonic acid-propylene-ether-methylene and all other R7 are hydrogen. In some embodiments, m is 2, one R7 is propyl-ether-ethylene and all other R7 are hydrogen. In some embodiments, m is 2, one R7 is methoxy and all other R7 are hydrogen. In some embodiments, one R7 is sulfonic acid difluoromethylene ester methylene (—CH2—O—C(O)—CF2—SO3H), and all other R7 are hydrogen.
- In some embodiments, pyrrole monomers contemplated for use to form the electrically conductive polymer in the new composition comprise Formula II below.
- where in Formula II:
-
- R1 is independently selected so as to be the same or different at each occurrence and is selected from hydrogen, alkyl, alkenyl, alkoxy, alkanoyl, alkythio, aryloxy, alkylthioalkyl, alkylaryl, arylalkyl, amino, alkylamino, dialkylamino, aryl, alkylsulfinyl, alkoxyalkyl, alkylsulfonyl, arylthio, arylsulfinyl, alkoxycarbonyl, arylsulfonyl, acrylic acid, phosphoric acid, phosphonic acid, halogen, nitro, cyano, hydroxyl, epoxy, silane, siloxane, alcohol, benzyl, carboxylate, ether, amidosulfonate, ether carboxylate, ether sulfonate, ester sulfonate, and urethane; or both R1 groups together may form an alkylene or alkenylene chain completing a 3, 4, 5, 6, or 7-membered aromatic or alicyclic ring, which ring may optionally include one or more divalent nitrogen, sulfur, selenium, tellurium, or oxygen atoms; and
- R2 is independently selected so as to be the same or different at each occurrence and is selected from hydrogen, alkyl, alkenyl, aryl, alkanoyl, alkylthioalkyl, alkylaryl, arylalkyl, amino, epoxy, silane, siloxane, alcohol, benzyl, carboxylate, ether, ether carboxylate, ether sulfonate, ester sulfonate, and urethane.
- In some embodiments, R1 is the same or different at each occurrence and is independently selected from hydrogen, alkyl, alkenyl, alkoxy, cycloalkyl, cycloalkenyl, alcohol, benzyl, carboxylate, ether, amidosulfonate, ether carboxylate, ether sulfonate, ester sulfonate, urethane, epoxy, silane, siloxane, and alkyl substituted with one or more of sulfonic acid, carboxylic acid, acrylic acid, phosphoric acid, phosphonic acid, halogen, nitro, cyano, hydroxyl, epoxy, silane, or siloxane moieties.
- In some embodiments, R2 is selected from hydrogen, alkyl, and alkyl substituted with one or more of sulfonic acid, carboxylic acid, acrylic acid, phosphoric acid, phosphonic acid, halogen, cyano, hydroxyl, epoxy, silane, or siloxane moieties.
- In some embodiments, the pyrrole monomer is unsubstituted and both R1 and R2 are hydrogen.
- In some embodiments, both R1 together form a 6- or 7-membered alicyclic ring, which is further substituted with a group selected from alkyl, heteroalkyl, alcohol, benzyl, carboxylate, ether, ether carboxylate, ether sulfonate, ester sulfonate, and urethane. These groups can improve the solubility of the monomer and the resulting polymer. In some embodiments, both R1 together form a 6- or 7-membered alicyclic ring, which is further substituted with an alkyl group. In some embodiments, both R1 together form a 6- or 7-membered alicyclic ring, which is further substituted with an alkyl group having at least 1 carbon atom.
- In some embodiments, both R1 together form —O—(CHY)m—O—, where m is 2 or 3, and Y is the same or different at each occurrence and is selected from hydrogen, alkyl, alcohol, benzyl, carboxylate, amidosulfonate, ether, ether carboxylate, ether sulfonate, ester sulfonate, and urethane. In some embodiments, at least one Y group is not hydrogen. In some embodiments, at least one Y group is a substituent having F substituted for at least one hydrogen. In some embodiments, at least one Y group is perfluorinated.
- In some embodiments, aniline monomers contemplated for use to form the electrically conductive polymer in the new composition comprise Formula III below.
- wherein:
- a is 0 or an integer from 1 to 4;
- b is an integer from 1 to 5, with the proviso that a+b=5; and R1 is independently selected so as to be the same or different at each occurrence and is selected from hydrogen, alkyl, alkenyl, alkoxy, alkanoyl, alkythio, aryloxy, alkylthioalkyl, alkylaryl, arylalkyl, amino, alkylamino, dialkylamino, aryl, alkylsulfinyl, alkoxyalkyl, alkylsulfonyl, arylthio, arylsulfinyl, alkoxycarbonyl, arylsulfonyl, acrylic acid, phosphoric acid, phosphonic acid, halogen, nitro, cyano, hydroxyl, epoxy, silane, siloxane, alcohol, benzyl, carboxylate, ether, ether carboxylate, amidosulfonate, ether sulfonate, ester sulfonate, and urethane; or both R1 groups together may form an alkylene or alkenylene chain completing a 3, 4, 5, 6, or 7-membered aromatic or alicyclic ring, which ring may optionally include one or more divalent nitrogen, sulfur or oxygen atoms.
- When polymerized, the aniline monomeric unit can have Formula IV(a) or Formula IV(b) shown below, or a combination of both formulae.
- where a, b and R1 are as defined above.
- In some embodiments, the aniline monomer is unsubstituted and a=0.
- In some embodiments, a is not 0 and at least one R1 is fluorinated.
- In some embodiments, at least one R1 is perfluorinated.
- In some embodiments, fused polycyclic heteroaromatic monomers contemplated for use to form the electrically conductive polymer in the new composition have two or more fused aromatic rings, at least one of which is heteroaromatic. In some embodiments, the fused polycyclic heteroaromatic monomer has Formula V:
- wherein:
-
- Q is S, Se, Te, or NR6;
- R6 is hydrogen or alkyl;
- R8, R9, R10, and R11 are independently selected so as to be the same or different at each occurrence and are selected from hydrogen, alkyl, alkenyl, alkoxy, alkanoyl, alkythio, aryloxy, alkylthioalkyl, alkylaryl, arylalkyl, amino, alkylamino, dialkylamino, aryl, alkylsulfinyl, alkoxyalkyl, alkylsulfonyl, arylthio, arylsulfinyl, alkoxycarbonyl, arylsulfonyl, acrylic acid, phosphoric acid, phosphonic acid, halogen, nitro, nitrile, cyano, hydroxyl, epoxy, silane, siloxane, alcohol, benzyl, carboxylate, ether, ether carboxylate, amidosulfonate, ether sulfonate, ester sulfonate, and urethane; and
- at least one of R8 and R9, R9 and R10, and R10 and R11 together form an alkenylene chain completing a 5 or 6-membered aromatic ring, which ring may optionally include one or more divalent nitrogen, sulfur, selenium, tellurium, or oxygen atoms.
- In some embodiments, the fused polycyclic heteroaromatic monomer has a formula selected from the group consisting of Formula V(a), V(b), V(c), V(d), V(e), V(f), V(g), V(h), V(i), V(j), and V(k):
- wherein:
-
- Q is S, Se, Te, or NH; and
- T is the same or different at each occurrence and is selected from S, NR6, O, SiR6 2, Se, Te, and PR6;
- Y is N; and
- R6 is hydrogen or alkyl.
The fused polycyclic heteroaromatic monomers may be further substituted with groups selected from alkyl, heteroalkyl, alcohol, benzyl, carboxylate, ether, ether carboxylate, ether sulfonate, ester sulfonate, and urethane. In some embodiments, the substituent groups are fluorinated. In some embodiments, the substituent groups are fully fluorinated.
- In some embodiments, the fused polycyclic heteroaromatic monomer is a thieno(thiophene). Such compounds have been discussed in, for example, Macromolecules, 34, 5746-5747 (2001); and Macromolecules, 35, 7281-7286 (2002). In some embodiments, the thieno(thiophene) is selected from thieno(2,3-b)thiophene, thieno(3,2-b)thiophene, and thieno(3,4-b)thiophene. In some embodiments, the thieno(thiophene) monomer is further substituted with at least one group selected from alkyl, heteroalkyl, alcohol, benzyl, carboxylate, ether, ether carboxylate, ether sulfonate, ester sulfonate, and urethane. In some embodiments, the substituent groups are fluorinated. In some embodiments, the substituent groups are fully fluorinated.
- In some embodiments, polycyclic heteroaromatic monomers contemplated for use to form the polymer in the new composition comprise Formula VI:
- wherein:
-
- Q is S, Se, Te, or NR6;
- T is selected from S, NR6, O, SiR6 2, Se, Te, and PR6;
- E is selected from alkenylene, arylene, and heteroarylene;
- R6 is hydrogen or alkyl;
- R12 is the same or different at each occurrence and is selected from hydrogen, alkyl, alkenyl, alkoxy, alkanoyl, alkythio, aryloxy, alkylthioalkyl, alkylaryl, arylalkyl, amino, alkylamino, dialkylamino, aryl, alkylsulfinyl, alkoxyalkyl, alkylsulfonyl, arylthio, arylsulfinyl, alkoxycarbonyl, arylsulfonyl, acrylic acid, phosphoric acid, phosphonic acid, halogen, nitro, nitrile, cyano, hydroxyl, epoxy, silane, siloxane, alcohol, benzyl, carboxylate, ether, ether carboxylate, amidosulfonate, ether sulfonate, ester sulfonate, and urethane; or both R12 groups together may form an alkylene or alkenylene chain completing a 3, 4, 5, 6, or 7-membered aromatic or alicyclic ring, which ring may optionally include one or more divalent nitrogen, sulfur, selenium, tellurium, or oxygen atoms.
- In some embodiments, the electrically conductive polymer is a copolymer of a precursor monomer and at least one second monomer. Any type of second monomer can be used, so long as it does not detrimentally affect the desired properties of the copolymer. In some embodiments, the second monomer comprises no more than 50% of the polymer, based on the total number of monomer units. In some embodiments, the second monomer comprises no more than 30%, based on the total number of monomer units. In some embodiments, the second monomer comprises no more than 10%, based on the total number of monomer units.
- Exemplary types of second monomers include, but are not limited to, alkenyl, alkynyl, arylene, and heteroarylene. Examples of second monomers include, but are not limited to, fluorene, oxadiazole, thiadiazole, benzothiadiazole, phenylenevinylene, phenyleneethynylene, pyridine, diazines, and triazines, all of which may be further substituted.
- In some embodiments, the copolymers are made by first forming an intermediate precursor monomer having the structure A-B-C, where A and C represent precursor monomers, which can be the same or different, and B represents a second monomer. The A-B-C intermediate precursor monomer can be prepared using standard synthetic organic techniques, such as Yamamoto, Stille, Grignard metathesis, Suzuki, and Negishi couplings. The copolymer is then formed by oxidative polymerization of the intermediate precursor monomer alone, or with one or more additional precursor monomers.
- In some embodiments, the electrically conductive polymer is selected from the group consisting of a polythiophene, a polypyrrole, a polymeric fused polycyclic heteroaromatic, a copolymer thereof, and combinations thereof.
- In some embodiments, the electrically conductive polymer is selected from the group consisting of poly(3,4-ethylenedioxythiophene), unsubstituted polypyrrole, poly(thieno(2,3-b)thiophene), poly(thieno(3,2-b)thiophene), and poly(thieno(3,4-b)thiophene).
- b. Non-Fluorinated Polymeric Acid
- Any non-fluorinated polymeric acid, which is capable of doping the conductive polymer, can be used to make new compositions. Any polymer having acidic groups with acidic protons can be used. The use of such acids with conducting polymers such as polythiophenes, polyanilines and polypyrroles is well known in the art. Examples of acidic groups include, but are not limited to, carboxylic acid groups, sulfonic acid groups, sulfonimide groups, phosphoric acid groups, phosphonic acid groups, and combinations thereof. The acidic groups can all be the same, or the polymer may have more than one type of acidic group.
- In one embodiment, the acid is a non-fluorinated polymeric sulfonic acid. Some non-limiting examples of the acids are poly(styrenesulfonic acid) (“PSSA”), poly(2-acrylamido-2-methyl-1-propanesulfonic acid) (“PAAMPSA”), and mixtures thereof.
- The amount of non-fluorinated polymeric acid present is generally in excess of that required to counterbalance the charge on the conducting polymer. In some embodiments, the ratio of acid equivalents of non-fluorinated polymeric acid to molar equivalents of conducting polymer is in the range of 1-5.
- The amount of doped conducting polymer in the composite dispersion is generally at least 0.1 wt. %, based on the total weight of the dispersion. In some embodiments, the wt. % is from 0.2 to 5.
- The solvent is a high-boiling, polar organic liquid. In some embodiments, the solvent has a boiling point (“b.p.”) of at least 120° C.; in some embodiments, at least 150° C. The solvent is soluble in, miscible with, or dispersible in water. Examples of solvents include, but are not limited to ethylene glycol, dimethylsulfoxide, dimethylacetamide, and N-methylpyrrolidone. Mixtures of solvents may also be used.
- The solvent is generally present in the composite dispersion in the amount of from 1 to 15 wt. %, based on the total weight of the dispersion; in some embodiments, from 5 to 10 wt. %.
- The additive is selected from the group consisting of carbon fullerenes, nanotubes and combinations thereof.
- Fullerenes are an allotrope of carbon characterized by a closed-cage structure consisting of an even number of three-coordinate carbon atoms devoid of hydrogen atoms. The fullerenes are well known and have been extensively studied.
- Examples of fullerenes include C60, C60-PCMB, and C70, shown below,
- as well as C84 and higher fullerenes. Any of the fullerenes may be derivatized with a (3-methoxycarbonyl)-propyl-1-phenyl group (“PCBM”), such as C70-PCBM, C84-PCBM, and higher analogs. Combinations of fullerenes can be used.
- In some embodiments, the fullerene is selected from the group consisting of C60, C60-PCMB, C70, C70-PCMB, and combinations thereof.
- Carbon nanotubes have a cylindrical shape. The nanotubes can be single-walled or multi-walled. The materials are made by methods including arc discharge, laser ablation, high pressure carbon monoxide, and chemical vapor deposition. The materials are well known and commercially available. In some embodiments, single-walled nanotubes are used.
- The amount of additive present is generally at least 0.2 wt. %, based on the total weight of the dispersion. The weight ratio of conductive polymer to additive is generally in the range of 0.5 to 50; in some embodiments, the ratio is 1 to 10.
- In the following discussion, the doped conductive polymer, solvent, and additive will be referred to in the singular. However, it is understood that more than one of any or all of these may be used.
- The new electrically conductive polymer composition is prepared by first forming the doped conductive polymer and then adding the solvent and the additive, in any order.
- The doped electrically conductive polymer is generally formed by oxidative polymerization of the precursor monomer in the presence of the non-fluorinated polymeric acid in an aqueous medium. Many of these materials are commercially available. The additive can be dispersed in water or a solvent/water mixture. These mixtures can then be added to an aqueous dispersion of the doped conductive polymer, optionally with additional solvent.
- Alternatively, the additive can be added to the doped conductive polymer dispersion directly as a solid. The solvent can be added to this mixture.
- In some embodiments, the pH is increased either prior to the addition of the additive or after. The pH can be adjusted by treatment with cation exchange resins, and/or base resins prior to additive addition. In some embodiments, the pH is adjusted by the addition of aqueous base solution. Cations for the base can be, but are not limited to, alkali metal, alkaline earth metal, ammonium, and alkylammonium. In some embodiments, alkali metal is preferred over alkaline earth metal cations.
- Films made from the composite aqueous dispersions described herein, are hereinafter referred to as “the new films described herein”. The films can be made using any liquid deposition technique, including continuous and discontinuous techniques. Continuous deposition techniques, include but are not limited to, spin coating, gravure coating, curtain coating, dip coating, slot-die coating, spray coating, and continuous nozzle coating. Discontinuous deposition techniques include, but are not limited to, ink jet printing, gravure printing, and screen printing.
- The films thus formed are smooth, relatively transparent, and can have a conductivity greater than at least 100 S/cm.
- Organic light-emitting diodes (OLEDs) are an organic electronic device comprising an organic layer capable of electroluminescence. OLEDs can have the following configuration:
-
- anode/buffer layer/EL material/cathode
with additional layers between the electrodes. Electrically conducting polymers having low conductivity in the range of 10−3 to 10−7 S/cm are commonly used as the buffer layer in direct contact with an electrically conductive, inorganic oxide anode such as ITO. However, films of the new compositions having conductivity greater than 100 S/cm can serve both anode and buffer layer functions.
In another embodiment of the invention, there are provided buffer layers deposited from composite aqueous dispersions. The term “buffer layer” or “buffer material” is intended to mean electrically conductive or semiconductive materials and may have one or more functions in an organic electronic device, including but not limited to, planarization of the underlying layer, charge transport and/or charge injection properties, scavenging of impurities such as oxygen or metal ions, and other aspects to facilitate or to improve the performance of the organic electronic device. The term “layer” is used interchangeably with the term “film” and refers to a coating covering a desired area. The term is not limited by size. The area can be as large as an entire device or as small as a specific functional area such as the actual visual display, or as small as a single sub-pixel. Layers and films can be formed by any conventional deposition technique, including vapor deposition, liquid deposition (continuous and discontinuous techniques), and thermal transfer. Continuous deposition techniques, include but are not limited to, spin coating, gravure coating, curtain coating, dip coating, slot-die coating, spray coating, and continuous nozzle coating. Discontinuous deposition techniques include, but are not limited to, ink jet printing, gravure printing, and screen printing.
- anode/buffer layer/EL material/cathode
- The new films described herein can be used in electronic devices where the high conductivity is desired in combination with transparency. In some embodiments, the films are used as electrodes. In some embodiments, the films are used as transparent conductive coatings.
- In another embodiment of the invention, there are provided electronic devices comprising at least one electroactive layer positioned between two electrical contact layers, wherein the device further includes the new buffer layer. The term “electroactive” when referring to a layer or material is intended to mean a layer or material that exhibits electronic or electro-radiative properties. An electroactive layer material may emit radiation or exhibit a change in concentration of electron-hole pairs when receiving radiation.
- As shown in
FIG. 1 , a typical device, 100, has ananode layer 110, anelectroactive layer 140, and acathode layer 160. Also shown are three optional layers:buffer layer 120;hole transport layer 130; and electron injection/transport layer 150. - The device may include a support or substrate (not shown) that can be adjacent to the
anode layer 110 or thecathode layer 160. Most frequently, the support is adjacent to theanode layer 110. The support can be flexible or rigid, organic or inorganic. Examples of support materials include, but are not limited to, glass, ceramic, metal, and plastic films. - The
anode layer 110 is an electrode that is more efficient for injecting holes compared to thecathode layer 160. The new films of this invention described herein are particularly suitable as the anode layer because of their high conductivity. In some embodiments, they have a conductivity of 100 S/cm or greater. In some embodiments, they have a conductivity of 200 S/cm or greater. They are deposited onto substrates using a variety of techniques well-known to those skilled in the art. Typical deposition techniques include liquid deposition (continuous and discontinuous techniques), and thermal transfer. - In some embodiments, the new films described herein are used alone as an anode without
optional buffer layer 120. In this embodiment, the new films of this invention serve the functions of both anode layer and buffer layer. - In some embodiments, the new films described herein are used as the top layer in a bilayer or multilayer anode. The other anode layers can include materials containing a metal, mixed metal, alloy, metal oxide or mixed oxide. Suitable materials include the mixed oxides of the Group 2 elements (i.e., Be, Mg, Ca, Sr, Ba, Ra), the Group 11 elements, the elements in Groups 4, 5, and 6, and the Group 8-10 transition elements. If the
anode layer 110 is to be light transmitting, mixed oxides of Groups 12, 13 and 14 elements, such as indium-tin-oxide, may be used. As used herein, the phrase “mixed oxide” refers to oxides having two or more different cations selected from the Group 2 elements or the Groups 12, 13, or 14 elements. Some non-limiting, specific examples of materials foranode layer 110 include, but are not limited to, indium-tin-oxide (“ITO”), indium-zinc-oxide, aluminum-tin-oxide, gold, silver, copper, and nickel. The mixed oxide layer may be formed by a chemical or physical vapor deposition process or spin-cast process. Chemical vapor deposition may be performed as a plasma-enhanced chemical vapor deposition (“PECVD”) or metal organic chemical vapor deposition (“MOCVD”). Physical vapor deposition can include all forms of sputtering, including ion beam sputtering, as well as e-beam evaporation and resistance evaporation. Specific forms of physical vapor deposition include rf magnetron sputtering and inductively-coupled plasma physical vapor deposition (“IMP-PVD”). These deposition techniques are well known within the semiconductor fabrication arts. - In one embodiment, the mixed oxide layer is patterned. The pattern may vary as desired. The layers can be formed in a pattern by, for example, positioning a patterned mask or resist on the first flexible composite barrier structure prior to applying the first electrical contact layer material. Alternatively, the layers can be applied as an overall layer (also called blanket deposit) and subsequently patterned using, for example, a patterned resist layer and wet chemical or dry etching techniques. Other processes for patterning that are well known in the art can also be used.
-
Optional buffer layer 120 may be present adjacent to theanode layer 110. The term “buffer layer” or “buffer material” is intended to mean electrically conductive or semiconductive materials having conductivity usually in the range between 10−3 to 10−7S/cm, but higher conductivity can be used for some device geometries. The buffer layer may have one or more functions in an organic electronic device, including but not limited to, planarization of the underlying layer, charge transport and/or charge injection properties, scavenging of impurities such as oxygen or metal ions, and other aspects to facilitate or to improve the performance of the organic electronic device. - In some embodiments, the
buffer layer 120 comprises the new film described herein, where the conductivity is 100 S/cm or less. - In some embodiments, optional
hole transport layer 130 is present. betweenanode layer 110 andelectroactive layer 140. In some embodiments, optional hole transport layer is present between abuffer layer 120 andelectroactive layer 140. Examples of hole transport materials have been summarized for example, in Kirk-Othmer Encyclopedia of Chemical Technology, Fourth Edition, Vol. 18, p. 837-860, 1996, by Y. Wang. Both hole transporting molecules and polymers can be used. Commonly used hole transporting molecules include, but are not limited to: 4,4′,4″-tris(N,N-diphenyl-amino)-triphenylamine (TDATA); 4,4′,4″-tris(N-3-methylphenyl-N-phenyl-amino)-triphenylamine (MTDATA); N,N′-diphenyl-N,N′-bis(3-methylphenyl)-[1,1′-biphenyl]-4,4′-diamine (TPD); 1,1-bis[(di-4-tolylamino)phenyl]cyclohexane (TAPC); N,N′-bis(4-methylphenyl)-N,N′-bis(4-ethylphenyl)-[1,1′-(3,3′-dimethyl)biphenyl]-4,4′-diamine (ETPD); tetrakis-(3-methylphenyl)-N,N,N′,N′-2,5-phenylenediamine (PDA); α-phenyl-4-N,N-diphenylaminostyrene (TPS); p-(diethylamino)benzaldehyde diphenylhydrazone (DEH); triphenylamine (TPA); bis[4-(N,N-diethylamino)-2-methylphenyl](4-methylphenyl)methane (MPMP); 1-phenyl-3-[p-(diethylamino)styryl]-5-[p-(diethylamino)phenyl]pyrazoline (PPR or DEASP); 1,2-trans-bis(9H-carbazol-9-yl)cyclobutane (DCZB); N,N,N′,N′-tetrakis(4-methylphenyl)-(1,1′-biphenyl)-4,4′-diamine (TTB); N,N′-bis(naphthalen-1-yl)-N,N′-bis-(phenyl)benzidine (α-NPB); and porphyrinic compounds, such as copper phthalocyanine. Commonly used hole transporting polymers include, but are not limited to, polyvinylcarbazole, (phenylmethyl)polysilane, poly(dioxythiophenes), polyanilines, and polypyrroles. It is also possible to obtain hole transporting polymers by doping hole transporting molecules such as those mentioned above into polymers such as polystyrene and polycarbonate. - Depending upon the application of the device, the
electroactive layer 140 can be a light-emitting layer that is activated by an applied voltage (such as in a light-emitting diode or light-emitting electrochemical cell), a layer of material that responds to radiant energy and generates a signal with or without an applied bias voltage (such as in a photodetector). In one embodiment, the electroactive material is an organic electroluminescent (“EL”) material, Any EL material can be used in the devices, including, but not limited to, small molecule organic fluorescent compounds, fluorescent and phosphorescent metal complexes, conjugated polymers, and mixtures thereof. Examples of fluorescent compounds include, but are not limited to, pyrene, perylene, rubrene, coumarin, derivatives thereof, and mixtures thereof. Examples of metal complexes include, but are not limited to, metal chelated oxinoid compounds, such as tris(8-hydroxyquinolato)aluminum (Alq3); cyclometalated iridium and platinum electroluminescent compounds, such as complexes of iridium with phenylpyridine, phenylquinoline, or phenylpyrimidine ligands as disclosed in Petrov et al., U.S. Pat. No. 6,670,645 and Published PCT Applications WO 03/063555 and WO 2004/016710, and organometallic complexes described in, for example, Published PCT Applications WO 03/008424, WO 03/091688, and WO 03/040257, and mixtures thereof. Electroluminescent emissive layers comprising a charge carrying host material and a metal complex have been described by Thompson et al., in U.S. Pat. No. 6,303,238, and by Burrows and Thompson in published PCT applications WO 00/70655 and WO 01/41512. Examples of conjugated polymers include, but are not limited to poly(phenylenevinylenes), polyfluorenes, poly(spirobifluorenes), polythiophenes, poly(p-phenylenes), copolymers thereof, and mixtures thereof. -
Optional layer 150 can function both to facilitate electron injection/transport, and can also serve as a confinement layer to prevent quenching reactions at layer interfaces. More specifically,layer 150 may promote electron mobility and reduce the likelihood of a quenching reaction iflayers optional layer 150 include, but are not limited to, metal chelated oxinoid compounds, such as bis(2-methyl-8-quinolinolato)(para-phenyl-phenolato)aluminum(III) (BAlQ) and tris(8-hydroxyquinolato)aluminum (Alq3); tetrakis(8-hydroxyquinolinato)zirconium; azole compounds such as 2-(4-biphenylyl)-5-(4-t-butylphenyl)-1,3,4-oxadiazole (PBD), 3-(4-biphenylyl)-4-phenyl-5-(4-t-butylphenyl)-1,2,4-triazole (TAZ), and 1,3,5-tri(phenyl-2-benzimidazole)benzene (TPBI); quinoxaline derivatives such as 2,3-bis(4-fluorophenyl)quinoxaline; phenanthroline derivatives such as 9,10-diphenylphenanthroline (DPA) and 2,9-dimethyl-4,7-diphenyl-1,10-phenanthroline (DDPA); and any one or more combinations thereof. Alternatively,optional layer 150 may be inorganic and comprise BaO, LiF, Li2O, or the like. - The
cathode layer 160 is an electrode that is particularly efficient for injecting electrons or negative charge carriers. Thecathode layer 160 can be any metal or nonmetal having a lower work function than the first electrical contact layer (in this case, the anode layer 110). As used herein, the term “lower work function” is intended to mean a material having a work function no greater than about 4.4 eV. As used herein, “higher work function” is intended to mean a material having a work function of at least approximately 4.4 eV. - Materials for the cathode layer can be selected from alkali metals of Group 1 (e.g., Li, Na, K, Rb, Cs,), the Group 2 metals (e.g., Mg, Ca, Ba, or the like), the Group 12 metals, the lanthanides (e.g., Ce, Sm, Eu, or the like), and the actinides (e.g., Th, U, or the like). Materials such as aluminum, indium, yttrium, and combinations thereof, may also be used. Specific non-limiting examples of materials for the
cathode layer 160 include, but are not limited to, barium, lithium, cerium, cesium, europium, rubidium, yttrium, magnesium, samarium, and alloys and combinations thereof. - The
cathode layer 160 is usually formed by a chemical or physical vapor deposition process. In some embodiments, the cathode layer will be patterned, as discussed above in reference to theanode layer 110. - Other layers in the device can be made of any materials which are known to be useful in such layers upon consideration of the function to be served by such layers.
- In some embodiments, an encapsulation layer (not shown) is deposited over the
contact layer 160 to prevent entry of undesirable components, such as water and oxygen, into thedevice 100. Such components can have a deleterious effect on theorganic layer 140. In one embodiment, the encapsulation layer is a barrier layer or film. In one embodiment, the encapsulation layer is a glass lid. - Though not depicted, it is understood that the
device 100 may comprise additional layers. Other layers that are known in the art or otherwise may be used. In addition, any of the above-described layers may comprise two or more sub-layers or may form a laminar structure. Alternatively, some or all ofanode layer 110, thebuffer layer 120, thehole transport layer 130, theelectron transport layer 150,cathode layer 160, and other layers may be treated, especially surface treated, to increase charge carrier transport efficiency or other physical properties of the devices. The choice of materials for each of the component layers is preferably determined by balancing the goals of providing a device with high device efficiency with device operational lifetime considerations, fabrication time and complexity factors and other considerations appreciated by persons skilled in the art. It will be appreciated that determining optimal components, component configurations, and compositional identities would be routine to those of ordinary skill of in the art. - In one embodiment, the different layers have the following range of thicknesses:
anode 110, 500-5000 Å, in one embodiment 1000-2000 Å;optional buffer layer 120, 50-2000 Å, in one embodiment 200-1000 Å; optionalhole transport layer 130, 50-2000 Å, in one embodiment 100-1000 Å;photoactive layer 140, 10-2000 Å, in one embodiment 100-1000 Å; optionalelectron transport layer 150, 50-2000 Å, in one embodiment 100-1000 Å;cathode 160, 200-10000 Å, in one embodiment 300-5000 Å. The location of the electron-hole recombination zone in the device, and thus the emission spectrum of the device, can be affected by the relative thickness of each layer. Thus the thickness of the electron-transport layer should be chosen so that the electron-hole recombination zone is in the light-emitting layer. The desired ratio of layer thicknesses will depend on the exact nature of the materials used. - In operation, a voltage from an appropriate power supply (not depicted) is applied to the
device 100. Current therefore passes across the layers of thedevice 100. Electrons enter the organic polymer layer, releasing photons. In some OLEDs, called active matrix OLED displays, individual deposits of photoactive organic films may be independently excited by the passage of current, leading to individual pixels of light emission. In some OLEDs, called passive matrix OLED displays, deposits of photoactive organic films may be excited by rows and columns of electrical contact layers. - Although methods and materials similar or equivalent to those described herein can be used in the practice or testing of the present invention, suitable methods and materials are described below. All publications, patent applications, patents, and other references mentioned herein are incorporated by reference in their entirety. In case of conflict, the present specification, including definitions, will control. In addition, the materials, methods, and examples are illustrative only and not intended to be limiting.
- It is to be appreciated that certain features of the invention which are, for clarity, described above and below in the context of separate embodiments, may also be provided in combination in a single embodiment. Conversely, various features of the invention that are, for brevity, described in the context of a single embodiment, may also be provided separately or in any subcombination. Further, reference to values stated in ranges include each and every value within that range.
- One small drop of each dispersion sample was placed on a 3″×1″ microscope slide placed on a hot plate set at ˜170° C. in air. The liquid was spread with a small diameter (˜1 mm) glass rod to form a thin film on ⅔ area of the slide as the liquid was evaporating. The slide was removed from the hot plate and the film was trimmed to a long strip with a razor blade. Width of the strip ranged from 0.2 cm to 0.7 cm and the length was about 3 cm. The microscope slide containing the strip was then placed on a hot plate set at 210° C. for 10 minutes. Once cooled to room temperature, silver paste was then painted perpendicular to the length of the strip to form four electrodes. The two inner parallel electrodes were about 0.3 cm to 0.5 cm apart and were connected to a Keithley model 616 electrometer for measurement of voltage. The two outside parallel electrodes were connected to a Keithley model 225 Current Supplier. A series of corresponding current/voltage data obtained at room temperature was recorded to see whether Ohm's law was followed. All the samples in the Examples followed Ohm's law, which provided a more or less identical resistance of the corresponding current/voltage data. Once resistance measurement was done, the area in the two inner electrodes was measured for thickness with a Profilometer. Thickness of the tested films is typically in the range of 1 micrometer (um). Since resistance, thickness, separation length of the two inner electrodes and the width of the filmstrip are known, electrical conductivity is then calculated. The conductivity unit is expressed as S (Siemens)/cm.
- This example illustrates preparation and film conductivity of a stable aqueous dispersion containing carbon-nanotubes (CNT), electrically conducting polymer, and a high boiling organic liquid.
- CNT used in this example was HIPco CE608, purchased from CNI (Carbon Nanotechnologies, Inc.) at Houston, Tex., USA. HIPco CE608 CNT is single wall nanotubes, which contains about 3-4% (w/w) residual catalyst. It was made by a process using high-pressure carbon monoxide and then purified by the Company.
- Electrically conducting polymer used in this example is poly(3,4-ethylenedioxythiophene) doped with non-fluorinated doping acid poly(styrenesulfonic acid), abbreviated as “PEDOT/PSSA”. PEDOT/PSSA is a well-known electrically conductive polymer. The polymer dispersed in water is commercially available from H. C. Starck GmbH (Leverkuson, Germany) in several grades under a trade name of Baytron-P. Baytron-P HCV4, one of the commercial aqueous dispersion products, purchased from Starck was used. The Baytron-P HCV4 sample was determined gravimetrically to have 1.01% (w/w) solid, which should be PEDOT/PSSA in water. According to the product brochure, the weight ratio of PEDOT:PSSA is 1:2.5.
- Prior to preparation of a CNT composite dispersion, an ethylene glycol/water solution was prepared. The solution was for reducing PEDOT-PSSA solid % of HCV4, therefore reducing its viscosity. A 19.93% (w/w) ethylene glycol/water solution was made by adding 3.9988 g ethylene glycol to 16.0610 g deionized water.
- 0.0876 g CNT were first placed in a glass jug. To the CNT solids, 14.7193 g ethylene glycol (19.93%, w/w)/water solution were added, followed with 13.9081 g Baytron-P HCV4. Based on the quantity of each component, the mixture contains 0.49% (w/w) PEDOT-PSSA, 10.22% (w/w) ethylene glycol, 0.31% (w/w) CNT, and the remaining is water. The mixture was subjected to sonication for 15 minutes continuously using a Branson Model 450 Sonifier having power set at #4. The glass jug was immersed in ice water contained in a tray to remove heat produced from intense cavitation during entire period of sonication. The mixture formed a smooth, stable dispersion without any sign of sedimentation. PH of the dispersion was measured to be 2.1 using a pH meter (model 63) from Jenco Electronics, Ltd (San Diego, Calif.).
- Films were prepared according to the general procedure described in thin film preparation. Thin films are optically transmissive and stronger mechanically than those of the conducting polymer without CNT. Thin films were tested for electrical conductivity as described in the general procedure. The conductivity of five film samples at room temperature was measured to be 509.3 S/cm, 667.3 S/cm, 441.3 S/cm, 546.8 S/cm, and 551.2 S/cm.
- This example illustrates addition of a base solution on stability of the composite dispersion prepared in Example 1.
- About 10 g of the dispersion sample made in Example 1 was first adjusted to pH3.9 using 0.5N NaOH/water solution first and then 0.1N NaOH/water as pH got closer to the targeted pH. One half of the pH3.9 dispersion was further adjusted to pH7.0 with sodium hydroxide/water solution too. Concentration of each component in the dispersions was not significantly affected because only a very small amount of base solution was used. Addition of the base solution still maintains homogeneity of the dispersion. There is no sign of sedimentation in both high pH dispersions. The high pH dispersions also form homogeneous films.
- This example illustrates preparation and film conductivity of a stable aqueous dispersion containing a different carbon nanotube (CNT), electrically conducting polymer, and a high boiling organic liquid.
- CNT used in this example was HIPco P0244, also purchased from CNI (Carbon Nanotechnologies, Inc.) at Houston, Tex., USA. HIPco P0244 CNT is single wall nanotubes, which contains about 10% (w/w) residual catalyst. It was made by a process using high-pressure carbon monoxide and then purified by the Company. Electrically conducting polymer used in this example is also Baytron-P HCV4. This lot of sample was determined gravimetrically to have 1.1% (w/w) solid, which should be PEDOT/PSSA in water. According to the product brochure, the weight ratio of PEDOT:PSSA is 1:2.5.
- Prior to preparation of a CNT composite dispersion, an ethylene glycol/water solution was prepared. The solution was for reducing PEDOT-PSSA solid % of HCV4, therefore reducing its viscosity. A 18.01% (w/w) ethylene glycol/water solution was made by adding 3.6035 g ethylene glycol to 16.4057 g deionized water.
- 0.0981 g CNT were first placed in a glass jug. To the CNT solids, 17.2521 g ethylene glycol (18.01%, w/w)/water solution were added, followed with 15.5701 g Baytron-P HCV4. Based on the quantity of each component, the mixture contains 0.52% (w/w) PEDOT-PSSA, 9.44% (w/w) ethylene glycol, 0.298% (w/w) CNT, and the remaining is water. The mixture was subjected to sonication for 28 minutes continuously using a Branson Model 450 Sonifier having power set at #4. The glass jug was immersed in ice water contained in a tray to remove heat produced from intense cavitation during entire period of sonication. The mixture formed a smooth, stable dispersion without any sign of sedimentation. pH of the dispersion was measured to be 2.0 using a pH meter (model 63) from Jenco Electronics, Ltd (San Diego, Calif.).
- Films were prepared according to the general procedure described in thin film preparation. Thin films are optically transmissive and stronger mechanically than those of the conducting polymer without CNT. Thin films were tested for electrical conductivity as described in the general procedure. The conductivity of six film samples at room temperature was measured to be 608.7 S/cm, 459.3 S/cm, 366.6 S/cm, 528.8 S/cm, 481.0 S/cm, and 472.3 S/cm.
- Note that not all of the activities described above in the general description or the examples are required, that a portion of a specific activity may not be required, and that one or more further activities may be performed in addition to those described. Still further, the order in which activities are listed are not necessarily the order in which they are performed.
- In the foregoing specification, the concepts have been described with reference to specific embodiments. However, one of ordinary skill in the art appreciates that various modifications and changes can be made without departing from the scope of the invention as set forth in the claims below. Accordingly, the specification and figures are to be regarded in an illustrative rather than a restrictive sense, and all such modifications are intended to be included within the scope of invention.
- Benefits, other advantages, and solutions to problems have been described above with regard to specific embodiments. However, the benefits, advantages, solutions to problems, and any feature(s) that may cause any benefit, advantage, or solution to occur or become more pronounced are not to be construed as a critical, required, or essential feature of any or all the claims.
- It is to be appreciated that certain features are, for clarity, described herein in the context of separate embodiments, may also be provided in combination in a single embodiment. Conversely, various features that are, for brevity, described in the context of a single embodiment, may also be provided separately or in any subcombination.
- The use of numerical values in the various ranges specified herein is stated as approximations as though the minimum and maximum values within the stated ranges were both being preceded by the word “about.” In this manner slight variations above and below the stated ranges can be used to achieve substantially the same results as values within the ranges. Also, the disclosure of these ranges is intended as a continuous range including every value between the minimum and maximum average values including fractional values that can result when some of components of one value are mixed with those of different value. Moreover, when broader and narrower ranges are disclosed, it is within the contemplation of this invention to match a minimum value from one range with a maximum value from another range and vice versa.
Claims (20)
1. An aqueous dispersion comprising:
at least one electrically conductive polymer doped with a non-fluorinated polymeric acid polymer;
at least one high-boiling polar solvent, and
an additive selected from the group consisting of fullerenes, carbon nanotubes, and combinations thereof.
2. The dispersion of claim 1 , wherein the electrically conductive polymer is selected from the group consisting of poly(selenophenes), poly(tellurophenes), polypyrroles, polyanilines, polycyclic aromatic polymers, copolymers thereof, and combinations thereof.
3. The dispersion of claim 2 , wherein the electrically conductive polymer is selected from the group consisting of a polyaniline, a polypyrrole, a polymeric fused polycyclic heteroaromatic, copolymers thereof, and combinations thereof.
4. The dispersion of claim 3 , wherein the electrically conductive polymer is selected from the group consisting of unsubstituted polyaniline, and unsubstituted polypyrrole.
5. The dispersion of claim 1 wherein the non-fluorinated polymeric acid polymer is a polymeric sulfonic acid.
6. The dispersion of claim 5 wherein the polymeric sulfonic acid is selected from the group consisting of poly(styrenesulfonic acid), poly(2-acrylamido-2-methyl-1-propanesulfonic acid) and mixtures thereof.
7. The dispersion of claim 1 wherein the amount of doped conducting polymer in the composite dispersion is in the range of from 0.1% to 5% by weight based on the total weight of the dispersion.
8. The dispersion of claim 1 wherein an additive is a fullerene.
9. The dispersion of claim 8 wherein the fullerene is selected from the group consisting of C60, C60-PCMB, C70, C70-PCBM, and combinations thereof.
10. The dispersion of claim 1 wherein the amount of additive present is in the range of from 0.2% to 50% by weight based on the total weight of the dispersion.
11. The dispersion of claim 1 wherein the solvent has a boiling point of at least 120° C.
12. The dispersion of claim 1 wherein the solvent is present in the composite dispersion in the range of from 1% to 15% by weight based on the total weight of the dispersion.
13. The dispersion of claim 1 having a pH greater than 2.
14. A film made from the dispersion of claim 1 .
15. The film of claim 14 having a conductivity of at least 100 S/cm.
16. An electronic device comprising at least one layer made from the dispersion of claim 1 .
17. The device of claim 16 , wherein the layer is an anode.
18. The device of claim 16 , wherein the layer is a buffer layer.
19. The dispersion of claim 1 wherein the at least one polar solvent is selected from the group consisting of ethylene glycol, dimethylsulfoxide, dimethylacetamide, N-methylpyrrolidone, and mixtures thereof.
20. The dispersion of claim 1 wherein the fullerene is selected from the group consisting of C60, C60-PCBM, C70, C70-PCBM, and mixtures thereof, the carbon nanotube is HIPco CE608, and mixtures of the nanotube and fullerenes.