TWI688677B - 用於銅及銅合金表面之蝕刻溶液 - Google Patents
用於銅及銅合金表面之蝕刻溶液 Download PDFInfo
- Publication number
- TWI688677B TWI688677B TW105143097A TW105143097A TWI688677B TW I688677 B TWI688677 B TW I688677B TW 105143097 A TW105143097 A TW 105143097A TW 105143097 A TW105143097 A TW 105143097A TW I688677 B TWI688677 B TW I688677B
- Authority
- TW
- Taiwan
- Prior art keywords
- copper
- etching solution
- etching
- copper alloy
- acid
- Prior art date
Abstract
Description
本發明係關於用於銅及銅合金表面之蝕刻溶液。具體而言,其係關於可用於製造印刷電路板、IC基板、中介層等之電子工業領域中之用於銅及銅合金表面之蝕刻溶液。
在印刷電路板之製造中,在利用蝕刻光阻劑、阻銲劑等之乾膜塗覆銅表面之前處理銅之表面以促進銅表面與阻劑之間之黏合。在處理帶有精細佈線圖案之基板中,通常使用化學蝕刻。在多層印刷電路板之製造中,已嘗試在維持氧化物層之幾何形狀的同時(例如)藉由在銅表面上形成氧化物層並藉由還原劑將氧化物層還原為金屬銅促進銅導電圖案化層與樹脂層之間之黏合。 電路之負型圖案係藉由以下來形成:a) 在銅層上施加蝕刻阻劑,例如聚合乾膜阻劑或金屬阻劑,b) 蝕刻出彼等未經蝕刻阻劑覆蓋之銅部分,及c) 自剩餘銅電路去除蝕刻阻劑。 針對此任務所施加之蝕刻溶液係選自不同類型之組合物,例如氧化劑及酸之混合物。兩種主要類型之蝕刻溶液基於酸(例如硫酸或鹽酸)且含有過氧化氫、銅離子或鐵離子作為氧化劑。此等蝕刻溶液揭示於C. F. Coombs, Jr.,「Printed Circuits Handbook」,第5版,2001,第33.4.3章第33.14至33.15頁及第33.4.5章第33.17頁中。 電路在欲蝕刻銅層之線寬/線間間隔值及厚度方面之持續小型化不容許使用諸如上文所闡述者之習用蝕刻溶液。 若藉由半加成製程(SAP)製造銅軌道,則已知蝕刻溶液之缺點會甚至更明顯。此處,首先使用用作導電層之晶種層塗覆裸介電基板。晶種層包含(例如)藉由無電電鍍沈積之銅。然後,在晶種層上形成圖案化阻劑層,且藉由電鍍至晶種層上圖案化阻劑層之開口中來沈積更厚之第二銅層。剝除圖案化阻劑層且銅軌道之間藉由電鍍沈積之晶種層需要藉由微分蝕刻步驟去除。藉由無電電鍍沈積之晶種層具有較藉由電鍍沈積之第二銅層更為精細之晶粒結構。不同晶粒結構可產生個別銅層之不同蝕刻行為。 在藉由改良半加成製程(m-SAP)或高級改良SAP (Am-SAP)製造銅軌道時(其中將較厚之第二厚銅層沈積於第一薄銅層上之圖案化阻劑層之開口中),存在類似情形。藉由(例如)使附接至介電基板之銅覆層薄化來製造第一銅層。同樣,第一及第二銅層二者均具有不同晶粒結構。 施加用於微分蝕刻步驟之蝕刻溶液應僅去除銅軌道之間之第一銅層,而不(實質上)侵蝕藉由電鍍沈積之銅軌道之側壁及頂部以及下伏第一銅層或銅晶種層。 基於硫酸及過氧化氫之蝕刻溶液在蝕刻期間使得不期望地底切第一銅層(圖1b),此導致銅層在介電基板上之黏合力不足。WO 2010/016562揭示用於銅蝕刻之組合物,其含有聚乙烯基吡咯啶酮(PVP)以及作為氧化劑之鐵及銅離子。此等銅蝕刻組合物中PVP之使用亦造成底切(參見比較應用實例2b)。 基於硫酸及鐵離子之蝕刻溶液通常顯示如圖1c中所示之蝕刻行為。此梯形線形係不期望的,此乃因經蝕刻之銅線之較寬底部可導致不可接受之電路短路。此形成梯形蝕刻結果之現象在本文中稱為「線形改變」。 銅蝕刻之另一不期望之副作用通常係線寬之減小。此通常係由過強蝕刻自經處理銅線之所有表面溶解銅離子而造成(參見圖1d)。 EP 0855454 A1教示用於銅蝕刻溶液中之陽離子聚合物。此等陽離子聚合物尤其包括具有胺之聚合物,例如聚乙烯亞胺。然而,含有聚乙烯亞胺之蝕刻溶液改變線形並減小所處理銅線之線寬,導致不規則線形(參見比較應用實例3c及3d)。由於其損害電子設備之導電佈局,尤其造成此等產品之壽命更短,故此高度不期望。
本發明之目標
因此,本發明之目標係提供克服先前技術之限制及缺點之用於銅及銅合金之蝕刻之蝕刻溶液及其使用方法。本發明之目標亦係提供使得在處理後銅或銅合金線之幾何結構(例如矩形線形)之保持改良(可藉由頂部-底部差值量測)、線寬減小較不明顯及底切避免之用於銅及銅合金之蝕刻之蝕刻溶液及其使用方法。 以上所提及之目標係藉由如技術方案1之用於銅及銅合金表面之蝕刻溶液及其使用解決。本發明之較佳實施例可參見附屬申請專利範圍。該等目標進一步係藉由如技術方案14之方法解決。
除非另有說明,否則整個本說明書中之百分比係重量百分比(wt.-%)。一個例外係產率,其係作為理論產率之百分比給出。除非另有說明,否則本說明書中所給出之濃度係指全部溶液之體積。 用於銅及銅合金表面之蝕刻水溶液包含至少一種酸、至少一種適於氧化銅之氧化劑、至少一種鹵離子源,且特徵在於其包含至少一種含有至少一個根據式(I)之聚合部分之聚醯胺其中每一a彼此獨立地選自2及3;每一b係彼此獨立地在5至10000範圍內之整數;每一R1
係彼此獨立地選自由經取代或未經取代之C1-C8-烷基組成之群之單價殘基。在本文中,此溶液將稱為「蝕刻溶液」。 根據本發明,術語「烷基」包含包括環狀及/或非環狀結構性要素之具支鏈或無支鏈烷基,其中烷基之環狀結構性要素自然需要至少3個碳原子。根據本發明,術語「C1-CX-烷基」係指具有1至X個碳原子之烷基。舉例而言,C1-C8-烷基尤其包括甲基、乙基、正丙基、異丙基、正丁基、異丁基、第二丁基、第三丁基、正戊基、異戊基、第二戊基、第三戊基、新戊基、己基、庚基及辛基。理論上,可藉由以諸如胺基、羥基、硫醇、烷氧基及硫代烷基之官能基替代至少一個氫來獲得經取代之烷基。較佳地,烷基未經取代或其經羥基及/或胺基取代。 就本說明書中及申請專利範圍中所使用之術語「芳基」而言,其係指環形芳香族烴殘基,例如苯基或萘基,其中個別環碳原子可經N、O及/或S替代,例如苯并噻唑基。此外,芳基殘基可藉由在每一情形下以諸如胺基、羥基、硫醇、烷氧基及硫代烷基之官能基替代氫來取代。較佳地,芳基未經取代或其經羥基及/或胺基取代。 就本說明書中及申請專利範圍中所使用之術語「芳烷基」而言,其係指由烷基及芳基組成之烴殘基,例如苄基及甲苯基。 至少一個根據式(I)之聚合部分係直鏈的。因此,至少一個根據式(I)之聚合部分既無支鏈亦不與(例如)另一根據式(I)之聚合部分交聯。較佳地,全部含有至少一個根據式(I)之聚合部分之聚醯胺係直鏈的,且不為具支鏈亦不交聯。 根據式(I)之聚合部分可為均聚物或共聚物。均聚物僅由一種單體製成,共聚物由兩種或更多種不同單體製成。聚合物之個別構建單元可以任何順序配置在該聚合物中,此意味著該等聚合物可為(例如)嵌段聚合物、統計聚合物、分段聚合物、梯度聚合物、週期性聚合物或交替聚合物。共聚物較佳,此乃因其使線寬減小減少(參見應用實例6)。 至少一種含有至少一個根據式(I)之聚合部分之聚醯胺之質量平均莫耳質量(Mw
)較佳在500 amu至1,000,000 amu、更佳在1,000 amu至500,000 amu範圍內。在蝕刻溶液中使用質量平均莫耳質量低於500 amu之含有至少一個根據式(I)之聚合部分之聚醯胺可導致不太有效之蝕刻結果。若質量平均莫耳質量超過1,000,000 amu,則有效性亦似乎顯著降低,此可與該等聚合物之溶解度有關。根據本發明之其他較佳實施例,至少一種含有至少一個根據式(I)之聚合部分之聚醯胺之質量平均莫耳質量係在5,000 amu至100,000 amu範圍內。令人驚訝地,上文所提及之聚醯胺確實容許在保持銅或銅合金線之期望矩形形狀的同時改良銅或銅合金表面之蝕刻結果(參照應用實例5),或其使各別銅或銅合金表面變粗糙以提供改良之對有機材料(例如包括FR-4及FR-5之預浸體)之黏合(參照應用實例1)。質量平均莫耳質量可藉由標準方法(例如凝膠滲透層析(GPC)或黏度測定法)測定,較佳藉由GPC測定。用於此等GPC量測之可用方法可參見R. Hoogenboom、M. W. M. Fijten、M. A. R. Meier、U. S. Schubert,Macromolecular Rapid Communications, 2003, 第24 (1)卷, 第92-97頁。 較佳地,每一單價殘基R1
彼此獨立地選自由C1-C6-烷基組成之群。更佳地,每一R1
彼此獨立地選自由以下組成之群:甲基、乙基、正丙基、異丙基、正丁基、異丁基、第二丁基及第三丁基。 在其中聚醯胺包含至少兩個根據式(I)之聚合部分之彼等情形下,該等聚合部分可彼此直接相鄰連接,或通常其可藉由橋連部分來連接。該橋連部分可係伸烷基、伸芳基或自另一聚合物、特定而言自含胺之聚合物衍生及/或其可為根據式(II)之部分或由其形成之寡聚物或聚合物。該根據式(II)之部分係其中每一c係獨立地範圍為1至3、較佳2至3之整數。較佳地,該橋連部分係根據式(II)之部分或由其形成之寡聚物或聚合物。在本文中寡聚物將意指具2至4個該等部分之直鏈分子實體;聚合物將由5個或更多個該等部分組成。 含有至少一個根據式(I)之聚合部分之聚醯胺視情況(儘管通常)含有兩個聚合物封端基團。此等聚合物封端基團(業內亦稱為末端基團)係由聚合製程之起始或終止所產生之部分。其可來源於其中進行聚合之溶劑;pH調整劑,例如酸或鹼;聚合起始物,例如親核劑(例如包含烷基或芳烷基之彼等);終止試劑,例如水或其他親電子劑;及自由基起始劑,例如過硫酸鹽、過氧化物或偶氮化合物;鏈轉移劑,例如含硫化合物,其包括(但不限於)硫醇、硫代烷醇(例如硫代乙醇)、含有硫基之羧酸(例如硫代乙酸)或單體。較佳地,聚合物封端基團彼此獨立地選自由以下組成之群:氫;羥基;胺基;硫醇;經取代或未經取代之C1-C8-烷基,其尤其包括C1-C8-羥基烷基、C1-C8-胺基烷基、C1-C8-硫代烷基;亞胺基醇,例如α-亞胺基烷-ω-醇(例如-NH-(CH2
)n
-OH;n係整數且範圍為1至8);芳烷基,例如苄基以及甲苯基;及芳基。 較佳地,聚醯胺由至少一個、更佳一個根據式(I)之聚合部分及兩個彼此獨立地選自上文所定義之基團之聚合物封端基團組成。更佳地,封端基團彼此獨立地選自由以下組成之群:氫、羥基、胺基、硫醇、C1-C8-羥基烷基、C1-C8-胺基烷基、C1-C8-硫代烷基、α-亞胺基烷-ω-醇(例如-NH-(CH2
)n
-OH;n係整數且範圍為1至8)、芳烷基及未經取代之C1-C8-烷基。甚至更佳地,聚醯胺係由根據式(I)之聚合部分及兩個聚合物封端基團組成,其中一個聚合物封端基團係選自由芳烷基及非官能化之C1-C8-烷基組成之群且另一聚合物封端基團係選自由以下組成之群:氫、羥基、α-亞胺基烷-ω-醇及胺基。 用於銅及銅合金表面之蝕刻溶液包含含有至少一個根據式(I)之聚合部分之聚醯胺,較佳地總濃度為1至2000 mg/l。該濃度範圍容許獲得最佳結果。在該範圍以外之濃度產生較差之蝕刻結果。例如更高之濃度可對經處理之銅或銅合金表面產生過強之蝕刻。 含有至少一個根據式(I)之聚合部分之聚醯胺可藉由標準文獻方法製備或原樣購買。如(例如) R. Hoogenboom、M. W. M. Fijten、M. A. R. Meier、U. S. Schubert,Macromolecular Rapid Communications, 2003, 第24 (1)卷, 第92-97頁及K. Aoi、M. Okada,Progess in Polymer Science, 1996, 第21卷, 第151-208頁(具體而言其中之部分5及6,第160-189頁)所闡述之陽離子聚合適當官能化之噁唑啉及/或噁嗪衍生物產生聚噁唑啉、聚噁嗪或各別共聚物尤佳,此乃因合成容易。其替代製備程序包括乙烯基醯胺之自由基聚合,或可藉由與適宜添加劑(例如醯氯(或酸性氯化物))反應將適宜聚伸烷基亞胺轉化為含有至少一個根據式(I)之聚合部分之聚醯胺。 在合成含有根據式(I)之聚合部分之聚醯胺期間為避免不期望之副反應,R1
較佳不包含任何不飽和部分(例如雙鍵或三鍵)。此等不飽和部分可損害合成之有效性且因此可導致聚醯胺之有用性降低。出於相同原因,甚至更佳地,R1
係選自未經取代之烷基。 蝕刻溶液包含至少一種適於氧化銅之氧化劑。適於氧化銅之氧化劑對於既定濃度及pH值通常具有大於銅之標準氧化電位。通常,至少一種適於氧化銅之氧化劑之濃度係在0.05 wt.-%至20 wt.-%、較佳1.0 wt.-%至10.0 wt.-%或15 wt.-%範圍內。 較佳地,該至少一種氧化劑係選自由以下組成之群:過氧化物,例如過氧化氫、金屬過氧化物(例如過氧化鈉、過氧化鉀);金屬超氧化物,例如超氧化鉀;銅離子及鐵離子。為防止過氧化物之分解,可添加其他額外的化合物,例如對酚磺酸。較佳以1 g/l至150 g/l之濃度範圍含有過氧化物及超氧化物。 鐵離子可藉由任何水溶性鐵離子源提供,例如鐵(III)鹽(即鐵鹽)或鐵(III)錯合物。較佳地,鐵離子源係選自由以下組成之群:硫酸鐵(Fe2
(SO4
)3
)、三氯化鐵(FeCl3
)、溴化鐵(FeBr3
)、硝酸鐵(Fe(NO3
)3
)、乙酸鐵(Fe(OC(O)CH3
)3
)、氫氧化鐵(Fe(OH)3
)、其各別水合物或以上所提及者之混合物。較佳以1 g/l至50 g/l之濃度範圍含有鐵離子。 銅離子可藉由任何水溶性銅離子源提供,例如銅鹽或銅錯合物。任何水溶性銅鹽係可能之銅離子源,較佳之銅離子源係硫酸銅(II)、氯化銅(II)、溴化銅(II)、乙酸銅(II)、甲酸銅(II)、氧化銅(II)、氫氧化銅(II)、烷基磺酸銅(II)、芳基磺酸銅(II)、其水合物或以上所提及者之混合物。較佳以1 g/l至70 g/l之濃度範圍含有銅離子。 更佳地,該至少一種氧化劑係選自由銅離子及鐵離子組成之群。甚至更佳地,蝕刻溶液包含至少一種鐵離子源及至少一種銅離子源作為氧化劑。 蝕刻溶液包含至少一種酸。該至少一種酸較佳係選自由以下組成之群:硫酸、烷基磺酸(例如甲烷磺酸)、芳基磺酸(例如苯基磺酸、甲苯磺酸)、硝酸、磷酸、甲酸、乙酸、丙酸及其混合物。硫酸、烷基磺酸及芳基磺酸更佳,此乃因其高導電性使得其在蝕刻溶液欲藉由電解方式再生時極其有用。上述酸之總濃度較佳在10 g/L至250 g/L範圍內。 根據本發明之蝕刻溶液包含至少一種鹵離子源。氯離子源及溴離子源較佳。氟離子在酸性介質中可形成氫氟酸,其極其有毒且難以處置,而碘離子在蝕刻溶液中可氧化,此使得其失效。適宜氯離子源之實例係水溶性氯鹽。較佳地,至少一種氯離子源係選自由以下組成之群:氯化氫、水溶性金屬氯化物,例如鹼金屬氯化物(例如氯化鋰、氯化鈉、氯化鉀及氯化銫),鹼土金屬氯化物(例如氯化猛、氯化鈣、氯化鍶及氯化鋇),過渡金屬氯化物(例如氯化猛、氯化鐵、氯化鈷、氯化鎳、氯化銅及氯化鋅)、氯化銨及其混合物。更佳地,至少一種氯離子源係選自由以下組成之群:氯化氫、鹼金屬氯化物及氯化銨。適宜溴離子源之實例係水溶性溴鹽。較佳地,至少一種溴離子源係選自由以下組成之群:溴化氫、水溶性金屬溴化物,例如鹼金屬溴化物(例如溴化鋰、溴化鈉、溴化鉀及溴化銫),鹼土金屬溴化物(例如溴化錳、溴化鈣、溴化鍶及溴化鋇),過渡金屬溴化物(例如溴化錳、溴化鐵、溴化鈷、溴化鎳、溴化銅及溴化鋅)、溴化銨及其混合物。更佳地,至少一種溴離子源係選自由以下組成之群:溴化氫、鹼金屬溴化物、溴化銨及溴化鋅。鹵離子之濃度較佳端視存在於蝕刻溶液中之氧化劑來選擇。若鐵離子用作唯一氧化劑,則所有鹵離子之濃度較佳在1 mg/l至500 mg/l、更佳10 mg/l至200 mg/l且最佳20 mg/l至100 mg/l範圍內。該等濃度亦可適用於過氧化物或超氧化物作為唯一氧化劑。若銅離子用作唯一氧化劑,則所有鹵離子之濃度較佳在0.1 g/l至200 g/l、更佳1 g/l至100 g/l範圍內。鹵化鐵或鹵化銅作為氧化劑亦可提供可選鹵離子。就可防止極細銅線(例如寬度小於10 µm之彼等)之不期望蝕刻及線形改變較不明顯而言,鹵離子改良蝕刻結果。 根據本發明之蝕刻溶液視情況包含至少一種選自由以下組成之群之唑腐蝕抑制劑:苯并***、5-甲基苯并***、1H
-1,2,3-甲基苯并***、咪唑、1H
-1,2,3-***、4-甲基噻唑、3-胺基-1H
-1,2,4-***、1H
-四唑、5-甲基-1H
-四唑、5-苯基-1H
-四唑及5-胺基-1H
-四唑。較佳地,唑腐蝕抑制劑係選自1H
-四唑、5-甲基-1H
-四唑、5-苯基-1H
-四唑及5-胺基-1H
-四唑,此乃因此等四唑衍生物提供改良之蝕刻溶液之穩定性。添加唑腐蝕抑制劑由於形成保護性唑層而有利地降低欲處理之金屬表面之腐蝕,且有時在使用期間其亦減少沈澱物自蝕刻溶液形成。偶爾,在一些銅自銅或銅合金表面溶解之後,沈澱物形成,其限制蝕刻溶液之壽命。若蝕刻溶液包含至少一種唑腐蝕抑制劑,則可選唑腐蝕抑制劑之總濃度較佳在0.01 wt.-%至2.0 wt.-%範圍內。 根據本發明之蝕刻溶液視情況包含至少一種聚伸烷基二醇化合物,例如聚乙二醇、聚丙二醇、聚乙二醇及聚丙二醇之共聚物及其衍生物,其皆可改良欲處理之銅或銅合金表面之可潤濕性及由此本發明之蝕刻溶液之蝕刻行為。若蝕刻溶液包含至少一種聚伸烷基化合物,則蝕刻溶液中可選聚伸烷基化合物之總濃度係在100 mg/l至2000 mg/l範圍內。 根據本發明之蝕刻溶液視情況包含至少一種亞鐵離子源。亞鐵離子可藉由任何水溶性亞鐵離子源提供,例如鐵(II)鹽(即亞鐵鹽)或鐵(II)錯合物。較佳地,亞鐵離子源係選自由以下組成之群:硫酸亞鐵(FeSO4
)、硫酸亞鐵銨((NH4
)2
Fe(SO4
)2
)、氯化亞鐵(FeCl2
)、溴化亞鐵(FeBr2
)、硝酸亞鐵(Fe(NO3
)2
)、乙酸亞鐵(Fe(OC(O)CH3
)2
)及氫氧化亞鐵(Fe(OH)2
)及其各別水合物。較佳以1 g/l至50 g/l之濃度範圍使用可選亞鐵離子。當鐵離子用作氧化劑且期望蝕刻溶液再生時,使用可選亞鐵離子尤其有用。 根據本發明之蝕刻溶液係水溶液。此意味著主要溶劑為水。可添加可與水混溶之其他溶劑,例如極性溶劑,包括醇、二醇及二醇醚。出於其生態學良性特性,較佳僅使用水(即基於所有溶劑大於99 wt.-%)。 根據本發明之蝕刻溶液之pH值較佳≤ 7、更佳≤ 4。 根據本發明之蝕刻溶液可藉由將所有組份溶於水中來製備。若出現溶解度問題,則可使用pH調整劑(例如酸及鹼)來增加欲溶解組份之溶解度。其亦可藉由提供濃縮物然後在本發明之蝕刻溶液使用之前稀釋及/或混合該等濃縮物來製備。 在本發明之一個實施例中,蝕刻溶液係包含以下各項或由以下各項組成之水溶液: a) 至少一種含有至少一個根據式(I)之聚合部分之聚醯胺; b) 至少一種酸; c) 至少一種適於氧化銅之氧化劑; d) 至少一種鹵離子源; e) 至少一種溶劑、較佳水; f) 視情況,至少一種唑腐蝕抑制劑; g) 視情況,至少一種聚伸烷基化合物;及 h) 視情況,至少一種亞鐵離子源 個別組份具有上文所界定之濃度。 在本發明之較佳實施例(本文中稱為「鐵離子蝕刻溶液」)中,蝕刻溶液係包含以下各項或由以下各項組成之水溶液: a) 至少一種含有至少一個根據式(I)之聚合部分之聚醯胺;濃度較佳為1 mg/l至2000 mg/l (基於所有聚醯胺之總量) b) 至少一種酸; c) 至少一種鐵離子源,濃度較佳在1 g/l至50 g/l範圍內; d) 至少一種鹵離子源; e) 至少一種溶劑、較佳水; f) 視情況,至少一種唑腐蝕抑制劑;及 g) 視情況,至少一種聚伸烷基化合物。 在本發明之另一較佳實施例(本文中稱為「銅離子蝕刻溶液」)中,蝕刻溶液係包含以下各項或由以下各項組成之水溶液: a) 至少一種含有至少一個根據式(I)之聚合部分之聚醯胺;較佳地濃度為1 mg/l或50 mg/l至2000 mg/l (基於所有聚醯胺之總量) b) 至少一種酸; c) 至少一種銅離子源,濃度較佳在1 g/l至70 g/l範圍內; d) 至少一種鹵離子源; e) 至少一種溶劑、較佳水; f) 視情況,至少一種唑腐蝕抑制劑;及 g) 視情況,至少一種聚伸烷基化合物。 鐵離子蝕刻溶液及銅離子蝕刻溶液尤其可用於改良隨後積層之有機基質至此等經處理之銅或銅合金表面上之黏合強度。鐵離子蝕刻溶液亦可用於微分蝕刻,同時保留此等經處理之銅或銅合金線之幾何形式,減少底切之風險。包含過氧化物或超氧化物作為氧化劑之蝕刻溶液尤其可用於使銅或銅合金表面變粗糙。利用根據本發明之蝕刻溶液,甚至在具有高導體密度之區域中亦可完全去除晶種層。 根據本發明之蝕刻溶液可用於銅及銅合金表面之蝕刻,由此在避免顯著線形改變、底切及線寬減小的同時容許隨後將有機基質或精整加工(例如浸漬錫)緊密結合至銅或銅合金表面或結合至其上結合之有機基質。由此可提供有機基質與精整加工之充分黏合。 本發明之用於處理銅或銅合金表面之方法包含以下步驟: (i) 提供包含銅或銅合金表面之基板;及 (ii) 使該銅或銅合金表面之至少一部分與根據本發明之蝕刻溶液接觸。 該等步驟係以上文給出之順序實施。 在本發明之上下文中之基板可係任何包含銅及銅合金表面之基板。基板可整體由銅或銅合金製得,或者其包含由銅或銅合金製得之表面。較佳地,基板選自銅箔、銅合金箔、印刷電路板、IC基板、中介層、鍍銅半導體晶圓及覆銅層壓板(CCL)。鍍銅半導體晶圓意指其上具有銅或銅合金結構(例如槽、線、點等)之晶圓基板。 銅表面在本文中定義為較佳由99 wt.-%或更多之銅製成。術語「銅合金」根據本發明較佳係指由90 wt.-%至99 wt.-%銅組成之合金。較佳地,合金之其他組份係選自以下之一或多者:硼、矽、磷或另一金屬,例如鎳、鐵、鎘、鋅、錫、鈦。 尤佳者係電解沈積(ED)銅及銅合金表面、更佳平均粒度d50
為1 µm至5 µm之彼等,如藉由SEM (掃描電子顯微鏡)所測定。 步驟(ii)在本文中稱為「處理步驟」。銅或銅合金表面之至少一部分與蝕刻溶液之接觸可藉由業內已知之任何方式實現。通常,蝕刻溶液可以噴塗、擦拭或以其他方式置於銅或銅合金表面上或銅或銅合金表面可浸入或浸漬於蝕刻溶液中。較佳地,蝕刻溶液噴塗於該表面上。噴塗通常改良蝕刻溶液之再生,但尤其係在銅離子蝕刻溶液之情形下。亦改良蝕刻溶液至表面之輸送且最小化擴散過程。 蝕刻溶液亦可用於臥式設備、捲盤至捲盤、垂直及垂直傳送帶式設備。 在步驟(ii)中蝕刻溶液之溫度較佳在20℃至50℃範圍內。蝕刻溶液之更高溫度導致更快之銅或銅合金表面之蝕刻過程。然而,過高之溫度可對蝕刻溶液之穩定性有害。 蝕刻溶液與銅或銅合金表面之接觸時間必須根據蝕刻溶液之溫度及所期望之蝕刻深度調整。蝕刻溶液與銅或銅合金表面之接觸時間通常在5秒至300秒範圍內。在一些情形下,例如若要去除更多銅,則需要根據所期望之蝕刻結果調整接觸時間。若需要,此調整可藉由常規實驗進行。 較佳將空氣進料或氧進料提供至蝕刻溶液中,同時使其與銅或銅合金表面接觸。可例示性地藉由將該等氣體鼓泡至蝕刻溶液中來提供空氣進料或氧進料。此改良混合並減少必要之處理時間及/或改良蝕刻之均勻性。 根據本發明之方法在個別製程步驟期間可包含用溶劑(例如水)之沖洗步驟。具體而言,在銅或銅合金表面與蝕刻溶液接觸之後,適當地用水沖洗銅或銅合金表面以去除任何不期望之溶液殘留物。根據本發明之方法可進一步包含乾燥步驟。可(例如)在處理步驟之後利用熱水沖洗銅或銅合金表面,隨後利用熱空氣或在烘箱中進行乾燥。然後,在任何進一步處理之前,可用稀酸溶液(例如10 wt.-%鹽酸或10 wt.-%硫酸)浸漬或以其他方式處理銅或銅合金表面。 在先前技術之某些製程中,藉由滲出(去除)適當量之蝕刻溶液並向剩餘溶液添加(進給)新鮮蝕刻溶液來去除一些或所有所添加之銅離子。 一種自水溶液去除銅離子之特定方法係以電解方式將銅離子還原為金屬銅。原則上,電解需要配備有陽極及陰極以及整流器之第二罐。將根據本發明之蝕刻溶液之部分自第一罐(在其中或自其進行銅或銅合金層之蝕刻)轉移至配備用於電解之第二罐。在電解期間,銅離子在陰極還原為金屬銅且同時亞鐵離子在陽極氧化為鐵離子。 可收集金屬銅並使其再循環。在無電解再生池之情形下,則將需要向蝕刻溶液連續添加氧化劑(例如鐵離子)。藉由應用上述再生,所消耗之鐵離子在陽極再生(Fe2+
氧化為Fe3+
),且藉此在使用蝕刻溶液期間無需添加(進給)氧化劑。 可用於此製程之方法及裝置揭示於US 2006/0175204 A1中。此方法涉及將蝕刻溶液進給至氣密密封或具有陽極罩之電解池中,該電解池包含陰極、惰性陽極、用於自陰極去除電解沈積銅之構件及用於收集所去除銅並向所去除銅施加電勢之構件,其中該電解池不具有離子交換膜或隔膜。或者,可使用化學氧化劑(chemical oxidant)用於適於氧化銅之氧化劑(例如鐵離子)之再生。用於此目的之可用化學氧化劑尤其係過氧化物、過硫酸鹽(例如過硫酸鈉)及臭氧。 本發明之用於處理銅或銅合金表面之方法視情況進一步包含以下步驟 (ia) 預處理銅或銅合金表面。 預處理係在步驟(i)與(ii)之間進行。銅及銅合金表面之預處理方法為業內所已知。此預處理尤其包括清潔步驟、去除不期望之層(例如鉻酸鹽及/或氧化物層)及沈積有機單層(例如通常用於電解鍍銅中之唑腐蝕抑制劑、整平劑或增亮劑化合物之單層)。 清潔銅及銅合金表面可藉由業內已知之各種方式完成。通常,此等清潔步驟使用可為酸性或鹼性之水溶液,其視情況包含表面活性劑及/或共溶劑(例如二醇)。鉻酸鹽層可藉由採用(例如)含有過硫酸鈉及/或其他氧化劑之水溶液之氧化處理來去除。銅或銅合金表面上之氧化物層或其他不期望殘餘物可藉由酸性水性處理來去除。有機單層可藉由利用包含唑腐蝕抑制劑(例如苯并***)之水溶液處理銅或銅合金表面來形成。 本發明之用於處理銅或銅合金表面之方法視情況進一步包含以下步驟 (iii) 使銅或銅合金表面與後浸溶液接觸。 此步驟稱為「後浸步驟」。 可選步驟(iii) (後浸步驟)在步驟(ii) (處理步驟)之後包括於本發明之用於處理銅或銅合金表面之方法中。銅或銅合金表面與後浸之接觸係選自與步驟(ii)中針對蝕刻溶液與銅或銅合金表面之間之接觸所給出相同之可能性。可選擇相同或不同之接觸可能性。若進行後浸步驟,則有利地在光阻劑或焊料遮罩施加之前徹底沖洗銅或銅合金表面或以其他方式自其去除任何殘餘物。 後浸步驟使用鹼性後浸溶液或酸性後浸溶液。酸性後浸溶液係水溶液含有至少一種酸、較佳鹽酸。酸性後浸之pH值通常為1或更小。若在蝕刻溶液中使用氯化銅作為氧化劑,則通常使用酸性後浸。或者,若隨後或在本發明之方法之後期階段應用光阻劑,由於光阻劑對鹼性處理或存在於其上沈積此一光阻劑之表面上之此等鹼性殘留物不穩定,則可使用酸性後浸。 鹼性後浸溶液係含有至少一種氫氧離子(OH-
)源之水溶液。此等氫氧離子源可係任何與水接觸後釋放或以其他方式形成氫氧離子(例如鹼)之水溶性化合物。較佳地,氫氧離子源係選自金屬氫氧化物,例如鹼金屬氫氧化物及胺(例如氨)。鹼性後浸溶液之pH值通常為10或更高。若隨後或在任何後期階段欲施加焊料遮罩,由於焊料遮罩對酸性處理、其上沈積此一焊料遮罩之表面上之酸性殘留物不穩定,或若在蝕刻溶液中存在除銅離子之外之氧化劑,則視情況使用鹼性後浸溶液。 本發明之用於處理銅或銅合金表面之方法視情況進一步包含以下步驟 (iv) 使有機基質積層至經處理之銅或銅合金表面。 有機基質包括(但不限於)預浸體、焊料遮罩、光阻劑及諸如此類。預浸體係纖維增強塑膠,通常使用玻璃增強環氧基質(例如FR-4、FR-5)及依序堆積膜(例如Ajinomoto GX92、Ajinomoto GXT31)。 對於步驟(iv)或者或另外,可將步驟 (v) 將精整加工沈積於經處理之銅或銅合金表面或其部分上 包括於本發明之方法中。 該等精整加工包括諸如以下之加工:浸漬錫、無電鎳浸漬金(ENIG)、無電鎳無電鈀無電金(ENEPIG)、無電鈀無電金(EPIG)、浸漬銀、有機焊料防腐劑(OSP)及諸如此類。該等加工在業內充分確定。可用之錫沈積方法包括(例如)如EP 2476779 B1中所述之浸漬鍍錫。 有利地,由於極少或無銅自銅槽及線之側面溶解,因此本發明之方法及本發明之蝕刻溶液之使用產生極少線形劣化或無線形劣化。由於在蝕刻溶液中存在含有至少一個根據式(I)之聚合部分之聚醯胺,蝕刻速率變得(幾乎)與噴塗壓力無關,此進而產生更均勻之蝕刻結果,尤其在阻劑佈局變化或單一基板上之空間線比率(line in space ratio)改變之情況下。 以下非限制性實例進一步說明本發明。實例
蝕刻溶液係藉由將所有組份溶解於水中或(若需要)溶解於稀酸化溶液中來製備。實驗中所使用之ED銅箔具有0.5-3 µm之平均粒度,如藉由電拋光樣品之SEM所測定。實驗中所使用之電路化板包含22根銅線,其在處理之前及/或之後以橫截面進行分析。個別銅線具有如圖3中所繪示及表I中所給出之佈局。 表I:電路化板之佈局。
根據IPC-TM-650測試方法手冊編號2.4.8修訂版C中所述之方法量測經處理之銅表面與有機基質之間之黏合強度值(亦稱為剝離強度值)。 藉由掃描原子力顯微鏡(Digital Instruments, NanoScope,配備有來自Nanosensors之具有小於7 nm之尖部半徑之PointProbe®
)來測定外表面之光滑度(或粗糙度),掃描大小:5 × 5 µm,以輕敲模式掃描。藉由該等量測獲得RSAI值(相對表面積增加)及Sa
(平均粗糙度),並以下文之各別實例提供。 使用Carl Zeiss SMT Ltd. EVO15-07.05或Helios NanoLab 650掃描電子顯微鏡(SEM,均為FEI Company)進行銅表面之微觀表徵。或者,若適用,使用光顯微鏡(Olympus Optical Ltd., BX 60F-3)。 聚合物之數量平均莫耳質量Mn
係藉由NMR量測測定。將聚合物溶解於適宜溶劑(例如D2
O或d4
-甲醇)中,且基於屬起始基團之氫原子之積分及屬聚合鏈之氫原子之積分計算數量平均莫耳質量Mn
。使用多分散指數使Mn
及Mw
彼此轉變。 為評價線形改變(及由此所期望矩形形狀之保持),量測頂部-底部差值。頂部-底部差值係藉由量測橫截面中頂部(寬度頂部
)及底部(寬度底部
)處之各別銅或銅合金線之寬度獲得。自下式獲得頂部-底部差值: 頂部-底部差值=寬度頂部
-寬度底部
因此,負的頂部底部差值係關於主要在頂部蝕刻之銅線而正的頂部-底部差值意味著在該等銅線之底部之蝕刻佔優。由於此等銅線具有矩形形狀,因此經處理銅線之頂部-底部差值應接近於0。 底切之形成係藉由量測橫截面中突出(over-standing)銅線(參見圖4)之銅線邊界與假想延長線(圖4中之β)之距離(圖4中之α)來定量。若底切存在於銅線之兩側上,則將兩個值相加以形成總底切,其在此情形下提供於本文實驗中。通常,不期望底切,然而,圖4中該值α愈小愈佳。 線寬減小係藉由量測處理之前及之後之銅線大小來獲得。該值愈小愈佳。 蝕刻速率係藉由處理覆銅層壓板60 s並量測蝕刻之前及之後之質量來獲得。可將其差值再計算為對於60 s之蝕刻速率。 Lupasol ® G 500 (BASF SE之產品)係質量平均莫耳質量為25000 amu之聚乙烯亞胺。在本文中比較有時縮寫為comp.且本發明縮寫為inv.。合成實例 A :
將反應燒瓶加熱至70℃並用氬吹掃1 h以自其去除任何痕量水。然後,於該燒瓶中將36.0 g 2-乙基-4,5-二氫噁唑在氬氣氛中溶解於50 ml無水二甲基乙醯胺中。在添加作為起始試劑之0.777 g苄基溴後,將反應混合物加熱至100℃並在該溫度下攪拌20 h。在冷卻至25℃後,獲得紅色-橙色之聚醯胺溶液,其用1 ml作為終止試劑之水淬滅。在減壓下去除揮發性組份。將反應混合物溶解於80 ml氯仿中並添加200 ml正己烷。一旦澄清,則棄去所得上部相,並在減壓下及在真空中自下部相去除任何揮發物。 所得橙色固體(定量產率)為質量平均莫耳質量Mn
為2200 amu之期望聚醯胺。合成實例 B 至 C :
遵循合成實例1所給出之程序,其他噁唑及噁嗪衍生物(共)聚合。試劑及結果於表II中給出。 表II:聚合結果。 應用實例 1:
製備各自含有25 g/l鐵離子(添加為硫酸鐵(III))、160 ml/l硫酸(50 wt.-%)、30 mg/l氯離子(添加為氯化鈉)及如表III中所給出之添加劑之蝕刻水溶液。 利用含有150 g/L過硫酸鈉及130 mL/L硫酸(50 wt.-%)之水溶液在35℃下將ED銅箔預處理15秒以去除鉻酸鹽層。在用去離子水沖洗之後,此等經處理之ED銅箔準備好使用。將上文所述之蝕刻溶液噴塗(1.8巴(bar),35℃)至ED銅箔上。調整處理時間以具有與下表中所給出之所有測試試樣相當之蝕刻深度。再次沖洗之後,利用鼓風機在60℃下乾燥樣品。將樣品積層至預浸體(來自Isola Group S.a.r.l.之Isola 104 ML FR-4 (「FR-4」),Tg
=135℃)上。黏合強度值量測之結果匯總於下表中。給出各個蝕刻深度(即分別0.3 µm、0.5 µm及0.8 µm)之黏合強度值。 本發明之應用實例1b至1d之聚醯胺包含一個根據式(I)之聚合部分,其中R1
係甲基,a為1且質量平均莫耳質量為50000 amu。 本發明之應用實例1e至1g之聚醯胺包含一個根據式(I)之聚合部分,其中R1
係甲基,a為1且質量平均莫耳質量為500000 amu。 表III:依賴於蝕刻深度之黏合強度值。 1
50000 amu;2
500000 amu,3
蝕刻深度;comp.意指比較;inv.意指本發明;n.d.未測定。 本發明實例之黏合強度量測之結果優於不含此添加劑之比較實例1a。對於所有測試,黏合強度很大程度上與蝕刻深度無關。 值得注意地,與自Mw
為50000 amu之聚醯胺獲得之結果相比,利用包含具有較高Mw
之聚醯胺之蝕刻溶液處理之銅表面之黏合強度顯著改良。具有較高Mw
之聚醯胺之最佳濃度為約70 mg/l。更高之濃度不再增加黏合。對於較小之聚醯胺而言,所發現之最佳濃度為25 mg/l;此外,在此情形下更高之濃度並不產生任何進一步之黏合強度改良。 使用其他聚合物產生顯著更低之黏合強度值。此外,利用比較蝕刻溶液處理之銅表面之粗糙度較不明顯,此可係關於為什麼對有機基質黏合弱之一個原因。應用實例 2 :
藉由將組份溶解於水中製備三種蝕刻溶液: 應用實例2a (比較):10 g/kg鐵離子(添加為氯化鐵(III))、50 g/kg甲酸及25 mg/kg聚乙烯亞胺 應用實例2b (比較):15 g/l銅(添加為硫酸銅(II))、80 g/l氯化物(添加為氯化鈉)、100 g/l甲酸、0,001 g/l鐵離子(添加為硫酸鐵(III))、25 mg/l聚乙烯基吡咯啶酮 應用實例2c (根據本發明之方法):15 g/l鐵離子(添加為硫酸鐵(III))、30 g/l銅(II)離子(添加為硫酸銅(II))、160 ml/l硫酸(50 wt.-%)、60 mg/l氯離子(添加為氯化鈉)及一種包含一個根據式(I)之聚合部分之聚醯胺,其中R1
係甲基,a為1且質量平均莫耳質量為50000 amu。 電路化板不經任何預處理即使用。將上文所述蝕刻溶液之每一者噴塗(1.8巴,35℃)至個別電路化板上。調整處理時間以完全清潔銅晶種層。再次沖洗之後,利用鼓風機在60℃下乾燥樣品。然後,形成橫截面並評估幾何特徵(底切、頂部-底部差值、線寬減小)。 表IV:經處理之銅線之幾何特徵。
分別使用聚乙烯亞胺及聚乙烯基吡咯啶酮之比較實例2a及2b較本發明實例2c產生更強之底切形成。利用含有聚乙烯亞胺之蝕刻溶液處理之銅線之頂部-底部差值顯示與本發明實例相當之線寬減小,但銅線不為所期望之矩形,此可自頂部-底部差值之較高值看出。 儘管比較實例2b中經處理之銅線之頂部-底部差值足夠,但嚴重底切形成及顯著線寬減小使得結果不可接受。 另一方面,本發明實例2c在保持經處理之銅線之矩形形狀(由頂部-底部差值表示)及可接受之線寬減小的同時顯示極少底切形成。應用實例 3 :蝕刻性能
製備各自含有15 g/l鐵離子(添加為硫酸鐵(III))、30 g/l銅(II)離子(添加為硫酸銅(II))、160 ml/l硫酸(50 wt.-%)、30 mg/l氯離子(添加為氯化鈉)及如表V中所給出之添加劑之蝕刻水溶液。 電路化板不經任何預處理即使用。將個別蝕刻溶液加熱至35℃並噴塗至電路化銅板上(1.5巴)。將蝕刻深度調整至大於所需0.2 µm以完全去除晶種層。 然後,該經處理之覆銅層壓板之橫截面形成且就線形改變(頂部-底部差值)、線寬減小及底切形成來分析個別22根銅線。結果匯總於表V中。 表V:含有各種添加劑之蝕刻溶液之蝕刻性能。 1
Mw
= 50000 amu,2
Mw
= 1200 amu,3
Mw
= 60000 amu,4
Mw
= 29000 amu 應用實例3a、3c至3f係比較實例,而應用實例3b為根據本發明者。處理之結果可參見圖2,其顯示經應用實例3之蝕刻溶液處理之銅線之橫截面。圖2A係關於應用實例3a,圖2B係關於應用實例3b,圖2C係關於應用實例3c,圖2D係關於應用實例3d,圖2E係關於應用實例3e且圖2F係關於應用實例3f。 比較應用實例3a不含任何添加劑且顯示嚴重之線形改變以及線寬減小。此等結果不可接受。 本發明之應用實例3b含有包含根據式(I)之聚合部分之聚醯胺,其中R1
係甲基且a總係1。與不含任何添加劑之比較應用實例3a之蝕刻溶液相比,線形改變及線寬減小改良。頂部底部差值及線寬減小改良且底切之形成幾乎完全避免。 比較應用實例3d含有Lupasol G 500,其為聚乙烯亞胺。經含有該添加劑之蝕刻溶液處理之銅線之線形改變及線寬減小不可接受,且與自不含添加劑(應用實例3a)之蝕刻溶液獲得之結果相比甚至更差。 此外,比較應用實例3e含有具有較小質量平均莫耳質量之第二聚乙亞胺。然而,結果與藉由比較應用實例3d所獲得之彼等類似且因此不可接受。 在比較應用實例3e中使用聚乙烯基吡啶顯示優於前述比較應用實例之聚乙烯亞胺之結果。然而,結果仍不可接受(尤其頂部底部差值及線寬減小)且較本發明實例3b之彼等差。 應用實例3f之聚乙烯基吡咯啶酮顯示可接受之線形改變及底切。但是,結果仍劣於本發明之應用實例3b之彼等。應用實例 4 :噴塗壓力變化
製備各自含有15 g/l鐵離子(添加為硫酸鐵(III))、15 g/l 亞鐵離子(添加為硫酸鐵(II))、30 g/l銅(II)離子(添加為硫酸銅(II))、160 ml/l硫酸(50 wt.-%)、30 mg/l氯離子(添加為氯化鈉)及如表VI中所給出之添加劑之蝕刻水溶液。 在噴塗模組(體積1l)中,將蝕刻溶液(35℃)在各種噴塗壓力下噴塗於覆銅層壓板上。在表VI中,噴塗壓力對蝕刻速率之效應係關於在0.5巴噴塗壓力下所使用之每一調配物獲得之蝕刻速率給出。所有值作為該0.5巴噴塗壓力之值之百分比提供。 本發明之應用實例4b之聚醯胺包含一個根據式(I)之聚合部分,其中R1
係甲基,a為1且質量平均莫耳質量為50000 amu。 表VI:所用添加劑及噴塗壓力對蝕刻速率之依賴性。 1
1200 amu,2
29000 amu 本發明之應用實例4b顯示蝕刻速率對噴塗壓力無依賴性。此在處理具有不同縱橫比或L/S (空間線)比率之表面時尤其有用。若表面上之蝕刻速率與噴塗壓力無關,則將確保對於緻密及隔離結構之類似蝕刻結果。 比較應用實例4a及4c至4f皆顯示蝕刻速率隨噴塗壓力增加而增加。此係不利的,此乃因具有不同大小之結構及孔口之銅表面將不均勻地蝕刻。此係由此等孔口中之局部流動特性所致。應用實例 5 :
製備各自含有15 g/l銅(II)離子(添加為硫酸銅(II))、100 g/l甲酸(50 wt.-%)、80 g/l氯離子(添加為氯化鈉)、1 mg/l鐵離子(添加為硫酸鐵五水合物)及如表VII中所給出之添加劑之蝕刻水溶液。 在8l噴塗模組中,利用上文所述之蝕刻溶液使電路化板經受噴塗處理(35℃,0.5巴)。在該處理後量測該等電路化板上之銅線且各別值可參見表VII。 應用實例5a係比較實例。本發明之應用實例5b之聚醯胺包含一個根據式(I)之聚合部分,其中R1
係乙基,a為1且質量平均莫耳質量為50000 amu。 表VII:蝕刻結果。
將聚醯胺大量添加至應用實例5a之比較蝕刻溶液顯著改良線寬減小及頂部-底部差值。應用實例 6 :合成實例 A 至 C 之用途
製備各自含有15 g/l鐵離子(提供為硫酸鐵(III))、160 ml/l硫酸(50 wt.-%)、氯離子(添加為氯化鈉)及如表VIII中所給出之添加劑之蝕刻水溶液。 在2l噴塗模組中,利用上文所述之蝕刻溶液使電路化板經受噴塗處理(35℃,1.5巴)。在該處理之前及之後量測該等電路化板上之銅線且各別值可參見表VIII。 將蝕刻深度調整至0.6 µm並量測線寬減小。 表VIII:聚醯胺對蝕刻結果之濃度依賴性。
合成實例A及B之均聚物顯示較合成實例C之共聚物略高之線寬減小。此幾乎與蝕刻溶液中之氯化物濃度無關。應用實例 7 :
製備各自含有25 g/l鐵離子(添加為硫酸鐵(III))、30 g/l銅(II)離子(添加為硫酸銅(II))、160 ml/l硫酸(50 wt.-%)、60 mg/l氯離子(添加為氯化鈉)及如表IX中所給出之添加劑之蝕刻水溶液。 利用含有150 g/L過硫酸鈉及130 mL/L硫酸(50 wt.-%)之水溶液在35℃下將DC面板預處理15秒以去除鉻酸鹽層。在用去離子水沖洗之後,此等經處理之ED銅箔準備好投用。將上文所述之蝕刻溶液噴塗(1.8巴,35℃)至DC面板上。調整處理時間以具有與下表中所給出之素有測試試樣相當之蝕刻深度。再次沖洗之後,利用鼓風機在60℃下乾燥樣品。附著焊料遮罩(Green Cure焊料遮罩,LM600,根據如技術數據表中所提供之製造商之說明書應用),之後為浸漬錫沈積(Stannatech 2000 V,Atotech Deutschland GmbH之產品,根據如技術數據表中所提供之製造商之說明書應用)。利用膠帶測試(Scotch Crystal膠帶,45°)測定各個蝕刻深度(即0.3 µm、0.5 µm及0.8 µm)之黏合強度。此後,光學檢查基板,藉此計數綠色殘餘物之數量。該等綠色殘餘物代表該等焊料遮罩之個別附著點(此處總計為9個)。結果提供於表IX中。 本發明之應用實例7b之聚醯胺包含一個根據式(I)之聚合部分,其中R1
係甲基,a為1且質量平均莫耳質量為500000 amu。 表IX:依賴於蝕刻深度之黏合強度值。 1
蝕刻深度 對於比較應用實例7a,焊料遮罩藉由膠帶測試完全去除。與此相反,焊料遮罩更佳黏合至應用實例7b中之經本發明之蝕刻溶液處理之DC面板。僅觀察到1個綠點,而比較DC面板計數到9個綠點。 熟習此項技術者將自考量本說明書或實踐本文所揭示之本發明後明瞭本發明之其他實施例。本說明書及各實例僅意欲視為例示性,其中本發明之真實範圍僅藉由以下申請專利範圍來界定。
1‧‧‧銅線2‧‧‧底切α‧‧‧距離、值β‧‧‧假想延長線
圖1顯示繪示以下各項之各種銅線之橫截面: a) 未處理之銅線(圖1A); b) 具有底切形成之銅線(圖1B); c) 具有線形改變之銅線(圖1C);及 d) 具有線寬減小之銅線(圖1D)。 在圖1B中,銅線標記為1且底切標記為2。可看出底切存在於銅線下方。圖1C繪示具有不期望之線形改變之銅線。所示銅線具有梯形形狀且虛線突出所期望之矩形形狀。圖1D顯示圖1A之未經處理之銅線(上方)及經處理之銅線(下方),且藉由虛線強調線寬減小。 圖2A-2F顯示經如應用實例3中所報導之各種蝕刻溶液處理之銅線之橫截面。 圖3顯示(例如)在應用實例3至6中所使用之電路化SAP測試板(圖3A,本文縮寫為電路化板)及其橫截面(圖3B)之圖片。圖3A中之虛線繪示橫截面之位置。 圖4圖解說明底切之量測。
Claims (15)
- 如請求項1之用於銅及銅合金表面之蝕刻溶液,其中該至少一種含有至少一個根據式(I)之聚合部分之聚醯胺具有1,000amu至500,000amu之質量平均莫耳質量。
- 如請求項1或2之用於銅及銅合金表面之蝕刻溶液,其中該至少一種含有至少一個根據式(I)之聚合部分之聚醯胺具有5,000amu至100,000amu之質量平均莫耳質量。
- 如請求項1或2之用於銅及銅合金表面之蝕刻溶液,其中每一R1彼此獨立地選自由以下組成之群:甲基、乙基、正丙基、異丙基、正丁基、異丁基、第二丁基及第三丁基。
- 如請求項1或2之用於銅及銅合金表面之蝕刻溶液,其中進一步含有至少一個根據式(I)之聚合部分之該聚醯胺含有兩個彼此獨立地選自由以下組成之群之聚合物封端基團:氫;羥基;胺基;硫醇;經取代或未經取代之C1-C8-烷基;亞胺基醇;芳烷基;及芳基。
- 如請求項1或2之用於銅及銅合金表面之蝕刻溶液,其中該至少一種聚醯胺由至少一個根據式(I)之聚合部分及兩個聚合物封端基團組成。
- 如請求項6之用於銅及銅合金表面之蝕刻溶液,其中一個聚合物封端基團係選自由芳烷基及非官能化之C1-C8-烷基組成之群且另一聚合物封端基團係選自由氫、羥基、α-亞胺基烷-ω-醇及胺基組成之群。
- 如請求項1或2之用於銅及銅合金表面之蝕刻溶液,其中該至少一個根據式(I)之聚合部分係直鏈。
- 如請求項1或2之用於銅及銅合金表面之蝕刻溶液,其中其包含總濃度為1mg/l至2000mg/l之含有至少一個根據式(I)之聚合部分之聚醯胺。
- 如請求項1或2之用於銅及銅合金表面之蝕刻溶液,其中該至少一種適於氧化銅之氧化劑係選自由以下組成之群:過氧化氫;金屬過氧化物;金屬超氧化物;銅離子及鐵離子。
- 如請求項1或2之用於銅及銅合金表面之蝕刻溶液,其中該至少一種 酸係選自由以下組成之群:硫酸、烷基磺酸、芳基磺酸、硝酸、磷酸、甲酸、乙酸、丙酸及其混合物。
- 如請求項1或2之用於銅及銅合金表面之蝕刻溶液,其中該至少一種鹵離子源係選自氯離子源及溴離子源。
- 一種如請求項1至12中任一項之蝕刻溶液之用途,其用於蝕刻銅及銅合金表面。
- 一種用於根據本發明處理銅或銅合金表面之方法,其包含以下步驟:(i)提供包含至少一個銅或銅合金表面之基板;及(ii)使該銅或銅合金表面之至少一部分與如請求項1至12中任一項之蝕刻溶液接觸。
- 如請求項14之用於處理銅或銅合金表面之方法,其中包含銅或銅合金表面之該基板選自銅箔、銅合金箔、印刷電路板、IC基板、中介層、鍍銅半導體晶圓及覆銅層壓板。