TWI481648B - 表面修飾劑 - Google Patents
表面修飾劑 Download PDFInfo
- Publication number
- TWI481648B TWI481648B TW102119554A TW102119554A TWI481648B TW I481648 B TWI481648 B TW I481648B TW 102119554 A TW102119554 A TW 102119554A TW 102119554 A TW102119554 A TW 102119554A TW I481648 B TWI481648 B TW I481648B
- Authority
- TW
- Taiwan
- Prior art keywords
- integer
- ocf
- modifying agent
- group
- formula
- Prior art date
Description
本發明係針對一種用於多種基材表面上形成低表面張力層或防污層之表面修飾劑,以及一種使用該表面修飾劑來形成經處理層之方法。此外,本發明係關於其中使用該表面修飾劑之光學元件(例如抗反射膜、濾光片、光學透鏡、眼鏡鏡片、分束器、稜鏡、鏡面等);施用至顯示器(例如液晶顯示器、陰極射線管(CRT)顯示器、投影電視、電漿顯示器、電致發光(EL)顯示器等)之螢幕表面之抗反射光學元件;光學功能構件;其中此種光學功能構件係貼附於顯示器之螢幕表面之顯示器裝置;經處理之玻璃;經處理之陶瓷器;等。
抗反射塗層、濾光片、光學透鏡、眼鏡鏡片、分束器、稜鏡、鏡面和其它光學元件及衛生器皿於使用時容易受到指紋、皮脂、汗液、化妝品等的污染。一旦污漬黏附上時,此種污漬不容易被去除,特別黏附於具有抗反射塗層的光學構件上的污漬容易被注意到而造成問題。此外,汽車和飛機的窗戶也要求有耐久撥水性(durable water repellency:簡稱DWR)。
為了解決此等有關污漬和撥水性的問題,至目前為止已經提出使用多種防污漬劑之技術。
例如,日本專利申請公開案第1997-61605號提示一種經由使用含全氟烷基之化合物表面處理基材所得防污漬之抗反射濾光片。日本專利公告案第1994-29332號提示一種包含含全氟烷基之甲矽烷和乙矽烷化合物與鹵矽烷、烷基矽烷或烷氧基矽烷化合物之抗反射塗層塗覆於其表面上之防污漬低反射性塑膠。日本專利公開案第1995-16940號提示一種經由於主要由二氧化矽所組成之光學薄膜上形成(甲基)丙烯酸全氟烷酯與含烷氧基矽烷之單體之共聚物所得之光學構件。
但經由目前已知方法所形成之耐污漬塗層都有耐污漬性不足的缺點,特別諸如指紋、皮脂、汗液和化妝品等污漬難以從其上去除。此外,當長期使用此等耐污漬層時其將使耐污漬性大減。因此,期望發展出具有絕佳耐污漬性和絕佳耐用性之耐污漬塗層。
本發明欲解決前述先前技術之問題,提供一種表面修飾劑,其可形成高度耐用的優異的低表面張力處理層,該層可防止水分或諸如指紋、皮脂、汗液、化妝品等污漬黏附於各種基材表面上,特別為黏附於抗反射膜等光學構件及眼鏡之表面上,且允許污漬和水分一旦黏附時容易被擦拭去除。
本發明之另一目的係提供一種可形成優異
低表面張力層的表面修飾劑之製造方法。
本發明之又一目的係提供一種優異低表面張力層之方便形成方法。
本發明之又一目的係提供裝設有優異低表面張力層之光學構件和多種基材。
本發明之又一目的係提供裝設有優異低表面張力層之抗反射光學構件。
本發明之又一目的係提供一種裝設有抗反射構件之光學功能構件。
本發明之又一目的係提供具有一種裝設有光學功能構件之顯示器螢幕表面之顯示器裝置。
本發明之又一目的係提供本發明化合物應用至微製造例如奈米轉印領域,微製造領域近年來已有重大技術進展,因而允許精確地離型(mold releasing)。
本發明之又一目的係提供本發明化合物應用至裝置的製造,來提供一種材料和一種加工方法,由於本發明化合物具有高度撥水(repellency)性質因而使所提供之材料和加工方法容易加工具有極小寬度之線。
本發明之又一目的係提供本發明化合物應用於處理諸如混凝土、石灰石、花崗石或大理石等石器。
本發明提供一種防污劑,包含通式(A)所表示之有機聚矽氧化合物及/或通式(B)之部分水解產物。
F-(CF2
)q
-(OC3
F6
)m
-(OC2
F4
)n
-(OCF2
)o
(CH2
)p
X(CH2
)r
Si(X'
)3-a
(R1
)a
(A)
通式(A)中,q為1至3之整數;m、n及o分別為0至200之整數;p為1或2;X為O或二價有機基;r為2至20之整數;R1
為C1-22
直線或分支烴基;a為0至2之整數;及X’為可水解基團。
F-(CF2
)q
-(OC3
F6
)m
-(OC2
F4
)n
-(OCF2
)o
(CH2
)p
X(CH2
)r
(X'
)2-a
(R1
)a
SiO(F-(CF2
)q
-(OC3
F6
)m
-(OC2
F4
)n
-(OCF2
)o
(CH2
)p
X(CH2
)r
(X'
)1-a
(R1
)a
SiO)z
F-(CF2
)q
-(OC3
F6
)m
-(OC2
F4
)n
-(OCF2
)o
(CH2
)p
X(CH2
)r
(X'
)2-a
(R1
)a
Si(B)
通式(B)中,q為1至3之整數;m、n及o分別為0至200之整數;p為1或2;X為O或二價有機基;r為2至20之整數;R1
為C1-22
直線或分支烴基;a為0至2之整數;X’為可水解基團;及當a為0或1時,z為0至10之整數。
此外,本發明提供一種前述表面修飾劑之製造方法。
本發明提供一種使用該表面修飾劑形成低表面張力之方法。
本發明提供一種經由該表面修飾劑所得低表面張力之表面。
本發明提供一種裝設有經處理之含有該表面修飾劑之層之光學構件。
本發明提供一種裝設有經處理之含有該表面修飾劑之層之抗反射光學構件。
本發明提供一種含有該抗反射光學構件之光學功能構件。
本發明提供一種裝設有該光學功能構件之顯示器裝置。
本發明提供一種有一表面裝設有經處理之含有該表面修飾劑之層之無機基材,諸如玻璃。
本發明提供一種汽車用和航太用玻璃和衛生器皿,其具有無機基材,該無機基材具有前述表面。
本發明提供表面修飾劑應用於奈米轉印之精確離型。
本發明提供一種使用該表面修飾劑容易製造具有微結構之裝置之方法。
因本發明之表面修飾劑含有特殊有機聚矽氧化合物,故當使用該表面修飾劑,於基材例如各種光學構件(抗反射膜、濾光片、光學透鏡、眼鏡鏡片、分束器、稜鏡、鏡面等)上形成處理層時,可防止諸如指紋、皮脂、汗液、化妝品等污漬或水分黏著,而不會有損光學構件的光學性質;且污漬和水分一旦黏著時容易被擦拭去除,藉此獲得處理層之高度耐用性。
本發明之防污劑含有通式(A)及/或通式(B)所表示之有機聚矽氧化合物。
F-(CF2
)q
-(OC3
F6
)m
-(OC2
F4
)n
-(OCF2
)o
(CH2
)p
X(CH2
)r
Si(X'
)3-a
(R1
)a
(A)
F-(CF2
)q
-(OC3
F6
)m
-(OC2
F4
)n
-(OCF2
)o
(CH2
)p
X(CH2
)r
(X'
)2-a
(R1
)a
SiO(F-(CF2
)q
-(OC3
F6
)m
-(OC2
F4
)n
-(OCF2
)o
(CH2
)p
X(CH2
)r
(X'
)1-a
(R1
)a
SiO)z
F-(CF2
)q
-(OC3
F6
)m
-(OC2
F4
)n
-(OCF2
)o
(CH2
)p
X(CH2
)r
(X'
)2-a
(R1
)a
Si(B)
通式(A)中,q為1至3之整數;m、n及o分別為0至200之整數;p為1或2;X為O或二價有機基;r為2至20之整數;R1
為C1-22
直線或分支烴基;a為0至2之整數;及X’為可水解基團。
通式(B)中,q為1至3之整數;m、n及o分別為0至200之整數;p為1或2;X為O或二價有機基;r為2至20之整數;R1
為C1-22
直線或分支烴基;a為0至2之整數;X’為可水解基團;及當a為0或1時,z為0至10之整數。
於通式(A)及(B)中,X較佳為氧原子或二價有機基,諸如C1-22
線性或分支伸烷基;R1
為C1-22
烷基,更佳為C1-12
烷基;以及X’為氯、烷氧基(-OR)或-O-N=CH2
其中R為C1-22
線性或分支烴基,特別為線性或分支烷基。
通式(A)或(B)之可水解基團X’係以下式基團舉例說明:烷氧基或經烷氧基取代之烷氧基,例如甲氧基、乙氧基、丙氧基及甲氧基乙氧基;醯氧基例如乙醯氧基、丙醯氧基及苯甲醯氧基;烯氧基諸如異丙烯氧基和異丁烯氧基;亞胺氧基諸如二甲基酮肟、甲基乙基酮肟、二乙基酮肟、環己酮肟基;經取代之胺基諸如甲基胺基、乙基胺基、二甲基胺基及二乙基胺基;醯胺基如N-甲基乙醯
胺基及N-乙基醯胺基;經取代之胺基氧基諸如二甲基胺基氧基及二乙基胺基氧基;鹵素諸如氯等。此等可水解基團中,以-OCH3
、-OC2
H5
、及-O-N=(CH3
)2
為特佳。此等可水解基團可單獨或呈二者或更多者之組合而含於本發明之防污劑之有機聚矽氧化合物中。
通式(A)和(B)中,m、n及o之和較佳為5或5以上,及更佳為10或10以上。X較佳為氧,r較佳為3。通式(A)中,a為較佳為0。
通式(A)所表示之化合物中,通式(A)表示之特佳化合物其中X為氧、r為3、a為0及X’為-OCH3
,可經由在過渡金屬存在下使三氯矽烷與如下通式(C)表示之化合物間進行矽氫化反應,然後藉甲醇進行去氯化氫反應(dehydrachlorination)而合成。使用酸受體諸如甲氧化鈉或原甲酸三甲酯來促進去氯化氫反應為較佳者。
可用於矽氫化反應中的觸媒VIII族過渡金屬較佳為鉑或銠。最佳為鉑。較佳係呈氯鉑酸或呈與1,3-二乙烯基-1,1,3,3-四甲基二矽氧烷之鉑錯合物之形式來供應鉑,或呈參(三苯基膦基)Rh1
Cl來供應銠。
F-(CF2
)q
-(OC3
F6
)m
-(OC2
F4
)n
-(OCF2
)o
(CH2
)p
XCH2
CH=CH2
(C)
通式(C)中,q為1至3之整數;m、n及o分別為0至200之整數;p為1或2;X為氧或二價有機基。
具體地,特佳化合物可根據如下反應圖來
製造。
如上反應圖中,q為1至3之整數;m、n及o分別為0至200之整數;p為1或2;X為氧或二價有機基。於上述反應圖中,經由以HSi(OMe)或HSi(OEt)3
取代HSiCl3
,可製備其它較佳化合物,其具有無需進行去氯化氫反應作為第二步驟的額外優點。
矽氫化反應可經由以過量氫化矽於一段適當時間和適當的溫度下反應來進行以將驅使反應至完成。依照其選擇,可添加適當溶劑來促進混合。多種儀器方法諸如核磁共振或紅外光譜術可用來監視反應的進行。例如,較佳條件為:使每莫耳氟化合物與1.05至30莫耳三氯矽烷,於0.01至10毫莫耳鉑之存在下,於30至90℃反應1至10小時,該鉑係以與1,3-二乙烯基-1,1,3,3-四甲基二矽氧烷觸媒(亦即VIII族過渡金屬)形成鉑錯合物之形式提供。任何過量之氫化矽容易藉真空蒸餾而從反應產物中去除。
若三氯矽烷用於矽氫化反應時,則第二反應較佳係經由於每莫耳於第一反應所獲得之化合物中,將0.05至10莫耳濃度過量之原甲酸三甲酯與甲醇之混合物
於30至70℃下反應1至10小時而進行。多種儀器方法諸如核磁共振或紅外光譜術可用來監視反應的進行。任何過量之原甲酸三甲酯和甲醇容易藉真空蒸餾而從反應產物中去除。
由上式通式(C)所表示之氟化合物中,特佳
為通式(C)所表示之化合物,其中q為3,m為10至200,n為1,o為0,p為1,X為氧。
其它通式(A)所表示之化合物也可根據前述
反應圖以類似方式來合成。
通式(B)所表示之化合物可經由通式(A)表
示之化合物之部分水解與縮合反應而合成。
通式(A)及/或(B)所表示之有機聚矽氧化合
物可單獨使用或呈兩種或更多種之組合來使用以形成本發明之表面修飾劑。
若有所需可使用視需要之觸媒來促進通式
(A)及/或(B)所表示之有機聚矽氧化合物之表面修飾作用(surface modification)。該等觸媒其可單獨使用或呈二者或更多者之組合來使用以形成本發明之表面修飾劑。適當觸媒化合物之實例包括有機酸之金屬鹽例如二辛酸二丁基錫、硬脂酸鐵、辛酸鉛等;鈦酸酯類諸如鈦酸四異丙酯、鈦酸四丁酯;螯合物化合物諸如乙醯基丙酮酸鈦等。較佳以100份重量以通式(A)及/或(B)所表示之有機聚矽氧化合物為基準,視需要之觸媒用量係於0至5重量份,且更佳為0.01至2重量份之範圍。
通式(A)及/或(B)之有機聚矽氧化合物為表
面修飾劑之活性成分。表面修飾劑可由通式(A)及/或(B)之有機聚矽氧化合物組成。表面修飾劑包含通式(A)及/或(B)之有機聚矽氧化合物和液體介質例如有機溶劑。有機聚矽氧化合物於表面修飾劑之濃度以表面修飾劑為基準計較佳為0.01至80%重量份。
有機溶劑可為多種其偏好溶解有機聚矽氧
化合物之溶劑,但有機溶劑不會與本發明組成物中所含的成分(特別為有機聚矽氧化合物)起反應。有機溶劑之實例包括含氟溶劑例如含氟烷、含氟氯烷、含氟芳香族化合物、和含氟醚(例如氫氟醚(HFE))。
欲使用本發明之表面修飾劑處理來形成表
面處理層之基材並無特殊限制。基材之實例包括光學構件包含:無機基材諸如玻璃板、包含無機層之玻璃板、陶瓷等;及有機基材諸如透明塑膠基材和包含無機層之透明塑膠基材板;等。
無機基材之實例包含玻璃板。形成包含無
機層之玻璃板用之無機化合物實例包括金屬氧化物[矽氧化物(二氧化矽、一氧化矽等)、氧化鋁、氧化鎂、氧化鈦、氧化錫、氧化鋯、氧化鈉、氧化銻、氧化銦、氧化鉍、氧化釔、氧化鈰、氧化鋅、ITO(氧化銦錫)等];及金屬鹵化物(氟化鎂、氟化鈣、氟化鈉、氟化鑭、氟化鈰、氟化鋰、氟化釷等)。
包含此種無機化合物之無機層或無機基材
可為單層或多層。無機層係作為抗反射層,無機層可經由已知方法諸如濕塗覆、PVD(物理氣相沉積)、CVD(化學氣相沉積)等方法製成。濕塗覆法之實例包括浸塗、旋塗、流塗、噴塗、輥塗、凹版塗覆等方法。PVD方法之實例包括真空蒸鍍、反應性沉積、離子束輔助沉積、濺鍍、離子披覆(ion plating)等方法。
有用之有機基材中,透明塑膠基材之實例
包括包含多種有機聚合物之基材。由透明度、折射率、分散性等光學性質,以及由諸如防震性、耐熱性及耐用性等多種其它性質之觀點,用作為光學構件之基材通常包含聚烯烴類(聚乙烯、聚丙烯等)、聚酯類(聚乙烯對苯二甲酸酯、聚乙烯萘甲酸酯等)、聚醯胺類(尼龍6、尼龍66等)、聚苯乙烯、聚氯乙烯、聚醯亞胺類、聚乙烯醇、乙烯乙烯醇共聚物(ethylene vinyl alcohol)、丙烯酸系聚合物、纖維素類(三乙醯基纖維素、二乙醯基纖維素、賽珞芳(cellophane)等)、或此等有機聚合物之共聚物。值得一提是,此等基材可作為本發明中待受處理之透明塑膠基材之實例。
有用之材料之實例包括經由將諸如抗靜電
劑、紫外光吸收劑、增塑劑、潤滑劑、著色劑、抗氧化劑、阻燃劑等已知添加劑添加至此等有機基材之有機聚合物所製備之材料。
也可使用經由於有機基材上形成無機層所
製備之基材來作為本發明之基材。於此種情況下,無機層作為抗反射層,且可經由如前述方法而形成於有機基材上。
欲處理之無機基材或有機基材並無特殊限
制。用作為光學構件之透明塑膠基材通常係呈薄膜或薄片形式。呈薄膜或薄片形式之基材也可用作為本發明之基材。呈薄膜或薄片形式之基材可為單層或多種有機聚合物所形成之層合物。厚度並無特殊限制,但較佳為0.01毫米至5毫米。
硬質塗層可形成於透明塑膠基材與無機層
間。硬質塗層可改良基材表面之硬度,同時平坦化且光滑化基材表面,如此改良透明塑膠基材與無機層間之黏著性。因此,可防止因鉛筆等負荷所造成的刮痕。此外,硬質塗層可抑制因透明塑膠基材之彎曲而造成無機層的裂開,如此改良光學構件之機械強度。
硬質塗層之材料並無特殊限制,只要具有
透明度、適當硬度、和機械強度即可。例如熱固性樹脂和藉游離輻射或紫外光輻射固化之樹脂係為有用者。紫外光固化丙烯酸系樹脂、有機矽樹脂、和熱固性聚矽氧樹脂為特佳者。此種樹脂之折射率較佳係等於或接近於透明塑膠基材之折射率。
形成此種硬質塗層之塗覆方法並無特殊限
制。可使用任一種可達成均勻塗覆之方法。當硬質塗層具有3微米或以上之厚度時,可提供足夠強度。但就透明度、塗覆準確度、與容易加工等觀點,以5微米至7微米之範圍為佳。
此外,經由將具有平均粒徑為0.01微米至3
微米之無機粒子或有機粒子混合且分散於硬質塗層,可實施通稱為「防炫光」之光學漫射加工。雖然任一種透明粒子皆可用作為此種粒子,但以低折射率材料為佳。就安定性、耐熱性等方面而言,以矽氧化物和氟化鎂為特佳。經由於硬質塗層設置凹面,也可達成光學漫射加工。
如前述之基材可用作為本發明之抗反射光
學構件之透明基材。特別,包含抗反射層於表面上之此種基材可為包含抗反射層之透明基材。本發明之抗反射光學構件可經由於此種基材表面形成防污層而獲得。
除了此種光學構件外,本發明之表面修飾劑還可施用於汽車或飛機之窗構件,如此提供先進功能。為了進一步改良表面硬度,也可經由使用本發明之表面修飾劑與TEOS(四乙氧基矽烷)的組合,藉由所謂之溶膠-凝膠方法執行表面改質。
於奈米轉印加工程序中,經由使用本發明之表面修飾劑作為離型劑,容易達成精確的離型。當表面係使用本發明之表面修飾劑加工時,修飾劑幾乎擴散成單層之狀態,故結果所形成之層只具有數奈米厚度。儘管只有此種厚度,仍然可形成,如後文實例中所示之,具有水接觸角為110度或以上及水滴落角為5度或以下之表面。
本發明之表面修飾劑具有絕佳液體撥除性,如此可應用於微影術和裝置的形成。
此外,經由加工陶瓷材料表面,可製造容易維護的衛生器皿和外牆。
加工層之形成方法並無特殊限制。例如可使用濕塗覆法和乾塗覆法。
濕塗覆法之實例包括浸塗、旋塗、流塗、噴塗、輥塗、凹版塗覆等方法。
乾塗覆法之實例包括真空蒸鍍、濺鍍、CVD等方法。真空蒸鍍法之特例包括電阻加熱、電子束、高頻加熱、離子束等方法。CVD方法之實例包括電漿-CVD、光學-CVD、加熱CVD等方法。
此外,也可藉常壓電漿法塗覆。
當使用濕塗覆法時,有用的稀釋劑溶劑並無特殊限制。鑑於組成物之安定性和揮發性,以下列化合物為佳:含5至12個碳原子之全氟脂肪族烴類,諸如全氟己烷、全氟甲基環己烷、全氟-1,3-二甲基環己烷;全氟化芳香族烴類諸如貳(三氟甲基)苯;全氟化脂肪族烴類、全氟丁基甲基醚等HFE類等。此等溶劑可單獨使用或呈兩種或兩種以上之溶劑之混合物來使用。
濕塗覆法較佳係用於有複雜形狀及/或大面積的基材。
另一方面,考慮於形成防污層時之工作環境,以無需稀釋劑溶劑的乾塗覆法為佳。以真空蒸鍍法為特佳。
於藉濕塗覆法或乾塗覆法而於基材上形成防污層之後,若有所需,可施行加熱、濕化、照光、電子束照射等。
經由使用本發明之防污劑所形成之防污層之厚度並無特殊限制。就防污性、耐刮性、和光學構件之光學性能而言,以1奈米至10奈米之範圍為佳。
下列實例意圖用來舉例說明本發明之細節,但非限制本發明之範圍。
於裝配有磁攪棒、回流冷凝器、溫度控制器和乾氮頂上空間滌氣器之1升3頸燒瓶內,加入411.2克(F3
CCF2
CF2
(OCF2
CF2
CF2
)11
OCF2
CF2
CH2
OCH2
CH2
=CH2
),286.13克1,3-貳(三氟甲基)苯及110.47克三氯矽烷。將內容物加熱至60℃,隨後於3.7小時時間內加入0.045克以1,3-二乙烯基-1,1,3,3-四甲基二矽氧烷錯合之鉑金屬。該內容物又於60℃維持30分鐘來製造F3
CCF2
CF2
(OCF2
CF2
CF2
)11
OCF2
CF2
CH2
OCH2
CH2
CH2
SiCl3
。殘餘三氯矽烷和溶劑從反應混合物中真空汽提去除,隨後加入156.5克原甲酸三甲酯和1.8克甲醇。燒瓶內容物維持於60℃隔夜以促進氯矽烷的甲氧化反應。經14小時後,又加入額外5.2克甲醇,並維持於該溫度3小時。加入活性碳2.5克。於真空下去除過量試劑。產物係於5微米膜上通過西來特(Celite)過濾助劑床過濾。產物F3
CCF2
CF2
(OCF2
CF2
CF2)11
OCF2
CF2
CH2
OCH2
CH2
CH2
Si(OMe)3
係呈濾液分離。藉紅外光譜術和核磁共振光譜術分析,顯示CH2
=CHCH2
O和SiCl官能基的完全消失。
於裝配有磁攪棒、回流冷凝器、溫度控制
器和乾氮頂上空間滌氣器之25毫升2頸瓶內,加入7.52克(F3
CCF2
CF2
(OCF2
CF2
CF2
)11
OCF2
CF2
CH2
OCH2
CH2
=CH2
),12.02克1,3-貳(三氟甲基)苯和3.91克三甲氧基矽烷。將內容物加熱至100℃,隨後以16小時時間緩慢加入1.4E-3克以1,3-二乙烯基-1,1,3,3-四甲基二矽氧烷錯合之鉑金屬。又經2小時後,真空去除過量試劑。產物F3
CCF2
CF2
(OCF2
CF2
CF2
)11
OCF2
CF2
CH2
OCH2
CH2
CH2
Si(OMe)3
呈燒瓶殘餘物分離,混合活性碳及過濾。藉紅外光譜術和核磁共振光譜術分析,顯示未殘留任何初始CH2
=CHCH2
O官能基。
經由合成例1所述相同方法,合成下列化合物。
F3
CCF2
CF2
(OCF2
CF2
CF2
)21
OCF2
CF2
CH2
OCH2
CH2
CH2
Si(OMe)3
F3
CCF2
CF2
(OCF2
CF2
CF2
)30
OCF2
CF2
CH2
OCH2
CH2
CH2
Si(OMe)3
F3
CCF2
CF2
(OCF2
CF2
CF2
)21
OCF2
CF2
CONHCH2
CH2
CH2
Si(OMe)3
F3
CCF2
CF2
O[CF(CF3
)CF2
O]3
CF(CF3
)CH2
OCH2
CH2
CH2
Si(OMe)3
F3
CCF2
CF2
O[CF(CF3
)CF2
O]3
CF(CF3
)CONHCH2
CH2
CH2
Si(OMe)3
F3
CCF2
CF2
O[CF(CF3
)CF2
O]4
CF(CF3
)CH2
OCH2
CH2
CH2
Si(OMe)3
F3
CCF2
CF2
O[CF(CF3
)CF2
O]5
CF(CF3
)CH2
OCH2
CH2
CH2
Si(OMe)3
購買歐普圖(Optool)DSX(大金工業公司(Daikin Industries,Ltd.)製造),稱作為比較化合物a。
矽晶圓(2厘米×4厘米×0.7毫米)於丙酮中25℃下以超音波處理10分鐘,於硫酸/30重量%過氧化氫溶液=70/30(V/V)中於100℃下洗滌1小時。然後將晶圓以甲醇和乙醇依此種順序來洗滌,並於室溫下於減壓下乾燥。進一步,於70巴下進行紫外光/臭氧處理,藉此確認該晶圓之水接觸角為0度。
合成化合物和比較化合物各自以HFE-7200(3M公司製造)稀釋成濃度分別為0.05重量%、0.10重量%和0.50重量%。將如上前處理之矽晶圓浸泡於25℃之稀釋化合物中30分鐘,及於25℃乾燥24小時。然後晶圓於HFE-7200中於25℃下超音波清潔10分鐘,及於25℃於減壓下乾燥1小時。
經處理試樣之水接觸角和水傾斜角係使用型號CA-X(共和界面科學公司(Kyowa Interface Science
Co.,Ltd.))測定。測定係於20℃和65%相對濕度條件下,使用20微升蒸餾水數滴來進行。
將手指按壓於經處理的試樣表面上來讓指紋黏附,指紋的黏附性和顯著性係根據下述標準目測評估。
A:指紋只略為黏附,即使黏附也不容易發現。
B:指紋的黏附顯著。
黏附於試樣表面之指紋使用不織布纖維素織物(編卡(Bencot)M-3,旭化成公司(Asahi Chemical Co.,Ltd.)製造)擦拭,來根據下述標準目測評估指紋的去除性。
A:指紋可完全被擦拭去除。
B:擦拭後留下微量指紋。
C:指紋無法被擦拭去除。
試樣表面使用不織布纖維素織物(編卡M-3,旭化成公司製造)在500gf之負載下摩擦100次,並接受如上測試。
表1中,括弧內之數值為耐磨性試驗之數值。
表1顯示使用本發明之表面修飾劑所形成之經處理層具有類似於比較例之經處理之層之水接觸角,但具有遠較小的水傾斜角,如此其難以水來濕潤,因而容易擦拭去除指紋。該表也顯示此等絕佳性質為持久者。
以實例1之相同方式,測量合成化合物2至8之各項性質。其結果顯示於表2至5。
表2、表3、表4和表5顯示如同表1所述的相同結果。
使用本發明之表面修飾劑於基材表面上所
形成的處理層具有比使用目前已知處理劑所形成之處理層遠更小的傾斜角,如此更佳可對抗諸如指紋、皮脂、汗液和化妝品等污漬。進一步,即使此等污漬黏附於本發明之表面修飾劑之處理層,也容易被擦拭去除。此外,其穩定具有此等性質。
此外,經由黏合本發明之光學元件或抗反
射光學構件至光學功能構件如偏轉板(deflection plate)所得之光學功能元件具有有前述絕佳功能和高度耐用性的處理層形成於其表面上,因此當黏合至例如各種顯示器(液晶顯示器、CRT顯示器、投影顯示器、電漿顯示器、EL顯示器等)之顯示螢幕的前面板上時,可提供具有高度影像辨識性質本發明之顯示裝置。
此外,使用本發明之表面修飾劑於基材表
面上所形成之經處理之層為極薄,如此具有高度精確可加工處理能力和絕佳微切削性質。
Claims (35)
- 一種表面修飾劑,包含通式(A)及通式(B)所表示之有機聚矽氧化合物之一者或二者:F-(CF2 )q -(OCF2 CF2 CF2 )m -(OC2 F4 )n -(OCF2 )o (CH2 )p X(CH2 )r Si(X’)3-a (R1 )a (A)其中q為1至3之整數;m為10至200之整數,n及o分別為0至200之整數;p為1或2;X為O;r為3;R1 為C1-22 直線或分支烴基;a為0至2之整數;及X’為可水解基團;以及F-(CF2 )q -(OCF2 CF2 CF2 )m -(OC2 F4 )n -(OCF2 )o (CH2 )p X(CH2 )r Si(X’)2-a (R1 )a SiO(F-(CF2 )q -(OCF2 CF2 CF2 )m -(OC2 F4 )n -(OCF2 )o (CH2 )p X(CH2 )r Si(X’)1-a (R1 )a SiO)z F-(CF2 )q -(OCF2 CF2 CF2 )m -(OC2 F4 )n -(OCF2 )o (CH2 )p X(CH2 )r Si(X’)2-a (R1 )a Si(B)其中q為1至3之整數;m為10至200之整數,n及o分別為0至200之整數;p為1或2;X為O;r為3;R1 為C1-22 直線或分支烴基;a為0至2之整數;X’為可水解基團;及當a為0或1時,z為0至10之整數;其中該有機聚矽氧化合物(A)係使用通式(C)所示化合物的矽氫化反應而製備:F-(CF2 )q -(OCF2 CF2 CF2 )m -(OC2 F4 )n -(OCF2 )o (CH2 )p OCH2 CH=CH2 (C)其中q、m、n、o及p與上述相同定義。
- 如申請專利範圍第1項之表面修飾劑,其中於通式(A)及/或通式(B)中,q為3,m為10至200之整數,n為1,o為0,p為1,X為O,r為3及a為0或1。
- 如申請專利範圍第1項之表面修飾劑,以添加觸媒來促進表面改質。
- 如申請專利範圍第1項之表面修飾劑,以添加觸媒來促進表面改質,其中通式(A)及/或通式(B)所表示之化合物與觸媒之比例為0.001份至2份。
- 如申請專利範圍第1至4項中任一項之表面修飾劑,其中該可水解基團為烷氧基或經烷氧基取代之烷氧基、醯氧基、烯氧基、亞胺氧基、甲基胺基、乙基胺基、二甲基胺基、二乙基胺基、醯胺基、二甲基胺基氧基、二乙基胺基氧基或鹵素。
- 一種通式(A)所表示之有機聚矽氧化合物之製造方法,其中r為3,X’為氯或烷氧基,及a為0,該方法係使用於過渡金屬存在下,三氯矽烷或三烷氧基矽烷與如下通式(C)所表示之化合物間之矽氫化反應:F-(CF2 )q -(OCF2 CF2 CF2 )m -(OC2 F4 )n -(OCF2 )o (CH2 )p X(CH2 )r Si(X’)3-a (R1 )a (A)其中q為1至3之整數;m為10至200之整數,n及o分別為0至200之整數;p為1或2;X為O;r為3; R1 為C1-22 直線或分支烴基;a為0至2之整數;及X’為可水解基團;F-(CF2 )q -(OCF2 CF2 CF2 )m -(OC2 F4 )n -(OCF2 )o (CH2 )p XCH2 CH=CH2 (C)其中q為1至3之整數;m為10至200之整數,n及o分別為0至200之整數;p為1或2;及X為氧。
- 一種通式(A)所表示之有機聚矽氧化合物之製造方法,其中X’為-OR,其R為C1-22 線性或分支烴基,該方法係於過渡金屬存在下,使用三氯矽烷與通式(C)所表示之化合物間之矽氫化反應,而然後,使用C1-22 線性或分支脂肪族醇之烷氧化反應,藉此去除氯化氫,或使用金屬烷氧化物之烷氧化反應F-(CF2 )q -(OCF2 CF2 CF2 )m -(OC2 F4 )n -(OCF2 )o (CH2 )p X(CH2 )r Si(X’)3-a (R1 )a (A)其中q為1至3之整數;m為10至200之整數,n及o分別為0至200之整數;p為1或2;X為O;r為3;R1 為C1-22 直線或分支烴基;a為0至2之整數;及X’為可水解基團;F-(CF2 )q -(OCF2 CF2 CF2 )m -(OC2 F4 )n -(OCF2 )o (CH2 )p XCH2 CH=CH2 (C)其中q為1至3之整數;m為10至200之整數,n及o 分別為0至200之整數;p為1或2;及X為氧。
- 一種通式(A)所表示之有機聚矽氧化合物之製造方法,其中X’為-O-N=CR2 ,R為C1-22 線性或分支烴基,該方法係於過渡金屬存在下,使用三氯矽烷與通式(C)所表示之化合物間之矽氫化反應,而然後,與HO-N=CR2 ,R為C1-22 線性或分支烴基所表示之二烷基酮肟反應F-(CF2 )q -(OCF2 CF2 CF2 )m -(OC2 F4 )n -(OCF2 )o (CH2 )p X(CH2 )r Si(X’)3-a (R1 )a (A)其中q為1至3之整數;m為10至200之整數,n及o分別為0至200之整數;p為1或2;X為O;r為3;R1 為C1-22 直線或分支烴基;a為0至2之整數;及X’為可水解基團;F-(CF2 )q -(OCF2 CF2 CF2 )m -(OC2 F4 )n -(OCF2 )o (CH2 )p XCH2 CH=CH2 (C)其中q為1至3之整數;m為10至200之整數,n及o分別為0至200之整數;p為1或2;及X為氧。
- 如申請專利範圍第6至8項中任一項之有機聚矽氧化合物之製造方法,其中該過渡金屬為鉑或銠。
- 一種通式(B)所表示之有機聚矽氧化合物之製造方法,該方法係使用如申請專利範圍第6至9項中任一項之方法而獲得之通式(A)所表示之化合物進行部分水解與縮合反應, F-(CF2 )q -(OCF2 CF2 CF2 )m -(OC2 F4 )n -(OCF2 )o (CH2 )p X(CH2 )r Si(X’)3-a (R1 )a (A)其中q為1至3之整數;m為10至200之整數,n及o分別為0至200之整數;p為1或2;X為O;r為3;R1 為C1-22 直線或分支烴基;a為0至2之整數;及X’為可水解基團;以及F-(CF2 )q -(OCF2 CF2 CF2 )m -(OC2 F4 )n -(OCF2 )o (CH2 )p X(CH2 )r Si(X’)2-a (R1 )a SiO(F-(CF2 )q -(OCF2 CF2 CF2 )m -(OC2 F4 )n -(OCF2 )o (CH2 )p X(CH2 )r Si(X’)1-a (R1 )a SiO)z F-(CF2 )q -(OCF2 CF2 CF2 )m -(OC2 F4 )n -(OCF2 )o (CH2 )p X(CH2 )r Si(X’)2-a (R1 )a Si(B)其中q為1至3之整數;m為10至200之整數,n及o分別為0至200之整數;p為1或2;X為O;r為3;R1 為C1-22 直線或分支烴基;a為0至2之整數;X’為可水解基團;及當a為0或1時,z為0至10之整數。
- 一種經由使用如申請專利範圍第1至5項中任一項之表面修飾劑所得之經處理之表面,該經處理之表面具有水接觸角至少為110度,和水傾斜角不超過5度。
- 一種經由使用如申請專利範圍第1至5項中任一項之表面修飾劑所得之經處理之表面,該經處理之表面包含呈單分子薄膜形式之全氟聚 醚。
- 一種如申請專利範圍第11項之表面之製造方法,包含根據濕塗覆法,於基材上形成如申請專利範圍第1至5項中任一項之表面修飾劑薄膜之步驟。
- 一種如申請專利範圍第11項之表面之製造方法,包含根據乾塗覆法,於基材上形成如申請專利範圍第1至5項中任一項之表面修飾劑薄膜之步驟。
- 一種表面之形成方法,包含下列步驟:以如申請專利範圍第1至5項中任一項之表面修飾劑浸漬多孔物件,以及經由於真空加熱該表面修飾劑已經浸漬於其中的多孔物件,來蒸發去除該表面修飾劑,而於基材上形成經處理層。
- 如申請專利範圍第15項之表面之形成方法,其中該多孔物件包含選自於由SiO2 、TiO2 、ZrO2 、MgO、Al2 O3 、CaSO4 、Cu、Fe、Al、不鏽鋼及碳所組成之組群中之至少一者。
- 如申請專利範圍第15或16項之表面之形成方法,其中該浸漬於多孔物件之表面修飾劑係根據選自於電阻加熱、電子束加熱、離子束加熱、高頻加熱、及光加熱中之至少一種加熱方法而被蒸發。
- 一種如申請專利範圍第15項之表面之形成方法,包含於電漿存在下,經由噴嘴-噴霧如申請專利範圍第1至5項中任一項之表面修飾劑,而於基材上形成薄膜之步驟。
- 如申請專利範圍第18項之方法,其中該電漿為氬氣或氦氣之常壓電漿。
- 一種抗反射光學構件,包含透明基材、形成於該透明基材的至少一側上之一抗反射薄膜、以及形成於最外表面之經處理層,該經處理層包含如申請專利範圍第1至5項中任一項之表面修飾劑。
- 如申請專利範圍第20項之抗反射光學構件,其中該透明基材為有機基材,或無機基材。
- 一種光學功能構件,包含如申請專利範圍第20或21項之抗反射光學構件而該功能光學構件係貼附於該抗反射光學構件。
- 如申請專利範圍第22項之光學功能構件,其中該功能構件為偏光板。
- 一種顯示器裝置,包含以黏著劑黏附於顯示器螢幕表面之前面板之前側的塗覆構件,該塗覆構件為如申請專利範圍第22或23項之光學功能構件。
- 如申請專利範圍第24項之顯示器裝置,其中該顯示器為液晶顯示器、陰極射線管(CRT)顯示器、投影顯示器、電漿顯示器、或電致發光(EL)顯示器。
- 一種玻璃,具有使用如申請專利範圍第1至5項中任一項之表面修飾劑而獲得之表面。
- 如申請專利範圍第26項之玻璃,其係供汽車使用或航 太使用。
- 一種眼鏡鏡片,具有使用如申請專利範圍第1至5項中任一項之表面修飾劑而獲得之表面。
- 一種衛生器皿,具有使用如申請專利範圍第1至5項中任一項之表面修飾劑獲得之表面。
- 一種離型方法,係使用如申請專利範圍第1至5項中任一項之表面修飾劑作為離型劑。
- 一種離型方法,係使用如申請專利範圍第1至5項中任一項之表面修飾劑用於奈米轉印。
- 一種使用如申請專利範圍第1至5項中任一項之表面修飾劑之微結構之形成方法。
- 一種如申請專利範圍第1至5項中任一項之表面修飾劑之用途,係用於微影術或裝置製造之用途。
- 一種石器,具有使用如申請專利範圍第1至5項中任一項之表面修飾劑而獲得之表面。
- 一種光學鏡片,具有使用如申請專利範圍第1至5項中任一項之表面修飾劑而獲得之表面。