RU2613211C1 - Bituminous concrete mixture on basis of modified bitumen for highway coating - Google Patents
Bituminous concrete mixture on basis of modified bitumen for highway coating Download PDFInfo
- Publication number
- RU2613211C1 RU2613211C1 RU2015156094A RU2015156094A RU2613211C1 RU 2613211 C1 RU2613211 C1 RU 2613211C1 RU 2015156094 A RU2015156094 A RU 2015156094A RU 2015156094 A RU2015156094 A RU 2015156094A RU 2613211 C1 RU2613211 C1 RU 2613211C1
- Authority
- RU
- Russia
- Prior art keywords
- bitumen
- fly ash
- calcium fly
- highway
- asphalt
- Prior art date
Abstract
Description
Изобретение относится к дорожно-строительным материалам и может быть использовано для устройства покрытий автомобильных дорог.The invention relates to road-building materials and can be used for paving roads.
Известна асфальтобетонная смесь, предназначенная для устройства покрытий автомобильных дорог, включающая: битум (сверх 100% минеральной части) - 5,8-7,5, щебень из хвостов сухой магнитной сепарации - 60-80, отсев дробления из хвостов сухой магнитной сепарации - 8-32, минеральный порошок - 12-8, целлюлозное волокно (сверх 100% к минеральной части) - 0,3-0,5 [Патент на изобретение RU №2285679 C1, МПК С04В 26/26, опубл. 20.10.2006].Known asphalt mix intended for the device of coatings for roads, including: bitumen (over 100% of the mineral part) - 5.8-7.5, crushed stone from the tails of dry magnetic separation - 60-80, screening crushing from the tails of dry magnetic separation - 8 -32, mineral powder - 12-8, cellulose fiber (in excess of 100% of the mineral part) - 0.3-0.5 [Patent for the invention RU No. 2285679 C1, IPC SB04/26, publ. 10/20/2006].
В качестве недостатков данной асфальтобетонной смеси можно выделить ограниченную номенклатуру применяемого сырья, связанную с необходимостью использования в качестве заполнителей смеси щебня и отсева дробления в виде хвостов сухой магнитной сепарации железосодержащих руд, а также недостаточно высокие показатели физико-механических характеристик, таких как прочность при сжатии при 50 и 20°С, сдвигоустойчивость по сцеплению при сдвиге при температуре 50°С, водонасыщение и водостойкость при длительном водонасыщении.The disadvantages of this asphalt mix can be identified by the limited range of raw materials used, related to the need to use crushed stone and crushing screening as tails of dry magnetic separation of iron ores, as well as insufficiently high physical and mechanical characteristics, such as compressive strength at 50 and 20 ° C, shear resistance to adhesion during shear at a temperature of 50 ° C, water saturation and water resistance during prolonged water saturation.
Наиболее близкой к предлагаемому решению, принятой за прототип является асфальтобетонная смесь, включающая (мас. %): шлаковый щебень фракции 5-20 мм - 31, шлаковый песок фракции 0-5 мм - 61-65, в качестве наполнителя и структурирующего компонента шлам химводоочистки ТЭЦ - 4-8 (сверх 100% минеральной части), нефтяной вязкий битум - 6,0 (сверх минеральной части), в качестве гидрофобно-пластифицирующей и структурирующей добавки кремнийорганическую жидкость ГКЖ-11 - 0,04-0,17 (сверх 100% минеральной части) [Патент на изобретение RU №2277519 С2, МПК С04В 26/26, Е01С 7/18, опубл. 10.06.2006].Closest to the proposed solution adopted for the prototype is an asphalt mixture, including (wt.%): Slag crushed stone fraction 5-20 mm - 31, slag sand fraction 0-5 mm - 61-65, as a filler and a structuring component of chemical water treatment sludge TPP - 4-8 (over 100% of the mineral part), viscous petroleum bitumen - 6.0 (over the mineral part), GKZh-11 organosilicon liquid - 0.04-0.17 (over 100) as a hydrophobic-plasticizing and structuring additive % of the mineral part) [Patent for invention RU No. 2277519 C2, IPC С04В 26/26, ЕСС 7/18, publ. 06/10/2006].
Недостатками данной смеси являются высокие значения набухания и водонасыщения, а также низкие значения водостойкости и водостойкости при длительном водонасыщении.The disadvantages of this mixture are high values of swelling and water saturation, as well as low values of water resistance and water resistance during prolonged water saturation.
Задачей, на решение которой направлено данное изобретение, является повышение качества дорожного покрытия за счет улучшения физико-механических характеристик асфальтобетонной смеси на основе модифицированного битума, а именно: снижение набухания и водонасыщения, повышение водостойкости и водостойкости при длительном водонасыщении.The objective of the invention is to improve the quality of the road surface by improving the physicomechanical characteristics of the asphalt mix based on modified bitumen, namely: reducing swelling and water saturation, increasing water resistance and water resistance during prolonged water saturation.
Это достигается тем, что асфальтобетонная смесь для устройства покрытий автомобильных дорог включает в качестве связующего модифицированное битумное вяжущее, состоящее из битума БЕД 60/90 и высококальциевой золы-уноса, в качестве заполнителя - гранитный щебень и отсев дробления, а в качестве наполнителя - известняковый минеральный порошок при следующем соотношении компонентов, мас. %:This is achieved by the fact that the asphalt mixture for the device of road coatings includes a modified bitumen binder consisting of BED 60/90 bitumen and high-calcium fly ash as a binder, granite crushed stone and crushing screening as a filler, and limestone mineral as a filler powder in the following ratio of components, wt. %:
- гранитный щебень фракции 5-20 мм - 38,7;- granite crushed stone fraction 5-20 mm - 38.7;
- отсев дробления гранитов - 46,6;- screening crushing granites - 46.6;
- известняковый минеральный порошок - 8,5;- limestone mineral powder - 8.5;
- битум марки БНД 60/90 - 5,04;- Bitumen grade BND 60/90 - 5.04;
- высококальциевая зола-уноса - 0,56.- high calcium fly ash - 0.56.
Предложенный состав смеси позволяет достигнуть заявленного результата за счет того, что вводимая в разогретый битум добавка высококальциевой золы-уноса оказывает структурирующее воздействие, повышая его вязкость, что приводит к повышению физико-механических характеристик при сниженном расходе битума в составе асфальтобетонной смеси для устройства покрытий автомобильных дорог.The proposed composition of the mixture allows us to achieve the stated result due to the fact that the addition of high-calcium fly ash introduced into the heated bitumen has a structural effect, increasing its viscosity, which leads to an increase in physical and mechanical characteristics with a reduced consumption of bitumen in the composition of the asphalt mix for the construction of road coatings .
Роль высококальциевой золы-уноса заключается в интенсификации процессов хемосорбции в результате взаимодействия битумной пленки с поверхностью алюмосиликатного модификатора (высококальциевой золы-уноса) за счет особенностей его состава и физической адсорбции за счет структуры, что приводит к повышению физико-механических и реологических характеристик битумного вяжущего, используемого для приготовления асфальтобетонной смеси. Данное обстоятельство способствует увеличению физико-механических характеристик асфальтобетонного покрытия, а также повышению его деформативной устойчивости.The role of high-calcium fly ash is to intensify the chemisorption processes as a result of the interaction of the bitumen film with the surface of the aluminosilicate modifier (high-calcium fly ash) due to the peculiarities of its composition and physical adsorption due to the structure, which leads to an increase in the physicomechanical and rheological characteristics of the bitumen binder, used for the preparation of asphalt mix. This circumstance contributes to an increase in the physicomechanical characteristics of the asphalt concrete pavement, as well as an increase in its deformation stability.
Увеличение физико-механических характеристик асфальтобетона на основе заявленного состава асфальтобетонной смеси возможно за счет малых размеров, большой удельной поверхности и особенностей строения частиц добавки в виде высококальциевой золы-уноса, позволяющей оптимизировать структуру асфальтобетона, создавая более плотную структуру асфальтобетона без пор и пустот.An increase in the physical and mechanical characteristics of asphalt concrete based on the claimed composition of the asphalt concrete mixture is possible due to the small size, large specific surface area and structural features of the additive particles in the form of high-calcium fly ash, which allows optimizing the structure of asphalt concrete, creating a denser structure of asphalt concrete without pores and voids.
Пример приготовления асфальтобетонной смесиAn example of the preparation of asphalt mix
Характеристика компонентов:Component Feature:
Основными исходными материалами для получения асфальтобетонной смеси являлись: битум марки БНД 60/90 Московского нефтеперерабатывающего завода, модифицированный высококальциевой золой-уноса Назаровской ТЭС (табл. 1, 2); гранитный щебень (ОАО «Павловскгранит»); отсев дробления гранитов (ОАО «Павловскгранит»); известняковый минеральный порошок (ООО «Стромис»).The main starting materials for producing the asphalt mixture were: bitumen grade BND 60/90 of the Moscow oil refinery, modified with high-calcium fly ash of Nazarovskaya TPP (Tables 1, 2); crushed granite (Pavlovskgranit OJSC); screening of granite crushing (Pavlovskgranit OJSC); limestone mineral powder (Stromis LLC).
Для получения модифицированного битумного вяжущего основными исходными материалами являлись высококальциевая зола-уноса (табл. 1 и 2) и битум марки БНД 60/90.To obtain a modified bitumen binder, the main starting materials were high-calcium fly ash (Tables 1 and 2) and bitumen grade BND 60/90.
Асфальтобетонную смесь в лабораторных условиях получали следующим образом. Дозировали битум в количестве 0,5 кг, разогревали до температуры 160°С, дозировали 0,03 кг высококальциевой золы-уноса, затем добавляли в емкость к битуму и смешивали с помощью лопастной мешалки в течение 5 минут. Дозированные крупный и мелкий заполнитель (гранитный щебень - 4,27 кг и отсев дробления гранитов - 4,9 кг) загружали в асфальтобетоносмесительную установку и разогревали до постоянной температуры 120°С, затем вводили известняковый минеральный порошок (0,9 кг) и подготовленный модифицированный битум и перемешивали до получения однородной смеси в течение 10 минут.Asphalt mix in laboratory conditions was obtained as follows. Bitumen was dosed in an amount of 0.5 kg, heated to a temperature of 160 ° C, dosed 0.03 kg of high-calcium fly ash, then added to the bitumen tank and mixed with a paddle mixer for 5 minutes. Dosed coarse and fine aggregate (granite crushed stone - 4.27 kg and screening crushing granites - 4.9 kg) were loaded into an asphalt mixing plant and heated to a constant temperature of 120 ° C, then limestone mineral powder (0.9 kg) was introduced and the prepared modified bitumen and mixed until a homogeneous mixture for 10 minutes.
Подбор рационального состава асфальтобетонной смеси для устройства покрытий автомобильных дорог производился по результатам испытаний пробных составов асфальтобетонных смесей с использованием различного количества модифицированного битума, так было определено оптимальное количество связующего в составе асфальтобетонной смеси, которое обеспечивает ей максимальные физико-механические характеристики. Подбор состава минеральной части производился с помощью программного обеспечения. Испытания образцов асфальтобетона из полученной асфальтобетонной смеси проводили по стандартным методикам в соответствии с требованиями нормативных документов.The rational composition of the asphalt mix for the installation of road coatings was selected according to the results of testing trial compositions of asphalt mixes using various amounts of modified bitumen, so the optimum amount of binder in the composition of the asphalt mix was determined, which provides it with maximum physical and mechanical characteristics. The selection of the composition of the mineral part was carried out using software. Tests of samples of asphalt concrete from the obtained asphalt concrete mixture were carried out according to standard methods in accordance with the requirements of regulatory documents.
Примеры реализации составов предложенной асфальтобетонной смеси и ее основные характеристики представлены в таблице 3.Examples of the implementation of the compositions of the proposed asphalt mix and its main characteristics are presented in table 3.
Таким образом, в результате анализа полученных результатов установлено существенное влияние модифицированного битумного вяжущего на свойства асфальтобетона на его основе, так асфальтобетон на основе битума, модифицированного высококальциевой золой-уноса, характеризуется сниженными показателями набухания и водонасыщения, повышенными показателями водостойкости и водостойкости при длительном водонасыщении.Thus, as a result of the analysis of the obtained results, a significant effect of the modified bitumen binder on the properties of asphalt concrete based on it was found, asphalt concrete based on bitumen modified with high-calcium fly ash is characterized by reduced swelling and water saturation, increased water resistance and water resistance during prolonged water saturation.
Введение малого количества добавки в вяжущее способствует снижению физико-механических характеристик асфальтобетона. Так, при введении высококальциевой золы-уноса в битум в количестве 5% от массы вяжущего (состав №1) асфальтобетон на его основе имеет гораздо более низкие физико-механические характеристики в сравнении с составом без использования добавки высококальциевой золы-уноса. При низком содержании добавки высококальциевой золы-уноса в битуме не происходит должного структурирующего эффекта, который позволил бы значительно повысить физико-механические характеристики асфальтобетона на его основе.The introduction of a small amount of additives in the binder helps to reduce the physical and mechanical properties of asphalt concrete. So, when high-calcium fly ash is introduced into bitumen in an amount of 5% by weight of the binder (composition No. 1), asphalt concrete based on it has much lower physical and mechanical characteristics compared to the composition without the use of high-calcium fly ash. With a low content of additives of high-calcium fly ash in bitumen, there is no proper structuring effect, which would significantly increase the physicomechanical characteristics of asphalt concrete based on it.
Введение добавки высококальциевой золы-уноса в битум в количестве 20% от массы вяжущего (состав №4) приводит к значительному загущению системы вяжущего, что в свою очередь препятствует равномерному его распределению на минеральной части (щебень, песок, минеральный порошок) асфальтобетонной смеси, вследствие чего снижаются физико-механические характеристики асфальтобетона.The introduction of the additive of high calcium fly ash into bitumen in an amount of 20% by weight of the binder (composition No. 4) leads to a significant thickening of the binder system, which in turn prevents its uniform distribution on the mineral part (crushed stone, sand, mineral powder) of the asphalt mix, due to which decreases the physical and mechanical characteristics of asphalt concrete.
Анализ физико-механических характеристик образцов асфальтобетона из асфальтобетонной смеси на основе битума, модифицированного высококальциевой золой-уноса, свидетельствует о влиянии добавки, приводящей к оптимизации структуры вяжущего и асфальтобетона в целом, что способствует формированию более плотной структуры асфальтобетона.An analysis of the physicomechanical characteristics of samples of asphalt concrete from an asphalt mix based on bitumen modified with high-calcium fly ash indicates the influence of an additive leading to optimization of the structure of cement and asphalt as a whole, which contributes to the formation of a denser structure of asphalt concrete.
Таким образом, представленное техническое решение в виде состава асфальтобетонной смеси на основе модифицированного битума для устройства покрытий автомобильных дорог с использованием в качестве модифицирующей добавки высококальциевой золы-уноса позволяет получить асфальтобетонную смесь со сдвигоустойчивостью при сдвиге при температуре 50°С 0,86; водостойкостью 0,98; водонасыщением 0,95%; набуханием 0,002 и водостойкостью при длительном водонасыщении 1,01.Thus, the presented technical solution in the form of the composition of asphalt mix based on modified bitumen for the device of road coatings using high calcium fly ash as a modifying additive allows to obtain an asphalt mix with shear stability at a temperature of 50 ° C of 0.86; water resistance of 0.98; water saturation 0.95%; swelling of 0.002 and water resistance with prolonged water saturation of 1.01.
Применение битумного вяжущего, модифицированного высококальциевой золой-уноса, в составе асфальтобетонной смеси способствует снижению стоимости асфальтобетонного покрытия за счет снижения расхода битума при прочих равных условиях.The use of bitumen binder, modified with high-calcium fly ash, in the composition of the asphalt mixture helps to reduce the cost of asphalt coating by reducing the consumption of bitumen, ceteris paribus.
Получаемая асфальтобетонная смесь для устройства покрытий автомобильных дорог характеризуется высокими физико-механическими характеристиками при сниженном содержании битума в составе смеси.The resulting asphalt mixture for the coating of roads is characterized by high physical and mechanical characteristics with a reduced content of bitumen in the mixture.
Claims (2)