RU2191788C2 - Multicomponent stone hard putty and method of its preparation - Google Patents
Multicomponent stone hard putty and method of its preparation Download PDFInfo
- Publication number
- RU2191788C2 RU2191788C2 RU2000110127/04A RU2000110127A RU2191788C2 RU 2191788 C2 RU2191788 C2 RU 2191788C2 RU 2000110127/04 A RU2000110127/04 A RU 2000110127/04A RU 2000110127 A RU2000110127 A RU 2000110127A RU 2191788 C2 RU2191788 C2 RU 2191788C2
- Authority
- RU
- Russia
- Prior art keywords
- component
- stone
- stone putty
- multicomponent
- putty according
- Prior art date
Abstract
Description
Изобретение относится к многокомпонентной каменной шпатлевке на основе ненасыщенных полиэфирных смол или акриловых смол, предназначенной преимущественно для машинной обработки, содержащей три компонента I, II, III, пигменты, наполнители и структурирующие вещества. The invention relates to a multicomponent stone putty based on unsaturated polyester resins or acrylic resins, intended primarily for machine processing, containing three components I, II, III, pigments, fillers and structuring agents.
Подобная каменная шпатлевка известна, например, под названием структурная шпатлевка, из полезной модели DE 29508712 U1. Такая структурная шпатлевка основана, главным образом, на затвердевающих на холоду двухкомпонентных полиэфирных смолах или на затвердевающих на холоду двухкомпонентных эпоксидных смолах. Такая многокомпонентная каменная шпатлевка может найти применение не только в качестве шпатлевочной массы, но и в качестве материала для заделки швов и соответственно для исправления или заполнения неровностей в искусственных и естественных камнях, причем заполненные швы и другие неровности должны быть, конечно, после затвердевания шпатлевочной массы отшлифованы и отполированы для придания сходства с материалом камня. A similar stone putty is known, for example, under the name of structural putty, from the utility model DE 29508712 U1. This structural putty is mainly based on cold-hardening two-component polyester resins or on cold-hardening two-component epoxy resins. Such a multicomponent stone putty can be used not only as a filler mass, but also as a material for filling joints and, accordingly, for correcting or filling irregularities in artificial and natural stones, and filled joints and other irregularities should, of course, after the putty mass has hardened. polished and polished to give a resemblance to the material of the stone.
Недостатком известной из уровня техники многокомпонентной каменной шпатлевки является неудовлетворительная обрабатываемость, поскольку уже по истечении определенного срока хранения в ней образуется осадок, который почти не поддается гомогенизации. A disadvantage of the multicomponent stone putty known from the prior art is its poor machinability, since after a certain storage period has elapsed, a precipitate forms in it, which almost cannot be homogenized.
Другими недостатками являются невысокая стабильность в процессе хранения, умеренная стабильность смеси компонентов и более медленное полное отверждение, несмотря на более короткий срок, отпущенный на использование смеси. Other disadvantages are low stability during storage, moderate stability of the mixture of components and slower complete cure, despite the shorter time allowed for the use of the mixture.
В соответствии с изложенным задача настоящего изобретения заключается в предоставлении такой многокомпонентной каменной шпатлевки, которая более легко перерабатывается, которая лишена хотя бы части недостатков известного из уровня техники состава и экономична в производстве и которая по возможности обеспечивает неизменное качество в процессе применения и обработки. In accordance with the foregoing, the objective of the present invention is to provide such a multi-component stone putty, which is more easily processed, which is devoid of at least some of the disadvantages of the prior art composition and is economical in production and which, if possible, ensures consistent quality during application and processing.
Поставленная задача решается с помощью представленной выше системной шпатлевки на основе ненасыщенных полиэфирных смол или акриловых смол, преимущественно для машинной обработки, содержащей три компонента I, II и III, пигменты, наполнители и структурирующие вещества, причем компонент I образован каменной шпатлевкой, содержащей ускоритель, выбранный из группы, состоящей из третичных ароматических аминов, металлов или металлорганических соединений, компонент II образован каменной шпатлевкой без ускорителя, содержащей по меньшей мере один стабилизатор, выбранный из группы, состоящей из фенолов и хинонов, и компонент III содержит по меньшей мере один органический пероксид. The problem is solved with the help of the above systemic putty based on unsaturated polyester resins or acrylic resins, mainly for machine processing, containing three components I, II and III, pigments, fillers and structuring substances, and component I is formed by a stone putty containing an accelerator selected from the group consisting of tertiary aromatic amines, metals or organometallic compounds, component II is formed by a stone putty without an accelerator containing at least one a tabulator selected from the group consisting of phenols and quinones, and component III contains at least one organic peroxide.
При этом также предпочтительно, чтобы в состав компонента I и/или компонента II входила еще по меньшей мере одна реологическая добавка и/или по меньшей мере одна присадка, ускоряющая сушку. Особенно предпочтительно, когда компонент III получен из не менее чем одного стабилизированного в пластификаторе органического пероксида, в частности дибензоилпероксида. It is also preferable that the composition of component I and / or component II included at least one rheological additive and / or at least one additive that accelerates drying. Particularly preferably, when component III is obtained from at least one stabilized organic peroxide in a plasticizer, in particular dibenzoyl peroxide.
Особое преимущество многокомпонентной каменной шпатлевки согласно изобретению заключается в том, что становится возможной более качественная машинная обработка, при этом дополнительным преимуществом является обеспечение постоянного и правильного соотношения компонентов в смеси и улучшение смеси. В результате этого отвержденная каменная шпатлевка прекрасно шлифуется и полируется, что почти недостижимо при ручной обработке. Еще одно преимущество состоит в очень хорошем заполнении как мелких, так и больших отверстий в ходе автоматического шпатлевания, что обеспечивает стабильность качества, не зависящую от квалификации и производительности проводящего эту операцию лица. A particular advantage of the multi-component stone putty according to the invention is that better machining is possible, with the additional advantage of ensuring a constant and correct ratio of components in the mixture and improving the mixture. As a result of this, the cured stone putty is perfectly ground and polished, which is almost unattainable with manual processing. Another advantage is the very good filling of both small and large holes during automatic putty, which ensures quality stability that does not depend on the qualifications and performance of the person performing this operation.
Многокомпонентная каменная шпатлевка согласно изобретению в отличие от известных из уровня техники продуктов имеет также значительно более стабильную консистенцию, это значит, что она в значительно меньшей степени подвержена расслоению и осаждению осадка. Не поддающийся диспергированию осадок, если уж он и выпадает, образуется только при крайне длительных сроках хранения. Другие преимущества представлены улучшенной стабильностью при хранении, а также более высокой устойчивостью смеси компонентов. The multicomponent stone putty according to the invention, in contrast to the products known from the prior art, also has a significantly more stable consistency, which means that it is much less prone to delamination and sedimentation. The precipitate that is not amenable to dispersion, even if it precipitates, is formed only with extremely long storage periods. Other advantages are represented by improved storage stability as well as higher stability of the component mixture.
При переработке многокомпонентной каменной шпатлевки согласно изобретению сначала смешивают соответствующее количество компонента III, содержащего органический пероксид, с компонентом II. Благодаря содержанию в компоненте II по меньшей мере одного стабилизатора полученная смесь сохраняет способность к переработке в течение не менее трех дней. Компоненты I и смесь компонентов II и III предпочтительно смешивают и перерабатывают в основном в количественном соотношении 1:1. При машинной обработке компонент I и смесь компонентов II и III загружают в соответствующие расходные емкости и по трубопроводам под давлением подают к месту использования, где их после выхода из трубопроводов смешивают и подают на шпатлевочную операцию. When processing a multi-component stone putty according to the invention, an appropriate amount of component III containing organic peroxide is first mixed with component II. Due to the content of at least one stabilizer in component II, the resulting mixture retains the ability to process for at least three days. Components I and a mixture of components II and III are preferably mixed and processed mainly in a quantitative ratio of 1: 1. In machine processing, component I and a mixture of components II and III are loaded into appropriate consumables and piped under pressure to the place of use, where they are mixed after they exit the pipelines and fed to a putty operation.
Благодаря такому оформлению процесса достигается значительно более равномерное распределение и перемешивание компонентов, чем это возможно при традиционных каменных шпатлевках. Обычное для уровня техники соотношение компонентов смеси от 100:1 до 100:4 для каменной шпатлевки и инициатора крайне трудно реализуемо. При ручной переработке чаще всего ошибаются при отмеривании соответствующего достаточного количества инициатора и, кроме того, почти недостижимо гомогенное распределение инициатора в составе каменной шпатлевки. Эти недостатки преодолеваются за счет многокомпонентной каменной шпатлевки согласно изобретению, причем, кроме того, обеспечивается и более продолжительное время на переработку, чем в случае использования известных каменных шпатлевок. Неожиданно оказалось, что несмотря на это, достигается более быстрое полное отверждение шпатлевки, и зашпатлеванная поверхность камня может в более короткие сроки поступать на окончательную обработку, т.е. на такие отделочные операции, как шлифование и полировка. Thanks to this process design, a much more uniform distribution and mixing of components is achieved than is possible with traditional stone putties. The ratio of the components of the mixture, usual for the prior art, from 100: 1 to 100: 4 for stone putty and initiator is extremely difficult to implement. In manual processing, they are most often mistaken when measuring the corresponding sufficient amount of initiator and, in addition, a homogeneous distribution of the initiator in the stone putty is almost unattainable. These disadvantages are overcome due to the multicomponent stone putty according to the invention, and, moreover, a longer processing time is provided than in the case of using the known stone putties. Unexpectedly, it turned out that despite this, a faster complete curing of the putty is achieved, and the putty surface of the stone can be supplied to the final processing in a shorter time, i.e. for finishing operations such as grinding and polishing.
В первую очередь следует обратить внимание на специальный жидкий органический пероксид в качестве компонента III, который после смешения компонентов приводит к образованию мягкой тиксотропной структуры смеси. Результатом этого становится прекрасная консистенция шпатлевочной массы, благодаря которой предотвращается или по крайней мере значительно уменьшается проседание неотвержденной шпатлевки даже в более крупных отверстиях. First of all, attention should be paid to a special liquid organic peroxide as component III, which, after mixing the components, leads to the formation of a soft thixotropic structure of the mixture. The result is an excellent consistency of the putty mass, which prevents or at least significantly reduces the sagging of uncured putty even in larger holes.
В предпочтительном составе многокомпонентной каменной шпатлевки компонент I содержит: от 20 до 60 мас.% связующего средства, от 0 до 5 мас.% ускорителя, от 0,5 до 10 мас.% реологической добавки, от 0 до 5 мас.% неорганических и органических пигментов, от 0 до 70 мас.% неорганических наполнителей, от 0 до 30 мас.% структурирующих веществ и от 0,1 до 0,5 мас.% присадки, ускоряющей сушку. In the preferred composition of the multi-component stone putty, component I contains: from 20 to 60 wt.% A binder, from 0 to 5 wt.% Accelerator, from 0.5 to 10 wt.% Rheological additives, from 0 to 5 wt.% Inorganic and organic pigments, from 0 to 70 wt.% inorganic fillers, from 0 to 30 wt.% structuring substances and from 0.1 to 0.5 wt.% additives that accelerate drying.
При этом компонент II содержит: от 20 до 60 мас.% связующего средства, от 0 до 5 мас.% стабилизатора, от 0,5 до 10 мас.% реологической добавки, от 0 до 5 мас.% неорганических и органических пигментов, от 0 до 70 мас.% неорганических наполнителей, от 0 до 30 мас.% структурирующих веществ и от 0,1 до 0,5 мас.% присадки, ускоряющей сушку. In this case, component II contains: from 20 to 60 wt.% A binder, from 0 to 5 wt.% Stabilizer, from 0.5 to 10 wt.% Rheological additives, from 0 to 5 wt.% Inorganic and organic pigments, from 0 to 70 wt.% Inorganic fillers, from 0 to 30 wt.% Structuring substances and from 0.1 to 0.5 wt.% Additives that accelerate drying.
Компонент III состоит предпочтительно из 50 мас.% дибензоилпероксида, стабилизированного в пластификаторе. Component III preferably consists of 50% by weight of dibenzoyl peroxide stabilized in a plasticizer.
В качестве связующего средства в многокомпонентной каменной шпатлевке согласно изобретению используют ненасыщенные полиэфирные смолы или акриловые смолы, растворенные в мономере, например в стироле, α-метилстироле, гександиолдиметакрилате, метилметакрилате. В составе компонента I использованные ненасыщенные полиэфирные смолы или акриловые смолы содержат ускоритель, например N, N-диметил-п-толуидин, N,N-ди-2-гидроксиэтил-п-толуидин, диметиланилин или металл, например кобальт, или же металлорганические соединения, например октоаты кобальта. В компоненте II в качестве стабилизаторов содержатся фенолы или хиноны, причем в качестве примера можно привести такие соединения, как гидрохинон, трет-бутилпирокатехин, п-бензохинон, нафтохинон и хлоранил. Unsaturated polyester resins or acrylic resins dissolved in the monomer, for example styrene, α-methyl styrene, hexanediol dimethacrylate, methyl methacrylate, are used as a binder in the multi-component stone putty according to the invention. In component I, the unsaturated polyester resins or acrylic resins used contain an accelerator, for example N, N-dimethyl-p-toluidine, N, N-di-2-hydroxyethyl-p-toluidine, dimethylaniline or a metal, such as cobalt, or organometallic compounds , for example, cobalt octoates. In component II, phenols or quinones are contained as stabilizers, and compounds such as hydroquinone, tert-butyl pyrocatechol, p-benzoquinone, naphthoquinone and chloranil can be given as examples.
В качестве реологических добавок в многокомпонентной каменной шпатлевке находят применение предпочтительно немодифицированные или модифицированные органическими группами, такими как, например, алкильные группы, осажденные или высокодисперсные кремневые кислоты, отвержденные или неотвержденные производные касторового масла, немодифицированные или модифицированные органическими группами слоистые силикаты и полиамиды. В качестве присадок, ускоряющих сушку, используют предпочтительно парафины или производные парафинов, полученные синтетическим путем. Preferably, unmodified or modified organic groups, such as, for example, alkyl groups, precipitated or highly dispersed silicic acids, cured or uncured derivatives of castor oil, unmodified or modified organic groups, layered silicates and polyamides, are used as rheological additives in multicomponent stone putty. As additives that accelerate the drying, preferably used paraffins or derivatives of paraffins, obtained synthetically.
В качестве наполнителей специалист может использовать целый ряд широко известных и используемых в этой области наполнителей, но предпочтение при этом отдают в первую очередь тальку, тяжелому шпату, кальциту, доломиту, кварцевой муке, оксиду или гидроксиду алюминия и каолину. Подходящий размер зерен этих наполнителей лежит в пределах от 0,1 до 150 мкм. As fillers, a specialist can use a number of widely known and used fillers in this field, but preference is given primarily to talc, heavy spar, calcite, dolomite, silica flour, aluminum oxide or hydroxide and kaolin. A suitable grain size of these fillers is in the range from 0.1 to 150 microns.
В качестве так называемых структурирующих веществ, с помощью которых становится возможной улучшенная подгонка к большому разнообразию природных камней, следует в первую очередь упомянуть слюду, пигменты с перламутровым блеском, пигменты с металлизирующим эффектом, а также грубые сорта талька. As the so-called structuring substances, with the help of which an improved fit to a wide variety of natural stones becomes possible, it is worth mentioning first of all mica, pigments with a pearlescent shine, pigments with a metallizing effect, as well as coarse varieties of talc.
Традиционно используемые пигменты также в общих чертах известны работающему в данной области специалисту, и они могут быть выбраны из большого числа натуральных и искусственных пигментов как органической, так и неорганической природы. В первую очередь здесь следует назвать, например, оксиды титана, железа, хрома, кобальта, а также сажи в качестве примеров неорганических пигментов, и фталоцианины, а также азокрасители в качестве примеров органических пигментов. Предпочтительно используют эти вещества. The traditionally used pigments are also generally known to those skilled in the art and can be selected from a large number of natural and artificial pigments of both organic and inorganic nature. First of all, it should be mentioned, for example, oxides of titanium, iron, chromium, cobalt, and soot as examples of inorganic pigments, and phthalocyanines, as well as azo dyes as examples of organic pigments. These substances are preferably used.
Настоящее изобретение более подробно иллюстрируется следующими далее примерами. The present invention is illustrated in more detail by the following examples.
Пример
Компонент I
Смешивают 350 г растворенной в стироле ненасыщенной полиэфирной смолы, 7 г аминного ускорителя, 9 г реологической добавки, 0,7 г диоксида титана, 0,7 г пигментного оксида железа и 1,5 г ускоряющей сушку присадки и диспергируют смесь в высокопроизводительном перемешивающем устройстве.Example
Component i
350 g of a unsaturated polyester resin dissolved in styrene, 7 g of an amine accelerator, 9 g of a rheological additive, 0.7 g of titanium dioxide, 0.7 g of pigmented iron oxide and 1.5 g of an accelerating drying additive are mixed, and the mixture is dispersed in a high-performance mixing device.
Компонент II
Смешивают 350 г растворенной в стироле ненасыщенной полиэфирной смолы, 1 г стабилизатора, 9 г реологической добавки, 0,7 г оксида титана, 0,7 г пигментного оксида железа и 1,5 г ускоряющей сушку присадки и диспергируют смесь в высокопроизводительном перемешивающем устройстве.Component II
350 g of a unsaturated polyester resin dissolved in styrene, 1 g of a stabilizer, 9 g of a rheological additive, 0.7 g of titanium oxide, 0.7 g of pigmented iron oxide and 1.5 g of an accelerating drying additive are mixed, and the mixture is dispersed in a high-performance mixing device.
Компонент III
В качестве третьего компонента служит смесь, содержащая 50 мас.% дибензоилпероксида в пластификаторе, причем дибензоилпероксид смешан с пластификатором для повышения стабильности.Component III
The third component is a mixture containing 50 wt.% Dibenzoyl peroxide in a plasticizer, and dibenzoyl peroxide is mixed with a plasticizer to increase stability.
Переработка
К компоненту II прибавляют 6 мас.% компонента III и обе составляющих тщательно перемешивают друг с другом. Эта смесь стабильна и пригодна для обработки в течение не менее трех дней.Processing
6 wt.% Of component III are added to component II and both components are thoroughly mixed with each other. This mixture is stable and suitable for processing for at least three days.
Для дальнейшей переработки смешивают компонент I и смесь компонентов II и III в соотношении 1: 1 и используют в качестве шпатлевки. Эта операция может проводиться как вручную, так и машинным путем. For further processing, component I and a mixture of components II and III are mixed in a ratio of 1: 1 and used as a putty. This operation can be carried out either manually or by machine.
Для машинной переработки компонент I, а также описанную выше смесь компонентов II и III загружают в соответствующий резервуар, работающий под давлением. Затем через соответствующие напорные трубопроводы компонент I и смесь компонентов II и III подают на обрабатываемое место, где поступающие из трубопроводов компоненты смешивают и используют в качестве шпатлевки. For machine processing, component I, as well as the mixture of components II and III described above, are loaded into an appropriate pressure vessel. Then, through the corresponding pressure pipelines, component I and a mixture of components II and III are fed to the place where the components coming from the pipelines are mixed and used as putty.
Смесь компонента I и смесь компонентов II и III поддается переработке в течение примерно двух-трех минут и еще через 10 минут затвердевает настолько, что зашпатлеванная поверхность камня может подвергаться шлифовке и полировке. The mixture of component I and the mixture of components II and III can be processed within about two to three minutes and after 10 minutes it hardens so much that the putty surface of the stone can be ground and polished.
Из данного примера следует, что ошибка при отмеривании инициатора может быть лишь очень незначительной, поскольку для обработки, особенно для машинной обработки, могут быть приготовлены специальные согласованные между собой по размерам упаковочные емкости для отдельных компонентов, а благодаря изготовлению смеси компонента II с инициатором, т.е. отверждающим компонентом III, для конечной переработки следует смешать только два примерно равных объема, в результате чего возможная ошибка в дозировке инициатора удерживается в очень узких границах. Кроме того, таким образом обеспечивается равномерное распределение инициатора по всей массе каменной шпатлевки. From this example it follows that the error in measuring the initiator can be only very insignificant, because for processing, especially for machine processing, special packaging containers of individual sizes can be prepared for each other, and due to the manufacture of a mixture of component II with the initiator, t .e. curing component III, for final processing should be mixed only two approximately equal volumes, as a result of which the possible error in the dosage of the initiator is kept within very narrow limits. In addition, this ensures uniform distribution of the initiator throughout the mass of the filler.
Claims (11)
Связующее средство - 20-60
Реологическая добавка - 0,5-10
Органические и/или неорганические пигменты - 0-5
Неорганические наполнители - 0-70
Структурирующие вещества - 0-30
Присадка, ускоряющая сушку - 0,1-0,5
при этом компонент I содержит до 5 мас.% ускорителя, а компонент II содержит 5 мас.% стабилизатора.4. The multi-component stone putty according to claim 2 or 3, characterized in that component I and component II in each case contains, wt.%:
Binder - 20-60
Rheological additive - 0.5-10
Organic and / or inorganic pigments - 0-5
Inorganic Fillers - 0-70
Structuring substances - 0-30
The additive accelerating drying - 0.1-0.5
wherein component I contains up to 5 wt.% accelerator, and component II contains 5 wt.% stabilizer.