RU2018101716A - Катализатор, предотвращающий проскок аммиака, с низким образованием h2o - Google Patents
Катализатор, предотвращающий проскок аммиака, с низким образованием h2o Download PDFInfo
- Publication number
- RU2018101716A RU2018101716A RU2018101716A RU2018101716A RU2018101716A RU 2018101716 A RU2018101716 A RU 2018101716A RU 2018101716 A RU2018101716 A RU 2018101716A RU 2018101716 A RU2018101716 A RU 2018101716A RU 2018101716 A RU2018101716 A RU 2018101716A
- Authority
- RU
- Russia
- Prior art keywords
- catalyst
- scr
- catalytic reduction
- selective catalytic
- layer
- Prior art date
Links
- 239000003054 catalyst Substances 0.000 title claims 145
- QGZKDVFQNNGYKY-UHFFFAOYSA-N Ammonia Chemical compound N QGZKDVFQNNGYKY-UHFFFAOYSA-N 0.000 title claims 76
- 229910021529 ammonia Inorganic materials 0.000 title claims 38
- 230000015572 biosynthetic process Effects 0.000 title claims 14
- BASFCYQUMIYNBI-UHFFFAOYSA-N platinum Chemical compound [Pt] BASFCYQUMIYNBI-UHFFFAOYSA-N 0.000 claims 64
- 238000010531 catalytic reduction reaction Methods 0.000 claims 56
- 239000000203 mixture Substances 0.000 claims 42
- 239000002808 molecular sieve Substances 0.000 claims 39
- URGAHOPLAPQHLN-UHFFFAOYSA-N sodium aluminosilicate Chemical compound [Na+].[Al+3].[O-][Si]([O-])=O.[O-][Si]([O-])=O URGAHOPLAPQHLN-UHFFFAOYSA-N 0.000 claims 39
- 229910052697 platinum Inorganic materials 0.000 claims 32
- 239000007789 gas Substances 0.000 claims 28
- 238000009825 accumulation Methods 0.000 claims 16
- 238000000034 method Methods 0.000 claims 14
- 239000011148 porous material Substances 0.000 claims 12
- XEEYBQQBJWHFJM-UHFFFAOYSA-N Iron Chemical compound [Fe] XEEYBQQBJWHFJM-UHFFFAOYSA-N 0.000 claims 8
- 229910052878 cordierite Inorganic materials 0.000 claims 8
- JSKIRARMQDRGJZ-UHFFFAOYSA-N dimagnesium dioxido-bis[(1-oxido-3-oxo-2,4,6,8,9-pentaoxa-1,3-disila-5,7-dialuminabicyclo[3.3.1]nonan-7-yl)oxy]silane Chemical group [Mg++].[Mg++].[O-][Si]([O-])(O[Al]1O[Al]2O[Si](=O)O[Si]([O-])(O1)O2)O[Al]1O[Al]2O[Si](=O)O[Si]([O-])(O1)O2 JSKIRARMQDRGJZ-UHFFFAOYSA-N 0.000 claims 8
- 239000010949 copper Substances 0.000 claims 7
- PXHVJJICTQNCMI-UHFFFAOYSA-N Nickel Chemical compound [Ni] PXHVJJICTQNCMI-UHFFFAOYSA-N 0.000 claims 6
- KDLHZDBZIXYQEI-UHFFFAOYSA-N Palladium Chemical compound [Pd] KDLHZDBZIXYQEI-UHFFFAOYSA-N 0.000 claims 6
- 239000010953 base metal Substances 0.000 claims 6
- HNPSIPDUKPIQMN-UHFFFAOYSA-N dioxosilane;oxo(oxoalumanyloxy)alumane Chemical compound O=[Si]=O.O=[Al]O[Al]=O HNPSIPDUKPIQMN-UHFFFAOYSA-N 0.000 claims 6
- RYGMFSIKBFXOCR-UHFFFAOYSA-N Copper Chemical compound [Cu] RYGMFSIKBFXOCR-UHFFFAOYSA-N 0.000 claims 5
- 229910000323 aluminium silicate Inorganic materials 0.000 claims 5
- 229910052802 copper Inorganic materials 0.000 claims 5
- VYPSYNLAJGMNEJ-UHFFFAOYSA-N Silicium dioxide Chemical compound O=[Si]=O VYPSYNLAJGMNEJ-UHFFFAOYSA-N 0.000 claims 4
- 239000011651 chromium Substances 0.000 claims 4
- 239000010931 gold Substances 0.000 claims 4
- 239000011572 manganese Substances 0.000 claims 4
- 229910052751 metal Inorganic materials 0.000 claims 4
- 239000002184 metal Substances 0.000 claims 4
- 229910000510 noble metal Inorganic materials 0.000 claims 4
- 239000010948 rhodium Substances 0.000 claims 4
- LEONUFNNVUYDNQ-UHFFFAOYSA-N vanadium atom Chemical compound [V] LEONUFNNVUYDNQ-UHFFFAOYSA-N 0.000 claims 4
- GHOKWGTUZJEAQD-ZETCQYMHSA-N (D)-(+)-Pantothenic acid Chemical compound OCC(C)(C)[C@@H](O)C(=O)NCCC(O)=O GHOKWGTUZJEAQD-ZETCQYMHSA-N 0.000 claims 3
- XUIMIQQOPSSXEZ-UHFFFAOYSA-N Silicon Chemical compound [Si] XUIMIQQOPSSXEZ-UHFFFAOYSA-N 0.000 claims 3
- 230000000694 effects Effects 0.000 claims 3
- 229910052742 iron Inorganic materials 0.000 claims 3
- 238000006722 reduction reaction Methods 0.000 claims 3
- 229910052710 silicon Inorganic materials 0.000 claims 3
- 239000010703 silicon Substances 0.000 claims 3
- 229910052684 Cerium Inorganic materials 0.000 claims 2
- 229910004625 Ce—Zr Inorganic materials 0.000 claims 2
- VYZAMTAEIAYCRO-UHFFFAOYSA-N Chromium Chemical compound [Cr] VYZAMTAEIAYCRO-UHFFFAOYSA-N 0.000 claims 2
- PWHULOQIROXLJO-UHFFFAOYSA-N Manganese Chemical compound [Mn] PWHULOQIROXLJO-UHFFFAOYSA-N 0.000 claims 2
- ZOKXTWBITQBERF-UHFFFAOYSA-N Molybdenum Chemical compound [Mo] ZOKXTWBITQBERF-UHFFFAOYSA-N 0.000 claims 2
- KJTLSVCANCCWHF-UHFFFAOYSA-N Ruthenium Chemical compound [Ru] KJTLSVCANCCWHF-UHFFFAOYSA-N 0.000 claims 2
- BQCADISMDOOEFD-UHFFFAOYSA-N Silver Chemical compound [Ag] BQCADISMDOOEFD-UHFFFAOYSA-N 0.000 claims 2
- GWXLDORMOJMVQZ-UHFFFAOYSA-N cerium Chemical compound [Ce] GWXLDORMOJMVQZ-UHFFFAOYSA-N 0.000 claims 2
- 229910052804 chromium Inorganic materials 0.000 claims 2
- 229910017052 cobalt Inorganic materials 0.000 claims 2
- 239000010941 cobalt Substances 0.000 claims 2
- GUTLYIVDDKVIGB-UHFFFAOYSA-N cobalt atom Chemical compound [Co] GUTLYIVDDKVIGB-UHFFFAOYSA-N 0.000 claims 2
- PCHJSUWPFVWCPO-UHFFFAOYSA-N gold Chemical compound [Au] PCHJSUWPFVWCPO-UHFFFAOYSA-N 0.000 claims 2
- 229910052737 gold Inorganic materials 0.000 claims 2
- 229910052748 manganese Inorganic materials 0.000 claims 2
- 150000004706 metal oxides Chemical class 0.000 claims 2
- 229910052750 molybdenum Inorganic materials 0.000 claims 2
- 239000011733 molybdenum Substances 0.000 claims 2
- 229910052759 nickel Inorganic materials 0.000 claims 2
- 229910052763 palladium Inorganic materials 0.000 claims 2
- 229910052703 rhodium Inorganic materials 0.000 claims 2
- MHOVAHRLVXNVSD-UHFFFAOYSA-N rhodium atom Chemical compound [Rh] MHOVAHRLVXNVSD-UHFFFAOYSA-N 0.000 claims 2
- 229910052707 ruthenium Inorganic materials 0.000 claims 2
- 239000000377 silicon dioxide Substances 0.000 claims 2
- 229910052709 silver Inorganic materials 0.000 claims 2
- 239000004332 silver Substances 0.000 claims 2
- WFKWXMTUELFFGS-UHFFFAOYSA-N tungsten Chemical compound [W] WFKWXMTUELFFGS-UHFFFAOYSA-N 0.000 claims 2
- 229910052721 tungsten Inorganic materials 0.000 claims 2
- 239000010937 tungsten Substances 0.000 claims 2
- 229910052720 vanadium Inorganic materials 0.000 claims 2
- 241001026509 Kata Species 0.000 claims 1
- 229910021536 Zeolite Inorganic materials 0.000 claims 1
- 229910052741 iridium Inorganic materials 0.000 claims 1
- GKOZUEZYRPOHIO-UHFFFAOYSA-N iridium atom Chemical compound [Ir] GKOZUEZYRPOHIO-UHFFFAOYSA-N 0.000 claims 1
- 238000004519 manufacturing process Methods 0.000 claims 1
- 229910044991 metal oxide Inorganic materials 0.000 claims 1
- TWNQGVIAIRXVLR-UHFFFAOYSA-N oxo(oxoalumanyloxy)alumane Chemical compound O=[Al]O[Al]=O TWNQGVIAIRXVLR-UHFFFAOYSA-N 0.000 claims 1
- 239000010970 precious metal Substances 0.000 claims 1
- 238000011084 recovery Methods 0.000 claims 1
- 239000010457 zeolite Substances 0.000 claims 1
Classifications
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
- B01J23/70—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper
- B01J23/89—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper combined with noble metals
- B01J23/8926—Copper and noble metals
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J29/00—Catalysts comprising molecular sieves
- B01J29/04—Catalysts comprising molecular sieves having base-exchange properties, e.g. crystalline zeolites
- B01J29/06—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof
- B01J29/70—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof of types characterised by their specific structure not provided for in groups B01J29/08 - B01J29/65
- B01J29/72—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof of types characterised by their specific structure not provided for in groups B01J29/08 - B01J29/65 containing iron group metals, noble metals or copper
- B01J29/76—Iron group metals or copper
- B01J29/763—CHA-type, e.g. Chabazite, LZ-218
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D53/00—Separation of gases or vapours; Recovering vapours of volatile solvents from gases; Chemical or biological purification of waste gases, e.g. engine exhaust gases, smoke, fumes, flue gases, aerosols
- B01D53/34—Chemical or biological purification of waste gases
- B01D53/92—Chemical or biological purification of waste gases of engine exhaust gases
- B01D53/94—Chemical or biological purification of waste gases of engine exhaust gases by catalytic processes
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D53/00—Separation of gases or vapours; Recovering vapours of volatile solvents from gases; Chemical or biological purification of waste gases, e.g. engine exhaust gases, smoke, fumes, flue gases, aerosols
- B01D53/34—Chemical or biological purification of waste gases
- B01D53/92—Chemical or biological purification of waste gases of engine exhaust gases
- B01D53/94—Chemical or biological purification of waste gases of engine exhaust gases by catalytic processes
- B01D53/9404—Removing only nitrogen compounds
- B01D53/9409—Nitrogen oxides
- B01D53/9413—Processes characterised by a specific catalyst
- B01D53/9418—Processes characterised by a specific catalyst for removing nitrogen oxides by selective catalytic reduction [SCR] using a reducing agent in a lean exhaust gas
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J21/00—Catalysts comprising the elements, oxides, or hydroxides of magnesium, boron, aluminium, carbon, silicon, titanium, zirconium, or hafnium
- B01J21/02—Boron or aluminium; Oxides or hydroxides thereof
- B01J21/04—Alumina
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J21/00—Catalysts comprising the elements, oxides, or hydroxides of magnesium, boron, aluminium, carbon, silicon, titanium, zirconium, or hafnium
- B01J21/06—Silicon, titanium, zirconium or hafnium; Oxides or hydroxides thereof
- B01J21/063—Titanium; Oxides or hydroxides thereof
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J21/00—Catalysts comprising the elements, oxides, or hydroxides of magnesium, boron, aluminium, carbon, silicon, titanium, zirconium, or hafnium
- B01J21/06—Silicon, titanium, zirconium or hafnium; Oxides or hydroxides thereof
- B01J21/08—Silica
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
- B01J23/38—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of noble metals
- B01J23/40—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of noble metals of the platinum group metals
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
- B01J23/38—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of noble metals
- B01J23/40—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of noble metals of the platinum group metals
- B01J23/42—Platinum
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
- B01J23/70—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper
- B01J23/89—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper combined with noble metals
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J29/00—Catalysts comprising molecular sieves
- B01J29/04—Catalysts comprising molecular sieves having base-exchange properties, e.g. crystalline zeolites
- B01J29/06—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof
- B01J29/40—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof of the pentasil type, e.g. types ZSM-5, ZSM-8 or ZSM-11, as exemplified by patent documents US3702886, GB1334243 and US3709979, respectively
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J29/00—Catalysts comprising molecular sieves
- B01J29/04—Catalysts comprising molecular sieves having base-exchange properties, e.g. crystalline zeolites
- B01J29/06—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof
- B01J29/40—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof of the pentasil type, e.g. types ZSM-5, ZSM-8 or ZSM-11, as exemplified by patent documents US3702886, GB1334243 and US3709979, respectively
- B01J29/42—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof of the pentasil type, e.g. types ZSM-5, ZSM-8 or ZSM-11, as exemplified by patent documents US3702886, GB1334243 and US3709979, respectively containing iron group metals, noble metals or copper
- B01J29/44—Noble metals
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J29/00—Catalysts comprising molecular sieves
- B01J29/04—Catalysts comprising molecular sieves having base-exchange properties, e.g. crystalline zeolites
- B01J29/06—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof
- B01J29/40—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof of the pentasil type, e.g. types ZSM-5, ZSM-8 or ZSM-11, as exemplified by patent documents US3702886, GB1334243 and US3709979, respectively
- B01J29/42—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof of the pentasil type, e.g. types ZSM-5, ZSM-8 or ZSM-11, as exemplified by patent documents US3702886, GB1334243 and US3709979, respectively containing iron group metals, noble metals or copper
- B01J29/46—Iron group metals or copper
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J29/00—Catalysts comprising molecular sieves
- B01J29/04—Catalysts comprising molecular sieves having base-exchange properties, e.g. crystalline zeolites
- B01J29/06—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof
- B01J29/70—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof of types characterised by their specific structure not provided for in groups B01J29/08 - B01J29/65
- B01J29/72—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof of types characterised by their specific structure not provided for in groups B01J29/08 - B01J29/65 containing iron group metals, noble metals or copper
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J29/00—Catalysts comprising molecular sieves
- B01J29/04—Catalysts comprising molecular sieves having base-exchange properties, e.g. crystalline zeolites
- B01J29/06—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof
- B01J29/70—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof of types characterised by their specific structure not provided for in groups B01J29/08 - B01J29/65
- B01J29/72—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof of types characterised by their specific structure not provided for in groups B01J29/08 - B01J29/65 containing iron group metals, noble metals or copper
- B01J29/723—CHA-type, e.g. Chabazite, LZ-218
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J29/00—Catalysts comprising molecular sieves
- B01J29/04—Catalysts comprising molecular sieves having base-exchange properties, e.g. crystalline zeolites
- B01J29/06—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof
- B01J29/70—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof of types characterised by their specific structure not provided for in groups B01J29/08 - B01J29/65
- B01J29/72—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof of types characterised by their specific structure not provided for in groups B01J29/08 - B01J29/65 containing iron group metals, noble metals or copper
- B01J29/76—Iron group metals or copper
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J29/00—Catalysts comprising molecular sieves
- B01J29/04—Catalysts comprising molecular sieves having base-exchange properties, e.g. crystalline zeolites
- B01J29/06—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof
- B01J29/80—Mixtures of different zeolites
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J29/00—Catalysts comprising molecular sieves
- B01J29/82—Phosphates
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J35/00—Catalysts, in general, characterised by their form or physical properties
- B01J35/19—Catalysts containing parts with different compositions
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J35/00—Catalysts, in general, characterised by their form or physical properties
- B01J35/50—Catalysts, in general, characterised by their form or physical properties characterised by their shape or configuration
- B01J35/56—Foraminous structures having flow-through passages or channels, e.g. grids or three-dimensional monoliths
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
- B01J37/02—Impregnation, coating or precipitation
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
- B01J37/02—Impregnation, coating or precipitation
- B01J37/0201—Impregnation
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
- B01J37/02—Impregnation, coating or precipitation
- B01J37/024—Multiple impregnation or coating
- B01J37/0244—Coatings comprising several layers
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
- B01J37/02—Impregnation, coating or precipitation
- B01J37/03—Precipitation; Co-precipitation
- B01J37/038—Precipitation; Co-precipitation to form slurries or suspensions, e.g. a washcoat
-
- F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
- F01—MACHINES OR ENGINES IN GENERAL; ENGINE PLANTS IN GENERAL; STEAM ENGINES
- F01N—GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR MACHINES OR ENGINES IN GENERAL; GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR INTERNAL COMBUSTION ENGINES
- F01N3/00—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust
- F01N3/08—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust for rendering innocuous
- F01N3/10—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust for rendering innocuous by thermal or catalytic conversion of noxious components of exhaust
- F01N3/18—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust for rendering innocuous by thermal or catalytic conversion of noxious components of exhaust characterised by methods of operation; Control
- F01N3/20—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust for rendering innocuous by thermal or catalytic conversion of noxious components of exhaust characterised by methods of operation; Control specially adapted for catalytic conversion ; Methods of operation or control of catalytic converters
- F01N3/2066—Selective catalytic reduction [SCR]
-
- F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
- F01—MACHINES OR ENGINES IN GENERAL; ENGINE PLANTS IN GENERAL; STEAM ENGINES
- F01N—GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR MACHINES OR ENGINES IN GENERAL; GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR INTERNAL COMBUSTION ENGINES
- F01N3/00—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust
- F01N3/08—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust for rendering innocuous
- F01N3/10—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust for rendering innocuous by thermal or catalytic conversion of noxious components of exhaust
- F01N3/24—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust for rendering innocuous by thermal or catalytic conversion of noxious components of exhaust characterised by constructional aspects of converting apparatus
- F01N3/28—Construction of catalytic reactors
- F01N3/2803—Construction of catalytic reactors characterised by structure, by material or by manufacturing of catalyst support
- F01N3/2825—Ceramics
- F01N3/2828—Ceramic multi-channel monoliths, e.g. honeycombs
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D2255/00—Catalysts
- B01D2255/10—Noble metals or compounds thereof
- B01D2255/102—Platinum group metals
- B01D2255/1021—Platinum
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D2255/00—Catalysts
- B01D2255/10—Noble metals or compounds thereof
- B01D2255/102—Platinum group metals
- B01D2255/1023—Palladium
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D2255/00—Catalysts
- B01D2255/10—Noble metals or compounds thereof
- B01D2255/102—Platinum group metals
- B01D2255/1025—Rhodium
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D2255/00—Catalysts
- B01D2255/10—Noble metals or compounds thereof
- B01D2255/102—Platinum group metals
- B01D2255/1026—Ruthenium
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D2255/00—Catalysts
- B01D2255/10—Noble metals or compounds thereof
- B01D2255/102—Platinum group metals
- B01D2255/1028—Iridium
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D2255/00—Catalysts
- B01D2255/10—Noble metals or compounds thereof
- B01D2255/104—Silver
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D2255/00—Catalysts
- B01D2255/10—Noble metals or compounds thereof
- B01D2255/106—Gold
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D2255/00—Catalysts
- B01D2255/20—Metals or compounds thereof
- B01D2255/206—Rare earth metals
- B01D2255/2065—Cerium
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D2255/00—Catalysts
- B01D2255/20—Metals or compounds thereof
- B01D2255/207—Transition metals
- B01D2255/20707—Titanium
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D2255/00—Catalysts
- B01D2255/20—Metals or compounds thereof
- B01D2255/207—Transition metals
- B01D2255/20723—Vanadium
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D2255/00—Catalysts
- B01D2255/20—Metals or compounds thereof
- B01D2255/207—Transition metals
- B01D2255/2073—Manganese
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D2255/00—Catalysts
- B01D2255/20—Metals or compounds thereof
- B01D2255/207—Transition metals
- B01D2255/20738—Iron
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D2255/00—Catalysts
- B01D2255/20—Metals or compounds thereof
- B01D2255/207—Transition metals
- B01D2255/20746—Cobalt
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D2255/00—Catalysts
- B01D2255/20—Metals or compounds thereof
- B01D2255/207—Transition metals
- B01D2255/20753—Nickel
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D2255/00—Catalysts
- B01D2255/20—Metals or compounds thereof
- B01D2255/207—Transition metals
- B01D2255/20761—Copper
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D2255/00—Catalysts
- B01D2255/20—Metals or compounds thereof
- B01D2255/207—Transition metals
- B01D2255/20769—Molybdenum
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D2255/00—Catalysts
- B01D2255/20—Metals or compounds thereof
- B01D2255/207—Transition metals
- B01D2255/20776—Tungsten
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D2255/00—Catalysts
- B01D2255/20—Metals or compounds thereof
- B01D2255/207—Transition metals
- B01D2255/20784—Chromium
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D2255/00—Catalysts
- B01D2255/20—Metals or compounds thereof
- B01D2255/209—Other metals
- B01D2255/2092—Aluminium
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D2255/00—Catalysts
- B01D2255/30—Silica
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D2255/00—Catalysts
- B01D2255/50—Zeolites
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D2255/00—Catalysts
- B01D2255/50—Zeolites
- B01D2255/504—ZSM 5 zeolites
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D2255/00—Catalysts
- B01D2255/90—Physical characteristics of catalysts
- B01D2255/902—Multilayered catalyst
- B01D2255/9022—Two layers
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D2255/00—Catalysts
- B01D2255/90—Physical characteristics of catalysts
- B01D2255/902—Multilayered catalyst
- B01D2255/9025—Three layers
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D2255/00—Catalysts
- B01D2255/90—Physical characteristics of catalysts
- B01D2255/911—NH3-storage component incorporated in the catalyst
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J29/00—Catalysts comprising molecular sieves
- B01J29/04—Catalysts comprising molecular sieves having base-exchange properties, e.g. crystalline zeolites
- B01J29/06—Crystalline aluminosilicate zeolites; Isomorphous compounds thereof
- B01J2029/062—Mixtures of different aluminosilicates
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J2229/00—Aspects of molecular sieve catalysts not covered by B01J29/00
- B01J2229/10—After treatment, characterised by the effect to be obtained
- B01J2229/18—After treatment, characterised by the effect to be obtained to introduce other elements into or onto the molecular sieve itself
- B01J2229/186—After treatment, characterised by the effect to be obtained to introduce other elements into or onto the molecular sieve itself not in framework positions
-
- F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
- F01—MACHINES OR ENGINES IN GENERAL; ENGINE PLANTS IN GENERAL; STEAM ENGINES
- F01N—GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR MACHINES OR ENGINES IN GENERAL; GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR INTERNAL COMBUSTION ENGINES
- F01N2370/00—Selection of materials for exhaust purification
- F01N2370/02—Selection of materials for exhaust purification used in catalytic reactors
- F01N2370/04—Zeolitic material
-
- F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
- F01—MACHINES OR ENGINES IN GENERAL; ENGINE PLANTS IN GENERAL; STEAM ENGINES
- F01N—GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR MACHINES OR ENGINES IN GENERAL; GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR INTERNAL COMBUSTION ENGINES
- F01N2510/00—Surface coverings
- F01N2510/06—Surface coverings for exhaust purification, e.g. catalytic reaction
- F01N2510/063—Surface coverings for exhaust purification, e.g. catalytic reaction zeolites
-
- F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
- F01—MACHINES OR ENGINES IN GENERAL; ENGINE PLANTS IN GENERAL; STEAM ENGINES
- F01N—GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR MACHINES OR ENGINES IN GENERAL; GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR INTERNAL COMBUSTION ENGINES
- F01N2510/00—Surface coverings
- F01N2510/06—Surface coverings for exhaust purification, e.g. catalytic reaction
- F01N2510/068—Surface coverings for exhaust purification, e.g. catalytic reaction characterised by the distribution of the catalytic coatings
-
- F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
- F01—MACHINES OR ENGINES IN GENERAL; ENGINE PLANTS IN GENERAL; STEAM ENGINES
- F01N—GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR MACHINES OR ENGINES IN GENERAL; GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR INTERNAL COMBUSTION ENGINES
- F01N2570/00—Exhaust treating apparatus eliminating, absorbing or adsorbing specific elements or compounds
- F01N2570/14—Nitrogen oxides
-
- F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
- F01—MACHINES OR ENGINES IN GENERAL; ENGINE PLANTS IN GENERAL; STEAM ENGINES
- F01N—GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR MACHINES OR ENGINES IN GENERAL; GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR INTERNAL COMBUSTION ENGINES
- F01N2570/00—Exhaust treating apparatus eliminating, absorbing or adsorbing specific elements or compounds
- F01N2570/18—Ammonia
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
- Y02A—TECHNOLOGIES FOR ADAPTATION TO CLIMATE CHANGE
- Y02A50/00—TECHNOLOGIES FOR ADAPTATION TO CLIMATE CHANGE in human health protection, e.g. against extreme weather
- Y02A50/20—Air quality improvement or preservation, e.g. vehicle emission control or emission reduction by using catalytic converters
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
- Y02C—CAPTURE, STORAGE, SEQUESTRATION OR DISPOSAL OF GREENHOUSE GASES [GHG]
- Y02C20/00—Capture or disposal of greenhouse gases
- Y02C20/10—Capture or disposal of greenhouse gases of nitrous oxide (N2O)
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Materials Engineering (AREA)
- Organic Chemistry (AREA)
- Crystallography & Structural Chemistry (AREA)
- Combustion & Propulsion (AREA)
- Health & Medical Sciences (AREA)
- General Engineering & Computer Science (AREA)
- Toxicology (AREA)
- Mechanical Engineering (AREA)
- Ceramic Engineering (AREA)
- Environmental & Geological Engineering (AREA)
- Analytical Chemistry (AREA)
- General Chemical & Material Sciences (AREA)
- Oil, Petroleum & Natural Gas (AREA)
- Biomedical Technology (AREA)
- Catalysts (AREA)
- Exhaust Gas Treatment By Means Of Catalyst (AREA)
- Exhaust Gas After Treatment (AREA)
Claims (71)
1. Катализатор, содержащий комбинацию платины на носителе с низким накоплением аммиака и первого катализатора селективного каталитического восстановления (SCR).
2. Катализатор по п. 1, где комбинация является смесью платины на носителе с низким накоплением аммиака с первым катализатором селективного каталитического восстановления (SCR).
3. Катализатор по п. 1, где комбинация является двойным слоем, имеющим верхний слой, содержащий первый катализатор селективного каталитического восстановления (SCR), и нижний слой, содержащий платину на носителе с низким накоплением аммиака, где нижний слой расположен на основе или на третьем катализаторе селективного каталитического восстановления (SCR), расположенном между нижним слоем и основой.
4. Катализатор по п. 1, где носитель с низким накоплением аммиака является кремнийсодержащим носителем.
5. Катализатор по п. 4, где кремнийсодержащий носитель содержит кремнезем или цеолит с отношением кремнезема к оксиду алюминия ≥100, предпочтительно ≥500.
6. Катализатор по п. 4, в котором кремнийсодержащий носитель содержит BEA, CDO, CON, FAU, MEL, MFI или MWW.
7. Катализатор по п. 2, где отношение количества первого катализатора селективного каталитического восстановления (SCR) к количеству платины на носителе с низким накоплением аммиака находится в интервале от 0:1 до 300:1, предпочтительно в интервале от 3:1 до 300:1, включительно, в расчете на массу этих компонентов.
8. Катализатор по п. 2, где смесь платины на носителе с низким накоплением аммиака с первым катализатором селективного каталитического восстановления (SCR) дополнительно содержит по меньшей мере один элемент из палладия (Pd), золота (Au), серебра (Ag), рутения (Ru) или родия (Rh).
9. Катализатор по п. 3, где нижний слой, содержащий платину на носителе с низким накоплением аммиака, дополнительно содержит по меньшей мере один элемент из золота (Au), иридия (Ir), палладия (Pd), родия (Rh), рутения (Ru) или серебра (Ag).
10. Катализатор по п. 1, где первый катализатор селективного каталитического восстановления (SCR) является Cu-SCR катализатором, содержащим медь и молекулярное сито, или Fe-SCR катализатором, содержащим железо и молекулярное сито.
11. Катализатор по п. 10, где молекулярное сито является алюмосиликатом, алюмофосфатом (AlPO), силикоалюмофосфатом (SAPO) или их смесями.
12. Катализатор по п. 10, где молекулярное сито выбрано из группы типов каркасной структуры, состоящей из ACO, AEI, AEN, AFN, AFT, AFX, ANA, APC, APD, ATT, BEA, CDO, CHA, DDR, DFT, EAB, EDI, EPI, ERI, FER, GIS, GOO, IHW, ITE, ITW, LEV, KFI, MER, MFI, MON, NSI, OWE, PAU, PHI, RHO, RTH, SAT, SAV, SIV, THO, TSC, UEI, UFI, VNI, YUG и ZON, и их смесей и/или сростков.
13. Катализатор по п. 10, где молекулярное сито выбрано из группы типов каркасной структуры, состоящей из AEI, AFX, BEA, CHA, DDR, ERI, FER, ITE, KFI, LEV, MFI и SFW, и их смесей и/или сростков.
14. Катализатор по п. 2, где платина присутствует в по меньшей мере одном интервале из (a) 0,01-0,3 масс.%, (b) 0,03-0,2 масс.%, (c) 0,05-0,17 масс.% и (d) 0,07-0,15 масс.%, включительно, по отношению к сумме «масса носителя платины + масса платины + масса первого катализатора селективного каталитического восстановления (SCR) в смеси».
15. Катализатор по п. 3, где платина присутствует в количестве от 0,1 масс.% до 2 масс.%, включительно, предпочтительно от 0,1 до 1 масс.%, включительно, более предпочтительно от 0,1 масс.% до 0,5 масс.%, включительно, по отношению к массе слоя.
16. Катализатор по п. 2, дополнительно содержащий второй катализатор селективного каталитического восстановления (SCR), где второй катализатор селективного каталитического восстановления (SCR) расположен рядом со смесью платины на носителе с низким накоплением аммиака с первым катализатором селективного каталитического восстановления (SCR) и по меньшей мере частично покрывает смесь платины на носителе с низким накоплением аммиака и первого катализатора селективного каталитического восстановления (SCR).
17. Катализатор по п. 16, где второй катализатор селективного каталитического восстановления (SCR) содержит неблагородный металл, оксид неблагородного металла, благородный металл, молекулярное сито, металлзамещенное молекулярное сито, смешанный оксид или их смесь.
18. Катализатор по п. 17, где неблагородный металл выбран из группы, состоящей из ванадия (V), молибдена (Mo), вольфрама (W), хрома (Cr), церия (Ce), марганца (Mn), железа (Fe), кобальта (Co), никеля (Ni) и меди (Cu), и их смесей.
19. Катализатор по п. 18, дополнительно содержащий по меньшей мере один промотор на основе неблагородного металла.
20. Катализатор по п. 19, где промотором на основе неблагородного металла является Nb.
21. Катализатор по п. 17, где молекулярное сито или металлзамещенное молекулярное сито является молекулярным ситом с малым, средним или большим размером пор или же их смесью.
22. Катализатор по п. 17, где второй катализатор селективного каталитического восстановления (SCR) содержит молекулярное сито с малым размером пор, выбранное из группы, состоящей из алюмосиликатных молекулярных сит, металлзамещенных алюмосиликатных молекулярных сит, алюмофосфатных (AlPO) молекулярных сит, металлзамещенных алюмофосфатных молекулярных сит (MeAlPO), силикоалюмофосфатных (SAPO) молекулярных сит и металлзамещенных силикоалюмофосфатных молекулярных сит (MeAPSO), и их смесей.
23. Катализатор по п. 18, где второй катализатор селективного каталитического восстановления (SCR) содержит молекулярное сито с малым размером пор, выбранное из группы типов каркасной структуры, состоящей из ACO, AEI, AEN, AFN, AFT, AFX, ANA, APC, APD, ATT, CDO, CHA, DDR, DFT, EAB, EDI, EPI, ERI, GIS, GOO, IHW, ITE, ITW, LEV, KFI, MER, MON, NSI, OWE, PAU, PHI, RHO, RTH, SAT, SAV, SIV, THO, TSC, UEI, UFI, VNI, YUG и ZON, и их смесей и/или сростков.
24. Катализатор по п. 18, где второй катализатор селективного каталитического восстановления (SCR) содержит молекулярное сито с малым размером пор выбранное из группы типов каркасной структуры, состоящей из CHA, LEV, AEI, AFX, ERI, SFW, KFI, DDR и ITE.
25. Катализатор по п. 18, где второй катализатор селективного каталитического восстановления (SCR) содержит молекулярное сито со средним размером пор, выбранное из группы типов каркасной структуры, состоящей из AEL, AFO, AHT, BOF, BOZ, CGF, CGS, CHI, DAC, EUO, FER, HEU, IMF, ITH, ITR, JRY, JSR, JST, LAU, LOV, MEL, MFI, MFS, MRE, MTT, MVY, MWW, NAB, NAT, NES, OBW, PAR, PCR, PON, PUN, RRO, RSN, SFF, SFG, STF, STI, STT, STW, SVR, SZR, TER, TON, TUN, UOS, VSV, WEI и WEN, и их смесей и/или сростков.
26. Катализатор по п. 18, где второй катализатор селективного каталитического восстановления (SCR) содержит молекулярное сито с большим размером пор, выбранное из группы типов каркасной структуры, состоящей из AFI, AFR, AFS, AFY, ASV, ATO, ATS, BEA, BEC, BOG, BPH, BSV, CAN, CON, CZP, DFO, EMT, EON, EZT, FAU, GME, GON, IFR, ISV, ITG, IWR, IWS, IWV, IWW, JSR, LTF, LTL, MAZ, MEI, MOR, MOZ, MSE, MTW, NPO, OFF, OKO, OSI, RON, RWY, SAF, SAO, SBE, SBS, SBT, SEW, SFE, SFO, SFS, SFV, SOF, SOS, STO, SSF, SSY, USI, UWY и VET, и их смесей и/или сростков.
27. Катализатор по п. 16, где второй катализатор селективного каталитического восстановления (SCR) полностью покрывает смесь платины на носителе с низким накоплением аммиака с первым катализатором селективного каталитического восстановления (SCR).
28. Катализатор по п. 16, где второй катализатор селективного каталитического восстановления (SCR) является Cu-SCR катализатором, содержащим медь и молекулярное сито, Fe-SCR катализатором, содержащим железо и молекулярное сито, катализатором на основе ванадия, промотированным Ce-Zr или промотированным MnO2.
29. Катализатор по п. 16, дополнительно содержащий третий катализатор селективного каталитического восстановления (SCR), где третий катализатор селективного каталитического восстановления (SCR) расположен рядом со смесью платины на носителе с низким накоплением аммиака с первым катализатором селективного каталитического восстановления (SCR), и смесь платины на носителе с низким накоплением аммиака с первым катализатором селективного каталитического восстановления (SCR) по меньшей мере частично покрывает третий катализатор селективного каталитического восстановления (SCR).
30. Катализатор по п. 29, где третий катализатор селективного каталитического восстановления (SCR) является неблагородным металлом, оксидом неблагородного металла, благородным металлом, молекулярным ситом, металлзамещенным молекулярным ситом или их смесью.
31. Катализатор по п. 30, где неблагородный металл выбран из группы, состоящей из ванадия (V), молибдена (Mo), вольфрама (W), хрома (Cr), церия (Ce), марганца (Mn), железа (Fe), кобальта (Co), никеля (Ni) и меди (Cu), и их смесей.
32. Катализатор по п. 30, дополнительно содержащий по меньшей мере один промотор на основе неблагородного металла.
33. Катализатор по п. 30, где молекулярное сито или металлзамещенное молекулярное сито является молекулярным ситом с малым, средним или большим размером пор или же их смесью.
34. Катализатор по п. 30, где третий катализатор селективного каталитического восстановления (SCR) содержит молекулярное сито с малым размером пор, выбранное из группы, состоящей из алюмосиликатных молекулярных сит, металлзамещенных алюмосиликатных молекулярных сит, алюмофосфатных (AlPO) молекулярных сит, металлзамещенных алюмофосфатных молекулярных сит (MeAlPO), силикоалюмофосфатных (SAPO) молекулярных сит и металлзамещенных силикоалюмофосфатных молекулярных сит (MeAPSO), и их смесей.
35. Катализатор по п. 30, где третий катализатор селективного каталитического восстановления (SCR) содержит молекулярное сито с малым размером пор, выбранное из группы типов каркасной структуры, состоящей из ACO, AEI, AEN, AFN, AFT, AFX, ANA, APC, APD, ATT, CDO, CHA, DDR, DFT, EAB, EDI, EPI, ERI, GIS, GOO, IHW, ITE, ITW, LEV, KFI, MER, MON, NSI, OWE, PAU, PHI, RHO, RTH, SAT, SAV, SIV, THO, TSC, UEI, UFI, VNI, YUG и ZON, и их смесей и/или сростков.
36. Катализатор по п. 30, где третий катализатор селективного каталитического восстановления (SCR) содержит молекулярное сито с малым размером пор выбранное из группы типов каркасной структуры, состоящей из CHA, LEV, AEI, AFX, ERI, SFW, KFI, DDR и ITE.
37. Катализатор по п. 30, где третий катализатор селективного каталитического восстановления (SCR) содержит молекулярное сито со средним размером пор, выбранное из группы типов каркасной структуры, состоящей из AEL, AFO, AHT, BOF, BOZ, CGF, CGS, CHI, DAC, EUO, FER, HEU, IMF, ITH, ITR, JRY, JSR, JST, LAU, LOV, MEL, MFI, MFS, MRE, MTT, MVY, MWW, NAB, NAT, NES, OBW, PAR, PCR, PON, PUN, RRO, RSN, SFF, SFG, STF, STI, STT, STW, SVR, SZR, TER, TON, TUN, UOS, VSV, WEI и WEN, и их смесей и/или сростков.
38. Катализатор по п. 30, где третий катализатор селективного каталитического восстановления (SCR) содержит молекулярное сито с большим размером пор, выбранное из группы типов каркасной структуры, состоящей из AFI, AFR, AFS, AFY, ASV, ATO, ATS, BEA, BEC, BOG, BPH, BSV, CAN, CON, CZP, DFO, EMT, EON, EZT, FAU, GME, GON, IFR, ISV, ITG, IWR, IWS, IWV, IWW, JSR, LTF, LTL, MAZ, MEI, MOR, MOZ, MSE, MTW, NPO, OFF, OKO, OSI, RON, RWY, SAF, SAO, SBE, SBS, SBT, SEW, SFE, SFO, SFS, SFV, SOF, SOS, STO, SSF, SSY, USI, UWY и VET, и их смесей и/или сростков.
39. Катализатор по п. 30, где третий катализатор селективного каталитического восстановления (SCR) является Cu-SCR катализатором, содержащим медь и молекулярное сито, Fe-SCR катализатором, содержащим железо и молекулярное сито, катализатором на основе ванадия, промотированным Ce-Zr или промотированным MnO2.
40. Катализатор по п. 1, где катализатор обеспечивает улучшение в выходе N2 от аммиака при температуре от примерно 250°C до примерно 350°C по сравнению с катализатором, содержащим сравнимый состав, в котором первый катализатор селективного каталитического восстановления (SCR) присутствует в качестве первого слоя, и нанесенная платина присутствует во втором слое, и газ, содержащий NH3, проходит через первый слой перед прохождением через второй слой.
41. Катализатор по п. 2, где катализатор обеспечивает улучшение в выходе N2 от аммиака при температуре от примерно 250°C до примерно 350°C по сравнению с катализатором, содержащим сравнимый состав, в котором первый катализатор селективного каталитического восстановления (SCR) присутствует в качестве первого слоя, и нанесенная платина присутствует во втором слое, и газ, содержащий NH3, проходит через первый слой перед прохождением через второй слой.
42. Катализатор по п. 3, где катализатор обеспечивает улучшение в выходе N2 от аммиака при температуре от примерно 250°C до примерно 350°C по сравнению с катализатором, содержащим сравнимый состав, в котором первый катализатор селективного каталитического восстановления (SCR) присутствует в качестве первого слоя, и нанесенная платина присутствует во втором слое, и газ, содержащий NH3, проходит через первый слой перед прохождением через второй слой.
43. Катализатор по п. 14, где катализатор обеспечивает по меньшей мере один эффект из (a) улучшения в выходе N2 от аммиака при температуре от примерно 350°C до примерно 450°C и (b) уменьшения образования NOх при температуре от примерно 350°C до примерно 450°C, по сравнению с катализатором, содержащим сравнимый состав, в котором первый катализатор селективного каталитического восстановления (SCR) присутствует в качестве первого слоя, и нанесенная платина присутствует во втором слое, и газ, содержащий NH3, проходит через первый слой перед прохождением через второй слой.
44. Катализатор по п. 27, где катализатор обеспечивает по меньшей мере один эффект из (a) улучшения в выходе N2 от аммиака при температуре от примерно 350°C до примерно 450°C и (b) уменьшения образования NOх при температуре от примерно 350°C до примерно 450°C, по сравнению с катализатором, содержащим сравнимый состав, в котором первый катализатор селективного каталитического восстановления (SCR) присутствует в качестве первого слоя, и нанесенная платина присутствует во втором слое, и газ, содержащий NH3, проходит через первый слой перед прохождением через второй слой.
45. Катализатор по п. 29, где катализатор обеспечивает по меньшей мере один эффект из (a) улучшения в выходе N2 от аммиака при температуре от примерно 350°C до примерно 450°C и (b) уменьшения образования NOх при температуре от примерно 350°C до примерно 450°C, по сравнению с катализатором, содержащим сравнимый состав, в котором первый катализатор селективного каталитического восстановления (SCR) присутствует в качестве первого слоя, и нанесенная платина присутствует во втором слое, и газ, содержащий NH3, проходит через первый слой перед прохождением через второй слой.
46. Катализатор по п. 1, где катализатор обеспечивает уменьшенное образование N2O от NH3 по сравнению с катализатором, содержащим сравнимый состав, в котором первый катализатор селективного каталитического восстановления (SCR) присутствует в качестве первого слоя, и нанесенная платина присутствует во втором слое, и газ, содержащий NH3, проходит через первый слой перед прохождением через второй слой.
47. Изделие, содержащее катализатор по п. 1, основу, впускное отверстие и выпускное отверстие.
48. Изделие по п. 47, где основой является кордиерит, высокопористый кордиерит, металлическая основа, экструдированный SCR, фильтр с проточными стенками, фильтр или фильтр селективного каталитического восстановления (SCRF).
49. Изделие, содержащее катализатор по п. 14, основу, впускное отверстие и выпускное отверстие.
50. Изделие по п. 49, где основой является кордиерит, высокопористый кордиерит, металлическая основа, экструдированный SCR, фильтр с проточными стенками, фильтр или фильтр селективного каталитического восстановления (SCRF).
51. Изделие по п. 49, где второй катализатор селективного каталитического восстановления (SCR) расположен на впускной стороне катализатора, содержащего смесь платины на носителе с низким накоплением аммиака с первым катализатором селективного каталитического восстановления (SCR).
52. Изделие по п. 49, где второй катализатор селективного каталитического восстановления (SCR) расположен на выпускной стороне катализатора, содержащего смесь платины на носителе с низким накоплением аммиака с первым катализатором селективного каталитического восстановления (SCR).
53. Изделие, содержащее катализатор по п. 29, основу, впускное отверстие и выпускное отверстие, где третий катализатор селективного каталитического восстановления (SCR) расположен на впускной стороне катализатора, содержащего смесь платины на носителе с низким накоплением аммиака с первым катализатором селективного каталитического восстановления (SCR).
54. Изделие по п. 51, где основой является кордиерит, высокопористый кордиерит, металлическая основа, экструдированный SCR, фильтр с проточными стенками, фильтр или фильтр селективного каталитического восстановления (SCRF).
55. Изделие по п. 52, где основой является кордиерит, высокопористый кордиерит, металлическая основа, экструдированный SCR, фильтр с проточными стенками, фильтр или фильтр селективного каталитического восстановления (SCRF).
56. Система выпуска отработавших газов, содержащая катализатор по п. 1 и средство для образования NH3 в выхлопных газах.
57. Система выпуска отработавших газов, содержащая катализатор по п. 16 и средство для образования NH3 в выхлопных газах.
58. Система выпуска отработавших газов, содержащая катализатор по п. 29 и средство для образования NH3 в выхлопных газах.
59. Способ изготовления катализатора по п. 2, данный способ включает смешивание катализатора, содержащего смесь платины на носителе с низким накоплением аммиака, с первым катализатором селективного каталитического восстановления (SCR).
60. Способ улучшения выхода N2 от аммиака в выхлопных газах при температуре от примерно 250°C до примерно 350°C, включающий осуществление контакта выхлопных газов, содержащих аммиак, с катализатором по п. 1.
61. Способ по п. 60, где улучшение в выходе составляет от примерно 5% до примерно 10% по сравнению с катализатором, содержащим сравнимый состав, в котором первый катализатор селективного каталитического восстановления (SCR) присутствует в качестве первого слоя, и платина на носителе, который накапливает аммиак, присутствует во втором слое, и газ, содержащий NH3, проходит через первый слой перед прохождением через второй слой.
62. Способ улучшения выхода N2 от аммиака в выхлопных газах при температуре от примерно 250°C до примерно 350°C, включающий осуществление контакта выхлопных газов, содержащих аммиак, с катализатором по п. 12.
63. Способ по п. 62, где улучшение в выходе составляет от примерно 10% до примерно 20% по сравнению с катализатором, содержащим сравнимый состав, в котором первый катализатор селективного каталитического восстановления (SCR) присутствует в качестве первого слоя, и платина на носителе, который накапливает аммиак, присутствует во втором слое, и газ, содержащий NH3, проходит через первый слой перед прохождением через второй слой.
64. Способ улучшения выхода N2 от аммиака в выхлопных газах при температуре от примерно 250°C до примерно 350°C, включающий осуществление контакта выхлопных газов, содержащих аммиак, с катализатором по п. 25.
65. Способ по п. 64, где улучшение в выходе составляет от примерно 10% до примерно 20% по сравнению с катализатором, содержащим сравнимый состав, в котором первый катализатор селективного каталитического восстановления (SCR) присутствует в качестве первого слоя, и платина на носителе, который накапливает аммиак, присутствует во втором слое, и газ, содержащий NH3, проходит через первый слой перед прохождением через второй слой.
66. Способ уменьшения образования N2O из NH3 в выхлопных газах, включающий осуществление контакта выхлопных газов, содержащих аммиак, с катализатором по п. 1.
67. Способ по п. 66, где уменьшение образования N2O составляет от примерно 20% до примерно 40% по сравнению с катализатором, содержащим сравнимый состав, в котором первый катализатор селективного каталитического восстановления (SCR) присутствует в качестве первого слоя, и платина на носителе, который накапливает аммиак, присутствует во втором слое, и газ, содержащий NH3, проходит через первый слой перед прохождением через второй слой.
68. Способ уменьшения образования N2O из NH3 в выхлопных газах, данный способ включающий осуществление контакта выхлопных газов, содержащих аммиак, с катализатором по п. 12.
69. Способ по п. 68, где уменьшение образования N2O составляет от примерно 50% до примерно 80% по сравнению с катализатором, содержащим сравнимый состав, в котором первый катализатор селективного каталитического восстановления (SCR) присутствует в качестве первого слоя, и платина на носителе, который накапливает аммиак, присутствует во втором слое, и газ, содержащий NH3, проходит через первый слой перед прохождением через второй слой.
70. Способ уменьшения образования N2O из NH3 в выхлопных газах, включающий осуществление контакта выхлопных газов, содержащих аммиак, с катализатором по п. 25.
71. Способ по п. 70, где уменьшение образования N2O составляет от примерно 50% до примерно 80% по сравнению с катализатором, содержащим сравнимый состав, в котором первый катализатор селективного каталитического восстановления (SCR) присутствует в качестве первого слоя, и платина на носителе, который накапливает аммиак, присутствует во втором слое, и газ, содержащий NH3, проходит через первый слой перед прохождением через второй слой.