NL8401841A - ELECTROLYTIC COMPOSITION AND METHOD FOR ELECTROLYTIC PRECIPITATION OF COPPER. - Google Patents
ELECTROLYTIC COMPOSITION AND METHOD FOR ELECTROLYTIC PRECIPITATION OF COPPER. Download PDFInfo
- Publication number
- NL8401841A NL8401841A NL8401841A NL8401841A NL8401841A NL 8401841 A NL8401841 A NL 8401841A NL 8401841 A NL8401841 A NL 8401841A NL 8401841 A NL8401841 A NL 8401841A NL 8401841 A NL8401841 A NL 8401841A
- Authority
- NL
- Netherlands
- Prior art keywords
- electrolyte
- copper
- brightener
- present
- brighteners
- Prior art date
Description
k * *Λ —- VC €37ck * * Λ —- VC € 37c
Elektrolyc-samenstelling alsmede werkwijze voor het elektrolytisch neerslaan van koper.Electrolyc composition and process for the electrolytic deposition of copper.
De onderhavige uitvinding heeft betrekking op een waterige elektrolytsamenstelling alsmede een werkwijze voor het elektrolytisch neerslaan van koper op een geleidend substraat, in het bijzonder op een verbeterd waterig zuur kopergalvaniseringsbad dat een nieuwe 5 combinatie vein glansmiddelen bevat waarmee een koperlaag wordt verkregen die ductiel, egaal en glanzend is, in het bijzonder in de lage-stroomdichtheidsgebieden.The present invention relates to an aqueous electrolyte composition as well as a method for the electrolytic deposition of copper on a conductive substrate, in particular to an improved aqueous acid copper galvanizing bath containing a new combination of brighteners to obtain a copper layer which is ductile, uniform and glossy, especially in the low current density regions.
Verschillende waterige elektrolytsamenstellingen en werkwijzen zijn reeds voorgesteld voor het elektrolytisch neerslaan van 10 egale, glanzende, ductiele koperbekledingen. Van belang zijnde samenstellingen en werkwijzen worden beschreven in de Amerikaanse octrooi-schriften 2.707.166; 2.707.167; 2.738. 318; 2.882.209; 3.267.010; 3.328.273; 3.770.598; 4.11Q.176 en 4.272.335. Volgens het Amerikaanse octrooischrift 4.272.335 gaat men uit van een verbeterde waterige zure 15 koperelektrolyt die een gesubstitueerd ftalocyanineradicaal als glansmiddel bevat waarbij bij voorkeur secundaire glansmiddelen worden opgenomen zoals polysulfiden, sulfiden en/of polyether-verbindingen. Hoewel men met de waterige zuurelektrolyt beschreven in het voornoemde Amerikaanse octrooischrift verbeteringen in de glans, gelijkmatigheid en ductili-20 text van koperbekledingen bij bepaalde werkparameters en samenstellings-variaties kan bereiken, wordt in de lagere stroomdichtheidsgebieden van de te bekleden voorwerpen geen optimale glans van de koperbekleding bereikt.Various aqueous electrolyte compositions and methods have already been proposed for the electrolytic deposition of uniform, glossy, ductile copper coatings. Compositions and methods of interest are described in U.S. Patents 2,707,166; 2,707,167; 2,738. 318; 2,882,209; 3,267,010; 3,328,273; 3,770,598; 4.11Q.176 and 4.272.335. US Pat. No. 4,272,335 is based on an improved aqueous acidic copper electrolyte containing a substituted phthalocyanine radical as brightener, preferably including secondary brighteners such as polysulfides, sulfides and / or polyether compounds. While improvements in the gloss, uniformity, and ductility of copper coatings can be achieved with the aqueous acid electrolyte described in the aforementioned U.S. patent for certain operating parameters and composition variations, optimal glossiness of the articles to be coated is not achieved in the lower current density ranges of the articles to be coated. copper cladding reached.
Wanneer men verder een apo safranine-glansmiddel afzon-25 derlijk of in combinatie met andere glansmiddelen, zoals polysulfiden, organische sulfiden en/of poiyetherverbindingen toepast verkrijgt men onder bepaalde omstandigheden in de lage stroomdichtheidsgebieden een onbevredigende glans en gelijkmatigheid van de bekleding. Wanneer men de concentratie van het apo safranine-glasmiddel verhoogt om het lage-30 stroomdichtheidsprobleem te overwinnen ontstaan in de lage stroomdichtheidsgebieden donkere strepen waardoor de bekleding onaanvaardbaar wordt.Furthermore, when an apo safranine brightener is used individually or in combination with other brighteners, such as polysulfides, organic sulfides and / or polyether compounds, unsatisfactory gloss and uniformity of the coating is obtained under certain conditions in the low current density ranges. Increasing the concentration of the apo safranin glass agent to overcome the low current density problem creates dark streaks in the low current density areas, making the coating unacceptable.
Aldus bestaat er een behoefte aan een verdere verbete- 8401841 5 ring van waterige zure koperelektrolyten waarmede men een uitstekende glans van koperbekledingen in de lage stroomdichtheidsgebieden van de te bekleden voorwerpen kan bereiken, welk voordeel men steeds over een breed traject van samenstellings- en bewerkingsomstandigheden kan be-5 reiken. De waterige zuurelektrolyt volgens de uitvinding bezat een gekozen combinatie van glansmiddelen waarmede een synergistisch glans-bevor-derend effect kan worden bereikt, in het bijzonder in genoemde lage stroomdichtheidsgebieden over een betrekkelijk breed traject van concentraties en badbewerkingsomstandigheden.Thus, there is a need for a further improvement of aqueous acidic copper electrolytes which can achieve excellent gloss of copper coatings in the low current density ranges of the articles to be coated, which advantage can always be achieved over a wide range of composition and processing conditions. be-5 reach. The aqueous acid electrolyte of the invention had a selected combination of brighteners which can achieve a synergistic gloss enhancing effect, particularly in said low current density ranges over a relatively wide range of concentrations and bath processing conditions.
10 De voordelen van de onderhavige uitvinding worden verkre gen met een elektrolytsamenstelling en een werkwijze voor het elektroly-tisch neerslaan van koper uit een waterig zuur galvaniseringsbad dat een voor glansdoeleinden effectieve combinatie van verbindingen met inbegrip van een badoplosbaar gesubstitueerd ftalocyanine-radicaal en een 15 apo safranine-verbinding, die in ingestelde hoeveelheden aanwezig zijn, bevat. Meer in het bijzonder is de waterige zuurelektrolyt van het koper-sulfaat of fluorboraat-type waarbij voldoend koper aanwezig is om een elektrolytische koperlaag neer te slaan, alsmede een voor glansdoeleinden effectieve hoeveelheid van het gesubstitueerde ftalocyanine-radicaal 20 voorgesteld door de formule Pc-(X)n» waarin Pc een ftalocyanineradicaal is; X -S02NR2,-S03M,-CH2SC(NR2)2+Y- is; R H, alkyl met 1-6 koolstof-atomen, aryl met 6 koolstof atomen, aralkyl met 6 koolstof atomen in het aryldeel en 1 - 6 koolstofatomen in het alkyldeel, een heterocyclische groep met 2-5 koolstofatomen en tenminste 1 stikstof-, zuurstof-, zwa-25 vel- of fosforatoom, en alkyl, aryl, aralkyl en een heterocyclische groep als boven gedefinieerd die 1-5 amino-, hydroxy-, sulfonzuur-, of fosfonzuurgroepen bevatten; η 1 - 6 is; γ halogeen of alkylsulfaat met 1-4 koolstofatomen in het alkyldeel is en Μ H, Li, Na, K of Mg is, verder gecombineerd met een verbinding voorgesteld door formule A 30 van het formuleblad, waarin R gelijk of verschillend is en -CH^, -C^H^ en -C^H^ omvat en X anion is gekozen uit chloride, bromide, jodide, fluoride, sulfaat, bisulfaat en nitraat.The advantages of the present invention are obtained with an electrolyte composition and method for the electrolytic deposition of copper from an aqueous acidic galvanizing bath containing a gloss-effective combination of compounds including a bath-soluble substituted phthalocyanine radical and an apo safranin compound, which are present in set amounts. More specifically, the copper sulfate or fluoroborate type aqueous acid electrolyte with sufficient copper present to precipitate an electrolytic copper layer, as well as a gloss effective amount of the substituted phthalocyanine radical represented by the formula Pc- ( X) n »wherein Pc is a phthalocyanine radical; X is -SO 2 NR 2, -SO 3 M, -CH 2 SC (NR 2) 2 + Y-; RH, alkyl of 1-6 carbon atoms, aryl of 6 carbon atoms, aralkyl of 6 carbon atoms in the aryl part and 1-6 carbon atoms in the alkyl part, a heterocyclic group of 2-5 carbon atoms and at least 1 nitrogen, oxygen sulfur or phosphorus atom, and alkyl, aryl, aralkyl and a heterocyclic group as defined above containing 1-5 amino, hydroxy, sulfonic, or phosphonic acid groups; η is 1 - 6; γ is halogen or alkyl sulfate with 1-4 carbon atoms in the alkyl moiety and Μ is H, Li, Na, K or Mg, further combined with a compound represented by formula A 30 of the formula sheet, wherein R is the same or different and -CH ^ , -C 1 H 2 and -C 2 H 3 and X anion is selected from chloride, bromide, iodide, fluoride, sulfate, bisulfate and nitrate.
Het ftalocyanine-glasmiddel kan metaalvrij zijn maar ook een stabiel divalent of trivalent metaal bevatten, zoals kobalt, 35 nikkel, chroom, ijzer, of koper, alsmede mengsels daarvan waarvan koper het voorkeursmetaal is. Ten gebruike in de uitvinding geschikte ftalo- 8401841 . C5-- * cyanine-glansmiddelen hebben een badoplosbaarheid van tenminste ongeveer 0,1 milligram per liter (mg/1).The phthalocyanine glass medium can be metal-free, but it can also contain a stable divalent or trivalent metal, such as cobalt, nickel, chromium, iron, or copper, as well as mixtures thereof of which copper is the preferred metal. Phthalo 8401841 suitable for use in the invention. C5 * * cyanine brighteners have a bath solubility of at least about 0.1 milligrams per liter (mg / l).
Volgens een voorkeursuitvoeringsvorm van de onderhavige uitvinding worden het ftalocyanineradicaal en het apo safranine-glans-5 middel aangevuld met secundaire glansmiddelen met inbegrip van alifati-sche polysulfiden, organische sulfiden en/of polyether-verbindingen om de glans en de fysische eigenschappen van de koperbekleding verder te verbeteren.In a preferred embodiment of the present invention, the phthalocyanine radical and the apo safranin brightener are supplemented with secondary brighteners including aliphatic polysulfides, organic sulfides and / or polyether compounds to further enhance the gloss and physical properties of the copper cladding to improve.
Volgens de werkwijzeaspecten van de onderhavige uitvin-10 ding kan het waterige zure elektrolytische bekledingsbad worden toegepast bij temperaturen van ongeveer 15° tot ongeveer 50°C en bij stroomdichtheden die variëren van ongeveer 0,05 tot ongeveer 43 ampère per vierkante decimeter.According to the process aspects of the present invention, the aqueous acidic electrolytic coating bath can be used at temperatures from about 15 ° to about 50 ° C and at current densities ranging from about 0.05 to about 43 amperes per square decimeter.
Verdere voordelen van de onderhavige uitvinding wor-15 den toegelicht aan de hand van de voorkeursuitvoeringsvormen in samenhang met de bijgaande voorbeelden.Further advantages of the present invention are illustrated by the preferred embodiments in conjunction with the accompanying examples.
Volgens de werkwijze van de onderhavige uitvinding wordt uitgegaan van een waterige zure elektrolyt, die van het sulfaat-type kan zijn en typerend ongeveer 180 tot ongeveer 250 g/1 kopersulfaat en 20 ongeveer 30 tot ongeveer 80 g/1 zwavelzuur bevat. Men kan ook fluor-boraatbaden bereiden die ongeveer 200 tot ongeveer 600 g/1 koperfluor-boraat en tot ongeveer 60 g/1 fluorboorzuur bevatten. Voorts kunnen kopernitraatzouten in bij benadering equivalente hoeveelheden in plaats van kopersulfaat worden toegepast, terwijl de elektrolyt met equiva-25 lente hoeveelheden fosforzuur, salpeterzuur of zwavelzuur kan worden aangezuurd. Volgens een voorkeursuitvoeringsvorm van de uitvinding worden sulfaat-type koperbaden toegepast.The process of the present invention is based on an aqueous acidic electrolyte, which may be of the sulfate type and typically contains about 180 to about 250 g / l copper sulfate and about 30 to about 80 g / l sulfuric acid. Fluoroborate baths can also be prepared containing from about 200 to about 600 g / l of copper fluoroborate and up to about 60 g / l of fluoroboric acid. Furthermore, copper nitrate salts can be used in approximately equivalent amounts instead of copper sulfate, while the electrolyte can be acidified with equivalent amounts of phosphoric, nitric or sulfuric acid. In a preferred embodiment of the invention, sulfate-type copper baths are used.
De waterige elektrolyt kan verder halogenide-ionen bevatten, zoals chloride- en/of bromide-ionen in een hoeveelheid tot 30 ongeveer 0,5 g/1.The aqueous electrolyte may further contain halide ions, such as chloride and / or bromide ions, in an amount up to about 0.5 g / l.
Het bijzondere glansvermogen dat in de lage stroomdichtheid inspringende holtegebieden wordt verkregen ontstaat door toepassing van een synergistische combinatie van het gesubstitueerde ftalo-cyanineradicaal-glansmiddel en het apo safranine-glansmiddel in inge-35 stelde concentraties en hoeveelheden, bij voorkeur verder gecombineerd met extra organische glasmiddelen. Het gesubstitueerde ftalocyanine-radi- 840184? Γ ^ 4 caal kan metaalvrij zijn of een stabiel divalent of trivalent metaal bevatten wat door coödinatie van de isoindool-stikstofatomen van het molecuul is gebonden, welk metaal wordt gekozen uit kobalt, nikkel, chroom, ijzer of koper, alsmede mengsels van de voornoemde waarvan ko-5 per het meest de voorkeur hebbende metaal is. Dergelijke voor toepassing in de onderhavige werkwijze geschikte ftalocyanineverbindingen hebben een badoplosbaarheid van tenminste ongeveer 0,1 mg/1 en komen overeen met de structuurformule B van het formuleblad, waarin X de voornoemde betekenissen heeft; Z Ni, Co, Cr, Pe of Cu is; a 0 - 1 is 10 es B 0-2 is, onder voorwaarde dat het totale aantal X-substituenten 1 - 6 is.The particular glossiness that is induced in cavity regions in the low current density results from the use of a synergistic combination of the substituted phthalocyanine radical brightener and the apo safranine brightener in adjusted concentrations and amounts, preferably further combined with additional organic glazing agents . The substituted phthalocyanine radir-840184? Aal ^ 4 cals can be metal-free or contain a stable divalent or trivalent metal bonded by coordination of the molecule's isoindole nitrogen atoms, which metal is selected from cobalt, nickel, chromium, iron or copper, as well as mixtures of the aforementioned ko-5 per the most preferred metal. Such phthalocyanine compounds suitable for use in the present process have a bath solubility of at least about 0.1 mg / l and correspond to the structural formula B of the formula sheet, wherein X has the aforementioned meanings; Z is Ni, Co, Cr, Pe or Cu; a 0 - 1 is 10 es B is 0-2, provided that the total number of X substituents is 1 - 6.
Gesubstitueerde ftalocyanineverbindingen die geschikt zijn voor de onderhavige uitvinding omvatten verder de verbindingen als beschreven in het Amerikaanse octrooischrift 4.272.335, waarvan 15 de beschrijving hierin als referentie wordt opgenomen. Een ftalocyanine-verbinding die bijzondere voorkeur heeft omvat Alcian Blue.Substituted phthalocyanine compounds suitable for the present invention further include those described in U.S. Patent 4,272,335, the disclosure of which is incorporated herein by reference. A particularly preferred phthalocyanine compound includes Alcian Blue.
De gecombineerde glansmiddelen die overeenkomen met de formule A en het gesubstitueerde ftalocyanine-radicaal-glansmiddel worden bij badconcentraties van ongeveer 0,0005 g/1 tot ongeveer 1 g/1 20 toegepast waarbij concentraties van ongeveer 0,002 g/1 tot ongeveer 0,01 g/1 voorkeur hebben. Het gesubstitueerde ftalocyanine-glansmiddel dient ongeveer 35 tot ongeveer 80 gew.% van het gecombineerde gewicht . van de twee toegepaste glansmiddelen uit te maken. Een bijzonder bevredigende combinatie omvat Methic Turquoise als het gesubstitueerde ftalo-25 cyanine-glasmiddel in een concentratie van 3 mg/1 in combinatie met een apo safranine-glansmiddel voorgesteld door formule A, waarin R ethyl omvat, dat tevens in een concentratie van 3 mg/1 aanwezig is.The combined brighteners of formula A and the substituted phthalocyanine radical brightener are used at bath concentrations from about 0.0005 g / L to about 1 g / L with concentrations from about 0.002 g / L to about 0.01 g / 1 are preferred. The substituted phthalocyanine brightener serves from about 35% to about 80% by weight of the combined weight. of the two brighteners used. A particularly satisfactory combination includes Methic Turquoise as the substituted phthalo-25 cyanine glass agent at a concentration of 3 mg / l in combination with an apo safranine brightener represented by formula A, wherein R includes ethyl, which is also at a concentration of 3 mg / 1 is present.
Behalve de gesubstitueerde ftalocyanine- en apo safra-nine-glasmiddelen is het voordelig gebleken tenminste een extra glans-30 middel van in de techniek bekende typen toe te voegen om de glans, duc-tiliteit en spreiding van het elektrolytisch neergeslagen koper verder te verbeteren. Dergelijke extra glansmiddelen omvatten polyether-verbindingen en organische sulfide- en disulfideverbindingen.In addition to the substituted phthalocyanine and apo safra-nine glazing agents, it has been found to be advantageous to add at least one additional brightener of art-known types to further improve the gloss, ductility and spread of the electrolytically deposited copper. Such additional brighteners include polyether compounds and organic sulfide and disulfide compounds.
De voorkeurs-organische polyetherverbindingen zijn 35 badoplosbare en verenigbare polyethers die tenminste 4 etherzuurstofatomen bevatten, bij een gemiddeld molecuulgewicht van ongeveer 180 tot 8401841 5 1.000.000. Bijzonder bevredigende resultaten zijn verkregen met polypro-pyleen- en polyethyleenglycolen met inbegrip van mengsels van de voor-noemde, met een gemiddeld molecuulgewicht van ongeveer 600 tot ongeveer 6000, alsmede gealkoxyleerde aromatische alcoholen met een mole-5 cuulgewicht van ongeveer 300 tot 2500. Voorbeelden van dergelijke polyether-glansmiddelen die bij voorkeur worden toegepast zijn polyethyleenglycolen met een gemiddeld molecuulgewicht van ongeveer 400 tot ongeveer 1.000.000; geëthoxyleerde naftolen met 5-45 mol ethyleen-oxydegroepen; gepropoxyleerde naftolen met 5-15 mol propyleenoxyde-10 groepen; geêthoxyleerd nonylfenol met 5-30 mol ethyleenoxydegroepen; propyleenglycolen met een gemiddeld molecuulgewicht van ongeveer 350 tot ongeveer 1000; blokpolymeren van polyoxyethyleen- en polyoxypropy-leenglycolen met een gemiddeld molecuulgewicht van ongeveer 350 tot 250.000; geëthoxyleerde fenolen met 5-100 mol ethyleenoxydegroepen; 15 gepropoxyleerde fenolen met 5-15 mol propyleenoxydegroepen, alsmede ethyleendiamineblokpolymeren met een molecuulgewicht van ongeveer 1600 tot ongeveer 30.000. Andere polyetherverbindingen die in de onderhavige werkwijze bruikbaar zijn worden beschreven in het Amerikaanse octrooi-schrift 4.272.335, waarvan de beschrijving hierin als referentie wordt 20 opgenomen.The preferred organic polyether compounds are bath-soluble and compatible polyethers containing at least 4 ether oxygen atoms, with an average molecular weight of about 180 to 8401841 1,000,000. Particularly satisfactory results have been obtained with polypropylene and polyethylene glycols, including mixtures of the foregoing, with an average molecular weight of about 600 to about 6000, as well as alkoxylated aromatic alcohols with a molecular weight of about 300 to 2500. Examples such preferred polyether brighteners are polyethylene glycols having an average molecular weight of about 400 to about 1,000,000; ethoxylated naphthols with 5-45 moles of ethylene oxide groups; propoxylated naphthols with 5-15 moles of propylene oxide-10 groups; ethoxylated nonylphenol with 5-30 moles of ethylene oxide groups; propylene glycols with an average molecular weight of about 350 to about 1000; block polymers of polyoxyethylene and polyoxypropylene glycols having an average molecular weight of about 350 to 250,000; ethoxylated phenols with 5-100 moles of ethylene oxide groups; Propoxylated phenols with 5-15 moles of propylene oxide groups, as well as ethylene diamine block polymers having a molecular weight from about 1600 to about 30,000. Other polyether compounds useful in the present process are described in U.S. Patent 4,272,335, the disclosure of which is incorporated herein by reference.
De polyether-glansmiddelen worden toegepast in een hoeveelheid van ongeveer 0,001 tot ongeveer 5 g/1, waarbij de hoge moleculaire polyethers meestal bij de lagere concentraties worden toegepast.The polyether brighteners are used in an amount from about 0.001 to about 5 g / l, with the high molecular weight polyethers usually being used at the lower concentrations.
Organische sulfiden-glansmiddelen die in de werkwijze 25 vein de uitvinding bruikbaar zijn omvatten verschillende sulfonaat-organische sulfideverbindingen zoals beschreven in het Amerikaanse octrooischrift 3.267.010, in het bijzonder in tabel I daarvan, waarvan de beschrijving hierin als referentie wordt opgenomen; organische zwavel-verbindingen als beschreven in het Amerikaanse octrooischrift 30 4.181.582, in het bijzonder in tabel XII daarvan, waarvan de beschrijving hierin als referentie wordt opgenomen; en de organische polysulfide-verbindingen beschreven in het Amerikaanse octrooischrift 3.328.273, in het bijzonder in tabel I daarvan, waarvan de beschrijving hierin als referentie wordt opgenomen. Organische sulfideverbindingen die sul-35 fonzuur- of fosfonzuurgroepen bevatten kunnen tevens verschillende andere substituentgroepen bevatten, zoals methyl, chloor, broom, methoxy, ethoxy, 8401841 “ Λ.Organic sulfide brighteners useful in the method of the invention include various sulfonate organic sulfide compounds as disclosed in U.S. Patent 3,267,010, particularly in Table I thereof, the disclosure of which is incorporated herein by reference; organic sulfur compounds as disclosed in U.S. Patent No. 30 4,181,582, particularly in Table XII thereof, the disclosure of which is incorporated herein by reference; and the organic polysulfide compounds disclosed in U.S. Patent 3,328,273, particularly in Table I thereof, the disclosure of which is incorporated herein by reference. Organic sulfide compounds containing sulfonic acid or phosphonic acid groups may also contain various other substituent groups, such as methyl, chlorine, bromine, methoxy, ethoxy, 8401841 ”Λ.
s·s
DD
carboxy of hydroxy, in het bijzonder bij de aromatische en heterocyclische sulfide-sulfonzuren of fosfonzuren. Dergelijke verbindingen kunnen als de vrije zuren, de alkalimetaalzbuten, de organische aminezouten, enz. worden toegepast.carboxy or hydroxy, especially with the aromatic and heterocyclic sulfide sulfonic or phosphonic acids. Such compounds can be used as the free acids, the alkali metal butts, the organic amine salts, etc.
5 Andere geschikte organische divalente zwavelverbinding- en die geschikt zijn omvatten HC^P-iCH^-S-S-iCH^-PC^H, alsmede mer-captanen, thiocarbamaten, thiolcarbamaten, thioxanthaten en thiocarbo-naten die tenminste één sulfonzuur of fosfonzuurgroep bevatten.Other suitable organic divalent sulfur compounds which are suitable include HCl 4 -CHCH -S-S-CHCH-PCH, as well as mercaptans, thiocarbamates, thiol carbamates, thioxanthates and thiocarbonates containing at least one sulfonic acid or phosphonic acid group.
Een bijzondere voorkeursgroep van organische divalente 10 zwavelverbindingen als beschreven in het Amerikaanse octrooischrift 3.328.273 zijn de organische polysulfide-verbindingen met de formule XRj-(S)nR2S03H of XRj-(S)nR2PO.jH, waarin R^ en R2 gelijleof verschillende alkyleengroepen zijn die ongeveer 1-6 koolstof atomen bevatten, X waterstof, SO^H of PO^H is en n een getal is van ongeveer 2-5. Deze 15 organische divalente zwavelverbindingen zijn alifatische polysulfiden waarin tenminste twee divalente zwavelatomen vicinaal zijn en waarbij het molecuul tenminste een of twee eindstandige sulfonzuur- of fosfon-zuurgroepen bevat. Het alkyleendeel van het molecuul kan net groepen zoals methyl, ethyl, chloor, broom, ethoxy, hydroxy en dergelijke zijn 20 gesubstitueerd. Deze verbindingen kunnen als vrije zuren of als de alkali-metaal- of aminezouten worden toegevoegd.A particularly preferred group of organic divalent sulfur compounds as described in U.S. Pat. No. 3,328,273 are the organic polysulfide compounds of the formula XRj- (S) nR2SO3H or XRj- (S) nR2PO.jH, wherein R2 and R2 are different alkylene groups are containing about 1-6 carbon atoms, X is hydrogen, SO ^ H or PO ^ H and n is a number of about 2-5. These organic divalent sulfur compounds are aliphatic polysulfides in which at least two divalent sulfur atoms are vicinal and wherein the molecule contains at least one or two terminal sulfonic or phosphonic acid groups. The alkylene portion of the molecule can be substituted with groups such as methyl, ethyl, chlorine, bromine, ethoxy, hydroxy and the like. These compounds can be added as free acids or as the alkali metal or amine salts.
Het organische sulfide-glansmiddel of mengsel van verbindingen is in de elektrolyt aanwezig in een hoeveelheid van ongeveer 0,0005 tot ongeveer 1 g/1.The organic sulfide brightener or mixture of compounds is present in the electrolyte in an amount from about 0.0005 to about 1 g / l.
25 Volgens de werkwijzeaspecten van de onderhavige uit vinding wordt een waterige zure koperelektrolyt met de voornoemde samenstelling toegepast, waarin een elektrolytisch geleidend substraat wordt ondergedompeld dat gedurende een bepaalde tijdsperiode om de gewenste dikte van de koperlaag daarop af te zetten kathodisch wordt ge-30 laden. Gedurende de elektrolytische bekledingsbehandeling wordt het bad ingesteld op een temperatuur van ongeveer 15 tot aan ongeveer 50°C terwijl de kathodestroomdichtheden variëren van slechts 0,05 ampère per vierkante decimeter tot aan waarden van 43 ampère per vierkante decimeter, maar bij voorkeur zijn zij ongeveer 1 tot ongeveer 5,4 ampère per 35 vierkante decimeter.According to the process aspects of the present invention, an aqueous acidic copper electrolyte of the aforementioned composition is used, in which an electrolytically conductive substrate is immersed which is cathodically charged over a period of time to deposit the desired thickness of the copper layer thereon. During the electrolytic coating treatment, the bath is set at a temperature from about 15 to about 50 ° C while the cathode current densities range from only 0.05 amperes per square decimeter to values of 43 amperes per square decimeter, but preferably they are about 1 to about 5.4 amps per 35 square decimeters.
Teneinde de onderhavige uitvinding verder te illustreren 8 4 0 1 8 4 1 7 worden de nu volgende typerende voorbeelden gegeven. Deze dienen alleen ter illustratie en zijn niet als beperkend bedoeld.In order to further illustrate the present invention, the following typical examples are given. These are for illustrative purposes only and are not intended to be limiting.
Voorbeeld IExample I
Er werd een waterige zure koperelektrolyt bereid die 5 ongeveer 165 tot ongeveer 225 g/1 kopersulfaat-pentahydraat, ongeveer 42 tot ongeveer 75 g/1 zwavelzuur en ongeveer 0,04 tot ongeveer 0,1 g/1 chloride-ionen bevat. Aan de voomoemde waterige oplossing werd 3 mg/1 Methic Turquoise, dat het ftalocyanine-glansmiddel omvatte, toegevoegd alsmede 3 mg/1 diëthyl sapo safranine. Als verdere glansmiddelen bevat-10 te het bad 50 mg/1 polypropyleenglycol met een gemiddeld molecuul- gewicht van 700 en 20 mg/1 bis (3-sulfopropyl-disulfide-dinatriumzout).An aqueous acidic copper electrolyte containing about 165 to about 225 g / l copper sulfate pentahydrate, about 42 to about 75 g / l sulfuric acid and about 0.04 to about 0.1 g / l chloride ion was prepared. To the aforementioned aqueous solution, 3 mg / l of Methic Turquoise, which included the phthalocyanine brightener, was added as well as 3 mg / l of diethyl sapo safranine. As further brighteners, the bath contains 50 mg / l polypropylene glycol with an average molecular weight of 700 and 20 mg / l bis (3-sulfopropyl disulfide disodium salt).
Door elektrolyse van het bad bij een stroomdichtheid van ongeveer 0,05 tot ongeveer 43 ampère per vierkante decimeter bij een temperatuur van ongeveer 21 eC tot 27°C verkreeg men bijzonder goed egale, 15 fijnkorrelige koperbekledingen zonder fysische gebreken.Electrolysis of the bath at a current density of about 0.05 to about 43 amperes per square decimeter at a temperature of about 21 ° C to 27 ° C gave particularly good uniform fine-grain copper coatings without physical defects.
Voorbeeld XIExample XI
Er werd een waterige zure koperelektrolyt bereid die ongeveer 165 tot ongeveer 225 g/1 kopersulfaat-pentahydraat, ongeveer 42 tot ongeveer 75 g/1 zwavelzuur en ongeveer 0,04 tot ongeveer 0,1 g/1 20 chloride-ionen bevatte. Aan de voomoemde waterige oplossing werd 3 mg/1 Methic Turquoise, dat het ftalocyanine-glansmiddel bevatte, toegevoegd tezamen met 60 mg/1 van een blokpolymeer van ethyleenpropyleenoxyde (molecuulgewicht 3000), 20 mg/1 bis (3-sulfopropyl-disulfide-dinatrium-zout) en 1,5 mg/1 van het reactieprodukt van polyethyleenimine (mole-25 cuulgewicht 600) met benzylchloride als extra glansmiddelen..An aqueous acidic copper electrolyte containing about 165 to about 225 g / l copper sulfate pentahydrate, about 42 to about 75 g / l sulfuric acid and about 0.04 to about 0.1 g / l chloride ions was prepared. To the aforementioned aqueous solution, 3 mg / l of Methic Turquoise containing the phthalocyanine brightener was added along with 60 mg / l of a block polymer of ethylene propylene oxide (molecular weight 3000), 20 mg / l bis (3-sulfopropyl disulfide disodium) salt) and 1.5 mg / l of the reaction product of polyethyleneimine (molecular weight 600) with benzyl chloride as additional brighteners.
Door elektrolyse van het bad bij een temperatuur van ongeveer 21 tot ongeveer 27°C en bij stroomdichtheden van ongeveer 2,1 tot ongeveer 8,5 ampère per vierkante decimeter verkrijgt men glanzende gespreide koperafzettingen. Door verdere toevoeging van 3 mg/1 diëthyl-30 apo safranine aan de elektrolyt verkreeg men een zeer opvallende verbetering in de spreidingseigenschappen van de afzetting waarbij tevens de glans in de lage stroomdichtheidsgebieden van de proef panelen, onder toepassing van dezelfde galvaniseringsparameters, aanzienlijk werd verbeterd.Electrolysis of the bath at a temperature of from about 21 to about 27 ° C and at current densities from about 2.1 to about 8.5 amperes per square decimeter gives shiny spread copper deposits. By further adding 3 mg / l diethyl-30 apo safranine to the electrolyte, a very marked improvement in the spreading properties of the deposit was obtained, while also significantly improving the gloss in the low current density areas of the test panels, using the same galvanizing parameters. .
35 Voorbeeld IIIExample III
Er werd een waterige zure koperelektrolyt bereid die 8401841 8 ongeveer 165 tot ongeveer 250 g/1 kopersulfaat-pentahydraat, ongeveer 42 tot ongeveer 75 g/1 zwavelzuur en ongeveer 0,04 tot ongeveer 0,1 g/1 chloride-ionen bevatte. Aan de voomoemde waterige oplossing werd 2 mg/1 diëthyl apo safranine toegevoegd gecombineerd met extra glansmiddelen be-5 staande uit 20 mg/1 bis (3-sulfopropyl-disulfide-dinatriumzout), 200 mg/1 polyethyleenoxyde (molecuulgewicht 6000) en 1,5 mg/1 van een reactie-produkt van polyethyleen,imlne (molecuulgewicht 600) omgezet met benzyl-chloride.An aqueous acidic copper electrolyte containing about 40 to about 250 g / l copper sulfate pentahydrate, about 42 to about 75 g / l sulfuric acid and about 0.04 to about 0.1 g / l chloride ions was prepared. To the aforementioned aqueous solution, 2 mg / l diethyl apo safranin was added combined with additional brighteners consisting of 20 mg / l bis (3-sulfopropyl disulfide disodium salt), 200 mg / l polyethylene oxide (molecular weight 6000) and 1. 5 mg / l of a reaction product of polyethylene, imine (molecular weight 600) reacted with benzyl chloride.
De voornoemde elektrolyt produceerde een glanzende, 10 gespreide koperafzetting bij bekleding op een J-vormig proefpaneel bij een gemiddelde stroomdichtheid van ongeveer 5,4 ampère per vierkante decimeter gedurende een periode van 15 minuten maar in het lage stroomdichtheidsgebied geeft de afzetting strepen. Door toevoeging van 3 mg/1 Methic Turquoise, wat het gesubstitueerde ftalocyanine-radicaal-15 glansmiddel bevatte, aan de elektrolyt werden de strepen in het lage stroomdichtheidsgebied van het J-type proefpaneel dat onder dezelfde omstandigheden elektrolyt!sch werd bekleed verwijderd, zonder verlies aan glans en spreiding van de koperafzetting, 84 01 8 4 1The aforementioned electrolyte produced a shiny, spread copper deposit on coating on a J-shaped test panel at an average current density of about 5.4 amps per square decimeter over a period of 15 minutes but in the low current density range, the deposit streaked. By adding 3 mg / l Methic Turquoise, which contained the substituted phthalocyanine radical-15 brightener, to the electrolyte, the streaks in the low current density region of the J-type test panel electrolytically coated under the same conditions were removed without loss of gloss and dispersion of the copper deposit, 84 01 8 4 1
Claims (18)