MX360510B - Lamina de acero galvanizado por inmersion en caliente, de alta resistencia, que tiene excelente resistencia a la fractura retardada, y metodo para producir la misma. - Google Patents

Lamina de acero galvanizado por inmersion en caliente, de alta resistencia, que tiene excelente resistencia a la fractura retardada, y metodo para producir la misma.

Info

Publication number
MX360510B
MX360510B MX2014003793A MX2014003793A MX360510B MX 360510 B MX360510 B MX 360510B MX 2014003793 A MX2014003793 A MX 2014003793A MX 2014003793 A MX2014003793 A MX 2014003793A MX 360510 B MX360510 B MX 360510B
Authority
MX
Mexico
Prior art keywords
steel sheet
particle size
galvanized steel
dip galvanized
fracture resistance
Prior art date
Application number
MX2014003793A
Other languages
English (en)
Other versions
MX2014003793A (es
Inventor
Kuwayama Takuya
Yasui Takeshi
Kawata Hiroyuki
Maruyama Naoki
Minami Akinobu
Murasato Akinobu
Ban Hiroyuki
Hiramatsu Kaoru
Original Assignee
Nippon Steel & Sumitomo Metal Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Steel & Sumitomo Metal Corp filed Critical Nippon Steel & Sumitomo Metal Corp
Publication of MX2014003793A publication Critical patent/MX2014003793A/es
Publication of MX360510B publication Critical patent/MX360510B/es

Abstract

Una capa enchapada de zinc por inmersión en caliente o una capa aleada, enchapada en zinc por inmersión en caliente, se forma sobre la superficie de una lámina de acero base que comprende, en términos de fracciones de volumen, 40 a 90% de la fase de ferrita, y no más de 5% de una fase de austenita retenida, y la proporción de la ferrita no recristalizada con respecto a la fase total de ferrita no es más de 50% en términos de fracción en volumen. Además, la proporción de tamaño de partícula de los granos de cristales en la fase de ferrita, que se obtiene dividiendo el tamaño promedio de partícula en la dirección del laminado por el tamaño promedio de partícula en la dirección de anchura de la lámina es 0.75 a 1.33; la proporción de longitud de las estructuras duras dispersadas en formas de islas, que se obtiene dividiendo la longitud promedio en la dirección de laminado por la longitud promedio en la dirección de la anchura de la lámina, es 0.75 a 1.33; y la proporción de aspecto promedio de inclusiones es no más de 5.0.
MX2014003793A 2011-09-30 2012-09-28 Lamina de acero galvanizado por inmersion en caliente, de alta resistencia, que tiene excelente resistencia a la fractura retardada, y metodo para producir la misma. MX360510B (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2011218776 2011-09-30
PCT/JP2012/075108 WO2013047760A1 (ja) 2011-09-30 2012-09-28 耐遅れ破壊特性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法

Publications (2)

Publication Number Publication Date
MX2014003793A MX2014003793A (es) 2014-07-10
MX360510B true MX360510B (es) 2018-11-05

Family

ID=47995785

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2014003793A MX360510B (es) 2011-09-30 2012-09-28 Lamina de acero galvanizado por inmersion en caliente, de alta resistencia, que tiene excelente resistencia a la fractura retardada, y metodo para producir la misma.

Country Status (14)

Country Link
US (1) US8993120B2 (es)
EP (1) EP2762583B1 (es)
JP (1) JP5352793B2 (es)
KR (1) KR101605980B1 (es)
CN (1) CN103842543B (es)
BR (1) BR112014007483B1 (es)
CA (1) CA2850462C (es)
ES (1) ES2706996T3 (es)
MX (1) MX360510B (es)
PL (1) PL2762583T3 (es)
RU (1) RU2585889C2 (es)
TW (1) TWI499675B (es)
WO (1) WO2013047760A1 (es)
ZA (1) ZA201402351B (es)

Families Citing this family (49)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
BR112014007545B1 (pt) * 2011-09-30 2019-05-14 Nippon Steel & Sumitomo Metal Corporation Chapa de aço galvanizada por imersão a quente de alta resistência, chapa de aço galvanizada por imersão a quente de alta resistência ligada e método para produção das mesmas.
JP5304924B2 (ja) * 2011-12-27 2013-10-02 Ｊｆｅスチール株式会社 脆性亀裂伝播停止特性に優れた構造用高強度厚鋼板およびその製造方法
WO2014156188A1 (ja) * 2013-03-29 2014-10-02 Ｊｆｅスチール株式会社 水素用鋼構造物ならびに水素用蓄圧器および水素用ラインパイプの製造方法
JP6128223B2 (ja) * 2013-08-26 2017-05-17 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板及びその製造方法
JP5817804B2 (ja) * 2013-10-22 2015-11-18 Ｊｆｅスチール株式会社 伸びの面内異方性が小さい高強度鋼板およびその製造方法
JP5817805B2 (ja) * 2013-10-22 2015-11-18 Ｊｆｅスチール株式会社 伸びの面内異方性が小さい高強度鋼板およびその製造方法
KR101585744B1 (ko) 2013-12-26 2016-01-14 주식회사 포스코 표면품질 및 내지연파괴 특성이 우수한 아연도금강판 및 그 제조방법
JP5888471B1 (ja) 2014-03-31 2016-03-22 Ｊｆｅスチール株式会社 高降伏比高強度冷延鋼板及びその製造方法
EP3153598B1 (en) * 2014-07-14 2020-09-09 Nippon Steel Corporation Hot-rolled steel sheet
MX2017005567A (es) 2014-10-30 2017-06-23 Jfe Steel Corp Lamina de acero de alta resistencia, lamina de acero galvanizada por inmersion en caliente de alta resistencia, lamina de acero recubierta de aluminio por inmersion en caliente de alta resistencia, y lamina de acero electrogalvanizada de alta resistencia, y metodos para fabricacion de las mismas.
EP3216886A4 (en) 2014-11-05 2018-04-11 Nippon Steel & Sumitomo Metal Corporation Hot-dip galvanized steel sheet
PL3216892T3 (pl) * 2014-11-05 2019-12-31 Nippon Steel Corporation Blacha stalowa cienka ocynkowana ogniowo
ES2761600T3 (es) * 2014-11-05 2020-05-20 Nippon Steel Corp Lámina de acero galvanizada en caliente
CN104532126B (zh) * 2014-12-19 2017-06-06 宝山钢铁股份有限公司 一种低屈强比超高强度热轧q&p钢及其制造方法
KR101569508B1 (ko) * 2014-12-24 2015-11-17 주식회사 포스코 굽힘 특성이 우수한 hpf 성형부재 및 그 제조방법
CN107532266B (zh) 2015-04-22 2020-02-14 日本制铁株式会社 镀覆钢板
WO2017009936A1 (ja) * 2015-07-13 2017-01-19 新日鐵住金株式会社 鋼板、溶融亜鉛めっき鋼板、及び合金化溶融亜鉛めっき鋼板、並びにそれらの製造方法
BR112018000090A2 (pt) 2015-07-13 2018-08-28 Nippon Steel & Sumitomo Metal Corporation chapa de aço, chapa de aço galvanizada por imersão a quente, chapa de aço galvanizada por imersão a quente em liga e métodos de produção para as mesmas
JP6536294B2 (ja) * 2015-08-31 2019-07-03 日本製鉄株式会社 溶融亜鉛めっき鋼板、合金化溶融亜鉛めっき鋼板、およびそれらの製造方法
KR101696121B1 (ko) 2015-12-23 2017-01-13 주식회사 포스코 내수소지연파괴특성, 내박리성 및 용접성이 우수한 열간성형용 알루미늄-철 합금 도금강판 및 이를 이용한 열간성형 부재
BR112018012606A2 (pt) * 2016-02-25 2018-12-04 Nippon Steel & Sumitomo Metal Corporation chapa de aço galvanizada por imersão a quente de alta resistência com excelente resistência ao destacamento por impacto e resistência à corrosão em seção trabalhada
JP7186694B2 (ja) 2016-05-10 2022-12-09 ユナイテッド ステイツ スチール コーポレイション 高強度鋼製品及び該製品を製造するためのアニーリング工程
US11993823B2 (en) 2016-05-10 2024-05-28 United States Steel Corporation High strength annealed steel products and annealing processes for making the same
US11560606B2 (en) 2016-05-10 2023-01-24 United States Steel Corporation Methods of producing continuously cast hot rolled high strength steel sheet products
CN110121568B (zh) * 2016-12-27 2021-02-19 杰富意钢铁株式会社 高强度镀锌钢板及其制造方法
JP6384641B1 (ja) 2017-02-13 2018-09-05 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
EP3572546B1 (en) * 2017-03-13 2022-02-09 JFE Steel Corporation High-strength cold-rolled steel sheet and method for manufacturing the same
US11186900B2 (en) 2017-03-13 2021-11-30 Jfe Steel Corporation High-strength cold rolled steel sheet and method for manufacturing the same
CN108977726B (zh) * 2017-05-31 2020-07-28 宝山钢铁股份有限公司 一种抗延迟开裂的马氏体超高强度冷轧钢带及其制造方法
KR102010048B1 (ko) 2017-06-01 2019-10-21 주식회사 포스코 도장 밀착성과 도장 후 내식성이 우수한 열간 프레스 성형 부재용 강판 및 그 제조방법
RU2650951C1 (ru) * 2017-11-27 2018-04-18 Юлия Алексеевна Щепочкина Сталь
EP3725904B1 (en) 2017-12-15 2024-03-06 Nippon Steel Corporation Steel sheet, hot-dip zinc-coated steel sheet, and alloyed hot-dip zinc-coated steel sheet
WO2019122965A1 (en) * 2017-12-19 2019-06-27 Arcelormittal Cold rolled and coated steel sheet and a method of manufacturing thereof
WO2019122957A1 (en) * 2017-12-19 2019-06-27 Arcelormittal A coated steel substrate
EP3715493A4 (en) * 2017-12-27 2020-11-25 JFE Steel Corporation HIGH STRENGTH STEEL SHEET AND METHOD OF MANUFACTURING ITEM
TWI651418B (zh) * 2018-03-30 2019-02-21 日商新日鐵住金股份有限公司 合金化熔融鍍鋅鋼板
EP3757243B1 (en) * 2018-03-30 2022-05-04 JFE Steel Corporation High-strength galvanized steel sheet, high strength member, and method for manufacturing the same
CN111902554B (zh) * 2018-03-30 2022-03-29 日本制铁株式会社 钢板及其制造方法
WO2020079926A1 (ja) * 2018-10-18 2020-04-23 Ｊｆｅスチール株式会社 高延性高強度電気亜鉛系めっき鋼板およびその製造方法
KR102153197B1 (ko) * 2018-12-18 2020-09-08 주식회사 포스코 가공성이 우수한 냉연강판, 용융아연도금강판 및 이들의 제조방법
KR102544884B1 (ko) 2018-12-26 2023-06-19 제이에프이 스틸 가부시키가이샤 고강도 용융 아연 도금 강판 및 그의 제조 방법
WO2020184154A1 (ja) * 2019-03-11 2020-09-17 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
CN110057650B (zh) * 2019-05-20 2022-03-15 常德力元新材料有限责任公司 钢带晶粒的评价方法
DE102019130381A1 (de) * 2019-11-11 2021-05-12 Benteler Automobiltechnik Gmbh Kraftfahrzeugbauteil mit gesteigerter Festigkeit
KR102305748B1 (ko) * 2019-12-18 2021-09-27 주식회사 포스코 내부식성이 우수한 용융 합금도금 강재 및 그 제조방법
JP7425359B2 (ja) 2020-04-07 2024-01-31 日本製鉄株式会社 鋼板
KR20230160382A (ko) * 2021-04-27 2023-11-23 닛폰세이테츠 가부시키가이샤 강판 및 도금 강판
CN115537681B (zh) * 2021-06-30 2023-10-17 宝山钢铁股份有限公司 高韧性、低屈强比及低纵横向强度各向异性500MPa级钢板及其制造方法
CN115029630B (zh) * 2022-05-23 2023-06-02 武汉钢铁有限公司 一种提高1800MPa级抗延迟开裂热成形钢及生产方法

Family Cites Families (24)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP3247907B2 (ja) 1992-11-05 2002-01-21 川崎製鉄株式会社 延性と耐遅れ破壊特性に優れた高強度冷延鋼板およびその製造方法
JP3477955B2 (ja) * 1995-11-17 2003-12-10 Ｊｆｅスチール株式会社 極微細組織を有する高張力熱延鋼板の製造方法
TW565621B (en) * 2000-05-26 2003-12-11 Jfe Steel Corp Cold-rolled steel sheet and galvanized steel sheet having strain age hardenability property and method for producing the same
FR2844281B1 (fr) * 2002-09-06 2005-04-29 Usinor Acier a tres haute resistance mecanique et procede de fabrication d'une feuille de cet acier revetue de zinc ou d'alliage de zinc
JP4317384B2 (ja) 2003-04-28 2009-08-19 新日本製鐵株式会社 耐水素脆化、溶接性および穴拡げ性に優れた高強度亜鉛めっき鋼板とその製造方法
JP4384523B2 (ja) 2004-03-09 2009-12-16 新日本製鐵株式会社 形状凍結性に極めて優れた低降伏比型高強度冷延鋼板およびその製造方法
JP4555694B2 (ja) * 2005-01-18 2010-10-06 新日本製鐵株式会社 加工性に優れる焼付け硬化型熱延鋼板およびその製造方法
JP4741376B2 (ja) * 2005-01-31 2011-08-03 新日本製鐵株式会社 外観が良好な高強度合金化溶融亜鉛めっき鋼板及びその製造方法と製造設備
WO2007086158A1 (ja) 2006-01-30 2007-08-02 Nippon Steel Corporation 成形性及びめっき性に優れた高強度溶融亜鉛めっき鋼板及び高強度合金化溶融亜鉛めっき鋼板ならびにそれらの製造方法及び製造装置
JP4781836B2 (ja) 2006-02-08 2011-09-28 新日本製鐵株式会社 耐水素脆性に優れた超高強度鋼板とその製造方法及び超高強度溶融亜鉛めっき鋼板の製造方法並びに超高強度合金化溶融亜鉛めっき鋼板の製造方法
JP5194878B2 (ja) * 2007-04-13 2013-05-08 Ｊｆｅスチール株式会社 加工性および溶接性に優れる高強度溶融亜鉛めっき鋼板およびその製造方法
WO2009119751A1 (ja) * 2008-03-27 2009-10-01 新日本製鐵株式会社 成形性と溶接性に優れた高強度冷延鋼板、高強度亜鉛めっき鋼板、高強度合金化溶融亜鉛めっき鋼板、及びそれらの製造方法
JP4712882B2 (ja) 2008-07-11 2011-06-29 株式会社神戸製鋼所 耐水素脆化特性および加工性に優れた高強度冷延鋼板
JP5131844B2 (ja) * 2008-08-12 2013-01-30 新日鐵住金株式会社 熱間プレス用熱延鋼板およびその製造方法ならびに熱間プレス鋼板部材の製造方法
JP5195413B2 (ja) 2008-12-26 2013-05-08 新日鐵住金株式会社 曲げ加工性及び靭性の異方性に優れた高強度熱延鋼板及びその製造方法
JP2010168651A (ja) 2008-12-26 2010-08-05 Nakayama Steel Works Ltd 高強度熱延鋼板およびその製造方法
JP5740847B2 (ja) * 2009-06-26 2015-07-01 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板およびその製造方法
JP5696359B2 (ja) * 2009-07-08 2015-04-08 新日鐵住金株式会社 高強度鋼板およびその溶鋼の溶製方法
JP5644095B2 (ja) 2009-11-30 2014-12-24 新日鐵住金株式会社 延性及び耐遅れ破壊特性の良好な引張最大強度９００ＭＰａ以上を有する高強度鋼板および高強度冷延鋼板の製造方法、高強度亜鉛めっき鋼板の製造方法
JP5499663B2 (ja) * 2009-11-30 2014-05-21 新日鐵住金株式会社 機械切断特性に優れた引張最大強度９００ＭＰａ以上の高強度冷延鋼板及びその製造方法、並びに、高強度亜鉛めっき鋼板及びその製造方法
JP5370104B2 (ja) 2009-11-30 2013-12-18 新日鐵住金株式会社 耐水素脆化特性に優れた引張最大強度９００ＭＰａ以上の高強度鋼板および高強度冷延鋼板の製造方法、高強度亜鉛めっき鋼板の製造方法
JP5434537B2 (ja) 2009-12-03 2014-03-05 新日鐵住金株式会社 溶接性に優れた高Ｓｉ含有合金化溶融めっき鋼板およびその製造方法
JP5786317B2 (ja) * 2010-01-22 2015-09-30 Ｊｆｅスチール株式会社 材質安定性と加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP2011153349A (ja) 2010-01-27 2011-08-11 Sumitomo Metal Ind Ltd 外観特性に優れた合金化溶融亜鉛めっき鋼板およびその製造方法

Also Published As

Publication number Publication date
TWI499675B (zh) 2015-09-11
CA2850462C (en) 2016-10-11
EP2762583B1 (en) 2018-11-07
PL2762583T3 (pl) 2019-04-30
US20140234659A1 (en) 2014-08-21
ZA201402351B (en) 2015-03-25
EP2762583A1 (en) 2014-08-06
US8993120B2 (en) 2015-03-31
EP2762583A4 (en) 2015-12-02
MX2014003793A (es) 2014-07-10
BR112014007483A2 (pt) 2017-04-04
KR101605980B1 (ko) 2016-03-23
ES2706996T3 (es) 2019-04-02
JPWO2013047760A1 (ja) 2015-03-30
CA2850462A1 (en) 2013-04-04
JP5352793B2 (ja) 2013-11-27
RU2014117668A (ru) 2015-11-10
KR20140052070A (ko) 2014-05-02
CN103842543B (zh) 2016-01-27
CN103842543A (zh) 2014-06-04
WO2013047760A1 (ja) 2013-04-04
RU2585889C2 (ru) 2016-06-10
TW201331383A (zh) 2013-08-01
BR112014007483B1 (pt) 2019-12-31

Similar Documents

Publication Publication Date Title
MX360510B (es) Lamina de acero galvanizado por inmersion en caliente, de alta resistencia, que tiene excelente resistencia a la fractura retardada, y metodo para producir la misma.
MX2017005507A (es) Hoja de acero galvanizad por inmersion en caliente.
MX2014000917A (es) Lamina de acero laminada en frio de alta resistencia que tiene excelente capacidad de conformacion en formas complejas y capacidad de perforacion de precision y metodo de fabricacion de la misma.
MX2017005591A (es) Hoja de acero galvanizada por inmersion en caliente.
MX2013011863A (es) Hoja de acero laminada en caliente de alta resistencia que tiene excelente capacidad de deformacion local y metodo para fabricar la misma.
MX336096B (es) Lamina de cero laminada en caliente y metodo para producir la misma.
MX2013002906A (es) Lamina de acero de alta resistencia y lamina de acero revestida con zinc de alta resistencia que tiene excelente ductilidad y capacidad de embridado por estiramiento y metodo de fabricacion de las mismas.
MX2019009513A (es) Lamina de acero galvanizada de alta resistencia y metodo para producir la misma.
MX2016011756A (es) Chapa de acero laminado en frio de alta resistencia y chapa de acero galvanizado de alta resistencia que tienen una excelente ductilidad y capacidad de flexion, y metodos para su produccion.
MX2012005996A (es) Acero elaborado por inmersion en caliente y metodo para producirlo.
MX2016007954A (es) Lamina de acero galvanizada de alta resistencia y metodo para la fabricacion de la misma.
MX2018009164A (es) Lamina de acero galvanizado de alta resistencia y alta relacion de rendimiento y metodo para producir la misma.
MX2014009471A (es) Plancha de acero laminada en frio de alta resistencia y proceso para fabricar la misma.
PL2762588T3 (pl) BLACHA STALOWA CIENKA O DUŻEJ WYTRZYMAŁOŚCI CYNKOWANA ZANURZENIOWO NA GORĄCO MAJĄCA DOSKONAŁĄ PODATNOŚĆ NA FORMOWANIE, NISKĄ ANIZOTROPIĘ MATERIAŁU I GRANICZNĄ WYTRZYMAŁOŚĆ NA ROZCIĄGANIE WYNOSZĄCĄ 980 MPa LUB WIĘCEJ, STOPOWA BLACHA STALOWA CIENKA O DUŻEJ WYTRZYMAŁOŚCI CYNKOWANA ZANURZENIOWO NA GORĄCO ORAZ SPOSÓB ICH WYTWARZANIA
MX2018007579A (es) Lamina de acero de alta resistencia y metodo para fabricar la misma.
MX2017005503A (es) Hoja de acero galvanizada por inmersion en caliente.
MY172243A (en) Hot-dip zinc alloy coated steel sheet excellent in coating adhesion, and method for producing the same
MX2018011871A (es) Lamina de acero, lamina de acero recubierta, metodo para producir lamina de acero laminada en caliente, metodo para producir lamina de acero laminada en frio de dureza completa, metodo para producir lamina tratada termicamente, metodo para producir lamina de acero y metodo para producir lamina de acero recubierta.
MX2019009876A (es) Cuerpo estampado en caliente.
MX2015004736A (es) Lamina de acero galvanizada por inmersion en caliente aleada y metodo para manufacturar la misma.
MX2016003143A (es) Laminas de acero galvanizadas por inmersion en caliente y laminas de acero recocidas despues de galvanizadas que tienen buen aspecto y buena adherencia al recubrimiento y metodos para la produccion de las mismas.
MX2018011778A (es) Chapa de acero, chapa de acero revestida, metodo para producir chapa de acero laminada en caliente, metodo para producir chapa de acero muy dura laminada en frio, metodo para producir chapa de acero y metodo para producir chapa de acero revestida.
MX2016012797A (es) Chapa de acero laminada en frio de alta resistencia, chapa de acero galvanizada en baño caliente de alta resistencia y chapa de acero galvanofusionado en baño caliente de alta resistencia que tiene excelente ductilidad, abocardabilidad por estiramiento y soldabilidad.
MX353202B (es) Plancha de acero laminada en frio, plancha de acero chapada y metodo para fabricarla.
MX2019009880A (es) Carroceria de estampado en caliente.

Legal Events

Date Code Title Description
FG Grant or registration