BR112018000090A2 - chapa de aço, chapa de aço galvanizada por imersão a quente, chapa de aço galvanizada por imersão a quente em liga e métodos de produção para as mesmas - Google Patents
chapa de aço, chapa de aço galvanizada por imersão a quente, chapa de aço galvanizada por imersão a quente em liga e métodos de produção para as mesmasInfo
- Publication number
- BR112018000090A2 BR112018000090A2 BR112018000090-6A BR112018000090A BR112018000090A2 BR 112018000090 A2 BR112018000090 A2 BR 112018000090A2 BR 112018000090 A BR112018000090 A BR 112018000090A BR 112018000090 A2 BR112018000090 A2 BR 112018000090A2
- Authority
- BR
- Brazil
- Prior art keywords
- coated carbon
- dip zinc
- hot
- carbon steel
- manufacturing methods
- Prior art date
Abstract
trata-se de uma chapa de aço de acordo com uma modalidade da presente invenção que tem uma composição química predeterminada. a estrutura de uma porção que compreende ¼ da espessura de chapa inclui, expressa como frações de volume, 30 a 70% de martensita temperada e um total de pelo menos 20%, porém, não mais que 70% de ferrita e/ou bainita. a estrutura da porção que compreende ¼ da espessura de chapa inclui, expressa como frações de volume, menos que 10% de austenita retida, não mais que 10% de martensita fresca e não mais que 10% de pearlita. a fração de volume total de austenita retida, martensita fresca e pearlita na dita estrutura não é mais que 15%. a densidade numérica dos carbonetos à base de ferro que têm um diâmetro longitudinal de pelo menos 5 nm na martensita temperada na porção que compreende ¼ da espessura de chapa é pelo menos 5×107 por mm2. a razão do número de e carbonetos para o número dos carbonetos à base de ferro que têm um diâmetro longitudinal de pelo menos 5 nm na porção que compreende ¼ da espessura de chapa é de pelo menos 20%. a resistência à tração é de pelo menos 780 mpa.
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
PCT/JP2015/070069 WO2017009938A1 (ja) | 2015-07-13 | 2015-07-13 | 鋼板、溶融亜鉛めっき鋼板、及び合金化溶融亜鉛めっき鋼板、並びにそれらの製造方法 |
Publications (1)
Publication Number | Publication Date |
---|---|
BR112018000090A2 true BR112018000090A2 (pt) | 2018-08-28 |
Family
ID=57757132
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
BR112018000090-6A BR112018000090A2 (pt) | 2015-07-13 | 2015-07-13 | chapa de aço, chapa de aço galvanizada por imersão a quente, chapa de aço galvanizada por imersão a quente em liga e métodos de produção para as mesmas |
Country Status (10)
Country | Link |
---|---|
US (1) | US10822672B2 (pt) |
EP (1) | EP3323907B1 (pt) |
JP (1) | JP6460239B2 (pt) |
KR (1) | KR102057946B1 (pt) |
CN (1) | CN107849666B (pt) |
BR (1) | BR112018000090A2 (pt) |
ES (1) | ES2785410T3 (pt) |
MX (1) | MX2018000329A (pt) |
PL (1) | PL3323907T3 (pt) |
WO (1) | WO2017009938A1 (pt) |
Families Citing this family (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
KR102031445B1 (ko) * | 2017-12-22 | 2019-10-11 | 주식회사 포스코 | 내충격특성이 우수한 고강도 강판 및 그 제조방법 |
WO2020262652A1 (ja) * | 2019-06-28 | 2020-12-30 | 日本製鉄株式会社 | 鋼板 |
US20230087014A1 (en) * | 2020-03-16 | 2023-03-23 | Nippon Steel Corporation | Steel sheet |
CN113355602A (zh) * | 2021-06-03 | 2021-09-07 | 全球能源互联网研究院有限公司 | 一种架空导线用芯线材料及其制备方法 |
DE102021121997A1 (de) | 2021-08-25 | 2023-03-02 | Thyssenkrupp Steel Europe Ag | Kaltgewalztes Stahlflachprodukt und Verfahren zu seiner Herstellung |
Family Cites Families (30)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH01230715A (ja) | 1987-06-26 | 1989-09-14 | Nippon Steel Corp | プレス成形性の優れた高強度冷延鋼板の製造方法 |
JPH0733551B2 (ja) | 1989-02-18 | 1995-04-12 | 新日本製鐵株式会社 | 優れた成形性を有する高強度鋼板の製造方法 |
JP2826058B2 (ja) * | 1993-12-29 | 1998-11-18 | 株式会社神戸製鋼所 | 水素脆化の発生しない超高強度薄鋼板及び製造方法 |
JP3406094B2 (ja) | 1994-11-10 | 2003-05-12 | 株式会社神戸製鋼所 | 耐水素脆化特性にすぐれる超高強度薄鋼板の製造方法 |
JP3435035B2 (ja) | 1997-09-24 | 2003-08-11 | 新日本製鐵株式会社 | 加工性およびほうろう密着性に優れた連続鋳造ほうろう用鋼板およびその製造方法 |
JP3527092B2 (ja) | 1998-03-27 | 2004-05-17 | 新日本製鐵株式会社 | 加工性の良い高強度合金化溶融亜鉛めっき鋼板とその製造方法 |
JPH11293383A (ja) | 1998-04-09 | 1999-10-26 | Nippon Steel Corp | 水素性欠陥の少ない厚鋼板およびその製造方法 |
EP1431406A1 (en) * | 2002-12-20 | 2004-06-23 | Sidmar N.V. | A steel composition for the production of cold rolled multiphase steel products |
US8257513B2 (en) | 2007-08-01 | 2012-09-04 | Kobe Steel, Ltd. | High strength steel sheet excellent in bending workability and fatigue strength |
JP5365216B2 (ja) * | 2008-01-31 | 2013-12-11 | Jfeスチール株式会社 | 高強度鋼板とその製造方法 |
KR101243563B1 (ko) * | 2008-03-07 | 2013-03-20 | 가부시키가이샤 고베 세이코쇼 | 냉간 압연 강판 |
JP4712882B2 (ja) | 2008-07-11 | 2011-06-29 | 株式会社神戸製鋼所 | 耐水素脆化特性および加工性に優れた高強度冷延鋼板 |
WO2010109702A1 (ja) * | 2009-03-27 | 2010-09-30 | 株式会社神戸製鋼所 | 冷延鋼板 |
US8128762B2 (en) | 2008-08-12 | 2012-03-06 | Kobe Steel, Ltd. | High-strength steel sheet superior in formability |
JP5359168B2 (ja) | 2008-10-08 | 2013-12-04 | Jfeスチール株式会社 | 延性に優れる超高強度冷延鋼板およびその製造方法 |
BRPI1010678A2 (pt) * | 2009-05-27 | 2016-03-15 | Nippon Steel Corp | chapade aço de alta resistência, chapa de aço banhada a quente e chapa de aço banhada a quente de liga que têm excelentes características de fadiga, alongamento e colisão, e método de fabricação para as ditas chapas de aço |
CN101928875A (zh) | 2009-06-22 | 2010-12-29 | 鞍钢股份有限公司 | 具有良好成形性能的高强度冷轧钢板及其制备方法 |
PL2508640T3 (pl) | 2009-11-30 | 2020-02-28 | Nippon Steel Corporation | BLACHA STALOWA O DUŻEJ WYTRZYMAŁOŚCI I DOSKONAŁEJ ODPORNOŚCI NA KRUCHOŚĆ WODOROWĄ ORAZ WYTRZYMAŁOŚCI NA ROZCIĄGANIE WYNOSZĄCEJ 900 MPa LUB WIĘCEJ I SPOSÓB JEJ WYTWARZANIA |
MX2012008690A (es) | 2010-01-29 | 2012-08-23 | Nippon Steel Corp | Placa de acero y proceso para producir la placa de acero. |
JP4893844B2 (ja) * | 2010-04-16 | 2012-03-07 | Jfeスチール株式会社 | 成形性および耐衝撃性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法 |
ES2617477T3 (es) | 2010-09-16 | 2017-06-19 | Nippon Steel & Sumitomo Metal Corporation | Lámina de acero laminada en frío de alta resistencia con excelente ductilidad y expansibilidad, y lámina de acero galvanizada de alta resistencia, y método para fabricar las mismas |
JP5765116B2 (ja) * | 2010-09-29 | 2015-08-19 | Jfeスチール株式会社 | 深絞り性および伸びフランジ性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法 |
MX366222B (es) | 2011-07-29 | 2019-07-03 | Nippon Steel Corp Star | Laminas de acero de alta resistencia y laminas de acero galvanizadas de alta resistencia con capacidad de fijacion de forma excelente, y metodo para la fabricacion de las mismas. |
BR112014007483B1 (pt) | 2011-09-30 | 2019-12-31 | Nippon Steel & Sumitomo Metal Corp | chapa de aço galvanizado a quente e processo de fabricação da mesma |
JP5569647B2 (ja) | 2011-09-30 | 2014-08-13 | 新日鐵住金株式会社 | 溶融亜鉛めっき鋼板及びその製造方法 |
CA2850195C (en) * | 2011-09-30 | 2016-10-25 | Nippon Steel & Sumitomo Metal Corporation | High-strength hot-dip galvanized steel sheet excellent in impact resistance property and manufacturing method thereof, and high-strength alloyed hot-dip galvanized steel sheet and manufacturing method thereof |
CN103857819B (zh) * | 2011-10-04 | 2016-01-13 | 杰富意钢铁株式会社 | 高强度钢板及其制造方法 |
CN103290307B (zh) | 2012-02-27 | 2016-09-21 | 株式会社神户制钢所 | 耐冲击性优越的高强度钢板及其制造方法 |
KR20150029736A (ko) | 2012-07-31 | 2015-03-18 | 제이에프이 스틸 가부시키가이샤 | 성형성 및 형상 동결성이 우수한 고강도 용융 아연 도금 강판, 그리고 그의 제조 방법 |
JP5632947B2 (ja) | 2012-12-12 | 2014-11-26 | 株式会社神戸製鋼所 | 加工性と低温靭性に優れた高強度鋼板およびその製造方法 |
-
2015
- 2015-07-13 BR BR112018000090-6A patent/BR112018000090A2/pt active Search and Examination
- 2015-07-13 PL PL15898251T patent/PL3323907T3/pl unknown
- 2015-07-13 ES ES15898251T patent/ES2785410T3/es active Active
- 2015-07-13 JP JP2017528042A patent/JP6460239B2/ja active Active
- 2015-07-13 US US15/743,398 patent/US10822672B2/en active Active
- 2015-07-13 MX MX2018000329A patent/MX2018000329A/es unknown
- 2015-07-13 WO PCT/JP2015/070069 patent/WO2017009938A1/ja active Application Filing
- 2015-07-13 EP EP15898251.2A patent/EP3323907B1/en active Active
- 2015-07-13 KR KR1020187000710A patent/KR102057946B1/ko active IP Right Grant
- 2015-07-13 CN CN201580081574.9A patent/CN107849666B/zh active Active
Also Published As
Publication number | Publication date |
---|---|
JP6460239B2 (ja) | 2019-01-30 |
CN107849666B (zh) | 2020-05-12 |
US10822672B2 (en) | 2020-11-03 |
US20180209006A1 (en) | 2018-07-26 |
EP3323907B1 (en) | 2020-03-04 |
EP3323907A4 (en) | 2018-12-12 |
PL3323907T3 (pl) | 2020-07-27 |
CN107849666A (zh) | 2018-03-27 |
ES2785410T3 (es) | 2020-10-06 |
KR102057946B1 (ko) | 2019-12-20 |
MX2018000329A (es) | 2018-03-14 |
KR20180016549A (ko) | 2018-02-14 |
WO2017009938A1 (ja) | 2017-01-19 |
JPWO2017009938A1 (ja) | 2018-03-29 |
EP3323907A1 (en) | 2018-05-23 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
BR112018012681A2 (pt) | chapa de aço de alta resistência e chapa de aço galvanizada de alta resistência | |
BR112018076347A2 (pt) | chapa de aço | |
BR112018000090A2 (pt) | chapa de aço, chapa de aço galvanizada por imersão a quente, chapa de aço galvanizada por imersão a quente em liga e métodos de produção para as mesmas | |
BR112019003791A2 (pt) | chapa de aço laminada a frio e tratada termicamente, junta soldada por pontos de resistência, método para a fabricação de uma chapa de aço laminada a frio e tratada termicamente e processo para a produção de uma junta soldada por pontos de resistência | |
MX2017012194A (es) | Lamina de acero laminada en frio y metodo de fabricacion para la misma. | |
BR112018001133A2 (pt) | chapa de aço com estrutura compósita do tipo de transformação induzida por tensão e método para fabricação da mesma | |
BR112017020003A2 (pt) | membro de folha de aço tratada termicamente e método de produção do mesmo | |
BR112017025366A2 (pt) | ?chapa de aço, método para fabricação de uma chapa laminada a frio e recozida e uso de chapas de aço? | |
BR112016013130A2 (pt) | Folha de aço e método para fabricar uma folha de aço | |
MX2018010467A (es) | Hoja de acero de alta resistencia y metodo para fabricar la misma. | |
BR112018000633A2 (pt) | chapa de aço laminada a quente de alta resistência | |
BR112015002312A2 (pt) | chapa de aço laminada a frio e método para produção da mesma, e elememento conformado por estampagem a quente | |
MX2021004933A (es) | Lamina de acero de alta resistencia y metodo para la fabricacion de la misma. | |
BR112014007432A2 (pt) | folha de aço galvanizada e método de fabricação da mesma | |
BR112018071668A2 (pt) | chapa de aço galvanizada por imersão a quente | |
BR112018013375A2 (pt) | ?chapa de aço e método de fabricação de uma chapa de aço? | |
MX2019007170A (es) | Hoja de acero enrollada en frio, de alta resistencia con alta capacidad de formacion y un metodo para fabricar la misma. | |
MX2018009643A (es) | Lamina de acero de alta resistencia y metodo para la produccion de la misma. | |
BR112015023632B1 (pt) | chapa de aço laminada a quente e método para produção da mesma | |
BR112015032233A2 (pt) | folhas de aço, métodos de fabricação de folhas de aço e veículo | |
BR112017024692A2 (pt) | placa de aço e método de produção da mesma | |
MX2017001529A (es) | Lamina de acero de alta resistencia y metodo de produccion para la misma, y metodo de produccion para lamina de acero galvanizada de alta resistencia. | |
BR112016001258A2 (pt) | Chapa de aço laminada, processo de fabricação de uma chapa de aço, processo de fabricação de uma peça a partir de uma chapa e uso de uma chapa laminada | |
BR112017009762A2 (pt) | aço de baixa liga para tubo de poço de óleo e método de fabricação de tubo de poço de óleo de aço de baixa liga | |
MX2019001760A (es) | Pieza conformada por prensado en caliente. |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
B06U | Preliminary requirement: requests with searches performed by other patent offices: procedure suspended [chapter 6.21 patent gazette] | ||
B25D | Requested change of name of applicant approved |
Owner name: NIPPON STEEL CORPORATION (JP) |
|
B09A | Decision: intention to grant [chapter 9.1 patent gazette] | ||
B11D | Dismissal acc. art. 38, par 2 of ipl - failure to pay fee after grant in time |