PL2762588T3 - BLACHA STALOWA CIENKA O DUŻEJ WYTRZYMAŁOŚCI CYNKOWANA ZANURZENIOWO NA GORĄCO MAJĄCA DOSKONAŁĄ PODATNOŚĆ NA FORMOWANIE, NISKĄ ANIZOTROPIĘ MATERIAŁU I GRANICZNĄ WYTRZYMAŁOŚĆ NA ROZCIĄGANIE WYNOSZĄCĄ 980 MPa LUB WIĘCEJ, STOPOWA BLACHA STALOWA CIENKA O DUŻEJ WYTRZYMAŁOŚCI CYNKOWANA ZANURZENIOWO NA GORĄCO ORAZ SPOSÓB ICH WYTWARZANIA - Google Patents
BLACHA STALOWA CIENKA O DUŻEJ WYTRZYMAŁOŚCI CYNKOWANA ZANURZENIOWO NA GORĄCO MAJĄCA DOSKONAŁĄ PODATNOŚĆ NA FORMOWANIE, NISKĄ ANIZOTROPIĘ MATERIAŁU I GRANICZNĄ WYTRZYMAŁOŚĆ NA ROZCIĄGANIE WYNOSZĄCĄ 980 MPa LUB WIĘCEJ, STOPOWA BLACHA STALOWA CIENKA O DUŻEJ WYTRZYMAŁOŚCI CYNKOWANA ZANURZENIOWO NA GORĄCO ORAZ SPOSÓB ICH WYTWARZANIAInfo
- Publication number
- PL2762588T3 PL2762588T3 PL12836248T PL12836248T PL2762588T3 PL 2762588 T3 PL2762588 T3 PL 2762588T3 PL 12836248 T PL12836248 T PL 12836248T PL 12836248 T PL12836248 T PL 12836248T PL 2762588 T3 PL2762588 T3 PL 2762588T3
- Authority
- PL
- Poland
- Prior art keywords
- strength
- steel plate
- galvanized steel
- dip galvanized
- hot dip
- Prior art date
Links
- 229910001335 Galvanized steel Inorganic materials 0.000 title 2
- 239000008397 galvanized steel Substances 0.000 title 2
- 238000004519 manufacturing process Methods 0.000 title 1
- 239000000463 material Substances 0.000 title 1
Classifications
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
- C23C2/06—Zinc or cadmium or alloys based thereon
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B21—MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
- B21B—ROLLING OF METAL
- B21B3/00—Rolling materials of special alloys so far as the composition of the alloy requires or permits special rolling methods or sequences ; Rolling of aluminium, copper, zinc or other non-ferrous metals
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B15/00—Layered products comprising a layer of metal
- B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
- B32B15/013—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of a metal other than iron or aluminium
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
- C21D8/0226—Hot rolling
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
- C21D8/0236—Cold rolling
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
- C21D8/0273—Final recrystallisation annealing
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C18/00—Alloys based on zinc
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C18/00—Alloys based on zinc
- C22C18/04—Alloys based on zinc with aluminium as the next major constituent
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/001—Ferrous alloys, e.g. steel alloys containing N
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/08—Ferrous alloys, e.g. steel alloys containing nickel
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/16—Ferrous alloys, e.g. steel alloys containing copper
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/26—Ferrous alloys, e.g. steel alloys containing chromium with niobium or tantalum
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/28—Ferrous alloys, e.g. steel alloys containing chromium with titanium or zirconium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/32—Ferrous alloys, e.g. steel alloys containing chromium with boron
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/34—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of silicon
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/38—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of manganese
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
- C22C38/58—Ferrous alloys, e.g. steel alloys containing chromium with nickel with more than 1.5% by weight of manganese
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
- C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
- C23C2/0224—Two or more thermal pretreatments
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
- C23C2/024—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by cleaning or etching
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
- C23C2/12—Aluminium or alloys based thereon
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/26—After-treatment
- C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/26—After-treatment
- C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
- C23C2/29—Cooling or quenching
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D
- C23C28/02—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D only coatings only including layers of metallic material
- C23C28/021—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D only coatings only including layers of metallic material including at least one metal alloy layer
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D
- C23C28/02—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D only coatings only including layers of metallic material
- C23C28/023—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D only coatings only including layers of metallic material only coatings of metal elements only
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C30/00—Coating with metallic material characterised only by the composition of the metallic material, i.e. not characterised by the coating process
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C30/00—Coating with metallic material characterised only by the composition of the metallic material, i.e. not characterised by the coating process
- C23C30/005—Coating with metallic material characterised only by the composition of the metallic material, i.e. not characterised by the coating process on hard metal substrates
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D2211/00—Microstructure comprising significant phases
- C21D2211/001—Austenite
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D2211/00—Microstructure comprising significant phases
- C21D2211/005—Ferrite
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
- C21D8/0263—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment following hot rolling
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/0278—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips involving a particular surface treatment
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
- C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/12—All metal or with adjacent metals
- Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
- Y10T428/12736—Al-base component
- Y10T428/1275—Next to Group VIII or IB metal-base component
- Y10T428/12757—Fe
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/12—All metal or with adjacent metals
- Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
- Y10T428/12771—Transition metal-base component
- Y10T428/12785—Group IIB metal-base component
- Y10T428/12792—Zn-base component
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/12—All metal or with adjacent metals
- Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
- Y10T428/12771—Transition metal-base component
- Y10T428/12785—Group IIB metal-base component
- Y10T428/12792—Zn-base component
- Y10T428/12799—Next to Fe-base component [e.g., galvanized]
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/12—All metal or with adjacent metals
- Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
- Y10T428/12771—Transition metal-base component
- Y10T428/12861—Group VIII or IB metal-base component
- Y10T428/12951—Fe-base component
- Y10T428/12958—Next to Fe-base component
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/12—All metal or with adjacent metals
- Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
- Y10T428/12771—Transition metal-base component
- Y10T428/12861—Group VIII or IB metal-base component
- Y10T428/12951—Fe-base component
- Y10T428/12972—Containing 0.01-1.7% carbon [i.e., steel]
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Mechanical Engineering (AREA)
- Materials Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Thermal Sciences (AREA)
- Physics & Mathematics (AREA)
- Crystallography & Structural Chemistry (AREA)
- Oil, Petroleum & Natural Gas (AREA)
- Heat Treatment Of Sheet Steel (AREA)
- Coating With Molten Metal (AREA)
Applications Claiming Priority (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2011218040 | 2011-09-30 | ||
EP12836248.0A EP2762588B1 (en) | 2011-09-30 | 2012-09-28 | High-strength hot dip galvanized steel plate having excellent moldability, weak material anisotropy and ultimate tensile strength of 980 mpa or more, high-strength alloyed hot dip galvanized steel plate and manufacturing method therefor |
PCT/JP2012/075214 WO2013047819A1 (ja) | 2011-09-30 | 2012-09-28 | 引張最大強度980MPa以上を有する材質異方性の少ない成形性に優れた高強度溶融亜鉛めっき鋼板、高強度合金化溶融亜鉛めっき鋼板及びその製造方法 |
Publications (1)
Publication Number | Publication Date |
---|---|
PL2762588T3 true PL2762588T3 (pl) | 2020-10-19 |
Family
ID=47995842
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PL12836248T PL2762588T3 (pl) | 2011-09-30 | 2012-09-28 | BLACHA STALOWA CIENKA O DUŻEJ WYTRZYMAŁOŚCI CYNKOWANA ZANURZENIOWO NA GORĄCO MAJĄCA DOSKONAŁĄ PODATNOŚĆ NA FORMOWANIE, NISKĄ ANIZOTROPIĘ MATERIAŁU I GRANICZNĄ WYTRZYMAŁOŚĆ NA ROZCIĄGANIE WYNOSZĄCĄ 980 MPa LUB WIĘCEJ, STOPOWA BLACHA STALOWA CIENKA O DUŻEJ WYTRZYMAŁOŚCI CYNKOWANA ZANURZENIOWO NA GORĄCO ORAZ SPOSÓB ICH WYTWARZANIA |
Country Status (15)
Country | Link |
---|---|
US (1) | US9540720B2 (pl) |
EP (1) | EP2762588B1 (pl) |
JP (1) | JP5321765B1 (pl) |
KR (1) | KR101608163B1 (pl) |
CN (1) | CN103987868B (pl) |
BR (1) | BR112014007412B1 (pl) |
CA (1) | CA2850091C (pl) |
ES (1) | ES2804542T3 (pl) |
IN (1) | IN2014DN03211A (pl) |
MX (1) | MX2014003714A (pl) |
PL (1) | PL2762588T3 (pl) |
RU (1) | RU2583194C2 (pl) |
TW (1) | TWI479028B (pl) |
WO (1) | WO2013047819A1 (pl) |
ZA (1) | ZA201402969B (pl) |
Families Citing this family (38)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE102013004905A1 (de) * | 2012-03-23 | 2013-09-26 | Salzgitter Flachstahl Gmbh | Zunderarmer Vergütungsstahl und Verfahren zur Herstellung eines zunderarmen Bauteils aus diesem Stahl |
EP3162908B8 (en) | 2014-07-14 | 2019-07-31 | Nippon Steel Corporation | Hot-rolled steel sheet |
JP6304381B2 (ja) * | 2014-07-14 | 2018-04-04 | 新日鐵住金株式会社 | 熱延鋼板 |
JP6295893B2 (ja) * | 2014-08-29 | 2018-03-20 | 新日鐵住金株式会社 | 耐水素脆化特性に優れた超高強度冷延鋼板およびその製造方法 |
DE102014017274A1 (de) * | 2014-11-18 | 2016-05-19 | Salzgitter Flachstahl Gmbh | Höchstfester lufthärtender Mehrphasenstahl mit hervorragenden Verarbeitungseigenschaften und Verfahren zur Herstellung eines Bandes aus diesem Stahl |
CN104561791A (zh) * | 2015-01-28 | 2015-04-29 | 河北钢铁股份有限公司承德分公司 | 800MPa级别汽车箱体用钢及其生产方法 |
TWI504756B (zh) | 2015-01-30 | 2015-10-21 | China Steel Corp | Manufacture method of high strength and high ductility steel |
CN107250409B (zh) * | 2015-02-17 | 2019-07-05 | 杰富意钢铁株式会社 | 高强度冷轧薄钢板及其制造方法 |
MX2017012198A (es) * | 2015-03-25 | 2017-12-15 | Jfe Steel Corp | Lamina de acero de alta resistencia y metodo para la produccion de la misma. |
EP3276021B1 (en) * | 2015-03-27 | 2019-12-04 | JFE Steel Corporation | High-strength steel sheet and production method therefor |
JP6172404B1 (ja) * | 2015-09-04 | 2017-08-02 | Jfeスチール株式会社 | 高強度薄鋼板およびその製造方法 |
CN105483552A (zh) * | 2015-11-25 | 2016-04-13 | 河北钢铁股份有限公司承德分公司 | 一种900MPa级汽车梁钢板及其生产方法 |
JP2017115205A (ja) * | 2015-12-24 | 2017-06-29 | 日新製鋼株式会社 | めっき密着性に優れた溶融Zn−Al−Mg合金めっき鋼板の製造方法 |
EP3444372B1 (en) * | 2016-04-14 | 2020-12-02 | JFE Steel Corporation | High strength steel sheet and manufacturing method therefor |
WO2018033960A1 (ja) | 2016-08-16 | 2018-02-22 | 新日鐵住金株式会社 | 熱間プレス成形部材 |
TWI602932B (zh) * | 2016-08-16 | 2017-10-21 | 新日鐵住金股份有限公司 | 熱壓製成形構件 |
WO2018033990A1 (ja) | 2016-08-18 | 2018-02-22 | 新日鐵住金株式会社 | 熱延鋼板 |
TWI607096B (zh) * | 2016-08-18 | 2017-12-01 | 新日鐵住金股份有限公司 | 熱軋鋼板 |
MX2019005168A (es) | 2016-11-04 | 2019-10-02 | Nucor Corp | Acero multifase laminado en frío de resistencia ultra alta. |
US11021776B2 (en) | 2016-11-04 | 2021-06-01 | Nucor Corporation | Method of manufacture of multiphase, hot-rolled ultra-high strength steel |
CN106801198B (zh) * | 2017-02-07 | 2018-02-09 | 和县隆盛精密机械有限公司 | 一种适用于机械臂弯曲件的合金铸件及其热处理工艺 |
CN110312813B (zh) * | 2017-02-13 | 2021-07-20 | 杰富意钢铁株式会社 | 高强度钢板及其制造方法 |
CN110168125B (zh) | 2017-02-20 | 2021-11-26 | 日本制铁株式会社 | 高强度钢板 |
US11408046B2 (en) | 2017-02-20 | 2022-08-09 | Nippon Steel Corporation | High strength steel sheet |
CN109207867A (zh) * | 2017-06-29 | 2019-01-15 | 宝山钢铁股份有限公司 | 一种冷轧退火双相钢、钢板及其制造方法 |
US11313009B2 (en) | 2017-07-07 | 2022-04-26 | Nippon Steel Corporation | Hot-rolled steel sheet and method for manufacturing same |
US11939651B2 (en) | 2018-05-31 | 2024-03-26 | Posco Co., Ltd | Al—Fe-alloy plated steel sheet for hot forming, having excellent TWB welding characteristics, hot forming member, and manufacturing methods therefor |
JP7217274B2 (ja) * | 2018-06-29 | 2023-02-02 | 東洋鋼鈑株式会社 | 熱延鋼板、高強度冷延鋼板およびそれらの製造方法 |
CN109097681B (zh) * | 2018-08-15 | 2020-09-29 | 敬业钢铁有限公司 | 一种高强度低夹杂汽车钢板及其连铸过程电磁搅拌工艺 |
MX2021008066A (es) * | 2019-01-07 | 2021-08-05 | Nippon Steel Corp | Lamina de acero y metodo de fabricacion de la misma. |
CN113302322B (zh) * | 2019-01-07 | 2023-07-21 | 日本制铁株式会社 | 钢板及其制造方法 |
JP7188618B2 (ja) * | 2019-12-09 | 2022-12-13 | 日本製鉄株式会社 | 熱延鋼板 |
CN112319129A (zh) * | 2020-02-27 | 2021-02-05 | 浙江航通机械制造股份有限公司 | 一种轻量化汽车轮辋结构及制造方法 |
JP7024877B2 (ja) * | 2020-03-11 | 2022-02-24 | Jfeスチール株式会社 | 鋼材およびその製造方法、ならびにタンク |
TWI711706B (zh) * | 2020-05-15 | 2020-12-01 | 中國鋼鐵股份有限公司 | 具高降伏強度的汽車用鋼材及其製造方法 |
US20230295761A1 (en) * | 2020-09-30 | 2023-09-21 | Nippon Steel Corporation | Steel sheet and steel sheet manufacturing method |
CN114438417B (zh) * | 2022-02-09 | 2023-02-28 | 马鞍山钢铁股份有限公司 | 具有良好抗脱锌粉性能及表面质量的纯锌镀层钢板及其生产方法和应用 |
CN115216607B (zh) * | 2022-06-30 | 2023-11-10 | 武汉钢铁有限公司 | 一种热镀锌铁合金外板合金化斑迹缺陷的控制方法 |
Family Cites Families (23)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS59219473A (ja) | 1983-05-26 | 1984-12-10 | Nippon Steel Corp | カラ−エツチング液及びエツチング方法 |
JP2782468B2 (ja) | 1990-05-18 | 1998-07-30 | 新日本製鐵株式会社 | 溶融亜鉛めっき高張力熱延鋼板の製造方法 |
JP3521851B2 (ja) | 2000-07-26 | 2004-04-26 | 住友金属工業株式会社 | 高張力高延性亜鉛めっき鋼板の製造方法 |
CN101125473B (zh) * | 2001-06-06 | 2012-07-18 | 新日本制铁株式会社 | 热浸镀锌薄钢板和热浸镀锌层扩散处理薄钢板及制造方法 |
JP3598087B2 (ja) | 2001-10-01 | 2004-12-08 | 新日本製鐵株式会社 | 加工性の優れた高強度合金化溶融亜鉛めっき鋼板およびその製造方法 |
US7503984B2 (en) | 2001-10-04 | 2009-03-17 | Nippon Steel Corporation | High-strength thin steel sheet drawable and excellent in shape fixation property and method of producing the same |
JP4718782B2 (ja) | 2003-02-06 | 2011-07-06 | 新日本製鐵株式会社 | 合金化溶融亜鉛めっき鋼板、およびその製造方法 |
JP4464720B2 (ja) | 2003-04-10 | 2010-05-19 | 新日本製鐵株式会社 | 高強度溶融亜鉛めっき鋼板およびその製造方法 |
JP4445365B2 (ja) | 2004-10-06 | 2010-04-07 | 新日本製鐵株式会社 | 伸びと穴拡げ性に優れた高強度薄鋼板の製造方法 |
JP5062985B2 (ja) * | 2004-10-21 | 2012-10-31 | 新日鉄マテリアルズ株式会社 | 加工性に優れた高Al含有鋼板及びその製造方法 |
JP4555693B2 (ja) | 2005-01-17 | 2010-10-06 | 新日本製鐵株式会社 | 深絞り性に優れた高強度冷延鋼板およびその製造方法 |
JP4837426B2 (ja) * | 2006-04-10 | 2011-12-14 | 新日本製鐵株式会社 | バーリング加工性に優れた高ヤング率薄鋼板及びその製造方法 |
JP4964488B2 (ja) * | 2006-04-20 | 2012-06-27 | 新日本製鐵株式会社 | プレス成形性の良好な高強度高ヤング率鋼板、溶融亜鉛めっき鋼板、合金化溶融亜鉛めっき鋼板及び鋼管、並びにそれらの製造方法 |
JP5365194B2 (ja) * | 2006-11-21 | 2013-12-11 | 新日鐵住金株式会社 | 高い{222}面集積度を有する鋼板およびその製造方法 |
JP5478804B2 (ja) | 2006-12-28 | 2014-04-23 | 新日鐵住金株式会社 | 表面外観及びめっき密着性に優れた合金化溶融亜鉛めっき鋼板 |
JP5223366B2 (ja) | 2007-02-08 | 2013-06-26 | Jfeスチール株式会社 | 成形性および溶接性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法 |
JP5053157B2 (ja) * | 2007-07-04 | 2012-10-17 | 新日本製鐵株式会社 | プレス成形性の良好な高強度高ヤング率鋼板、溶融亜鉛めっき鋼板、合金化溶融亜鉛めっき鋼板及び鋼管、並びに、それらの製造方法 |
JP5068689B2 (ja) * | 2008-04-24 | 2012-11-07 | 新日本製鐵株式会社 | 穴広げ性に優れた熱延鋼板 |
JP4772927B2 (ja) * | 2009-05-27 | 2011-09-14 | 新日本製鐵株式会社 | 疲労特性と伸び及び衝突特性に優れた高強度鋼板、溶融めっき鋼板、合金化溶融めっき鋼板およびそれらの製造方法 |
JP5499664B2 (ja) | 2009-11-30 | 2014-05-21 | 新日鐵住金株式会社 | 疲労耐久性に優れた引張最大強度900MPa以上の高強度冷延鋼板及びその製造方法、並びに、高強度亜鉛めっき鋼板及びその製造方法 |
JP4903915B2 (ja) | 2010-01-26 | 2012-03-28 | 新日本製鐵株式会社 | 高強度冷延鋼板及びその製造方法 |
ES2665982T3 (es) | 2011-03-28 | 2018-04-30 | Nippon Steel & Sumitomo Metal Corporation | Lámina de acero laminada en frío y su procedimiento de producción |
PL2700728T3 (pl) * | 2011-04-21 | 2018-03-30 | Nippon Steel & Sumitomo Metal Corporation | Blacha stalowa cienka walcowana na zimno o wysokiej wytrzymałości, wysoce jednorodnej rozciągliwości i doskonałej podatności na powiększanie otworu oraz sposób jej wytwarzania |
-
2012
- 2012-09-28 TW TW101135879A patent/TWI479028B/zh not_active IP Right Cessation
- 2012-09-28 RU RU2014116640/02A patent/RU2583194C2/ru not_active IP Right Cessation
- 2012-09-28 CN CN201280059400.9A patent/CN103987868B/zh active Active
- 2012-09-28 EP EP12836248.0A patent/EP2762588B1/en active Active
- 2012-09-28 PL PL12836248T patent/PL2762588T3/pl unknown
- 2012-09-28 WO PCT/JP2012/075214 patent/WO2013047819A1/ja active Application Filing
- 2012-09-28 KR KR1020147010709A patent/KR101608163B1/ko active IP Right Grant
- 2012-09-28 IN IN3211DEN2014 patent/IN2014DN03211A/en unknown
- 2012-09-28 CA CA2850091A patent/CA2850091C/en not_active Expired - Fee Related
- 2012-09-28 BR BR112014007412-7A patent/BR112014007412B1/pt not_active IP Right Cessation
- 2012-09-28 ES ES12836248T patent/ES2804542T3/es active Active
- 2012-09-28 JP JP2013513312A patent/JP5321765B1/ja active Active
- 2012-09-28 MX MX2014003714A patent/MX2014003714A/es active IP Right Grant
- 2012-09-28 US US14/347,269 patent/US9540720B2/en active Active
-
2014
- 2014-04-23 ZA ZA2014/02969A patent/ZA201402969B/en unknown
Also Published As
Publication number | Publication date |
---|---|
MX2014003714A (es) | 2014-07-09 |
US9540720B2 (en) | 2017-01-10 |
KR20140068217A (ko) | 2014-06-05 |
EP2762588A1 (en) | 2014-08-06 |
EP2762588B1 (en) | 2020-05-20 |
CA2850091C (en) | 2016-06-28 |
CN103987868A (zh) | 2014-08-13 |
RU2014116640A (ru) | 2015-11-10 |
TWI479028B (zh) | 2015-04-01 |
TW201319266A (zh) | 2013-05-16 |
BR112014007412B1 (pt) | 2019-01-29 |
ES2804542T3 (es) | 2021-02-08 |
RU2583194C2 (ru) | 2016-05-10 |
IN2014DN03211A (pl) | 2015-05-22 |
CN103987868B (zh) | 2016-03-09 |
WO2013047819A1 (ja) | 2013-04-04 |
BR112014007412A2 (pt) | 2017-04-04 |
US20140242415A1 (en) | 2014-08-28 |
EP2762588A4 (en) | 2015-11-11 |
JPWO2013047819A1 (ja) | 2015-03-30 |
KR101608163B1 (ko) | 2016-03-31 |
CA2850091A1 (en) | 2013-04-04 |
ZA201402969B (en) | 2015-04-29 |
JP5321765B1 (ja) | 2013-10-23 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
PL2762588T3 (pl) | BLACHA STALOWA CIENKA O DUŻEJ WYTRZYMAŁOŚCI CYNKOWANA ZANURZENIOWO NA GORĄCO MAJĄCA DOSKONAŁĄ PODATNOŚĆ NA FORMOWANIE, NISKĄ ANIZOTROPIĘ MATERIAŁU I GRANICZNĄ WYTRZYMAŁOŚĆ NA ROZCIĄGANIE WYNOSZĄCĄ 980 MPa LUB WIĘCEJ, STOPOWA BLACHA STALOWA CIENKA O DUŻEJ WYTRZYMAŁOŚCI CYNKOWANA ZANURZENIOWO NA GORĄCO ORAZ SPOSÓB ICH WYTWARZANIA | |
ZA201402970B (en) | High-strength hot-dipped galvanized steel sheet and high-strength alloyed hot-dipped galvanized steel sheet,each having tensile strength of 980 mpa or more,excellent plating adhesion,excellent formability and excellent bore expanding properties ,and method for producing same | |
EP2703512A4 (en) | HIGH-RESISTANCE STEEL PLATE WITH EXCELLENT FORMABILITY AND MATERIAL STABILITY AND MANUFACTURING METHOD THEREFOR | |
PL3034644T3 (pl) | Blacha stalowa o dużej wytrzymałości i ocynkowana blacha stalowa o dużej wytrzymałości z doskonałą ciągliwością i podatnością na wywijanie kołnierza oraz sposób ich wytwarzania | |
EP2559783A4 (en) | HOT ROLLED HIGH-STRENGTH STEEL PLATE HAVING EXCELLENT STRETCH EDGE DEFORMABILITY AND FATIGUE RESISTANCE PROPERTIES, AND METHOD FOR PRODUCING THE SAME | |
EP2634281A4 (en) | HIGH-RESISTANCE FIRE-GRAINED STEEL PLATE WITH EXCELLENT EVEN STRENGTH AND EXCELLENT PLATING CHARACTERISTICS, AND METHOD OF MANUFACTURING THEREOF | |
MX357839B (es) | Hoja de acero platinada con zinc de alta resistencia y lámina de acero de alta resistencia que tiene maleabilidad superior y método para producir cada una de ellas. | |
EP2559782A4 (en) | HIGHLY RESISTANT STEEL PLATE OF EXCELLENT FORMABILITY AND SHOCK STRENGTH, AND METHOD FOR THE PRODUCTION THEREOF | |
EP3533894A4 (en) | COLD-ROLLED HIGH-STRENGTH STEEL SHEET HAVING A STRENGTH OF 1500 MPA OR MORE AND EXCELLENT FORMABILITY, AND MANUFACTURING METHOD THEREOF | |
EP2798094A4 (en) | HIGH-FIXED FIRE-GRAINED STEEL PLATE WITH EXCELLENT PLATING SURFACE QUALITY AND LIABILITY AND MANUFACTURING METHOD THEREFOR | |
ZA201402351B (en) | High-strength hot-dip galvanized steel sheet having excellent delayed fracture resistance and manufacturing method thereof | |
EP2415896A4 (en) | HIGH-FIXED FIRE-PLATED STEEL PLATE AND METHOD FOR THE PRODUCTION THEREOF | |
EP2407572A4 (en) | HIGH-FIXED FIRE-PLATED STEEL PLATE AND METHOD FOR THE PRODUCTION THEREOF | |
EP2873746A4 (en) | HIGH-RESISTANCE FIRED GALVANIZED STEEL PLATE WITH EXCELLENT LIMITABILITY AND DEFORMABILITY AND MANUFACTURING METHOD THEREFOR | |
ZA201401348B (en) | High-strength cold-rolled steel sheet having excellent stretch flangeability and precision punchability,and manufacturing method thereof | |
EP2444510A4 (en) | HIGH-FIXED, FIRED GRAINED STEEL PLATE WITH EXCELLENT PROCESSING AND MATERIAL FEELING PROPERTIES AND METHOD OF MANUFACTURING THEREOF | |
EP2757171A4 (en) | HIGH-RESISTANCE HOT-DIP GALVANIZED STEEL SHEET HAVING EXCELLENT FORMING CAPABILITY AND EXCELLENT SHOCK RESISTANCE AND METHOD OF MANUFACTURING THE SAME | |
EP2426230A4 (en) | HIGH-STRENGTH HOT-SIDED STEEL SHEET HAVING EXCELLENT SHAPEABILITY, EXCELLENT WELDABILITY, AND EXCELLENT FATIGUE RESISTANCE PROPERTIES, AND METHOD OF MANUFACTURING THE SAME | |
EP2524972A4 (en) | HIGH STRENGTH STEEL SHEET HAVING EXCELLENT FORMABILITY AND PROCESS FOR PRODUCING THE SAME | |
EP2738275A4 (en) | HIGH-FIXED GALVANIZED STEEL PLATE AND HIGH-RESISTANCE STEEL PLATE WITH EXCELLENT FORMABILITY AND METHOD FOR THE PRODUCTION THEREOF | |
BR112013028931A2 (pt) | processo de fabricação de uma chapa e de uma peça de aço com estrutura totalmente martensítica e chapa com limite de elasticidade superior a 1300 mpa de aço | |
EP2767604A4 (en) | HIGH-RESISTANT COLD-ROLLED STEEL PLATE WITH EXCELLENT DEEP-DRAWN CAPACITY AND MATERIAL UNIFORMITY ON COIL AS WELL AS MANUFACTURING METHOD THEREFOR | |
EP2241646A4 (en) | HIGH-STRENGTH THICKNESS STEEL PLATE WITH EXCELLENT WELDING CAPACITY AND A TENSILE STRENGTH OF 780 MPA OR HIGHER, AND METHOD FOR THEIR PRODUCTION | |
EP2520684A4 (en) | AUSTENITIC STEEL MATERIAL WITH SUPERIOR DUCTILITY | |
UA113529C2 (xx) | Мартенситні сталі з міцністю при розтягуванні 1700-2200 мпа |