MX2021008669A - Metodo de produccion de lamina de acero galvanizada por inmersion en caliente. - Google Patents
Metodo de produccion de lamina de acero galvanizada por inmersion en caliente.Info
- Publication number
- MX2021008669A MX2021008669A MX2021008669A MX2021008669A MX2021008669A MX 2021008669 A MX2021008669 A MX 2021008669A MX 2021008669 A MX2021008669 A MX 2021008669A MX 2021008669 A MX2021008669 A MX 2021008669A MX 2021008669 A MX2021008669 A MX 2021008669A
- Authority
- MX
- Mexico
- Prior art keywords
- steel sheet
- inclusive
- dip galvanized
- hot
- galvanized steel
- Prior art date
Abstract
Se divulga un método de producción de una lámina de acero galvanizada por inmersión en caliente con excelente aspecto de superficie, adherencia de recubrimiento, y resistencia a la corrosión. Un método de producción de una lámina de acero galvanizada por inmersión en caliente divulgado en la presente incluye: llevar a cabo primer recocido que comprende retener una lámina de acero que tiene una composición química que contiene, en % en masa, Si: 0.10% o más y 3.0% o menos y Mn: 1.0% o más y 10.0% o menos dentro de un intervalo de temperatura de 650°C a 900°C durante 30 segundos o más en una atmósfera reductora que contiene hidrógeno y que tiene un punto de rocío de -65°C o superior y -20°C o inferior, y a continuación enfriar la lámina de acero; a continuación formar, sobre una superficie de la lámina de acero, un recubrimiento de Fe con un peso de recubrimiento de 0.3 g/m2 o más y 10.0 g/m2 o menos; a continuación llevar a cabo segundo recocido que comprende retener la lámina de acero dentro de un intervalo de temperatura de 700°C a 900°C durante 30 segundos o más en una atmósfera reductora que contiene hidrógeno y que tiene un punto de rocío de 0°C o inferior, calentar la lámina de acero hasta un temperatura máxima de llegada de 900°C o inferior, y a continuación enfriar la lámina de acero; y a continuación aplicar un recubrimiento galvanizado por inmersión en caliente sobre la lámina de acero.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2019007320 | 2019-01-18 | ||
PCT/JP2019/038021 WO2020148944A1 (ja) | 2019-01-18 | 2019-09-26 | 溶融亜鉛めっき鋼板の製造方法 |
Publications (1)
Publication Number | Publication Date |
---|---|
MX2021008669A true MX2021008669A (es) | 2021-08-19 |
Family
ID=71614513
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
MX2021008669A MX2021008669A (es) | 2019-01-18 | 2019-09-26 | Metodo de produccion de lamina de acero galvanizada por inmersion en caliente. |
Country Status (5)
Country | Link |
---|---|
EP (1) | EP3913106A4 (es) |
JP (1) | JP6897857B2 (es) |
CN (1) | CN113272466B (es) |
MX (1) | MX2021008669A (es) |
WO (1) | WO2020148944A1 (es) |
Families Citing this family (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2022097732A1 (ja) * | 2020-11-06 | 2022-05-12 | Jfeスチール株式会社 | Fe系電気めっき鋼板,電着塗装鋼板,自動車部品,電着塗装鋼板の製造方法,及びFe系電気めっき鋼板の製造方法 |
EP4242359A4 (en) * | 2020-11-06 | 2024-05-22 | JFE Steel Corporation | GALVANIZED STEEL SHEET, GALVANIZED STEEL SHEET, AUTOMOTIVE PART, METHOD FOR PRODUCING A GALVANIZED STEEL SHEET AND METHOD FOR PRODUCING A GALVANIZED STEEL SHEET |
MX2023005275A (es) * | 2020-11-06 | 2023-07-26 | Jfe Steel Corp | Lámina de acero galvanizado por aleación, lámina de acero recubierta por electrodeposición, pieza automotriz, método de producción de lámina de acero recubierta por electrodeposición, y método de producción de lámina de acero galvanizado por aleación. |
WO2022097738A1 (ja) * | 2020-11-06 | 2022-05-12 | Jfeスチール株式会社 | Fe系電気めっき鋼板及び合金化溶融亜鉛めっき鋼板、並びにこれらの製造方法 |
CN116457504A (zh) * | 2020-11-06 | 2023-07-18 | 杰富意钢铁株式会社 | 镀锌钢板、电沉积涂装钢板、汽车部件、电沉积涂装钢板的制造方法以及镀锌钢板的制造方法 |
CN116457481A (zh) * | 2020-11-06 | 2023-07-18 | 杰富意钢铁株式会社 | 合金化镀锌钢板、电沉积涂装钢板、汽车部件、电沉积涂装钢板的制造方法以及合金化镀锌钢板的制造方法 |
JP7444283B2 (ja) * | 2021-05-17 | 2024-03-06 | Jfeスチール株式会社 | Fe系電気めっき鋼板および溶融亜鉛めっき鋼板ならびにそれらの製造方法 |
Family Cites Families (9)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH0768583B2 (ja) * | 1984-03-07 | 1995-07-26 | 住友金属工業株式会社 | 高張力冷延鋼板の製造法 |
JPH07252622A (ja) * | 1994-03-16 | 1995-10-03 | Nisshin Steel Co Ltd | 高強度合金化溶融亜鉛めっき鋼板の製造方法 |
JP3581451B2 (ja) * | 1995-09-06 | 2004-10-27 | 新日本製鐵株式会社 | 亜鉛−錫合金めっき鋼板の製造法 |
JP3598086B2 (ja) * | 2001-10-01 | 2004-12-08 | 新日本製鐵株式会社 | 加工性の優れた高強度合金化溶融亜鉛めっき鋼板の製造方法 |
JP4473588B2 (ja) | 2004-01-14 | 2010-06-02 | 新日本製鐵株式会社 | めっき密着性および穴拡げ性に優れた溶融亜鉛めっき高強度鋼板の製造方法 |
JP5695332B2 (ja) * | 2010-03-31 | 2015-04-01 | 株式会社神戸製鋼所 | めっき密着性に優れた合金化溶融亜鉛めっき鋼板の製造方法 |
KR20130076589A (ko) * | 2011-12-28 | 2013-07-08 | 주식회사 포스코 | 도금표면 품질 및 도금밀착성이 우수한 고강도 용융아연도금강판 및 그 제조방법 |
EP3081665B1 (en) * | 2013-12-13 | 2018-07-11 | JFE Steel Corporation | Method for manufacturing high-strength hot-dip galvanized steel sheet |
CN111492075B (zh) * | 2017-12-15 | 2021-10-12 | 日本制铁株式会社 | 钢板、热浸镀锌钢板和合金化热浸镀锌钢板 |
-
2019
- 2019-09-26 JP JP2020502725A patent/JP6897857B2/ja active Active
- 2019-09-26 WO PCT/JP2019/038021 patent/WO2020148944A1/ja unknown
- 2019-09-26 CN CN201980088479.XA patent/CN113272466B/zh active Active
- 2019-09-26 EP EP19910043.9A patent/EP3913106A4/en active Pending
- 2019-09-26 MX MX2021008669A patent/MX2021008669A/es unknown
Also Published As
Publication number | Publication date |
---|---|
EP3913106A4 (en) | 2022-03-09 |
CN113272466A (zh) | 2021-08-17 |
JP6897857B2 (ja) | 2021-07-07 |
EP3913106A1 (en) | 2021-11-24 |
JPWO2020148944A1 (ja) | 2021-02-18 |
CN113272466B (zh) | 2023-07-21 |
WO2020148944A1 (ja) | 2020-07-23 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
MX2021008669A (es) | Metodo de produccion de lamina de acero galvanizada por inmersion en caliente. | |
EP2794950B1 (en) | Hot-dip galvanized steel sheet having excellent adhesiveness at ultra-low temperatures and method of manufacturing the same | |
AU2012377741B2 (en) | Steel sheet provided with a coating offering sacrificial cathodic protection, method for the production of a part using such a sheet, and resulting part | |
JP2022513740A (ja) | 耐食性ホットスタンプ部品の製造方法及び装置 | |
WO2006006696A1 (ja) | 耐食性に優れた高強度焼き入れ成形体およびその製造方法 | |
CA2605486A1 (en) | Hot dip galvannealed steel sheet and method of production of the same | |
CN108018513A (zh) | 一种热浸镀锌铝镁镀层钢板及其制造方法 | |
JP2006299341A (ja) | 合金化溶融亜鉛メッキ鋼板の製造方法 | |
BRPI0908226A2 (pt) | processo de revestimento de uma cinta metálica e instalação de aplicação do processo | |
MY161932A (en) | Hot-dip zinc-aluminium alloy coated steel sheet having high corrosion resistance and formability and method for producing the same | |
KR101707981B1 (ko) | 용융 아연 도금 강판의 제조 방법 | |
KR101621630B1 (ko) | 도장 후 내식성이 우수한 합금화 용융 아연 도금 강판 | |
KR101639877B1 (ko) | 표면이 미려한 고내식 아연합금 도금강판 및 이의 제조방법 | |
JP2005256108A (ja) | 溶融亜鉛系めっき鋼材の製造方法 | |
JP2000248346A (ja) | Si含有高強度溶融亜鉛めっき鋼板ならびに高強度合金化溶融亜鉛めっき鋼板の製造方法 | |
JPS63312960A (ja) | 加工性の良い溶融亜鉛合金めっき鋼板の製造法 | |
JP5211657B2 (ja) | 溶融亜鉛めっき鋼板の製造方法 | |
TW202037736A (zh) | 鍍鋅鋼片及其製造方法 | |
MX2022000380A (es) | Métodos para fabricar respectivamente lámina de acero galvanizada por inmersión en caliente y lámina de acero galvanizada por inmersión en caliente con aleación. | |
KR20120054239A (ko) | 친환경 오염방지와 초내후성 중성화방지를 위한 금속 부식 방지용 표면 코팅재 및 그 제조방법 | |
JP2002194518A (ja) | 溶接性に優れた溶融亜鉛めっき鋼板およびその製造方法 | |
JP2841898B2 (ja) | 表面平滑性に優れた合金化溶融亜鉛めっき鋼板 | |
JP4600951B2 (ja) | 加工性に優れた合金化溶融亜鉛めっき鋼板及びその製造方法 | |
JPH0356654A (ja) | 溶融アルミニウムめっきクロム含有鋼板の製造方法 | |
JP5604784B2 (ja) | めっき性の良好な合金化溶融亜鉛めっき鋼板の製造方法 |