MX2019008167A - Lamina de acero y proceso para producir la misma. - Google Patents
Lamina de acero y proceso para producir la misma.Info
- Publication number
- MX2019008167A MX2019008167A MX2019008167A MX2019008167A MX2019008167A MX 2019008167 A MX2019008167 A MX 2019008167A MX 2019008167 A MX2019008167 A MX 2019008167A MX 2019008167 A MX2019008167 A MX 2019008167A MX 2019008167 A MX2019008167 A MX 2019008167A
- Authority
- MX
- Mexico
- Prior art keywords
- steel plate
- less
- production method
- method therefor
- over
- Prior art date
Abstract
Se proporciona una lámina de acero con una alta concentración de Mn contenido que tiene una excelente característica de alargamiento uniforme y alta resistencia. Una lámina de acero caracterizada por contener, en % en masa, C: más de 0.10% y menos de 0.55%, Si: 0.001% o más y menos de 3.50%, Mn: más que 4.00% y menos de 9.00%, sol. Al: 0.001% o más y menos de 3.00%, y un equilibrio de hierro e impurezas inevitables, en donde una estructura metálica en una posición de 1/4 de espesor desde una superficie en una sección transversal en L de la lámina de acero comprende, por % de área, 25% a 90% de martensita templada, 3% menos de ferrita, 10% a 75% de austenita residual y 5% o menos de bainita.
Applications Claiming Priority (4)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2017005258 | 2017-01-16 | ||
JP2017005265 | 2017-01-16 | ||
JP2017005250 | 2017-01-16 | ||
PCT/JP2018/001076 WO2018131722A1 (ja) | 2017-01-16 | 2018-01-16 | 鋼板及びその製造方法 |
Publications (1)
Publication Number | Publication Date |
---|---|
MX2019008167A true MX2019008167A (es) | 2019-09-06 |
Family
ID=62840134
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
MX2019008167A MX2019008167A (es) | 2017-01-16 | 2018-01-16 | Lamina de acero y proceso para producir la misma. |
Country Status (9)
Country | Link |
---|---|
US (1) | US20190368002A1 (es) |
EP (1) | EP3569727A4 (es) |
JP (1) | JP6844627B2 (es) |
KR (1) | KR20190109407A (es) |
CN (1) | CN110177896B (es) |
BR (1) | BR112019013362A2 (es) |
MX (1) | MX2019008167A (es) |
TW (1) | TWI666329B (es) |
WO (1) | WO2018131722A1 (es) |
Families Citing this family (15)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
TW202006154A (zh) * | 2018-07-18 | 2020-02-01 | 日商日本製鐵股份有限公司 | 鋼板 |
JP6737411B2 (ja) * | 2018-07-18 | 2020-08-12 | 日本製鉄株式会社 | 鋼板 |
KR102153197B1 (ko) | 2018-12-18 | 2020-09-08 | 주식회사 포스코 | 가공성이 우수한 냉연강판, 용융아연도금강판 및 이들의 제조방법 |
JP6744003B1 (ja) * | 2018-12-27 | 2020-08-19 | 日本製鉄株式会社 | 鋼板 |
WO2020195279A1 (ja) * | 2019-03-27 | 2020-10-01 | 日本製鉄株式会社 | 鋼板 |
EP4029959A4 (en) * | 2019-10-23 | 2023-02-15 | JFE Steel Corporation | HIGH STRENGTH STEEL SHEET AND METHOD OF PRODUCTION THE SAME |
JP7168072B2 (ja) * | 2019-10-23 | 2022-11-09 | Jfeスチール株式会社 | 高強度鋼板およびその製造方法 |
KR20220068245A (ko) * | 2019-10-23 | 2022-05-25 | 제이에프이 스틸 가부시키가이샤 | 고강도 강판 및 그의 제조 방법 |
MX2022011929A (es) * | 2020-04-03 | 2022-10-20 | Nippon Steel Corp | Hoja de acero y metodo para producir la misma. |
WO2022172540A1 (ja) * | 2021-02-10 | 2022-08-18 | Jfeスチール株式会社 | 高強度鋼板およびその製造方法 |
JP7107464B1 (ja) * | 2021-02-10 | 2022-07-27 | Jfeスチール株式会社 | 高強度鋼板およびその製造方法 |
EP4253577A1 (en) * | 2021-02-10 | 2023-10-04 | JFE Steel Corporation | High-strength steel sheet and method for manufacturing same |
WO2022172539A1 (ja) * | 2021-02-10 | 2022-08-18 | Jfeスチール株式会社 | 高強度鋼板およびその製造方法 |
KR20230066166A (ko) * | 2021-11-05 | 2023-05-15 | 주식회사 포스코 | 내충돌성능 및 성형성이 우수한 고강도 강판 및 이의 제조방법 |
WO2023111656A1 (en) * | 2021-12-17 | 2023-06-22 | Arcelormittal | Method for manufacturing an annealed steel sheet |
Family Cites Families (14)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2601581B2 (ja) | 1991-09-03 | 1997-04-16 | 新日本製鐵株式会社 | 加工性に優れた高強度複合組織冷延鋼板の製造方法 |
JP3857939B2 (ja) * | 2001-08-20 | 2006-12-13 | 株式会社神戸製鋼所 | 局部延性に優れた高強度高延性鋼および鋼板並びにその鋼板の製造方法 |
JP5287770B2 (ja) * | 2010-03-09 | 2013-09-11 | Jfeスチール株式会社 | 高強度鋼板およびその製造方法 |
JP5136609B2 (ja) * | 2010-07-29 | 2013-02-06 | Jfeスチール株式会社 | 成形性および耐衝撃性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法 |
JP5825119B2 (ja) | 2011-04-25 | 2015-12-02 | Jfeスチール株式会社 | 加工性と材質安定性に優れた高強度鋼板およびその製造方法 |
KR20150029736A (ko) * | 2012-07-31 | 2015-03-18 | 제이에프이 스틸 가부시키가이샤 | 성형성 및 형상 동결성이 우수한 고강도 용융 아연 도금 강판, 그리고 그의 제조 방법 |
TWI491742B (zh) * | 2014-01-06 | 2015-07-11 | Nippon Steel & Sumitomo Metal Corp | 鋼板及其製造方法 |
JP6290074B2 (ja) * | 2014-12-12 | 2018-03-07 | 株式会社神戸製鋼所 | 加工性に優れた高強度冷延鋼板および高強度合金化溶融亜鉛めっき鋼板 |
JP6554397B2 (ja) * | 2015-03-31 | 2019-07-31 | 株式会社神戸製鋼所 | 加工性および衝突特性に優れた引張強度が980MPa以上の高強度冷延鋼板、およびその製造方法 |
CN114990431A (zh) * | 2015-06-11 | 2022-09-02 | 日本制铁株式会社 | 合金化热浸镀锌钢板及其制造方法 |
JP6620474B2 (ja) * | 2015-09-09 | 2019-12-18 | 日本製鉄株式会社 | 溶融亜鉛めっき鋼板および合金化溶融亜鉛めっき鋼板、並びにそれらの製造方法 |
KR101677396B1 (ko) * | 2015-11-02 | 2016-11-18 | 주식회사 포스코 | 성형성 및 구멍확장성이 우수한 초고강도 강판 및 이의 제조방법 |
JP6875915B2 (ja) * | 2016-05-30 | 2021-05-26 | 株式会社神戸製鋼所 | 高強度鋼板およびその製造方法 |
BR112019010681A2 (pt) * | 2016-12-05 | 2019-09-17 | Nippon Steel Corp | chapa de aço de alta resistência |
-
2018
- 2018-01-16 BR BR112019013362A patent/BR112019013362A2/pt not_active Application Discontinuation
- 2018-01-16 JP JP2018561456A patent/JP6844627B2/ja active Active
- 2018-01-16 CN CN201880007068.9A patent/CN110177896B/zh active Active
- 2018-01-16 WO PCT/JP2018/001076 patent/WO2018131722A1/ja active Application Filing
- 2018-01-16 TW TW107101610A patent/TWI666329B/zh not_active IP Right Cessation
- 2018-01-16 US US16/478,410 patent/US20190368002A1/en not_active Abandoned
- 2018-01-16 KR KR1020197020570A patent/KR20190109407A/ko active IP Right Grant
- 2018-01-16 MX MX2019008167A patent/MX2019008167A/es unknown
- 2018-01-16 EP EP18739322.8A patent/EP3569727A4/en not_active Withdrawn
Also Published As
Publication number | Publication date |
---|---|
EP3569727A4 (en) | 2020-07-15 |
TW201833343A (zh) | 2018-09-16 |
KR20190109407A (ko) | 2019-09-25 |
EP3569727A1 (en) | 2019-11-20 |
US20190368002A1 (en) | 2019-12-05 |
CN110177896A (zh) | 2019-08-27 |
CN110177896B (zh) | 2021-09-14 |
WO2018131722A1 (ja) | 2018-07-19 |
JPWO2018131722A1 (ja) | 2019-11-07 |
JP6844627B2 (ja) | 2021-03-17 |
BR112019013362A2 (pt) | 2019-12-31 |
TWI666329B (zh) | 2019-07-21 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
MX2019008167A (es) | Lamina de acero y proceso para producir la misma. | |
MX2019013949A (es) | Lamina de acero de alta resistencia y su metodo de produccion. | |
MX2019014434A (es) | Lamina de acero para fabricar partes endurecidas por presion, parte endurecida por presion que tiene una combinacion de alta resistencia y ductilidad al choque, y metodos de fabricacion de las mismas. | |
MX2022004076A (es) | Acero para conformado en caliente y pieza conformada en caliente fabricada de tal acero. | |
MX2018010467A (es) | Hoja de acero de alta resistencia y metodo para fabricar la misma. | |
MX2019003282A (es) | Lamina de acero de alta resistencia y alta conformabilidad laminada en frio y tratada termicamente y metodo de fabricacion. | |
MX2018008561A (es) | Lamina de acero de alta resistencia que tiene excelente conformabilidad y un metodo de fabricacion de la misma. | |
MX2018009643A (es) | Lamina de acero de alta resistencia y metodo para la produccion de la misma. | |
MX2017009200A (es) | Lamina de acero galvanizada de alta resistencia y metodo para producir la misma. | |
MX2019006862A (es) | Producto de acero plano laminado en caliente y metodo para la produccion del mismo. | |
MX2018011688A (es) | Lamina de acero y lamina de acero enchapada, metodo para producir lamina de acero laminada en caliente, metodo para producir lamina de acero de dureza completa laminada en frio, metodo para producir lamina termicamente tratada, metodo para producir lamina de acero, y metodo para producir lamina de acero enchapada. | |
MX2017010340A (es) | Lamina de acero galvanizada de alta resistencia y metodo para la fabricacion de la misma. | |
MX2016011356A (es) | Chapa de acero galvanofusionado por inmersion en caliente de alta resistencia que tiene una excelente propiedad de endurecimiento por horneado y capacidad de flexion. | |
MX2010008404A (es) | Chapa de acero de alta resistencia y metodo para elaboracion de la misma. | |
MX2018009735A (es) | Lamina de acero de alta resistencia y metodo para fabricar la misma. | |
MX2019004000A (es) | Lamina de acero recubierta de metal, metodo de fabricacion de lamina de acero galvanizada por inmersion en caliente, y metodo de fabricacion de lamina de acero galvanizada-recocida aleada. | |
MX2021006793A (es) | Placa de acero de alta resistencia que tiene excelente formabilidad, tenacidad y soldabilidad, y metodo de produccion de la misma. | |
MX2015013941A (es) | Lamina de acero laminada en frio y metodo para la fabricacion de la misma. | |
MX2018011778A (es) | Chapa de acero, chapa de acero revestida, metodo para producir chapa de acero laminada en caliente, metodo para producir chapa de acero muy dura laminada en frio, metodo para producir chapa de acero y metodo para producir chapa de acero revestida. | |
MX2017010339A (es) | Lamina de acero galvanizada de alta resistencia y metodo para la fabricacion de la misma. | |
MX2021015171A (es) | Un acero martensitico laminado en frio y un metodo de acero martensitico del mismo. | |
MX2021002972A (es) | Hoja de acero laminado en caliente con una alta proporcion de expansion de agujero y proceso de fabricacion de la misma. | |
MX2020012659A (es) | Lamina de acero de alta resistencia. | |
MX2018010932A (es) | Lamina delgada de acero de alta resistencia y metodo de fabricacion de la misma. | |
MX2022007459A (es) | Hoja de acero laminada en frio y tratada termicamente y metodo de fabricacion de la misma. |