MX2022011929A - Hoja de acero y metodo para producir la misma. - Google Patents

Hoja de acero y metodo para producir la misma.

Info

Publication number
MX2022011929A
MX2022011929A MX2022011929A MX2022011929A MX2022011929A MX 2022011929 A MX2022011929 A MX 2022011929A MX 2022011929 A MX2022011929 A MX 2022011929A MX 2022011929 A MX2022011929 A MX 2022011929A MX 2022011929 A MX2022011929 A MX 2022011929A
Authority
MX
Mexico
Prior art keywords
less
steel sheet
retained austenite
area
producing same
Prior art date
Application number
MX2022011929A
Other languages
English (en)
Inventor
Yoshihiro Suwa
Koutarou Hayashi
Takahiko KOHTAKE
Original Assignee
Nippon Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Steel Corp filed Critical Nippon Steel Corp
Publication of MX2022011929A publication Critical patent/MX2022011929A/es

Abstract

Una hoja de acero que tiene una composición química predeterminada que contiene, en % en masa, C: más de 0.18% y menos de 0.30%, Mn: más de 2.50% y 4.00% o menos, y otros elementos. La microestructura del acero en una posición a una profundidad de 1/4 del espesor de la hoja desde la superficie en una sección transversal en L de la hoja de acero es, en % de área, martensita revenida: 25 a 90%, ferrita: 5% o menos, austenita retenida: 10 a 50%, y bainita: 5% o menos. En una posición a una profundidad de 1/4 del espesor de la hoja desde la superficie de la sección transversal en L, la proporción del área total de granos de austenita retenida que tienen un área de 1 µm2 o más y que tienen una circularidad de forma de grano de 0.1 o más es menor que 50% con respecto a toda el área de austenita retenida. La hoja de acero satisface la fórmula CMn?/CMna ? 1.2.
MX2022011929A 2020-04-03 2021-03-17 Hoja de acero y metodo para producir la misma. MX2022011929A (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2020067685 2020-04-03
PCT/JP2021/010853 WO2021200164A1 (ja) 2020-04-03 2021-03-17 鋼板およびその製造方法

Publications (1)

Publication Number Publication Date
MX2022011929A true MX2022011929A (es) 2022-10-20

Family

ID=77929296

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2022011929A MX2022011929A (es) 2020-04-03 2021-03-17 Hoja de acero y metodo para producir la misma.

Country Status (7)

Country Link
US (1) US20230021370A1 (es)
EP (1) EP4130305A1 (es)
JP (1) JP7364963B2 (es)
KR (1) KR20220156958A (es)
CN (1) CN115362280B (es)
MX (1) MX2022011929A (es)
WO (1) WO2021200164A1 (es)

Family Cites Families (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP5327106B2 (ja) * 2010-03-09 2013-10-30 Ｊｆｅスチール株式会社 プレス部材およびその製造方法
JP5136609B2 (ja) * 2010-07-29 2013-02-06 Ｊｆｅスチール株式会社 成形性および耐衝撃性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
CN103703157B (zh) * 2011-07-29 2015-12-02 新日铁住金株式会社 形状保持性优异的高强度钢板、高强度镀锌钢板及它们的制造方法
EP2881481B1 (en) * 2012-07-31 2019-04-03 JFE Steel Corporation High-strength hot-dip galvanized steel sheet having excellent moldability and shape fixability, and method for manufacturing same
WO2016021198A1 (ja) * 2014-08-07 2016-02-11 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法、ならびに高強度亜鉛めっき鋼板の製造方法
MX2018012659A (es) 2016-04-19 2019-02-28 Jfe Steel Corp Lamina de acero, lamina de acero recubierta, y metodos para la fabricacion de las mismas.
WO2017208762A1 (ja) * 2016-05-30 2017-12-07 株式会社神戸製鋼所 高強度鋼板およびその製造方法
US11732341B2 (en) * 2016-10-19 2023-08-22 Nippon Steel Corporation Metal coated steel sheet, manufacturing method of hot-dip galvanized steel sheet, and manufacturing method of alloyed galvannealed steel sheet
BR112019010681A2 (pt) 2016-12-05 2019-09-17 Nippon Steel Corp chapa de aço de alta resistência
EP3569727A4 (en) * 2017-01-16 2020-07-15 Nippon Steel Corporation STEEL PLATE AND MANUFACTURING METHOD THEREFOR
EP3733897B1 (en) * 2017-12-26 2021-11-10 JFE Steel Corporation High-strength cold rolled steel sheet and method for manufacturing same
CN112154222B (zh) * 2018-06-29 2022-04-01 日本制铁株式会社 高强度钢板及其制造方法
CN113272461B (zh) 2019-03-15 2023-04-25 日本制铁株式会社 钢板

Also Published As

Publication number Publication date
CN115362280B (zh) 2023-10-17
JP7364963B2 (ja) 2023-10-19
CN115362280A (zh) 2022-11-18
US20230021370A1 (en) 2023-01-26
JPWO2021200164A1 (es) 2021-10-07
KR20220156958A (ko) 2022-11-28
EP4130305A1 (en) 2023-02-08
WO2021200164A1 (ja) 2021-10-07

Similar Documents

Publication Publication Date Title
EP2325346B1 (en) High-strength steel plate and manufacturing method thereof
MX2017010340A (es) Lamina de acero galvanizada de alta resistencia y metodo para la fabricacion de la misma.
EP2767606B1 (en) High-strength hot-rolled steel sheet and process for producing same
MX2021008505A (es) Lamina de acero de alta resistencia.
CA2453964A1 (en) Steel material having high toughness and method of producing steel pipes using the same
US20210164761A1 (en) Safety steel or wear-resistant steel, and use
US20200061971A1 (en) Three-layer high-strength steel or ballistic steel, method for producing a component, and use thereof
JP2007332438A (ja) 低サイクル疲労特性に優れた浸炭焼入れ鋼材及び浸炭焼入れ部品
MX2021009452A (es) Lamina de acero galvanizada por inmersion en caliente y metodo para producir la misma.
MX2020010313A (es) Lamina de acero de alta resistencia y metodo para su produccion.
MX2022002303A (es) Lamina de acero y metodo para fabricar la misma.
MX2021009365A (es) Lamina de acero galvanizada por inmersion en caliente y metodo para producir la misma.
MX2020010053A (es) Lamina de acero galvanizada-recocida.
MX2017010339A (es) Lamina de acero galvanizada de alta resistencia y metodo para la fabricacion de la misma.
MX2023005834A (es) Lamina de acero y metodo para producir la misma.
MX2019012243A (es) Lamina de acero galvanizada por inmersion en caliente de alta resistencia y metodo de produccion de la misma.
MX2021004105A (es) Lamina de acero laminada en caliente y metodo para fabricar la misma.
JP2011063886A (ja) 低サイクル疲労特性に優れた浸炭焼入れ鋼材及び浸炭焼入れ部品
MX2021007559A (es) Lamina de acero laminada en caliente y metodo para fabricar la misma.
MX2022016037A (es) Lamina de acero y metodo de fabricacion de la misma.
MX2021002972A (es) Hoja de acero laminado en caliente con una alta proporcion de expansion de agujero y proceso de fabricacion de la misma.
MX2021008617A (es) Lamina de acero galvanizada de alta resistencia y metodo para la fabricacion de la misma.
MX2021011077A (es) Lamina de acero y metodo de produccion para la misma.
MX2021008840A (es) Lamina de acero galvanizada por inmersion en caliente y metodo para producir la misma.
KR100951249B1 (ko) 수소응력균열 저항성과 저온인성이 우수한 후판강재 및 그제조방법