KR920008209A - 내화성, 내열충격성 산화물 피복을 형성하는 분말공급 조성과 방법 및 그 피복을 갖는 물품 - Google Patents
내화성, 내열충격성 산화물 피복을 형성하는 분말공급 조성과 방법 및 그 피복을 갖는 물품 Download PDFInfo
- Publication number
- KR920008209A KR920008209A KR1019910017861A KR910017861A KR920008209A KR 920008209 A KR920008209 A KR 920008209A KR 1019910017861 A KR1019910017861 A KR 1019910017861A KR 910017861 A KR910017861 A KR 910017861A KR 920008209 A KR920008209 A KR 920008209A
- Authority
- KR
- South Korea
- Prior art keywords
- powder feed
- zro
- feed composition
- powder
- zirconium silicate
- Prior art date
Abstract
내용 없음
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
도면은 동적 및 정적 국부 조건하에 금속 또는 금속산화물을 픽업하기 위한 노상롤상의 애즈-증착 피복성질을 시험하기 위해 사용되는 장치의 개략도이다.
Claims (14)
- CaO, Y2O3, MgO 및 HfO2로 이루어지는 그룹으로 부터 선택한 산화물로 완전히 또는 부분적으로 안정화된 지르코니아 입자를 갖는 혼합물에 존재하는 규산 지르코늄 입자를 포함하는, 금속표면상에 내마모성 내화 산화물 피복을 형성하기 위한 열분무 분말 공급조성.
- 제1항에 있어서, 적어도 약 40wt.%의 상기 안정화된 지르코니아와 60wt.%이하의 규산지르코늄을 함유함을 특징으로 하는 열분무 분말 공급조성.
- 제2항에 있어서, 상기 안정화된 지르코니아 입자가 상기 분말 조성의 주요 성분임을 특징으로 하는 열분무 분말 공급조성.
- 금속기판상에 내마모성 및 내열충격성 내화산화물 피복을 형성시키는 방법에 있어서, CaO, Y2O3, MgO, CeO2및 HfO2로 이루어지는 그룹으로 부터 선택한 산화물로 적어도 부분적으로 안정화되는 지르코늄 분말 입자와 지르코니아 분말입자를 혼합한 것을 포함하는 분말 공급 조성을 조절하는 단계; 및 X-선 상 분석에 의하여 X가 안정화 산화물 ZrSiO4및 SiO2중 하나인 ZrO2·X를 함유하는 애즈-증착된 피복 조성을 형성하기 위해 금속 기판상에 상기 분말 공급조성을 열분무하는 단계를 포함함을 특징으로 하는 방법.
- 제4항에 있어서, 상기 분말입자 조성이 적어도 약 40wt.%의 안정화된 지르코니아와 60wt.%이하의 규산 지르코늄을 함유함을 특징으로 하는 방법.
- 제5항에 있어서, 상기 분말 공급조성을 열분무하기 전에 상기 금속기판상에 세라믹 금속 합금의 하부 피복을 증착시키는 단계를 포함함을 특징으로 하는 방법.
- 제6항에 있어서, 상기 세라믹 금속합금이 Co-Cr-Al-Ta-Y 및 Al2O3를 함유하는 코발트기 금속 기지임을 특징으로 하는 방법.
- 제4 또는 7항에 있어서, 상기 애즈-증착된 피복이 적어도 65wt.%의 상기 부분적으로 안정화된 지르코니아 및 35wt.%이하의 규산 지르코니아를 플라즈마 토오치를 통해 공급함으로써 형성됨을 특징으로 하는 방법.
- 제4 또는 7항에 있어서, 상기 애즈-증착된 피복이 적어도 40wt.%의 상기 부분적으로 안정화된 지르코니아 및 60wt.%이하의 규산 지르코니아를 함유하는 상기 분말 공급 조성을 디토네이션 건에 의해 공급함으로써 형성됨을 특징으로 하는 방법.
- 제9항에 있어서, 상기 분말 공급 조성이 적어도 50wt.%의 부분적으로 안정화된 지르코니아를 함유함을 특징으로 하는 방법.
- X-선 상 분석에 의하여 X를 CaO, Y2O3, MgO , CeO2및 HfO2로 이루어지는 그룹으로 부터 선택하는 ZrO2·X와 ZrSiO4를 함유하는 내화성 산화물층을 갖는 열분무 피복과 금속기판을 가지는 물품.
- 제11항에 있어서, 상기 금속판은 강의 연속 어닐링용 노상롤이고, 상기 ZrO2·X는 적어도 약 40wt.%의 양으로 존재하고 나머지는 규산 지르코늄 및/또는 그것의 분해 생성물 SiO2및 ZrO2임을 특징으로 하는 물품.
- 제12항에 있어서, 상기 ZrO2·X는 55 내지 85wt.%의 양으로 존재하고 나머지는 규산 지르코늄 및/또는 그것의 분해 생성물 SiO2및 ZrO2임을 특징으로 하는 물품.
- 제12항에 있어서, 상기 ZrO2·X는 70 내지 85wt.%의 양으로 존재하고 나머지는 규산 지르코늄 및/또는 그것의 분해 생성물 SiO2및 ZrO2임을 특징으로 하는 물품.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.