KR890012017A - 프리하든 금형강 - Google Patents
프리하든 금형강 Download PDFInfo
- Publication number
- KR890012017A KR890012017A KR1019880000143A KR880000143A KR890012017A KR 890012017 A KR890012017 A KR 890012017A KR 1019880000143 A KR1019880000143 A KR 1019880000143A KR 880000143 A KR880000143 A KR 880000143A KR 890012017 A KR890012017 A KR 890012017A
- Authority
- KR
- South Korea
- Prior art keywords
- less
- mold steel
- sulfur
- manganese
- steel
- Prior art date
Abstract
내용 없음
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (4)
- 프리하든 금형강에 있어서, 탄소(C) 0.30-0.65%, 시리콘(Si) 0.10-1.50%, 망간(Mn) 0.10-1.50%, 크롬(Cr) 3.00-7.00%, 몰리브덴(Mo) 1.00-2.00%, 바나듐(V) 0.20-1.50%, 칼슘(Ca) 0.0005-0.1000%, 지르코늄(Zr) 0.005-0.400%, 셀레니움(Se) 0.0005-0.2000%, 유황(S) 0.005-0.20%,나머지가 철(Fe)과 0.030%이하의 인(P), 0.01%이하의 질소(N)와 산소(O), 0.5%이하의 수소등 불순물로 된 조성(중량%)을 가지며 담금질과 템퍼링에 의한 열처리경도(HRC) 38-42를 갖는 AlㆍZn다이용 및 고급 플라스틱 사출 금형강.
- 제1항에 있어서, 유황(S)의 함량이 0.030%이하로 제한함으로써 황화망간 (MnS)의 생성을 억제하는 것을 특징을 하는 프리하든 금형강.
- 프라히든 금형강의 제조방법에 있어서, 탄소(C) 0.30-0.65%,시리콘(Si) 0.10-1.50%, 망간(Mn) 0.10-1.50%, 크롬(Cr) 3.00-7.00%, 몰리브덴(Mo) 1.00-2.00%, 바나듐(V) 0.20-1.50%, 칼슘(Ca) 0.0005-0.1000%, 지르코늄(Zr) 0.005-0.400%, 셀레니움(Se) 0.0005-0.2000%, 유황(S) 0.005-0.20%, 나머지가 철(Fe)과 0.030%이하의 인(P), 0.01%이하의 질소(N)와 산소(O), 0.5%이하의 수소등 불순물로 된 조성(중량%)을 가지는 금형강을 제강, 단조한 후 840-900℃사이로 어닐링하고 1000-1060℃에서 담금질하며 620-680℃로 템퍼링함을 특징으로 하여 최적경도 38-42의 프리하든 금형강을 제조하는 방법.
- 제3항에 있어서, 620-680℃에서 재템퍼링을 수행하는 것을 특징으로 하는 방법.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.