KR20190128039A - 사출 성형 조성물용 바인더 - Google Patents

사출 성형 조성물용 바인더 Download PDF

Info

Publication number
KR20190128039A
KR20190128039A KR1020190049294A KR20190049294A KR20190128039A KR 20190128039 A KR20190128039 A KR 20190128039A KR 1020190049294 A KR1020190049294 A KR 1020190049294A KR 20190049294 A KR20190049294 A KR 20190049294A KR 20190128039 A KR20190128039 A KR 20190128039A
Authority
KR
South Korea
Prior art keywords
binder
volume
ethylene
injection molding
molding composition
Prior art date
Application number
KR1020190049294A
Other languages
English (en)
Other versions
KR102277881B1 (ko
Inventor
다미앙 까르띠에
조나땅 뒤맹
Original Assignee
코마도 쏘시에떼 아노님
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 코마도 쏘시에떼 아노님 filed Critical 코마도 쏘시에떼 아노님
Publication of KR20190128039A publication Critical patent/KR20190128039A/ko
Application granted granted Critical
Publication of KR102277881B1 publication Critical patent/KR102277881B1/ko

Abstract

본 발명은 사출 성형 컴포지션용 바인더에 관한 것으로,
- 40 ~ 55 부피% 의 폴리머 베이스,
- 35 ~ 45 부피% 의 왁스 혼합물 또는 왁스 및 팜 오일 혼합물, 및
- 적어도 5 부피% 의 적어도 하나의 계면활성제를 포함하고,
폴리머 베이스는 에틸렌 및 메타크릴 또는 아크릴 산의 코폴리머, 에틸렌 및 프로필렌의 코폴리머 및/또는 말레산 무수물 그래프트된 폴리프로필렌, 및 이소프로필 알코올, 프로필 알코올 및/또는 테레빈을 포함하는 군으로부터 선택되고 또한 셀룰로오스 아세테이트 부티레이트, 폴리비닐 부티랄 및 코폴리아미드를 포함하는 군으로부터 선택되는 용매에서 용해성인 폴리머들로 형성되고, 바인더 컴포넌트들의 각 양은 그들의 합이 100 부피% 의 바인더와 동등하도록 되어 있다.

Description

사출 성형 조성물용 바인더{BINDER FOR INJECTION MOULDING COMPOSITIONS}
본 발명은, 형상화된 금속 또는 세라믹 부품들의 제조를 위해 의도되는 사출 성형 조성물용 바인더 및 사출 성형 조성물 (공급원료) 에 관한 것이다.
쥬얼리 및 시계 산업을 위한, 또는 심지어 의료 기구, 전자 장치, 전화 기술, 공구, 기계 절삭 인서트, 소비재 산업을 위한 경질 재료의 제작 시에 그리고 특히 무기 '세라믹' 의 일반명 하에서 일반적으로 지정되는 경질 재료와 관련하여, 금속 야금 기술이 구현된다. 얻어진 합성 무기 재료는 재료의 특성에 관계 없이 본원에서 '세라믹' 으로 불릴 것이고, 이는 사파이어, 루비, 인조 다이아몬드, 사파이어 글래스, 세라믹, 마이크로 마그넷, 금속, 합금 등이다.
일반적으로 말하면, 기본 원료는 본질적으로 상이하고, 적어도 한편으로는 세라믹 분말을 그리고 다른 한편으로는 수지 또는 플라스틱 재료 또는 유사한 것과 같은 유기 바인더를 포함하고, 이는 모든 원료들의 혼합물로 만들어진 컴포넌트의 주입 및 양호한 내성을 고려한다. 다른 첨가제가 혼합물에 포함될 수도 있다. 이러한 원료는 또한 상이한 텍스처, 즉 고체, 분말, 액체 또는 페이스트일 수도 있다. 혼합물의 구조는, 그의 형성 동안, 특히 그러나 배타적이지 않게, 수지의 상보적인 컴포넌트들이 폴리머 반응을 겪을 때에, 또한 변경될 수도 있다.
무기 세라믹 컴포넌트의 전반적인 제작 프로세스는 적어도 이하의 단계들을 포함한다:
- 원료를 준비하는 단계;
- 원료를 혼합하는 단계, 또는/및 필요한 경우 두 개 (또는 그 이상) 씩 예비 혼합하는 단계;
- 균질화 단계;
- 과립화 단계;
- '그린 부품 (green part)' 으로서 공지된 블랭크를 형성하기 위하여, 균질화 및 과립화 단계로부터 얻어진 다량의 분말 또는 공급원료 펠릿들을 특히 프레싱 챔버 내에서 프레싱하는 단계. 이러한 프레싱 작업은, 특히 균질화 및 과립화 단계로부터 얻어진 다량의 분말 또는 공급원료 펠릿들을 가열하기 위한 수단을 포함하는 스크류 인젝터에서, 압력 하에서, 사출 성형에 의해 수행될 수 있다.
- 적합한 용매에서 혼합물의 특정 구성성분의 연소 및/또는 용해 (용매 디바인딩) 를 위해 온도-제어식으로 디바인딩 (열적 디바인딩) 하는 단계;
- 2 차 열적 디바인딩 프로세스를 위한 디바인딩, 및 마무리된 컴포넌트에 최종 코히어런시 (coherency) 를 부여하는 신터링 후에 그린 부품을 열처리하는 단계. 이러한 열처리는 치수 수축을 야기하여, 최종 치수를 갖는 컴포넌트를 얻을 수 있다.
- 컴포넌트의 표면 마무리 처리.
본 발명의 특정 목적은 제어된 수축 계수로 높은 재현가능한 품질의 제품을 얻기 위하여, 세라믹 또는 금속을 얻도록 분말 야금 혼합을 용이하게 하는 최적화된 사출 성형 컴포지션용 바인더를 제공하는 것이다.
예를 들어, 출원인에 의한 특허 출원 WO 2014/191304 는 이미 공지되어 있고, 이는 신터링된 무기 분말 및 유기 바인더를 포함하는 성형된 세라믹 또는 금속 부품들의 제작을 위한 사출 성형 컴포지션 (공급원료) 을 개시하고, 상기 유기 바인더는 본질적으로 에틸렌 및 메타크릴 산의 코폴리머, 폴리에틸렌, 폴리프로필렌, 아크릴 수지 및 왁스의 혼합물로 형성된다.
이러한 공급원료들은 다양한 이점들을 가진다. 더 구체적으로, 공급원료들은 보다 복잡한 형상의 금속 또는 세라믹 부품들의 제작을 허용하는 양호한 균질성과 양호한 유동성을 제공한다. 공급원료들은 생산 스트레스 (핸들링 및 여러 마무리 작업) 에 대한 그린 부품 및 바인더의 기계적 저항을 증가시키고, 또한 간단한 열 처리에 의해 제거될 수 있는 무공해성 용매를 사용하여 유기 바인더의 일부를 제거하도록 용매 디바인딩을 수행할 수 있다.
본 발명의 목적은, 보다 효과적인 용매 디바인딩을 얻기 위하여 그리고 개선된 미적 품질의 컴포넌트들을 얻기 위하여, 사출 컴포지션의 점도를 추가로 개선시키기 위한 신규의 공급원료를 제안함으로써 전술한 단점들을 극복하는 것이다.
그러므로, 본 발명은 사출 성형 컴포지션용 바인더에 관한 것으로,
- 40 ~ 55 부피% 의 폴리머 베이스,
- 35 ~ 45 부피% 의 왁스 혼합물 또는 왁스 및 팜 오일 혼합물, 및
- 적어도 5 부피% 의 적어도 하나의 계면활성제를 포함하고,
상기 폴리머 베이스는 에틸렌 및 메타크릴 또는 아크릴 산의 코폴리머, 에틸렌 및 프로필렌의 코폴리머 및/또는 말레산 무수물 그래프트된 폴리프로필렌, 및 이소프로필 알코올, 프로필 알코올, 테레빈, 및 이들의 혼합물을 포함하는 군으로부터 선택되고 또한 셀룰로오스 아세테이트 부티레이트, 폴리비닐 부티랄 및 코폴리아미드를 포함하는 군으로부터 선택되는 용매에서 용해성인 폴리머들로 형성되고, 바인더 컴포넌트들의 각 양은 그들의 합이 100 부피% 의 바인더와 동등하도록 되어 있다.
또한, 본 발명은 76 ~ 96 wt.% 의 무기 분말 및 4 ~ 24 wt.% 의 전술한 바인더를 포함하는 형상화된 금속 또는 세라믹 부품들의 제작을 위해 의도되는 사출 성형 컴포지션 (공급원료) 에 관한 것이다.
본 발명에 따른 사출 성형 컴포지션은, 보다 효과적인 용매 디바인딩을 얻기 위하여 그리고 개선된 미적 품질의 컴포넌트들을 얻기 위하여, 사출 컴포지션의 점도를 개선시킬 수 있다.
본 발명에 따라, 사출 성형 컴포지션용 바인더는 이하의 컴포넌트들:
- 40 ~ 55 부피%, 바람직하게는 45 ~ 54 부피% 의 폴리머 베이스,
- 35 ~ 45 부피%, 바람직하게는 39 ~ 42 부피% 의 왁스 혼합물 또는 왁스 및 팜 오일 혼합물, 및
- 적어도 5 부피%, 바람직하게는 5 ~ 15 부피% 의 적어도 하나의 계면활성제를 포함하고,
상기 폴리머 베이스는 에틸렌 및 메타크릴 또는 아크릴 산의 코폴리머, 에틸렌 및 프로필렌의 코폴리머 및/또는 말레산 무수물 그래프트된 폴리프로필렌, 및 이소프로필 알코올, 및/또는 프로필 알코올, 및/또는 테레빈을 포함하는 군으로부터 선택되고 또한 셀룰로오스 아세테이트 부티레이트, 폴리비닐 부티랄 및 코폴리아미드를 포함하는 군으로부터 선택되는 용매에서 용해성인 폴리머들로 형성되고, 바인더 컴포넌트들의 각 양은 그들의 합이 100 부피% 의 바인더와 동등하도록 되어 있다.
바람직하게는, 본 발명의 바인더의 폴리머 베이스는, 100 부피% 의 바인더에 대해, 2 ~ 7 부피% 의 에틸렌 및 메타크릴 또는 아크릴 산의 코폴리머, 0 ~ 40 부피% 의 에틸렌 및 프로필렌의 코폴리머, 0 ~ 35 부피% 의 말레산 무수물 그래프트된 폴리프로필렌, 및 이소프로필 알코올 및/또는 프로필 알코올 및/또는 테레빈에서 용해성인 6 ~ 15 부피% 의 폴리머를 포함하고, 에틸렌 및 프로필렌의 코폴리머 및 말레산 무수물 그래프트된 폴리프로필렌의 전반적인 양은 30 ~ 40 부피% 로 포함되고, 바인더 컴포넌트의 각 양은 그들의 합이 100 부피% 의 바인더와 동등하도록 되어 있다.
바람직하게는, 폴리머 베이스는 에틸렌 및 프로필렌의 코폴리머 및 말레산 무수물 그래프트된 폴리프로필렌의 혼합물을 포함한다.
바람직하게는, 본 발명의 바인더의 폴리머 베이스는, 100 부피% 의 바인더에 대해, 2 ~ 7 부피% 의 에틸렌 및 메타크릴 또는 아크릴 산의 코폴리머, 25 ~ 30 부피% 의 에틸렌 및 프로필렌의 코폴리머, 5 ~ 10 부피% 의 말레산 무수물 그래프트된 폴리프로필렌, 및 이소프로필 알코올 및/또는 프로필 알코올 및/또는 테레빈에서 용해성인 6 ~ 15 부피% 의 폴리머를 포함한다.
더 바람직하게는, 본 발명의 바인더의 폴리머 베이스는, 100 부피% 의 바인더에 대해, 3 ~ 5 부피% 의 에틸렌 및 메타크릴 또는 아크릴 산의 코폴리머, 26 ~ 29 부피% 의 에틸렌 및 프로필렌의 코폴리머, 6 ~ 8 부피% 의 말레산 무수물 그래프트된 폴리프로필렌, 및 이소프로필 알코올 및/또는 프로필 알코올 및/또는 테레빈에서 용해성인 6 ~ 12 부피% 의 폴리머를 포함한다.
바람직하게는, 에틸렌-프로필렌 코폴리머는 140℃ ~ 150℃ 의 융점을 갖는 에틸렌 및 프로필렌의 (무작위) 통계적 코폴리머이고, 이러한 융점은 상기 코폴리머 내의 에틸렌 및 프로필렌의 백분율에 따라 변한다. 예를 들어, 옥사이드 및 니트라이드 분말에 대해, 에틸렌 및 프로필렌의 통계적 코폴리머는 바람직하게는 약 147℃ 의 융점을 가지도록 더 많은 프로필렌을 포함한다. 금속 분말에 대해, 에틸렌 및 프로필렌의 통계적 코폴리머는 바람직하게는 약 140℃ 의 융점을 가지도록 더 많은 에틸렌을 포함한다.
바람직하게는, 상기 에틸렌 및 메타크릴 또는 아크릴 산의 코폴리머가 3 ~ 10 wt.% 의 메타크릴 또는 아크릴 코폴리머를 포함한다.
바람직하게는, 말레산 무수물 그래프트된 폴리프로필렌은 1% ~ 2% 의 그래프팅율 및 100℃ ~ 140℃ 의 융점을 갖는다.
바람직하게는, 상기 이소프로필 알코올 및/또는 프로필 알코올 및/또는 테레빈에서 용해성인 폴리머는 폴리머의 중량에 대해 37 wt.% ~ 53 wt.% 의 부티릴 함량, 2 wt.% ~ 13 wt.% 의 아세틸 함량, 125℃ ~ 165℃ 의 융점 및 16000 ~ 40000 의 분자량을 가지는 셀룰로오스 아세테이트 부티레이트이다.
유리하게는, 왁스는 Carnauba 왁스 또는 파라핀 왁스 또는 이러한 원소들의 혼합물이다. 왁스가 팜 오일과의 혼합물일 때, 왁스는 바람직하게는 Carnauba 왁스이다.
다른 바람직한 특징에 따라, 계면활성제는, N,N'-에틸렌 비스스테아로아미드, 또는 스테아르 및 팔미트 산의 혼합물 (스테아린), 또는 이러한 원소들의 혼합물이다.
다른 특징에 따라, 계면활성제는 이소프로필 알코올 및/또는 프로필 알코올 및/또는 테레빈에서 용해성이다.
또한, 본 발명은 76 ~ 96 wt.% 의 무기 분말 및 4 ~ 24 wt.% 의 전술한 바인더를 포함하는 형상화된 금속 또는 세라믹 부품들의 제작을 위해 의도되는 사출 성형 컴포지션 (공급원료) 에 관한 것이다.
특정 특징에 따라, 사출 성형 컴포지션의 무기 분말은 옥사이드 분말, 니트라이드 분말, 카바이드 분말, 금속 분말, 또는 상기 분말들의 혼합물을 포함하는 군으로부터 선택될 수 있고, 바람직하게는 무기 분말은 알루미나 분말, 지르코늄 옥사이드 분말, 크롬 카바이드 분말, 티타늄 카바이드 분말 또는 텅스텐 카바이드 분말, 금속 텅스텐 분말 또는 실리콘 니트라이드 분말, 스테인리스 강 분말, 금속 티타늄 분말 또는 상기 분말들의 혼합물을 포함하는 군으로부터 선택된다.
사출 성형 컴포지션의 바람직한 실시형태에 따라, 사출 성형 컴포지션은, 중량% 로,
- 76 ~ 88% 의 알루미나, 및 전술한 바와 같은 본 발명에 따른 12 ~ 24% 의 바인더, 또는
- 76 ~ 88% 의 알루미나, 0.1 ~ 0.6% 의 산화 마그네슘, 및 본 발명에 따른 12 ~ 24% 의 바인더, 또는
- 58 ~ 86.5% 의 지르코늄 옥사이드, 3.9 ~ 4.6% 의 이트륨 옥사이드, 0.18 ~ 18.5% 의 알루미나, 및 본 발명에 따른 9 ~ 22% 의 바인더, 또는
- 61.5 ~ 84% 의 지르코늄 옥사이드, 3.9 ~ 4.6% 의 이트륨 옥사이드, 0.2 ~ 9% 의 알루미나, 산화철, 산화 코발트, 산화 크롬, 산화 티타늄, 산화 망간, 산화 아연 또는 상기 산화물의 혼합물을 포함하는 리스트로부터의 2 ~ 5.5% 의 무기 안료, 및 본 발명에 따른 9 ~ 22% 의 바인더, 또는
- 88 ~ 91% 의 크롬 또는 티타늄 카바이드, 및 본 발명에 따른 9 ~ 12% 의 바인더, 또는
- 93 ~ 96% 의 텅스텐 카바이드 또는 금속 텅스텐, 및 본 발명에 따른 4 ~ 7% 의 바인더, 또는
- 78 ~ 85% 실리콘 니트라이드, 및 본 발명에 따른 15 ~ 22% 의 바인더를 포함한다.
본 발명에 따른 형상화된 금속 또는 세라믹 부품들의 제작을 위해 의도된 사출 성형 컴포지션 (공급원료) 은 등가 전단 속도에 대해 공지된 공급원료보다 낮은 점도를 갖는다. 결론적으로, 본 발명의 컴포지션은 특히 얇은 벽을 갖는 영역에서 사출 성형 동안 부품들을 보다 양호하게 충전할 수 있다. 더욱이, 본 발명에 따른 컴포지션은, 특히 이소프로필 알코올 및/또는 프로필 알코올 및/또는 테레빈 용매에서 바인더 컴포넌트의 개선된 제거를 통해 부품들의 보다 효과적인 용매 디바인딩을 가능하게 한다. 97℃ 의 비점을 갖는 프로필 알코올은 특히 Carnauba 왁스 (82℃ 의 융점) 의 향상된 제거를 통해 향상된 효율을 위해 보다 높은 온도에서 디바인딩할 수 있다.
본 발명의 컴포지션은 가시적인 균열 또는 용접선 없이 개선된 표면 외관을 가지는 성형 및 신터링된 부품들을 얻을 수 있다.
본 발명은 지금부터 이하의 비제한적인 실시예들에 의해 더 상세하게 설명될 것이다.
실시예들
바인더의 폴리머 부분은 예비 혼합물 (premix) 를 형성하기 위하여 약 150℃ 의 온도에서 무기 분말과 혼합된다. 일종의 균질 페이스트를 형성하기 위하여 상기 예비 혼합물에는 왁스 및 계면활성제가 첨가되고, 온도는 약 180℃ 까지 추가로 증가되고, 상기 균질 페이스트는 그런 다음 냉각 및 과립화되어 응고되고, 그런 다음 공지된 사출 성형 기술에 의해 성형된 부품의 제작에 사용될 수 있는 공급원료를 형성하기 위해 유지된다.
이러한 기술은 캐비티가 있는 몰드에서의 고압, 고온 사출 성형 작업을 통상적으로 포함한다. 부품은 캐비티 내에서 냉각된 다음 몰드로부터 배출된다. 모든 프로세스는 약 170℃ ~ 180℃ 에서 실행된다. 그런 다음 그린 부품은 신터링되기 전에 이소프로필 알코올에서 디바인딩된다. 디바인딩은 부품으로부터 유기 바인더의 일부를 제거하고, 또한 응집력을 유지하기에 충분한 바인더, 또는 다른 말로, 그린 부품의 성형된 형상을 남긴다. 바인더는 통상적으로 부품이 침지되는 용매를 가열함으로써 그린 부품으로부터 제거된다. 이러한 작업 동안, 적어도 40% 의 바인더 컴파운드는 용해되어야 한다. 본 발명의 바인더로, 그린 부품은 통상적으로 이소프로필 알코올 용매 내에 침지되고, 약 70℃ 의 온도로 가열된다. 이러한 온도에서, 왁스 혼합물 또는 왁스 및 오일 혼합물은 계면활성제 및 이소프로필 알코올 용해성 폴리머가 화학적으로 용해되는 동안 열적으로 분해된다. 일단 용매 디바인딩 작업이 완료되면, 부품은 다공성이 된다. 그런 다음, 첫째로, 잔류 바인더를 제거 (통상적으로 400℃ 미만의 온도에서의 열적 디바인딩) 하고, 그런 다음 둘째로, 고온에서 그 부품을 신터링하기 위하여, 부품은 고온의 노에 배치되고, 이러한 작업은 용매 디바인딩 동안 부품 내에 남겨진 다공성에 의해 용이해진다.
부품들은 무기 분말의 특성에 따라 이하의 표 1 에 나타낸 컴포지션으로 본 발명의 여러 바인더로부터 전술한 방법에 따라 만들어진다:
Figure pat00001
컴포넌트들은 상업적으로 이용가능하다. 에틸렌-폴리프로필렌 코폴리머 (무작위의 폴리프로필렌 코폴리머) 는 Total Refining & Chemicals 에 의해 유통되는 PPR 10232 이다. 말레산 무수물 그래프트된 폴리프로필렌은 DuPont™ 에 의해 유통되는 Fusabond® P353 이다. 셀룰로오스 아세테이트 부티레이트는 Eastman™ 에 의해 유통되는 CAB-551-0.01 이다.
컴포지션은 유기 분말로서 Saint-Gobain Zir Black 블랙 지르코늄 옥사이드 ZrO2 분말을 갖는 전술한 실시예 1 에 따라 만들어졌다. 이러한 컴포지션의 점도는 직경 1 mm 및 길이 20 mm 의 다이를 갖는 Instron Ceast SR20 모세관 레오미터로 측정되었다.
비교에 의해, 동일한 Saint-Gobain Zir Black 블랙 무기 지르코늄 옥사이드 ZrO2 분말을 갖는 특허 출원 WO 2014/191304 의 실시예 1 에서 개시된 공급원료 컴포지션의 점도가 측정되었다.
결과들은 이하의 표 2 에서 제시된다.
Figure pat00002
본 발명에 따른 사출 성형 컴포지션은 등가 전단 속도에 대해 공지된 공급원료보다 낮은 점도를 갖는다.
더욱이, 이소프로필 알코올 용매에서 디바인딩되는 동안 바인더의 제거가 개선된다: 용매 내에서 특허 출원 WO2014/191304 에서 개시된 약 45% 의 바인더가 제거되는 반면, 본 발명의 적어도 50% 의 바인더, 특히 셀룰로오스 아세테이트 부티레이트가 제거된다. 금속 분말의 경우, 제거율은 최대 65% 까지 될 수 있다.
얻어진 성형 및 신터링된 부품들은 가시적인 균열 또는 용접선 없이 개선된 표면 외관을 가진다.

Claims (16)

  1. 사출 성형 컴포지션용 바인더로서,
    - 40 ~ 55 부피% 의 폴리머 베이스,
    - 35 ~ 45 부피% 의 왁스 혼합물 또는 왁스 및 팜 오일 혼합물, 및
    - 적어도 5 부피% 의 적어도 하나의 계면활성제를 컴포넌트들로서 포함하고,
    상기 폴리머 베이스는 에틸렌 및 메타크릴 또는 아크릴 산의 코폴리머, 에틸렌 및 프로필렌의 코폴리머 및/또는 말레산 무수물 그래프트된 폴리프로필렌 (maleic anhydride-grafted polypropylene), 및 이소프로필 알코올, 프로필 알코올, 테레빈 (turpentine), 및 이들의 혼합물을 포함하는 군으로부터 선택되고 또한 셀룰로오스 아세테이트 부티레이트, 폴리비닐 부티랄 및 코폴리아미드를 포함하는 군으로부터 선택되는 용매에서 용해성인 폴리머들로 형성되고,
    바인더 컴포넌트들의 각 양은 그들의 합이 100 부피% 의 바인더와 동등하도록 되어 있는, 사출 성형 컴포지션용 바인더.
  2. 제 1 항에 있어서,
    상기 폴리머 베이스는, 100 부피% 의 바인더에 대해, 2 ~ 7 부피% 의 에틸렌 및 메타크릴 또는 아크릴 산의 코폴리머, 0 ~ 40 부피% 의 에틸렌 및 프로필렌의 코폴리머, 0 ~ 35 부피% 의 말레산 무수물 그래프트된 폴리프로필렌, 및 이소프로필 알코올, 프로필 알코올, 테레빈 및 이들의 혼합물을 포함하는 군으로부터 선택된 용매에서 용해성인 6 ~ 15 부피% 의 폴리머를 포함하고, 에틸렌 및 프로필렌의 코폴리머 및 말레산 무수물 그래프트된 폴리프로필렌의 양은 30 ~ 40 부피% 로 포함되고, 바인더 컴포넌트들의 각 양은 그들의 합이 100 부피% 의 바인더와 동등하도록 되어 있는 것을 특징으로 하는, 사출 성형 컴포지션용 바인더.
  3. 제 1 항에 있어서,
    상기 폴리머 베이스는 에틸렌 및 프로필렌의 코폴리머 및 말레산 무수물 그래프트된 폴리프로필렌의 혼합물을 포함하는 것을 특징으로 하는, 사출 성형 컴포지션용 바인더.
  4. 제 3 항에 있어서,
    상기 폴리머 베이스는, 100 부피% 의 바인더에 대해, 2 ~ 7 부피% 의 에틸렌 및 메타크릴 또는 아크릴 산의 코폴리머, 25 ~ 30 부피% 의 에틸렌 및 프로필렌의 코폴리머, 5 ~ 10 부피% 의 말레산 무수물 그래프트된 폴리프로필렌, 및 이소프로필 알코올, 프로필 알코올, 테레빈 및 이들의 혼합물을 포함하는 군으로부터 선택된 용매에서 용해성인 6 ~ 15 부피% 의 폴리머를 포함하는 것을 특징으로 하는, 사출 성형 컴포지션용 바인더.
  5. 제 1 항에 있어서,
    상기 에틸렌 및 프로필렌의 코폴리머는 140℃ ~ 150℃ 의 융점을 갖는 에틸렌 및 프로필렌의 무작위의 통계적 코폴리머인 것을 특징으로 하는, 사출 성형 컴포지션용 바인더.
  6. 제 1 항에 있어서,
    상기 에틸렌 및 메타크릴 또는 아크릴 산의 코폴리머가 3 ~ 10 wt.% 의 메타크릴 또는 아크릴 코폴리머를 포함하는 것을 특징으로 하는, 사출 성형 컴포지션용 바인더.
  7. 제 1 항에 있어서,
    상기 말레산 무수물 그래프트된 폴리프로필렌은 1% ~ 2% 의 그래프팅율 및 100℃ ~ 140℃ 의 융점을 갖는 것을 특징으로 하는, 사출 성형 컴포지션용 바인더.
  8. 제 1 항에 있어서,
    상기 이소프로필 알코올, 프로필 알코올, 테레빈 및 이들의 혼합물을 포함하는 군으로부터 선택된 용매에서 용해성인 폴리머는 폴리머의 중량에 대해 37 wt.% ~ 53 wt.% 의 부티릴 함량, 2 wt.% ~ 13 wt.% 의 아세틸 함량, 125℃ ~ 165℃ 의 융점 및 16000 ~ 40000 의 분자량을 가지는 셀룰로오스 아세테이트 부티레이트인 것을 특징으로 하는, 사출 성형 컴포지션용 바인더.
  9. 제 1 항에 있어서,
    상기 왁스는 Carnauba 왁스, 파라핀 왁스 또는 이들의 혼합물인 것을 특징으로 하는, 사출 성형 컴포지션용 바인더.
  10. 제 1 항에 있어서,
    상기 왁스 및 팜 오일 혼합물에서 왁스는 Carnauba 왁스인 것을 특징으로 하는, 사출 성형 컴포지션용 바인더.
  11. 제 1 항에 있어서,
    상기 계면활성제는, N,N'-에틸렌 비스(스테아로아미드) 또는 스테아르 및 팔미트 산의 혼합물 (스테아린), 또는 이러한 원소들의 혼합물인 것을 특징으로 하는, 사출 성형 컴포지션용 바인더.
  12. 제 1 항에 있어서,
    상기 계면활성제는 이소프로필 알코올, 프로필 알코올, 테레빈 및 이들의 혼합물을 포함하는 군으로부터 선택된 용매에서 용해성인 것을 특징으로 하는, 사출 성형 컴포지션용 바인더.
  13. 76 ~ 96 wt.% 의 무기 분말 및 4 ~ 24 wt.% 의 사출 성형 컴포지션용 바인더를 포함하는 형상화된 금속 또는 세라믹 부품들의 제작을 위해 의도되는 사출 성형 컴포지션 (공급원료) 으로서, 상기 사출 성형 컴포지션용 바인더는
    - 40 ~ 55 부피% 의 폴리머 베이스,
    - 35 ~ 45 부피% 의 왁스 혼합물 또는 왁스 및 팜 오일 혼합물, 및
    - 적어도 5 부피% 의 적어도 하나의 계면활성제를 컴포넌트들로서 포함하고,
    상기 폴리머 베이스는 에틸렌 및 메타크릴 또는 아크릴 산의 코폴리머, 에틸렌 및 프로필렌의 코폴리머 및/또는 말레산 무수물 그래프트된 폴리프로필렌, 및 이소프로필 알코올, 프로필 알코올, 테레빈, 및 이들의 혼합물을 포함하는 군으로부터 선택되고 또한 셀룰로오스 아세테이트 부티레이트, 폴리비닐 부티랄 및 코폴리아미드를 포함하는 군으로부터 선택되는 용매에서 용해성인 폴리머들로 형성되고,
    바인더 컴포넌트들의 각 양은 그들의 합이 100 부피% 의 바인더와 동등하도록 되어 있는, 사출 성형 컴포지션.
  14. 제 13 항에 있어서,
    상기 무기 분말은 옥사이드 분말, 니트라이드 분말, 카바이드 분말, 금속 분말 또는 이들의 혼합물을 포함하는 군으로부터 선택되는, 사출 성형 컴포지션.
  15. 제 14 항에 있어서,
    상기 무기 분말은 알루미나 분말, 지르코늄 옥사이드 분말, 크롬 카바이드 분말, 티타늄 카바이드 분말 또는 텅스텐 카바이드 분말, 금속 텅스텐 또는 실리콘 니트라이드 분말, 스테인리스 강 분말, 금속 티타늄 분말 또는 상기 분말들의 혼합물을 포함하는 군으로부터 선택되는, 사출 성형 컴포지션.
  16. 제 15 항에 있어서,
    - 76 ~ 88 % 의 알루미나, 및 12 ~ 24% 의 바인더,
    - 76 ~ 88% 의 알루미나, 0.1 ~ 0.6% 의 산화 마그네슘, 및 12 ~ 24% 의 바인더,
    - 58 ~ 86.5% 의 지르코늄 옥사이드, 3.9 ~ 4.6% 의 이트륨 옥사이드, 0.18 ~ 18.5% 의 알루미나, 및 9 ~ 22% 의 바인더,
    - 61.5 ~ 84% 의 지르코늄 옥사이드, 3.9 ~ 4.6% 의 이트륨 옥사이드, 0.2 ~ 9% 의 알루미나, 산화철, 산화 코발트, 산화 크롬, 산화 티타늄, 산화 망간, 산화 아연 또는 상기 산화물들의 혼합물을 포함하는 리스트로부터의 2 ~ 5.5% 의 무기 안료, 및 9 ~ 22% 의 바인더,
    - 88 ~ 91% 의 크롬 또는 티타늄 카바이드, 및 9 ~ 12% 의 바인더,
    - 93 ~ 96% 의 텅스텐 카바이드 또는 금속 텅스텐, 및 4 ~ 7% 의 바인더,
    - 78 ~ 85 의 실리콘 니트라이드, 및 15 ~ 22% 의 바인더를, 중량% 로, 포함하는, 사출 성형 컴포지션.
KR1020190049294A 2018-05-04 2019-04-26 사출 성형 조성물용 바인더 KR102277881B1 (ko)