KR20190045666A

KR20190045666A - Super capacitor with high voltage and method for manufacturing the same

Info

Publication number: KR20190045666A
Application number: KR1020170138511A
Authority: KR
Inventors: 허진우; 이문배; 임창건; 조진익
Original assignee: 삼신디바이스 주식회사
Priority date: 2017-10-24
Filing date: 2017-10-24
Publication date: 2019-05-03
Also published as: KR102016520B1

Abstract

The present invention relates to a high-voltage super capacitor and a manufacturing method thereof. The high-voltage super capacitor comprises: an anode; a cathode; an electrolyte solution; and a separator interposed between the anode and the cathode. The electrolyte solution includes an electrolyte, an organic solvent, and a gas generation inhibitor. According to the present invention, the super capacitor has excellent electrical characteristics such as high operation voltage or the like a well as a high capacity. In addition, according to the present invention, the super capacitor has the reliability in a long term period, excellent durability characteristics, etc. as well as the excellent electrical characteristics.

Description

고전압 슈퍼커패시터 및 그 제조방법 {SUPER CAPACITOR WITH HIGH VOLTAGE AND METHOD FOR MANUFACTURING THE SAME} BACKGROUND OF THE INVENTION 1. Field of the Invention [0001] The present invention relates to a high-voltage supercapacitor,

본 발명은 고전압 슈퍼커패시터(Super Capacitor) 및 그 제조방법에 관한 것으로, 하나의 구현예에 따라서 전해액에 가스 발생 억제제를 포함시켜 초고용량을 가짐은 물론 고전압 등의 전기적 특성이 개선된 고전압 슈퍼커패시터 및 그 제조방법에 관한 것이다. BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a high-voltage supercapacitor and a method of manufacturing the same, and more particularly, to a high-voltage supercapacitor having a super- And a manufacturing method thereof.

전기 화학 소자로서의 전기이중층 커패시터(EDLC ; Electric Double Layer Capacitor)나 리튬 커패시터(LiC ; Lithium Capacitor) 등의 초고용량을 가지는 슈퍼커패시터(Super Capacitor)는 일반적인 다른 2차 전지에 비해 에너지 밀도가 높고, 충전과 방전의 반복으로 인한 열화가 작아 보수가 거의 필요 없어 그 수요가 높다. A super capacitor having a very high capacity such as an electric double layer capacitor (EDLC) or a lithium capacitor (LiC) as an electrochemical device has a higher energy density than other general secondary batteries, And the deterioration due to repetition of discharge is small, so that there is almost no need for repair and the demand is high.

이에 따라, 슈퍼커패시터는 각종 전기ㆍ전자기기의 보조전원, IC 백업 전원 등으로 주로 사용되고 있으며, 최근에는 장난감, 산업용 전원, UPS(UNINTERRUPTED POWER SUPPLY), 태양열 에너지 저장, HEV/EV SUB POWER 등에까지 폭넓게 응용되고 있다. As a result, supercapacitors are widely used as auxiliary power supplies for various electric and electronic devices, IC backup power supplies, and the like. In recent years, super capacitors have been widely used for toys, industrial power supplies, uninterruptible power supplies, solar energy storage, Has been applied.

일반적으로, 전기이중층 커패시터(EDLC) 등의 슈퍼커패시터는 양극 및 음극의 두 전극(분극성 전극)과, 상기 두 전극의 사이에 개재되어 이온(ion) 전도만 가능케 하고 단락 방지(절연)를 위한 다공성 재질의 세퍼레이터(separator)와, 양극과 음극이 함침되어 이온(ion)을 전도시키는 전해액을 포함한다. 이때, 상기 양극과 음극은 슈퍼커패시터의 종류에 따라 동일하게 구성되거나 서로 다르게 구성되고 있으며, 대부분의 경우 다공성의 활성탄을 포함한다. 구체적으로, 대부분의 슈퍼커패시터는, 상기 양극과 음극 중에서 적어도 하나 이상의 전극을 알루미늄 포일(Al foil) 등의 금속 집전체 상에 활성탄 전극 조성물(전극 활물질)을 코팅, 압연하여 제조한 것을 주로 사용하고 있다. Generally, supercapacitors such as electric double layer capacitors (EDLC) have two electrodes (polarized electrodes) of an anode and a cathode, and a pair of electrodes which are interposed between the two electrodes to enable only ion conduction, A separator made of a porous material, and an electrolyte solution impregnated with an anode and a cathode to conduct ions. At this time, the positive electrode and the negative electrode may be the same or different depending on the kind of the supercapacitor, and in most cases, they include porous activated carbon. Specifically, most of the supercapacitors are produced by coating at least one of the positive electrode and the negative electrode with an activated carbon electrode composition (electrode active material) coated on a metal current collector such as an aluminum foil and rolling the same have.

활성탄은, 비표면적이 높아 전기이중층 커패시터(EDLC) 등의 전극 재료로서 유용하다. 예를 들어, 전기이중층 커패시터(EDLC)의 용량은 전기이중층에 축적되는 전하량에 따라 정해지며, 그 전하량은 전극의 비표면적이 클수록 증가된다. 이에 따라, 다공성 구조를 가지는 활성탄은 높은 비표면적을 가지므로 전극을 고용량화시키고 에너지 밀도를 향상시킬 수 있다. Activated carbon has a high specific surface area and is useful as an electrode material for electric double layer capacitors (EDLC) and the like. For example, the capacitance of the electric double layer capacitor (EDLC) is determined by the amount of charge accumulated in the electric double layer, and the amount of the electric charge is increased as the specific surface area of the electrode is larger. Accordingly, the activated carbon having the porous structure has a high specific surface area, so that the capacity of the electrode can be increased and the energy density can be improved.

일반적으로, 활성탄은 탄소 원료(탄소 전구체)를 고온에서 탄화시킨 다음, 다공성 구조로 활성화시켜 제조되고 있다. 이때, 활성화 공정에서는 주로 탄소 원료에 수산화칼륨(KOH) 등의 알칼리 활성화제를 혼합한 다음, 불활성 가스 분위기에서 가열하여, 알칼리 금속을 탄소 결정층 사이에 침입, 반응시켜 미세 다공이 형성되도록 하고 있다. 이러한 알칼리 활성화로 수득된 활성탄은 비표면적이 크고, 입자 크기가 균일하여 전기이중층 커패시터(EDLC)의 전극 재료로서 유용하다. 예를 들어, 일본 공개특허 2009-260177호 및 일본 공개특허 2010-245482호 등에는 이와 관련한 기술이 제시되어 있다. Generally, activated carbon is produced by carbonizing a carbon raw material (carbon precursor) at a high temperature and then activating the carbon precursor into a porous structure. At this time, in the activation step, an alkali activating agent such as potassium hydroxide (KOH) is mixed mainly with the carbon raw material, and then heated in an inert gas atmosphere to cause alkali metal to penetrate between the carbon crystal layers and react to form micropores . The activated carbon obtained by such alkali activation has a large specific surface area and uniform particle size, and is useful as an electrode material of an electric double layer capacitor (EDLC). For example, Japanese Patent Application Laid-Open No. 2009-260177 and Japanese Patent Application Laid-Open No. 2010-245482 disclose techniques related to this.

또한, 활성탄은 탄소 원료로서 페놀 수지를 활성화한 제품과 코코넛 쉘(야자 껍질), 살구씨, 왕겨 등을 활성화한 제품이 많이 사용되고 있다. 예를 들어, 대한민국 등록특허 제10-0348499호에는 왕겨를 이용하여 활성탄을 제조하는 방법이 제시되어 있으며, 대한민국 등록특허 제10-0342069호에는 왕겨 활성탄에 바인더(binder) 등을 혼합하여 판상으로 성형하여 제조하는 전극의 제조방법이 제시되어 있다. 그리고 대한민국 등록특허 제10-1105715호에는 페놀 수지계 활성탄과 코코넛 쉘계 활성탄을 이용한 전극의 제조방법이 제시되어 있다. Activated carbon is also widely used as a raw material for carbon, which is activated by phenol resin, activated by coconut shell (coconut shell), apricot seeds and rice hull. For example, Korean Patent No. 10-0348499 discloses a method for producing activated carbon using rice hulls, and Korean Patent No. 10-0342069 discloses a method of mixing a binder and the like in rice hull activated carbon, A method of manufacturing an electrode is disclosed. Korean Patent No. 10-1105715 discloses a method for producing an electrode using phenol resin-based activated carbon and coconut shell-based activated carbon.

일반적으로, 대부분의 활성탄은 불순물 등의 함량이 높아 저항 특성 등이 낮다. 이에 따라, 전기이중층 커패시터(EDLC)의 전극을 제조함에 있어서는 활성탄에 전기전도성의 도전재를 첨가하고 있다. 구체적으로, 입자상의 활성탄과, 활성탄 입자 간을 전기적으로 연결시켜 주는 입자상의 도전재, 및 이들을 결합시키기 위한 바인더(binder) 등을 혼합하여 활성탄 전극 조성물을 얻은 다음, 이를 금속 집전체 상에 코팅, 압연하여 전극을 제조하고 있다. 이때, 상기 도전재로는 주로 카본 블랙(carbon black) 등이 사용된다. 도전재의 첨가에 의해 전기전도도가 향상되어 저항 특성이 개선될 수 있다. 또한, 상기 금속 집전체로는 알루미늄(Al) 등의 금속 박막을 에칭(etching) 처리한 에칭 포일(etching foil)이 주로 사용된다. 에칭 포일은 전극의 표면적을 개선할 수 있다. Generally, most of the activated carbon has a high content of impurities and the like, resulting in low resistance characteristics. Accordingly, in manufacturing an electrode of the electric double layer capacitor (EDLC), an electrically conductive conductive material is added to activated carbon. Specifically, an activated carbon electrode composition is obtained by mixing a particulate activated carbon, a particulate conductive material for electrically connecting activated carbon particles, and a binder for binding them, and then coating the same on the metal current collector, And rolled to manufacture an electrode. At this time, carbon black or the like is mainly used as the conductive material. By the addition of the conductive material, the electric conductivity can be improved and the resistance characteristic can be improved. As the metal current collector, an etching foil in which a thin metal film such as aluminum (Al) is etched is mainly used. The etch foil can improve the surface area of the electrode.

그러나 종래 기술에 따른 전기이중층 커패시터(EDLC)는 용량이 낮다. 예를 들어, 저항 특성의 개선을 위해 도전재를 다량 첨가하는 경우, 상대적으로 활성탄의 함량이 낮아져 높은 정전 용량을 보이기 어렵다. 또한, 종래 기술에 따른 전기이중층 커패시터(EDLC)는 장기 신뢰성이 낮다. 구체적으로, 종래 기술에 따른 전기이중층 커패시터(EDLC)는 사용 시간이 증가함에 따라 내압 상승이나 전극의 열화 등의 이유로 용량이 떨어지고 저항도 증가되는 등의 장기 신뢰성이 낮아지는 문제점이 있다. 아울러, 내압 상승 등의 이유로 높은 동작 전압을 갖기 어렵다. However, the electric double layer capacitor (EDLC) according to the prior art has a low capacity. For example, when a large amount of conductive material is added to improve the resistance characteristic, the content of activated carbon is relatively low, and it is difficult to show a high capacitance. Also, the electric double layer capacitor (EDLC) according to the prior art has low long-term reliability. Specifically, the electric double layer capacitor (EDLC) according to the related art has a problem that the long-term reliability such as a drop in capacitance and an increase in resistance due to an increase in the internal pressure or deterioration of the electrode becomes lower as the use time increases. In addition, it is difficult to obtain a high operating voltage due to an increase in internal pressure or the like.

한편, IC 및 백업전원 등의 제품을 포함한 거의 대부분의 전자제품은 동작 전압이 1.8V 이상, 유용하게는 3V 이상이다. 높게는 전기자동차용의 경우 48V까지의 넓은 전압 범위에서의 사용을 필요로 한다. 이에 따라, 높은 전압을 필요로 하는 제품에는 2개 이상의 단위 셀(unit cell)을 직렬로 연결하여 동작 전압을 적어도 5V로 증가시키고 있으며, 예를 들어 산업용 기기, 전기자동차 및 UPS 등에는 10개 내지 100개의 단위 셀을 직렬/병렬로 패키징(packing)하여 10V 내지 48V의 전압이 구동되도록 하고 있다. On the other hand, almost all electronic products including products such as IC and backup power supply have an operating voltage of 1.8V or more, and advantageously, 3V or more. Highly, it requires use in a wide voltage range up to 48V for electric vehicles. Accordingly, in a product requiring a high voltage, two or more unit cells are connected in series to increase the operating voltage to at least 5 V. For example, in industrial devices, electric vehicles and UPS, 100 unit cells are packed in series / parallel so that a voltage of 10V to 48V is driven.

그러나 2개 이상의 단위 셀을 직렬로 연결하여 전기이중층 커패시터(EDLC)의 동작 전압을 증가시키는 경우에는 필연적으로 발생하는 각 단위 셀 간의 밸런스 문제를 해결해야 하는 또 다른 문제점을 안고 있다. 구체적으로, 단위 셀의 용량, 등가직렬저항(ESR) 및 누설전류 등을 고려하여 전기이중층 커패시터(EDLC)의 전체 동작 전압이 하나의 단위 셀에 집중되지 않도록 저항, 다이오드, 기타 IC 등의 전압 밸런스 보호회로를 필요로 하게 된다. 이때, 더욱더 중요한 것은 위의 패키징 역시 전체 동작 전압의 여유를 주기 위하여, 적어도 1개 정도의 단위 셀을 더 추가하여 전체 전압 분배를 각 단위 셀의 동작 전압보다 월등히 낮게 하여 설계해야 한다. However, when two or more unit cells are connected in series to increase the operating voltage of the electric double layer capacitor (EDLC), there is another problem that must solve the balance problem between each unit cell that necessarily occurs. Specifically, in consideration of the capacity of the unit cell, the equivalent series resistance (ESR), the leakage current, and the like, the voltage balance of the resistor, diode, and other ICs is adjusted so that the entire operating voltage of the electric double layer capacitor A protection circuit is required. In this case, moreover, in order to provide a margin of the total operating voltage, the above packaging should also be designed by adding at least one unit cell so that the total voltage distribution is much lower than the operating voltage of each unit cell.

또한, 에너지 저장에 관한 하나의 자료가 되는 에너지 저장량은 일반적인 2차 전지 등과 마찬가지로 전기이중층 커패시터(EDLC)의 경우에도 에너지의 양을 비교할 수 있는 좋은 지표라 할 수 있다. 이때, 에너지 저장량은 아래와 같은 식을 통하여 구해질 수 있다. Also, the energy storage amount, which is one of the data relating to the energy storage, is a good index for comparing the amount of energy in the case of an electric double layer capacitor (EDLC) like a general secondary battery. At this time, the energy storage amount can be obtained by the following equation.

에너지 저장량(J) = 1/2CV² Energy storage amount (J) = 1 / 2CV ²

(위 식에서, C는 셀의 정전 용량(F), V는 전압이다.)(Where C is the cell's capacitance (F) and V is the voltage).

위 식에 나타낸 바와 같이, 에너지 저장량은 용량(C)과는 비례관계에 있지만, 전압(V)과는 제곱에 비례관계에 있다. 예를 들어, 용량을 2배 증가시키면 에너지 저장량은 2배로 증가하지만, 전압을 2배 증가시키면 에너지 저장량은 4배로 증가한다. 따라서, 전기이중층 커패시터(EDLC)의 최대 에너지의 양을 증가시키는 가장 좋은 방법은 동작 전압(V)을 증가시키는 것이라 할 수 있다. As shown in the above equation, the energy storage amount is proportional to the capacitance (C), but is proportional to the square of the voltage (V). For example, doubling the capacity increases the energy storage by a factor of two, but doubling the voltage increases the energy storage by a factor of four. Therefore, the best way to increase the maximum amount of energy of the electric double layer capacitor (EDLC) is to increase the operating voltage (V).

그러나 종래의 전기이중층 커패시터(EDLC)는 동작 전압(V)이 낮아 높은 에너지 저장량을 보이기 어렵다. 예를 들어, 원통형 전기이중층 커패시터(EDLC)는 2.3 ~ 2.5V의 범위로서 동작 전압(V)이 낮다. 이에 따라, 종래 대부분의 전기이중층 커패시터(EDLC)는 IC 등의 제품에 적용되는 경우에 적어도 2개 이상을 직렬로 연결하여 사용해야 하는 문제점이 있다. 또한, 이 경우에는 인쇄회로기판(PCB)에 설치되는 전기이중층 커패시터(EDLC)의 체적이 증가되어 전기ㆍ전자 제품의 소형화가 어려운 문제점도 있다. However, a conventional electric double layer capacitor (EDLC) has a low operating voltage (V), and thus it is difficult to show a high energy storage amount. For example, a cylindrical electric double layer capacitor (EDLC) has a low operating voltage (V) in the range of 2.3 to 2.5V. Accordingly, most of the conventional electric double layer capacitors (EDLC) have a problem that at least two or more electric double layer capacitors (EDLC) are connected in series when they are applied to products such as ICs. Also, in this case, the volume of the electric double layer capacitor (EDLC) installed on the printed circuit board (PCB) is increased, which makes it difficult to miniaturize the electric / electronic product.

일본 공개특허 2009-260177호Japanese Laid-Open Patent Application No. 2009-260177 일본 공개특허 2010-245482호Japanese Laid-Open Patent Application No. 2010-245482 대한민국 등록특허 제10-0348499호Korean Patent No. 10-0348499 대한민국 등록특허 제10-0342069호Korean Patent No. 10-0342069 대한민국 등록특허 제10-1105715호Korean Patent No. 10-1105715

이에, 본 발명은 개선된 슈퍼커패시터 및 그 제조방법을 제공하는 데에 그 목적이 있다. 본 발명은 하나의 구현예에 따라서, 동작 전압이 개선된 고전압 슈퍼커패시터 및 그 제조방법을 제공하는 데에 그 목적이 있다. Accordingly, it is an object of the present invention to provide an improved supercapacitor and a manufacturing method thereof. According to one embodiment of the present invention, there is provided a high-voltage supercapacitor having an improved operating voltage and a method of manufacturing the same.

본 발명은 다른 구현예에 따라서, 낮은 저항 특성을 유지하면서 높은 용량을 가지는 고전압 슈퍼커패시터 및 그 제조방법을 제공하는 데에 그 목적이 있다. According to another embodiment of the present invention, there is provided a high-voltage supercapacitor having a high capacity while maintaining a low resistance characteristic, and a method of manufacturing the same.

상기 목적을 달성하기 위하여 본 발명은, According to an aspect of the present invention,

양극; anode;

음극; cathode;

전해액; 및 Electrolytic solution; And

상기 양극과 음극의 사이에 개재된 세퍼레이터를 포함하고, And a separator interposed between the positive electrode and the negative electrode,

상기 전해액은 전해질, 유기 용매 및 가스 발생 억제제를 포함하는 슈퍼커패시터를 제공한다. The electrolyte solution includes an electrolyte, an organic solvent, and a gas generation inhibitor.

바람직한 실시 형태에 따라서, 상기 양극과 음극 중에서 선택된 하나 이상은 금속 집전체와, 상기 금속 집전체 상에 형성된 활성탄 전극을 포함하고, 상기 금속 집전체는 활성탄 전극과 접합하는 표면에 산화되어 형성된 금속 산화막층을 포함하는 것이 좋다. 아울러, 상기 활성탄 전극은 활성탄, 바인더 및 도전재를 포함하고, 상기 바인더는 카르복시메틸셀룰로오스와 부타디엔-스티렌-알킬 메타크릴레이트 공중합체를 포함하는 것이 바람직하다. According to a preferred embodiment of the present invention, at least one selected from the anode and the cathode comprises a metal current collector and an activated carbon electrode formed on the metal current collector, Layer. In addition, the activated carbon electrode may include activated carbon, a binder, and a conductive material, and the binder preferably includes carboxymethyl cellulose and a butadiene-styrene-alkyl methacrylate copolymer.

또한, 본 발명은, Further, according to the present invention,

양극을 준비하는 단계; Preparing an anode;

음극을 준비하는 단계; Preparing a cathode;

상기 양극과 음극의 사이에 세퍼레이터를 개재한 적층체를 얻는 단계; 및 Obtaining a laminate including a separator between the anode and the cathode; And

상기 적층체를 전해액에 함침하는 단계를 포함하고, Impregnating the laminate with an electrolytic solution,

상기 전해액은 전해질, 유기 용매 및 가스 발생 억제제를 포함하는 슈퍼커패시터의 제조방법을 제공한다. The electrolyte solution includes an electrolyte, an organic solvent, and a gas generation inhibitor.

바람직한 실시 형태에 따라서, 상기 양극을 준비하는 단계와 음극을 준비하는 단계 중에서 선택된 하나 이상의 단계는, 금속 집전체를 전해 수용액에 침지한 다음, 상기 금속 집전체를 양극(+)으로 하고 전압을 인가하여, 상기 금속 집전체의 표면에 금속 산화막층을 형성하는 공정 a); 및 상기 금속 산화물층 상에 활성탄 전극을 형성하는 공정 b)를 포함하는 것이 좋다. According to a preferred embodiment, at least one step selected from the steps of preparing the positive electrode and preparing the negative electrode comprises: immersing the metal current collector in an electrolytic aqueous solution; A) forming a metal oxide film layer on the surface of the metal current collector; And a step b) of forming an activated carbon electrode on the metal oxide layer.

또한, 바람직한 실시 형태에 따라서, 상기 금속 산화막층을 형성하는 공정 a)에서는 상기 전해 수용액으로서 과염소산(HClO₄)과 옥살산(C₂H₂O₄)을 포함하는 전해 수용액을 사용하고, 1㎛ 내지 5㎛의 두께를 가지는 금속 산화막층을 형성하는 것이 좋다. According to a preferred embodiment, in the step a) of forming the metal oxide film layer, an electrolytic aqueous solution containing perchloric acid (HClO ₄ ) and oxalic acid (C ₂ H ₂ O ₄ ) is used as the electrolytic aqueous solution, It is preferable to form a metal oxide film layer having a thickness of 5 mu m.

아울러, 상기 활성탄 전극을 형성하는 공정 b)에서는 활성탄, 바인더 및 도전재를 포함하는 활성탄 전극 조성물을 시트 상으로 제조한 다음, 상기 시트를 금속 집전체의 금속 산화막층 상에 롤링 압연하여 활성탄 전극을 형성하거나, 활성탄, 바인더 및 도전재를 포함하는 활성탄 전극 조성물을 상기 금속 집전체의 금속 산화막층 상에 코팅한 다음, 롤링 압연하여 활성탄 전극을 형성하되, 상기 롤링 압연은 상온에서 진행하는 것이 바람직하다. In addition, in the step b) of forming the activated carbon electrode, an activated carbon electrode composition including activated carbon, a binder and a conductive material is formed into a sheet, and the sheet is rolled and rolled on the metal oxide layer of the metal current collector to form an activated carbon electrode Or an activated carbon electrode composition including activated carbon, a binder and a conductive material is coated on the metal oxide layer of the metal current collector, and then rolled to form an activated carbon electrode, and the rolling is preferably performed at room temperature .

또한, 상기 활성탄 전극을 형성하는 공정 b)에서는 활성탄, 바인더 및 도전재를 포함하는 활성탄 전극 조성물을 사용하되, 상기 바인더로는 카르복시메틸셀룰로오스와 부타디엔-스티렌-알킬 메타크릴레이트 공중합체를 포함하는 바인더를 사용하는 것이 좋다. In the step b) of forming the activated carbon electrode, an activated carbon electrode composition including activated carbon, a binder and a conductive material is used. As the binder, a binder containing carboxymethylcellulose and a butadiene-styrene-alkyl methacrylate copolymer .

본 발명에 따르면, 개선된 특성을 가지는 슈퍼커패시터 및 그 제조방법이 제공된다. 본 발명에 따르면, 예를 들어 내압 상승이 방지되어 높은 동작 전압(고전압 특성)을 가지는 효과가 있다. 또한, 본 발명에 따르면, 우수한 전기적 특성과 함께 높은 장기 신뢰성 등을 구현하는 효과를 갖는다. According to the present invention, there is provided a supercapacitor having improved characteristics and a method of manufacturing the same. According to the present invention, for example, an increase in the internal pressure is prevented, and the high operating voltage (high voltage characteristic) is obtained. Further, according to the present invention, it has an effect of realizing high long-term reliability with good electrical characteristics.

도 1은 본 발명의 예시적인 실시 형태에 따른 전기이중층 커패시터(EDLC)의 제조 공정도이다.
도 2는 본 발명에 따른 전기이중층 커패시터(EDLC)를 구성하는 금속 집전체의 단면 구성도 및 전극의 제조 공정도이다.
도 3은 본 발명의 실시예 및 비교예에 따른 전극 시트의 층간 접착력 평가 결과를 보인 그래프이다.
도 4는 본 발명의 실시예에 따른 전극 시트의 층간 접착력 평가 결과를 보인 그래프이다. 1 is a manufacturing process diagram of an electric double layer capacitor (EDLC) according to an exemplary embodiment of the present invention.
2 is a cross-sectional view of a metal current collector constituting an electric double layer capacitor (EDLC) according to the present invention and a manufacturing process of the electrode.
3 is a graph showing the results of evaluation of interlaminar adhesive strength of an electrode sheet according to Examples and Comparative Examples of the present invention.
4 is a graph showing the results of evaluating the interlaminar adhesive strength of the electrode sheet according to the embodiment of the present invention.

본 발명에서 "및/또는"은 전후에 나열한 구성요소들 중에서 적어도 하나 이상을 포함하는 의미로 사용된다. 본 발명에서 사용되는 용어 "하나 이상"은 하나 또는 둘 이상을 의미한다. 본 발명에서 "제1" 및 "제2" 등의 용어는 하나의 구성요소를 다른 구성요소로부터 구별하기 위해 사용되며, 각 구성요소가 상기 용어들에 의해 제한되는 것은 아니다. In the present invention, " and / or " is used to mean at least one of the components listed before and after. As used herein, the term " one or more " means one or more than one. In the present invention, terms such as " first " and " second " are used to distinguish one element from another, and the elements are not limited thereto.

또한, 본 발명에서 "상에 형성", "상부에 형성", "상에 설치" 및 "상부에 설치" 등은 당해 구성요소들이 직접 접하여 적층 형성(설치)되는 것만을 의미하는 것은 아니고, 당해 구성요소들 간의 사이에 다른 구성요소가 더 형성(설치)되어 있는 의미를 포함한다. 예를 들어, "상에 형성된다." 및 "상에 설치된다."라는 것은, 제1구성요소에 제2구성요소가 직접 접하여 형성(설치)되는 의미는 물론, 상기 제1구성요소와 제2구성요소의 사이에 제3구성요소가 더 형성(설치)될 수 있는 의미를 포함한다. In addition, in the present invention, " forming on top of ", " forming on top ", " mounting on top ", and " mounting on top " do not mean only that the components are directly laminated And includes the meaning that another component is formed (installed) between the components. For example, " formed on " And " mounted on " means not only that the second component is formed directly in contact with the first component, but also a third component between the first component and the second component It also includes a meaning that can be further formed (installed).

본 발명에 따른 슈퍼커패시터는 양극; 음극; 전해액; 및 상기 양극과 음극의 사이에 개재된 세퍼레이터(separator)를 포함하되, 상기 전해액은 전해질, 유기 용매 및 가스 발생 억제제를 포함한다. A supercapacitor according to the present invention includes: a positive electrode; cathode; Electrolytic solution; And a separator interposed between the anode and the cathode, wherein the electrolyte contains an electrolyte, an organic solvent, and a gas generation inhibitor.

바람직한 실시 형태에 따라서, 상기 양극과 음극 중에서 선택된 적어도 하나 이상은 금속 집전체와, 상기 금속 집전체 상에 형성된 활성탄 전극을 포함하되, 상기 금속 집전체는 활성탄 전극과 접합하는 표면에 산화되어 형성된 금속 산화막층을 포함한다. According to a preferred embodiment of the present invention, at least one selected from the anode and the cathode comprises a metal current collector and an activated carbon electrode formed on the metal current collector, wherein the metal current collector is formed of a metal Oxide layer.

또한, 본 발명에 따른 슈퍼커패시터의 제조방법은 양극을 준비하는 단계; 음극을 준비하는 단계; 상기 양극과 음극의 사이에 세퍼레이터(separator)를 개재한 적층체를 얻는 단계; 및 상기 적층체를 전해액에 함침하는 단계를 포함하되, 상기 전해액으로는 전해질, 유기 용매 및 가스 발생 억제제를 포함하는 용액이 사용된다. According to another aspect of the present invention, there is provided a method of manufacturing a supercapacitor, comprising: preparing a positive electrode; Preparing a cathode; Obtaining a laminate through a separator between the anode and the cathode; And impregnating the laminate with an electrolytic solution, wherein a solution containing an electrolyte, an organic solvent and a gas generation inhibitor is used as the electrolytic solution.

바람직한 실시 형태에 따라서, 상기 양극을 준비하는 단계와 음극을 준비하는 단계 중에서 선택된 적어도 하나 이상의 단계는 금속 집전체를 전해 수용액에 침지한 다음, 상기 금속 집전체를 양극(+)으로 하고 전압을 인가하여 금속 집전체의 표면에 금속 산화막층을 형성하는 공정 a)와; 상기 금속 산화막층 상에 활성탄 전극을 형성하는 공정 b)를 포함한다. According to a preferred embodiment, at least one step selected from the steps of preparing the positive electrode and preparing the negative electrode comprises: dipping the metal current collector in an electrolytic aqueous solution; A) forming a metal oxide film layer on the surface of the metal current collector; And b) forming an activated carbon electrode on the metal oxide film layer.

본 발명에 따르면, 적어도 고전압 특성을 갖는다. 즉, 본 발명에 따르면, 적어도 동작 전압이 향상된다. 하나의 예시에서, 상기 동작 전압(고전압 특성)은 상기 전해액에 포함된 가스 발생 억제제에 의해 향상된다. 다른 예시에서, 상기 동작 전압(고전압 특성)은 활성탄 전극의 구성 및/또는 금속 집전체의 구성에 의해서도 향상된다. 본 발명에 따른 슈퍼커패시터는 종래보다 예를 들어 0.3V 이상 높은 전압에서 작동될 수 있다. 또한, 본 발명에 따르면, 정전 용량 및/또는 저항 등의 전기적 특성, 및/또는 수명 특성 등이 개선되어 장기 신뢰성을 갖는다. According to the present invention, it has at least a high voltage characteristic. That is, according to the present invention, at least the operating voltage is improved. In one example, the operating voltage (high voltage characteristic) is enhanced by the gas generation inhibitor contained in the electrolyte solution. In another example, the operating voltage (high voltage characteristic) is improved by the configuration of the activated carbon electrode and / or the configuration of the metal current collector. The supercapacitor according to the present invention can be operated at a voltage higher than 0.3 V, for example, than in the prior art. Further, according to the present invention, electrical characteristics such as electrostatic capacity and / or resistance and / or lifetime characteristics are improved and long-term reliability is obtained.

이하, 첨부된 도면을 참조하여 본 발명의 예시적인 실시 형태를 설명한다. 첨부된 도면은 본 발명의 예시적인 실시 형태를 도시한 것으로, 이는 단지 본 발명의 이해를 돕기 위해 제공된다. 또한, 이하 본 발명의 예시적인 실시 형태를 설명함에 있어서, 관련된 공지의 범용적인 기능 및/또는 구성에 대한 상세한 설명은 생략한다. Hereinafter, exemplary embodiments of the present invention will be described with reference to the accompanying drawings. BRIEF DESCRIPTION OF THE DRAWINGS The accompanying drawings illustrate exemplary embodiments of the invention and are provided to aid in the understanding of the invention only. In the following description of the exemplary embodiments of the present invention, detailed descriptions of commonly known general functions and / or configurations are omitted.

도 1에는 본 발명의 예시적인 실시 형태에 따른 슈퍼커패시터의 요부 구성도(제조 공정도)가 도시되어 있다. 도 2에는 본 발명에 따른 슈퍼커패시터를 구성하는 금속 집전체의 단면 구성도 및 전극의 제조 공정도가 도시되어 있다. Fig. 1 is a block diagram (manufacturing process diagram) of a supercapacitor according to an exemplary embodiment of the present invention. FIG. 2 is a cross-sectional view of a metal current collector constituting a supercapacitor according to the present invention and a process of manufacturing the electrode.

이하, 첨부된 도면을 참고하여, 본 발명에 따른 슈퍼커패시터의 실시 형태를 설명함에 있어, 전기이중층 커패시터(EDLC)를 예로 들어 설명한다. 그러나 본 발명에 따른 슈퍼커패시터는 전기이중층 커패시터(EDLC)로 국한되지 않으며, 이는 에너지를 저장하는 전기 화학 소자로서 리튬이온 커패시터(LiC ; Lithium Ion Capacitor), 의사 커패시터(Pseudo Capacitor) 및 하이브리드 커패시터(Hybrid Capacitor) 등은 물론이고 리튬이온 이차전지 및 리튬 폴리머 전지 등을 포함할 수 있다. Hereinafter, an embodiment of a supercapacitor according to the present invention will be described with reference to an electric double layer capacitor (EDLC). However, the supercapacitor according to the present invention is not limited to an electric double layer capacitor (EDLC), and it is an electrochemical device for storing energy, such as a lithium ion capacitor (LiC), a pseudo capacitor (PseudoCapacitor), and a hybrid capacitor Capacitors, etc., as well as lithium ion secondary batteries and lithium polymer batteries.

또한, 본 발명에서 사용되는 용어 "전기적 특성"은 슈퍼커패시터의 용량, 에너지 밀도, 전압, 저항 및 누설 전류 등으로부터 선택된 적어도 하나 이상을 의미한다. 예를 들어, "전기적 특성이 우수하다(개선된다)."라는 것은 "슈퍼커패시터의 용량, 에너지 밀도, 전압, 저항 및 누설 전류 등으로부터 선택된 적어도 하나 이상이 우수하다(개선된다)."라는 것을 의미한다. The term " electrical characteristic " used in the present invention means at least one or more selected from the capacity, energy density, voltage, resistance and leakage current of the supercapacitor. For example, " excellent electrical characteristics (improved) " means that at least one selected from the capacity, energy density, voltage, resistance and leakage current of the super capacitor is excellent it means.

먼저, 도 1을 참조하면, 본 발명에 따른 전기이중층 커패시터(EDLC)는 적어도 하나 이상의 양극(10); 적어도 하나 이상의 음극(20); 적어도 하나 이상의 세퍼레이터(30); 및 전해액을 포함한다. 상기 세퍼레이터(30)는 양극(10)과 음극(20)의 사이에 개재된다. 본 발명에 따른 전기이중층 커패시터(EDLC)는, 예를 들어 세퍼레이터(30)를 사이에 두고 양극(10)과 음극(20)이 교대로 적층된 적층체(100)를 포함하되, 이러한 적층체(100)를 적어도 하나 이상 포함한다. 그리고 양극(10)과 음극(20)은 전해액에 함침된다. Referring first to FIG. 1, an electric double layer capacitor (EDLC) according to the present invention includes at least one anode 10; At least one cathode (20); At least one separator (30); And an electrolytic solution. The separator 30 is sandwiched between the positive electrode 10 and the negative electrode 20. The electric double layer capacitor (EDLC) according to the present invention includes a stacked body 100 in which an anode 10 and a cathode 20 are alternately stacked with a separator 30 interposed therebetween, 100). The positive electrode 10 and the negative electrode 20 are impregnated with the electrolytic solution.

본 발명에서 상기 양극(10), 음극(20) 및 세퍼레이터(30)의 개수는 제한되지 않는다. 또한, 본 발명에 따른 전기이중층 커패시터(EDLC)는 원통형(와인딩형), 각형(박스형), 코인형 및 파우치형 등으로부터 선택될 수 있으며, 그 형상이나 종류는 특별히 제한되지 않는다. In the present invention, the number of the positive electrode 10, the negative electrode 20, and the separator 30 is not limited. In addition, the electric double layer capacitor (EDLC) according to the present invention can be selected from a cylindrical (winding) type, a rectangular type (box type), a coin type, and a pouch type, and the shape and kind thereof are not particularly limited.

도 1에는 원통형의 전기이중층 커패시터(EDLC)가 예시되어 있다. 도 1에 예시한 바와 같이, 상기 양극(10), 음극(20) 및 세퍼레이터(30)를 포함하는 적층체(100)는 원통형으로 와인딩(winding)된 다음, 테이프(50)에 의해 밴딩(banding)될 수 있다. 또한, 상기 양극(10) 및 음극(20)에는 각각 양극 단자(15) 및 음극 단자(25)가 형성되고, 상기 각 단자(15)(25)의 일부는 외부로 인출될 수 있다. Figure 1 illustrates a cylindrical electric double layer capacitor (EDLC). 1, the laminate 100 including the positive electrode 10, the negative electrode 20 and the separator 30 is wound in a cylindrical shape and then subjected to banding ). The positive and negative electrodes 15 and 25 are formed on the anode 10 and the cathode 20 respectively and a part of the terminals 15 and 25 may be drawn out.

상기 적층체(100)는 하우징(200)에 내장될 수 있다. 이때, 상기 하우징(200) 내에는 전해액이 주입되어, 적어도 상기 양극(10) 및 음극(20)은 전해액에 함침된다. 상기 하우징(200)은, 예를 들어 알루미늄(Al) 등의 금속재 및/또는 플라스틱재 등으로 구성될 수 있다. 아울러, 본 발명의 예시적인 실시 형태에 따라서, 상기 하우징(200)의 상부에는 마감판(도시하지 않음)이 설치된 다음, 상단 단부를 구부리는 커링(curling) 공정을 통해 마감될 수 있다. The laminate 100 may be embedded in the housing 200. At this time, an electrolytic solution is injected into the housing 200, and at least the anode 10 and the cathode 20 are impregnated with the electrolytic solution. The housing 200 may be made of, for example, a metal material such as aluminum (Al) and / or a plastic material. In addition, according to an exemplary embodiment of the present invention, a finishing plate (not shown) may be installed on the upper portion of the housing 200, and then closed by a curling process in which the upper end is bent.

상기 양극(10) 및 음극(20)은 금속 집전체(12)(22)와, 상기 금속 집전체(12)(22) 상에 형성된 활성탄 전극(14)(24)을 포함한다. 상기 활성탄 전극(14)(24)은 금속 집전체(12)(22)의 적어도 한 면에 형성된다. 구체적으로, 상기 활성탄 전극(14)(24)은 금속 집전체(12)(22)의 한쪽 면에만 형성되거나, 양쪽 면 모두에 형성될 수 있다. 이하, 본 발명에 따른 전기이중층 커패시터(EDLC)를 구성하는 각 구성요소의 예시적인 실시 형태를 설명하면 다음과 같다. The anode 10 and the cathode 20 include metal collectors 12 and 22 and activated carbon electrodes 14 and 24 formed on the metal collectors 12 and 22. The activated carbon electrodes 14 and 24 are formed on at least one surface of the metal collectors 12 and 22. Specifically, the activated carbon electrodes 14 and 24 may be formed on only one side of the metal collectors 12 and 22, or on both sides of the metal collectors 12 and 22. Hereinafter, an exemplary embodiment of each component constituting the electric double layer capacitor (EDLC) according to the present invention will be described.

[1] 금속 집전체[1] metal collectors

상기 금속 집전체(12)(22)는 금속 포일(metal foil)로부터 선택된다. 상기 금속 집전체(12)(22)는, 구체적인 예를 들어 알루미늄(Al), 구리(Cu), 티탄(Ti), 니켈(Ni), 스테인레스 스틸(SUS) 또는 이들의 합금으로부터 선택된 금속 박막으로 구성될 수 있다. 이때, 상기 금속 집전체(12)(22)는 높은 표면적을 위해 표면이 에칭(etching) 처리된 금속 에칭 포일(metal etching foil)로부터 선택되는 것이 바람직하다. 하나의 예시에서, 상기 금속 집전체(12)(22)는 알루미늄(Al) 에칭 포일을 유용하게 사용할 수 있다. The metal collectors 12 and 22 are selected from a metal foil. The metal current collectors 12 and 22 are made of a metal thin film selected from aluminum (Al), copper (Cu), titanium (Ti), nickel (Ni), stainless steel (SUS) Lt; / RTI > At this time, it is preferable that the metal current collectors 12 and 22 are selected from a metal etching foil whose surface is etched for a high surface area. In one example, the metal current collectors 12 and 22 may advantageously use an aluminum (Al) etched foil.

또한, 상기 금속 집전체(12)(22)는, 예를 들어 15㎛ 이하의 두께(T)를 가질 수 있다. 상기 금속 집전체(12)(22)는, 구체적인 예를 들어 2㎛ 내지 15㎛의 두께(T)를 가질 수 있다. 이때, 금속 집전체(12)(22)의 두께(T)가 2㎛ 미만으로서 너무 얇으면 고전압 특성 등이 낮아질 수 있고, 15㎛를 초과하여 너무 두꺼우면 플렉시블(flexible) 특성 등이 떨어질 수 있다. 이러한 점을 고려할 때, 상기 금속 집전체(12)(22)는 5㎛ 내지 12㎛의 두께(T)를 가지는 것이 바람직하다. The metal collectors 12 and 22 may have a thickness T of, for example, 15 占 퐉 or less. The metal current collectors 12 and 22 may have a thickness T of 2 to 15 占 퐉, for example. At this time, when the thickness T of the metal current collectors 12 and 22 is less than 2 mu m, the high voltage characteristics and the like may be lowered if it is too thin, and the flexible characteristics and the like may be lowered if it is too thick . In consideration of this point, it is preferable that the metal current collectors 12 and 22 have a thickness T of 5 mu m to 12 mu m.

본 발명의 실시 형태에 따라서, 상기 양극(10) 및 음극(20)을 구성하는 금속 집전체(12)(22) 중에서 적어도 하나 이상의 금속 집전체(12)(22)는 산화에 의해 형성된 금속 산화막층(12a)(22a)을 포함한다. 구체적으로, 도 2를 참조하면, 상기 금속 집전체(12)(22)는 활성탄 전극(14)(24)과 접합하는 표면에 금속 산화막층(12a)(22a)이 형성된 구조를 갖는다. 이때, 양극(10) 및 음극(20)을 구성하는 둘 모두의 금속 집전체(12)(22)가 금속 산화막층(12a)(22a)을 포함하는 것이 바람직하다. According to the embodiment of the present invention, at least one of the metal collectors 12 and 22 among the metal collectors 12 and 22 constituting the positive electrode 10 and the negative electrode 20 is a metal oxide film Layer 12a (22a). 2, the metal collectors 12 and 22 have a structure in which metal oxide layers 12a and 22a are formed on the surfaces of the metal collectors 12 and 22, which are joined to the activated carbon electrodes 14 and 24, respectively. At this time, it is preferable that both the metal collectors 12 and 22 constituting the anode 10 and the cathode 20 include the metal oxide film layers 12a and 22a.

상기 금속 산화막층(12a)(22a)은 금속 집전체(12)(22)의 표면 산화에 의해 형성되며, 이는 다공성을 갖는다. 또한, 도 2에 도시한 바와 같이, 상기 금속 산화막층(12a)(22a)은 요철 구조(a)를 가질 수 있다. 이때, 상기 요철 구조(a)는, 예를 들어 랜덤(random)하고, 불규칙한 조도(roughness)를 갖는다. 본 발명에 따르면, 이러한 금속 산화막층(12a)(22a)에 의해, 적어도 활성탄 전극(14)(24)과 금속 집전체(12)(22) 간의 접촉 면적이 넓어져 고용량을 갖는다. 이와 함께 활성탄 전극(14)(24)과 금속 집전체(12)(22) 간의 층간 결합력이 향상된다. The metal oxide film layers 12a and 22a are formed by surface oxidation of the metal collectors 12 and 22 and have porosity. Further, as shown in Fig. 2, the metal oxide film layer 12a (22a) may have a concavo-convex structure (a). At this time, the concavo-convex structure (a) has, for example, random and irregular roughness. According to the present invention, the contact area between at least the activated carbon electrodes 14 and 24 and the metal collectors 12 and 22 is widened by the metal oxide film layers 12a and 22a to have a high capacity. The interlayer coupling force between the activated carbon electrodes 14 and 24 and the metal collectors 12 and 22 is improved.

또한, 상기 금속 산화막층(12a)(22a)은, 예를 들어 0.1㎛ 내지 10㎛의 두께(Ta)를 가질 수 있다. 이때, 금속 산화막층(12a)(22a)의 두께(Ta)가 0.1㎛ 미만인 경우, 이의 형성에 따른 접촉 면적의 개선(용량 개선) 등의 효과가 미미할 수 있다. 그리고 금속 산화막층(12a)(22a)의 두께(Ta)가 10㎛를 초과하는 경우, 예를 들어 저항 특성 등이 바람직하지 않을 수 있다. 이러한 점을 고려할 때, 상기 금속 산화막층(12a)(22a)은 0.5㎛ 내지 8㎛, 또는 1㎛ 내지 5㎛의 두께(Ta)를 가지는 것이 바람직하다. The metal oxide film layers 12a and 22a may have a thickness (Ta) of, for example, 0.1 탆 to 10 탆. At this time, when the thickness Ta of the metal oxide film layer 12a (22a) is less than 0.1 占 퐉, the effect of improving the contact area (capacity improvement) due to its formation may be insignificant. When the thickness (Ta) of the metal oxide film layer 12a (22a) exceeds 10 占 퐉, for example, the resistance characteristic and the like may not be preferable. Considering this point, it is preferable that the metal oxide film layer 12a (22a) has a thickness (Ta) of 0.5 占 퐉 to 8 占 퐉, or 1 占 퐉 to 5 占 퐉.

본 발명의 바람직한 실시 형태에 따라서, 상기 금속 집전체(12)(22)는 5㎛ 내지 12㎛의 두께(T)를 가지되, 여기에 형성된 상기 금속 산화막층(12a)(22a)은 1㎛ 내지 5㎛의 두께(Ta)를 가지는 것이 활성탄 전극(14)(24)과의 접촉 면적의 개선(용량 개선), 저항 특성 및/또는 고전압 특성(동작 전압) 등에서 바람직하다. According to a preferred embodiment of the present invention, the metal current collectors 12 and 22 have a thickness T of 5 占 퐉 to 12 占 퐉, and the metal oxide film layers 12a and 22a formed thereon have a thickness of 1 占 퐉 (Capacity improvement), resistance characteristics, and / or high-voltage characteristics (operation voltage) of the contact area with the activated carbon electrodes 14 and 24 are preferable.

상기 금속 산화막층(12a)(22a)은 전해 방식을 이용한 산화 반응을 통해 형성된다. 이때, 전해 산화 시, 상기 금속 집전체(12)(22)를 양극(+)으로 한다. 그리고 전해 산화 시 음극(-)은, 예를 들어 흑연판(또는 흑연봉) 등의 탄소체를 사용할 수 있다. 또한, 전해 산화 시, 전해 수용액으로는 산(acid) 수용액을 사용한다. The metal oxide film layers 12a and 22a are formed through an oxidation reaction using electrolysis. At this time, in the electrolytic oxidation, the metal collectors 12 and 22 are made positive (+). As the negative electrode (-) for electrolytic oxidation, for example, a carbon material such as a graphite plate (or a black rope) can be used. In electrolytic oxidation, an aqueous acid solution is used as the electrolytic aqueous solution.

하나의 실시 형태에 따라서, 전해조에 산(acid) 수용액을 주입한 다음, 상기 금속 집전체(12)(22)와 흑연판을 산(acid) 수용액에 침지하고, 양극(+)에는 금속 집전체(12)(22)를 연결한다. 그리고 음극(-)에는 흑연판을 연결한 후, 전압을 인가한다. 이와 같이 전압을 인가하면, 산화가 진행되어, 금속 집전체(12)(22)의 표면에 다공성의 금속 산화막층(12a)(22a)이 성장되며, 금속 산화막층(12a)(22a)의 표면은 요철 구조(a)를 갖는다. An acid aqueous solution is injected into the electrolytic bath according to one embodiment and then the metal current collectors 12 and 22 and the graphite plate are immersed in an aqueous acid solution, (12) and (22). Then, a graphite plate is connected to the negative electrode (-), and then a voltage is applied. When the voltage is applied in this way, the oxidation proceeds to grow porous metal oxide film layers 12a and 22a on the surfaces of the metal collectors 12 and 22, and the surface of the metal oxide film layers 12a and 22a Has a concavo-convex structure (a).

또한, 위와 같은 전해 산화 시, 인가되는 전압, 전압의 인가 시간 및/또는 전해 수용액의 온도 등의 조절을 통해 금속 산화막층(12a)(22a)의 두께(Ta)를 제어할 수 있다. 예를 들어, 5V 내지 15V의 전압에서 30초(sec) 내지 30분(min) 동안 산화를 진행할 수 있다. 그리고 전해 수용액은 10℃ 내지 50℃의 온도로 유지해 줄 수 있다. 이러한 조건에서 산화를 진행하는 경우, 상기 예시한 바와 같은 두께(Ta) 범위를 가지는 금속 산화막층(12a)(22a)을 형성시킬 수 있다. 그리고 특별히 한정하는 것은 아니지만, 상기 전해 산화 시에는 약 0.2A 내지 5A의 전류가 인가될 수 있다. In addition, the thickness Ta of the metal oxide layer 12a 22a can be controlled by adjusting the applied voltage, the application time of the voltage, and / or the temperature of the electrolytic aqueous solution during the electrolytic oxidation. For example, the oxidation can be performed at a voltage of 5 V to 15 V for 30 seconds (sec) to 30 minutes (min). And the electrolytic aqueous solution can be maintained at a temperature of from 10 캜 to 50 캜. When the oxidation proceeds under these conditions, the metal oxide film layers 12a and 22a having the above-described thickness Ta can be formed. Although not particularly limited, a current of about 0.2 A to 5 A may be applied during the electrolytic oxidation.

아울러, 바람직한 구현예에 따라서, 상기 전해 산화 시에는 초음파 발생기를 이용하여 전해 수용액에 초음파 진동을 가할 수 있다. 이와 같이 초음파 진동을 가하면서 산화를 진행하는 경우, 금속 산화막층(12a)(22a)의 다공성, 요철 구조(a) 및/또는 성장 속도 등이 개선될 수 있다. In addition, according to a preferred embodiment, ultrasonic vibration may be applied to the electrolytic aqueous solution using the ultrasonic generator during the electrolytic oxidation. When oxidation proceeds while applying ultrasonic vibration as described above, the porosity, the concavo-convex structure (a) and / or growth rate of the metal oxide film layers 12a and 22a can be improved.

상기 전해 수용액은 과염소산(HClO₄), 황산(H₂SO₄), 염산(HCl), 질산(HNO₃) 및 인산(H₃PO₄) 등으로부터 선택된 하나 이상의 산(acid)을 포함하는 수용액을 사용할 수 있다. 이때, 바람직한 실시 형태에 따라서, 상기 전해 수용액은 옥살산(C₂H₂O₄)을 더 포함하는 것이 좋다. 구체적으로, 상기 전해 수용액은 제1산과 제2산을 포함하되, 상기 제1산은 과염소산(HClO₄), 황산(H₂SO₄), 염산(HCl), 질산(HNO₃) 및 인산(H₃PO₄) 등으로부터 선택된 하나 이상이고, 상기 제2산은 옥살산(C₂H₂O₄)으로부터 선택되어, 상기 전해 수용액은 옥살산(C₂H₂O₄)을 더 포함하는 것이 바람직하다. 이와 같이, 전해 수용액에 옥살산(C₂H₂O₄)이 더 포함된 경우, 금속 산화막층(12a)(22a)의 내화학성 및/또는 경도 등이 개선된다. The electrolytic aqueous solution is an aqueous solution containing at least one acid selected from perchloric acid (HClO ₄ ), sulfuric acid (H ₂ SO ₄ ), hydrochloric acid (HCl), nitric acid (HNO ₃ ) and phosphoric acid (H ₃ PO ₄ ) Can be used. At this time, according to a preferred embodiment, it is preferable that the electrolytic aqueous solution further contains oxalic acid (C ₂ H ₂ O ₄ ). Specifically, the electrolytic solution comprises a first acid and a second acid, said first acid is perchloric acid (HClO _4), sulfuric acid (H ₂ SO _4), hydrochloric acid (HCl), nitric acid (HNO ₃₎ and phosphoric acid (H ₃ PO ₄ ), and the like, and the second acid is selected from oxalic acid (C ₂ H ₂ O ₄ ), and the electrolytic aqueous solution preferably further comprises oxalic acid (C ₂ H ₂ O ₄ ). As described above, when oxalic acid (C ₂ H ₂ O ₄ ) is further contained in the electrolytic aqueous solution, the chemical resistance and / or hardness of the metal oxide film layers 12a and 22a are improved.

구체적으로, 상기 나열한 제1산만을 포함하는 전해 수용액을 사용하는 경우보다 제2산으로서 옥살산(C₂H₂O₄)을 더 포함하는 전해 수용액을 사용하는 경우, 금속 산화막층(12a)(22a)의 내화학성 및/또는 경도 등이 개선된다. 상기 금속 산화막층(12a)(22a)은 전기이중층 커패시터(EDLC)의 전해액(특히, 유기 용매)에 의해 용해될 수 있는데, 위와 같이 옥살산(C₂H₂O₄)을 더 포함하는 전해 수용액을 사용하여 산화시키는 경우, 금속 산화막층(12a)(22a)의 내화학성 및/또는 경도 등이 개선되어 전해액에 의해 의한 용해가 방지될 수 있다. 이에 따라, 예를 들어 충/방전 시 가스 발생이 적고, 전기적 특성이 개선될 수 있다. 아울러, 상기 제1산으로서 과염소산(HClO₄)을 사용하는 경우에 금속 산화막층(12a)(22a)의 다공성, 요철 구조(a) 및/또는 성장 속도 등에서 유리하다. Specifically, in the case of using an electrolytic aqueous solution containing oxalic acid (C ₂ H ₂ O ₄ ) as a second acid rather than the electrolytic aqueous solution containing the first disturbance listed above, the metal oxide film layer 12a (22a The chemical resistance and / or the hardness and the like are improved. The metal oxide film layers 12a and 22a may be dissolved by an electrolyte (particularly an organic solvent) of an electric double layer capacitor (EDLC). An electrolytic aqueous solution containing oxalic acid (C ₂ H ₂ O ₄ ) It is possible to improve the chemical resistance and / or hardness of the metal oxide film layers 12a and 22a and to prevent dissolution by the electrolytic solution. Thus, for example, gas generation during charging / discharging is small and electrical characteristics can be improved. In addition, when perchloric acid (HClO ₄ ) is used as the first acid, it is advantageous in terms of the porosity, the concavo-convex structure (a) and / or the growth rate of the metal oxide film layers 12a and 22a.

하나의 실시 형태에 따라서, 상기 전해 수용액은, 전해 수용액 전체 중량 기준으로 상기 나열한 제1산 5 ~ 15중량%, 제2산(옥살산) 0.5 ~ 3중량% 및 잔량의 물(증류수 등)을 포함할 수 있다. 또한, 상기 전해 수용액은 전기를 더 잘 흐르게 하는 전도성 염을 더 포함할 수 있으며, 이러한 전도성 염은 전해 수용액 전체 중량 기준으로 예를 들어 2 ~ 15중량%로 포함될 수 있다. According to one embodiment, the electrolytic aqueous solution contains 5 to 15% by weight of the first acid, 0.5 to 3% by weight of the second acid (oxalic acid) and the remaining amount of water (distilled water, etc.) based on the total weight of the electrolytic aqueous solution can do. In addition, the electrolytic aqueous solution may further include a conductive salt which flows electricity more efficiently, and the conductive salt may be contained in an amount of, for example, 2 to 15% by weight based on the total weight of the electrolytic aqueous solution.

상기 전도성 염은 특별히 제한되지 않으며, 이는 예를 들어 붕산나트륨(NaBO₂) 및/또는 염화나트륨(NaCl) 등으로부터 선택될 수 있다. 하나의 예시에서, 상기 전해 수용액은 과염소산(HClO₄) 5 ~ 15중량%, 옥살산(C₂H₂O₄) 0.5 ~ 3중량%, 붕산나트륨(NaBO₂) 2 ~ 15중량% 및 잔량의 물(증류수 등)을 포함할 수 있다. The conductive salt is not particularly limited, and may be selected from, for example, sodium borate (NaBO ₂ ) and / or sodium chloride (NaCl). In one example, the electrolytic aqueous solution comprises 5 to 15 wt% of perchloric acid (HClO ₄ ), 0.5 to 3 wt% of oxalic acid (C ₂ H ₂ O ₄ ), 2 to 15 wt% of sodium borate (NaBO ₂ ) (Such as distilled water).

[2] 활성탄 전극[2] activated carbon electrode

상기 활성탄 전극(14)(24)은, 바람직하게는 활성탄, 바인더(binder) 및 도전재를 포함한다. 활성탄 전극(14)(24)은 상기와 같은 금속 집전체(12)(22)의 금속 산화막층(12a)(22a) 상에 형성된다. 구체적으로 활성탄, 바인더 및 도전재를 포함하는 활성탄 전극 조성물을 이용하여, 상기 금속 집전체(12)(22)의 금속 산화막층(12a)(22a) 상에 적어도 1층 이상의 활성탄 전극(14)(24)을 형성한다. The activated carbon electrodes 14 and 24 preferably include activated carbon, a binder, and a conductive material. The activated carbon electrodes 14 and 24 are formed on the metal oxide film layers 12a and 22a of the metal collectors 12 and 22 as described above. More specifically, at least one activated carbon electrode 14 ((a) is formed on the metal oxide film layer 12a (22a) of the metal current collectors 12 and 22 by using an activated carbon electrode composition including activated carbon, a binder and a conductive material. 24 are formed.

이때, 상기 활성탄 전극(14)(24)은, 예를 들어 활성탄, 바인더 및 도전재를 포함하는 활성탄 전극 조성물을 시트(sheet) 상으로 제조한 다음, 상기 시트를 금속 집전체(12)(22)의 금속 산화막층(12a)(22a) 상에 롤링(rolling) 압연하여 형성하거나, 상기 활성탄 전극 조성물을 금속 집전체(12)(22)의 금속 산화막층(12a)(22a) 상에 코팅 및 건조한 다음, 롤링 압연하여 형성할 수 있다. 도 2에는 활성탄 전극 조성물이 금속 집전체(12)(22)의 금속 산화막층(12a)(22a) 상에 코팅 및 건조된 다음, 롤러(R)를 통해 롤링 압연되고 있는 모습이 예시되어 있다. At this time, the activated carbon electrodes 14 and 24 may be produced by forming an activated carbon electrode composition including, for example, activated carbon, a binder and a conductive material on a sheet, Or by rolling and rolling the activated carbon electrode composition on the metal oxide film layers 12a and 22a of the metal collectors 12 and 22, Dried, and then rolled and rolled. 2 shows an activated carbon electrode composition coated and dried on the metal oxide layers 12a and 22a of the metal collectors 12 and 22 and rolled through a roller R.

또한, 상기 활성탄 전극(14)(24)을 형성함에 있어, 롤링 압연 시에는 통상과 같은 범위의 온도가 가해질 수 있다. 롤링 압연 시, 예를 들어 120℃ 내지 180℃의 온도가 가해질 수 있다. 즉, 도 2를 참조하면, 롤러(R)를 이용한 롤링 압연 시, 상기 롤러(R)의 온도를 120℃ 내지 180℃로 유지하여 롤링 압연할 수 있다. In forming the activated carbon electrodes 14 and 24, a temperature in the same range as usual may be applied during rolling. During rolling, a temperature of, for example, 120 ° C to 180 ° C may be applied. That is, referring to FIG. 2, when the rolling is performed using the roller R, the temperature of the roller R may be maintained at 120 ° C. to 180 ° C. to perform rolling.

본 발명의 바람직한 구현예에 따라서, 상기 롤링 압연 시에는 별도의 온도를 가하지 않고 상온에서 진행될 수 있다. 즉, 도 2에서, 상기 롤러(R)의 온도를 상온으로 하여 롤링 압연할 수 있다. 이 경우, 롤러(R)에 별도의 온도가 가해지지 않아 에너지 절약 면에서 유리함은 물론, 특히 활성탄 전극(14)(24)의 저항 증가를 방지할 수 있다. According to a preferred embodiment of the present invention, the rolling may be carried out at room temperature without applying a separate temperature. That is, in FIG. 2, the temperature of the roller R can be rolled to room temperature. In this case, since no extra temperature is applied to the roller R, it is advantageous in terms of energy saving, and in particular, the increase in resistance of the activated carbon electrodes 14 and 24 can be prevented.

구체적으로, 롤링 압연 시, 고온(예를 들어, 120℃ 내지 180℃)에서 진행한 경우, 예를 들어 바인더의 체적이 넓어져(바인더의 부피 팽창) 활성탄 전극(14)(24)의 저항이 증가될 수 있다. 그러나 본 발명의 바람직한 구현예에 따라서, 상온에서 롤링 압연하는 경우, 바인더의 부피가 팽창되는 현상이 일어나지 않아 저항 증가를 방지할 수 있으며, 이에 따라 낮은 저항 특성을 갖게 할 수 있다. Concretely, when rolling is performed at a high temperature (for example, 120 to 180 ° C) during rolling, the volume of the binder is widened (volume expansion of the binder) and the resistance of the activated carbon electrodes 14 and 24 Can be increased. However, according to a preferred embodiment of the present invention, when the rolling is performed at room temperature, the bulge of the binder does not occur and the increase in resistance can be prevented.

본 발명에서, 상온은 인위적으로 열(온도)을 가하지 않는 온도를 의미하며, 이는 계절에 따라 다를 수 있다. 본 발명에서 상온은, 예를 들어 2℃ 내지 35℃ 범위 내가 될 수 있으며, 보다 구체적인 예를 들어 5℃ 내지 30℃, 또는 5℃ 내지 25℃가 될 수 있다. In the present invention, room temperature refers to a temperature at which no artificial heat (temperature) is applied, which may vary depending on the season. In the present invention, the ambient temperature may be in the range of, for example, 2 ° C to 35 ° C, more specifically 5 ° C to 30 ° C, or 5 ° C to 25 ° C.

(1) 활성탄 (1) activated carbon

상기 활성탄은 특별히 제한되지 않는다. 상기 활성탄은, 예를 들어 당업계에서 통상적으로 사용되는 분말상의 활성탄을 사용할 수 있다. 또한, 상기 활성탄은, 예를 들어 비표면적이 적어도 800㎡/g 이상이고, 평균 입도 크기가 2㎛ ~ 50㎛인 것으로부터 선택될 수 있다. 상기 활성탄은, 비표면적이 클수록 전기적 특성에서 유리하다. 이를 위해, 상기 활성탄은 1500㎡/g 이상의 비표면적을 가지는 것으로부터 선택될 수 있으며, 바람직하게는 1800㎡/g 이상의 비표면적을 가지는 것으로부터 선택될 수 있다. 그러나 활성탄의 비표면적이 너무 큰 경우 전극 밀도가 낮아질 수 있다. 이러한 점을 고려할 때, 상기 활성탄은 1500 ~ 2500㎡/g의 비표면적을 가지는 것이 좋으며, 보다 바람직하게는 1800 ~ 2200㎡/g의 비표면적을 가지는 것이 좋다. The activated carbon is not particularly limited. As the activated carbon, for example, powdery activated carbon commonly used in the art can be used. The activated carbon may be selected from, for example, those having a specific surface area of at least 800 m 2 / g or more and an average particle size of 2 μm to 50 μm. The larger the specific surface area of the activated carbon, the more advantageous it is in the electrical characteristics. For this, the activated carbon may be selected from those having a specific surface area of 1500 m < 2 > / g or more, preferably from 1800 m < 2 > However, if the specific surface area of activated carbon is too large, the electrode density may be lowered. Considering this point, the activated carbon preferably has a specific surface area of 1500 to 2500 m 2 / g, more preferably a specific surface area of 1800 to 2200 m 2 / g.

또한, 상기 활성탄의 평균 입도 크기는 에너지 저장 및 저항 특성 등에 영향을 끼칠 수 있다. 상기 활성탄의 평균 입도 크기가 2㎛ 미만인 경우, 예를 들어 에너지 저장 특성 등이 낮아질 수 있다. 그리고 활성탄의 평균 입도 크기가 50㎛를 초과하는 경우, 예를 들어 저항 특성 등이 떨어질 수 있다. 이러한 점을 고려하여, 상기 활성탄은 5㎛ ~ 30㎛의 평균 입도 분포를 가지는 것으로부터 선택될 수 있다. In addition, the average particle size of the activated carbon may affect energy storage and resistance characteristics and the like. When the average particle size of the activated carbon is less than 2 mu m, for example, energy storage characteristics and the like may be lowered. If the average particle size of the activated carbon is more than 50 mu m, for example, the resistance characteristic may be deteriorated. In view of this point, the activated carbon may be selected from those having an average particle size distribution of 5 mu m to 30 mu m.

본 발명에서, 상기 활성탄은 탄소 원료(활성탄 전구체)로부터 탄화 및 활성화되어 다공성 구조를 가지는 것이면 좋으며, 그 원료 및 활성화 방법은 특별히 한정되지 않는다. 상기 활성탄은, 예를 들어 페놀 수지 등의 수지계; 야자 껍질(코코넛 쉘), 살구씨 및 왕겨 등의 식물계; 및/또는 피치 코크스(pitch cokes) 등의 석탄/석유계 등을 원료로 하여 탄화 및 활성화시킨 것으로부터 선택될 수 있다. In the present invention, the activated carbon may be carbonized and activated from a carbon raw material (activated carbon precursor) to have a porous structure, and the raw material and the activation method are not particularly limited. The activated carbon may be, for example, a resin such as phenol resin; Plant systems such as palm shells (coconut shells), apricot seeds and rice hulls; And coal / petroleum based materials such as pitch cokes and the like as raw materials and carbonizing and activating them.

또한, 상기 활성탄은 수산화칼륨(KOH) 등의 알칼리 활성화제를 이용하여 활성화한 것, 및/또는 스팀(steam)을 이용하여 활성화한 것을 사용할 수 있으나, 바람직하게는 스팀(수증기)을 이용하여 활성화한 활성탄을 사용하는 것이 좋다. 이때, 스팀(수증기)에 의해 활성화된 활성탄은 알칼리 활성화제(KOH 등)를 이용하여 활성화한 활성탄보다 불순물이 적고 가스 발생이 낮으며, 전기적 특성에 유리하여 본 발명에 바람직하다. The activated carbon may be activated by using an alkali activating agent such as potassium hydroxide (KOH) and / or activated by steam, but it is preferably activated by steam (water vapor) It is better to use activated carbon. At this time, activated carbon activated by steam (water vapor) is less in impurities and less in gas generation than activated carbon activated by an alkali activator (such as KOH), and is favorable for the present invention because it is advantageous in electrical characteristics.

하나의 구현예에 따라서, 상기 활성탄은 야자 껍질의 탄화물을 스팀(수증기)으로 활성화한 야자 껍질 활성탄을 유용하게 사용할 수 있다. 그리고 상용화된 제품으로는, 예를 들어 YP 시리즈 제품(예를 들어, YP-50F 및 YP-80F 등)을 사용할 수 있다. According to one embodiment, the activated carbon may be a palm shell activated carbon activated by steam of a coconut shell carbide. As commercialized products, for example, YP series products (for example, YP-50F and YP-80F) can be used.

(2) 바인더 (2) Binders

상기 바인더(binder)는 접착성을 가지는 것이면 좋으며, 이는 예를 들어 당업계에서 통상적으로 사용되는 것으로부터 선택될 수 있다. 상기 바인더는, 예를 들어 폴리테트라플루오로에틸렌(PTFE), 카르복시메틸셀룰로오스(CMC), 폴리비닐피롤리돈(PVP), 폴리비닐리덴플루오라이드(PVDF), 아크릴산, 아크릴 고무, 니트릴-부타디엔 고무(NBR), 스티렌-부타디엔 고무(SBR), 부틸 고무(BR) 및 폴리비닐알콜(PVA) 등으로부터 선택된 하나 이상을 사용할 수 있으나, 이들에 의해 한정되는 것은 아니다. The binder may be an adhesive, and may be selected from those conventionally used in the art, for example. The binder may be selected from the group consisting of polytetrafluoroethylene (PTFE), carboxymethylcellulose (CMC), polyvinylpyrrolidone (PVP), polyvinylidene fluoride (PVDF), acrylic acid, acrylic rubber, nitrile-butadiene rubber Butadiene rubber (NBR), styrene-butadiene rubber (SBR), butyl rubber (BR), and polyvinyl alcohol (PVA).

상기 바인더는 활성탄 100중량부에 대하여 0.5 ~ 20중량부(고형분 기준)가 사용될 수 있다. 이때, 바인더의 함량이 0.5중량부 미만인 경우, 이의 사용에 따른 접착성이 미미하고, 20중량부를 초과하는 경우 과잉 사용에 따른 상승효과가 그다지 크지 않고 전기적 특성에 바람직하지 않을 수 있다. 이러한 점을 고려할 때, 바인더는 활성탄 100중량부에 대하여 1 ~ 15중량부(고형분 기준)로 사용될 수 있다. The binder may be used in an amount of 0.5 to 20 parts by weight (based on the solid content) based on 100 parts by weight of the activated carbon. When the content of the binder is less than 0.5 part by weight, the adhesion of the binder is insignificant. When the amount of the binder is more than 20 parts by weight, the synergistic effect of excessive use is not so large, which may be undesirable for electrical properties. Considering this point, the binder may be used in an amount of 1 to 15 parts by weight (based on the solid content) based on 100 parts by weight of the activated carbon.

본 발명의 바람직한 실시 형태에 따라서, 상기 바인더는 부타디엔-스티렌-알킬 메타크릴레이트 공중합체(Butadiene-Styrene-Alkyl Methacrylate copolymer)를 포함한다. 구체적인 구현예에 따라서, 바인더는 상기 나열된 바인더들 중에서 선택된 하나 이상의 바인더(제1바인더)와, 상기 부타디엔-스티렌-알킬 메타크릴레이트 공중합체(제2바인더)의 혼합으로 구성되거나, 상기 부타디엔-스티렌-알킬 메타크릴레이트 공중합체(제2바인더) 단독으로 구성될 수 있다. According to a preferred embodiment of the present invention, the binder includes a butadiene-styrene-alkyl methacrylate copolymer. According to a specific embodiment, the binder comprises a mixture of one or more binders selected from the listed binders (first binder) and the butadiene-styrene-alkyl methacrylate copolymer (second binder), or the butadiene-styrene -Alkyl methacrylate copolymer (second binder) alone.

상기 부타디엔-스티렌-알킬 메타크릴레이트 공중합체(제2바인더)는 부타디엔, 스티렌 및 알킬 메타크릴레이트의 3원 공중합체로서, 이는 예를 들어 부타디엔계 단량체 30 내지 45중량%, 스티렌계 단량체 5 내지 15중량% 및 알킬 메타크릴레이트계 단량체 40 내지 60중량%가 공중합된 것을 사용할 수 있다. 이때, 상기 알킬 메타크릴레이트계 단량체는, 예를 들어 메틸 메타크릴레이트, 에틸 메타크릴레이트 및/또는 n-부틸 메타크릴레이트 등으로부터 선택될 수 있다. The butadiene-styrene-alkyl methacrylate copolymer (second binder) is a ternary copolymer of butadiene, styrene, and alkyl methacrylate. The butadiene-styrene-alkyl methacrylate copolymer includes 30 to 45% by weight of butadiene- 15% by weight and an alkyl methacrylate monomer in an amount of 40 to 60% by weight. At this time, the alkyl methacrylate monomer may be selected from, for example, methyl methacrylate, ethyl methacrylate and / or n-butyl methacrylate.

상기 부타디엔-스티렌-알킬 메타크릴레이트 공중합체(제2바인더)는, 구체적인 예를 들어 부타디엔-스티렌-메틸 메타크릴레이트 공중합체, 부타디엔-스티렌-에틸 메타크릴레이트 공중합체 및/또는 부타디엔-스티렌-부틸 메타크릴레이트 공중합체 등으로부터 선택될 수 있다. Specific examples of the butadiene-styrene-alkyl methacrylate copolymer (second binder) include butadiene-styrene-methyl methacrylate copolymer, butadiene-styrene-ethyl methacrylate copolymer and / or butadiene- Butyl methacrylate copolymer, and the like.

본 발명에 따르면, 상기 부타디엔-스티렌-알킬 메타크릴레이트 공중합체(제2바인더)는 종래 통상적으로 사용되고 있는 상기의 바인더들(제1바인더)에 비하여 활성탄 입자 및 도전재 입자 상호간의 결집력 향상은 물론, 활성탄 전극(14)(24)과 금속 집전체(12)(22) 간의 층간 접착력 및 활성탄 전극(14)(24)의 전극 밀도를 효과적으로 개선시키며, 이와 함께 가스 발생이 적어 바람직하다. 또한, 이러한 이유로 용량 및 저항 등의 전기적 특성이 개선될 수 있다. According to the present invention, the butadiene-styrene-alkyl methacrylate copolymer (second binder) can improve the binding force between the activated carbon particles and the conductive material particles as compared with the conventional binders (first binder) , The interlayer adhesion between the activated carbon electrodes 14 and 24 and the metal collectors 12 and 22 and the electrode density of the activated carbon electrodes 14 and 24 are effectively reduced. For this reason, electrical characteristics such as capacitance and resistance can be improved.

바람직한 형태에 따라서, 상기 바인더는 적어도 카르복시메틸셀룰로오스(제1바인더)와 부타디엔-스티렌-알킬 메타크릴레이트 공중합체(제2바인더)를 포함할 수 있다. 이때, 카르복시메틸셀룰로오스(제1바인더)는 바인더의 기능과 함께 부타디엔-스티렌-알킬 메타크릴레이트 공중합체(제2바인더)의 분산성을 효과적으로 개선시킨다. 이에 따라, 본 발명에 따르면, 바인더로서 카르복시메틸셀룰로오스(제1바인더)와 부타디엔-스티렌-알킬 메타크릴레이트 공중합체(제2바인더)를 혼합하여 사용하는 경우, 층간 접착력, 가스 발생 및/또는 전기적 특성 등에서 최적의 효과를 구현한다. According to a preferred form, the binder may comprise at least carboxymethylcellulose (first binder) and butadiene-styrene-alkyl methacrylate copolymer (second binder). At this time, carboxymethylcellulose (first binder) effectively improves the dispersibility of the butadiene-styrene-alkyl methacrylate copolymer (second binder) together with the function of the binder. Accordingly, according to the present invention, when carboxymethylcellulose (first binder) and butadiene-styrene-alkyl methacrylate copolymer (second binder) are mixed and used as a binder, interlayer adhesion, gas generation and / Characteristics and the like.

이때, 본 발명의 바람직한 구현예에 따라서, 상기 바인더는 카르복시메틸셀룰로오스(제1바인더)와 부타디엔-스티렌-알킬 메타크릴레이트 공중합체(제2바인더)를 1 : 0.2 ~ 5의 중량비로 사용될 수 있다. 이때, 카르복시메틸셀룰로오스(제1바인더)에 대하여, 부타디엔-스티렌-알킬 메타크릴레이트 공중합체(제2바인더)의 사용량이 0.2 중량비 미만인 경우, 부타디엔-스티렌-알킬 메타크릴레이트 공중합체(제2바인더)의 사용에 따른 개선 효과(층간 접착력 및 전기적 특성 등)가 미미할 수 있다. 그리고 부타디엔-스티렌-알킬 메타크릴레이트 공중합체(제2바인더)의 사용량이 5 중량비를 초과하는 경우, 상대적으로 카르복시메틸셀룰로오스(제1바인더)의 함량이 낮아져, 예를 들어 부타디엔-스티렌-알킬 메타크릴레이트 공중합체(제2바인더)의 분산성 등이 낮아질 수 있다. According to a preferred embodiment of the present invention, the binder may be used in a weight ratio of 1: 0.2 to 5: carboxymethylcellulose (first binder) and butadiene-styrene-alkyl methacrylate copolymer (second binder) . At this time, when the amount of the butadiene-styrene-alkyl methacrylate copolymer (second binder) used is less than 0.2 weight ratio with respect to carboxymethyl cellulose (first binder), a butadiene-styrene-alkyl methacrylate copolymer (Such as interlayer adhesion and electrical characteristics) may be insignificant. When the amount of the butadiene-styrene-alkyl methacrylate copolymer (second binder) is more than 5 parts by weight, the content of carboxymethyl cellulose (first binder) becomes relatively low and, for example, a butadiene-styrene- The dispersibility and the like of the acrylate copolymer (second binder) may be lowered.

아울러, 상기 부타디엔-스티렌-알킬 메타크릴레이트 공중합체(제2바인더)는, 바람직하게는 평균 입자 크기가 50nm ~ 400nm인 나노 미립자로부터 선택될 수 있으며, 보다 바람직하게는 평균 입자 크기가 80nm ~ 230nm인 나노 미립자로부터 선택될 수 있다. 이와 같이 부타디엔-스티렌-알킬 메타크릴레이트 공중합체(제2바인더)가 나노 크기를 가지는 경우, 활성탄 입자들 간의 사이에 균일하게 분산되어 접착력 및 전기적 특성 등이 더욱 효과적으로 개선된다. 이때, 하나의 구현예에 따라서, 상기 바인더는 카르복시메틸셀룰로오스(제1바인더)를 포함하는 용액(예를 들어, 수용액)에 상기 나노 크기의 부타디엔-스티렌-알킬 메타크릴레이트 공중합체(제2바인더)가 분산된 것을 사용할 수 있다. The butadiene-styrene-alkyl methacrylate copolymer (second binder) may be selected from nano-particles having an average particle size of 50 nm to 400 nm, more preferably an average particle size of 80 nm to 230 nm Nanoparticles. &Lt; / RTI > When the butadiene-styrene-alkyl methacrylate copolymer (second binder) has a nano-size, it is uniformly dispersed among the activated carbon particles to improve the adhesive strength and electrical characteristics more effectively. At this time, according to one embodiment, the binder may be added to a solution (for example, an aqueous solution) containing carboxymethylcellulose (first binder), the nano-sized butadiene-styrene-alkyl methacrylate copolymer ) Can be used.

(3) 도전재 (3) Conductive material

상기 도전재는 전기전도성을 가지는 것이면 특별히 제한되지 않으며, 이는 예를 들어 당업계에서 통상적으로 사용되는 것으로부터 선택될 수 있다. 상기 도전재는, 예를 들어 아세틸렌 블랙(acetylene black), 그래파이트(graphite), 그래핀(graphene), 탄소나노튜브(CNT) 및 탄소나노섬유(CNF) 등의 카본 블랙; 및/또는 산화티탄 및 산화루테늄 등의 산화물 분말 등으로부터 선택된 하나 이상을 사용할 수 있다. The conductive material is not particularly limited as long as it has electrical conductivity and can be selected from those conventionally used in the art, for example. The conductive material may include, for example, carbon black such as acetylene black, graphite, graphene, carbon nanotube (CNT), and carbon nanofiber (CNF); And / or an oxide powder such as titanium oxide and ruthenium oxide, and the like.

또한, 상기 도전재는, 예를 들어 40㎛ 이하의 평균 입자 크기, 보다 구체적으로는 3㎛ ~ 20㎛의 평균 입자 크기를 가질 수 있다. 아울러, 상기 도전재는 활성탄 100중량부에 대하여 0.2 ~ 20중량부로 사용될 수 있다. 이때, 도전재의 함량이 0.2중량부 미만인 경우, 이의 사용에 따른 전기전도성의 개선(즉, 내부 저항 특성의 개선)이 미미하고, 20중량부를 초과하는 경우 정전 용량이 감소될 수 있다. 이러한 점을 고려할 때, 상기 도전재는 활성탄 100중량부에 대하여 2 ~ 10중량부로 사용될 수 있다. In addition, the conductive material may have an average particle size of, for example, 40 탆 or less, more specifically, an average particle size of 3 탆 to 20 탆. The conductive material may be used in an amount of 0.2 to 20 parts by weight based on 100 parts by weight of activated carbon. At this time, when the content of the conductive material is less than 0.2 parts by weight, the improvement of the electric conductivity (that is, the improvement of the internal resistance characteristic) is small with use thereof, and when it exceeds 20 parts by weight, the capacitance may be decreased. Considering this point, the conductive material may be used in an amount of 2 to 10 parts by weight based on 100 parts by weight of activated carbon.

(4) 용매(4) Solvent

한편, 상기 활성탄 전극 조성물은 경우에 따라서 용매를 더 포함할 수 있다. 이때, 상기 용매는 활성탄 전극(14)(24)을 제조함에 있어, 예를 들어 금속 집전체(12)(22) 상에 코팅하는 방법으로 활성탄 전극(14)(24)을 형성하는 경우, 분산성 및 코팅성을 위한 희석제로서 포함될 수 있다. Meanwhile, the activated carbon electrode composition may further include a solvent. When the activated carbon electrodes 14 and 24 are formed by coating on the metal collectors 12 and 22 in manufacturing the activated carbon electrodes 14 and 24, May be included as a diluent for acid and coating properties.

상기 용매는 열에 의해 휘발되거나 자연 건조에 의해 휘발될 수 있는 것이면 좋으며, 이는 예를 들어 물 및/또는 유기 용제 등으로부터 선택될 수 있다. 이때, 상기 유기 용제로는, 예를 들어 메틸 피롤리돈(NMP) 등을 들 수 있다. 또한, 상기 용매는 활성탄 100중량부에 대하여 예를 들어 5 ~ 500중량부로 혼합될 수 있다. The solvent is not particularly limited as long as it is volatilized by heat or can be volatilized by natural drying, for example, water and / or an organic solvent. Examples of the organic solvent include methyl pyrrolidone (NMP) and the like. The solvent may be mixed with, for example, 5 to 500 parts by weight based on 100 parts by weight of activated carbon.

[3] 세퍼레이터 [3] separator

상기 세퍼레이터(30)는 절연성의 다공성 부재로서, 이는 예를 들어 당업계에서 통상적으로 사용되는 것을 사용할 수 있다. The separator 30 is an insulating porous member, for example, which is commonly used in the art can be used.

상기 세퍼레이터(30)는, 예를 들어 폴리에틸렌(PE)계, 폴리프로필렌(PP)계 및/또는 셀룰로오스계 등으로부터 선택된 부직포(또는 직물)이나 유리 섬유 부직포 등으로부터 선택될 수 있으나, 이들에 의해 한정되는 것은 아니다. The separator 30 may be selected from, for example, a nonwoven fabric (or a woven fabric) or a glass fiber nonwoven fabric selected from polyethylene (PE) based, polypropylene (PP) based and / or cellulose based, It is not.

[4] 전해액[4] electrolyte

상기 전해액은, 예를 들어 고전압 특성 등을 위해 유기 전해질 용액으로부터 선택될 수 있다. 상기 전해액은 전해질(전해 염), 유기 용매 및 가스 발생 억제제를 포함한다. 이때, 상기 전해질과 유기 용매의 종류는 특별히 제한되지 않으며, 이들은 당업계에서 통상적으로 사용되고 있는 것을 사용할 수 있다. The electrolytic solution may be selected from an organic electrolyte solution, for example, for high-voltage characteristics and the like. The electrolytic solution includes an electrolyte (electrolytic salt), an organic solvent, and a gas generation inhibitor. At this time, the types of the electrolyte and the organic solvent are not particularly limited, and those conventionally used in the art can be used.

상기 전해질은, 예를 들어 테트라 에틸 암모늄, 트리에틸 메틸 암모늄 등의 4급 암모늄염; (C₂H₅)₄NBF₄ 등의 4불화 붕소 암모늄염; N-에틸-N-메틸피롤리디늄, N,N-테트라메틸렌 피롤리디늄 등의 지방족 고리형 암모늄염; 1,3-디메틸이미다졸, 1-에틸-3-메틸이미다졸 등의 4급 이미다졸; 및/또는 이들의 유도체 등으로부터 선택될 수 있다. 아울러, 상기 전해질은, 전해액 내에 예를 들어 0.1 ~ 4.0mol/L, 바람직하게는 0.5 ~ 3.0mol/L으로 포함(용해)될 수 있다. 이때, 전해질의 농도가 높으면 전해액의 저항이 커지거나 방전 특성이 저하될 수 있으며, 전해질의 농도가 낮으면 용해성이 떨어지거나 결정 석출이 우려될 수 있다. Examples of the electrolyte include quaternary ammonium salts such as tetraethylammonium and triethylmethylammonium; (C ₂ H ₅ ) ₄ NBF ₄ ; Aliphatic cyclic ammonium salts such as N-ethyl-N-methylpyrrolidinium and N, N-tetramethylenepyrrolidinium; Quaternary imidazole such as 1,3-dimethylimidazole and 1-ethyl-3-methylimidazole; And / or derivatives thereof, and the like. In addition, the electrolyte may be contained (dissolved) in the electrolyte solution, for example, at 0.1 to 4.0 mol / L, preferably 0.5 to 3.0 mol / L. At this time, if the concentration of the electrolyte is high, the resistance of the electrolyte may become large or the discharge characteristic may be deteriorated. If the concentration of the electrolyte is low, the solubility may be deteriorated or crystal precipitation may be caused.

상기 유기 용매는 전해질을 용해(희석)시킬 수 있는 것이면 특별히 제한되지 않는다. 상기 유기 용매는, 예를 들어 프로필렌 카보네이트, 에틸렌 카보네이트, 부틸렌 카보네이트, 디메틸 카보네이트, 디에틸 카보네이트, 에틸 메틸 카보네이트, γ-부틸올락톤, 디메틸설폭사이드, 설포란, 디메틸 폼 아미드, 디메틸아세트아미드, 인산 트리에스테르, 무수 말레산, 석신산 무수물, 무수프탈산, 1,3-프로판설톤, 니트로벤젠, 1,2-디메톡시 에탄, 테트라하이드로 푸란, 아세토니트릴, 니트로메탄 및/또는 이들의 유도체 등으로부터 선택될 수 있다. The organic solvent is not particularly limited as long as it can dissolve (dilute) the electrolyte. Examples of the organic solvent include organic solvents such as propylene carbonate, ethylene carbonate, butylene carbonate, dimethyl carbonate, diethyl carbonate, ethyl methyl carbonate,? -Butylolactone, dimethylsulfoxide, sulfolane, dimethylformamide, dimethylacetamide, Or a derivative thereof such as tricresyl phosphate, tricresyl phosphate, tricresyl phosphate, tricresyl phosphate, tricresyl phosphate, tricresyl phosphate, tricresyl phosphate, tricresyl phosphate, tricresyl phosphate, tricresyl phosphate, tricresyl phosphate, Can be selected.

일반적으로, 전기이중층 커패시터(EDLC)는 사용 시간이 지남에 따라 내압(내부 압력)이 상승된다. 이는 낮은 동작 전압의 원인을 제공한다. 즉, 내압이 높아지면, 전해액이 누액되거나 전기이중층 커패시터(EDLC) 셀이 파손될 수 있다. 이에, 압력 축적(내압 상승)을 방지하기 위해, 낮은 전압에서 작동시켜야 하므로 결국 동작 전압이 낮다. In general, the electric double layer capacitor (EDLC) has an internal pressure (internal pressure) increased over time. This provides a source of low operating voltage. That is, if the internal pressure is increased, the electrolyte may be leaked or the electric double layer capacitor (EDLC) cell may be broken. Therefore, in order to prevent accumulation of pressure (increase in internal pressure), the operation voltage must be low because it must be operated at a low voltage.

본 발명에서, 상기 가스 발생 억제제는 위와 같은 내압 상승의 문제를 해결하여 높은 동작 전압(고전압)을 갖게 한다. 부가적으로, 상기 가스 발생 억제제는 장수명 특성을 갖게 한다. 일반적으로, 전기이중층 커패시터(EDLC) 셀 내부에서는 가스가 발생한다. 가스 발생은, 예를 들어 전해질의 분해 반응에 의하거나, 활성탄 전극(14)(24)과 전해질의 접촉 계면에서 일어나는 화학 반응에 의할 수 있으며, 이때 발생된 가스는 산(acid) 성분을 포함할 수 있다. 이와 같이 발생된 가스는 내압 상승과 열화의 원인이 되어, 동작 전압과 수명 특성을 저하시킨다. In the present invention, the gas generation inhibitor solves the problem of the increase in the internal pressure as described above, and has a high operating voltage (high voltage). In addition, the gas generation inhibitor has a long life characteristic. Generally, gas is generated inside an electric double layer capacitor (EDLC) cell. The generation of gas can be caused by, for example, a decomposition reaction of the electrolyte, or a chemical reaction occurring at the contact interface between the activated carbon electrodes 14 and 24 and the electrolyte, wherein the generated gas includes an acid component can do. The gas thus generated causes rise of the internal pressure and deterioration, thereby lowering the operating voltage and lifetime characteristics.

상기 가스 발생 억제제는 가스 발생을 억제할 수 있으면 특별히 제한되지 않는다. 상기 가스 발생 억제제는, 예를 들어 전해액 내에서 발생된 가스를 흡착하거나 중화시켜 가스 발생을 억제(제거)할 수 있으면 좋다. The gas generation inhibitor is not particularly limited as long as it can suppress gas generation. The gas generation inhibitor should be capable of suppressing (eliminating) gas generation by adsorbing or neutralizing the gas generated in the electrolyte solution, for example.

상기 가스 발생 억제제는 액상 및/또는 고상일 수 있으며, 이는 전해액 내에 용해 및/또는 분산될 수 있다. 하나의 구현예에 따라서, 상기 가스 발생 억제제는 염기성 유기화합물 및 다공성 무기물 입자 등으로부터 선택된 하나 이상을 포함할 수 있다. 이때, 상기 염기성 유기화합물은, 예를 들어 전해액 내에 용해되어, 발생된 가스(산 성분)와 중화 반응을 통해 가스 발생을 억제(제거)할 수 있다. 또한, 상기 다공성 무기물 입자는, 예를 들어 전해액 내에 분산되어, 발생된 가스의 흡착을 통해 가스 발생을 억제(제거)할 수 있다. 이에, 본 발명에 따르면, 내압 상승과 열화의 원인이 되는 가스 발생이 억제(제거)되어 높은 동작 전압(고전압)과 장수명 특성을 가질 수 있다. The gas generation inhibitor may be liquid and / or solid and may be dissolved and / or dispersed in the electrolyte solution. According to one embodiment, the gas generation inhibitor may include at least one selected from a basic organic compound and a porous inorganic particle. At this time, the basic organic compound can be inhibited (removed) by, for example, dissolving in an electrolytic solution and generating a gas through a neutralization reaction with the generated gas (acid component). Further, the porous inorganic particles can be dispersed in, for example, an electrolyte solution, and the generation of gas can be suppressed (eliminated) by adsorbing the generated gas. Thus, according to the present invention, it is possible to suppress (remove) the generation of gas which causes rise in internal pressure and deterioration, and can have a high operating voltage (high voltage) and long life.

상기 염기성 유기화합물은, 예를 들어 분자 내에 1개 이상의 질소(N)를 가지는 알칼로이드(alkaloid) 화합물로부터 선택될 수 있으며, 구체적인 예를 들어 1,3-다이아졸(1,3-diazol), 피리딘(pyridine) 및 트리에틸아민(triethylamine) 등으로부터 선택된 하나 이상을 사용할 수 있다. 또한, 상기 다공성 무기물 입자는, 예를 들어 분자 내에 규소(Si), 알루미늄(Al), 마그네슘(Mg), 나트륨(Na), 칼륨(K), 티타늄(Ti) 및 망간(M) 등으로부터 선택된 하나 이상의 원소를 가지는 다공성의 무기 산화물 입자로부터 선택될 수 있으며, 구체적인 예를 들어 실리카, 알루미나, 티타니아 및 제올라이트 등으로부터 선택될 수 있다. 아울러, 다공성의 무기물 입자는, 예를 들어 0.1㎛ 내지 20㎛의 평균 입도 크기를 가질 수 있다. 또한, 하나의 구현예에 따라서, 상기 가스 발생 억제제는 전해액 내에 0.001중량% 내지 10중량%로 포함될 수 있으나, 이에 한정되는 것은 아니다. The basic organic compound may be selected from, for example, an alkaloid compound having at least one nitrogen (N) in the molecule, and specific examples thereof include 1,3-diazole, pyridine, triethylamine, and the like may be used. The porous inorganic particles may be selected from, for example, silicon (Si), aluminum (Al), magnesium (Mg), sodium (Na), potassium (K), titanium May be selected from porous inorganic oxide particles having one or more elements, and specific examples thereof may be selected from silica, alumina, titania and zeolite. In addition, the porous inorganic particles may have an average particle size of, for example, 0.1 탆 to 20 탆. In addition, according to one embodiment, the gas generation inhibitor may be included in the electrolytic solution in an amount of 0.001 wt% to 10 wt%, but is not limited thereto.

이상에서 설명한 본 발명에 따르면, 개선된 슈퍼커패시터 및 그 제조방법이 제공된다. 본 발명에 따르면, 예를 들어 전해액에 포함된 가스 발생 억제제에 의해, 적어도 높은 동작 전압(고전압 특성)을 갖는다. 또한, 본 발명에 따라서, 동작 전압은 상기한 바와 같은 활성탄 전극(14)(24)의 구성 및/또는 금속 집전체(12)(22)의 구성에 의해서도 높아진다. 이에 따라, 본 발명에 따르면, 높은 전압에서 작동되어 에너지 저장량이 개선된다. 그리고 장수명 특성을 갖는다. According to the present invention described above, an improved supercapacitor and a method of manufacturing the same are provided. According to the present invention, for example, it has at least a high operating voltage (high voltage characteristic) by the gas generation inhibitor contained in the electrolytic solution. According to the present invention, the operating voltage is also increased by the configuration of the activated carbon electrodes 14 and 24 and / or the configuration of the metal collectors 12 and 22 as described above. Thus, according to the present invention, the energy storage is improved by operating at a high voltage. And long life.

또한, 본 발명에 따르면, 상기 금속 산화막층(12a)(22a)에 의해, 예를 들어 활성탄 전극(14)(24)과 금속 집전체(12)(22) 간의 접촉 면적이 개선되어 우수한 전기적 특성을 갖는다. 또한, 본 발명에 따르면, 우수한 전기적 특성과 함께 장기 신뢰성 등을 갖는다. According to the present invention, the contact area between, for example, the activated carbon electrodes 14 and 24 and the metal collectors 12 and 22 is improved by the metal oxide film layers 12a and 22a, Respectively. Further, according to the present invention, it has excellent electrical characteristics and long-term reliability.

이하, 본 발명의 실시예 및 비교예를 예시한다. 하기의 실시예들은 본 발명의 이해를 돕기 위해 예시적으로 제공되는 것일 뿐, 이에 의해 본 발명의 기술적 범위가 한정되는 것은 아니다. 또한, 하기의 비교예는 종래 기술을 의미하는 것이 아니며, 이는 단지 실시예들과의 비교를 위해 제공된다. Hereinafter, examples and comparative examples of the present invention will be exemplified. The following examples are provided to illustrate the present invention only and the technical scope of the present invention is not limited thereto. In addition, the following comparative example is not meant to be a prior art, but is provided for comparison with embodiments only.

[실시예 1 내지 3][Examples 1 to 3]

(1) Al 에칭 포일의 산화 처리(1) Oxidation treatment of Al etched foil

두께 약 10㎛의 Al(알루미늄) 에칭 포일을 준비하였다. 상기 준비된 Al 에칭 포일을 수세 및 건조시켰다. 그리고 전해조에 상기 Al 에칭 포일과 흑연판을 침지한 다음, 양극(+)에는 Al 에칭 포일을 연결하고, 음극(-)에는 흑연판을 연결하였다. 이때, 상기 전해조에는 과염소산(HClO₄) 10중량%, 옥살산(C₂H₂O₄) 2중량%, 붕산나트륨(NaBO₂) 8중량% 및 잔량의 증류수로 이루어진 전해 수용액이 주입되었다. An Al (aluminum) etched foil having a thickness of about 10 mu m was prepared. The prepared Al etched foil was washed with water and dried. Then, the Al etching foil and the graphite plate were immersed in an electrolytic bath, and an Al etching foil was connected to the positive electrode (+) and a graphite plate was connected to the negative electrode (-). At this time, an electrolytic aqueous solution containing 10% by weight of perchloric acid (HClO ₄ ), ₂ % by weight of oxalic acid (C ₂ H ₂ O ₄ ), 8% by weight of sodium borate (NaBO ₂ ) and distilled water was injected into the electrolytic bath.

다음으로, 상기 전해 수용액의 온도를 약 25℃로 유지하고, 전해 수용액에 초음파 발생기를 통해 초음파 진동을 가하면서 약 12V의 전압과 약 0.8A의 전류를 인가하여 약 15분 동안 산화시켜 Al 에칭 포일의 표면에 두께 약 2.6㎛의 다공성 Al 산화막층을 형성시켰다. 이때, Al 산화막층의 두께는 주사전자현미경을 통한 단면 촬영을 통해 측정되었다. Next, while maintaining the temperature of the electrolytic aqueous solution at about 25 캜 and applying ultrasonic vibration through the ultrasonic generator to the electrolytic aqueous solution, a voltage of about 12 V and a current of about 0.8 A were applied for about 15 minutes to oxidize the Al etch foil A porous Al oxide film layer having a thickness of about 2.6 mu m was formed. At this time, the thickness of the Al oxide film layer was measured by a cross-sectional photograph using a scanning electron microscope.

(2) 전극 제조 (2) Electrode Fabrication

먼저, 카르복시메틸셀룰로오스(CMC)를 28중량%(고형분 기준)로 포함하는 수용액을 준비한 다음, 여기에 부타디엔-스티렌-메틸 메타크릴레이트 공중합체(BSM)를 넣고, 5,000rpm으로 15분 동안 혼합 교반하였다. 이때, 상기 부타디엔-스티렌-메틸 메타크릴레이트 공중합체(BSM)는 부타디엔 단량체 34중량%, 스티렌 단량체 8중량% 및 메틸 메타크릴레이트 단량체 58중량%가 공중합된 것으로서, 약 120nm ~ 220nm의 입도 분포를 가지는 나노 미립자를 사용하였다. First, an aqueous solution containing 28% by weight (based on solids) of carboxymethyl cellulose (CMC) was prepared and then a butadiene-styrene-methyl methacrylate copolymer (BSM) was added thereto. The mixture was stirred at 5,000 rpm for 15 minutes Respectively. The butadiene-styrene-methyl methacrylate copolymer (BSM) was prepared by copolymerizing 34% by weight of a butadiene monomer, 8% by weight of a styrene monomer and 58% by weight of a methyl methacrylate monomer and had a particle size distribution of about 120 nm to 220 nm Nanoparticles were used.

다음으로, 상기 교반 용액에 활성탄과 아세틸렌 블랙을 투입한 다음, 약 1,800rpm(at 30kPa)으로 10분 동안 혼합 교반하여 슬러리(slurry) 상의 활성탄 전극 조성물을 제조하였다. 이때, 상기 활성탄은 스팀으로 활성화된 야자 껍질 활성탄으로서 YP-50F 제품(평균 입도 약 8㎛)이 사용되었으며, 상기 아세틸렌 블랙은 Super P 제품(평균 입도 약 4.5㎛)이 사용되었다. 또한, 상기 활성탄 전극 조성물은 활성탄 100중량부에 대하여, 고형분 기준으로 아세틸렌 블랙 약 6중량부, 카르복시메틸셀룰로오스(CMC) 약 1.5중량부가 사용되었다. 그리고 상기 부타디엔-스티렌-메틸 메타크릴레이트 공중합체(BSM)는 활성탄 100중량부에 대하여 각 실시예에 따라 2중량부(실시예 1), 3중량부(실시예 2) 및 4중량부(실시예 3)로 달리 사용되었다. Next, activated carbon and acetylene black were put into the stirring solution, and then mixed and stirred at about 1,800 rpm (at 30 kPa) for 10 minutes to prepare an activated carbon electrode composition on a slurry. At this time, YP-50F product (average particle size about 8 μm) was used as the activated carbon activated coconut shell activated carbon, and Super P product (average particle size about 4.5 μm) was used for the acetylene black. The activated carbon electrode composition used about 6 parts by weight of acetylene black and about 1.5 parts by weight of carboxymethyl cellulose (CMC) based on 100 parts by weight of activated carbon. 2 parts by weight (Example 1), 3 parts by weight (Example 2) and 4 parts by weight (based on 100 parts by weight of activated carbon) of the butadiene-styrene-methyl methacrylate copolymer (BSM) Example 3).

상기 각 실시예(1 ~ 3)에 따른 활성탄 전극 조성물(슬러리)을 상기 Al 에칭 포일의 Al 산화막층 상에 닥터 블레이드법으로 코팅한 다음, 건조시켰다. 이후, 약 150℃에서 롤링 압연하여 상기 Al 산화막층 상에 두께 약 120㎛의 활성탄 전극을 형성시켜, Al 에칭 포일/Al 산화막층/활성탄 전극의 적층 구조를 가지는 전극 시트를 제조하였다. An activated carbon electrode composition (slurry) according to each of Examples 1 to 3 was coated on the Al oxide film layer of the Al etching foil by a doctor blade method and then dried. Thereafter, rolled and rolled at about 150 캜 to form an activated carbon electrode having a thickness of about 120 탆 on the Al oxide film layer to produce an electrode sheet having a laminated structure of Al etching foil / Al oxide film / activated carbon electrode.

(3) EDLC 셀 제조(3) Production of EDLC cell

상기 제조된 전극 시트를 이용하여 통상의 공정으로 원통형의 EDLC 셀(cell)을 제조하였다.　 구체적으로, 상기 제조된 전극 시트를 소정 크기(20mm x 15cm)로 절개한 다음, 접속 단자를 설치하고, 2장의 전극 시트 사이에 세퍼레이터(PE 부직포)를 개재하였다. 이후, 원통형으로 와인딩(winding)한 후, 테이핑(taping)하여 마감한 다음, 원통형 알루미늄 케이스에 수납하였다. 그리고 케이스 내에 전해액을 주입한 다음, 케이스의 상단을 밀봉 처리하였다. A cylindrical EDLC cell was prepared by the ordinary process using the electrode sheet prepared above. Specifically, the prepared electrode sheet was cut into a predetermined size (20 mm.times.15 cm), a connection terminal was provided, and a separator (PE nonwoven fabric) was interposed between the two electrode sheets. Thereafter, it was wound in a cylindrical shape, taped and finished, and then housed in a cylindrical aluminum case. Then, the electrolyte solution was injected into the case, and then the upper end of the case was sealed.

상기 전해액은 1.0mol/L의 (C₂H₅)₄NBF₄(전해질)과 아세토니트릴(유기 용매)이 혼합된 용액[(C₂H₅)₄NBF₄/ACN]을 준비한 다음, 여기에 염기성 유기화합물(가스 발생 억제제)로서 1,3-다이아졸(1,3-diazol)을 더 혼합(용해)하여 사용하였다. 이때, 상기 1,3-다이아졸은 전해액 전체 중량 기준으로 약 0.2중량%가 되도록 첨가되었다. The electrolytic solution was prepared by preparing a solution [(C ₂ H ₅ ) ₄ NBF ₄ / ACN] in which (C ₂ H ₅ ) ₄ NBF ₄ (electrolyte) and acetonitrile (organic solvent) were mixed at 1.0 mol / L A 1,3-diazole was further mixed (dissolved) as a basic organic compound (gas generation inhibitor). At this time, the 1,3-diazole was added in an amount of about 0.2 wt% based on the total weight of the electrolytic solution.

[실시예 4][Example 4]

상기 실시예 1과 대비하여, 활성탄으로서 KOH로 활성화된 제품을 사용한 것을 제외하고는 실시예 1과 동일하게 실시하여 EDLC 셀을 제조하였다. 구체적으로, 본 실시예에서는 활성탄으로서 KOH로 활성화된 페놀 수지계 활성탄(MSP-20 제품)이 사용되었다. An EDLC cell was prepared in the same manner as in Example 1, except that a product activated with KOH was used as the activated carbon in contrast to Example 1. [ Specifically, phenol resin-based activated carbon (product MSP-20) activated with KOH was used as activated carbon in this embodiment.

[실시예 5][Example 5]

상기 실시예 1과 대비하여, 바인더로서 부타디엔-스티렌-메틸 메타크릴레이트 공중합체(BSM) 대신에 스티렌-부탄디엔 고무(SBR)를 사용한 것을 제외하고는 실시예 1과 동일하게 실시하여 EDLC 셀을 제조하였다. 구체적으로, 본 실시예에서는 바인더로서 부타디엔-스티렌-메틸 메타크릴레이트 공중합체(BSM)를 사용하지 않고, EDLC 제조에서 일반적으로 사용되고 있는 스티렌-부탄디엔 고무(SBR)를 대신 사용하여, 활성탄 100중량부에 대하여 아세틸렌 블랙 약 6중량부, 카르복시메틸셀룰로오스(CMC) 약 1.5중량부 및 스티렌-부탄디엔 고무(SBR) 약 2중량부를 포함하는 활성탄 전극 조성물을 이용하여 활성탄 전극을 형성시켰다. An EDLC cell was prepared in the same manner as in Example 1, except that styrene-butadiene rubber (SBR) was used instead of butadiene-styrene-methyl methacrylate copolymer (BSM) . Specifically, in this example, styrene-butadiene rubber (SBR) generally used in the production of EDLC was used instead of butadiene-styrene-methyl methacrylate copolymer (BSM) as a binder, , An activated carbon electrode was formed using an activated carbon electrode composition comprising about 6 parts by weight of acetylene black, about 1.5 parts by weight of carboxymethyl cellulose (CMC), and about 2 parts by weight of styrene-butadiene rubber (SBR).

[실시예 6][Example 6]

상기 실시예 1과 대비하여, Al 에칭 포일의 산화 시, 전해 수용액의 조성을 달리한 것을 제외하고는 실시예 1과 동일하게 실시하여 EDLC 셀을 제조하였다. 구체적으로, 본 실시예에서는 Al 에칭 포일의 표면에 Al 산화막층을 형성함에 있어, 전해 수용액으로서 과염소산(HClO₄) 12중량%, 붕산나트륨(NaBO₂) 8중량% 및 잔량의 증류수로 이루어진 수용액을 사용하여 두께 약 2.6㎛의 다공성 Al 산화막층을 형성시켰다. In contrast to Example 1, an EDLC cell was prepared in the same manner as in Example 1, except that the composition of the electrolytic aqueous solution was changed when the Al etched foil was oxidized. Specifically, in this embodiment, in forming the Al oxide film layer on the surface of the Al etching foil, an aqueous solution containing 12% by weight of perchloric acid (HClO ₄ ), 8% by weight of sodium borate (NaBO ₂ ) Was used to form a porous Al oxide film layer having a thickness of about 2.6 mu m.

[실시예 7 및 8][Examples 7 and 8]

상기 실시예 1과 대비하여, Al 산화막층의 두께를 달리한 것을 제외하고는 실시예 1과 동일하게 실시하여 EDLC 셀을 제조하였다. 구체적으로, 본 실시예들에서는 Al 에칭 포일의 표면에 Al 산화막층을 형성함에 있어, 전해 수용액 및/또는 산화 조건을 달리하여, Al 산화막층의 두께가 약 0.8㎛(실시예 7) 및 약 6.2㎛(실시예 8)가 되게 하였다. An EDLC cell was fabricated in the same manner as in Example 1, except that the thickness of the Al oxide film layer was different from that of the first embodiment. Specifically, in this embodiment, in forming the Al oxide film layer on the surface of the Al etch foil, the thickness of the Al oxide film is about 0.8 mu m (Example 7) and about 6.2 mu m Mu m (Example 8).

이때, 상기 Al 산화막층의 형성 시, 실시예 7의 경우에는 황산(H₂SO₄) 10중량%, 옥살산(C₂H₂O₄) 2중량%, 붕산나트륨(NaBO₂) 8중량% 및 잔량의 증류수로 이루어진 전해 수용액을 사용하되, 약 10V의 전압을 인가하여 약 2분 동안 산화시켜 진행하였다. 그리고 실시예 8의 경우에는 과염소산(HClO₄) 10중량%, 옥살산(C₂H₂O₄) 2중량%, 붕산나트륨(NaBO₂) 8중량% 및 잔량의 증류수로 이루어진 전해 수용액을 사용하되, 약 15V의 전압을 인가하여 약 25분 동안 산화시켜 진행하였다. At this time, in the case of forming the Al oxide film layer, 10 wt% of sulfuric acid (H ₂ SO ₄ ), ₂ wt% of oxalic acid (C ₂ H ₂ O ₄ ), 8 wt% of sodium borate (NaBO ₂ ) An electrolytic aqueous solution consisting of distilled water was used and oxidized for about 2 minutes by applying a voltage of about 10V. In the case of Example 8, an electrolytic aqueous solution containing 10 wt% of perchloric acid (HClO ₄ ), 2 wt% of oxalic acid (C ₂ H ₂ O ₄ ), 8 wt% of sodium borate (NaBO ₂ ) A voltage of about 15 V was applied, and oxidation proceeded for about 25 minutes.

[비교예 1][Comparative Example 1]

상기 실시예 1과 비교하여, Al 에칭 포일 및 바인더를 달리한 것을 제외하고는 실시예 1과 동일하게 실시하여 EDLC 셀을 제조하였다. 구체적으로, 본 비교예서는, Al 에칭 포일로는 산화시키지 않을 사용하였다. 그리고 바인더로는 부타디엔-스티렌-메틸 메타크릴레이트 공중합체(BSM)를 사용하지 않고, EDLC 제조에서 일반적으로 사용되고 있는 스티렌-부탄디엔 고무(SBR)를 대신 사용하여, 활성탄 100중량부에 대하여 아세틸렌 블랙 약 6중량부, 카르복시메틸셀룰로오스(CMC) 약 1.5중량부 및 스티렌-부탄디엔 고무(SBR) 약 2중량부를 포함하는 활성탄 전극 조성물을 이용하여 활성탄 전극을 형성시켰다. An EDLC cell was fabricated in the same manner as in Example 1, except that the Al etch foil and the binder were different from those of Example 1. Specifically, in this comparative example, the Al etching foil was used without being oxidized. As a binder, instead of butadiene-styrene-methyl methacrylate copolymer (BSM), styrene-butadiene rubber (SBR) generally used in the production of EDLC was used instead of acetylene black An activated carbon electrode was formed using an activated carbon electrode composition comprising about 6 parts by weight of a carbon black, about 1.5 parts by weight of carboxymethyl cellulose (CMC), and about 2 parts by weight of styrene-butadiene rubber (SBR).

< 전기적 특성 평가 > &Lt; Evaluation of electrical characteristics &

상기 각 실시예 및 비교예에 따른 EDLC 셀에 대하여, 3.0V 전압에서의 단위 체적당 정전 용량(F/cc)과 내부 저항(mΩ)을 측정하고, 그 결과를 하기 [표 1]에 나타내었다. The capacitance (F / cc) and the internal resistance (m?) Per unit volume at a voltage of 3.0 V were measured for the EDLC cell according to each of the Examples and Comparative Examples, and the results are shown in Table 1 below .

< EDLC 셀의 전기적 특성 평가 결과(@ 3.0V) > <Evaluation results of electrical characteristics of EDLC cell (@ 3.0V)> 　
비　 고
Remarks Al 산화막층Al oxide film layer 활성탄 전극Activated carbon electrode 전해액Electrolyte 정전 용량
[F/cc]capacitance
[F / cc] 저항
[mΩ]resistance
[mΩ] 두께thickness 전해 수용액Electrolytic aqueous solution 활성탄Activated carbon 바인더(함량)Binder (content) 실시예 1Example 1 2.6㎛2.6 탆 HClO₄ + C₂H₂O₄ HClO ₄ + C ₂ H ₂ O ₄ YP-50FYP-50F CMC + BSM(2중량부)CMC + BSM (2 parts by weight) E/A/DE / A / D 13.713.7 7.67.6 실시예 2Example 2 2.6㎛2.6 탆 HClO₄ + C₂H₂O₄ HClO ₄ + C ₂ H ₂ O ₄ YP-50FYP-50F CMC + BSM(3중량부)CMC + BSM (3 parts by weight) E/A/DE / A / D 13.413.4 8.58.5 실시예 3Example 3 2.6㎛2.6 탆 HClO₄ + C₂H₂O₄ HClO ₄ + C ₂ H ₂ O ₄ YP-50FYP-50F CMC + BSM(4중량부)CMC + BSM (4 parts by weight) E/A/DE / A / D 13.213.2 8.68.6 실시예 4Example 4 2.6㎛2.6 탆 HClO₄ + C₂H₂O₄ HClO ₄ + C ₂ H ₂ O ₄ MSP-20MSP-20 CMC + BSM(2중량부)CMC + BSM (2 parts by weight) E/A/DE / A / D 16.416.4 11.511.5 실시예 5Example 5 2.6㎛2.6 탆 HClO₄ + C₂H₂O₄ HClO ₄ + C ₂ H ₂ O ₄ YP-50FYP-50F CMC + SBR(2중량부)CMC + SBR (2 parts by weight) E/A/DE / A / D 13.313.3 8.58.5 실시예 6Example 6 2.6㎛2.6 탆 HClO₄ HClO ₄ YP-50FYP-50F CMC + BSM(2중량부)CMC + BSM (2 parts by weight) E/A/DE / A / D 12.812.8 9.29.2 실시예 7Example 7 0.8㎛0.8 탆 H₂SO₄+ C₂H₂O₄ H ₂ SO ₄ + C ₂ H ₂ O ₄ YP-50FYP-50F CMC + BSM(2중량부)CMC + BSM (2 parts by weight) E/A/DE / A / D 12.812.8 8.98.9 실시예 8Example 8 6.2㎛6.2 탆 HClO₄ + C₂H₂O₄ HClO ₄ + C ₂ H ₂ O ₄ YP-50FYP-50F CMC + BSM(2중량부)CMC + BSM (2 parts by weight) E/A/DE / A / D 13.913.9 9.89.8 비교예 1Comparative Example 1 -- -- YP-50FYP-50F CMC + SBR(2중량부)CMC + SBR (2 parts by weight) E/AE / A 12.512.5 10.510.5
* YP-50F : 야자 껍질 활성탄(스팀으로 활성화된 제품)
* MSP-20 : 페놀 수지계 활성탄(KOH로 활성화된 제품)
* CMC : 카르복시메틸셀룰로오스
* BSM : 부타디엔-스티렌-메틸 메타크릴레이트 공중합체
* SBR : 스티렌-부타디엔 고무
* E : 전해질, (C₂H₅)₄NBF₄
* A : 유기 용매, 아세토니트릴(ACN)
* D : 가스 발생 억제제, 1,3-다이아졸

* YP-50F: Coconut shell activated carbon (activated by steam)
* MSP-20: Phenolic resin-based activated carbon (activated by KOH)
* CMC: Carboxymethylcellulose
* BSM: Butadiene-styrene-methyl methacrylate copolymer
* SBR: styrene-butadiene rubber
* E: electrolyte, (C ₂ H ₅ ) ₄ NBF ₄
* A: Organic solvent, acetonitrile (ACN)
* D: gas generation inhibitor, 1,3-diazole

상기 [표 1]에 보인 바와 같이, Al 에칭 포일에 Al 산화막층이 형성된 실시예들에 따른 셀 시편은 그렇지 않은 경우(비교예 1)보다 높은 용량을 가짐을 알 수 있다. 또한, 실시예 1, 실시예 7 및 실시예 8을 대비해 보면, Al 산화막층의 두께가 증가할수록 용량이 높아짐을 알 수 있다. 그러나 실시예 8에서와 같이, 두께가 너무 두꺼우면 저항이 다소 높아짐을 알 수 있다. As shown in Table 1, the cell specimen in which the Al oxide film layer is formed on the Al etched foil has higher capacity than the cell specimen in Comparative Example 1. Also, in comparison with Examples 1, 7, and 8, it can be seen that as the thickness of the Al oxide film increases, the capacity increases. However, as in Embodiment 8, it can be seen that the resistance becomes somewhat higher if the thickness is too thick.

아울러, 실시예 1 및 실시예 6을 대비해 보면, Al 산화막층을 형성함에 있어, 전해 수용액으로서 옥살산(C₂H₂O₄)을 더 포함시켜 사용하는 경우에 용량 및 저항 특성에서 유리함을 알 수 있다. 이는 옥살산(C₂H₂O₄)을 더 포함시켜 사용하는 경우, Al 산화막층의 내화학성 및 경도가 개선되어 전해액에 의한 Al 산화막층의 용해가 방지된 것이기 때문인 것으로 판단된다. In contrast to Examples 1 and 6, it was found that the use of further oxalic acid (C ₂ H ₂ O ₄ ) as an electrolytic aqueous solution in forming the Al oxide film layer is advantageous in capacity and resistance characteristics have. It is considered that this is because, when oxalic acid (C ₂ H ₂ O ₄ ) is further used, the chemical resistance and hardness of the Al oxide film layer are improved and the dissolution of the Al oxide film layer by the electrolytic solution is prevented.

한편, 실시예 1 및 실시예 4를 대비해 보면, 활성탄의 경우에는 스팀으로 활성화한 제품(YP-50F)이 KOH로 활성화한 제품(MSP-20)보다 저항 특성에서 유리함을 알 수 있다. 이는 스팀으로 활성화한 활성탄(YP-50F)이 KOH로 활성화한 활성탄(MSP-20)보다 불순물의 함량이 낮기 때문인 것으로 판단된다. On the other hand, in comparison with Examples 1 and 4, it can be seen that, in the case of activated carbon, the product activated by steam (YP-50F) is more advantageous in resistance than the product activated by KOH (MSP-20). This is because the activated carbon (YP-50F) activated by steam is lower in content of impurities than activated carbon activated by KOH (MSP-20).

또한, 실시예 1 및 실시예 5를 대비해 보면, 바인더로서 나노 크기의 부타디엔-스티렌-메틸 메타크릴레이트 공중합체(BSM)를 사용한 경우(실시예 1)가 스티렌-부타디엔 고무(SBR)를 사용하는 경우(실시예 5)보다 용량 및 저항 특성에서 유리함을 알 수 있다. 이는 높은 분산성을 가짐과 함께 접착력의 개선 및 가스 발생이 낮기 때문인 것으로 판단된다. In contrast to Examples 1 and 5, when a nano-sized butadiene-styrene-methyl methacrylate copolymer (BSM) was used as the binder (Example 1), styrene-butadiene rubber (SBR) (Example 5) is more advantageous in terms of capacity and resistance characteristics. This is because it has a high dispersibility and an improvement in adhesion and a low gas generation.

< 접착력 평가 > &Lt; Evaluation of adhesion &

바인더의 함량 및 종류에 따른 층간 접착력을 알아보고자, 상기 실시예 1 ~ 3, 실시예 5 및 비교예 1에 따른 전극 시트(Al 에칭 포일 + 활성탄 전극의 적층 시트)에 대하여 층간 접착력을 평가하였다. 이때, 층간 접착력은 90도 박리 테스트(peel test) 방법을 이용하였으며, Al 에칭 포일과 활성탄 전극 사이의 박리력을 평가하였다. 그 결과를 첨부된 도 3에 나타내었다. In order to evaluate the interlaminar adhesive strength depending on the content and type of the binder, the interlaminar adhesive strength of the electrode sheet (Al-etched foil + laminated sheet of activated carbon electrode) according to Examples 1 to 3, Example 5 and Comparative Example 1 was evaluated. At this time, a 90 degree peel test method was used for the interlayer adhesion, and the peeling force between the Al etched foil and the activated carbon electrode was evaluated. The results are shown in Fig.

첨부된 도 3에 나타낸 바와 같이, 바인더의 함량, 즉 부타디엔-스티렌-메틸 메타크릴레이트 공중합체(BSM)의 함량이 증가할수록 층간 접착력이 우수함을 알 수 있다. 또한, 실시예 1과, 실시예 5 및 비교예 1을 대비해 보면, 동일한 함량(2중량부)에서 부타디엔-스티렌-메틸 메타크릴레이트 공중합체(BSM)를 사용한 경우(실시예 1)가 스티렌-부타디엔 고무(SBR)를 사용하는 경우(실시예 5 및 비교예 1)보다 층간 접착력이 우수함을 알 수 있다. As shown in FIG. 3, it can be seen that as the content of the binder, that is, the content of the butadiene-styrene-methyl methacrylate copolymer (BSM) increases, the interlayer adhesion is excellent. In contrast to Example 1, Example 5 and Comparative Example 1, when a butadiene-styrene-methyl methacrylate copolymer (BSM) was used in the same amount (2 parts by weight) (Example 1) It can be seen that the interlaminar adhesive strength is superior to the case of using butadiene rubber (SBR) (Example 5 and Comparative Example 1).

[실시예 9 내지 17][Examples 9 to 17]

상기 실시예 1과 동일하게 실시하되, 하기 [표 2]에 보인 바와 같이 각 실시예에 따라 전해액의 조성과, 활성탄 전극을 구성하는 바인더의 종류 및 함량을 달리하였다. 그리고 각 실시예에 따른 EDLC 셀에 대하여 정전 용량 및 저항을 평가하고, 그 결과를 하기 [표 2]에 함께 나타내었다. 이때, 하기 [표 2]에서, 바인더의 함량(중량부)는 활성탄 100중량부에 대한 고형분 기준이다. The composition of the electrolytic solution and the kind and content of the binder constituting the activated carbon electrode were varied according to each example as shown in Table 2 below. The EDLC cell according to each example was evaluated for capacitance and resistance, and the results are shown in Table 2 below. At this time, in the following [Table 2], the content (parts by weight) of the binder is based on the solid basis with respect to 100 parts by weight of activated carbon.

구체적으로, 본 실시예 9 내지 17에서는 전해액으로서, 1.0mol/L의 (C₂H₅)₄NBF₄(전해질)과 프로필렌 카보네이트(유기 용매)이 혼합된 용액[(C₂H₅)₄NBF₄/PC]을 준비한 다음, 여기에 염기성 유기화합물(가스 발생 억제제)로서 트리에틸아민(triethylamine)을 더 첨가(용해)하여 제조한 유기 용액을 사용하였다. 이때, 상기 트리에틸아민은 전해액 전체 중량 기준으로 약 0.5중량%가 되도록 첨가되었다. Specifically, in Examples 9 to 17, as an electrolytic solution, a solution [(C ₂ H ₅ ) ₄ NBF (C ₂ H ₅ ) _{4] in which} 1.0 mol / L of (C ₂ H ₅ ) ₄ NBF ₄ (electrolyte) and propylene carbonate (organic solvent) ₄ / PC] was prepared, and then triethylamine was further added (dissolved) as a basic organic compound (gas generation inhibitor). At this time, the triethylamine was added in an amount of about 0.5% by weight based on the total weight of the electrolytic solution.

또한, 활성탄 전극을 형성함에 있어서, 실시예 9 ~ 11의 경우에는 바인더로서 카르복시메틸셀룰로오스(CMC)과 부타디엔-스티렌-부틸 메타크릴레이트 공중합체(BSB)의 혼합을 사용하되, 상기 부타디엔-스티렌-부틸 메타크릴레이트 공중합체(BSB)는 부타디엔 단량체 40중량%, 스티렌 단량체 5중량% 및 부틸 메타크릴레이트 단량체 55중량%가 공중합된 것으로서, 약 80nm ~ 120nm의 입도 분포를 가지는 나노 미립자를 사용하였다. 그리고 실시예 12 ~ 14의 경우에는 바인더로서 카르복시메틸셀룰로오스(CMC)과 스티렌-부타디엔 고무(SBR)의 혼합을 사용하였으며, 실시예 15 ~ 17의 경우에는 바인더로서 카르복시메틸셀룰로오스(CMC)와 폴리테트라플루오로에틸렌(PTFE)의 혼합을 사용하였다. In the case of Examples 9 to 11, a mixture of carboxymethylcellulose (CMC) and butadiene-styrene-butylmethacrylate copolymer (BSB) was used as the binder in the formation of the activated carbon electrode, and the butadiene- Butylmethacrylate copolymer (BSB) was prepared by copolymerizing 40% by weight of butadiene monomer, 5% by weight of styrene monomer and 55% by weight of butyl methacrylate monomer, and nanoparticles having a particle size distribution of about 80 to 120 nm were used. In Examples 12 to 14, a mixture of carboxymethylcellulose (CMC) and styrene-butadiene rubber (SBR) was used as a binder. In Examples 15 to 17, a mixture of carboxymethylcellulose (CMC) A mixture of fluoroethylene (PTFE) was used.

[실시예 18 및 19][Examples 18 and 19]

상기 실시예 9 및 12와 대비하여, 활성탄 전극의 롤링 압연 시, 롤링 온도를 달리한 것을 제외하고는 동일하게 실시하여 EDLC 셀을 제조하였다. 구체적으로, 실시예 18의 경우에는 실시예 9와 동일하게 실시하되, 상온(약 12℃)에서 활성탄 전극을 롤링 압연하였으며, 실시예 19의 경우에는 실시예 12와 동일하게 실시하되, 상온(약 12℃)에서 활성탄 전극을 롤링 압연하여 제조하였다. In contrast to Examples 9 and 12, an EDLC cell was manufactured by performing the same operation except that the rolling temperature of the activated carbon electrode was changed during rolling. Specifically, in the case of Example 18, the activated carbon electrode was rolled by rolling in the same manner as in Example 9 except that the activated carbon electrode was rolled at room temperature (about 12 ° C). In the case of Example 19, 12 < [deg.] &Gt; C).

[비교예 2][Comparative Example 2]

상기 실시예 19와 비교하여, 전해액에 염기성 유기화합물(가스 발생 억제제)로서 트리에틸아민(triethylamine)이 첨가되지 않는 것을 사용한 것을 제외하고는 동일하게 실시하였다. 즉, 본 비교예에서는 전해액으로서 1.0mol/L의 (C₂H₅)₄NBF₄(전해질)과 프로필렌 카보네이트(유기 용매)이 혼합된 용액[(C₂H₅)₄NBF₄/PC]을 사용하였다. The same procedure as in Example 19 was repeated except that triethylamine was not added as the basic organic compound (gas generation inhibitor) to the electrolytic solution. That is, in this comparative example, a solution [(C ₂ H ₅ ) ₄ NBF ₄ / PC] in which 1.0 mol / L of (C ₂ H ₅ ) ₄ NBF ₄ (electrolyte) and propylene carbonate (organic solvent) Respectively.

< EDLC 셀의 전기적 특성 평가 결과(@ 3.0V) > <Evaluation results of electrical characteristics of EDLC cell (@ 3.0V)> 비　 고Remarks 바인더(함량)Binder (content) 전해액Electrolyte 롤링 온도Rolling temperature 정전 용량
[F/cc]capacitance
[F / cc] 저항
[mΩ]resistance
[mΩ] 실시예 9Example 9 CMC(1.0중량부) + BSB(0.5중량부)CMC (1.0 part by weight) + BSB (0.5 part by weight) E/P/TE / P / T 150℃150 ℃ 12.512.5 18.018.0 실시예 10Example 10 CMC(1.0중량부) + BSB(0.75중량부)CMC (1.0 part by weight) + BSB (0.75 part by weight) E/P/TE / P / T 150℃150 ℃ 12.412.4 17.617.6 실시예 11Example 11 CMC(1.0중량부) + BSB(1.0중량부)CMC (1.0 part by weight) + BSB (1.0 part by weight) E/P/TE / P / T 150℃150 ℃ 12.412.4 17.217.2 실시예 12Example 12 CMC(1.0중량부) + SBR(0.5중량부)CMC (1.0 part by weight) + SBR (0.5 part by weight) E/P/TE / P / T 150℃150 ℃ 12.312.3 18.718.7 실시예 13Example 13 CMC(1.0중량부) + SBR(0.75중량부)CMC (1.0 part by weight) + SBR (0.75 part by weight) E/P/TE / P / T 150℃150 ℃ 12.212.2 18.518.5 실시예 14Example 14 CMC(1.0중량부) + SBR(1.0중량부)CMC (1.0 part by weight) + SBR (1.0 part by weight) E/P/TE / P / T 150℃150 ℃ 12.412.4 18.018.0 실시예 15Example 15 CMC(1.0중량부) + PTFE(0.5중량부)CMC (1.0 part by weight) + PTFE (0.5 part by weight) E/P/TE / P / T 150℃150 ℃ 12.212.2 20.720.7 실시예 16Example 16 CMC(1.0중량부) + PTFE(0.75중량부)CMC (1.0 part by weight) + PTFE (0.75 part by weight) E/P/TE / P / T 150℃150 ℃ 12.212.2 20.220.2 실시예 17Example 17 CMC(1.0중량부) + PTFE(1.0중량부)CMC (1.0 part by weight) + PTFE (1.0 part by weight) E/P/TE / P / T 150℃150 ℃ 12.312.3 20.020.0 실시예 18Example 18 CMC(1.0중량부) + BSB(0.5중량부)CMC (1.0 part by weight) + BSB (0.5 part by weight) E/P/TE / P / T 상온Room temperature 13.213.2 15.815.8 실시예 19Example 19 CMC(1.0중량부) + SBR(0.5중량부)CMC (1.0 part by weight) + SBR (0.5 part by weight) E/P/TE / P / T 상온Room temperature 12.812.8 16.916.9 비교예 2Comparative Example 2 CMC(1.0중량부) + SBR(0.5중량부)CMC (1.0 part by weight) + SBR (0.5 part by weight) E/PE / P 상온Room temperature 12.512.5 19.719.7
* CMC : 카르복시메틸셀룰로오스
* BSB : 부타디엔-스티렌-부틸 메타크릴레이트 공중합체
* SBR : 스티렌-부타디엔 고무
* PTFE : 폴리테트라플루오로에틸렌
* E : 전해질, (C₂H₅)₄NBF₄
* P : 유기 용매, 프로필렌 카보네이트(PC)
* T : 가스 발생 억제제, 트리에틸아민

* CMC: Carboxymethylcellulose
* BSB: Butadiene-styrene-butyl methacrylate copolymer
* SBR: styrene-butadiene rubber
* PTFE: Polytetrafluoroethylene
* E: electrolyte, (C ₂ H ₅ ) ₄ NBF ₄
* P: Organic solvent, propylene carbonate (PC)
* T: gas generation inhibitor, triethylamine

상기 [표 2]에 보인 바와 같이, 부타디엔-스티렌-부틸 메타크릴레이트 공중합체(BSB)를 사용한 경우가 스티렌-부타디엔 고무(SBR)이나 폴리테트라플루오로에틸렌(PTFE)을 사용하는 경우보다 우수한 정전 용량 및 저항 특성을 가짐을 알 수 있다. 아울러, 실시예 18(및 실시예 19)과 실시예 9(및 실시예 12)와 대비하여 보면, 롤링 압연 시 상온에서 진행한 경우에 저항 특성이 우수해짐을 알 수 있다. As shown in Table 2, the use of butadiene-styrene-butyl methacrylate copolymer (BSB) was superior to the case of using styrene-butadiene rubber (SBR) or polytetrafluoroethylene (PTFE) Capacity and resistance characteristics. Compared with Example 18 (and Example 19) and Example 9 (and Example 12), it is understood that resistance characteristics are improved when rolling is performed at normal temperature in rolling.

한편, 상기 실시예 9 ~ 17에 따른 전극 시트(Al 에칭 포일 + 활성탄 전극의 적층 시트)에 대하여, Al 에칭 포일과 활성탄 전극 사이의 층간 접착력(90도 박리 테스트)을 평가하였다. 그 결과를 첨부된 도 4에 나타내었다. On the other hand, the interlayer adhesion (90 degree peel test) between the Al etched foil and the activated carbon electrode was evaluated for the electrode sheet (Al etched foil + laminated sheet of activated carbon electrode) according to Examples 9-17. The results are shown in the attached FIG.

도 4에 보인 바와 같이, 바인더의 함량이 높을수록 층간 접착력이 증가함을 알 수 있다. 특히, 동일한 함량에서, 부타디엔-스티렌-부틸 메타크릴레이트 공중합체(BSB)를 사용한 경우가 스티렌-부타디엔 고무(SBR)이나 폴리테트라플루오로에틸렌(PTFE)을 사용하는 경우보다 우수한 층간 접착력을 가짐을 알 수 있다. As shown in FIG. 4, the higher the content of the binder, the greater the interlayer adhesion. Particularly, in the case of using the butadiene-styrene-butyl methacrylate copolymer (BSB) in the same content, the interlayer adhesion is superior to that in the case of using styrene-butadiene rubber (SBR) or polytetrafluoroethylene (PTFE) Able to know.

이상의 실험예를 통해 확인되는 바와 같이, 본 발명의 실시예들에 따른 셀 시편은 3.0V의 고전압에서 우수한 전기적 특성을 가짐을 알 수 있다. 이는 고전압 특성을 가짐을 의미한다. 아울러, 금속 집전체(Al 에칭 포일)에 금속 산화막층(Al 산화막층)이 형성된 경우가 그렇지 않은 경우보다 우수한 전기적 특성(고용량 등)을 가짐을 알 수 있다. As can be seen from the above experimental example, the cell specimen according to the embodiments of the present invention has excellent electrical characteristics at a high voltage of 3.0V. This means that it has a high voltage characteristic. It is also found that the case where the metal oxide film layer (Al oxide film layer) is formed on the metal current collector (Al etched foil) has better electrical characteristics (such as a high capacity) than the case where the metal oxide film layer (Al oxide film) is not formed.

또한, 바인더로서 나노 미립자의 부타디엔-스티렌-알킬 메타크릴레이트 공중합체를 사용하면, 층간 접착력 및 전극 밀도 등이 향상되어 우수한 전기적 특성(고용량 및 저저항 등)을 가지며, 이와 함께 높은 용량 유지율과 낮은 저항 증가율을 가져 장기 신뢰성 및 장수명 특성 등을 도모함을 알 수 있다. 부가적으로, 활성탄 전극의 형성 시, 상온에서 롤링 압연하는 경우가 고온(예, 150℃)에서 롤링 압연하는 경우보다 저항 특성에서 유리함을 알 수 있다. When a nano-particle butadiene-styrene-alkyl methacrylate copolymer is used as a binder, interlayer adhesion and electrode density are improved to have excellent electrical properties (such as high capacity and low resistance) It is possible to know the long-term reliability and long-life characteristics by increasing the resistance. In addition, it can be seen that, in the case of forming the activated carbon electrode, the case of rolling rolling at room temperature is more advantageous than the case of rolling rolling at a high temperature (for example, 150 ° C).

10 : 양극 20 : 음극
12, 22 : 금속 집전체 12a, 22a : 금속 산화막층
14, 24 : 활성탄 전극 15, 25 : 단자
30 : 세퍼레이터 50 : 테이프
100 : 전극체 200 : 하우징
a : 요철 구조 R : 롤러 10: anode 20: cathode
12, 22: metal current collectors 12a, 22a: metal oxide film layers
14, 24: activated carbon electrode 15, 25: terminal
30: separator 50: tape
100: electrode body 200: housing
a: concave and convex structure R: roller

Claims

양극;
음극;
전해액; 및
상기 양극과 음극의 사이에 개재된 세퍼레이터를 포함하고,
상기 전해액은 전해질, 유기 용매 및 가스 발생 억제제를 포함하는 것을 특징으로 하는 슈퍼커패시터.
anode;
cathode;
Electrolytic solution; And
And a separator interposed between the positive electrode and the negative electrode,
Wherein the electrolyte solution comprises an electrolyte, an organic solvent, and a gas generation inhibitor.

제1항에 있어서,
상기 가스 발생 억제제는 염기성 유기화합물 및 다공성 무기물 입자로부터 선택된 하나 이상을 포함하고,
상기 양극과 음극 중에서 선택된 하나 이상은 금속 집전체와, 상기 금속 집전체 상에 형성된 활성탄 전극을 포함하되,
상기 금속 집전체는 활성탄 전극과 접합하는 표면에 산화되어 형성된 금속 산화막층을 포함하며,
상기 활성탄 전극은 활성탄, 바인더 및 도전재를 포함하되,
상기 바인더는 카르복시메틸셀룰로오스와 부타디엔-스티렌-알킬 메타크릴레이트 공중합체를 포함하는 것을 특징으로 하는 슈퍼커패시터.
The method according to claim 1,
Wherein the gas generation inhibitor comprises at least one selected from a basic organic compound and a porous inorganic particle,
Wherein at least one selected from the anode and the cathode comprises a metal current collector and an activated carbon electrode formed on the metal current collector,
Wherein the metal current collector includes a metal oxide layer formed by oxidation on a surface bonded to an activated carbon electrode,
The activated carbon electrode includes activated carbon, a binder, and a conductive material,
Wherein the binder comprises carboxymethylcellulose and a butadiene-styrene-alkyl methacrylate copolymer.

제2항에 있어서,
상기 금속 집전체는 5㎛ 내지 12㎛의 두께를 가지는 금속 에칭 포일(metal etching foil)이고,
상기 금속 산화막층은 1㎛ 내지 5㎛의 두께를 가지며,
상기 활성탄은 스팀(steam)에 의해 활성화되고, 5 ~ 30㎛의 평균 입도 크기와 1500 ~ 2500㎥/g의 비표면적을 가지며,
상기 바인더는 카르복시메틸셀룰로오스와 부타디엔-스티렌-알킬 메타크릴레이트 공중합체를 1 : 0.2 ~ 5의 중량비로 포함하고,
상기 부타디엔-스티렌-알킬 메타크릴레이트 공중합체는 80nm ~ 230nm의 평균 입자 크기를 가지는 것을 특징으로 하는 슈퍼커패시터.
3. The method of claim 2,
The metal current collector is a metal etching foil having a thickness of 5 占 퐉 to 12 占 퐉,
Wherein the metal oxide film layer has a thickness of 1 탆 to 5 탆,
The activated carbon is activated by steam and has an average particle size of 5 to 30 mu m and a specific surface area of 1500 to 2500 m < 3 > / g,
The binder contains carboxymethylcellulose and a butadiene-styrene-alkyl methacrylate copolymer in a weight ratio of 1: 0.2 to 5,
Wherein the butadiene-styrene-alkyl methacrylate copolymer has an average particle size of 80 nm to 230 nm.

양극을 준비하는 단계;
음극을 준비하는 단계;
상기 양극과 음극의 사이에 세퍼레이터를 개재한 적층체를 얻는 단계; 및
상기 적층체를 전해액에 함침하는 단계를 포함하고,
상기 전해액은 전해질, 유기 용매 및 가스 발생 억제제를 포함하는 것을 특징으로 하는 슈퍼커패시터의 제조방법.
Preparing an anode;
Preparing a cathode;
Obtaining a laminate including a separator between the anode and the cathode; And
Impregnating the laminate with an electrolytic solution,
Wherein the electrolyte solution comprises an electrolyte, an organic solvent, and a gas generation inhibitor.

제4항에 있어서,
상기 양극을 준비하는 단계와 음극을 준비하는 단계 중에서 선택된 하나 이상의 단계는,
금속 집전체를 전해 수용액에 침지한 다음, 상기 금속 집전체를 양극(+)으로 하고 전압을 인가하여, 상기 금속 집전체의 표면에 금속 산화막층을 형성하는 공정 a); 및
상기 금속 산화물층 상에 활성탄 전극을 형성하는 공정 b)를 포함하되,
상기 금속 산화막층을 형성하는 공정 a)에서는,
상기 금속 집전체로서 5㎛ 내지 12㎛의 두께를 가지는 금속 에칭 포일(metal etching foil)을 사용하고,
상기 전해 수용액으로서 과염소산(HClO₄)과 옥살산(C₂H₂O₄)을 포함하는 전해 수용액을 사용하여, 1㎛ 내지 5㎛의 두께를 가지는 금속 산화막층을 형성하며,
상기 활성탄 전극을 형성하는 공정 b)에서는,
활성탄, 바인더 및 도전재를 포함하는 활성탄 전극 조성물을 사용하되,
상기 활성탄은 스팀(steam)에 의해 활성화되고, 5 ~ 30㎛의 평균 입도 크기와 1500 ~ 2500㎥/g의 비표면적을 가지는 활성탄을 사용하고,
상기 바인더는 카르복시메틸셀룰로오스와 부타디엔-스티렌-알킬 메타크릴레이트 공중합체를 1 : 0.2 ~ 5의 중량비로 포함하는 바인더를 사용하는 것을 특징으로 하는 슈퍼커패시터의 제조방법.
5. The method of claim 4,
Wherein the step of preparing the positive electrode and the step of preparing the negative electrode comprise:
A) a step (a) of immersing the metal current collector in an electrolytic aqueous solution and then forming the metal current collector on the surface of the metal current collector by applying a voltage to the positive electrode (+); And
And b) forming an activated carbon electrode on the metal oxide layer,
In the step a) of forming the metal oxide film layer,
A metal etching foil having a thickness of 5 占 퐉 to 12 占 퐉 is used as the metal current collector,
An electrolytic aqueous solution containing perchloric acid (HClO ₄ ) and oxalic acid (C ₂ H ₂ O ₄ ) is used as the electrolytic aqueous solution to form a metal oxide film layer having a thickness of 1 μm to 5 μm,
In the step b) of forming the activated carbon electrode,
An activated carbon electrode composition comprising activated carbon, a binder and a conductive material is used,
The activated carbon is activated by steam and uses activated carbon having an average particle size of 5 to 30 μm and a specific surface area of 1500 to 2500 m 3 / g,
Wherein the binder comprises a binder containing carboxymethylcellulose and a butadiene-styrene-alkyl methacrylate copolymer in a weight ratio of 1: 0.2 to 5.

제5항에 있어서,
상기 활성탄 전극을 형성하는 공정 b)에서는,
활성탄, 바인더 및 도전재를 포함하는 활성탄 전극 조성물을 시트 상으로 제조한 다음, 상기 시트를 금속 집전체의 금속 산화막층 상에 롤링 압연하여 활성탄 전극을 형성하거나,
활성탄, 바인더 및 도전재를 포함하는 활성탄 전극 조성물을 상기 금속 집전체의 금속 산화막층 상에 코팅한 다음, 롤링 압연하여 활성탄 전극을 형성하되,
상기 롤링 압연은 상온에서 진행하는 것을 특징으로 하는 슈퍼커패시터의 제조방법.
6. The method of claim 5,
In the step b) of forming the activated carbon electrode,
An activated carbon electrode composition including activated carbon, a binder and a conductive material is formed into a sheet, and the sheet is rolled and rolled on a metal oxide layer of a metal current collector to form an activated carbon electrode,
An activated carbon electrode composition comprising activated carbon, a binder and a conductive material is coated on the metal oxide layer of the metal current collector, followed by rolling to form an activated carbon electrode,
Wherein the rolling is performed at room temperature. &Lt; RTI ID = 0.0 > 11. < / RTI >