KR20170116080A - Adhesive composition for polarizing film, adhesive layer for polarizing film, adhesive layer-including polarizing film, and image display device - Google Patents

Adhesive composition for polarizing film, adhesive layer for polarizing film, adhesive layer-including polarizing film, and image display device Download PDF

Info

Publication number
KR20170116080A
KR20170116080A KR1020177025082A KR20177025082A KR20170116080A KR 20170116080 A KR20170116080 A KR 20170116080A KR 1020177025082 A KR1020177025082 A KR 1020177025082A KR 20177025082 A KR20177025082 A KR 20177025082A KR 20170116080 A KR20170116080 A KR 20170116080A
Authority
KR
South Korea
Prior art keywords
sensitive adhesive
pressure
polarizing film
adhesive layer
weight
Prior art date
Application number
KR1020177025082A
Other languages
Korean (ko)
Other versions
KR102046236B1 (en
Inventor
유 모리모토
유우스케 도야마
마사쿠니 후지타
Original Assignee
닛토덴코 가부시키가이샤
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 닛토덴코 가부시키가이샤 filed Critical 닛토덴코 가부시키가이샤
Publication of KR20170116080A publication Critical patent/KR20170116080A/en
Application granted granted Critical
Publication of KR102046236B1 publication Critical patent/KR102046236B1/en

Abstract

본 발명은, 큰 정전기가 발생한 경우여도, 발생한 백색 불균일을 단시간에 소실시킬 수 있고, 엄격한 조건 하의 가열 가습 시험 후에 있어서도 내구성을 만족할 수 있으며, 또한 우수한 외관을 갖는 점착제층을 형성할 수 있는 편광 필름용 점착제 조성물을 제공하는 것을 목적으로 한다. 또, 본 발명은, 상기 점착제 조성물로 형성되는 점착제층, 당해 점착제층을 사용한 점착제층이 형성된 편광 필름, 및 당해 점착제층이 형성된 편광 필름을 사용한 화상 표시 장치를 제공하는 것도 목적으로 한다.
(메트)아크릴계 폴리머 (A), 오늄-아니온염 (B1), 알칼리 금속염 (B2) 를 함유하고, 상기 알칼리 금속염 (B2) 는, 상기 (메트)아크릴계 폴리머 (A) 100 중량부에 대해, 0.4 ∼ 3.5 중량부 함유하고, 상기 알칼리 금속염 (B2) 와 오늄-아니온염 (B1) 의 중량비 (B2/B1) 가, 1.2 ∼ 4 인 것을 특징으로 하는, 편광 필름용 점착제 조성물이다.A polarizing film capable of forming a pressure-sensitive adhesive layer capable of satisfying durability even after a heating and humidifying test under severe conditions in a short period of time even when large static electricity is generated, Sensitive adhesive composition for a pressure-sensitive adhesive sheet. It is another object of the present invention to provide an image display apparatus using a pressure-sensitive adhesive layer formed of the pressure-sensitive adhesive composition, a polarizing film having a pressure-sensitive adhesive layer formed using the pressure-sensitive adhesive layer, and a polarizing film having the pressure-sensitive adhesive layer formed thereon.
(A), an onium salt (B1) and an alkali metal salt (B2), wherein the alkali metal salt (B2) is contained in an amount of 0.4 And the weight ratio (B2 / B1) of the alkali metal salt (B2) and the onium anionide (B1) is 1.2 to 4. The pressure-sensitive adhesive composition for a polarizing film according to claim 1,

Description

편광 필름용 점착제 조성물, 편광 필름용 점착제층, 점착제층이 형성된 편광 필름, 및 화상 표시 장치{ADHESIVE COMPOSITION FOR POLARIZING FILM, ADHESIVE LAYER FOR POLARIZING FILM, ADHESIVE LAYER-INCLUDING POLARIZING FILM, AND IMAGE DISPLAY DEVICE}TECHNICAL FIELD [0001] The present invention relates to a pressure-sensitive adhesive composition for a polarizing film, a pressure-sensitive adhesive layer for a polarizing film, a polarizing film on which a pressure-sensitive adhesive layer is formed,

본 발명은, 편광 필름용 점착제 조성물, 당해 편광 필름용 점착제 조성물로 형성되는 편광 필름용 점착제층, 및 상기 편광 필름용 점착제층을 사용한 점착제층이 형성된 편광 필름에 관한 것이다. 또한, 본 발명은, 상기 점착제층이 형성된 편광 필름을 사용한, 액정 표시 장치, 유기 EL 표시 장치, PDP 등의 화상 표시 장치에 관한 것이다.The present invention relates to a polarizing film comprising a pressure-sensitive adhesive composition for a polarizing film, a pressure-sensitive adhesive layer for a polarizing film formed from the pressure-sensitive adhesive composition for the polarizing film, and a pressure-sensitive adhesive layer using the pressure-sensitive adhesive layer for a polarizing film. Further, the present invention relates to an image display apparatus such as a liquid crystal display, an organic EL display, a PDP or the like using a polarizing film on which the pressure-sensitive adhesive layer is formed.

액정 표시 장치 등은, 그 화상 형성 방식에서 액정 셀의 양측에 편광 소자를 배치하는 것이 필요 불가결하고, 일반적으로는 편광 필름이 첩착 (貼着) 되어 있다. 상기 편광 필름을 액정 셀에 첩착시킬 때에는, 통상적으로 광의 손실을 저감시키기 위하여, 각각의 재료는 점착제를 사용하여 밀착되어 있다. 이와 같은 경우에, 편광 필름을 고착시키는 데에 건조 공정을 필요로 하지 않는 것 등의 메리트를 갖는 점에서, 점착제는, 편광 필름의 편측에 미리 점착제층으로서 형성된 점착제층이 형성된 편광 필름이 일반적으로 사용된다. 점착제층이 형성된 편광 필름의 점착제층에는, 통상적으로 이형 필름이 첩부 (貼付) 되어 있다.In a liquid crystal display device or the like, it is indispensable to arrange polarizing elements on both sides of a liquid crystal cell in the image forming system. In general, a polarizing film is attached (adhered). When the polarizing film is adhered to the liquid crystal cell, in order to reduce the loss of light, each material is adhered by using an adhesive. In such a case, in view of having merits such as not requiring a drying step in fixing the polarizing film, the polarizing film in which the pressure-sensitive adhesive layer formed in advance as a pressure-sensitive adhesive layer is formed on the one side of the polarizing film is generally used Is used. In the pressure-sensitive adhesive layer of the polarizing film on which the pressure-sensitive adhesive layer is formed, a release film is usually pasted (pasted).

액정 표시 장치의 제조시, 상기 점착제층이 형성된 편광 필름을 액정 셀에 첩부할 때에는, 점착제층이 형성된 편광 필름의 점착제층으로부터 이형 필름을 박리하는데, 당해 이형 필름의 박리에 의해 정전기가 발생한다. 이와 같이 하여 발생한 정전기는, 액정 표시 장치 내부의 액정의 배향에 영향을 주어, 불량을 초래하게 된다. 예를 들어, 액정 표시 장치의 사용시의 정전기에 의해, 흑색 표시시에 백색 불균일이 발생한 경우, 그 백색 불균일이, 몇 분간은 없어지지 않는다는 현상이 발생하여, 화면의 표시 특성이 열화된다는 문제점을 갖고 있었다. 또 텔레비전 등에 실장한 후여도, 백라이트와 편광판이 스쳤을 때에 발생하는 정전기가 원인으로, 동일한 백색 불균일이 발생하는 경우가 있었다.When the polarizing film on which the pressure-sensitive adhesive layer is formed is affixed to the liquid crystal cell in manufacturing the liquid crystal display device, the release film is peeled from the pressure-sensitive adhesive layer of the polarizing film on which the pressure-sensitive adhesive layer is formed. The static electricity generated in this way affects the orientation of the liquid crystal inside the liquid crystal display device, resulting in a failure. For example, when white unevenness occurs at the time of black display due to static electricity at the time of use of the liquid crystal display device, there arises a phenomenon that the white unevenness does not disappear for several minutes, and the display characteristic of the screen is deteriorated . Even after mounting on a television or the like, the same white unevenness may occur due to the static electricity generated when the backlight and the polarizing plate strike.

정전기의 발생은, 예를 들어, 편광 필름의 외면에 대전 방지층을 형성함으로써 억제할 수 있지만, 그 효과는 적고, 정전기 발생을 근본적으로 방지할 수 없다는 문제점이 있다. 그 때문에, 정전기 발생의 근본적인 위치에서 발생을 억제하기 위해서는, 점착제층에 대전 방지 기능을 부여하는 것이 요구된다. 점착제층에 대전 방지 기능을 부여하는 수단으로서, 예를 들어, 점착제층을 형성하는 점착제에, 이온성 화합물을 배합하는 것이 제안되어 있다 (예를 들어, 특허문헌 1 또는 2 참조). 특허문헌 1 에서는, 점착제층을 형성하는 점착제에, 이온성 액체, 알칼리 금속염을 대전 방지제로서 사용함으로써, 대전 방지성이 우수한 것이 기재되어 있다. 특허문헌 2 에서는, 이온성 화합물로서 오늄-아니온염에 더하여 알칼리 금속염을 병용함으로써 엄격한 조건 하의 가습 시험 후에 있어서도, 대전 방지 기능과 내구성을 유지할 수 있는 것이 기재되어 있다.The generation of static electricity can be suppressed, for example, by forming an antistatic layer on the outer surface of the polarizing film, but the effect is small and the generation of static electricity can not be fundamentally prevented. For this reason, in order to suppress the occurrence of static electricity at an essential position, it is required to impart an antistatic function to the pressure-sensitive adhesive layer. As means for imparting an antistatic function to the pressure-sensitive adhesive layer, for example, it has been proposed to blend an ionic compound with a pressure-sensitive adhesive for forming a pressure-sensitive adhesive layer (see, for example, Patent Document 1 or 2). Patent Document 1 discloses that an antistatic property is excellent by using an ionic liquid or an alkali metal salt as an antistatic agent in a pressure-sensitive adhesive for forming a pressure-sensitive adhesive layer. Patent Document 2 discloses that an antistatic function and durability can be maintained even after a humidification test under severe conditions by using an alkali metal salt in addition to an onium-anion salt as an ionic compound.

일본 공개특허공보 2006-152235호Japanese Laid-Open Patent Publication No. 2006-152235 일본 공개특허공보 2014-48497호Japanese Laid-Open Patent Publication No. 2014-48497

종래부터 문제가 되고 있던 정전기는, 비교적 작은 것으로서, 종래의 대전 방지 기능을 갖는 점착제층을 사용함으로써, 백색 불균일이 몇 초로 소실되기 때문에 문제되지는 않았다. 그러나, 발생하는 정전기가 큰 경우, 종래의 대전 방지 기능을 갖는 점착제층에서는 발생한 전하를 충분히 중화시킬 수 없기 때문에, 백색 불균일을 단시간에 소실시킬 수 없는 경우가 있었다. 이 경우, 화면상에 백색 불균일이 존재하고, 이른바「백화」라 불리는 불균일이 발생한다. 상기 특허문헌 1, 2 에 기재된 이온성 화합물을 함유하는 점착제 조성물에서는, 이온성 화합물과 알칼리 금속염의 첨가량이 충분히 제어되어 있지 않기 때문에, 발생하는 정전기가 큰 경우에 백화가 발생하는 경우도 있어, 대전 방지 기능 면에서 추가적인 검토의 여지가 있었다.The problem of static electricity, which has been a problem in the past, is a relatively small problem, and the use of a pressure-sensitive adhesive layer having a conventional antistatic function has not posed a problem because white unevenness disappears in a few seconds. However, when the generated static electricity is large, the charge generated in the pressure-sensitive adhesive layer having the antistatic function of the prior art can not be sufficiently neutralized, so that the white unevenness can not be lost in a short time. In this case, white unevenness exists on the screen, and so-called " whitening " occurs. In the pressure-sensitive adhesive composition containing an ionic compound described in Patent Documents 1 and 2, the addition amount of the ionic compound and the alkali metal salt is not sufficiently controlled, so that whitening may occur when the generated static electricity is large, There was room for further review in terms of prevention.

상기 서술한 바와 같이 발생하는 정전기가 큰 경우, 점착제에 높은 대전 방지 기능성을 부여함으로써 발생한 백색 불균일을 단시간에 소실시킬 수 있다. 점착제에 높은 대전 방지 기능성을 부여하는 방법으로는, 도전제량을 많게 하는 방법을 생각할 수 있다. 그러나, 단순히 도전제의 양을 많게 하면, 점착제 중에서 결정화가 일어나 외관 불량이 발생하는 경우가 있었다. 또, 도전제의 양을 많게 하면, 피착체 계면 부근에 도전제가 편석되고, 그 결과, 박리가 발생할 가능성이 있었다 (즉, 신뢰성이나 내구성이 떨어진다). 그 때문에 높은 대전 방지 기능과 신뢰성을 양립시킬 수 있는 점착제층이 요망되고 있었다.When the static electricity generated as described above is large, the white unevenness caused by giving the high antistatic function to the pressure sensitive adhesive can be lost in a short time. As a method of imparting a high antistatic function to the pressure-sensitive adhesive, a method of increasing the amount of the conductive agent can be considered. However, if the amount of the conductive agent is simply increased, crystallization occurs in the pressure-sensitive adhesive, resulting in appearance defects. If the amount of the conductive agent is increased, the conductive agent is segregated in the vicinity of the adherend interface, and as a result, peeling may occur (that is, reliability and durability are poor). Therefore, a pressure-sensitive adhesive layer capable of achieving high antistatic function and reliability has been demanded.

본 발명은, 큰 정전기가 발생한 경우여도, 발생한 백색 불균일을 단시간에 소실시킬 수 있고, 엄격한 조건 하의 가열 가습 시험 후에 있어서도 내구성을 만족할 수 있으며, 또한 우수한 외관을 갖는 점착제층을 형성할 수 있는 편광 필름용 점착제 조성물을 제공하는 것을 목적으로 한다. 또, 본 발명은, 상기 점착제 조성물로 형성되는 점착제층, 당해 점착제층을 사용한 점착제층이 형성된 편광 필름, 및 당해 점착제층이 형성된 편광 필름을 사용한 화상 표시 장치를 제공하는 것도 목적으로 한다.A polarizing film capable of forming a pressure-sensitive adhesive layer capable of satisfying durability even after a heating and humidifying test under severe conditions in a short period of time even when large static electricity is generated, Sensitive adhesive composition for a pressure-sensitive adhesive sheet. It is another object of the present invention to provide an image display apparatus using a pressure-sensitive adhesive layer formed of the pressure-sensitive adhesive composition, a polarizing film having a pressure-sensitive adhesive layer formed using the pressure-sensitive adhesive layer, and a polarizing film having the pressure-sensitive adhesive layer formed thereon.

본 발명자들은 상기 과제를 해결하기 위하여 예의 검토를 거듭한 결과, 하기 편광 필름용 점착제 조성물을 알아내어, 본 발명을 완성하기에 이르렀다.As a result of intensive investigations to solve the above problems, the present inventors have found the following pressure-sensitive adhesive composition for a polarizing film, and have completed the present invention.

즉, 본 발명은, (메트)아크릴계 폴리머 (A), 오늄-아니온염 (B1), 알칼리 금속염 (B2) 를 함유하고, Namely, the present invention relates to a process for producing a polyimide resin composition, which comprises (meth) acryl-based polymer (A), onium-anionite (B1) and alkali metal salt (B2)

상기 알칼리 금속염 (B2) 는, 상기 (메트)아크릴계 폴리머 (A) 100 중량부에 대해, 0.4 ∼ 3.5 중량부 함유하고,  The alkali metal salt (B2) is contained in an amount of 0.4 to 3.5 parts by weight based on 100 parts by weight of the (meth) acrylic polymer (A)

상기 알칼리 금속염 (B2) 와 오늄-아니온염 (B1) 의 중량비 (B2/B1) 가, 1.2 ∼ 4 인 것을 특징으로 하는, 편광 필름용 점착제 조성물에 관한 것이다. Wherein the weight ratio (B2 / B1) of the alkali metal salt (B2) to the onium-anionic salt (B1) is 1.2 to 4. [

본 발명의 편광 필름용 점착제 조성물에, 추가로, 티올계 실란 커플링제 (C1) 을 함유하는 것이 바람직하다.The pressure-sensitive adhesive composition for a polarizing film of the present invention preferably further contains a thiol-based silane coupling agent (C1).

상기 티올계 실란 커플링제 (C1) 은, 상기 (메트)아크릴계 폴리머 (A) 100 중량부에 대해, 0.001 ∼ 5 중량부인 것이 바람직하다.The thiol silane coupling agent (C1) is preferably 0.001 to 5 parts by weight based on 100 parts by weight of the (meth) acryl-based polymer (A).

상기 오늄-아니온염 (B1) 은, 상기 (메트)아크릴계 폴리머 (A) 100 중량부에 대해, 0.1 ∼ 1.5 중량부인 것이 바람직하다.The amount of the onium salt-anion salt (B1) is preferably 0.1 to 1.5 parts by weight based on 100 parts by weight of the (meth) acryl-based polymer (A).

본 발명의 편광 필름용 점착제 조성물에, 추가로, 가교제 (D) 를 함유하는 것이 바람직하다.The pressure-sensitive adhesive composition for a polarizing film of the present invention preferably further contains a crosslinking agent (D).

상기 가교제 (D) 는, (메트)아크릴계 폴리머 (A) 100 중량부에 대해, 0.01 ∼ 20 중량부 함유하는 것이 바람직하다.The crosslinking agent (D) is preferably contained in an amount of 0.01 to 20 parts by weight based on 100 parts by weight of the (meth) acrylic polymer (A).

상기 가교제 (D) 가, 이소시아네이트계 화합물, 및 과산화물로 이루어지는 군에서 선택되는 적어도 1 종의 가교제인 것이 바람직하다.It is preferable that the crosslinking agent (D) is at least one crosslinking agent selected from the group consisting of an isocyanate compound and a peroxide.

본 발명의 편광 필름용 점착제 조성물에, 추가로, 아세토아세틸기 함유 실란 커플링제 (C2) 를 함유하는 것이 바람직하다.It is preferable that the pressure-sensitive adhesive composition for a polarizing film of the present invention further contains an acetoacetyl group-containing silane coupling agent (C2).

또, 본 발명은, 상기 편광 필름용 점착제 조성물로 형성되는 것을 특징으로 하는 편광 필름용 점착제층에 관한 것이다.The present invention also relates to a pressure-sensitive adhesive layer for a polarizing film, which is formed of the pressure-sensitive adhesive composition for a polarizing film.

또, 본 발명은, 편광 필름과, 당해 편광 필름에 형성된 점착제층을 갖는 점착제층이 형성된 편광 필름으로서, The present invention also provides a polarizing film comprising a polarizing film and a pressure-sensitive adhesive layer having a pressure-sensitive adhesive layer formed on the polarizing film,

상기 편광 필름은, 편광자의 편측에만 투명 보호 필름을 갖고, 상기 점착제층은, 상기 편광자의 상기 투명 보호 필름을 갖지 않는 면에 형성되어 있고, 또한 Wherein the polarizing film has a transparent protective film only on one side of the polarizer, the pressure-sensitive adhesive layer is formed on a surface of the polarizer having no transparent protective film,

상기 점착제층이, 상기 편광 필름용 점착제층인 것을 특징으로 하는 점착제층이 형성된 편광 필름에 관한 것이다.Wherein the pressure-sensitive adhesive layer is the pressure-sensitive adhesive layer for the polarizing film.

상기 편광자의 두께가 10 ㎛ 이하인 것이 바람직하다.It is preferable that the thickness of the polarizer is 10 占 퐉 or less.

또한, 본 발명은, 상기 점착제층이 형성된 편광 필름을 적어도 1 개 사용한 것을 특징으로 하는 화상 표시 장치에 관한 것이다.Further, the present invention relates to an image display apparatus using at least one polarizing film on which the above-mentioned pressure-sensitive adhesive layer is formed.

본 발명의 편광 필름용 점착제 조성물은, (메트)아크릴계 폴리머 (A), 오늄-아니온염 (B1), 및 알칼리 금속염 (B2) 를 함유하고, 또한, 상기 오늄-아니온염 (B1) 과 알칼리 금속염 (B2) 의 첨가량을 특정의 범위로 함으로써, 큰 정전기가 발생한 경우여도, 발생한 백색 불균일을 단시간에 소실시킬 수 있고, 엄격한 조건 하의 가열 가습 시험 후에 있어서도 내구성을 만족할 수 있으며, 또한 우수한 외관을 갖는 점착제층을 형성할 수 있다.The pressure-sensitive adhesive composition for a polarizing film of the present invention is a pressure-sensitive adhesive composition for a polarizing film which contains a (meth) acryl-based polymer (A), an onium salt anion salt (B1) and an alkali metal salt (B2) (B2) is set in a specific range, it is possible to eliminate the white unevenness that occurs even in the case of occurrence of large static electricity in a short time, and it is possible to satisfy the durability even after the heating and humidifying test under the severe condition, Layer can be formed.

또, 본 발명의 편광 필름용 점착제 조성물로 형성된 점착제층, 및 당해 점착제층을 포함하는 점착제층이 형성된 편광 필름은, 우수한 대전 방지 기능 및 내구성을 만족하는 것이다. 또, 본 발명의 점착제층이 형성된 편광 필름을 갖는 화상 표시 장치는, 백색 불균일 (백화) 의 발생을 억제할 수 있다.The polarizing film on which the pressure-sensitive adhesive layer formed of the pressure-sensitive adhesive composition for a polarizing film of the present invention and the pressure-sensitive adhesive layer containing the pressure-sensitive adhesive layer are formed satisfies excellent antistatic function and durability. Further, the image display apparatus having the polarizing film in which the pressure-sensitive adhesive layer of the present invention is formed can suppress the occurrence of white unevenness (whitening).

1. 편광 필름용 점착제 조성물 1. Pressure-sensitive adhesive composition for polarizing film

본 발명의 편광 필름용 점착제 조성물은, (메트)아크릴계 폴리머 (A), 오늄-아니온염 (B1), 알칼리 금속염 (B2) 를 함유하고, The pressure-sensitive adhesive composition for a polarizing film of the present invention contains a (meth) acryl-based polymer (A), an onium-anionite (B1) and an alkali metal salt (B2)

상기 알칼리 금속염 (B2) 는, 상기 (메트)아크릴계 폴리머 (A) 100 중량부에 대해 0.4 ∼ 3.5 중량부 함유하고, The alkali metal salt (B2) is contained in an amount of 0.4 to 3.5 parts by weight based on 100 parts by weight of the (meth) acryl-based polymer (A)

상기 알칼리 금속염 (B2) 와 오늄-아니온염 (B1) 의 중량비 (B2/B1) 가, 1.2 ∼ 4 인 것을 특징으로 한다. 이하, 본 발명의 편광 필름용 점착제 조성물의 조성에 대해 상세하게 설명한다. Wherein the weight ratio (B2 / B1) of the alkali metal salt (B2) and the onium-anionite (B1) is 1.2 to 4. Hereinafter, the composition of the pressure-sensitive adhesive composition for a polarizing film of the present invention will be described in detail.

(1) (메트)아크릴계 폴리머 (A)(1) (meth) acryl-based polymer (A)

본 발명의 편광 필름용 점착제 조성물은, 베이스 폴리머로서 (메트)아크릴계 폴리머 (A) 를 함유한다. (메트)아크릴계 폴리머 (A) 는, 통상적으로 모노머 단위로서 알킬(메트)아크릴레이트를 주성분으로서 함유한다. 또한, (메트)아크릴레이트는, 아크릴레이트 및/또는 메타크릴레이트를 말하며, 본 발명의 (메트) 와는 동일한 의미이다.The pressure-sensitive adhesive composition for a polarizing film of the present invention contains (meth) acrylic polymer (A) as a base polymer. The (meth) acrylic polymer (A) usually contains alkyl (meth) acrylate as a main component as a monomer unit. Further, (meth) acrylate refers to acrylate and / or methacrylate and has the same meaning as (meth) of the present invention.

(메트)아크릴계 폴리머 (A) 의 주골격을 구성하는, 알킬(메트)아크릴레이트로는, 탄소수 1 ∼ 18 의 직사슬형 또는 분기사슬형의 알킬기를 갖는 것을 예시할 수 있다. 예를 들어, 상기 알킬기로는, 메틸기, 에틸기, 프로필기, 이소프로필기, 부틸기, 이소부틸기, 아밀기, 헥실기, 시클로헥실기, 헵틸기, 2-에틸헥실기, 이소옥틸기, 노닐기, 데실기, 이소데실기, 도데실기, 이소미리스틸기, 라우릴기, 트리데실기, 펜타데실기, 헥사데실기, 헵타데실기, 옥타데실기 등을 예시할 수 있다. 이들은 단독으로 혹은 조합하여 사용할 수 있다.Examples of the alkyl (meth) acrylate constituting the main skeleton of the (meth) acrylic polymer (A) include those having a linear or branched alkyl group having 1 to 18 carbon atoms. Examples of the alkyl group include a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, an amyl group, a hexyl group, a cyclohexyl group, a heptyl group, a 2-ethylhexyl group, A heptyl group, a heptyl group, a heptyl group, a heptyl group, a heptyl group, a heptyl group, a heptyl group, a heptyl group, a heptyl group, a heptyl group, These can be used alone or in combination.

상기 알킬(메트)아크릴레이트는, (메트)아크릴계 폴리머 (A) 를 구성하는 전체 모노머 중의 주성분으로 하는 것이다. 여기서, 주성분이란, (메트)아크릴계 폴리머 (A) 를 구성하는 전체 모노머 중, 알킬(메트)아크릴레이트가 80 ∼ 100 중량％ 정도인 것을 말하고, 85 ∼ 99.9 중량％ 정도가 바람직하고, 90 ∼ 99.9 중량％ 정도가 보다 바람직하다.The alkyl (meth) acrylate is a main component in all the monomers constituting the (meth) acrylic polymer (A). Here, the main component means that the alkyl (meth) acrylate is about 80 to 100% by weight, preferably about 85 to 99.9% by weight, more preferably about 90 to 99.9% by weight of the total monomers constituting the (meth) acrylic polymer By weight is more preferable.

상기 (메트)아크릴계 폴리머 (A) 중에는, 접착성이나 내열성의 개선을 목적으로, (메트)아크릴로일기 또는 비닐기 등의 불포화 이중 결합을 갖는 중합성의 관능기를 갖는, 1 종류 이상의 공중합 모노머를 공중합에 의해 도입할 수 있다. 그러한 공중합 모노머의 구체예로는, 예를 들어, (메트)아크릴산2-하이드록시에틸, (메트)아크릴산3-하이드록시프로필, (메트)아크릴산4-하이드록시부틸, (메트)아크릴산6-하이드록시헥실, (메트)아크릴산8-하이드록시옥틸, (메트)아크릴산10-하이드록시데실, (메트)아크릴산12-하이드록시라우릴이나 (4-하이드록시메틸시클로헥실)-메틸아크릴레이트 등의 하이드록실기 함유 모노머 ; (메트)아크릴산, 카르복시에틸(메트)아크릴레이트, 카르복시펜틸(메트)아크릴레이트, 이타콘산, 말레산, 푸마르산, 크로톤산 등의 카르복실기 함유 모노머 ; 무수 말레산, 무수 이타콘산 등의 산무수물기 함유 모노머 ; 아크릴산의 카프로락톤 부가물 ; 스티렌술폰산이나 알릴술폰산, 2-(메트)아크릴아미드-2-메틸프로판술폰산, (메트)아크릴아미드프로판술폰산, 술포프로필(메트)아크릴레이트, (메트)아크릴로일옥시나프탈렌술폰산 등의 술폰산기 함유 모노머 ; 2-하이드록시에틸아크릴로일포스페이트 등의 인산기 함유 모노머 등을 들 수 있다.Among the (meth) acryl-based polymers (A), one or more copolymerizable monomers having a polymerizable functional group having an unsaturated double bond such as a (meth) acryloyl group or a vinyl group are copolymerized for the purpose of improving adhesiveness and heat resistance. . ≪ / RTI > Specific examples of such copolymerizable monomers include, for example, 2-hydroxyethyl (meth) acrylate, 3-hydroxypropyl (meth) acrylate, 4-hydroxybutyl (meth) acrylate, Hydroxydecyl (meth) acrylate, hydrolysates such as 12-hydroxylauryl (meth) acrylate and (4-hydroxymethylcyclohexyl) -methylacrylate, A monomer having a carboxyl group; Carboxyl group-containing monomers such as (meth) acrylic acid, carboxyethyl (meth) acrylate, carboxypentyl (meth) acrylate, itaconic acid, maleic acid, fumaric acid and crotonic acid; Monomers containing acid anhydride groups such as maleic anhydride and itaconic anhydride; Caprolactone adducts of acrylic acid; Containing sulfonic acid group such as styrene sulfonic acid, allyl sulfonic acid, 2- (meth) acrylamide-2-methylpropane sulfonic acid, (meth) acrylamide propane sulfonic acid, sulfopropyl (meth) acrylate, and (meth) acryloyloxynaphthalenesulfonic acid Monomers; And a phosphoric acid group-containing monomer such as 2-hydroxyethyl acryloyl phosphate.

또, (메트)아크릴아미드, N,N-디메틸(메트)아크릴아미드, N-부틸(메트)아크릴아미드나 N-메틸올(메트)아크릴아미드, N-메틸올프로판(메트)아크릴아미드 등의 (N-치환)아미드계 모노머 ; (메트)아크릴산아미노에틸, (메트)아크릴산 N,N-디메틸아미노에틸, (메트)아크릴산t-부틸아미노에틸 등의 (메트)아크릴산알킬아미노알킬계 모노머 ; (메트)아크릴산메톡시에틸, (메트)아크릴산에톡시에틸 등의 (메트)아크릴산알콕시알킬계 모노머 ; N-(메트)아크릴로일옥시메틸렌숙신이미드나 N-(메트)아크릴로일-6-옥시헥사메틸렌숙신이미드, N-(메트)아크릴로일-8-옥시옥타메틸렌숙신이미드, N-아크릴로일모르폴린 등의 숙신이미드계 모노머 ; N-시클로헥실말레이미드나 N-이소프로필말레이미드, N-라우릴말레이미드나 N-페닐말레이미드 등의 말레이미드계 모노머 ; N-메틸이타콘이미드, N-에틸이타콘이미드, N-부틸이타콘이미드, N-옥틸이타콘이미드, N-2-에틸헥실이타콘이미드, N-시클로헥실이타콘이미드, N-라우릴이타콘이미드 등의 이타콘이미드계 모노머 등도 개질 목적의 모노머 예로서 들 수 있다.Examples of the (meth) acrylamide, N, N-dimethyl (meth) acrylamide, N-butyl (meth) acrylamide, N-methylol (meth) acrylamide and N-methylolpropane (N-substituted) amide-based monomers; (Meth) acrylic acid alkylaminoalkyl monomers such as aminoethyl (meth) acrylate, N, N-dimethylaminoethyl (meth) acrylate and t-butylaminoethyl (meth) acrylate; (Meth) acrylic acid alkoxyalkyl monomers such as methoxyethyl (meth) acrylate and ethoxyethyl (meth) acrylate; (Meth) acryloyloxymethylene succinimide, N- (meth) acryloyl-6-oxyhexamethylene succinimide, N- (meth) acryloyl- - succinimide-based monomers such as acryloylmorpholine; Maleimide-based monomers such as N-cyclohexylmaleimide and N-isopropylmaleimide, N-laurylmaleimide and N-phenylmaleimide; N-diisopropylethylenediamine, N-methylethylenediamine, N-methylethylenediamine, N-methylethylenediamine, N-methylethylenediamine, N-methylethylenediamine, And itaconimide-based monomers such as N, N-lauryl itaconimide and the like can also be cited as examples of the monomers for the purpose of modification.

또한, 개질 모노머로서 아세트산비닐, 프로피온산비닐, N-비닐피롤리돈, 메틸비닐피롤리돈, 비닐피리딘, 비닐피페리돈, 비닐피리미딘, 비닐피페라진, 비닐피라진, 비닐피롤, 비닐이미다졸, 비닐옥사졸, 비닐모르폴린, N-비닐카르복실산아미드류, 스티렌, α-메틸스티렌, N-비닐카프로락탐 등의 비닐계 모노머 ; 아크릴로니트릴, 메타크릴로니트릴 등의 시아노아크릴레이트계 모노머 ; (메트)아크릴산글리시딜 등의 에폭시기 함유 아크릴계 모노머 ; (메트)아크릴산폴리에틸렌글리콜, (메트)아크릴산폴리프로필렌글리콜, (메트)아크릴산메톡시에틸렌글리콜, (메트)아크릴산메톡시폴리프로필렌글리콜 등의 글리콜계 아크릴에스테르 모노머 ; (메트)아크릴산테트라하이드로푸르푸릴, 불소(메트)아크릴레이트, 실리콘(메트)아크릴레이트나 2-메톡시에틸아크릴레이트 등의 아크릴산에스테르계 모노머 등도 사용할 수 있다. 나아가서는, 이소프렌, 부타디엔, 이소부틸렌, 비닐에테르 등을 들 수 있다.Examples of the modified monomer include vinyl acetate, vinyl propionate, N-vinyl pyrrolidone, methyl vinyl pyrrolidone, vinyl pyridine, vinyl piperidone, vinyl pyrimidine, vinylpiperazine, vinyl pyrazine, vinyl pyrrole, vinyl imidazole, Vinyl monomers such as vinyl oxazole, vinyl morpholine, N-vinylcarboxylic acid amides, styrene,? -Methylstyrene, and N-vinylcaprolactam; Cyanoacrylate monomers such as acrylonitrile and methacrylonitrile; An epoxy group-containing acrylic monomer such as glycidyl (meth) acrylate; Glycol type acrylic ester monomers such as (meth) acrylic acid polyethylene glycol, (meth) acrylic acid polypropylene glycol, (meth) acrylic acid methoxyethylene glycol and (meth) acrylic acid methoxypolypropylene glycol; Acrylic acid ester monomers such as (meth) acrylate tetrahydrofurfuryl, fluorine (meth) acrylate, silicone (meth) acrylate and 2-methoxyethyl acrylate. Further, isoprene, butadiene, isobutylene, vinyl ether and the like can be mentioned.

또한, 상기 이외의 공중합 가능한 모노머로서, 규소 원자를 함유하는 실란계 모노머 등을 들 수 있다. 실란계 모노머로는, 예를 들어, 3-아크릴옥시프로필트리에톡시실란, 비닐트리메톡시실란, 비닐트리에톡시실란, 4-비닐부틸트리메톡시실란, 4-비닐부틸트리에톡시실란, 8-비닐옥틸트리메톡시실란, 8-비닐옥틸트리에톡시실란, 10-메타크릴로일옥시데실트리메톡시실란, 10-아크릴로일옥시데실트리메톡시실란, 10-메타크릴로일옥시데실트리에톡시실란, 10-아크릴로일옥시데실트리에톡시실란 등을 들 수 있다.Examples of the copolymerizable monomer other than the above include silane-based monomers containing a silicon atom. Examples of the silane-based monomer include 3-acryloxypropyltriethoxysilane, vinyltrimethoxysilane, vinyltriethoxysilane, 4-vinylbutyltrimethoxysilane, 4-vinylbutyltriethoxysilane, Vinyl octyltrimethoxysilane, 8-vinyl octyltrimethoxysilane, 10-methacryloyloxydecyltrimethoxysilane, 10-acryloyloxydecyltrimethoxysilane, 10-methacryloyloxyde Silyltriethoxysilane, 10-acryloyloxydecyltriethoxysilane, and the like.

또, 공중합 모노머로는, 트리프로필렌글리콜디(메트)아크릴레이트, 테트라에틸렌글리콜디(메트)아크릴레이트, 1,6-헥산디올디(메트)아크릴레이트, 비스페놀 A 디글리시딜에테르디(메트)아크릴레이트, 네오펜틸글리콜디(메트)아크릴레이트, 트리메틸올프로판트리(메트)아크릴레이트, 펜타에리트리톨트리(메트)아크릴레이트, 펜타에리트리톨테트라(메트)아크릴레이트, 디펜타에리트리톨펜타(메트)아크릴레이트, 디펜타에리트리톨헥사(메트)아크릴레이트, 카프로락톤 변성 디펜타에리트리톨헥사(메트)아크릴레이트 등의 (메트)아크릴산과 다가 알코올의 에스테르화물 등의 (메트)아크릴로일기, 비닐기 등의 불포화 이중 결합을 2 개 이상 갖는 다관능성 모노머나, 폴리에스테르, 에폭시, 우레탄 등의 골격에 모노머 성분과 동일한 관능기로서 (메트)아크릴로일기, 비닐기 등의 불포화 이중 결합을 2 개 이상 부가한 폴리에스테르(메트)아크릴레이트, 에폭시(메트)아크릴레이트, 우레탄(메트)아크릴레이트 등을 사용할 수도 있다.Examples of the copolymerizable monomer include tripropylene glycol di (meth) acrylate, tetraethylene glycol di (meth) acrylate, 1,6-hexanediol di (meth) acrylate, bisphenol A diglycidyl ether di Acrylate, trimethylolpropane tri (meth) acrylate, pentaerythritol tri (meth) acrylate, pentaerythritol tetra (meth) acrylate, dipentaerythritol penta (Meth) acryloyl groups such as esters of (meth) acrylic acid and polyhydric alcohols such as dipentaerythritol hexa (meth) acrylate, dipentaerythritol hexa (meth) acrylate and caprolactone modified dipentaerythritol hexa A polyfunctional monomer having two or more unsaturated double bonds such as a vinyl group, and a (meth) acrylate as a functional group which is the same as the monomer component in the backbone of polyester, epoxy, As may be used in the group, the vinyl group or the like of two or unsaturated polyester (meth) adding at least a double bond acrylate, epoxy (meth) acrylate, urethane (meth) acrylate and the like.

상기 공중합 모노머의 비율은, 특별히 제한되지 않지만, (메트)아크릴계 폴리머 (A) 를 구성하는 전체 모노머 중, 0 ∼ 20 중량％ 정도이고, 0.1 ∼ 15 중량％ 정도가 바람직하고, 0.1 ∼ 10 중량％ 정도가 보다 바람직하다.The proportion of the copolymerizable monomer is not particularly limited but is preferably from 0 to 20% by weight, preferably from 0.1 to 15% by weight, more preferably from 0.1 to 10% by weight, based on the total monomer constituting the (meth) acrylic polymer (A) Is more preferable.

이들 공중합 모노머 중에서도, 접착성, 내구성 면에서, 하이드록실기 함유 모노머, 카르복실기 함유 모노머가 바람직하게 사용된다. 하이드록실기 함유 모노머 및 카르복실기 함유 모노머는 병용할 수 있다. 이들 공중합 모노머는, 점착제 조성물이 가교제를 함유하는 경우에, 가교제와의 반응점이 된다. 하이드록실기 함유 모노머, 카르복실기 함유 모노머 등은 분자간 가교제와의 반응성이 풍부하기 때문에, 얻어지는 점착제층의 응집성이나 내열성의 향상을 위하여 바람직하게 사용된다.Of these copolymerizable monomers, hydroxyl group-containing monomers and carboxyl group-containing monomers are preferably used from the viewpoint of adhesiveness and durability. The hydroxyl group-containing monomer and the carboxyl group-containing monomer may be used in combination. When the pressure-sensitive adhesive composition contains a crosslinking agent, these copolymerized monomers are reaction points with the crosslinking agent. The hydroxyl group-containing monomer, carboxyl group-containing monomer and the like are preferably used because they are rich in reactivity with an intermolecular crosslinking agent, and thus are excellent in cohesiveness and heat resistance of the resulting pressure-sensitive adhesive layer.

공중합 모노머로서, 하이드록실기 함유 모노머를 함유하는 경우, 그 비율은, 0.01 ∼ 15 중량％ 가 바람직하고, 0.03 ∼ 10 중량％ 가 보다 바람직하고, 나아가서는 0.05 ∼ 7 중량％ 가 바람직하다. 공중합 모노머로서 카르복실기 함유 모노머를 함유하는 경우, 그 비율은, 10 중량％ 이하가 바람직하고, 0.05 ∼ 10 중량％ 가 보다 바람직하고, 0.1 ∼ 8 중량％ 가 더욱 바람직하고, 0.2 ∼ 6 중량％ 가 특히 바람직하다.When the copolymerizable monomer contains a hydroxyl group-containing monomer, the proportion thereof is preferably 0.01 to 15% by weight, more preferably 0.03 to 10% by weight, further preferably 0.05 to 7% by weight. When the monomer containing a carboxyl group is contained as the copolymerizable monomer, the proportion thereof is preferably 10% by weight or less, more preferably 0.05 to 10% by weight, still more preferably 0.1 to 8% by weight, particularly preferably 0.2 to 6% desirable.

본 발명의 (메트)아크릴계 폴리머 (A) 는, 통상적으로 중량 평균 분자량이 50 만 ∼ 300 만의 범위의 것이 사용된다. 내구성, 특히 내열성을 고려하면, 중량 평균 분자량은 70 만 ∼ 270 만인 것을 사용하는 것이 바람직하다. 나아가서는 80 만 ∼ 250 만인 것이 바람직하다. 중량 평균 분자량이 50 만보다 작으면 내열성 면에서 바람직하지 않다. 또, 중량 평균 분자량이 300 만보다 커지면, 도공하기 위한 점도로 조정하기 위하여 다량의 희석 용제가 필요해져, 비용 상승되는 점에서 바람직하지 않다. 또한, 중량 평균 분자량은, GPC (겔·퍼미에이션·크로마토그래피) 에 의해 측정하고, 폴리스티렌 환산에 의해 산출된 값을 말한다.The (meth) acryl-based polymer (A) of the present invention usually has a weight average molecular weight in the range of 500,000 to 3,000,000. Considering durability, particularly heat resistance, it is preferable to use one having a weight average molecular weight of 700,000 to 270,000. More preferably from 800,000 to 2.5 million. If the weight average molecular weight is less than 500,000, it is not preferable from the viewpoint of heat resistance. On the other hand, if the weight average molecular weight is greater than 3,000,000, a large amount of a diluting solvent is required to adjust the viscosity for coating, which is not preferable in view of an increase in cost. The weight average molecular weight refers to a value measured by GPC (Gel Permeation Chromatography) and calculated by polystyrene conversion.

이와 같은 (메트)아크릴계 폴리머 (A) 의 제조는, 용액 중합, 괴상 중합, 유화 중합, 각종 라디칼 중합 등의 공지된 제조 방법을 적당히 선택할 수 있다. 또, 얻어지는 (메트)아크릴계 폴리머 (A) 는, 랜덤 공중합체, 블록 공중합체, 그래프트 공중합체 등 어느 것이어도 된다.Such (meth) acrylic polymer (A) can be appropriately selected from known production methods such as solution polymerization, bulk polymerization, emulsion polymerization and various radical polymerization. The (meth) acryl-based polymer (A) to be obtained may be any of a random copolymer, a block copolymer and a graft copolymer.

또한, 용액 중합에 있어서는, 중합 용매로서 예를 들어, 아세트산에틸, 톨루엔 등이 사용된다. 구체적인 용액 중합예로는, 반응은 질소 등의 불활성 가스 기류하에서, 중합 개시제를 첨가하고, 통상적으로 50 ∼ 70 ℃ 정도에서, 5 ∼ 30 시간 정도의 반응 조건에서 실시된다.In the solution polymerization, for example, ethyl acetate, toluene and the like are used as polymerization solvents. As a specific example of the solution polymerization, the reaction is carried out under the reaction conditions of about 50 to 70 ° C and for about 5 to 30 hours by adding a polymerization initiator under an inert gas flow such as nitrogen.

라디칼 중합에 사용되는 중합 개시제, 연쇄 이동제, 유화제 등은 특별히 한정되지 않고 적당히 선택하여 사용할 수 있다. 또한, (메트)아크릴계 폴리머 (A) 의 중량 평균 분자량은, 중합 개시제, 연쇄 이동제의 사용량, 반응 조건에 의해 제어 가능하고, 이들의 종류에 따라 적당히 그 사용량이 조정된다.The polymerization initiator, chain transfer agent, and emulsifier used in the radical polymerization are not particularly limited and can be appropriately selected and used. The weight average molecular weight of the (meth) acryl-based polymer (A) can be controlled by the amount of the polymerization initiator, the amount of the chain transfer agent, and the reaction conditions, and the amount thereof is appropriately adjusted depending on the kind thereof.

중합 개시제로는, 예를 들어, 2,2'-아조비스이소부티로니트릴, 2,2'-아조비스(2-아미디노프로판)디하이드로클로라이드, 2,2'-아조비스[2-(5-메틸-2-이미다졸린-2-일)프로판]디하이드로클로라이드, 2,2'-아조비스(2-메틸프로피온아미딘)이황산염, 2,2'-아조비스(N,N'-디메틸렌이소부틸아미딘), 2,2'-아조비스[N-(2-카르복시에틸)-2-메틸프로피온아미딘]하이드레이트 (상품명 : VA-057, 와코 순약 공업 (주) 제조) 등의 아조계 개시제, 과황산칼륨, 과황산암모늄 등의 과황산염, 디(2-에틸헥실)퍼옥시디카보네이트, 디(4-t-부틸시클로헥실)퍼옥시디카보네이트, 디-sec-부틸퍼옥시디카보네이트, t-부틸퍼옥시네오데카노에이트, t-헥실퍼옥시피발레이트, t-부틸퍼옥시피발레이트, 디라우로일퍼옥사이드, 디-n-옥타노일퍼옥사이드, 1,1,3,3-테트라메틸부틸퍼옥시-2-에틸헥사노에이트, 디(4-메틸벤조일)퍼옥사이드, 디벤조일퍼옥사이드, t-부틸퍼옥시이소부틸레이트, 1,1-디(t-헥실퍼옥시)시클로헥산, t-부틸하이드로퍼옥사이드, 과산화수소 등의 과산화물계 개시제, 과황산염과 아황산수소나트륨의 조합, 과산화물과 아스코르브산나트륨의 조합 등의 과산화물과 환원제를 조합한 레독스계 개시제 등을 들 수 있는데, 이들에 한정되는 것은 아니다.Examples of the polymerization initiator include azo compounds such as 2,2'-azobisisobutyronitrile, 2,2'-azobis (2-amidinopropane) dihydrochloride, 2,2'-azobis [2- Azobis (N, N ', N'-tetramethyluronium tetrafluoroborate), 2,2'-azobis Azobis [N- (2-carboxyethyl) -2-methylpropionamidine] hydrate (trade name: VA-057, manufactured by Wako Pure Chemical Industries, Ltd.) (2-ethylhexyl) peroxydicarbonate, di (4-t-butylcyclohexyl) peroxydicarbonate, di-sec-butylperoxydicarbonate t-butyl peroxyneodecanoate, t-hexyl peroxy pivalate, t-butyl peroxy pivalate, dilauryl peroxide, di-n-octanoyl peroxide, 1,1,3,3- Tetramethylbutyl peroxy-2-ethyl hexanoate, Peroxide such as di (4-methylbenzoyl) peroxide, dibenzoyl peroxide, t-butyl peroxyisobutyrate, 1,1-di (t-hexylperoxy) cyclohexane, A system initiator, a combination of persulfate and sodium hydrogen sulfite, a redox initiator combined with a peroxide such as a combination of peroxide and sodium ascorbate, and a reducing agent, but the present invention is not limited thereto.

상기 중합 개시제는, 단독으로 사용해도 되고, 또 2 종 이상을 혼합하여 사용해도 되지만, 전체로서의 함유량은 모노머 100 중량부에 대해, 0.005 ∼ 1 중량부 정도인 것이 바람직하고, 0.02 ∼ 0.5 중량부 정도인 것이 보다 바람직하다.The polymerization initiator may be used alone or in admixture of two or more. The content of the polymerization initiator is preferably about 0.005 to 1 part by weight, more preferably about 0.02 to 0.5 part by weight per 100 parts by weight of the monomer Is more preferable.

또한, 중합 개시제로서 예를 들어, 2,2'-아조비스이소부티로니트릴을 사용하여, 상기 중량 평균 분자량의 (메트)아크릴계 폴리머 (A) 를 제조하려면, 중합 개시제의 사용량은, 모노머 성분의 전체량 100 중량부에 대해, 0.06 ∼ 0.2 중량부 정도로 하는 것이 바람직하고, 0.08 ∼ 0.175 중량부 정도로 하는 것이 보다 바람직하다.In order to produce the (meth) acrylic polymer (A) having a weight average molecular weight by using, for example, 2,2'-azobisisobutyronitrile as the polymerization initiator, the amount of the polymerization initiator used is preferably It is preferably about 0.06 to 0.2 part by weight, more preferably about 0.08 to 0.175 part by weight based on 100 parts by weight of the total amount.

또, 연쇄 이동제, 유화제등은, 종래 공지된 것을 적당히 사용할 수 있다. 그들의 첨가량에 대해서도, 본 발명의 효과를 저해하지 않는 범위에서 적당히 결정할 수 있다.As the chain transfer agent, the emulsifier, etc., conventionally known ones can be suitably used. The addition amount thereof can also be suitably determined within a range that does not impair the effect of the present invention.

(2) 오늄-아니온염 (B1)(2) Onium-Anionite (B1)

상기 오늄-아니온염 (B1) 은「이온성 화합물」에 관련된 것으로서, 이온성 액체, 이온성 고체라고도 불린다. 상기 오늄-아니온염 (B1) 은, 카티온 성분과 아니온 성분으로 구성되어 있는 카티온-아니온염에 관련된 것이다. 본 발명에서는 당해 카티온-아니온염 중에서도, 카티온이 오늄인 오늄-아니온염을 사용한다.The onium-anionite (B1) relates to an "ionic compound" and is also referred to as an ionic liquid or an ionic solid. The onium-anionite (B1) relates to a cation-anionite composed of a cation component and an anion component. Among the cation-anion salts, onium-anionite, which is cationic onium, is used in the present invention.

＜아니온 성분＞≪ Anion component >

아니온 성분으로는, 예를 들어, Cl-, Br-, I-, AlCl4 -, Al2Cl7 -, BF4 -, PF6 -, ClO4 -, NO3 -, CH3COO-, CF3COO-, CH3SO3 -, CF3SO3 -, (CF3SO2)3C-, AsF6 -, SbF6 -, NbF6 -, TaF6 -, (CN)2N-, C4F9SO3 -, C3F7COO-, (CF3SO2)(CF3CO)N-, -O3S(CF2)3SO3 - 나 하기 일반식 (1) ∼ (4), Examples of the anion component include, for example, Cl - , Br - , I - , AlCl 4 - , Al 2 Cl 7 - , BF 4 - , PF 6 - , ClO 4 - , NO 3 - , CH 3 COO - CF 3 COO -, CH 3 SO 3 -, CF 3 SO 3 -, (CF 3 SO 2) 3 C -, AsF 6 -, SbF 6 -, NbF 6 -, TaF 6 -, (CN) 2 N -, C 4 F 9 SO 3 -, C 3 F 7 COO -, (CF 3 SO 2) (CF 3 CO) N -, - O 3 S (CF 2) 3 SO 3 - or the following general formulas (1) - ( 4),

(1) : (CnF2n＋1SO2)2N- (단, n 은 1 ∼ 10 의 정수 (整數)), (1): (C n F 2n + 1 SO 2 ) 2 N - (wherein n is an integer of 1 to 10)

(2) : CF2(CmF2mSO2)2N- (단, m 은 1 ∼ 10 의 정수), (2): CF 2 (C m F 2 m SO 2 ) 2 N - wherein m is an integer of 1 to 10,

(3) : -O3S(CF2)lSO3 - (단, l 은 1 ∼ 10 의 정수), (3): - O 3 S (CF 2 ) 1 SO 3 - (wherein 1 is an integer of 1 to 10),

(4) : (CpF2p＋1SO2)N-(CqF2q＋1SO2), (단, p, q 는 1 ∼ 10 의 정수) 로 나타내는 것 등이 사용된다. 그 중에서도 특히, 불소 원자를 함유하는 아니온 성분은, 이온 해리성이 양호한 이온 화합물이 얻어지는 점에서 바람직하게 사용된다. 특히, 아니온 성분은, 불소 함유 이미드 아니온이 바람직하다.(4): ???????? (C p F 2p + 1 SO 2 ) N - (C q F 2q + 1 SO 2 ) (where p and q are integers of 1 to 10) Particularly, the anion component containing a fluorine atom is preferably used because an ionic compound having good ion dissociability can be obtained. Particularly, the anion component is preferably a fluorine-containing imide anion.

≪불소 함유 이미드 아니온≫«Fluoride-containing imide anion»

상기 불소 함유 이미드 아니온으로는, 예를 들어, 퍼플루오로알킬기를 갖는 이미드 아니온을 예시할 수 있다.As the fluorine-containing imide anion, for example, an imide anion having a perfluoroalkyl group can be exemplified.

구체적으로는, 상기 예시의 아니온 성분 중의, (CF3SO2)(CF3CO)N- 나 상기 일반식 (1), (2), (4), Specifically, (CF 3 SO 2 ) (CF 3 CO) N - in the anion component of the above example, the compounds represented by the general formulas (1), (2), (4)

(1) : (CnF2n＋1SO2)2N- (단, n 은 1 ∼ 10 의 정수), (1): ???????? (C n F 2n + 1 SO 2 ) 2 N - wherein n is an integer of 1 to 10,

(2) : CF2(CmF2mSO2)2N- (단, m 은 1 ∼ 10 의 정수), (2): CF 2 (C m F 2 m SO 2 ) 2 N - wherein m is an integer of 1 to 10,

(4) : (CpF2p＋1SO2)N-(CqF2q＋1SO2), (단, p, q 는 1 ∼ 10 의 정수) 로 나타내는 것 등이 사용된다. 이들 불소 함유 이미드 아니온은, 이온 해리성이 양호한 이온성 화합물이 얻어짐으로써 바람직하게 사용된다. 또, 상기 불소 함유 이미드 아니온은, 탄소수 1 ∼ 4 의 불화알킬기 또는 불화알킬렌기를 갖는 것이, 표면 저항값을 작게 제어할 수 있고 정전기 불균일을 억제하는 데에 있어서 바람직하다. 상기 불소 함유 이미드 아니온으로는, (CF3SO2)2N-, (C2F5SO2)2N- 등의 상기 일반식 (1) 로 나타내는 (퍼플루오로알킬술포닐)이미드가 바람직하고, 특히 (CF3SO2)2N- 로 나타내는 (트리플루오로메탄술포닐)이미드가 바람직하다.(4): ???????? (C p F 2p + 1 SO 2 ) N - (C q F 2q + 1 SO 2 ) (where p and q are integers of 1 to 10) These fluorine-containing imide anions are preferably used because ionic compounds having good ion dissociability are obtained. The fluorine-containing imide anion is preferably a fluorine-containing alkyl group or fluoroalkylene group having 1 to 4 carbon atoms in order to control the surface resistance value to a small value and to suppress static unevenness. The imide anion containing the fluorine, (CF 3 SO 2) 2 N -, (C 2 F 5 SO 2) 2 N - wherein the formula (1) represents an (alkyl-sulfonyl perfluoroalkyl) as such already (Trifluoromethanesulfonyl) imide represented by (CF 3 SO 2 ) 2 N - is particularly preferable.

＜오늄＞ <Onium>

상기 오늄-아니온염 (B1) 에 있어서의 카티온부를 구성하는 오늄으로는, 오늄 이온이 되는 원자가 프로톤화된 것이다. 또, 본 발명의 오늄은, 이중 결합, 삼중 결합 등의 불포화 결합에 의해 오늄염을 형성하고 있지 않은 것이 바람직하다. 즉, 본 발명의 오늄으로는, 유기기 등에 의한 치환에 의해 오늄 이온을 형성한 유기 오늄이 바람직하다.As the onium constituting the cation portion of the onium-anionite (B1), the atom which becomes the onium ion is protonated. It is preferable that the onium of the present invention does not form an onium salt by an unsaturated bond such as a double bond or a triple bond. That is, as the onium of the present invention, organic onium in which an onium ion is formed by substitution with an organic group is preferable.

또, 상기 유기 오늄에 있어서의 유기기로는, 알킬기, 알콕시기, 알케닐기 등을 예시할 수 있다. 이들 중에서도, 불포화 결합을 갖지 않는 것이 바람직하다. 알킬기의 탄소수는 예를 들어, 1 ∼ 12 에서 선택할 수 있지만, 바람직하게는 1 ∼ 8 이고, 더욱 바람직하게는 1 ∼ 4 이다. 유기 오늄으로는, 모든 치환기가, 탄소수 1 ∼ 4 의 알킬기를 갖는 알킬오늄인 것이 바람직하다. 알킬기는 직사슬 또는 분기사슬을 사용할 수 있는데, 직사슬이 바람직하다. 또, 유기 오늄이 고리형 구조를 갖는 경우에는, 오늄이 5 원자 고리 혹은 6 원자 고리를 갖고, 그 밖의 치환기가, 탄소수 1 ∼ 4 의 알킬기인 것이 바람직하다.Examples of the organic group in the organic onium include an alkyl group, an alkoxy group, and an alkenyl group. Of these, those having no unsaturated bond are preferable. The number of carbon atoms of the alkyl group can be selected, for example, from 1 to 12, but is preferably 1 to 8, and more preferably 1 to 4. As the organic onium, it is preferable that all the substituents are alkylonium having an alkyl group having 1 to 4 carbon atoms. The alkyl group may be a linear or branched chain, preferably a linear chain. When the organic onium has a cyclic structure, it is preferable that the onium has a five-membered ring or a six-membered ring and the other substituent is an alkyl group having 1 to 4 carbon atoms.

상기 오늄으로는, 특별히 제한은 없지만, 예를 들어, 함질소오늄, 함황오늄, 함인오늄 등을 들 수 있다. 이들 중에서도 함질소오늄, 함황오늄이 바람직하다.The onium is not particularly limited, and examples thereof include nitrogen nitrogen, ammonium fluoride, and phosphorus atom. Of these, onium nitrogen and ammonium iron are preferable.

함질소오늄으로는, 암모늄 카티온, 피페리디늄 카티온, 피롤리디늄 카티온, 피리디늄 카티온, 피롤린 골격을 갖는 카티온, 피롤 골격을 갖는 카티온, 이미다졸륨 카티온, 테트라하이드로피리미디늄 카티온, 디하이드로피리미디늄 카티온, 피라졸륨 카티온, 피라졸리늄 카티온 등을 들 수 있다. 이들 중에서도, 암모늄 카티온, 피페리디늄 카티온, 피롤리디늄 카티온이 바람직하고, 특히, 피롤리디늄이 바람직하다. 구체적인 함질소오늄으로는, 테트라알킬암모늄 카티온, 알킬피페리디늄 카티온, 알킬피롤리디늄 카티온이 바람직하다.Examples of the nitrogen-containing onium include ammonium cation, piperidinium cation, pyrrolidinium cation, pyridinium cation, cation having pyrroline skeleton, cation having pyrrole skeleton, imidazolium cation, Pyrimidinium cation, dihydropyrimidinium cation, pyrazolium cation, pyrazolinium cation, and the like. Among them, ammonium cation, piperidinium cation and pyrrolidinium cation are preferable, and pyrrolidinium is particularly preferable. Specific examples of the nitrogen-containing onium atom include tetraalkylammonium cation, alkylpiperidinium cation, and alkylpyrrolidinium cation.

함황오늄으로는, 술포늄 카티온 등을 들 수 있다. 또 함인오늄으로는, 포스포늄 카티온 등을 들 수 있다.Examples of ammonium fluoride include sulfonium cation and the like. As phosphonium onium, phosphonium cation and the like can be mentioned.

상기 오늄-아니온염 (B1) 은, 상기 오늄 성분과 아니온 성분의 조합으로 이루어지는 화합물이 적당히 선택되어 사용된다. 본 발명에서는, 당해 오늄-아니온염 (B1) 중에서도, 아니온이 불소 함유 이미드 아니온인, 오늄-불소 함유 이미드 아니온염이 바람직하다.As the onium-anionite (B1), a compound comprising a combination of the onium component and the anion component is suitably selected and used. In the present invention, among the onium-anionite (B1), an onium-fluorine-containing imide anionite, in which anion is a fluorine-containing imide anion, is preferable.

오늄-불소 함유 이미드 아니온염의 구체예로는, 상기 오늄 성분과 불소 함유 이미드 아니온 성분의 조합으로 이루어지는 화합물이 적당히 선택되어 사용되고, 함질소오늄염, 함황오늄염 및 함인오늄염에서 선택되는 어느 적어도 1 종이 바람직하게 사용된다. 나아가서는, 암모늄염, 피롤리디늄염, 피페리디늄염 및 술포늄염에서 선택되는 어느 적어도 1 종이 바람직하게 사용된다.Concrete examples of the onium-fluorine-containing imide anion salts include those selected from the group consisting of a combination of the onium component and the fluorine-containing imide anion component selected from nitrogen-containing onium salts, ammonium fluoride salts and boron-onium salts Is preferably used. Further, at least one species selected from ammonium salts, pyrrolidinium salts, piperidinium salts and sulfonium salts is preferably used.

예를 들어, 1-부틸-3-메틸피리디늄비스(트리플루오로메탄술포닐)이미드, 1-부틸-3-메틸피리디늄비스(펜타플루오로에탄술포닐)이미드, 1-에틸-3-메틸이미다졸륨비스(트리플루오로메탄술포닐)이미드, 1-에틸-3-메틸이미다졸륨비스(펜타플루오로에탄술포닐)이미드, 1-부틸-3-메틸이미다졸륨비스(트리플루오로메탄술포닐)이미드, 1,2-디메틸-3-프로필이미다졸륨비스(트리플루오로메탄술포닐)이미드, 테트라헥실암모늄비스(트리플루오로메탄술포닐)이미드, 디알릴디메틸암모늄비스(트리플루오로메탄술포닐)이미드, 디알릴디메틸암모늄비스(펜타플루오로에탄술포닐)이미드, N,N-디에틸-N-메틸-N-(2-메톡시에틸)암모늄비스(트리플루오로메탄술포닐)이미드, N,N-디에틸-N-메틸-N-(2-메톡시에틸)암모늄비스(펜타플루오로에탄술포닐)이미드, 글리시딜트리메틸암모늄비스(트리플루오로메탄술포닐)이미드, 글리시딜트리메틸암모늄비스(펜타플루오로에탄술포닐)이미드, N,N-디메틸-N-에틸-N-프로필암모늄비스(트리플루오로메탄술포닐)이미드, N,N-디메틸-N-에틸-N-부틸암모늄비스(트리플루오로메탄술포닐)이미드, N,N-디메틸-N-에틸-N-펜틸암모늄비스(트리플루오로메탄술포닐)이미드, N,N-디메틸-N-에틸-N-헥실암모늄비스(트리플루오로메탄술포닐)이미드, N,N-디메틸-N-에틸-N-헵틸암모늄비스(트리플루오로메탄술포닐)이미드, N,N-디메틸-N-에틸-N-노닐암모늄비스(트리플루오로메탄술포닐)이미드, N,N-디메틸-N,N-디프로필암모늄비스(트리플루오로메탄술포닐)이미드, N,N-디메틸-N-프로필-N-부틸암모늄비스(트리플루오로메탄술포닐)이미드, N,N-디메틸-N-프로필-N-펜틸암모늄비스(트리플루오로메탄술포닐)이미드, N,N-디메틸-N-프로필-N-헥실암모늄비스(트리플루오로메탄술포닐)이미드, N,N-디메틸-N-프로필-N-헵틸암모늄비스(트리플루오로메탄술포닐)이미드, N,N-디메틸-N-부틸-N-헥실암모늄비스(트리플루오로메탄술포닐)이미드, N,N-디메틸-N-부틸-N-헵틸암모늄비스(트리플루오로메탄술포닐)이미드, N,N-디메틸-N-펜틸-N-헥실암모늄비스(트리플루오로메탄술포닐)이미드, N,N-디메틸-N,N-디헥실암모늄비스(트리플루오로메탄술포닐)이미드, 트리메틸헵틸암모늄비스(트리플루오로메탄술포닐)이미드, N,N-디에틸-N-메틸-N-프로필암모늄비스(트리플루오로메탄술포닐)이미드, N,N-디에틸-N-메틸-N-펜틸암모늄비스(트리플루오로메탄술포닐)이미드, N,N-디에틸-N-메틸-N-헵틸암모늄비스(트리플루오로메탄술포닐)이미드, N,N-디에틸-N-프로필-N-펜틸암모늄비스(트리플루오로메탄술포닐)이미드, 트리에틸프로필암모늄비스(트리플루오로메탄술포닐)이미드, 트리에틸펜틸암모늄비스(트리플루오로메탄술포닐)이미드, 트리에틸헵틸암모늄비스(트리플루오로메탄술포닐)이미드, N,N-디프로필-N-메틸-N-에틸암모늄비스(트리플루오로메탄술포닐)이미드, N,N-디프로필-N-메틸-N-펜틸암모늄비스(트리플루오로메탄술포닐)이미드, N,N-디프로필-N-부틸-N-헥실암모늄비스(트리플루오로메탄술포닐)이미드, N,N-디프로필-N,N-디헥실암모늄비스(트리플루오로메탄술포닐)이미드, N,N-디부틸-N-메틸-N-펜틸암모늄비스(트리플루오로메탄술포닐)이미드, N,N-디부틸-N-메틸-N-헥실암모늄비스(트리플루오로메탄술포닐)이미드, 트리옥틸메틸암모늄비스(트리플루오로메탄술포닐)이미드, N-메틸-N-에틸-N-프로필-N-펜틸암모늄비스(트리플루오로메탄술포닐)이미드 등을 들 수 있다. 이들의 시판품으로서 예를 들어,「CIL-314」 (니혼 칼릿 (주) 제조),「ILA2-1」 (코에이 화학 공업 (주) 제조) 등이 사용 가능하다.For example, 1-butyl-3-methylpyridinium bis (trifluoromethanesulfonyl) imide, 1-butyl-3-methylpyridinium bis (pentafluoroethanesulfonyl) 3-methylimidazolium bis (trifluoromethanesulfonyl) imide, 1-ethyl-3-methylimidazolium bis (pentafluoroethanesulfonyl) imide, 1-butyl- Bis (trifluoromethanesulfonyl) imide, 1,2-dimethyl-3-propylimidazolium bis (trifluoromethanesulfonyl) imide, tetrahexylammonium bis (trifluoromethanesulfonyl) imide , Diallyldimethylammonium bis (trifluoromethanesulfonyl) imide, diallyldimethylammonium bis (pentafluoroethanesulfonyl) imide, N, N-diethyl-N-methyl- N, N-diethyl-N-methyl-N- (2-methoxyethyl) ammonium bis (pentafluoroethanesulfonyl) imide, glycidyl Cidyltrimethylammonium N, N-dimethyl-N-ethyl-N-propylammonium bis (trifluoromethanesulfonyl) imide, glycidyltrimethylammonium bis (pentafluoroethanesulfonyl) imide, (Trifluoromethanesulfonyl) imide, N, N-dimethyl-N-ethyl-N-pentylammonium bis (trifluoromethylsulfonyl) imide, N-dimethyl-N-ethyl-N-heptylammonium bis (trifluoromethanesulfonyl) imide, N, N-dimethyl- N, N-dimethyl-N-diphenylammonium bis (trifluoromethanesulfonyl) imide, N, N-dimethyl- (Trifluoromethanesulfonyl) imide, N, N-dimethyl-N-propyl-N-butylammonium bis (trifluoromethanesulfonyl) Bis (trifluoromethanesulfonyl) imide, N, N-dimethyl-N-propyl- N, N-dimethyl-N-heptylammonium bis (trifluoromethanesulfonyl) imide, N, N-dimethyl- N, N-dimethyl-N-butyl-N-heptylammonium bis (trifluoromethanesulfonyl) imide, N, N-dimethyl- (Trifluoromethanesulfonyl) imide, N, N-dimethyl-N, N-dihexylammonium bis (trifluoromethanesulfonyl) imide, trimethylheptylammonium bis N, N-diethyl-N-methyl-N-propylammonium bis (trifluoromethanesulfonyl) imide, N, Bis (trifluoromethanesulfonyl) imide, N, N-diethyl-N-methyl-N-heptylammonium bis (trifluoromethanesulfonyl) N-pentylammonium bis (trifluoromethanesulfonyl) imide, triethylpropyl (Trifluoromethanesulfonyl) imide, triethylpentylammonium bis (trifluoromethanesulfonyl) imide, triethylheptylammonium bis (trifluoromethanesulfonyl) imide, N, N-di Propyl-N-methyl-N-pentylammonium bis (trifluoromethanesulfonyl) imide, N, N-dipropyl- , N, N-dipropyl-N-butyl-N-hexylammonium bis (trifluoromethanesulfonyl) imide, N, N-dipropyl-N, N-dihexylammonium bis (trifluoromethanesulfonyl) (N, N-dibutyl-N-methyl-N-pentylammonium bis (trifluoromethanesulfonyl) imide, (Trifluoromethanesulfonyl) imide, N-methyl-N-ethyl-N-propyl-N-pentylammonium bis (trifluoromethanesulfonyl) imide and the like . As commercially available products thereof, for example, "CIL-314" (manufactured by Nippon Carboxyl Co., Ltd.) and "ILA2-1" (manufactured by Koei Chemical Industry Co., Ltd.) can be used.

또, 예를 들어, 테트라메틸암모늄비스(트리플루오로메탄술포닐)이미드, 트리메틸에틸암모늄비스(트리플루오로메탄술포닐)이미드, 트리메틸부틸암모늄비스(트리플루오로메탄술포닐)이미드, 트리메틸펜틸암모늄비스(트리플루오로메탄술포닐)이미드, 트리메틸헵틸암모늄비스(트리플루오로메탄술포닐)이미드, 트리메틸옥틸암모늄비스(트리플루오로메탄술포닐)이미드, 테트라에틸암모늄비스(트리플루오로메탄술포닐)이미드, 트리에틸부틸암모늄비스(트리플루오로메탄술포닐)이미드, 테트라부틸암모늄비스(트리플루오로메탄술포닐)이미드, 테트라헥실암모늄비스(트리플루오로메탄술포닐)이미드 등을 들 수 있다.Further, for example, there may be mentioned tetramethylammonium bis (trifluoromethanesulfonyl) imide, trimethylethylammonium bis (trifluoromethanesulfonyl) imide, trimethylbutylammonium bis (trifluoromethanesulfonyl) imide , Trimethylpentylammonium bis (trifluoromethanesulfonyl) imide, trimethylheptylammonium bis (trifluoromethanesulfonyl) imide, trimethyloctylammonium bis (trifluoromethanesulfonyl) imide, tetraethylammonium bis (Trifluoromethanesulfonyl) imide, triethylbenzylammonium bis (trifluoromethanesulfonyl) imide, tetrabutylammonium bis (trifluoromethanesulfonyl) imide, tetrahexylammonium bis (trifluoro Methanesulfonyl) imide, and the like.

또, 예를 들어, 1-디메틸피롤리디늄비스(트리플루오로메탄술포닐)이미드, 1-메틸-1-에틸피롤리디늄비스(트리플루오로메탄술포닐)이미드, 1-메틸-1-프로필피롤리디늄비스(트리플루오로메탄술포닐)이미드, 1-메틸-1-부틸피롤리디늄비스(트리플루오로메탄술포닐)이미드, 1-메틸-1-펜틸피롤리디늄비스(트리플루오로메탄술포닐)이미드, 1-메틸-1-헥실피롤리디늄비스(트리플루오로메탄술포닐)이미드, 1-메틸-1-헵틸피롤리디늄비스(트리플루오로메탄술포닐)이미드, 1-에틸-1-프로필피롤리디늄비스(트리플루오로메탄술포닐)이미드, 1-에틸-1-부틸피롤리디늄비스(트리플루오로메탄술포닐)이미드, 1-에틸-1-펜틸피롤리디늄비스(트리플루오로메탄술포닐)이미드, 1-에틸-1-헥실피롤리디늄비스(트리플루오로메탄술포닐)이미드, 1-에틸-1-헵틸피롤리디늄비스(트리플루오로메탄술포닐)이미드, 1,1-디프로필피롤리디늄비스(트리플루오로메탄술포닐)이미드, 1-프로필-1-부틸피롤리디늄비스(트리플루오로메탄술포닐)이미드, 1,1-디부틸피롤리디늄비스(트리플루오로메탄술포닐)이미드, 1-프로필피페리디늄비스(트리플루오로메탄술포닐)이미드, 1-펜틸피페리디늄비스(트리플루오로메탄술포닐)이미드, 1,1-디메틸피페리디늄비스(트리플루오로메탄술포닐)이미드, 1-메틸-1-에틸피페리디늄비스(트리플루오로메탄술포닐)이미드, 1-메틸-1-프로필피페리디늄비스(트리플루오로메탄술포닐)이미드, 1-메틸-1-부틸피페리디늄비스(트리플루오로메탄술포닐)이미드, 1-메틸-1-펜틸피페리디늄비스(트리플루오로메탄술포닐)이미드, 1-메틸-1-헥실피페리디늄비스(트리플루오로메탄술포닐)이미드, 1-메틸-1-헵틸피페리디늄비스(트리플루오로메탄술포닐)이미드, 1-에틸-1-프로필피페리디늄비스(트리플루오로메탄술포닐)이미드, 1-에틸-1-부틸피페리디늄비스(트리플루오로메탄술포닐)이미드, 1-에틸-1-펜틸피페리디늄비스(트리플루오로메탄술포닐)이미드, 1-에틸-1-헥실피페리디늄비스(트리플루오로메탄술포닐)이미드, 1-에틸-1-헵틸피페리디늄비스(트리플루오로메탄술포닐)이미드, 1,1-디프로필피페리디늄비스(트리플루오로메탄술포닐)이미드, 1-프로필-1-부틸피페리디늄비스(트리플루오로메탄술포닐)이미드, 1,1-디부틸피페리디늄비스(트리플루오로메탄술포닐)이미드, 1,1-디메틸피롤리디늄비스(펜타플루오로에탄술포닐)이미드, 1-메틸-1-에틸피롤리디늄비스(펜타플루오로에탄술포닐)이미드, 1-메틸-1-프로필피롤리디늄비스(펜타플루오로에탄술포닐)이미드, 1-메틸-1-부틸피롤리디늄비스(펜타플루오로에탄술포닐)이미드, 1-메틸-1-펜틸피롤리디늄비스(펜타플루오로에탄술포닐)이미드, 1-메틸-1-헥실피롤리디늄비스(펜타플루오로에탄술포닐)이미드, 1-메틸-1-헵틸피롤리디늄비스(펜타플루오로에탄술포닐)이미드, 1-에틸-1-프로필피롤리디늄비스(펜타플루오로에탄술포닐)이미드, 1-에틸-1-부틸피롤리디늄비스(펜타플루오로에탄술포닐)이미드, 1-에틸-1-펜틸피롤리디늄비스(펜타플루오로에탄술포닐)이미드, 1-에틸-1-헥실피롤리디늄비스(펜타플루오로에탄술포닐)이미드, 1-에틸-1-헵틸피롤리디늄비스(펜타플루오로에탄술포닐)이미드, 1,1-디프로필피롤리디늄비스(펜타플루오로에탄술포닐)이미드, 1-프로필-1-부틸피롤리디늄비스(펜타플루오로에탄술포닐)이미드, 1,1-디부틸피롤리디늄비스(펜타플루오로에탄술포닐)이미드, 1-프로필피페리디늄비스(펜타플루오로에탄술포닐)이미드, 1-펜틸피페리디늄비스(펜타플루오로에탄술포닐)이미드, 1,1-디메틸피페리디늄비스(펜타플루오로에탄술포닐)이미드, 1-메틸-1-에틸피페리디늄비스(펜타플루오로에탄술포닐)이미드, 1-메틸-1-프로필피페리디늄비스(펜타플루오로에탄술포닐)이미드, 1-메틸-1-부틸피페리디늄비스(펜타플루오로에탄술포닐)이미드, 1-메틸-1-펜틸피페리디늄비스(펜타플루오로에탄술포닐)이미드, 1-메틸-1-헥실피페리디늄비스(펜타플루오로에탄술포닐)이미드, 1-메틸-1-헵틸피페리디늄비스(펜타플루오로에탄술포닐)이미드, 1-에틸-1-프로필피페리디늄비스(펜타플루오로에탄술포닐)이미드, 1-에틸-1-헵틸피페리디늄비스(펜타플루오로에탄술포닐)이미드, 1-에틸-1-펜틸피페리디늄비스(펜타플루오로에탄술포닐)이미드, 1-에틸-1-헥실피페리디늄비스(펜타플루오로에탄술포닐)이미드, 1-에틸-1-헵틸피페리디늄비스(펜타플루오로에탄술포닐)이미드, 1-프로필-1-부틸피페리디늄비스(펜타플루오로에탄술포닐)이미드, 1,1-디프로필피페리디늄비스(펜타플루오로에탄술포닐)이미드, 1,1-디부틸피페리디늄비스(펜타플루오로에탄술포닐)이미드, N-메틸-N-프로필피페리디늄비스(트리플루오로메탄술포닐)이미드 등을 들 수 있다.Also, for example, 1-dimethylpyrrolidinium bis (trifluoromethanesulfonyl) imide, 1-methyl-1-ethylpyrrolidinium bis (trifluoromethanesulfonyl) imide, (Trifluoromethanesulfonyl) imide, 1-methyl-1-butylpyrrolidinium bis (trifluoromethanesulfonyl) imide, 1-methyl-1-pentylpyrrolidinium Methyl-1-hexylpyrrolidinium bis (trifluoromethanesulfonyl) imide, 1-methyl-1-heptylpyrrolidinium bis (trifluoromethanesulfonyl) imide, Ethyl-1-propylpyrrolidinium bis (trifluoromethanesulfonyl) imide, 1-ethyl-1-butylpyrrolidinium bis (trifluoromethanesulfonyl) imide, Ethyl-1-pentylpyrrolidinium bis (trifluoromethanesulfonyl) imide, 1-ethyl-1-hexylpyrrolidinium bis (trifluoromethanesulfonyl) Heptylpyrrolidinium bis (trifluoro Propyl-1-butylpyrrolidinium bis (trifluoromethanesulfonyl) imide, 1,1-dipropylpyrrolidinium bis (trifluoromethanesulfonyl) imide, (Trifluoromethanesulfonyl) imide, 1-propylpiperidinium bis (trifluoromethanesulfonyl) imide, 1-pentylpiperidinium bis (trifluoromethanesulfonyl) imide, (Trifluoromethanesulfonyl) imide, 1-methyl-1-ethylpiperidinium bis (trifluoromethanesulfonyl) imide, 1,1-dimethylpiperidinium bis Methyl-1-propylpiperidinium bis (trifluoromethanesulfonyl) imide, 1-methyl-1-butylpiperidinium bis (trifluoromethanesulfonyl) imide, 1-methyl- Methyl-1-hexylpiperidinium bis (trifluoromethanesulfonyl) imide, 1-methyl-1-heptylpiperidinium bis (trifluoromethanesulfonyl) imide, Fluoromethane sulphate Ethyl-1-butylpiperidinium bis (trifluoromethanesulfonyl) imide, 1-ethyl-1-propylpiperidinium bis (trifluoromethanesulfonyl) 1-pentylpiperidinium bis (trifluoromethanesulfonyl) imide, 1-ethyl-1-hexylpiperidinium bis (trifluoromethanesulfonyl) imide, 1-ethyl- Propyl-1-butylpiperidinium bis (trifluoromethanesulfonyl) imide, 1,1-dipropylpiperidinium bis (trifluoromethanesulfonyl) imide, 1-dimethylpyrrolidinium bis (pentafluoroethanesulfonyl) imide, 1,1-dibutylpiperidinium bis (trifluoromethanesulfonyl) imide, Methyl-1-ethylpyrrolidinium bis (pentafluoroethanesulfonyl) imide, 1-methyl-1-propylpyrrolidinium bis (pentafluoroethanesulfonyl) imide, Pyrrolidinium bis (pentafluoro Methyl-1-pentylpyrrolidinium bis (pentafluoroethanesulfonyl) imide, 1-methyl-1-hexylpyrrolidinium bis (pentafluoroethanesulfonyl) imide, Methyl-1-heptylpyrrolidinium bis (pentafluoroethanesulfonyl) imide, 1-ethyl-1-propylpyrrolidinium bis (pentafluoroethanesulfonyl) Ethyl-1-pentylpyrrolidinium bis (pentafluoroethanesulfonyl) imide, 1-ethyl-1-hexylpyrrolidinium bis (pentafluoroethanesulfonyl) imide, Ethyl-1-heptylpyrrolidinium bis (pentafluoroethanesulfonyl) imide, 1,1-dipropylpyrrolidinium bis (pentafluoroethanesulfonyl) imide, Imide, 1-propyl-1-butylpyrrolidinium bis (pentafluoroethanesulfonyl) imide, 1,1-dibutylpyrrolidinium bis (pentafluoroethanesulfonyl) Ridinium bis (pentafluoro (Pentafluoroethanesulfonyl) imide, 1,1-dimethylpiperidinium bis (pentafluoroethanesulfonyl) imide, 1-methyl-1 (Pentafluoroethanesulfonyl) imide, 1-methyl-1-propylpiperidinium bis (pentafluoroethanesulfonyl) imide, 1-methyl-1-butylpiperidinium bis Methyl-1-pentylpiperidinium bis (pentafluoroethanesulfonyl) imide, 1-methyl-1-hexylpiperidinium bis (pentafluoroethanesulfonyl) imide, Methyl-1-heptylpiperidinium bis (pentafluoroethanesulfonyl) imide, 1-ethyl-1-propylpiperidinium bis (pentafluoroethanesulfonyl) imide, 1 Ethyl-1-heptylpiperidinium bis (pentafluoroethanesulfonyl) imide, 1-ethyl-1-pentylpiperidinium bis (pentafluoroethanesulfonyl) Silpiperidinium bis (pentafluoro Ethyl-1-heptylpiperidinium bis (pentafluoroethanesulfonyl) imide, 1-propyl-1-butylpiperidinium bis (pentafluoroethanesulfonyl) imide , 1,1-dipropylpiperidinium bis (pentafluoroethanesulfonyl) imide, 1,1-dibutylpiperidinium bis (pentafluoroethanesulfonyl) imide, N-methyl- Piperidinium bis (trifluoromethanesulfonyl) imide, and the like.

또, 상기 화합물의 오늄 성분 대신에, 트리메틸술포늄 카티온, 트리에틸술포늄 카티온, 트리부틸술포늄 카티온, 트리헥실술포늄 카티온, 디에틸메틸술포늄 카티온, 디부틸에틸술포늄 카티온, 디메틸데실술포늄 카티온, 테트라메틸포스포늄 카티온, 테트라에틸포스포늄 카티온, 테트라부틸포스포늄 카티온, 테트라헥실포스포늄 카티온을 사용한 화합물 등을 들 수 있다.In addition, in place of the onium component of the above-mentioned compound, there can be used, for example, trimethylsulfonium cation, triethylsulfonium cation, tributylsulfonium cation, trihexylsulfonium cation, diethylsulfonium cation, dibutylethylsulfonium A compound using tetracyanophosphonium cation, tetradecylphosphonium cation, tetradethylphosphonium cation, tetrabutylphosphonium cation, tetrahexylphosphonium cation, and the like.

또, 상기의 비스(트리플루오로메탄술포닐)이미드 대신에, 비스(펜타플루오로술포닐)이미드, 비스(헵타플루오로프로판술포닐)이미드, 비스(노나플루오로부탄술포닐)이미드, 트리플루오로메탄술포닐노나플루오로부탄술포닐이미드, 헵타플루오로프로판술포닐트리플루오로메탄술포닐이미드, 펜타플루오로에탄술포닐노나플루오로부탄술포닐이미드, 시클로-헥사플루오로프로판-1,3-비스(술포닐)이미드 아니온 등을 사용한 화합물 등을 들 수 있다.In place of the bis (trifluoromethanesulfonyl) imide, bis (pentafluorosulfonyl) imide, bis (heptafluoropropanesulfonyl) imide, bis (nonafluorobutanesulfonyl) Heptafluoropropanesulfonyl trifluoromethanesulfonylimide, pentafluoroethanesulfonylnonafluorobutanesulfonylimide, cyclohexane sulfonylimide, heptafluoroethanesulfonylimide, heptafluoropropanesulfonyl trifluoromethanesulfonylimide, pentafluoroethanesulfonylonaphlorobutanesulfonylimide, cyclo- Hexafluoropropane-1,3-bis (sulfonyl) imidanion, and the like.

오늄-불소 함유 이미드 아니온염 이외의 오늄-아니온염 (B1) 로는, 상기 오늄 성분과 불소 함유 이미드 아니온염 이외의 아니온 성분의 조합으로 이루어지는 화합물이 적당히 선택되어 사용된다. 예를 들어, 1-부틸피리디늄테트라플루오로보레이트, 1-부틸피리디늄헥사플루오로포스페이트, 1-부틸-3-메틸피리디늄테트라플루오로보레이트, 1-부틸-3-메틸피리디늄트리플루오로메탄술포네이트, 1-헥실피리디늄테트라플루오로보레이트, 2-메틸-1-피롤린테트라플루오로보레이트, 1-에틸-2-페닐인돌테트라플루오로보레이트, 1,2-디메틸인돌테트라플루오로보레이트, 1-에틸카르바졸테트라플루오로보레이트, 1-에틸-3-메틸이미다졸륨테트라플루오로보레이트, 1-에틸-3-메틸이미다졸륨아세테이트, 1-에틸-3-메틸이미다졸륨트리플루오로아세테이트, 1-에틸-3-메틸이미다졸륨헵타플루오로부틸레이트, 1-에틸-3-메틸이미다졸륨트리플루오로메탄술포네이트, 1-에틸-3-메틸이미다졸륨퍼플루오로부탄술포네이트, 1-에틸-3-메틸이미다졸륨디시안아미드, 1-에틸-3-메틸이미다졸륨트리스(트리플루오로메탄술포닐)메티드, 1-부틸-3-메틸이미다졸륨테트라플루오로보레이트, 1-부틸-3-메틸이미다졸륨헥사플루오로포스페이트, 1-부틸-3-메틸이미다졸륨트리플루오로아세테이트, 1-부틸-3-메틸이미다졸륨헵타플루오로부틸레이트, 1-부틸-3-메틸이미다졸륨트리플루오로메탄술포네이트, 1-부틸-3-메틸이미다졸륨퍼플루오로부탄술포네이트, 1-헥실-3-메틸이미다졸륨브로마이드, 1-헥실-3-메틸이미다졸륨클로라이드, 1-헥실-3-메틸이미다졸륨테트라플루오로보레이트, 1-헥실-3-메틸이미다졸륨헥사플루오로포스페이트, 1-헥실-3-메틸이미다졸륨트리플루오로메탄술포네이트, 1-옥틸-3-메틸이미다졸륨테트라플루오로보레이트, 1-옥틸-3-메틸이미다졸륨헥사플루오로포스페이트, 1-헥실-2,3-디메틸이미다졸륨테트라플루오로보레이트, 1-메틸피라졸륨테트라플루오로보레이트, 3-메틸피라졸륨테트라플루오로보레이트, 디알릴디메틸암모늄테트라플루오로보레이트, 디알릴디메틸암모늄트리플루오로메탄술포네이트, N,N-디에틸-N-메틸-N-(2-메톡시에틸)암모늄테트라플루오로보레이트, N,N-디에틸-N-메틸-N-(2-메톡시에틸)암모늄트리플루오로메탄술포네이트, 1-부틸피리디늄(트리플루오로메탄술포닐)트리플루오로아세트아미드, 1-부틸-3-메틸피리디늄(트리플루오로메탄술포닐)트리플루오로아세트아미드, 1-에틸-3-메틸이미다졸륨(트리플루오로메탄술포닐)트리플루오로아세트아미드, N,N-디에틸-N-메틸-N-(2-메톡시에틸)암모늄(트리플루오로메탄술포닐)트리플루오로아세트아미드, 디알릴디메틸암모늄(트리플루오로메탄술포닐)트리플루오로아세트아미드, 글리시딜트리메틸암모늄(트리플루오로메탄술포닐)트리플루오로아세트아미드, 1-부틸-3메틸피리딘-1-윰트리플루오로메탄술포네이트 등을 들 수 있다.As the onium-anionite (B1) other than the onium-fluorine-containing imide anionite, a compound comprising a combination of the onium component and an anion component other than the fluorine-containing imide anionite is suitably selected and used. For example, 1-butylpyridinium tetrafluoroborate, 1-butylpyridinium hexafluorophosphate, 1-butyl-3-methylpyridinium tetrafluoroborate, 1-butyl- Methanesulfonate, 1-hexylpyridinium tetrafluoroborate, 2-methyl-1-pyrroline tetrafluoroborate, 1-ethyl-2-phenylindole tetrafluoroborate, 1,2- Ethylcarbazole tetrafluoroborate, 1-ethyl-3-methylimidazolium tetrafluoroborate, 1-ethyl-3-methylimidazolium acetate, 1-ethyl-3-methylimidazolium tri Ethyl-3-methylimidazolium heptafluorobutyrate, 1-ethyl-3-methylimidazolium trifluoromethanesulfonate, 1-ethyl-3-methylimidazolium perfluoro Butane sulfonate, 1-ethyl-3-methylimidazolium dicyanamide, 1-ethyl-3-methyl Butyl-3-methylimidazolium tetrafluoroborate, 1-butyl-3-methylimidazolium hexafluorophosphate, 1-butyl-3- Methylimidazolium trifluoroacetate, 1-butyl-3-methylimidazolium heptafluorobutyrate, 1-butyl-3-methylimidazolium trifluoromethanesulfonate, 1-butyl- 1-hexyl-3-methylimidazolium bromide, 1-hexyl-3-methylimidazolium chloride, 1-hexyl-3-methylimidazolium tetrafluoroborate, 1- 3-methylimidazolium hexafluorophosphate, 1-hexyl-3-methylimidazolium trifluoromethanesulfonate, 1-octyl-3-methylimidazolium tetrafluoroborate, 1-octyl-3 Methylimidazolium hexafluorophosphate, 1-hexyl-2,3-dimethylimidazolium tetrafluoroborate, 1-methyl Triazolium tetrafluoroborate, triazolium tetrafluoroborate, 3-methylpyrazolium tetrafluoroborate, diallyldimethylammonium tetrafluoroborate, diallyldimethylammonium trifluoromethanesulfonate, N, N-diethyl- (2-methoxyethyl) ammonium tetrafluoroborate, N, N-diethyl-N-methyl-N- (2-methoxyethyl) ammonium trifluoromethanesulfonate, 1-butylpyridinium 1-butyl-3-methylpyridinium (trifluoromethanesulfonyl) trifluoroacetamide, 1-ethyl-3-methylimidazolium (trifluoromethanesulfonyl) trifluoroacetamide ) Trifluoroacetamide, N, N-diethyl-N-methyl-N- (2-methoxyethyl) ammonium (trifluoromethanesulfonyl) trifluoroacetamide, diallyldimethylammonium Methanesulfonyl) trifluoroacetamide, glycidyltrimethylammonium (trifluoromethane sulphate Carbonyl) there may be mentioned dimethylacetamide, and 1-butyl -3-methylpyridin-1-ium trifluoromethanesulfonate trifluoromethyl.

본 발명에 있어서는, 상기 오늄-아니온염 (B1) 을 1 종 단독으로, 또는 2 종 이상을 혼합하여 사용할 수 있다. 또, 이들 중에서도, 1-메틸-1-에틸피롤리디늄비스(트리플루오로메탄술포닐)이미드가 바람직하다.In the present invention, the onium-anionite (B1) may be used singly or in combination of two or more. Among these, 1-methyl-1-ethylpyrrolidinium bis (trifluoromethanesulfonyl) imide is preferable.

본 발명의 점착제 조성물에 있어서의 오늄-아니온염 (B1) 의 비율은, (메트)아크릴계 폴리머 (A) 100 중량부에 대해, 0.1 ∼ 1.5 중량부가 바람직하다. 상기 오늄-아니온염 (B1) 이 0.1 중량부 미만에서는, 대전 방지 성능의 향상 효과가 충분하지 않은 경우가 있다. 상기 오늄-아니온염 (B1) 은, 0.2 중량부 이상이 바람직하고, 나아가서는 0.5 중량부 이상인 것이 바람직하다. 한편, 상기 오늄-아니온염 (B1) 이 1.5 중량부보다 많으면, 내구성이나 외관이 충분하지 않게 되는 경우가 있다. 상기 오늄-아니온염 (B1) 은, 1.3 중량부 이하가 바람직하고, 1.0 중량부 이하가 보다 바람직하고, 1.0 중량부 미만이 더욱 바람직하다. 상기 오늄-아니온염 (B1) 의 비율은, 상기 상한치 또는 하한치를 채용하여 바람직한 범위를 설정할 수 있다.The proportion of the onium salt-anion salt (B1) in the pressure-sensitive adhesive composition of the present invention is preferably 0.1 to 1.5 parts by weight based on 100 parts by weight of the (meth) acrylic polymer (A). If the amount of the onium salt is less than 0.1 part by weight, the effect of improving the antistatic performance may not be sufficient. The amount of the onium salt-anionite (B1) is preferably 0.2 part by weight or more, more preferably 0.5 part by weight or more. On the other hand, if the amount of the onium salt-anionite (B1) is more than 1.5 parts by weight, the durability and the appearance may be insufficient. The onium-anionite (B1) is preferably 1.3 parts by weight or less, more preferably 1.0 part by weight or less, and even more preferably 1.0 part by weight or less. The above-mentioned upper limit value or lower limit value can be adopted as the ratio of the onium-anionic salt (B1), and a preferable range can be set.

또, 상기 중에서도, 예를 들어, 1-메틸-1-에틸피롤리디늄비스(트리플루오로메탄술포닐)이미드와 같이, 고체이며, 또한 분자가 큰 것은, 첨가량을 1.5 중량부보다 많게 하면, 점착제 중에서 결정화가 일어나 외관 불량이 발생하는 경우가 있어, 특히 바람직하지 않다.Among the above, a solid and a large molecule such as 1-methyl-1-ethylpyrrolidinium bis (trifluoromethanesulfonyl) imide is preferable when the addition amount is more than 1.5 parts by weight , Crystallization occurs in the pressure-sensitive adhesive, resulting in appearance failure, which is not particularly preferable.

(3) 알칼리 금속염 (B2)(3) Alkali metal salt (B2)

알칼리 금속염 (B2) 로는, 알칼리 금속의 유기염 및 무기염을 사용할 수 있다.As the alkali metal salt (B2), an organic salt and an inorganic salt of an alkali metal can be used.

알칼리 금속염 (B2) 의 카티온부를 구성하는 알칼리 금속 이온으로는, 리튬, 나트륨, 칼륨의 각 이온을 들 수 있다. 이들 알칼리 금속 이온 중에서도 리튬 이온이 바람직하다.Examples of the alkali metal ion constituting the cation portion of the alkali metal salt (B2) include ions of lithium, sodium and potassium. Of these alkali metal ions, lithium ions are preferable.

알칼리 금속염의 아니온부는 유기물로 구성되어 있어도 되고, 무기물로 구성되어 있어도 된다. 유기염을 구성하는 아니온부로는, 예를 들어, CH3COO-, CF3COO-, CH3SO3 -, CF3SO3 -, (CF3SO2)3C-, C4F9SO3 -, C3F7COO-, (CF3SO2)(CF3CO)N-, -O3S (CF2)3SO3 -, PF6 -, CO3 2-, 나 하기 일반식 (1) ∼ (4), The anion portion of the alkali metal salt may be composed of an organic material or may be composed of an inorganic material. Anion portion constituting the organic salt is, for example, CH 3 COO -, CF 3 COO -, CH 3 SO 3 -, CF 3 SO 3 -, (CF 3 SO 2) 3 C -, C 4 F 9 SO 3 -, C 3 F 7 COO -, (CF 3 SO 2) (CF 3 CO) N -, - O 3 S (CF 2) 3 SO 3 -, PF 6 -, CO 3 2-, or to the general (1) to (4),

(1) : (CnF2n＋1SO2)2N- (단, n 은 1 ∼ 10 의 정수), (1): ???????? (C n F 2n + 1 SO 2 ) 2 N - wherein n is an integer of 1 to 10,

(2) : CF2(CmF2mSO2)2N- (단, m 은 1 ∼ 10 의 정수), (2): CF 2 (C m F 2 m SO 2 ) 2 N - wherein m is an integer of 1 to 10,

(3) : -O3S(CF2)lSO3 - (단, l 은 1 ∼ 10 의 정수), (3): - O 3 S (CF 2 ) 1 SO 3 - (wherein 1 is an integer of 1 to 10),

(4) : (CpF2p＋1SO2)N-(CqF2q＋1SO2), (단, p, q 는 1 ∼ 10 의 정수) 로 나타내는 것 등이 사용된다. 특히, 불소 원자를 함유하는 아니온부는, 이온 해리성이 양호한 이온 화합물이 얻어지는 점에서 바람직하게 사용된다. 무기염을 구성하는 아니온부로는, Cl-, Br-, I-, AlCl4 -, Al2Cl7 -, BF4 -, PF6 -, ClO4 -, NO3 -, AsF6 -, SbF6 -, NbF6 -, TaF6 -, (CN)2N- 등이 사용된다. 아니온부로는, (CF3SO2)2N-, (C2F5SO2)2N-, 등의 상기 일반식 (1) 로 나타내는 (퍼플루오로알킬술포닐)이미드가 바람직하고, 특히 (CF3SO2)2N- 로 나타내는 (트리플루오로메탄술포닐)이미드가 바람직하다.(4): ???????? (C p F 2p + 1 SO 2 ) N - (C q F 2q + 1 SO 2 ) (where p and q are integers of 1 to 10) Particularly, the anion moiety containing a fluorine atom is preferably used because an ionic compound having a good ion dissociation property can be obtained. The anion forming the inorganic salt includes Cl - , Br - , I - , AlCl 4 - , Al 2 Cl 7 - , BF 4 - , PF 6 - , ClO 4 - , NO 3 - , AsF 6 - , SbF 6 - , NbF 6 - , TaF 6 - , (CN) 2 N - and the like. The anion is preferably a (perfluoroalkylsulfonyl) imide represented by the above general formula (1) such as (CF 3 SO 2 ) 2 N - , (C 2 F 5 SO 2 ) 2 N - Particularly, (trifluoromethanesulfonyl) imide represented by (CF 3 SO 2 ) 2 N - is preferable.

알칼리 금속의 유기염으로는, 구체적으로는, 아세트산나트륨, 알긴산나트륨, 리그닌술폰산나트륨, 톨루엔술폰산나트륨, LiCF3SO3, Li(CF3SO2)2N, Li(C2F5SO2)2N, Li(C4F9SO2)2N, Li(CF3SO2)3C, KO3S(CF2)3SO3K, LiO3S(CF2)3SO3K 등을 들 수 있고, 이들 중 LiCF3SO3, Li(CF3SO2)2N, Li(C2F5SO2)2N, Li(C4F9SO2)2N, Li(CF3SO2)3C 등이 바람직하고, Li(CF3SO2)2N, Li(C2F5SO2)2N, Li(C4F9SO2)2N 등의 불소 함유 리튬이미드염이 보다 바람직하고, 특히 (퍼플루오로알킬술포닐)이미드리튬염이 바람직하다.Specific examples of the organic salts of alkali metals include sodium acetate, sodium alginate, sodium ligninsulfonate, sodium toluenesulfonate, LiCF 3 SO 3 , Li (CF 3 SO 2 ) 2 N, Li (C 2 F 5 SO 2 ) 2 N, Li (C 4 F 9 SO 2) to 2 N, Li (CF 3 SO 2) 3 C, KO 3 S (CF 2) 3 SO 3 K, LiO 3 S (CF 2) 3 SO 3 K , etc. there may be mentioned, LiCF of these 3 SO 3, Li (CF 3 SO 2) 2 N, Li (C 2 F 5 SO 2) 2 N, Li (C 4 F 9 SO 2) 2 N, Li (CF 3 SO 2) 3 C, etc. are preferred, and Li (CF 3 SO 2) 2 N, Li (C 2 F 5 SO 2) 2 N, Li (C 4 F 9 SO 2) is a fluorine-containing lithium, such as 2 N imide salt (Perfluoroalkylsulfonyl) imide lithium salt is particularly preferable.

또, 알칼리 금속의 무기염으로는, 과염소산리튬, 요오드화리튬을 들 수 있다.Examples of inorganic salts of alkali metals include lithium perchlorate and lithium iodide.

본 발명에 있어서는, 상기 알칼리 금속염 (B2) 를 1 종 단독으로, 또는 2 종 이상을 혼합하여 사용할 수 있다.In the present invention, the alkali metal salt (B2) may be used singly or in combination of two or more kinds.

본 발명의 점착제 조성물에 있어서의 알칼리 금속염 (B2) 의 비율은, (메트)아크릴계 폴리머 (A) 100 중량부에 대해 0.4 ∼ 3.5 중량부이다. 상기 알칼리 금속염 (B2) 가 0.4 중량부 미만에서는, 본 발명의 점착제 조성물로 형성되는 점착제층 표면의 표면 저항값이 높아져, 결과적으로 백색 불균일이 발생하는 경우가 있었다. 상기 알칼리 금속염 (B2) 는, 0.5 중량부 이상이 보다 바람직하다. 한편, 상기 알칼리 금속염 (B2) 가 3.5 중량부보다 많으면, 엄격한 조건의 가습 시험 후에 있어서의 대전 방지 성능의 향상 효과가 충분하지 않다. 또, 상기 알칼리 금속염 (B2) 가 많으면, 점착제 조성물로 형성되는 점착제층과 편광 필름 등의 피착체의 계면 부근에 알칼리 금속염 (B2) 가 편석되고, 그 결과, 박리가 발생하는 경우가 있어, 신뢰성이나 내구성이 떨어지는 것이었다. 상기 알칼리 금속염 (B2) 는, 3.0 중량부 이하가 바람직하고, 2.0 중량부 이하가 보다 바람직하다. 상기 알칼리 금속염 (B2) 의 비율은, 상기 상한치 또는 하한치를 채용하여 바람직한 범위를 설정할 수 있다.The proportion of the alkali metal salt (B2) in the pressure-sensitive adhesive composition of the present invention is 0.4 to 3.5 parts by weight based on 100 parts by weight of the (meth) acrylic polymer (A). When the amount of the alkali metal salt (B2) is less than 0.4 part by weight, the surface resistance value of the surface of the pressure-sensitive adhesive layer formed of the pressure-sensitive adhesive composition of the present invention becomes high, and as a result, white unevenness may occur. The alkali metal salt (B2) is more preferably 0.5 part by weight or more. On the other hand, if the amount of the alkali metal salt (B2) is more than 3.5 parts by weight, the effect of improving the antistatic performance after the humidification test under the severe condition is not sufficient. When the amount of the alkali metal salt (B2) is large, the alkali metal salt (B2) segregates near the interface between the pressure-sensitive adhesive layer formed of the pressure-sensitive adhesive composition and the adherend such as a polarizing film. As a result, peeling may occur, Or durability was poor. The amount of the alkali metal salt (B2) is preferably 3.0 parts by weight or less, more preferably 2.0 parts by weight or less. The upper limit or the lower limit of the ratio of the alkali metal salt (B2) may be adopted to set the preferable range.

또, 상기 알칼리 금속염 (B2) 와 오늄-아니온염 (B1) 의 중량비 (B2/B1) 는, 1.2 ∼ 4 이고, 1.2 ∼ 3.5 인 것이 바람직하고, 1.2 ∼ 3.0 인 것이 보다 바람직하다. 상기 중량비 (B2/B1) 가 1.2 미만이면, 고레벨의 도전 성능이 얻어지지 않고, 중량비 (B2/B1) 가 4 를 초과하면, 알칼리 금속염의 석출에 의한 외관 악화나 내습 시험시의 성능 악화가 발생하기 쉬워진다.The weight ratio (B2 / B1) of the alkali metal salt (B2) to the onium anionite (B1) is 1.2 to 4, preferably 1.2 to 3.5, and more preferably 1.2 to 3.0. If the weight ratio (B2 / B1) is less than 1.2, a high level of conductivity can not be obtained. If the weight ratio (B2 / B1) is more than 4, deterioration of appearance due to precipitation of alkali metal salt and deterioration of performance during humidity resistance test It becomes easier to do.

(4) 티올계 실란 커플링제 (C1)(4) Thiol-based silane coupling agent (C1)

본 발명의 편광 필름용 점착제 조성물은, 티올계 실란 커플링제 (C1) 을 함유하는 것이 바람직하다. 티올계 실란 커플링제 (C1) 은, 도전 성능에 악영향을 잘 미치지 않기 때문에, 점착제층의 도전 성능을 저해하지 않고, 피착체와의 접착 내구성을 향상시킬 수 있다. 그 때문에, 종래의 대전 방지 점착제 조성물에서는 해소할 수 없었던 큰 정전기가 발생한 경우여도 백색 불균일을 억제할 수 있는 것이다.The pressure-sensitive adhesive composition for a polarizing film of the present invention preferably contains a thiol-based silane coupling agent (C1). Since the thiol silane coupling agent (C1) does not adversely affect the conductive performance, the durability of adhesion to an adherend can be improved without deteriorating the conductive performance of the pressure-sensitive adhesive layer. Therefore, white non-uniformity can be suppressed even when large static electricity which can not be eliminated by the conventional antistatic pressure-sensitive adhesive composition is generated.

티올계 실란 커플링제 (C1) 로는, 예를 들어, 실록산 골격과 메르캅토기를 갖는 것이면 되고, 예를 들어, X-41-1810 (상품명, 메르캅토 당량 : 450 g/mol), X-41-1805 (상품명, 메르캅토 당량 : 800 g/mol), X-41-1818 (상품명, 메르캅토 당량 : 850 g/mol) (모두 신에츠 화학 공업 (주) 제조) 등을 들 수 있고, 이들을 1 종 단독으로 또는 2 종 이상을 혼합하여 사용할 수 있다. 또, 이들 중에서도, 점착제층의 급격한 점착력 상승을 억제하여, 피착체로부터 리워크하는 것이 가능한 점에서 X-41-1810 이 바람직하다.Examples of the thiol silane coupling agent (C1) include those having a siloxane skeleton and a mercapto group, such as X-41-1810 (trade name, mercapto equivalent: 450 g / mol), X-41 (Trade name, mercapto equivalent: 800 g / mol) and X-41-1818 (trade name, mercapto equivalent: 850 g / mol) (all available from Shin-Etsu Chemical Co., Ltd.) The species may be used singly or in combination of two or more species. Of these, X-41-1810 is preferable because it is possible to inhibit the abrupt adhesion increase of the pressure-sensitive adhesive layer and rework from the adherend.

티올계 실란 커플링제 (C1) 의 티올기의 함유량은, 예를 들어, 메르캅토기의 경우, 메르캅토 당량 1000 g/mol 이하인 것이 바람직하고, 850 g/mol 이하인 것이 보다 바람직하고, 급격한 점착력 상승을 억제하여 피착체로부터 리워크하는 것이 가능한 점에서 650 g/mol 이하인 것이 보다 바람직하다. 또, 메르캅토 당량의 하한치는 특별히 한정되는 것은 아니지만, 예를 들어, 100 g/mol 이상인 것이 바람직하다.The content of the thiol group in the thiol-based silane coupling agent (C1) is preferably 1,000 g / mol or less, more preferably 850 g / mol or less, in the case of a mercapto group, More preferably not more than 650 g / mol in view of being able to rework from an adherend. The lower limit of the mercapto equivalent is not particularly limited, but is preferably 100 g / mol or more, for example.

본 발명의 점착제 조성물에 있어서의 티올계 실란 커플링제 (C1) 의 비율은, (메트)아크릴계 폴리머 (A) 100 중량부에 대해, 0.001 ∼ 5 중량부가 바람직하다. 상기 티올계 실란 커플링제 (C1) 이 0.001 중량부 미만에서는, 유리 및 ITO 등의 투명 도전층 표면에 대한 신뢰성을 향상시키는 것이 곤란한 경우가 있다. 상기 티올계 실란 커플링제 (C1) 은, 0.01 중량부 이상이 바람직하고, 나아가서는 0.1 중량부 이상인 것이 바람직하다. 한편, 상기 티올계 실란 커플링제 (C1) 이 5 중량부보다 많으면 점착제층의 점착력의 상승이 과잉이 되기 때문에, 당해 점착제층을 피착체로부터 리워크하는 것이 곤란해지는 경우가 있다. 상기 티올계 실란 커플링제 (C1) 은, 4 중량부 이하가 바람직하고, 3 중량부 이하가 바람직하고, 2.5 중량부 이하가 바람직하고, 나아가서는 2 중량부 이하인 것이 바람직하다. 상기 티올계 실란 커플링제 (C1) 의 비율은, 상기 상한치 또는 하한치를 채용하여 바람직한 범위를 설정할 수 있다.The proportion of the thiol-based silane coupling agent (C1) in the pressure-sensitive adhesive composition of the present invention is preferably 0.001 to 5 parts by weight based on 100 parts by weight of the (meth) acrylic polymer (A). When the amount of the thiol-based silane coupling agent (C1) is less than 0.001 part by weight, it may be difficult to improve the reliability of the surface of the transparent conductive layer such as glass and ITO. The amount of the thiol-based silane coupling agent (C1) is preferably 0.01 part by weight or more, more preferably 0.1 part by weight or more. On the other hand, if the amount of the thiol-based silane coupling agent (C1) is more than 5 parts by weight, the increase in the adhesive strength of the pressure-sensitive adhesive layer becomes excessive, and it may become difficult to rework the pressure-sensitive adhesive layer from the adherend. The amount of the thiol-based silane coupling agent (C1) is preferably 4 parts by weight or less, more preferably 3 parts by weight or less, more preferably 2.5 parts by weight or less, further preferably 2 parts by weight or less. The upper limit or lower limit of the ratio of the thiol silane coupling agent (C1) may be employed to set the preferable range.

(5) 그 외(5) Others

본 발명의 점착제 조성물에는, 상기 이외에도, 가교제 (D) 를 함유할 수 있다. 가교제 (D) 로는, 유기계 가교제나 다관능성 금속 킬레이트를 사용할 수 있다. 유기계 가교제로는, 이소시아네이트계 가교제, 과산화물계 가교제, 에폭시계 가교제, 이민계 가교제 등을 들 수 있다. 다관능성 금속 킬레이트는, 다가 금속이 유기 화합물과 공유 결합 또는 배위 결합되고 있는 것이다. 다가 금속 원자로는, Al, Cr, Zr, Co, Cu, Fe, Ni, V, Zn, In, Ca, Mg, Mn, Y, Ce, Sr, Ba, Mo, La, Sn, Ti 등을 들 수 있다. 공유 결합 또는 배위 결합되는 유기 화합물 중의 원자로는 산소 원자 등을 들 수 있고, 유기 화합물로는 알킬에스테르, 알코올 화합물, 카르복실산 화합물, 에테르 화합물, 케톤 화합물 등을 들 수 있다.The pressure-sensitive adhesive composition of the present invention may contain, in addition to the above, a cross-linking agent (D). As the crosslinking agent (D), an organic crosslinking agent or a polyfunctional metal chelate can be used. Examples of the organic crosslinking agent include an isocyanate crosslinking agent, a peroxide crosslinking agent, an epoxy crosslinking agent, and an imine crosslinking agent. A polyfunctional metal chelate is one in which a polyvalent metal is covalently bonded or coordinated with an organic compound. Examples of the multivalent metal atom include Al, Cr, Zr, Co, Cu, Fe, Ni, V, Zn, In, Ca, Mg, Mn, Y, Ce, Sr, Ba, Mo, La, have. Examples of the reactive group in the organic compound to be covalently bonded or coordinated include an oxygen atom, and examples of the organic compound include an alkyl ester, an alcohol compound, a carboxylic acid compound, an ether compound, and a ketone compound.

가교제 (D) 로는, 이소시아네이트계 가교제 및 과산화물형 가교제로 이루어지는 군에서 선택되는 1 종 이상의 가교제가 바람직하고, 이소시아네이트계 가교제와 과산화물형 가교제를 병용하여 사용하는 것이 보다 바람직하다. 이소시아네이트계 가교제에 관련된 화합물로는, 예를 들어, 톨릴렌디이소시아네이트, 클로르페닐렌디이소시아네이트, 테트라메틸렌디이소시아네이트, 자일릴렌디이소시아네이트, 디페닐메탄디이소시아네이트, 수소 첨가된 디페닐메탄디이소시아네이트 등의 이소시아네이트 모노머 및 이들 이소시아네이트 모노머를 트리메틸올프로판 등과 부가한 이소시아네이트 화합물이나 이소시아누레이트화물, 뷰렛형 화합물, 나아가서는 폴리에테르폴리올이나 폴리에스테르폴리올, 아크릴폴리올, 폴리부타디엔폴리올, 폴리이소프렌폴리올 등 부가 반응시킨 우레탄프레폴리머형의 이소시아네이트 등을 들 수 있다. 특히 바람직하게는 폴리이소시아네이트 화합물이고, 헥사메틸렌디이소시아네이트, 수소 첨가 자일릴렌디이소시아네이트, 및 이소포론디이소시아네이트로 이루어지는 군에서 선택되는 1 종 또는 그것에서 유래하는 폴리이소시아네이트 화합물이다. 여기서, 헥사메틸렌디이소시아네이트, 수소 첨가 자일릴렌디이소시아네이트, 및 이소포론디이소시아네이트로 이루어지는 군에서 선택되는 1 종 또는 그것에서 유래하는 폴리이소시아네이트 화합물에는, 헥사메틸렌디이소시아네이트, 수소 첨가 자일릴렌디이소시아네이트, 이소포론디이소시아네이트, 폴리올 변성 헥사메틸렌디이소시아네이트, 폴리올 변성 수소 첨가 자일릴렌디이소시아네이트, 트리머형 수소 첨가 자일릴렌디이소시아네이트, 및 폴리올 변성 이소포론디이소시아네이트 등이 포함된다. 예시한 폴리이소시아네이트 화합물은, 수산기와의 반응이, 특히 폴리머에 함유되는 산, 염기를 촉매와 같이 하여, 신속하게 진행되기 때문에, 특히 빠른 가교에 기여하여 바람직하다.As the crosslinking agent (D), at least one crosslinking agent selected from the group consisting of an isocyanate crosslinking agent and a peroxide crosslinking agent is preferable, and it is more preferable to use the isocyanate crosslinking agent and the peroxide crosslinking agent in combination. Examples of the compound relating to the isocyanate-based crosslinking agent include isocyanate monomers such as tolylene diisocyanate, chlorophenylenediisocyanate, tetramethylene diisocyanate, xylylene diisocyanate, diphenylmethane diisocyanate and hydrogenated diphenylmethane diisocyanate And an isocyanate compound in which these isocyanate monomers are added with trimethylolpropane or the like, isocyanurate compounds, biuret type compounds, and further polyurethane polyols, polyester polyols, acrylic polyols, polybutadiene polyols, polyisoprene polyols, And polymer type isocyanates. Particularly preferably, the polyisocyanate compound is a polyisocyanate compound selected from the group consisting of hexamethylene diisocyanate, hydrogenated xylylene diisocyanate, and isophorone diisocyanate, or a polyisocyanate compound derived therefrom. The polyisocyanate compound selected from the group consisting of hexamethylene diisocyanate, hydrogenated xylylene diisocyanate, and isophorone diisocyanate or a polyisocyanate compound derived therefrom includes hexamethylene diisocyanate, hydrogenated xylylene diisocyanate, hydrogenated xylylene diisocyanate, Polyol modified hexamethylene diisocyanate, polyol modified hydrogenated xylylene diisocyanate, trimethylated hydrogenated xylylene diisocyanate, and polyol modified isophorone diisocyanate, and the like. The exemplified polyisocyanate compound is preferred because the reaction with the hydroxyl group proceeds particularly quickly, particularly with an acid and a base contained in the polymer, and thus contributes to rapid crosslinking.

과산화물로는, 가열 또는 광 조사에 의해 라디칼 활성종을 발생시켜 점착제 조성물의 베이스 폴리머의 가교를 진행시키는 것이면 적당히 사용 가능하지만, 작업성이나 안정성을 감안하여, 1 분간 반감기 온도가 80 ℃ ∼ 160 ℃ 인 과산화물을 사용하는 것이 바람직하고, 90 ℃ ∼ 140 ℃ 인 과산화물을 사용하는 것이 보다 바람직하다.The peroxide is not particularly limited if it is capable of generating radical active species by heating or light irradiation to promote crosslinking of the base polymer of the pressure-sensitive adhesive composition. However, considering the workability and stability, the half- It is preferable to use peroxides which are phosphorus-containing peroxides. It is more preferable to use peroxides of 90 to 140 ° C.

사용할 수 있는 과산화물로는, 예를 들어, 디(2-에틸헥실)퍼옥시디카보네이트 (1 분간 반감기 온도 : 90.6 ℃), 디(4-t-부틸시클로헥실)퍼옥시디카보네이트 (1 분간 반감기 온도 : 92.1 ℃), 디-sec-부틸퍼옥시디카보네이트 (1 분간 반감기 온도 : 92.4 ℃), t-부틸퍼옥시네오데카노에이트 (1 분간 반감기 온도 : 103.5 ℃), t-헥실퍼옥시피발레이트 (1 분간 반감기 온도 : 109.1 ℃), t-부틸퍼옥시피발레이트 (1 분간 반감기 온도 : 110.3 ℃), 디라우로일퍼옥사이드 (1 분간 반감기 온도 : 116.4 ℃), 디-n-옥타노일퍼옥사이드 (1 분간 반감기 온도 : 117.4 ℃), 1,1,3,3-테트라메틸부틸퍼옥시-2-에틸헥사노에이트 (1 분간 반감기 온도 : 124.3 ℃), 디(4-메틸벤조일)퍼옥사이드 (1 분간 반감기 온도 : 128.2 ℃), 디벤조일퍼옥사이드 (1 분간 반감기 온도 : 130.0 ℃), t-부틸퍼옥시이소부틸레이트 (1 분간 반감기 온도 : 136.1 ℃), 1,1-디(t-헥실퍼옥시)시클로헥산 (1 분간 반감기 온도 : 149.2 ℃) 등을 들 수 있다. 그 중에서도 특히 가교 반응 효율이 우수한 점에서, 디(4-t-부틸시클로헥실)퍼옥시디카보네이트 (1 분간 반감기 온도 : 92.1 ℃), 디라우로일퍼옥사이드 (1 분간 반감기 온도 : 116.4 ℃), 디벤조일퍼옥사이드 (1 분간 반감기 온도 : 130.0 ℃) 등이 바람직하게 사용된다.Examples of peroxides that can be used include di (2-ethylhexyl) peroxydicarbonate (1 minute half life temperature: 90.6 占 폚), di (4-t- butylcyclohexyl) peroxydicarbonate Butyl peroxyneodecanoate (1 minute half-life temperature: 103.5 占 폚), t-hexyl peroxy pivalate (1 minute), di-sec-butyl peroxydicarbonate (1 minute half-life temperature: 109.1 占 폚), t-butyl peroxypivalate (1 minute half life temperature: 110.3 占 폚), dilauroyl peroxide (1 minute half life temperature: 116.4 占 폚), di-n-octanoyl peroxide (Half-life temperature: 117.4 占 폚), 1,1,3,3-tetramethylbutylperoxy-2-ethylhexanoate (1 minute half life temperature: 124.3 占 폚), di (4-methylbenzoyl) peroxide Half-life temperature: 128.2 占 폚), dibenzoyl peroxide (one-minute half life temperature: 130.0 占 폚), t-butyl peroxyisobutyrate Between the half-life temperature: 136.1 ℃), 1,1- di (t--hexylperoxy) cyclohexane (one minute half life temperature: 149.2 ℃, and the like). Among them, di (4-t-butylcyclohexyl) peroxydicarbonate (1 minute half-life temperature: 92.1 占 폚), di rauroyl peroxide (1 minute half life temperature: 116.4 占 폚) Benzoyl peroxide (1 minute half-life temperature: 130.0 占 폚) and the like are preferably used.

또한, 과산화물의 반감기란, 과산화물의 분해 속도를 나타내는 지표로서, 과산화물의 잔존량이 절반이 될 때까지의 시간을 말한다. 임의의 시간에서 반감기를 얻기 위한 분해 온도나, 임의의 온도에서의 반감기 시간에 관해서는, 메이커 카탈로그 등에 기재되어 있고, 예를 들어, 닛폰 유지 (주)「유기 과산화물 카탈로그 제 9 판 (2003년 5월)」등에 기재되어 있다.The half-life of the peroxide is an index indicating the rate of decomposition of the peroxide, which is the time until the amount of the peroxide remaining becomes half. The decomposition temperature for obtaining a half-life at an arbitrary time and the half-life time at an arbitrary temperature are described in the manufacturer's catalog and are described in, for example, Nippon Oil and Fats Co., Month) &quot;.

가교제 (D) 의 사용량은, (메트)아크릴계 폴리머 (A) 100 중량부에 대해, 0.01 ∼ 20 중량부가 바람직하고, 나아가서는 0.03 ∼ 10 중량부가 바람직하다. 또한, 가교제 (D) 가 0.01 중량부 미만에서는 점착제의 응집력이 부족한 경향이 있어, 가열시에 발포가 발생할 우려가 있고, 한편, 20 중량부보다 많으면 내습성이 충분하지 않아, 신뢰성 시험 등에서 박리가 발생하기 쉬워진다.The amount of the crosslinking agent (D) to be used is preferably 0.01 to 20 parts by weight, more preferably 0.03 to 10 parts by weight, per 100 parts by weight of the (meth) acryl-based polymer (A). When the amount of the crosslinking agent (D) is less than 0.01 part by weight, the cohesive force of the pressure-sensitive adhesive tends to be insufficient and foaming may occur during heating. On the other hand, if the amount exceeds 20 parts by weight, the moisture resistance is insufficient, It becomes easy to occur.

상기 이소시아네이트계 가교제는 1 종을 단독으로 사용해도 되고, 또 2 종 이상을 혼합하여 사용해도 되지만, 전체로서의 함유량은, 상기 (메트)아크릴계 폴리머 (A) 100 중량부에 대해, 상기 이소시아네이트계 가교제를 0.01 ∼ 2 중량부 함유하여 이루어지는 것이 바람직하고, 0.02 ∼ 2 중량부 함유하여 이루어지는 것이 보다 바람직하고, 0.05 ∼ 1.5 중량부 함유하여 이루어지는 것이 더욱 바람직하다. 응집력, 내구성 시험에서의 박리의 저지 등을 고려하여 적당히 함유시키는 것이 가능하다.The isocyanate crosslinking agent may be used singly or in admixture of two or more. The total content of the isocyanate crosslinking agent is preferably in the range of 1 to 100 parts by weight, based on 100 parts by weight of the (meth) acrylic polymer (A) More preferably 0.01 to 2 parts by weight, more preferably 0.02 to 2 parts by weight, still more preferably 0.05 to 1.5 parts by weight. Cohesive force, prevention of peeling in the durability test, and the like.

상기 과산화물은 1 종을 단독으로 사용해도 되고, 또 2 종 이상을 혼합하여 사용해도 되지만, 전체로서의 함유량은, 상기 (메트)아크릴계 폴리머 (A) 100 중량부에 대해, 상기 과산화물 0.01 ∼ 2 중량부이고, 0.04 ∼ 1.5 중량부 함유하여 이루어지는 것이 바람직하고, 0.05 ∼ 1 중량부 함유하여 이루어지는 것이 보다 바람직하다. 가공성, 리워크성, 가교 안정성, 박리성 등의 조정을 위하여, 이 범위 내에서 적당히 선택된다.The peroxide may be used alone or in admixture of two or more. The content of the peroxide is preferably 0.01 to 2 parts by weight per 100 parts by weight of the (meth) acryl-based polymer (A) By weight, preferably 0.04 to 1.5 parts by weight, more preferably 0.05 to 1 part by weight. Is appropriately selected within this range for the purpose of adjusting the workability, reworkability, crosslinking stability, releasability and the like.

또한, 반응 처리 후의 잔존한 과산화물 분해량의 측정 방법으로는, 예를 들어, HPLC (고속 액체 크로마토그래피) 에 의해 측정할 수 있다.The method of measuring the amount of peroxide decomposition remaining after the reaction treatment can be measured by, for example, HPLC (high performance liquid chromatography).

보다 구체적으로는, 예를 들어, 반응 처리 후의 점착제 조성물을 약 0.2 g 씩 취출하고, 아세트산에틸 10 ㎖ 에 침지시키고, 진탕기로 25 ℃ 하, 120 rpm 으로 3 시간 진탕 추출한 후, 실온에서 3 일간 정치 (靜置) 한다. 이어서, 아세토니트릴 10 ㎖ 첨가하고, 25 ℃ 하, 120 rpm 으로 30 분 진탕하고, 멤브레인 필터 (0.45 ㎛) 에 의해 여과하여 얻어진 추출액 약 10 ㎕ 를 HPLC 에 주입하고 분석하여, 반응 처리 후의 과산화물량으로 할 수 있다.More specifically, for example, about 0.2 g of the pressure-sensitive adhesive composition after the reaction treatment was taken out, immersed in 10 ml of ethyl acetate, shaken out at 25 DEG C at 120 rpm for 3 hours with a shaker, (Static). Subsequently, 10 ml of acetonitrile was added, and the mixture was shaken at 25 DEG C at 120 rpm for 30 minutes and filtered through a membrane filter (0.45 mu m). About 10 mu l of the extract was injected into HPLC and analyzed. can do.

또한, 본 발명의 점착제 조성물에는, 아세토아세틸기 함유 실란 커플링제 (C2) 를 함유하는 것이 내구성의 향상의 관점에서 바람직하다. 아세토아세틸기 함유 실란 커플링제 (C2) 로는, 소켄 화학 (주) 제조의 A-100 (상품명) 등을 들 수 있다.The pressure-sensitive adhesive composition of the present invention preferably contains an acetoacetyl group-containing silane coupling agent (C2) from the viewpoint of improvement in durability. Examples of the acetoacetyl group-containing silane coupling agent (C2) include A-100 (trade name) manufactured by Soken Chemical &amp;

상기 실란 커플링제 (C2) 는, 단독으로 사용해도 되고, 또 2 종 이상을 혼합하여 사용해도 되지만, 전체로서의 함유량은 상기 (메트)아크릴계 폴리머 (A) 100 중량부에 대해, 상기 실란 커플링제 (C2) 0.001 ∼ 5 중량부가 바람직하고, 나아가서는 0.01 ∼ 1 중량부가 바람직하고, 나아가서는 0.02 ∼ 1 중량부가 보다 바람직하고, 나아가서는 0.05 ∼ 0.6 중량부가 바람직하다. 내구성을 향상시켜, 편광 필름에 대한 접착력을 적당히 유지하는 양이다.The silane coupling agent (C2) may be used singly or in admixture of two or more kinds. The total content of the silane coupling agent (C2) may be in the range of 1 to 100 parts by weight based on 100 parts by weight of the silane coupling agent C2) is preferably 0.001 to 5 parts by weight, more preferably 0.01 to 1 part by weight, further preferably 0.02 to 1 part by weight, further preferably 0.05 to 0.6 part by weight. The durability is improved and the adhesive force to the polarizing film is appropriately maintained.

상기 실란 커플링제 (C2) 와 상기 티올계 실란 커플링제 (C1) 의 비율은 특별히 한정되는 것은 아니지만, (C2)/(C1) 의 중량비가, 0.1 ∼ 2 정도인 것이 바람직하고, 0.1 ∼ 1 정도인 것이 보다 바람직하고, 0.2 ∼ 0.6 정도인 것이 더욱 바람직하다. 상기 실란 커플링제 (C2) 와 상기 티올계 실란 커플링제 (C1) 의 배합 비율이, 상기 범위에 있음으로써, 본 발명의 점착제 조성물로 형성되는 점착제층을 피착체에 첩부한 경우에, 첩부 초기에 있어서 피착체로부터 점착제층을 리워크하는 것이 가능하고, 또한 시간 경과에서의 점착력 내구성을 부여할 수 있기 때문에 바람직하다.Although the ratio of the silane coupling agent (C2) to the thiol silane coupling agent (C1) is not particularly limited, the weight ratio of (C2) / (C1) is preferably about 0.1 to about 2, , More preferably from about 0.2 to about 0.6. When the ratio of the silane coupling agent (C2) to the thiol silane coupling agent (C1) is in the above range, when the pressure-sensitive adhesive layer formed of the pressure-sensitive adhesive composition of the present invention is attached to an adherend, The pressure-sensitive adhesive layer can be reworked from the adherend, and durability of adhesive force over time can be imparted.

또, 본 발명의 점착제 조성물에는, 티올계 실란 커플링제 (C1), 아세토아세틸기 함유 실란 커플링제 (C2) 이외의 실란 커플링제를 함유할 수도 있고, 예를 들어, 3-글리시독시프로필트리메톡시실란, 3-글리시독시프로필트리에톡시실란, 3-글리시독시프로필메틸디에톡시실란, 2-(3,4-에폭시시클로헥실)에틸트리메톡시실란 등의 에폭시기 함유 실란 커플링제, 3-아미노프로필트리메톡시실란, N-2-(아미노에틸)-3-아미노프로필메틸디메톡시실란, 3-트리에톡시실릴-N-(1,3-디메틸부틸리덴)프로필아민, N-페닐-γ-아미노프로필트리메톡시실란 등의 아미노기 함유 실란 커플링제, 3-아크릴옥시프로필트리메톡시실란, 3-메타크릴옥시프로필트리에톡시실란 등의 (메트)아크릴기 함유 실란 커플링제, 3-이소시아네이트프로필트리에톡시실란 등의 이소시아네이트기 함유 실란 커플링제 등을 들 수 있다. 이들의 첨가량으로는, 특별히 한정되는 것이 아니고, 본 발명의 효과를 저해하지 않는 범위에서 첨가할 수 있는데, 예를 들어, 상기 (메트)아크릴계 폴리머 (A) 100 중량부에 대해, 0.2 중량부 미만인 것이 바람직하고, 본 발명에 있어서는 첨가하지 않는 것이 바람직하다.The pressure-sensitive adhesive composition of the present invention may contain a silane coupling agent other than the thiol silane coupling agent (C1) and the acetoacetyl group-containing silane coupling agent (C2), for example, 3-glycidoxypropyl tri Epoxy group-containing silane coupling agents such as methoxysilane, 3-glycidoxypropyltriethoxysilane, 3-glycidoxypropylmethyldiethoxysilane and 2- (3,4-epoxycyclohexyl) ethyltrimethoxysilane, Aminopropyltrimethoxysilane, N-2- (aminoethyl) -3-aminopropylmethyldimethoxysilane, 3-triethoxysilyl-N- (1,3-dimethylbutylidene) propylamine, N (Meth) acrylate-containing silane coupling agents such as 3-acryloxypropyltrimethoxysilane and 3-methacryloxypropyltriethoxysilane; amino group-containing silane coupling agents such as phenyl-γ-aminopropyltrimethoxysilane; , Isocyanate group-containing silane such as 3-isocyanate propyltriethoxysilane And a coupling agent. The amount of the (meth) acryl-based polymer (A) to be added is not particularly limited and may be added within a range that does not impair the effect of the present invention. For example, , And it is preferable not to add it in the present invention.

또한, 본 발명의 점착제 조성물에는, 그 밖의 공지된 첨가제를 함유하고 있어도 되고, 예를 들어, 폴리프로필렌글리콜 등의 폴리알킬렌글리콜의 폴리에테르 화합물, 착색제, 안료 등의 분체, 염료, 계면 활성제, 가소제, 점착성 부여제, 표면 윤활제, 레벨링제, 연화제, 산화 방지제, 노화 방지제, 광 안정제, 자외선 흡수제, 중합 금지제, 무기 또는 유기의 충전제, 금속 분말, 입자상, 박상물 등을 사용하는 용도에 따라 적당히 첨가할 수 있다. 또, 제어할 수 있는 범위 내에서 환원제를 첨가한 레독스계를 채용해도 된다.The pressure-sensitive adhesive composition of the present invention may contain other known additives. Examples thereof include polyether compounds of polyalkylene glycols such as polypropylene glycol, powders such as colorants and pigments, dyes, surfactants, Depending on the use of plasticizers, tackifiers, surface lubricants, leveling agents, softening agents, antioxidants, anti-aging agents, light stabilizers, ultraviolet absorbers, polymerization inhibitors, inorganic or organic fillers, metal powders, particulates, It can be suitably added. Also, a redox system to which a reducing agent is added may be employed within a controllable range.

2. 편광 필름용 점착제층 2. Pressure-sensitive adhesive layer for polarizing film

본 발명의 편광 필름용 점착제층은, 상기 편광 필름용 점착제 조성물로 형성되는 것을 특징으로 한다.The pressure-sensitive adhesive layer for a polarizing film of the present invention is characterized by being formed of the pressure-sensitive adhesive composition for a polarizing film.

점착제층을 형성하는 방법으로는, 예를 들어, 상기 점착제 조성물을 박리 처리한 세퍼레이터 등에 도포하고, 중합 용제 등을 건조 제거하여 점착제층을 형성하는 방법을 들 수 있다. 또, 후술하는 편광 필름에 상기 점착제 조성물을 도포하고, 중합 용제 등을 건조 제거하여 점착제층을 편광 필름에 형성하는 방법 등에 의해 제작할 수도 있다. 또한, 점착제 조성물의 도포시에는, 적당히 중합 용제 이외의 1 종 이상의 용제를 새로 첨가해도 된다.As a method of forming the pressure-sensitive adhesive layer, there can be mentioned, for example, a method of applying the pressure-sensitive adhesive composition to a separator or the like obtained by removing the pressure-sensitive adhesive composition, and drying the polymerization solvent or the like to remove the pressure-sensitive adhesive layer. Alternatively, the pressure-sensitive adhesive composition may be applied to a polarizing film described later, and the polymerization solvent or the like may be dried to remove the pressure-sensitive adhesive layer to form a polarizing film. Further, at the time of applying the pressure-sensitive adhesive composition, at least one solvent other than the polymerization solvent may be appropriately added.

박리 처리한 세퍼레이터로는, 실리콘 박리 라이너가 바람직하게 사용된다. 이와 같은 라이너 상에 본 발명의 점착제 조성물을 도포, 건조시켜 점착제층을 형성하는 경우, 점착제를 건조시키는 방법으로는, 목적에 따라, 적당히, 적절한 방법이 채용될 수 있다. 바람직하게는 상기 도포막을 가열 건조시키는 방법이 사용된다. 가열 건조 온도는, 바람직하게는 40 ℃ ∼ 200 ℃ 이고, 더욱 바람직하게는 50 ℃ ∼ 180 ℃ 이고, 특히 바람직하게는 70 ℃ ∼ 170 ℃ 이다. 가열 온도를 상기의 범위로 함으로써, 우수한 점착 특성을 갖는 점착제를 얻을 수 있다.As the separator subjected to the peeling treatment, a silicone peel liner is preferably used. When the pressure-sensitive adhesive composition of the present invention is coated on such a liner and dried to form a pressure-sensitive adhesive layer, a suitable method may be appropriately adopted as a method of drying the pressure-sensitive adhesive, depending on the purpose. Preferably, a method of heating and drying the coating film is used. The heat drying temperature is preferably 40 to 200 캜, more preferably 50 to 180 캜, and particularly preferably 70 to 170 캜. By setting the heating temperature within the above range, a pressure-sensitive adhesive having excellent adhesive properties can be obtained.

건조 시간은, 적당히, 적절한 시간이 채용될 수 있다. 상기 건조 시간은, 바람직하게는 5 초 ∼ 20 분, 더욱 바람직하게는 5 초 ∼ 10 분, 특히 바람직하게는 10 초 ∼ 5 분이다.The drying time can be appropriately and appropriately employed. The drying time is preferably 5 seconds to 20 minutes, more preferably 5 seconds to 10 minutes, and particularly preferably 10 seconds to 5 minutes.

상기 점착제 조성물의 도포 방법으로는, 각종 방법이 사용된다. 구체적으로는, 예를 들어, 롤 코트, 키스 롤 코트, 그라비아 코트, 리버스 코트, 롤 브러시, 스프레이 코트, 딥 롤 코트, 바 코트, 나이프 코트, 에어 나이프 코트, 커튼 코트, 립 코트, 다이 코터 등에 의한 압출 코트법 등의 방법을 들 수 있다.As the method of applying the pressure-sensitive adhesive composition, various methods are used. Specific examples of the coating composition include a roll coating, a kiss roll coating, a gravure coating, a reverse coating, a roll brush, a spray coating, a dip roll coating, a bar coating, a knife coating, an air knife coating, a curtain coating, And an extrusion coating method by means of an extrusion coating method.

점착제층의 두께는, 특별히 제한되지 않고, 예를 들어, 1 ∼ 100 ㎛ 정도이다. 바람직하게는 2 ∼ 50 ㎛, 보다 바람직하게는 2 ∼ 40 ㎛ 이고, 더욱 바람직하게는 5 ∼ 35 ㎛ 이다.The thickness of the pressure-sensitive adhesive layer is not particularly limited and is, for example, about 1 to 100 mu m. Preferably 2 to 50 占 퐉, more preferably 2 to 40 占 퐉, and still more preferably 5 to 35 占 퐉.

3. 점착제층이 형성된 편광 필름 3. Polarizing film formed with a pressure-sensitive adhesive layer

본 발명의 점착제층이 형성된 편광 필름은, 편광 필름과, 당해 편광 필름에 형성된 점착제층을 갖고, The polarizing film on which the pressure-sensitive adhesive layer of the present invention is formed has a polarizing film and a pressure-sensitive adhesive layer formed on the polarizing film,

상기 편광 필름은, 편광자의 편측에만 투명 보호 필름을 갖고, 상기 점착제층은, 상기 편광자의 상기 투명 보호 필름을 갖지 않는 면에 형성되어 있고, 또한 Wherein the polarizing film has a transparent protective film only on one side of the polarizer, the pressure-sensitive adhesive layer is formed on a surface of the polarizer having no transparent protective film,

상기 점착제층이, 본 발명의 편광 필름용 점착제층인 것을 특징으로 한다.Wherein the pressure-sensitive adhesive layer is a pressure-sensitive adhesive layer for a polarizing film of the present invention.

점착제층을 형성하는 방법으로는, 상기 서술한 바와 같다.The method of forming the pressure-sensitive adhesive layer is as described above.

본 발명의 점착제층이 형성된 편광 필름은, 점착제층을 박리 처리한 세퍼레이터 등 상에 형성한 경우, 당해 세퍼레이터 상의 점착제층을 편광 필름의 투명 보호 필름을 갖지 않는 면에 전사함으로써 형성할 수 있다. 또, 편광 필름의 투명 보호 필름을 갖지 않는 면에 상기 점착제 조성물을 도포하고, 중합 용제 등을 건조 제거하여 점착제층을 편광 필름에 형성하는 방법에 의해서도 제작된다.The polarizing film on which the pressure-sensitive adhesive layer of the present invention is formed can be formed by transferring the pressure-sensitive adhesive layer on the separator to a surface of the polarizing film having no transparent protective film when the pressure-sensitive adhesive layer is formed on a separator or the like. The pressure-sensitive adhesive composition is applied to a surface of the polarizing film not having a transparent protective film, and the polymerization solvent or the like is dried to form a pressure-sensitive adhesive layer on the polarizing film.

또, 상기 편광 필름의 점착제 조성물을 도포하는 표면 (편광 필름의 투명 보호 필름을 갖지 않는 면) 에, 앵커층을 형성하거나, 코로나 처리, 플라즈마 처리 등의 각종 접착 용이 처리를 실시한 후에 점착제층을 형성할 수 있다. 또, 점착제층의 표면에는 접착 용이 처리를 실시해도 된다.Further, after an anchor layer is formed on the surface to which the pressure-sensitive adhesive composition of the polarizing film is applied (the surface having no transparent protective film of the polarizing film), or various kinds of easy adhesion treatment such as corona treatment and plasma treatment are performed, can do. The surface of the pressure-sensitive adhesive layer may be easily subjected to adhesion.

상기 점착제층이 형성된 편광 필름의 점착제층이 노출되는 경우에는, 실용에 제공될 때까지 박리 처리한 시트 (세퍼레이터) 로 점착제층을 보호해도 된다.When the pressure-sensitive adhesive layer of the polarizing film on which the pressure-sensitive adhesive layer is formed is exposed, the pressure-sensitive adhesive layer may be protected with a sheet (separator) which has been peeled off until it is provided for practical use.

세퍼레이터의 구성 재료로는, 예를 들어, 폴리에틸렌, 폴리프로필렌, 폴리에틸렌테레프탈레이트, 폴리에스테르 필름 등의 플라스틱 필름, 종이, 천, 부직포 등의 다공질 재료, 네트, 발포 시트, 금속박, 및 이들의 라미네이트체 등의 적당한 박엽체 등을 들 수 있는데, 표면 평활성이 우수한 점에서 플라스틱 필름이 바람직하게 사용된다.Examples of the constituent material of the separator include plastic films such as polyethylene, polypropylene, polyethylene terephthalate and polyester film, porous materials such as paper, cloth and nonwoven fabric, nets, foamed sheets, metal foils, And the like, and a plastic film is preferably used because of its excellent surface smoothness.

그 플라스틱 필름으로는, 상기 점착제층을 보호할 수 있는 필름이면 특별히 한정되지 않고, 예를 들어, 폴리에틸렌 필름, 폴리프로필렌 필름, 폴리부텐 필름, 폴리부타디엔 필름, 폴리메틸펜텐 필름, 폴리염화비닐필름, 염화비닐 공중합체 필름, 폴리에틸렌테레프탈레이트 필름, 폴리부틸렌테레프탈레이트 필름, 폴리우레탄 필름, 에틸렌-아세트산비닐 공중합체 필름 등을 들 수 있다.The plastic film is not particularly limited as long as it is a film capable of protecting the pressure-sensitive adhesive layer. Examples of the plastic film include a polyethylene film, a polypropylene film, a polybutene film, a polybutadiene film, a polymethylpentene film, A vinyl chloride copolymer film, a polyethylene terephthalate film, a polybutylene terephthalate film, a polyurethane film, and an ethylene-vinyl acetate copolymer film.

상기 세퍼레이터의 두께는, 통상적으로 5 ∼ 200 ㎛, 바람직하게는 5 ∼ 100 ㎛ 정도이다. 상기 세퍼레이터에는, 필요에 따라, 실리콘계, 불소계, 장사슬 알킬계 혹은 지방산 아미드계의 이형제, 실리카분 (粉) 등에 의한 이형 및 방오 처리나, 도포형, 혼련형, 증착형 등의 대전 방지 처리를 할 수도 있다. 특히, 상기 세퍼레이터의 표면에 실리콘 처리, 장사슬 알킬 처리, 불소 처리 등의 박리 처리를 적당히 실시함으로써, 상기 점착제층으로부터의 박리성을 보다 높일 수 있다.The thickness of the separator is usually 5 to 200 占 퐉, preferably 5 to 100 占 퐉. If necessary, the separator may be subjected to antistatic treatment such as release and antifouling treatment with silicone, fluorine, long chain alkyl or fatty acid amide type releasing agent, silica powder or the like, coating type, kneading type, You may. Particularly, the releasability from the pressure-sensitive adhesive layer can be further improved by suitably carrying out the surface treatment of the separator, such as silicone treatment, long-chain alkyl treatment or fluorine treatment.

또한, 상기의 점착제층이 형성된 편광 필름의 제작시에 사용한, 박리 처리한 시트는, 그대로 점착제층이 형성된 편광 필름의 세퍼레이터로서 사용할 수 있고, 공정면에 있어서의 간략화를 할 수 있다.Further, the peeled sheet used in the production of the polarizing film having the above-mentioned pressure-sensitive adhesive layer can be used as a separator of a polarizing film in which a pressure-sensitive adhesive layer is formed as it is.

편광 필름은, 편광자의 편측에만 투명 보호 필름을 갖는 것이 사용된다.The polarizing film has a transparent protective film only on one side of the polarizer.

편광자는, 특별히 한정되지 않고, 각종의 것을 사용할 수 있다. 편광자로는, 예를 들어, 폴리비닐알코올계 필름, 부분 포르말화 폴리비닐알코올계 필름, 에틸렌·아세트산비닐 공중합체계 부분 비누화 필름 등의 친수성 고분자 필름에, 요오드나 이색성 염료의 이색성 물질을 흡착시켜 1 축 연신한 것, 폴리비닐알코올의 탈수 처리물이나 폴리염화비닐의 탈염산 처리물 등 폴리엔계 배향 필름 등을 들 수 있다. 이들 중에서도, 폴리비닐알코올계 필름과 요오드 등의 이색성 물질로 이루어지는 편광자가 바람직하고, 요오드 및/또는 요오드 이온을 함유하는 요오드계 편광자가 보다 바람직하다. 또, 이들의 편광자의 두께는 특별히 제한되지 않지만, 일반적으로 5 ∼ 80 ㎛ 정도이다.The polarizer is not particularly limited, and various kinds of polarizers can be used. Examples of the polarizer include a hydrophilic polymer film such as a polyvinyl alcohol film, a partially porous polyvinyl alcohol film, and a partially saponified ethylene / vinyl acetate copolymer film, And polyene-based oriented films such as polyvinyl alcohol dehydrated products and polyvinyl chloride dehydrochloric acid treated products. Among them, a polyvinyl alcohol film and a polarizer made of a dichroic substance such as iodine are preferable, and an iodine polarizer containing iodine and / or iodine ion is more preferable. The thickness of these polarizers is not particularly limited, but is generally about 5 to 80 占 퐉.

폴리비닐알코올계 필름을 요오드로 염색하여 1 축 연신한 편광자는, 예를 들어, 폴리비닐알코올을 요오드의 수용액에 침지시킴으로써 염색하고, 원래 길이의 3 ∼ 7 배로 연신함으로써 제작할 수 있다. 필요에 따라 붕산이나 황산아연, 염화아연 등을 함유하고 있어도 되는 요오드화칼륨 등의 수용액에 침지시킬 수도 있다. 또한, 필요에 따라 염색 전에 폴리비닐알코올계 필름을 물에 침지시켜 수세해도 된다. 폴리비닐알코올계 필름을 수세함으로써 폴리비닐알코올계 필름 표면의 오염물이나 블로킹 방지제를 세정할 수 있는 것 외에, 폴리비닐알코올계 필름을 팽윤시킴으로써 염색의 얼룩 등의 불균일을 방지하는 효과도 있다. 연신은 요오드로 염색한 후에 실시해도 되고, 염색하면서 연신해도 되고, 또 연신하고 나서 요오드로 염색해도 된다. 붕산이나 요오드화칼륨 등의 수용액이나 수욕 중이어도 연신할 수 있다.A polarizer obtained by dying a polyvinyl alcohol film with iodine and uniaxially stretching can be produced, for example, by dying polyvinyl alcohol in an aqueous solution of iodine and stretching it to 3 to 7 times its original length. If necessary, may be immersed in an aqueous solution such as potassium iodide, which may contain boric acid, zinc sulfate, zinc chloride or the like. If necessary, the polyvinyl alcohol film may be dipped in water and washed with water before dyeing. The polyvinyl alcohol film is washed with water to clean the contaminants and the antiblocking agent on the surface of the polyvinyl alcohol film, and the polyvinyl alcohol film is swollen to prevent unevenness such as uneven dyeing. The stretching may be carried out after dyeing with iodine, followed by stretching while dyeing, or after stretching, followed by dyeing with iodine. It can be stretched even in an aqueous solution such as boric acid or potassium iodide or in a water bath.

또, 본 발명에 있어서는, 두께가 10 ㎛ 이하인 박형 편광자도 사용할 수 있다. 박형화의 관점에서 말하면 당해 두께는 1 ∼ 7 ㎛ 인 것이 바람직하다. 이와 같은 박형의 편광자는, 두께 불균일이 적고, 시인성이 우수하고, 또 치수 변화가 적기 때문에 내구성이 우수하고, 나아가서는 편광 필름으로서의 두께도 박형화를 도모할 수 있는 점이 바람직하다.In the present invention, a thin polarizer having a thickness of 10 m or less can also be used. From the viewpoint of thinning, the thickness is preferably 1 to 7 mu m. Such a thin polarizer is preferable because it is excellent in durability because thickness irregularity is small, visibility is excellent, and dimensional change is small, and further thickness and thickness of a polarizing film can be achieved.

박형의 편광자로는, 대표적으로는, 일본 공개특허공보 소51-069644호나 일본 공개특허공보 2000-338329호나, 국제 공개 제2010/100917호 팜플렛, 국제 공개 제2010/100917호 팜플렛, 또는 일본 특허 제4751481호 명세서나 일본 공개특허공보 2012-073563호에 기재되어 있는 박형 편광막을 들 수 있다. 이들 박형 편광막은, 폴리비닐알코올계 수지 (이하, PVA 계 수지라고도 한다) 층과 연신용 수지 기재를 적층체의 상태에서 연신하는 공정과 염색하는 공정을 포함하는 제법에 의해 얻을 수 있다. 이 제법이면, PVA 계 수지층이 얇아도, 연신용 수지 기재에 지지되어 있음으로써 연신에 의한 파단 등의 문제없이 연신하는 것이 가능해진다.Typical examples of the thin polarizer include those disclosed in Japanese Laid-Open Patent Publication Nos. 51-069644 and 2000-338329, International Publication No. 2010/100917, International Publication No. 2010/100917, And a thin polarizing film described in JP-A-4751481 or in JP-A-2012-073563. These thin polarizing films can be obtained by a process comprising a step of stretching a layer of a polyvinyl alcohol resin (hereinafter also referred to as a PVA resin) and a lead resin base material in the form of a laminate, and a step of dyeing. With this method, even if the PVA resin layer is thin, it can be stretched without any problem such as breakage due to stretching because it is supported on the resin base material for drawing.

상기 박형 편광막으로는, 적층체의 상태에서 연신하는 공정과 염색하는 공정을 포함하는 제법 중에서도, 고배율로 연신할 수 있어 편광 성능을 향상시킬 수 있는 점에서, 국제 공개 제2010/100917호 팜플렛, 국제 공개 제2010/100917호 팜플렛, 또는 일본 특허 제4751481호 명세서나 일본 공개특허공보 2012-073563호에 기재가 있는 바와 같은 붕산 수용액 중에서 연신하는 공정을 포함하는 제법으로 얻어지는 것이 바람직하고, 특히 일본 특허 제4751481호 명세서나 일본 공개특허공보 2012-073563호에 기재가 있는 붕산 수용액 중에서 연신하기 전에 보조적으로 공중 연신하는 공정을 포함하는 제법에 의해 얻어지는 것이 바람직하다.As the thin polarizing film, in view of being capable of stretching at a high magnification and improving the polarization performance even in the process including a step of stretching in the state of a laminate and a step of dyeing, in the pamphlet of International Publication No. 2010/100917, In the aqueous solution of boric acid as described in the specification of International Patent Publication No. 2010/100917 or the specification of Japanese Patent No. 4751481 or the Japanese Patent Application Publication No. 2012-073563, It is preferably obtained by a process including a step of auxiliary drawing publicly before drawing in an aqueous solution of boric acid as described in Japanese Patent No. 4751481 or in Japanese Patent Application Laid-Open No. 2012-073563.

투명 보호 필름을 구성하는 재료로는, 예를 들어 투명성, 기계적 강도, 열 안정성, 수분 차단성, 등방성 등이 우수한 열가소성 수지가 사용된다. 이와 같은 열가소성 수지의 구체예로는, 트리아세틸셀룰로오스 등의 셀룰로오스 수지, 폴리에스테르 수지, 폴리에테르술폰 수지, 폴리술폰 수지, 폴리카보네이트 수지, 폴리아미드 수지, 폴리이미드 수지, 폴리올레핀 수지, (메트)아크릴 수지, 고리형 폴리올레핀 수지 (노르보르넨계 수지), 폴리아릴레이트 수지, 폴리스티렌 수지, 폴리비닐알코올 수지, 및 이들의 혼합물을 들 수 있다. 투명 보호 필름 중에는 임의의 적절한 첨가제가 1 종류 이상 함유되어 있어도 된다. 첨가제로는, 예를 들어, 자외선 흡수제, 산화 방지제, 활제, 가소제, 이형제, 착색 방지제, 난연제, 핵제, 대전 방지제, 안료, 착색제 등을 들 수 있다. 투명 보호 필름 중의 상기 열가소성 수지의 함유량은, 바람직하게는 50 ∼ 100 중량％, 보다 바람직하게는 50 ∼ 99 중량％, 더욱 바람직하게는 60 ∼ 98 중량％, 특히 바람직하게는 70 ∼ 97 중량％ 이다. 투명 보호 필름 중의 상기 열가소성 수지의 함유량이 50 중량％ 이하인 경우, 열가소성 수지가 본래 갖는 고투명성 등을 충분히 발현할 수 없을 우려가 있다.As a material constituting the transparent protective film, for example, a thermoplastic resin excellent in transparency, mechanical strength, thermal stability, moisture barrier property, isotropy and the like is used. Specific examples of such a thermoplastic resin include cellulose resin such as triacetyl cellulose, polyester resin, polyethersulfone resin, polysulfone resin, polycarbonate resin, polyamide resin, polyimide resin, polyolefin resin, (meth) acryl Resin, cyclic polyolefin resin (norbornene resin), polyarylate resin, polystyrene resin, polyvinyl alcohol resin, and mixtures thereof. The transparent protective film may contain one or more optional additives. Examples of the additive include ultraviolet absorbers, antioxidants, lubricants, plasticizers, mold release agents, coloring inhibitors, flame retardants, nucleating agents, antistatic agents, pigments, colorants and the like. The content of the thermoplastic resin in the transparent protective film is preferably 50 to 100% by weight, more preferably 50 to 99% by weight, still more preferably 60 to 98% by weight, particularly preferably 70 to 97% by weight . When the content of the thermoplastic resin in the transparent protective film is 50% by weight or less, there is a possibility that the high transparency and the like inherently possessed by the thermoplastic resin can not be sufficiently exhibited.

상기 편광자의 편측에는, 투명 보호 필름이 접착제층에 의해 첩합 (貼合) 된다. 편광자와 투명 보호 필름의 접착 처리에는, 접착제가 사용된다. 접착제로는, 이소시아네이트계 접착제, 폴리비닐알코올계 접착제, 젤라틴계 접착제, 비닐계 라텍스계, 수계 폴리에스테르 등을 예시할 수 있다. 상기 접착제는, 통상적으로 수용액으로 이루어지는 접착제로서 사용되고, 통상적으로 0.5 ∼ 60 중량％ 의 고형분을 함유하여 이루어진다. 상기 외에, 편광자와 투명 보호 필름의 접착제로는, 자외 경화형 접착제, 전자선 경화형 접착제 등을 들 수 있다. 전자선 경화형 편광 필름용 접착제는, 상기 각종의 투명 보호 필름에 대해, 바람직한 접착성을 나타낸다. 또 본 발명에서 사용하는 접착제에는, 금속 화합물 필러를 함유시킬 수 있다.On one side of the polarizer, a transparent protective film is bonded by an adhesive layer. An adhesive is used for the adhesion treatment of the polarizer and the transparent protective film. Examples of the adhesive include an isocyanate-based adhesive, a polyvinyl alcohol-based adhesive, a gelatin-based adhesive, a vinyl-based latex-based, water-based polyester, and the like. The adhesive is usually used as an adhesive comprising an aqueous solution, and usually contains 0.5 to 60% by weight of a solid content. In addition to the above, examples of the adhesive for the polarizer and the transparent protective film include an ultraviolet curable adhesive, an electron beam curable adhesive, and the like. The adhesive for an electron beam curing type polarizing film exhibits preferable adhesiveness to the various transparent protective films. The adhesive used in the present invention may contain a metal compound filler.

3. 화상 표시 장치 3. Image display device

본 발명은, 상기 점착제층이 형성된 편광 필름을 적어도 1 개 사용한 것을 특징으로 하는 화상 표시 장치에 관한 것이다.The present invention relates to an image display apparatus using at least one polarizing film on which the above-mentioned pressure-sensitive adhesive layer is formed.

본 발명의 점착제층이 형성된 편광 필름은, 액정 표시 장치 등의 각종 화상 표시 장치의 형성 등에 바람직하게 사용할 수 있다. 액정 표시 장치의 형성은, 종래에 준하여 실시할 수 있다. 즉 액정 표시 장치는 일반적으로, 액정 셀 등의 표시 패널과 점착제층이 형성된 편광 필름, 및 필요에 따른 조명 시스템 등의 구성 부품을 적당히 조립하여 구동 회로를 삽입하는 것 등에 의해 형성되는데, 본 발명에 있어서는 본 발명에 의한 점착제층이 형성된 편광 필름을 사용하는 점을 제외하고 특별히 한정은 없고, 종래에 준할 수 있다. 액정 셀에 대해서도, 예를 들어 TN 형이나 STN 형, π 형, VA 형, IPS 형 등의 임의의 타입의 것을 사용할 수 있다.The polarizing film on which the pressure-sensitive adhesive layer of the present invention is formed can be suitably used for the formation of various image display devices such as a liquid crystal display device. The formation of the liquid crystal display device can be carried out conventionally. That is, the liquid crystal display device is generally formed by appropriately assembling components such as a display panel such as a liquid crystal cell, a polarizing film on which a pressure-sensitive adhesive layer is formed, and an illumination system as required, and inserting a driving circuit. Except for using a polarizing film in which the pressure-sensitive adhesive layer according to the present invention is formed, there is no particular limitation, and it can be applied conventionally. As for the liquid crystal cell, any type of TN type, STN type, pi type, VA type, IPS type or the like can be used, for example.

액정 셀 등의 표시 패널의 편측 또는 양측에 점착제층이 형성된 편광 필름을 배치한 액정 표시 장치나, 조명 시스템에 백라이트 혹은 반사판을 사용한 것 등의 적당한 액정 표시 장치를 형성할 수 있다. 그 경우, 본 발명에 의한 점착제층이 형성된 편광 필름은 액정 셀 등의 표시 패널의 편측 또는 양측에 설치할 수 있다. 양측에 광학 필름을 형성하는 경우, 그것들은 동일한 것이어도 되고, 상이한 것이어도 된다. 또한, 액정 표시 장치의 형성시에는, 예를 들어 확산층, 안티글레어층, 반사 방지막, 보호판, 프리즘 어레이, 렌즈 어레이 시트, 광확산 시트, 백라이트 등의 적당한 부품을 적당한 위치에 1 층 또는 2 층 이상 배치할 수 있다.It is possible to form a suitable liquid crystal display device such as a liquid crystal display device in which a polarizing film having a pressure-sensitive adhesive layer formed on one side or both sides of a display panel such as a liquid crystal cell is arranged, or a backlight or a reflector is used for the illumination system. In this case, the polarizing film on which the pressure-sensitive adhesive layer according to the present invention is formed can be provided on one side or both sides of a display panel such as a liquid crystal cell. When the optical films are formed on both sides, they may be the same or different. In forming the liquid crystal display device, a suitable part such as a diffusion layer, an anti-glare layer, an antireflection film, a protective plate, a prism array, a lens array sheet, a light diffusion sheet, a backlight, Can be deployed.

실시예Example

이하에, 실시예에 의해 본 발명을 구체적으로 설명하는데, 본 발명은 이들 실시예에 의해 한정되는 것은 아니다. 또한, 각 예 중의 부 및 ％ 는 모두 중량 기준이다. 이하에 특별히 규정이 없는 실온 방치 조건은 모두 23 ℃ 65 ％ RH 이다.Hereinafter, the present invention will be described in detail by way of examples, but the present invention is not limited to these examples. In the examples, all parts and% are based on weight. The room temperature leaving conditions, which are not specifically defined below, are all 23 deg. C and 65% RH.

제조예 1 (아크릴계 폴리머 (A-1) 의 조제) Production Example 1 (Preparation of acrylic polymer (A-1)) [

교반 날개, 온도계, 질소 가스 도입관, 냉각기를 구비한 4 구 플라스크에, 부틸아크릴레이트 99 부 및 아크릴산4-하이드록시부틸 1 부를 함유하는 모노머 혼합물을 주입하였다. 또한, 상기 모노머 혼합물 (고형분) 100 부에 대해, 중합 개시제로서 2,2'-아조비스이소부티로니트릴 0.1 부를 아세트산에틸과 함께 주입하고, 완만하게 교반하면서 질소 가스를 도입하여 질소 치환한 후, 플라스크 내의 액온을 60 ℃ 부근으로 유지하며 7 시간 중합 반응을 실시하였다. 그 후, 얻어진 반응액에 아세트산에틸을 첨가하여, 고형분 농도 30 ％ 로 조정한, 중량 평균 분자량 140 만의 아크릴계 폴리머 (A-1) 의 용액을 조제하였다.A four-necked flask equipped with a stirrer, a thermometer, a nitrogen gas introducing tube and a condenser was charged with a monomer mixture containing 99 parts of butyl acrylate and 1 part of 4-hydroxybutyl acrylate. Further, 0.1 part of 2,2'-azobisisobutyronitrile as a polymerization initiator was poured into 100 parts of the monomer mixture (solid content) together with ethyl acetate, and nitrogen gas was introduced with gentle stirring to perform nitrogen substitution, The polymerization reaction was carried out for 7 hours while maintaining the liquid temperature in the flask at around 60 캜. Thereafter, ethyl acetate was added to the obtained reaction solution to prepare a solution of an acrylic polymer (A-1) having a weight average molecular weight of 1,400, adjusted to a solid concentration of 30%.

얻어진 (메트)아크릴계 폴리머 (A) 의 중량 평균 분자량은, 이하의 방법에 의해 측정하였다.The weight average molecular weight of the obtained (meth) acryl-based polymer (A) was measured by the following method.

＜(메트)아크릴계 폴리머 (A) 의 중량 평균 분자량의 측정＞ <Measurement of weight average molecular weight of (meth) acryl-based polymer (A)

(메트)아크릴계 폴리머 (A) 의 중량 평균 분자량은, GPC (겔·퍼미에이션·크로마토그래피) 에 의해 측정하였다.The weight average molecular weight of the (meth) acrylic polymer (A) was measured by GPC (gel permeation chromatography).

·분석 장치 : 토소사 제조, HLC-8120GPC Analytical Apparatus: manufactured by Toso Co., Ltd., HLC-8120GPC

·칼럼 : 토소사 제조, G7000HXL ＋ GMHXL ＋ GMHXL Column: manufactured by Toso Co., Ltd. G7000H XL + GMH XL + GMH XL

·칼럼 사이즈 : 각 7.8 ㎜φ × 30 ㎝ 합계 90 ㎝ · Column size: Each 7.8 mmφ × 30 cm Total 90 cm

·칼럼 온도 : 40 ℃ Column temperature: 40 ° C

·유량 : 0.8 ㎖/min Flow rate: 0.8 ml / min

·주입량 : 100 ㎕ · Injection volume: 100 μl

·용리액 : 테트라하이드로푸란 Eluent: tetrahydrofuran

·검출기 : 시차굴절계 (RI) Detector: Differential refractometer (RI)

·표준 시료 : 폴리스티렌· Standard sample: Polystyrene

제조예 2 (박형 편광 필름의 제작) Production Example 2 (Production of thin polarizing film)

박형 편광층을 제작하기 위하여, 먼저, 비정성 PET 기재에 9 ㎛ 두께의 PVA 층이 제막된 적층체를 연신 온도 130 ℃ 의 공중 보조 연신에 의해 연신 적층체를 생성하고, 다음으로, 연신 적층체를 염색에 의해 착색 적층체를 생성하고, 추가로 착색 적층체를 연신 온도 65 ℃ 의 붕산 수중 연신에 의해 총 연신 배율이 5.94 배가 되도록 비정성 PET 기재와 일체로 연신된 4 ㎛ 두께의 PVA 층을 포함하는 광학 필름 적층체를 생성하였다. 이와 같은 2 단 연신에 의해 비정성 PET 기재에 제막된 PVA 층의 PVA 분자가 고차로 배향되고, 염색에 의해 흡착된 요오드가 폴리요오드 이온 착물로서 일방향으로 고차로 배향된 고기능 편광층을 구성하는, 두께 4 ㎛ 의 PVA 층을 포함하는 광학 필름 적층체를 생성할 수 있었다. 또한, 당해 광학 필름 적층체의 편광층의 표면에 폴리비닐알코올계 접착제를 도포하면서, 비누화 처리한 40 ㎛ 두께의 트리아세틸셀룰로오스 필름을 첩합시킨 후, 비정성 PET 기재를 박리하여, 박형 편광층을 사용한 박형 편광 필름을 제작하였다.In order to produce a thin polarizing layer, first, a laminate having a PVA layer with a thickness of 9 占 퐉 formed on an amorphous PET substrate was subjected to air-assisted stretching at a stretching temperature of 130 占 폚 to form a stretched laminate, To obtain a colored layered product. Further, the colored layered product was stretched in boric acid aqueous solution having a stretching temperature of 65 占 폚 to give a PVA layer having a thickness of 4 占 퐉 which was integrally stretched with the amorphous PET substrate so as to have a total draw ratio of 5.94. To produce an optical film laminate. PVA molecules of the PVA layer formed on the amorphous PET substrate are oriented at a high degree by such two-step stretching, and iodine adsorbed by dyeing constitutes a highly functional polarizing layer oriented in one direction as a polyiodide ion complex, An optical film laminate including a PVA layer having a thickness of 4 占 퐉 could be produced. Further, a saponified triacetylcellulose film having a thickness of 40 탆 was applied to the surface of the polarizing layer of the optical film laminate while applying a polyvinyl alcohol adhesive, and then the amorphous PET substrate was peeled off to form a thin polarizing layer To prepare a thin polarizing film.

실시예 1Example 1

(점착제 조성물의 조제)(Preparation of pressure-sensitive adhesive composition)

제조예 1 에서 얻어진 아크릴계 폴리머 (A-1) 용액의 고형분 100 부에 대해, 오늄-아니온염 (B1) 로서, 에틸메틸피롤리디늄-비스(트리플루오로메탄술포닐)이미드 (토쿄 화성 공업 (주) 제조) 0.7 부, 알칼리 금속염 (B2) 로서, 리튬비스(트리플루오로메탄술포닐)이미드 (미츠비시머티리얼 전자 화성 (주) 제조) 1 부를 배합하고, 또한 가교제 (D) 로서, 트리메틸올프로판자일릴렌디이소시아네이트 (상품명 : 타케네이트 D110N, 미츠이 화학 (주) 제조) 0.095 부와, 디벤조일퍼옥사이드 (상품명 : 나이파 BMT40SV, 닛폰 유지 (주) 제조) 0.3 부, 티올계 실란 커플링제 (C1) 로서, 메틸기 및 메르캅토기 함유 알콕시실릴 수지 (상품명 : X-41-1810, 신에츠 화학 공업 (주) 제조) 0.2 부, 아세토아세틸기 함유 실란 커플링제 (C2) 로서, 아세토아세틸기 함유 실란 커플링제 (상품명 : A-100, 소켄 화학 (주) 제조) 0.2 부를 배합하여, 아크릴계 점착제 용액을 조제하였다.(Trifluoromethanesulfonyl) imide (commercially available from Tokyo Chemical Industry Co., Ltd.) as an onium-anion salt (B1), based on 100 parts of the solid content of the acrylic polymer (A- 1 part of lithium bis (trifluoromethanesulfonyl) imide (manufactured by Mitsubishi Materials Electronics Co., Ltd.) was used as the alkali metal salt (B2), and as the cross-linking agent (D) , 0.095 part of olpropanediyl xylene diisocyanate (trade name: Takenate D110N, manufactured by Mitsui Chemicals, Inc.), 0.3 part of dibenzoyl peroxide (trade name: Naipa BMT40SV, manufactured by Nippon Oil and Fats Co., Ltd.) 0.2 part of an alkoxysilyl resin containing a methyl group and a mercapto group (trade name: X-41-1810, Shin-Etsu Chemical Co., Ltd.) as the silane coupling agent (C1) Silane coupling agent (trade name: A-100, Soken 0.2 part) were blended to prepare an acrylic pressure-sensitive adhesive solution.

(점착제층이 형성된 편광 필름의 제작)(Production of a polarizing film having a pressure-sensitive adhesive layer)

이어서, 상기 아크릴계 점착제 용액을, 실리콘계 박리제로 처리된 폴리에틸렌테레프탈레이트 필름 (세퍼레이터 필름) 의 표면에, 파운틴 코터로 균일하게 도공하고, 155 ℃ 의 공기 순환식 항온 오븐에서 2 분간 건조시켜, 세퍼레이터 필름의 표면에 두께 20 ㎛ 의 점착제층을 형성하였다. 이어서, 제조예 2 에서 제작한 박형 편광 필름의 편광자의 편광층의 측에, 세퍼레이터 필름 상에 형성한 점착제층을 전사하여, 점착제층이 형성된 편광 필름을 제작하였다.Subsequently, the acrylic pressure-sensitive adhesive solution was uniformly coated on the surface of a polyethylene terephthalate film (separator film) treated with a silicone-based releasing agent with a fountain coater and dried in an air circulating thermostat oven at 155 ° C for 2 minutes to obtain a separator film A pressure-sensitive adhesive layer having a thickness of 20 mu m was formed on the surface. Subsequently, the pressure-sensitive adhesive layer formed on the separator film was transferred to the side of the polarizing layer of the polarizer of the thin polarizing film produced in Production Example 2 to prepare a polarizing film having the pressure-sensitive adhesive layer.

실시예 2 ∼ 10, 비교예 1 ∼ 11Examples 2 to 10 and Comparative Examples 1 to 11

실시예 1 에 있어서, 점착제 조성물의 조제시에, 오늄-아니온염 (B1), 알칼리 금속염 (B2) 의 첨가량, 및 실란 커플링제의 종류와 그 첨가량을 표 1 에 나타내는 바와 같이 바꾼 것 이외에는, 실시예 1 과 마찬가지로 하여, 점착제층이 형성된 편광 필름을 제작하였다.Except that the amount of the onium salt-anion salt (B1), the amount of the alkali metal salt (B2), the kind of the silane coupling agent and the amount of the silane coupling agent and the addition amount thereof were changed as shown in Table 1 in the preparation of the pressure-sensitive adhesive composition in Example 1 In the same manner as in Example 1, a polarizing film having a pressure-sensitive adhesive layer was produced.

상기 실시예 및 비교예에서 얻어진, 점착제층이 형성된 편광 필름에 대해 이하의 평가를 실시하였다. 평가 결과를 표 1 에 나타낸다.The following evaluations were performed on the polarizing films on which the pressure-sensitive adhesive layer was formed, obtained in the above-mentioned Examples and Comparative Examples. The evaluation results are shown in Table 1.

＜표면 저항값＞ <Surface resistance value>

실시예, 비교예에서 얻어진 점착제층이 형성된 편광 필름의 세퍼레이터 필름을 박리한 후, 점착제 표면의 표면 저항값 (Ω/□) 을 (주) 미츠비시 화학 애널리텍 제조, MCP-HT450 을 사용하여 측정하였다. 표면 저항값은, 1.0 × 1011 Ω/□ 미만인 것이 바람직하고, 9.0 × 1010 Ω/□ 이하인 것이 바람직하고, 5.0 × 1010 Ω/□ 이하인 것이 보다 바람직하다.After peeling off the separator film of the polarizing film on which the pressure-sensitive adhesive layer obtained in Examples and Comparative Examples was formed, the surface resistance value (Ω / □) of the pressure-sensitive adhesive surface was measured using MCP-HT450 manufactured by Mitsubishi Chemical Analytec Co., . The surface resistance value is preferably less than 1.0 x 10 11 ? /?, More preferably not more than 9.0 x 10 10 ? / ?, and most preferably not more than 5.0 x 10 10 ? /.

＜액정 패널의 백색 소실 시간＞ &Lt; Time of white color disappearance of liquid crystal panel &

실시예, 비교예에서 얻어진 점착제층이 형성된 편광 필름을 100 ㎜ × 100 ㎜ 의 크기로 절단하고, 액정 패널에 첩부하였다. 이 패널을 10000 cd 의 휘도를 갖는 백라이트 상에 두고, 정전기 발생 장치인 ESD (ESD-8012A, SANKI 사 제조) 를 사용하여, 5 ㎸, 15 ㎸ 의 정전기를 발생시킴으로써 액정의 배향 흐트러짐을 일으켰다. 그 배향 불량에 의한 표시 불량의 회복 시간 (초) 을, 순간 멀티 측광 검출기 (MCPD-3000, 오츠카 전자 (주) 제조) 를 사용하여 측정하였다. 표시 불량의 회복 시간은, 5 ㎸, 15 ㎸ 의 어느 경우에도 10 초 이하인 것이 바람직하고, 5 초 이하인 것이 보다 바람직하다.The polarizing film on which the pressure-sensitive adhesive layer obtained in the examples and comparative examples were formed was cut into a size of 100 mm x 100 mm and attached to the liquid crystal panel. This panel was placed on a backlight having a luminance of 10,000 cd, and static electricity of 5 kV and 15 kV was generated by using an ESD (ESD-8012A, manufactured by SANKI), which is a static electricity generator, to cause alignment disorder of the liquid crystal. The recovery time (sec) of display failure due to the orientation failure was measured using an instantaneous multi-photometer detector (MCPD-3000, manufactured by Otsuka Electronics Co., Ltd.). The recovery time of the defective display is preferably 10 seconds or less in all cases of 5 kV and 15 kV, and more preferably 5 seconds or less.

＜접착 내구성＞<Bonding durability>

실시예, 비교예에서 얻어진 점착제층이 형성된 편광 필름의 세퍼레이터 필름을 박리하고, 두께 0.7 ㎜ 의 무알칼리 유리 (코닝사 제조, 1737) 에 라미네이터를 사용하여 첩착하였다. 이어서, 50 ℃, 5 atm 에서, 15 분간의 오토클레이브 처리를 실시하여, 상기 점착제층이 형성된 편광 필름을 완전히 무알칼리 유리에 밀착시켰다. 이어서, 이것을, 85 ℃ 의 가열 오븐 (가열) 및 60 ℃/95 ％ RH 의 항온항습기 (가습) 의 조건 하에 각각 투입하여, 500 시간 후의 편광 필름의 박리의 유무를, 하기 기준으로 평가하였다. 또, 상기 무알칼리 유리를 ITO 유리 (상품명 : IT20-N-ES160-60, 지오마텍 (주) 제조) 로 변경하고, 마찬가지의 평가를 실시하였다.The separator film of the polarizing film on which the pressure-sensitive adhesive layer obtained in the Example and Comparative Example was formed was peeled off and adhered to a 0.7-mm-thick non-alkali glass (Corning 1737) using a laminator. Subsequently, the autoclave treatment was carried out at 50 DEG C and 5 atm for 15 minutes to adhere the polarizing film having the pressure-sensitive adhesive layer formed thereon to the completely alkali-free glass. Subsequently, this was put under the conditions of a heating oven (heating) of 85 캜 and a constant-temperature and humidity (humidification) condition of 60 캜 / 95% RH, and the presence or absence of peeling of the polarizing film after 500 hours was evaluated by the following criteria. Further, the above-mentioned alkali-free glass was changed to ITO glass (trade name: IT20-N-ES160-60, manufactured by Geomatec Co., Ltd.) and evaluated in the same manner.

◎ : 전혀 박리가 관찰되지 않았다.?: No peeling was observed at all.

○ : 육안으로는 확인할 수 없을 정도의 박리가 관찰되었다.○: Detachment was observed to the extent that it could not be confirmed by the naked eye.

△ : 육안으로 확인할 수 있는 작은 박리가 관찰되었다.?: Small peeling was observed, which can be confirmed by naked eyes.

× : 분명한 박리가 관찰되었다.X: Apparent peeling was observed.

＜외관＞<Appearance>

실시예, 비교예에서 얻어진 점착제층이 형성된 편광 필름에 대해, 육안으로 결정의 석출의 유무를 확인하고, 이하의 평가 기준으로 평가하였다. 평가 결과를 표 1 에 나타낸다.The polarizing films on which the pressure-sensitive adhesive layers obtained in the examples and comparative examples were formed were visually observed for the presence or absence of precipitation of crystals and evaluated according to the following evaluation criteria. The evaluation results are shown in Table 1.

○ : 결정의 석출이 관찰되지 않았다.?: No precipitation of crystals was observed.

× : 결정이 석출되어 있는 것이 관찰되었다.X: It was observed that crystals were precipitated.

Figure pct00001
Figure pct00001

표 1 중, In Table 1,

(C2) 는, 아세토아세틸기 함유 실란 커플링제 (상품명 : A-100, 소켄 화학 (주) 제조), (C2) is a silane coupling agent containing an acetoacetyl group (trade name: A-100, manufactured by Soken Chemical & Engineering Co., Ltd.)

(C3) 은, γ-글리시독시프로필메톡시실란 (상품명 : KBM-403, 신에츠 화학 공업 (주) 제조), (C3) is a copolymer of γ-glycidoxypropylmethoxysilane (trade name: KBM-403, Shin-Etsu Chemical Co., Ltd.)

(C4) 는, 에폭시기 함유 실란 커플링제 (상품명 : X-41-1056, 신에츠 화학 공업 (주) 제조) 를 나타낸다. (C4) represents an epoxy group-containing silane coupling agent (trade name: X-41-1056, Shin-Etsu Chemical Co., Ltd.).

Claims (12)

(메트)아크릴계 폴리머 (A), 오늄-아니온염 (B1), 알칼리 금속염 (B2) 를 함유하고,
상기 알칼리 금속염 (B2) 는, 상기 (메트)아크릴계 폴리머 (A) 100 중량부에 대해, 0.4 ∼ 3.5 중량부 함유하고,
상기 알칼리 금속염 (B2) 와 오늄-아니온염 (B1) 의 중량비 (B2/B1) 가, 1.2 ∼ 4 인 것을 특징으로 하는 편광 필름용 점착제 조성물.(Meth) acryl-based polymer (A), an onium-anionite (B1), and an alkali metal salt (B2)
The alkali metal salt (B2) is contained in an amount of 0.4 to 3.5 parts by weight based on 100 parts by weight of the (meth) acrylic polymer (A)
Wherein the weight ratio (B2 / B1) of the alkali metal salt (B2) to the onium salt-anionic salt (B1) is 1.2 to 4. 제 1 항에 있어서,
추가로, 티올계 실란 커플링제 (C1) 을 함유하는 것을 특징으로 하는 편광 필름용 점착제 조성물.The method according to claim 1,
A pressure-sensitive adhesive composition for a polarizing film, further comprising a thiol-based silane coupling agent (C1). 제 2 항에 있어서,
상기 티올계 실란 커플링제 (C1) 은, 상기 (메트)아크릴계 폴리머 (A) 100 중량부에 대해, 0.001 ∼ 5 중량부인 것을 특징으로 하는 편광 필름용 점착제 조성물.3. The method of claim 2,
Wherein the thiol-based silane coupling agent (C1) is used in an amount of 0.001 to 5 parts by weight based on 100 parts by weight of the (meth) acryl-based polymer (A). 제 1 항 내지 제 3 항 중 어느 한 항에 있어서,
상기 오늄-아니온염 (B1) 은, 상기 (메트)아크릴계 폴리머 (A) 100 중량부에 대해, 0.1 ∼ 1.5 중량부인 것을 특징으로 하는 편광 필름용 점착제 조성물.4. The method according to any one of claims 1 to 3,
Wherein the onium salt of an onium salt (B1) is 0.1 to 1.5 parts by weight based on 100 parts by weight of the (meth) acrylic polymer (A). 제 1 항 내지 제 4 항 중 어느 한 항에 있어서,
추가로, 가교제 (D) 를 함유하는 것을 특징으로 하는 편광 필름용 점착제 조성물.5. The method according to any one of claims 1 to 4,
The pressure-sensitive adhesive composition for a polarizing film, further comprising a cross-linking agent (D). 제 5 항에 있어서,
상기 가교제 (D) 는, (메트)아크릴계 폴리머 (A) 100 중량부에 대해, 0.01 ∼ 20 중량부 함유하는 것을 특징으로 하는 편광 필름용 점착제 조성물.6. The method of claim 5,
The pressure-sensitive adhesive composition for a polarizing film, wherein the crosslinking agent (D) is contained in an amount of 0.01 to 20 parts by weight based on 100 parts by weight of the (meth) acryl-based polymer (A). 제 5 항 또는 제 6 항에 있어서,
상기 가교제 (D) 가, 이소시아네이트계 화합물, 및 과산화물로 이루어지는 군에서 선택되는 적어도 1 종의 가교제인 것을 특징으로 하는 편광 필름용 점착제 조성물.The method according to claim 5 or 6,
Wherein the crosslinking agent (D) is at least one crosslinking agent selected from the group consisting of an isocyanate compound and a peroxide. 제 1 항 내지 제 7 항 중 어느 한 항에 있어서,
추가로, 아세토아세틸기 함유 실란 커플링제 (C2) 를 함유하는 것을 특징으로 하는 편광 필름용 점착제 조성물.8. The method according to any one of claims 1 to 7,
A pressure-sensitive adhesive composition for a polarizing film, further comprising an acetoacetyl group-containing silane coupling agent (C2). 제 1 항 내지 제 8 항 중 어느 한 항에 기재된 편광 필름용 점착제 조성물로 형성되는 것을 특징으로 하는 편광 필름용 점착제층.A pressure-sensitive adhesive layer for a polarizing film, which is formed from the pressure-sensitive adhesive composition for a polarizing film according to any one of claims 1 to 8. 편광 필름과, 당해 편광 필름에 형성된 점착제층을 갖는 점착제층이 형성된 편광 필름으로서,
상기 편광 필름은, 편광자의 편측에만 투명 보호 필름을 갖고, 상기 점착제층은, 상기 편광자의 상기 투명 보호 필름을 갖지 않는 면에 형성되어 있고, 또한
상기 점착제층이, 제 9 항에 기재된 편광 필름용 점착제층인 것을 특징으로 하는 점착제층이 형성된 편광 필름.A polarizing film comprising a polarizing film and a pressure-sensitive adhesive layer having a pressure-sensitive adhesive layer formed on the polarizing film,
Wherein the polarizing film has a transparent protective film only on one side of the polarizer, the pressure-sensitive adhesive layer is formed on a surface of the polarizer having no transparent protective film,
Wherein the pressure-sensitive adhesive layer is the pressure-sensitive adhesive layer for a polarizing film according to claim 9. 제 10 항에 있어서,
상기 편광자의 두께가 10 ㎛ 이하인 것을 특징으로 하는 점착제층이 형성된 편광 필름.11. The method of claim 10,
Wherein the thickness of the polarizer is 10 占 퐉 or less. 제 10 항 또는 제 11 항에 기재된 점착제층이 형성된 편광 필름을 적어도 1 개 사용한 것을 특징으로 하는 화상 표시 장치.An image display apparatus using at least one polarizing film on which the pressure-sensitive adhesive layer according to claim 10 or 11 is formed.
KR1020177025082A 2015-04-03 2016-03-31 Adhesive composition for polarizing film, adhesive layer for polarizing film, adhesive layer-including polarizing film, and image display device KR102046236B1 (en)