KR20170039007A - Polyester resin composition, and molded artice manufactured therefrom - Google Patents

Polyester resin composition, and molded artice manufactured therefrom Download PDF

Info

Publication number
KR20170039007A
KR20170039007A KR1020150137900A KR20150137900A KR20170039007A KR 20170039007 A KR20170039007 A KR 20170039007A KR 1020150137900 A KR1020150137900 A KR 1020150137900A KR 20150137900 A KR20150137900 A KR 20150137900A KR 20170039007 A KR20170039007 A KR 20170039007A
Authority
KR
South Korea
Prior art keywords
weight
parts
resin
polyethylene terephthalate
pet
Prior art date
Application number
KR1020150137900A
Other languages
Korean (ko)
Inventor
이정욱
정기봉
Original Assignee
코오롱플라스틱 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 코오롱플라스틱 주식회사 filed Critical 코오롱플라스틱 주식회사
Priority to KR1020150137900A priority Critical patent/KR20170039007A/en
Publication of KR20170039007A publication Critical patent/KR20170039007A/en

Abstract

The present invention is to provide a polyester resin composition having excellent curl properties, flame retardancy and quenching properties, and yarn for wig hairs manufactured therefrom. The polyester resin composition for wig hairs comprises: a first polyethylene terephthalate (PET) resin; a copolymer resin of isophthalic acid and PET; a halogen-based flame retardant agent; a pigment dispersing agent; and a second PET resin including a quenching agent.

Description

폴리에스터 수지 조성물 및 이를 이용한 플라스틱 성형체 제조 {POLYESTER RESIN COMPOSITION, AND MOLDED ARTICE MANUFACTURED THEREFROM}POLYESTER RESIN COMPOSITION AND POLYESTER RESIN COMPOSITION AND MOLDED ARTICE MANUFACTURED THEREFORM

본 발명은 폴리에스터 (Polyester) 수지 조성물 및 이를 이용한 플라스틱 성형체에 관한 것으로서, 보다 구체적으로는 소광제 및 폴리에스터 수지를 포함하는 소광용 조성물을 포함하는 가발사용 조성물에 관한 것이다.BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a polyester resin composition and a plastic molded article using the same. More particularly, the present invention relates to a composition for wig comprising a light extinguishing agent and a polyester resin.

일반적으로 가발모용 플라스틱 수지를 제조하는 재료로는 궁극적으로 외관, 감촉 등에서 인모와 유사한 효과를 나타낼 수 있어야 하며, 이를 위해서는 인모와 유사한 색상, 컬(Curl) 특성, 소광성, 및 난연성을 지녀야 한다. 최근에는 상기와 같은 요건뿐 아니라 내열성도 요구된다. Generally, as a material for producing a plastic resin for a wig, ultraviolet rays should have a similar effect to a human body in terms of appearance and texture. For this purpose, a color similar to human hair, a curl characteristic, a light emitting property, and a flame retardancy should be used. In recent years, heat resistance as well as the above requirements are required.

한편, 현재까지 가발모용은 크게 두 가지로 나뉜다. 자체 난연이 되지 않는 일반 가발사와 자체 난연이 되는 난연 가발사 또는 고열사로 나뉘어지고 있다. 일반가발사로 사용되는 수지에는 폴리프로필렌, 나일론 및 폴리에스터 수지 조성물이 있으며 난연가발사로 사용되는 수지에는 PVC, 모다크릴(modacryl)과 최근에 개발된 폴리에스터 수지에 난연기능이 첨가된 난연 폴리에스터 수지 등이 있는데, 이 중 PVC와 모다크릴(modacryl)은 분자 구조상 Cl기를 포함하며, 난연 폴리에스터 수지에는 Br기를 포함하며, 자기소화성에 의한 난연성이 있다. On the other hand, until now, there are two types of wigs. It is divided into ordinary wig which does not become flame retardant itself and flame retardant wig which becomes flame retardant itself or heat-resistant yarn. There are polypropylene, nylon and polyester resin compositions used as general wig wares. Resin used as flame retardant wig is PVC, modacryl, and flame retardant polyester resin with flame retardant added to recently developed polyester resin Among them, PVC and modacryl contain a Cl group in the molecular structure, and the flame retardant polyester resin contains a Br group and has flame retardancy due to self-extinguishing properties.

한편, 폴리에스터 수지로 제조된 가발모용 수지는 높은 유리전이온도에 의한 우수한 컬(Curl) 특성과 탄성율을 나타내고, 색상 및 광택성이 양호하며, 내열성이 높아 열 고찰 후 Curl이 용이하다는 장점 때문에, 다른 가발모용 수지보다 우수한 소재로 평가받고 있다. 하지만, 이와 같은 폴리에스터계 수지는 높은 탄성율로 인해 촉감이 나쁘고, 염색이 어려운 단점이 있으며, 또한 난연성을 부여하기 위해 난연제와 혼용하는 경우, 방사성이 떨어지고, 촉감이 더욱 저하되는 문제점이 있다.On the other hand, the wax-like resin made of a polyester resin exhibits excellent curl characteristics and elastic modulus due to a high glass transition temperature, good color and gloss, and high heat resistance, It has been evaluated as superior to other wigs. However, such a polyester-based resin is disadvantageous in that it has poor touch feeling due to a high modulus of elasticity and is difficult to dye, and when mixed with a flame retardant agent to impart flame retardancy, there is a problem that radioactivity deteriorates and the feel is further reduced.

난연성 폴리에스터 가발원사의 제조와 관련된 종래의 기술개발 동향을 살펴보면 다음과 같다. The development trend of conventional technology related to the production of flame retardant polyester wig yarn will be described as follows.

일본특허 특 2003-0064622호 및 일본특허 특개 제 2005-76147호에는 반응형 인계 난연제를 공중합시킨 열가소성 공중합 폴리알킬테레프탈레이트 수지로 난연성 폴리에스터 가발원사를 제조하는 방법이 있지만, 이 방법 역시 가발원사가 요구하는 난연성을 충족시키기 위해서 인 원자량을 환산하여 5-10중량%의 난연제를 첨가하는데 이 경우 난연성은 개선되지만 섬유 형성이 어렵게 되어 실용적인 방법이라 할 수 없다.Japanese Patent Publication No. 2003-0064622 and Japanese Patent Publication No. 2005-76147 disclose a method for producing a flame-retardant polyester wig yarn using a thermoplastic copolymerized polyalkyl terephthalate resin obtained by copolymerizing a reactive phosphorus flame retardant. In order to satisfy the required flame retardancy, 5-10 wt% of a flame retardant is added in terms of the phosphorus atomic weight. In this case, flame retardancy is improved but fiber formation is difficult, which is not a practical method.

가장 실용적인 방법으로 제안된 방법으로는 폴리에틸렌테레프탈레이트 수지 혹은 폴리부틸렌테레프탈레이트 수지를 난연화하는 방법으로 고분자형 브롬화 에폭시 혹은 페녹시 난연제를 첨가하는 방법이 일본특개소 60-71713호, 소59-129253호, 소 59-149954호, 소 58-101145호에 공지되어 있다. 이들 특허에서는 난연제로 브롬화비스페놀A 디글리시딜에테르와 브롬화비스페놀A를 주성분으로 하여 중합한 반응 생성물을 용융 혼련 하는 방법이 개시되어 있다. As a most practical method, a method of adding a polymer-type brominated epoxy or a phenoxy flame retardant to a method of smearing a polyethylene terephthalate resin or a polybutylene terephthalate resin is disclosed in Japanese Patent Application Laid-Open No. 60-71713, 129253, cat. No. 59-149954, cat. No. 58-101145. In these patents, a method of melting and kneading a reaction product obtained by polymerizing bisphenol A bromide and diglycidyl bromide as a flame retardant, and bisphenol A bromide as a main component is disclosed.

그러나 이들 방법으로 난연 폴리에스터 가발원사를 제조하는 경우 방사 시간이 경과함에 따라 열분해 탄화물 발생이 증가하여 노즐 홀이 막히거나 용융수지가 토출 되는 노즐 홀 주변에 열분해 탄화물이 쌓이게 되어 곡사 현상으로 인한 사절이 발생하여 연속적인 생산이 어렵게 되는 문제가 있다. 또한 이 방법의 압출하여 방사된 filament는 열을 주어 setting을 한 후 시간에 지남에 따라 가발모의 Curl의 형태가 처지게 되는 Curl 특성이 저하되는 경향을 띤다. 또한 압출 후 방사한 filament 에 열을 주어 setting 할 시 Curl을 형성하는 시간이 오래 걸리어 생산성이 떨어지는 단점이 있다. However, when the flame retardant polyester wig yarn is produced by these methods, the generation of pyrolytic carbides increases with the lapse of the spin time, and the pyrolysis carbides accumulate around the nozzle holes where the nozzle holes are closed or the molten resin is discharged. There is a problem that continuous production becomes difficult. In addition, the Curl characteristics of the wig pattern of curled wig tends to decrease with time after setting the filament by extruding and extruding this method. Also, there is a disadvantage that it takes a long time to form a curl when the filament is extruded and then the filament is heated and set, which lowers the productivity.

마지막으로 가발사용 폴리에스터 수지의 광택이 많이 날수록 실제모발과는 차이가 나는 단점을 가지고 있다.Finally, as the gloss of polyester resin used for wig increases, the hair is different from actual hair.

이에 본 발명은 소광제와 폴리에스터 수지를 예비혼합한 소광용 조성물을 포함함으로써 광택성을 개선함과 동시에 난연성 및 컬 특성이 우수한 가발모용 폴리에스터 수지 조성물을 제공하고자 한다.Accordingly, it is an object of the present invention to provide a polyester resin composition for a wigmat which has improved flame retardancy and curl characteristics by including a light-quenching composition premixed with a quencher and a polyester resin.

본 발명에 따른 바람직한 제 1 구현예는, 폴리에틸렌테레프탈레이트(PET) 제1 수지 100 중량부에 대하여, 이소프탈산과 폴리에틸렌테레프탈레이트(PET)의 공중합물 수지 9 내지 40 중량부, 할로겐계 난연제 15 내지 30중량부, 안료분산제 0.5 내지 3 중량부, 및 소광제를 포함하는 폴리에틸렌테레프탈레이트(PET) 제2 수지 20 내지 30 중량부를 포함하고, A first preferred embodiment of the present invention is a thermoplastic resin composition comprising 9 to 40 parts by weight of a copolymer resin of isophthalic acid and polyethylene terephthalate (PET), 15 to 30 parts by weight of a halogen-based flame retardant, 30 to 30 parts by weight of a pigment dispersant, 0.5 to 3 parts by weight of a pigment dispersant, and 20 to 30 parts by weight of a second resin of polyethylene terephthalate (PET)

상기 소광제를 포함하는 폴리에틸렌테레프탈레이트(PET) 제2 수지는, 폴리에틸렌테레프탈레이트 수지 100중량부에 대하여 소광제를 20 내지 30 중량부 포함하는 것이며, 소광제의 중량평균분자량이 1,200 내지 2,000 인 것을 특징으로 하는, 가발모용 폴리에스터 수지 조성물이다.The polyethylene terephthalate (PET) second resin comprising the quencher includes 20 to 30 parts by weight of a quenching agent per 100 parts by weight of the polyethylene terephthalate resin, and the quencher has a weight average molecular weight of 1,200 to 2,000 Wherein the polyester resin composition is a wax-like polyester resin composition.

상기 제 1 구현예에 의한 소광제는 실리케이트인 것일 수 있다.The quencher according to the first embodiment may be a silicate.

상기 제 1 구현예에 의한 폴리에틸렌테레프탈레이트(PET) 제1 수지의 고유 점도는 0.5 내지 1.2 dl/g 인 것일 수 있다.The intrinsic viscosity of the first polyethylene terephthalate (PET) resin according to the first embodiment may be 0.5 to 1.2 dl / g.

상기 제 1 구현예에 의한 이소프탈산과 폴리에틸렌테레프탈레이트의 공중합물 수지의 고유 점도는 0.5 내지 1.0dl/g인 것일 수 있다.The intrinsic viscosity of the copolymer resin of isophthalic acid and polyethylene terephthalate according to the first embodiment may be 0.5 to 1.0 dl / g.

상기 제 1 구현예에 의한 할로겐계 난연제는 할로겐의 함량을 50 내지 80중량%로 포함하는 것일 수 있다.The halogen-based flame retardant according to the first embodiment may have a halogen content of 50 to 80% by weight.

상기 제 1 구현예에 의한 안료 분산제는 탈크(talc), 유기 핵제, 왁스(WAX), 또는 이들의 혼합물인 것일 수 있다.The pigment dispersant according to the first embodiment may be talc, organic nucleating agent, wax (WAX), or a mixture thereof.

상기 제 1 구현예에 의한 폴리에스터는 한계 산소 지수(Limited Oxygen Index, LOI)값이 24 이상인 것일 수 있다.The polyester according to the first embodiment may have a Limited Oxygen Index (LOI) value of 24 or more.

또한, 본 발명에 따른 바람직한 제 2 구현예는, 상기 폴리에스터 수지 조성물을 포함하는 가발 원사이다.Further, a second preferred embodiment according to the present invention is a wig circle comprising the polyester resin composition.

아울러, 본 발명에 따른 바람직한 제 3 구현예는 폴리에틸렌테레프탈레이트 수지 100 중량부에 대하여 소광제 20 내지 30 중량부를 포함하는 폴리에틸렌테레프탈레이트 수지를 준비하는 단계(S1);According to another embodiment of the present invention, there is provided a method of manufacturing a polyethylene terephthalate resin, comprising: (S1) preparing a polyethylene terephthalate resin comprising 20 to 30 parts by weight of a quencher with respect to 100 parts by weight of a polyethylene terephthalate resin;

폴리에틸렌테레프탈레이트 수지 100 중량부에 대하여, 이소프탈산과 폴리에틸렌테레프탈레이트의 공중합물 수지 9 내지 40 중량부, 할로겐계 난연제 15 내지 40 중량부, 안료분산제 0.5 내지 3 중량부, 및 상기 S1 단계의 폴리에틸렌테레프탈레이트 수지 20 내지 30 중량부를 포함하는 폴리에스테르 수지 조성물을 준비하는 단계(S2);9 to 40 parts by weight of a copolymer resin of isophthalic acid and polyethylene terephthalate, 15 to 40 parts by weight of a halogen-based flame retardant, 0.5 to 3 parts by weight of a pigment dispersant, and 0.5 to 3 parts by weight of a polyethylene terephthalate (S2) preparing a polyester resin composition comprising 20 to 30 parts by weight of a phthalate resin;

상기 조성물을 용융 방사하는 단계(S3); 및(S3) melt spinning the composition; And

상기 용융 방사물을 연신하는 단계(S4)를 포함하는 가발 원사의 제조방법이다.And a step (S4) of stretching the molten yarn.

본 발명에 따르면 Polyester 수지의 가발사 제품으로 제조시에 광택성을 개선함과 동시에 난연성 및 Curl 특성을 가지는 폴리에스테르 수지 조성물을 이용한 가발모용 폴리에스테르 원사 및 그 제조방법을 제공할 수 있다.According to the present invention, it is possible to provide a polyester yarn for a wig using a polyester resin composition having improved flame retardancy and Curl properties while producing a wig product of a polyester resin, and a method for producing the polyester yarn.

본 발명의 일 양태에 따르면, 폴리에틸렌테레프탈레이트(PET) 제1 수지 100 중량부에 대하여, 이소프탈산과 폴리에틸렌테레프탈레이트(PET)의 공중합물 수지 9 내지 40 중량부, 할로겐계 난연제 15 내지 30중량부, 안료분산제 0.5 내지 3 중량부, 및 실리케이트계 소광제를 포함하는 폴리에틸렌테레프탈레이트(PET) 제2 수지 20 내지 30 중량부를 포함하고, 상기 소광제를 포함하는 폴리에틸렌테레프탈레이트(PET) 제2 수지는, 폴리에틸렌테레프탈레이트 수지 100중량부에 대하여 소광제를 20 내지 30 중량부 포함하는 것이며, 소광제의 중량평균분자량이 1,200 내지 2,000 인 것을 특징으로 하는, 가발모용 폴리에스터 수지 조성물을 제공하는 것이다.According to one aspect of the present invention, there is provided a thermoplastic resin composition comprising 9 to 40 parts by weight of a copolymer resin of isophthalic acid and polyethylene terephthalate (PET), 15 to 30 parts by weight of a halogen-based flame retardant, 100 parts by weight of a polyethylene terephthalate (PET) , 0.5 to 3 parts by weight of a pigment dispersant, and 20 to 30 parts by weight of a second resin of polyethylene terephthalate (PET) containing a silicate-based extinction agent, wherein the second resin of polyethylene terephthalate (PET) And 20 to 30 parts by weight of a quenching agent based on 100 parts by weight of the polyethylene terephthalate resin. The quencher has a weight average molecular weight of 1,200 to 2,000.

상기 조성물로 제조된 가발 원사는 Gloss Checker를 통하여 굴곡시편의 표면을 측정시 Optical range 60° 기준 70이하 Curl 특성(cm), 고데기로 Curl Setting후 한 시간이 지난 후에 가발사의 처짐 길이 측정 기준 길이 대비+3cm 이하, ASTM D 2863에 의한 산소한계 능력지수 (LOI : Limited Oxygen Index)가 24이상인 조성물을 특징으로 한다.When measuring the surface of a bending specimen using the Gloss Checker, the composition of the wig produced from the composition has a Curl characteristic (cm) of 70 or less based on an optical range of 60 °, and a deflection length measurement length + 3 cm or less, and a Limited Oxygen Index (LOI) of 24 or more according to ASTM D 2863.

1) 폴리에틸렌테레프탈레이트(PET) 수지1) Polyethylene terephthalate (PET) resin

본 발명에서 사용된 폴리에틸렌테레프탈레이트 수지는 가발모용 수지 조성물의 준비에 통상 사용되는 것이면 그 구성의 한정 없이 선택될 수 있으나 폴리에스테르 수지 조성물의 방사성 및 최종 제조되는 가발모용 원사의 촉감 등을 고려하여 고유점도가 0.5 내지 1.2 dl/g인 것을 사용할 수 있다.The polyethylene terephthalate resin used in the present invention can be selected without limitation of its constitution as long as it is usually used in the preparation of the resin composition for wig, And a viscosity of 0.5 to 1.2 dl / g may be used.

2) 폴리에틸렌테레프탈레이트(PET) 공중합물 수지2) Polyethylene terephthalate (PET) copolymer resin

본 발명에서 유연성 및 촉감을 향상시키기 위해 첨가한 폴리에틸렌테레프탈레이트 공중합물 수지는 이소프탈산을 함유하는 공중합물, Dicabo methoxy benzen sulfonate를 함유하는 공중합물, 폴리에틸렌테레프탈레이트에 SiO2를 첨가한 공중합물, full dull DMT를 함유하는 모노머를 공중합 시킨 공중합물, semi dull TPA를 함유하는 모노머를 공중합시킨 공중합물등 을 사용할 수 있으나, 용이하게 입수가능한 폴리에틸렌테레프탈레이트 공중합물 수지라면 이에 제한되는 것은 아니다.In the present invention, the polyethylene terephthalate copolymer resin added to improve flexibility and feel is selected from the group consisting of a copolymer containing isophthalic acid, a copolymer containing Dicabo methoxy benzen sulfonate, a copolymer containing SiO 2 added to polyethylene terephthalate, a full dull Copolymers obtained by copolymerizing monomers containing DMT and copolymers obtained by copolymerizing monomers containing semi-dull TPA can be used. However, the present invention is not limited to polyethylene terephthalate copolymer resins that are readily available.

상기 폴리에틸렌테레프탈레이트 공중합물 수지는 그 함량이 폴리에틸렌테레프탈레이트 수지 100 중량부에 대하여 9 내지 40 중량부일 수 있으며, 9 중량부 미만이면 유연성 및 촉감에 문제가 있고, 40 중량부 초과이면 내열성에 문제가 있을 수 있다.The content of the polyethylene terephthalate copolymer resin may be 9 to 40 parts by weight based on 100 parts by weight of the polyethylene terephthalate resin. If the content of the polyethylene terephthalate copolymer resin is less than 9 parts by weight, there is a problem in flexibility and feel. If the content is more than 40 parts by weight, Can be.

특히, 상기 폴리에틸렌테레프탈레이트 공중합물 수지는 최종적으로 제조된 폴리에스테르 수지 조성물의 방사성 및 상기 폴리에스테르 수지 조성물로 제조된 가발모용 원사의 유연성 및 촉감을 고려하여 바람직하게는 이소프탈산을 함유하는 공중합물를 사용할 수 있다. 가발모용 원사의 방사성 및 촉감 등을 고려하여 고유점도가 0.5 내지 1.0 dl/g 것을 사용 할 수 있다. 예를 들어, 화학식 1을 포함하는 공중합물로, 가발모용 원사의 방사성 및 촉감 등을 고려하여 고유점도가 0.5 내지 1.0 dl/g 것을 사용 할 수 있다. Particularly, the polyethylene terephthalate copolymer resin is preferably used in consideration of the radiation property of the finally produced polyester resin composition and the flexibility and tactile feeling of the woven yarn made of the polyester resin composition, preferably using a copolymer containing isophthalic acid . The intrinsic viscosity of 0.5 to 1.0 dl / g may be used in consideration of the radioactivity and tactile properties of the yarn for wig. For example, the copolymer having the formula (1) may have an intrinsic viscosity of 0.5 to 1.0 dl / g in consideration of radioactivity and tactility of the yarn for wig.

<화학식 1>&Lt; Formula 1 >

Figure pat00001
Figure pat00001

R1 : 탄소수 하나 이상의 카르복실기 R 1 : a carboxyl group having at least one carbon number

R2 : 수소 또는 탄소수 하나 이상의 알킬기R 2 : hydrogen or an alkyl group having at least one carbon number

R3 : 수소 또는 탄소수 하나 이상의 알킬기 또는 금속 이온기R 3 : hydrogen or an alkyl group or a metal ion group having at least one carbon atom

R4 : 수소 또는 탄소수 하나 이상의 알킬기R 4 : hydrogen or an alkyl group having at least one carbon number

R5 : 탄소수 하나 이상의 카르복실기R 5 : a carbon number of at least one carboxyl group

R6: 수소 또는 탄소수 하나 이상의 알킬기R 6 : hydrogen or an alkyl group having at least one carbon number

3) 할로겐계 난연제 (Halogen flame retardant)3) Halogen flame retardant

본 발명에서 사용된 할로겐계 난연제는 폴리에틸렌테레프탈레이트 수지 100 중량부에 대해 15 내지 40 중량부로 포함될 수 있는데, 15 중량부 미만으로 첨가하는 경우 충분한 정도의 난연성을 나타내기 어렵고, 40 중량부 초과로 첨가하는 경우 방사성이 떨어질 수 있다. The halogen-based flame retardant used in the present invention may be contained in an amount of 15 to 40 parts by weight based on 100 parts by weight of the polyethylene terephthalate resin. When the amount is less than 15 parts by weight, flame retardancy is not sufficiently exhibited. The radioactivity may be reduced.

한편, 상기 할로겐화 난연제는 할로겐의 함량이 할로겐화 난연제 총함량에 대해 50 내지 80중량%인 것을 사용할 수 있는데, 이와 같은 할로겐 함량을 갖는 할로겐화 난연제를 사용하는 경우, 폴리에스테르 수지 조성물에 충분한 정도의 난연성을 부여함과 동시에 가발모용 원사로 사용되기에 최적화된 촉감, 유연성 및 방사성을 나타낼 수 있다. 이와 같은 이유로, 더욱 바람직하게는 할로겐의 함량이 총 난연제 함량에 대해 50 내지 75중량% 인 할로겐화 난연제를 사용할 수 있다. On the other hand, the halogenated flame retardant may be one having a halogen content of 50 to 80% by weight based on the total halogenated flame retardant. When such a halogenated flame retardant having a halogen content is used, the polyester resin composition has sufficient flame retardancy At the same time as imparting, it can exhibit the tactile, soft, and radiative properties optimized for use as wigs. For this reason, more preferably, a halogenated flame retardant having a halogen content of 50 to 75% by weight based on the total flame retardant content can be used.

이와 같은 할로겐화 난연제는 폴리에스테르 수지 조성물의 방사성 및 최종 제조되는 가발모용 원사의 촉감을 고려하여 브롬화 난연제로 변경될 수 있다.  Such a halogenated flame retardant agent can be changed to a brominated flame retardant agent in consideration of the radioactivity of the polyester resin composition and the tactile feel of the yarn for the final wig.

상기와 브롬화 에폭시계 난연제를 전술한 바와 같은 중량비율로 폴리에스테르 수지 조성물에 첨가하는 경우, 가발모용으로 사용되기에 적합한 정도의 난연성을 나타낼 수 있음과 동시에, 가발모용 원사로 유용하게 사용될 수 있을 정도의 우수한 촉감, 컬감, 및 색감 등을 나타내고, 또한 우수한 유연성, 강도를 나타낼 수 있다. When the brominated epoxy flame retardant and the brominated epoxy flame retardant are added to the polyester resin composition in the weight ratio as described above, the flame retardancy can be exhibited to a degree suitable for use as a wig, and at the same time, And exhibits excellent softness, roughness, color feeling, etc., and can exhibit excellent flexibility and strength.

4) 안료 분산제 4) Pigment dispersant

본 발명에서 사용되는 안료분산제는 가발모용 수지 조성물 내에 포함되는 안료들의 분산을 용이하게 하는 역할을 하며, 폴리에스테르 조성물의 방사성을 떨어뜨리지 않는 범위 내에서 폴리에틸렌테레프탈레이트 수지 100 중량부에 대해, 0.5 내지 3 중량부로 포함될 수 있다. 안료분산제의 함량이 0.5 중량부 미만이면, 안료분산제 첨가에 따른 안료들의 분산효과가 미미하게 나타나며, 3 중량부를 초과하면 수지 조성물의 방사성이 떨어질 수 있다.The pigment dispersant used in the present invention has a role of facilitating the dispersion of the pigments contained in the resin composition for wiggly and is preferably used in an amount of from 0.5 to 5 parts by weight per 100 parts by weight of the polyethylene terephthalate resin within a range not lowering the radioactivity of the polyester composition. 3 parts by weight. When the content of the pigment dispersant is less than 0.5 parts by weight, the dispersing effect of the pigments due to the addition of the pigment dispersant is insignificant. When the content is more than 3 parts by weight, the radiation property of the resin composition may be deteriorated.

이와 같은 안료 분산제는 통상 수지 조성물의 안료의 분산을 용이하게 하는 구성이면, 그 구성의 한정이 없이 선택될 수 있다. 구체적으로, 탈크(talc), 유기 핵제, 왁스(WAX) 등을 사용할 수 있으나, 용이하게 입수 가능한 안료 분산제라면 이에 제한되는 것은 아니다. 상술한 안료분산제 외에 통상 사용되는 공정 안정제도 추가할 수 있다.Such a pigment dispersant can be selected without limitation in the constitution as long as it is a constitution that facilitates the dispersion of the pigment of the resin composition. Concretely, talc, organic nucleating agent, wax (WAX) or the like can be used, but the present invention is not limited thereto. In addition to the above-mentioned pigment dispersant, a commonly used process stabilizer can be added.

5) 소광제  5) Extinguishing agent

본 발명에서 사용되는 소광제는 가발모용 수지 조성물 내에 포함되는 폴리에틸렌테레프탈레이트의 광택성을 낮춰 주는 역할을 하며, 폴리에스테르 조성물의 방사성을 떨어뜨리지 않는 범위 내에서 중량평균분자량이 1,200 내지 2,000 의 Silicate를 사용하며 중량평균분자량이 1,200 미만이면 소광제 첨가에 따른 소광효과가 미미하게 나타나며, 2,000 를 초과하면 가발사로서의 광택성을 유지하지 못할 수 있다. The quencher used in the present invention lowers the luster of the polyethylene terephthalate contained in the resin composition for wig, and the silicate having a weight average molecular weight of 1,200 to 2,000 within the range of not lowering the radioactivity of the polyester composition When the weight average molecular weight is less than 1,200, the light extinction effect by the addition of the extinction agent is insignificant. When the weight average molecular weight is more than 2,000, the glossiness as a wig warp may not be maintained.

이와 같은 소광제는 통상 수지 조성물의 폴리에틸렌테레프탈레이트(PET)수지의 광택성을 줄이는 구성이면, 그 구성의 한정이 없이 선택될 수 있다. 구체적으로, 탈크(talc), 실리케이트(Silicate), 이산화티탄(TiO₂)등을 사용할 수 있다.Such a light extinguishing agent can be selected without limiting its constitution so far as it has a constitution that generally reduces the gloss of the polyethylene terephthalate (PET) resin of the resin composition. Specifically, talc, silicate, titanium dioxide (TiO2), or the like can be used.

이때 소광제는 실리케이트인 것이 바람직하며, 실리케이트의 직경이 25 내지 75 μm인 것이 PET 수지와의 혼합성을 고려할 때 바람직하다.At this time, it is preferable that the quenching agent is silicate, and the silicate having a diameter of 25 to 75 占 퐉 is preferable in consideration of the mixing property with the PET resin.

6) 기타 첨가제6) Other additives

본 발명에 따른 폴리에스테르 수지 조성물은 열안정성을 나타낼 수 있도록 열안정제를 추가로 포함할 수 있으며, 열안정제는 폴리에스테르 수지 조성물 내에서 산화 방지제의 역할을 할 수 있다. The polyester resin composition according to the present invention may further include a heat stabilizer to exhibit thermal stability, and the heat stabilizer may act as an antioxidant in the polyester resin composition.

상기 열안정제로는 하이드록시 페닐계 화합물, 힌더드 아민 화합물, 황계 화합물 및 인계화합물로 이루어진 군에서 선택되는 하나 이상일 수 있으나, 통상 폴리에스테르 수지 조성물 내에서 산화방지제의 역할을 할 수 있는 것이면 이에 제한되는 것은 아니다.The heat stabilizer may be at least one selected from the group consisting of a hydroxyphenyl compound, a hindered amine compound, a sulfur compound, and a phosphorus compound. However, the heat stabilizer is not limited thereto as long as it can act as an antioxidant in the polyester resin composition. It is not.

상기 열 안정제는 폴리에스테르 수지 조성물의 방사성 및 가발모용 원사의 촉감을 떨어뜨리지 않으면서, 수지 조성물의 열 안정성을 나타내기 위해, 폴리에틸렌테레프탈레이트 100 중량부에 대해 0.1 내지 0.5 중량부로 첨가될 수 있다.The thermal stabilizer may be added in an amount of 0.1 to 0.5 parts by weight based on 100 parts by weight of polyethylene terephthalate so as to exhibit thermal stability of the resin composition without deteriorating the feel of the yarn for spinning and spun yarn of the polyester resin composition.

또한 본 발명은 상기 폴리에스터 수지 조성물을 포함하는 가발 원사를 제공할 수 있다.The present invention can also provide a wig yarn comprising the polyester resin composition.

아울러, 본 발명은 폴리에틸렌테레프탈레이트 수지 100 중량부에 대하여 소광제 20 내지 30 중량부를 포함하는 폴리에틸렌테레프탈레이트 수지를 준비하는 단계(S1);In addition, the present invention provides a method for producing a polyethylene terephthalate resin, comprising: (S1) preparing a polyethylene terephthalate resin comprising 20 to 30 parts by weight of a light extinction agent per 100 parts by weight of a polyethylene terephthalate resin;

폴리에틸렌테레프탈레이트 수지 100 중량부에 대하여, 이소프탈산과 폴리에틸렌테레프탈레이트의 공중합물 수지 9 내지 40 중량부, 할로겐계 난연제 15 내지 40 중량부, 안료분산제 0.5 내지 3 중량부, 및 상기 S1 단계의 폴리에틸렌테레프탈레이트 수지 20 내지 30 중량부를 포함하는 폴리에스테르 수지 조성물을 준비하는 단계(S2);9 to 40 parts by weight of a copolymer resin of isophthalic acid and polyethylene terephthalate, 15 to 40 parts by weight of a halogen-based flame retardant, 0.5 to 3 parts by weight of a pigment dispersant, and 0.5 to 3 parts by weight of a polyethylene terephthalate (S2) preparing a polyester resin composition comprising 20 to 30 parts by weight of a phthalate resin;

상기 조성물을 용융 방사하는 단계(S3); 및(S3) melt spinning the composition; And

상기 용융 방사물을 연신하는 단계(S4)를 포함하는 가발 원사의 제조방법을 제공한다.And a step (S4) of stretching the molten yarn.

본 발명의 각 구성 성분은 압출기를 사용, 용융 혼련 압출하여 성형용 칩을 제조하는 컴파운딩 공정에서 제조하였다. 조성물의 혼련을 최대화하기 위하여 혼합기로는 2축 스크류 압출기를 사용하여 270℃ 내지 280℃ 온도에서 혼련하여 제조될 수 있는데, Silicate의 비중이 낮기 때문에 난연제를 제외한 수지를 Total Blending하여 메인 피더로 투입시 Silicate는 위로 뜨고 나머지 조성물들은 아래로 가라 앉어 층 분리가 생길 수 있다. 이러한 층 분리 현상을 방지하기 위하여 먼저 폴리에틸렌테레프탈레이트(PET)수지와 Silicate를 압출하여 Pellet형태를 만드는데 2축 스크류 압출기를 사용하여270℃ 내지 280℃ 온도에서 수지 조성물의 혼련을 최대화하기 위하여 투입구가 3개인 압출기를 이용하여 1차 투입구에 상기 폴리에틸렌테레프탈레이트(PET)수지를, 2차 투입구에 Silicate를 투입할 수 있다. 여기서 폴리에틸렌테레프탈레이트(PET)수지 100중량부에 Silicate는 0.01내지 0.1중량부가 들어가며 Silicate계 소광제가 포함된 Pellet형태 수지는 폴리에틸렌테레프탈레이트(PET) 수지 100중량부에 대해서 20내지 30 중량부가 들어갈 수 있고 생성된 Pellet함량이 20중량부 미만이면 소광 효과가 미비하고 30중량부 이상이면 방사시 절사 현상이 일어난다. 폴리에틸렌테레프탈레이트(PET) 수지, 폴리에틸렌테레프탈레이트(PET) 공중합 수지, 안료 분산제와 함께 Total blending하여 투입된다. 또한, 용융 혼련시에 조성물의 열분해를 방지하기 위해 체류시간을 최소화할 수 있으며, 본 조성물에서 분산성을 고려하여 최적의 스크류 회전수 및 output 조절이 필요한데 최대 부하의 80% 정도로 실시할 수 있다.Each component of the present invention was produced in a compounding process for producing a molding chip by melt-kneading and extruding using an extruder. In order to maximize the kneading of the composition, a mixer can be manufactured by kneading at 270 ° C to 280 ° C using a twin screw extruder. Since the specific gravity of silicate is low, total blending of the resin except the flame retardant is applied to the main feeder The silicate floats up and the remaining compositions sink down and layer separation can occur. In order to prevent the layer separation phenomenon, a polyethylene terephthalate (PET) resin and a silicate are extruded to form a pellet shape. In order to maximize kneading of the resin composition at a temperature of 270 ° C. to 280 ° C. using a twin-screw extruder, The polyethylene terephthalate (PET) resin may be injected into the primary injection port and the silicate may be injected into the secondary injection port using a personal extruder. Here, 0.01 to 0.1 part by weight of silicate is contained in 100 parts by weight of polyethylene terephthalate (PET) resin, and 20 to 30 parts by weight of pellet type resin containing silicate-based extinction agent is contained in 100 parts by weight of polyethylene terephthalate (PET) If the content of the generated pellets is less than 20 parts by weight, the light extinction effect is insufficient. If the content is more than 30 parts by weight, a spinning phenomenon occurs. (PET) resin, a polyethylene terephthalate (PET) copolymer resin, and a pigment dispersant. In order to prevent pyrolysis of the composition during melting and kneading, the residence time can be minimized and the optimum screw rotation speed and output can be controlled in consideration of dispersibility in the composition, which can be performed at about 80% of the maximum load.

이상에서 살펴 본 바와 같이, 본 발명에 따른 소광성을 가지는 난연 폴리에스터 수지는 폴리에틸렌테레프탈레이트(PET) 수지, 폴리에틸렌테레프탈레이트(PET) 공중합 수지, 브롬계난연제, 안료분산제, Silicate를 주성분으로 하는 물질을 포함하는 소광제이며, 이 조성물은 폴리에틸렌테레프탈레이트(PET) 수지, 폴리에틸렌테레프탈레이트(PET) 공중합 수지를 통해 Curl유지특성을 가지며, Silicate계 물질을 주성분으로 하는 소광제의 첨가를 통한 소광성을 가지는 것을 특징으로 한다. 특히, 본 발명에 따른 소광성을 가지는 난연 폴리에스터 수지 조성물은 가발사용으로 사용 가능하다.As described above, the flame retardant polyester resin having a light-emitting property according to the present invention is a resin having a light-emitting property such as a polyethylene terephthalate (PET) resin, a polyethylene terephthalate (PET) copolymer resin, a brominated flame retardant, a pigment dispersant, (PET) resin, a polyethylene terephthalate (PET) copolymer resin, and has a curl retention property. The composition has a quenching property through addition of a quencher containing a silicate-based material as a main component . Particularly, the flame retardant polyester resin composition having a light-emitting property according to the present invention can be used by using a wig.

본 발명의 실시 예를 기술할 때 첨가량은 별도의 기술이 없을 경우 중량부를 나타내며, 제조방법과 분석 평가 방법은 다음 방법에 따라 수행 하였다. 이하 본 발명의 상세한 실시 예를 표기하였으며 실시 예에 본 발명이 국한되지는 않는다.In describing an embodiment of the present invention, the addition amount represents parts by weight unless otherwise specified, and the preparation method and the analytical evaluation method were carried out according to the following method. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings.

[[ 실시예Example ]]

이하, 실시예를 통하여 본 발명을 더욱 상세히 설명하고자 한다. 이들 실시예는 오로지 본 발명을 보다 구체적으로 설명하기 위한 것으로서, 이에 의해 본 발명이 한정되는 것은 아니다.Hereinafter, the present invention will be described in more detail with reference to Examples. These examples are for the purpose of illustrating the present invention more specifically, and the present invention is not limited thereto.

<< 실시예Example 1>  1>

하기 표 1에 기재된 조성에 따라, PET 수지(코오롱 사제) 및 소광제(Sires, Waker社)를 준비하였다. PET resin (manufactured by Kolon) and quencher (Sires, Waker) were prepared according to the composition shown in Table 1 below.

각 성분들을 270℃ 내지 280℃로 가열된 이축 압출기내에서 용융 혼련한 후 압출하였고 온도에서 수지 조성물의 혼련을 최대화하기 위하여 투입구가 3개인 압출기를 이용하여 1차 투입구에 상기 폴리에틸렌테레프탈레이트(PET)수지를, 2차 투입구에 Silicate를 투입하여 수지를 생산하였다.The components were melted and kneaded in a twin-screw extruder heated to 270 ° C to 280 ° C and then extruded. To maximize kneading of the resin composition at a temperature, the polyethylene terephthalate (PET) was extruded into a primary inlet using an extruder having three injection ports. The resin was injected into the second injection port, and the resin was produced.

소광제의 분자량은 겔 투과 크로마토그래피 (GPC) 에 의해 Silicate 환산 중량평균분자량(Mw) 및 수평균분자량(Mn)을 구하였다. 측정하는 중합체는 테트라히드로푸란에 용해시켜 GPC에 주입하였다. GPC의 이동상은 테트라히드로푸란을 사용하고, 1mL/min의 유속으로 유입하였다The weight average molecular weight (Mw) and the number average molecular weight (Mn) of the quencher were determined by gel permeation chromatography (GPC) in terms of Silicate. The polymer to be measured was dissolved in tetrahydrofuran and injected into GPC. The mobile phase of GPC was introduced at a flow rate of 1 mL / min using tetrahydrofuran

광택도 측정: ASTM D638에 의거하여 12.7 x 12.7 x 6.4mm인 시편을 제작하여 Gloss Checker를 이용하여 Optical range를 60°를 설정하고 시편 표면에 누르고 측정하였다.Measurement of gloss: A specimen of 12.7 x 12.7 x 6.4 mm was prepared according to ASTM D638, and the optical range was set to 60 deg. Using a gloss checker.

구분division 성분별 함량Content by ingredient 측정평가Measurement evaluation PET
(중량부)PET
(Parts by weight) 소광제1 )
(중량부)Quenching first )
(Parts by weight) 소광제 분자량Molecular weight of quencher 광택도Glossiness 실시예1-1Example 1-1 100100 2020 13001300 6868 실시예1-2Examples 1-2 100100 2020 17001700 6666 실시예1-3Example 1-3 100100 2020 19001900 6363 비교예1-1Comparative Example 1-1 100100 2020 500500 7575 비교예1-2Comparative Example 1-2 100100 2020 900900 7171 비교예1-3Comparative Example 1-3 100100 2020 25002500 5353 1) 소광제 : 실리케이트(Silicate, 직경: 50μm 상품명: Sires 제조사: Wacker社1) Quenching agent: Silicate (Silicate, diameter: 50μm Brand name: Sires Manufacturer: Wacker

상기 표 1 를 참고하면, 실시예 1-1~1-3 과 같이 실시한 조성에서는 비교예 1-1~1-3과 비교하여 소광제 분자량이 너무 적으면 소광제 첨가에 따른 광택도 저하 성능이 떨어지고 소광제 분자량이 너무 많으면 가발사용도로서의 광택도를 잃게 된다. 1,200 내지 2,000 이 최적의 비율이라는 것을 본 발명을 통해 확인할 수 있었다. 이러한 기술적 근거나 자세한 사례는 찾아보기 힘들며, 소광제의 분자량은 광택도를 고려하여 최적 분자량을 결정하였다Referring to Table 1, when the molecular weight of the quencher is too low as compared with Comparative Examples 1-1 to 1-3 in the compositions of Examples 1-1 to 1-3, If the molecular weight of the extinguishing agent drops too much, the gloss as the wig use degree is lost. It can be confirmed from the present invention that 1,200 to 2,000 is the optimum ratio. This technical basis and detailed examples are hard to find, and the molecular weight of the quencher is determined by considering the gloss and the optimum molecular weight

<< 실시예Example 2> 2>

하기 표 2에 기재된 조성에 따라 각 성분들을 270℃ 내지 280℃로 가열된 이축 압출기내에서 용융 혼련한 후 압출하였고 온도에서 수지 조성물의 혼련을 최대화하기 위하여 투입구가 3개인 압출기를 이용하여 1차 투입구에 상기 폴리에틸렌테레프탈레이트(PET)수지를, 2차 투입구에 Silicate를 투입하여 압출 가공성을 평가하였다.Each component was melted and kneaded in a twin-screw extruder heated to 270 ° C to 280 ° C according to the composition shown in Table 2, and then extruded. To maximize kneading of the resin composition at a temperature, a three- (Polyethylene terephthalate (PET) resin), and silicate was injected into the secondary injection port to evaluate extrusion processability.

광택도 측정: ASTM D638에 의거하여 12.7 x 12.7 x 6.4mm인 시편을 제작하여 Gloss Checker를 이용하여 Optical range를 60°를 설정하고 시편 표면에 누르고 측정하였다.Measurement of gloss: A specimen of 12.7 x 12.7 x 6.4 mm was prepared according to ASTM D638, and the optical range was set to 60 deg. Using a gloss checker.

구분division 성분별 함량Content by ingredient 측정 평가Measurement evaluation PET(중량부)PET (parts by weight) 소광제 (중량부)Quenching agent (parts by weight) 압출가공성Extrusion processability 광택도Glossiness 실시예 2-1Example 2-1 100100 2020 양호Good 6565 실시예 2-2Example 2-2 100100 2525 양호Good 6262 실시예 2-3Example 2-3 100100 3030 양호Good 5959 비교예 2-1Comparative Example 2-1 100100 55 양호Good 7777 비교예 2-2Comparative Example 2-2 100100 1010 양호Good 7474 비교예 2-3Comparative Example 2-3 100100 4040 불량Bad 5454

상기 표 2 를 참고하면, 실시예 2-1~2-3 과 같이 실시한 조성에서는 비교예 2-1~2-3 과 비교하여 압출가공성 및 광택도가 우수하다는 것을 확인 할 수 있으며 소광제 중량부가 너무 적으면 광택도가 떨어지고 소광제의 중량부가 너무 많으면 압출이 잘 되지 않는 문제가 발생하여 PET수지 100중량부 중에 20~30중량부가 최적의 비율이라는 것을 본 발명을 통해 확인 할 수 있었다. Referring to the above Table 2, it can be confirmed that the compositions of Examples 2-1 to 2-3 are superior in extrusion processability and gloss in comparison with Comparative Examples 2-1 to 2-3, The degree of gloss decreases when the amount is too small and the amount of the extinction agent to be added is too large to cause extrusion. Thus, it can be confirmed from the present invention that 20-30 parts by weight is the optimum ratio in 100 parts by weight of the PET resin.

이러한 기술적 근거나 자세한 사례는 찾아보기 힘들며, PET와 Silicate의 함량 비율은 압출 가공성 및 광택도를 고려하여 최적의 함량을 결정하였다.The technical content and detailed examples are hard to find, and the content ratio of PET and silicate was determined by considering the extrusion processability and gloss.

<< 실시예Example 3> 3>

본 실시예 3에서는 하기 표 3에 기재된 조성에 따라, PET 100 중량부에 대하여 PET 공중합물, 난연제, 안료분산제, 및 소광제가 포함된 수지조성물 또는 소광제를 혼합하여 폴리에스터 수지 조성물을 제조하였다.In Example 3, a polyester resin composition was prepared by mixing a PET copolymer, a flame retardant, a pigment dispersant, and a resin composition containing a light extender or a quencher with respect to 100 parts by weight of PET according to the composition shown in Table 3 below.

상기 소광제가 포함된 소광용 조성물의 제조방법은 실시예 1 및 실시예 2에서 제조한 것과 동일한 방법으로, 소광제 분자량은 1,700 이고, 20 중량부로 사용된 소광용 조성물을 이용하였다.The light extinction composition containing the light extinction agent was prepared in the same manner as in Examples 1 and 2 except that the light extinction agent was used in an amount of 1,700 and 20 parts by weight.

하기 표 3에 기재된 조성에 따라 각 성분들을 270℃ 내지 280℃로 가열된 이축 압출기내에서 용융 혼련한 후 칩(Chip)상태로 폴리에스터 수지 조성물을 제조하고, 120 ℃, 4 시간 제습형 건조기를 이용 건조하였다.Each component was melted and kneaded in a twin-screw extruder heated to 270 ° C. to 280 ° C. according to the composition shown in the following Table 3, and then a polyester resin composition was prepared in a chip state. The polyester resin composition was dried at 120 ° C. for 4 hours in a dehumidifying- And dried.

그 후, 스크류식 사출기를 이용하여 270℃ 내지 280℃의 제조 온도 조건에서 시편을 제작하여 다음의 방법으로 제반 물성의 평가를 실시하였고 방사테스트를 통하여 Curl특성을 측정하였다.After that, test specimens were prepared by using a screw extruder at 270 ° C to 280 ° C, and the properties of the specimens were evaluated by the following method. Curl properties were measured by spinning test.

1. Curl특성 측정: 압출 후 방사한 filament 로 방사 이후에 고대기로 Curl을 형성하고 시간이 지난 후에 가발모의 처짐 길이를 측정하였다. 20cm의 압출 후 방사한 filament 에 고대기로 Setting하여 (Setting 후 길이: 15cm) Curl 형성 후 1시간이 지난 후에 가발모의 길이 변화를 측정하여 Curl특성을 평가하였다.1. Measurement of curl characteristics: Curl was formed after spinning with a filament spun after extrusion, and the deflection length of the wig was measured after a lapse of time. Curl characteristics were evaluated by measuring the change in length of the wig after one hour of curl formation by setting the filament spun after extrusion of 20 cm and setting it at an early stage (length after setting: 15 cm).

2. 산소한계능력지수(LOI)측정 : 본 시험은 ASTM D2863에 의거하여 150mm x 10mm x 4mm 두께의 시편을 제작하여 시편에 점화 후 시편이 계속적으로 연소하는데 필요한 산소의 최저농도를 측정하였다.2. Measurement of Oxygen Limit Capability Index (LOI): In this test, a specimen of 150 mm x 10 mm x 4 mm thickness was prepared in accordance with ASTM D2863, and the lowest concentration of oxygen required to continuously burn the specimen after ignition was measured.

3. 광택도 측정: ASTM D638에 의거하여 12.7 x 12.7 x 6.4mm인 시편을 제작하여 Gloss Checker를 이용하여 Optical range를 60°를 설정하고 시편 표면에 누르고 측정하였다.3. Measurement of gloss: A specimen of 12.7 x 12.7 x 6.4 mm was prepared according to ASTM D638, and the optical range was set to 60 ° using a gloss checker.

4. 유연성/촉감 평가 : 방사되어 나온 가발사를 손으로 만졌을 때 끈적이지 않으며 뻣뻣함이 없이 잘 변형되는지 측정하였다.4. Flexibility / tactile evaluation: When the wiggler was exposed to the hand, it was measured that it was not sticky and deformed well without stiffness.

5. 방사성 평가 : 방사 팩의 방사 Hole내에서 나오는 가발사 제품이 절사 현상없이 연속적으로 진행되는지를 측정하였다.5. Radioactivity evaluation: We measured whether the wig products coming out of the radiation hole of the spinning pack proceeded continuously without cutting phenomenon.



구분

division 성분별 함량Content by ingredient PET
(중량부)PET
(Parts by weight) PET 공중합물
(중량부)PET copolymer
(Parts by weight) 난연제1 )
(중량부)Flame retardant 1 )
(Parts by weight) 안료분산제2 )
(중량부)Pigment dispersant 2 )
(Parts by weight) 소광제3 )가 포함된 PET수지
(중량부)PET resin containing quenching agent 3 )
(Parts by weight) 소광제3 )
(중량부)Quenching third )
(Parts by weight) 실시예 1Example 1 100100 2020 2020 1One 2020 -- 실시예 2Example 2 100100 2525 2525 22 2525 -- 실시예 3Example 3 100100 3535 2525 22 2020 -- 비교예 1Comparative Example 1 100100 55 2525 1One 2020 -- 비교예 2Comparative Example 2 100100 5050 2525 22 2525 -- 비교예 3Comparative Example 3 100100 2020 1010 1One 2020 -- 비교예 4Comparative Example 4 100100 2525 4040 22 2525 -- 비교예 5Comparative Example 5 100100 2020 2020 0.30.3 2020 -- 비교예 6Comparative Example 6 100100 2525 2525 3.53.5 2525 -- 비교예 7Comparative Example 7 100100 2020 2020 1One 1010 -- 비교예 8Comparative Example 8 100100 2525 2525 22 4040 -- 비교예 9Comparative Example 9 100100 2020 2020 1One -- 2020 비교예 10Comparative Example 10 100100 2020 2020 1One -- 4040 1) 난연제 : 우진고분자社CXB3000H
2) 안료분산제 : KOCH社 KCM6300
3) 소광제 : Wacker社SY4301) Flame retardant: Woojin Polymer Co., Ltd. CXB3000H
2) Pigment dispersant: KOCH KCM6300
3) Quenching agent: Wacker SY430

구분division Curl 유지특성Curl Retention Characteristics LOILOI 광택도Glossiness 유연성/촉감 평가Flexibility / tactile evaluation 방사성 평가Radioactive evaluation 실시예 1Example 1 16.216.2 27.527.5 6565 ○○ ○○ 실시예 2Example 2 16.516.5 27.427.4 6060 ○○ ○○ 실시예 3Example 3 16.116.1 27.527.5 6262 ○○ ○○ 비교예 1Comparative Example 1 16.816.8 27.127.1 6464 XX ○○ 비교예 2Comparative Example 2 21.521.5 26.426.4 6262 ○○ ○○ 비교예 3Comparative Example 3 17.417.4 2020 6868 ○○ ○○ 비교예 4Comparative Example 4 16.916.9 30.130.1 5959 ○○ XX 비교예 5Comparative Example 5 18.518.5 27.427.4 6666 ○○ ○○ 비교예 6Comparative Example 6 16.116.1 27.727.7 6363 ○○ XX 비교예 7Comparative Example 7 17.117.1 28.128.1 7474 ○○ ○○ 비교예 8Comparative Example 8 17.317.3 28.628.6 5353 ○○ XX 비교예 9Comparative Example 9 16.816.8 27.527.5 7272 ○○ ○○ 비교예 10Comparative Example 10 17.317.3 27.827.8 7373 ○○ ○○

상기 표 4를 참고하면, 실시예 3-1~3-3과 같이 실시한 조성에서는 비교예 3-1~3-8와 비교하여 Curl특성, 광택도, LOI, 유연성/촉감, 및 방사성이 우수하다는 것을 확인할 수 있습니다.Referring to Table 4, the compositions of Examples 3-1 to 3-3 exhibited excellent curl characteristics, glossiness, LOI, flexibility / touch, and radioactivity as compared with Comparative Examples 3-1 to 3-8 You can see that.

PET 공중합물의 중량부가 너무 적으면 유연성 및 촉감이 부족하고 너무 많으면 내열성이 떨어져서 Curl을 유지하는 특성이 부족함을 확인할 수 있다. 난연제의 중량부가 너무 적으면 LOI수치가 적게 나와 쉽게 점화 됨을 알 수 있고 난연제의 중량부가 너무 많으면 방사성이 부족함을 확인할 수 있다. 안료분산제의 중량부가 너무 적으면 배합된 안료들의 분산성이 떨어져서 Curl 유지 특성이 떨어짐을 알 수 있고 너무 많으면 방사성이 부족함을 확인할 수 있다.If the weight ratio of the PET copolymer is too small, flexibility and touch are insufficient, and if it is too much, the heat resistance tends to be low, and thus it can be confirmed that the property of maintaining the curl is insufficient. If the weight ratio of the flame retardant is too small, the LOI value is low and it is easily ignited. If the weight ratio of the flame retardant is too large, it can be confirmed that the radiation is insufficient. If the weight ratio of the pigment dispersant is too small, the dispersibility of the formulated pigments deteriorates and curl retention characteristics are deteriorated. If too much, the lack of radioactivity can be confirmed.

소광제를 Total Blending하는 경우 소광제에 따른 소광효과가 없음을 확인할 수 있다.Total blending of the quencher shows no quenching effect with the quencher.

마지막으로 소광제를 포함한 PET수지의 중량부가 너무 적으면 첨가된 양에 비해 광택도가 높아 소광제 첨가에 의한 광택성 증가 효과를 보기 힘들고 너무 많으면 방사성이 부족함을 확인할 수 있다. 이러한 기술적 근거나 자세한 사례는 찾아보기 힘들며, 각 조성의 함량 비율은 Curl 유지특성, LOI, 광택도 및 방사성을 고려하여 최적의 함량을 결정하였다.Finally, if the weight of the PET resin containing the light-quenching agent is too small, it is difficult to see the effect of increasing the gloss due to the addition of the light-quenching agent because of the high glossiness as compared with the added amount. This technical basis and detailed examples are hard to find, and the content ratio of each composition is determined by considering curl retention characteristics, LOI, gloss and radioactivity.

전술한 본 발명의 설명은 예시를 위한 것이며, 본 발명이 속하는 기술 분야의 통상의 지식을 가진 자는 본 발명의 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 쉽게 변형이 가능하다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시예들은 모든 면에서 예시적인 것이며 한정적이 아닌 것으로 이해해야 한다.It will be understood by those skilled in the art that the foregoing description of the present invention is for illustrative purposes only and that those of ordinary skill in the art can readily understand that various changes and modifications may be made without departing from the spirit or essential characteristics of the present invention. will be. It is therefore to be understood that the embodiments described above are in all respects illustrative and not restrictive.

Claims (9)

폴리에틸렌테레프탈레이트(PET) 제1 수지 100 중량부에 대하여, 이소프탈산과 폴리에틸렌테레프탈레이트(PET)의 공중합물 수지 9 내지 40 중량부, 할로겐계 난연제 15 내지 30중량부, 안료분산제 0.5 내지 3 중량부, 및 소광제를 포함하는 폴리에틸렌테레프탈레이트(PET) 제2 수지 20 내지 30 중량부를 포함하고,
상기 소광제를 포함하는 폴리에틸렌테레프탈레이트(PET) 제2 수지는, 폴리에틸렌테레프탈레이트 수지 100중량부에 대하여 소광제를 20 내지 30 중량부 포함하는 것이며, 소광제의 중량평균분자량이 1,200 내지 2,000 인 것을 특징으로 하는, 가발모용 폴리에스터 수지 조성물.
9 to 40 parts by weight of a copolymer resin of isophthalic acid and polyethylene terephthalate (PET), 15 to 30 parts by weight of a halogen-based flame retardant, 0.5 to 3 parts by weight of a pigment dispersant, 100 parts by weight of a polyethylene terephthalate (PET) And 20 to 30 parts by weight of a second polyethylene terephthalate (PET) resin containing a quencher,
The polyethylene terephthalate (PET) second resin comprising the quencher includes 20 to 30 parts by weight of a quenching agent per 100 parts by weight of the polyethylene terephthalate resin, and the quencher has a weight average molecular weight of 1,200 to 2,000 Wherein the polyester resin composition is a wax-like polyester resin composition.
제1항에 있어서,
상기 소광제는 실리케이트인 것을 특징으로 하는, 폴리에스터 수지 조성물.
The method according to claim 1,
Wherein the quencher is a silicate.
제 1 항에 있어서,
상기 폴리에틸렌테레프탈레이트(PET) 제1 수지의 고유 점도는 0.5 내지 1.2 dl/g 인 것을 특징으로 하는, 폴리에스터 수지 조성물.
The method according to claim 1,
Wherein the first resin of the polyethylene terephthalate (PET) resin has an intrinsic viscosity of 0.5 to 1.2 dl / g.
제 1 항에 있어서,
상기 이소프탈산과 폴리에틸렌테레프탈레이트의 공중합물 수지의 고유 점도는 0.5 내지 1.0 dl/g인 것을 특징으로 하는, 폴리에스터 수지 조성물.
The method according to claim 1,
Wherein the copolymer resin of isophthalic acid and polyethylene terephthalate has an intrinsic viscosity of 0.5 to 1.0 dl / g.
제 1 항에 있어서,
상기 할로겐계 난연제는 할로겐의 함량을 50 내지 80중량%로 포함하는 것을 특징으로 하는, 폴리에스터 수지 조성물.
The method according to claim 1,
Wherein the halogen-based flame retardant comprises a halogen content of 50 to 80% by weight.
제 1 항에 있어서,
상기 안료 분산제는 탈크(talc), 유기 핵제, 왁스(WAX), 또는 이들의 혼합물인 것을 특징으로 하는, 폴리에스터 수지 조성물.
The method according to claim 1,
Wherein the pigment dispersant is a talc, an organic nucleating agent, a wax (WAX), or a mixture thereof.
제 1 항에 있어서,
상기 폴리에스터는 한계 산소 지수(Limited Oxygen Index, LOI)값이 24 이상인 것을 특징으로 하는, 폴리에스터 수지 조성물.
The method according to claim 1,
Wherein the polyester has a Limited Oxygen Index (LOI) value of 24 or more.
제 1 항 내지 제 7 항 중 어느 한 항의 폴리에스터 수지 조성물을 포함하는 가발 원사.
A wig yarn comprising the polyester resin composition of any one of claims 1 to 7.
폴리에틸렌테레프탈레이트 수지 100 중량부에 대하여 소광제 20 내지 30 중량부를 포함하는 폴리에틸렌테레프탈레이트 수지를 준비하는 단계(S1);
폴리에틸렌테레프탈레이트 수지 100 중량부에 대하여, 이소프탈산과 폴리에틸렌테레프탈레이트의 공중합물 수지 9 내지 40 중량부, 할로겐계 난연제 15 내지 30 중량부, 안료분산제 0.5 내지 3 중량부, 및 상기 S1 단계의 폴리에틸렌테레프탈레이트 수지 20 내지 30 중량부를 포함하는 폴리에스테르 수지 조성물을 준비하는 단계(S2);
상기 조성물을 용융 방사하는 단계(S3); 및
상기 용융 방사물을 연신하는 단계(S4)를 포함하는 가발 원사의 제조방법.
(S1) preparing a polyethylene terephthalate resin comprising 20 to 30 parts by weight of a quencher relative to 100 parts by weight of a polyethylene terephthalate resin;
9 to 40 parts by weight of a copolymer resin of isophthalic acid and polyethylene terephthalate, 15 to 30 parts by weight of a halogen-based flame retardant, 0.5 to 3 parts by weight of a pigment dispersant, and 0.5 to 3 parts by weight of a polyethylene terephthalate (S2) preparing a polyester resin composition comprising 20 to 30 parts by weight of a phthalate resin;
(S3) melt spinning the composition; And
And a step (S4) of stretching the molten yarn.
KR1020150137900A 2015-09-30 2015-09-30 Polyester resin composition, and molded artice manufactured therefrom KR20170039007A (en)