KR20160077556A - Film for coating attached on surface without base film and method for fabricating the same - Google Patents

Film for coating attached on surface without base film and method for fabricating the same Download PDF

Info

Publication number
KR20160077556A
KR20160077556A KR1020140187593A KR20140187593A KR20160077556A KR 20160077556 A KR20160077556 A KR 20160077556A KR 1020140187593 A KR1020140187593 A KR 1020140187593A KR 20140187593 A KR20140187593 A KR 20140187593A KR 20160077556 A KR20160077556 A KR 20160077556A
Authority
KR
South Korea
Prior art keywords
film
coating film
coating
release film
release
Prior art date
Application number
KR1020140187593A
Other languages
Korean (ko)
Inventor
윤홍승
유관태
진봉재
김윤하
Original Assignee
주식회사 나노기술
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 나노기술 filed Critical 주식회사 나노기술
Priority to KR1020140187593A priority Critical patent/KR20160077556A/en
Publication of KR20160077556A publication Critical patent/KR20160077556A/en

Abstract

The present invention discloses a non-substrate type coating film which is coated on the base material surface by a method for bonding the non-substrate type coating film to a base material surface and curing the non-substrate type coating film bonded to the base material surface. The disclosed non-substrate type coating film according to embodiments of the present invention comprises: a coating film in a sol or gel state; a first release film which is stacked on one side of the coating film to be detachable; and a second release film which is stacked on the other side of the coating film to be detachable. The coating film in the sol or gel state is attached to the surface of a base material, and then cured such that the coating film in the sol or gel state is solidified to the base material surface. One release film of the first release film and the second release film is delaminted from the coating film before the coating film is attached to the base material surface, and the other release film of the first release film and the second release film is delaminted from the coating film after the coating film is attached to the base material surface, and then cured. According to the present invention, the thickness of the coating film applied on the base material surface is uniform, and thickness increase and degradation in light transmittance of the base material can be minimized.

Description

무기재 방식 코팅용 필름 및 이의 제조 방법{Film for coating attached on surface without base film and method for fabricating the same} BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a film for inorganic coating and a method for fabricating the same,

본 발명은, 모재(母材)의 표면 특성이 향상되도록 모재의 표면에 부착되는 코팅용 필름 및 이의 제조 방법에 관한 것이다. The present invention relates to a coating film to be adhered to a surface of a base material so as to improve the surface characteristics of the base material and a method of manufacturing the same.

코팅(coating)은 모재의 표면 특성을 향상시키기 위해 모재의 표면에 특정 물질을 도포하는 것이다. 액상의 코팅제(coating agent)을 모재에 도포하는 습식 코팅(wet coating)의 경우에, 사용되는 도구에 따라 예를 들어, 마이크로 그라비아 롤러(micro gravure roller)를 사용하는 마이크로 그라비아 코팅(micro gravure coating), 콤마 롤러(comma roller)를 사용하는 콤마 코팅(comma coating), 슬롯 다이(slot die)를 사용하는 슬롯 다이 코팅, 분무기로 코팅제를 분무하는 스프레이 코팅(spray coating), 코팅제가 담긴 수조에 모재를 담그는 딥 코팅(dip coating), 모재 위에서 코팅제를 아래로 흘려 모재 표면에 코팅제를 도포하는 플로우 코팅(flow coating) 등으로 구분된다. Coating is the application of a specific material to the surface of the base material to improve the surface properties of the base material. In the case of a wet coating in which a liquid coating agent is applied to a base material, a micro gravure coating using, for example, a micro gravure roller, A comma coating using a comma roller, a slot die coating using a slot die, a spray coating spraying the coating with a sprayer, a spray coating using a sprayer, Dip coating, dip coating, and flow coating, in which a coating agent is applied to the surface of the base material by flowing the coating agent down on the base material.

상기 습식 코팅 방법 중에서 마이크로 그라비아 코팅, 콤마 코팅, 및 슬롯 다이 코팅은 코팅막 두께 조절이 용이하고 박막으로 코팅하기 용이하며, 코팅막의 품질 균일성이 높고, 연속 생산이 용이하여 생산성이 높으나, 예컨대, 필름(film)과 같은 플렉서블(flexible)한 웹(web)을 롤투롤 방식(roll-to-roll type)으로 코팅하는 경우에 적합하여 모재에 제약이 있다. 스프레이 코팅, 딥 코팅, 및 플로우 코팅은 딱딱한 모재에도 적용할 수 있으나, 코팅막 두께 편차, 모재 말단에서 코팅제가 뭉쳐서 처지는 새깅(sagging)과 같은 문제 때문에 코팅 품질의 신뢰성이 떨어진다. Among the above wet coating methods, microgravure coating, comma coating, and slot die coating are easy to control the thickness of the coating film, easy to coat with a thin film, high quality uniformity of the coating film and easy continuous production, it is suitable for coating a flexible web such as a film with a roll-to-roll type, and there is a restriction on the base material. Spray coating, dip coating, and flow coating can also be applied to hard base materials, but the reliability of the coating quality is degraded due to problems such as coating film thickness variation and sagging of the coating material from the base end of the base material.

이에 따라 코팅용 필름을 경성(硬性) 모재의 표면에 부착하여 모재의 표면 특성을 향상시키는 방법도 적용되고 있는데, 통상적인 코팅용 필름은 일 측면에 점착제가 도포된 기재 필름(base film)의 타 측면에 코팅제를 도포하고 경화하여 제조된다. 따라서, 기재 필름과 점착제로 인해 코팅용 필름이 도포된 모재의 두께가 두꺼워지며, 광투과성이 저하될 수 있다. 또한, 코팅용 필름을 모재 표면에 부착한 후 경화시킬 때 기재 필름과 코팅제의 변형율 차이로 인해 코팅용 필름의 변형이나, 심한 경우 모재 자체의 변형을 초래할 수도 있다. A method of improving the surface properties of a base material by attaching a coating film to the surface of a hard base material is also applied. A typical coating film is a base film having a base film coated with a pressure- Applying a coating agent on the side surface and curing. Therefore, the thickness of the base material coated with the coating film becomes thick due to the base film and the pressure-sensitive adhesive, and the light transmittance may be lowered. Further, when the coating film is adhered to the surface of the base material and then cured, the coating film may be deformed due to a difference in deformation rate between the base film and the coating material, or, in severe cases, deformation of the base material itself.

대한민국 등록특허공보 제10-1142628호Korean Patent Publication No. 10-1142628

본 발명은, 모재 표면에 부착하고 경화하는 방법에 의해 모재 표면에 코팅(coating)되는 코팅용 필름으로서, 기재 필름(base film) 없이 박막 형태의 코팅 물질만이 모재 표면에 부착되는 무기재 방식 코팅용 필름과, 이의 제조 방법을 제공한다. The present invention relates to a coating film which is coated on a surface of a base material by a method of adhering to a surface of a base material and curing the base film, And a method for producing the same.

또한 본 발명은, 모재의 표면에 부착하였을 때 모재의 두께 증가와 광투과성 저하를 최소화하며, 코팅층과 모재의 형태 변형이 방지되는 무기재 방식 코팅용 필름과, 이의 제조 방법을 제공한다. Another object of the present invention is to provide a film for an inorganic material coating which minimizes an increase in the thickness of the base material and a decrease in light transmittance when it is adhered to the surface of the base material and prevents the deformation of the coating layer and the base material.

본 발명은, 졸(sol) 또는 겔(gel) 상태의 코팅막, 상기 코팅막의 일 측면에 박리(剝離) 가능하게 적층되는 제1 이형 필름, 및 상기 코팅막의 타 측면에 박리 가능하게 적층되는 제2 이형 필름을 구비하고, 상기 상기 졸 또는 겔 상태의 코팅막은 모재의 표면에 부착된 후 경화되어 상기 모재의 표면에 고착(固着)되고, 상기 제1 이형 필름 및 상기 제2 이형 필름 중 하나의 이형 필름은 상기 코팅막이 상기 모재의 표면에 부착되기 전에 상기 코팅막에서 박리(剝離)되고, 다른 하나의 이형 필름은 상기 코팅막이 상기 모재의 표면에 부착되고 경화된 후에 상기 코팅막에서 박리되는 무기재 방식 코팅용 필름을 제공한다. The present invention provides a method of manufacturing a semiconductor device comprising a coating film in a sol or gel state, a first release film laminated on one side of the coating film so as to be releasable, and a second release film laminated on the other side of the coating film Wherein the sol or gel coating film is adhered to a surface of a base material and then cured and fixed to a surface of the base material, and a release film of one of the first release film and the second release film, The film is peeled off from the coating film before the coating film adheres to the surface of the base material and the other release film is peeled off from the coating film after the coating film is adhered to the surface of the base material and hardened, For example.

상기 제1 이형 필름과 상기 제2 이형 필름은 상기 코팅막에 대한 이형력(release force)이 서로 다를 수 있다. The first release film and the second release film may have different releasing forces with respect to the coating film.

상기 코팅막과 대면(對面)하는 상기 하나의 이형 필름의 측면에는 실리콘계 수지(silicone-based resin)를 포함하는 이형제(離形劑)가 도포되고, 상기 코팅막과 대면하는 상기 다른 하나의 이형 필름의 측면에는 아크릴계 수지(acrylic-based resin) 또는 플루오르계 수지(fluorine-based resin)를 포함하는 이형제가 도포될 수 있다. A releasing agent including a silicone-based resin is applied to a side surface of the one release film facing the coating film, and a side surface of the other release film facing the coating film A mold release agent including an acrylic-based resin or a fluorine-based resin may be applied.

상기 코팅막은 자외선 조사(照射)에 의해 경화될 수 있다. The coating film can be cured by ultraviolet ray irradiation.

상기 코팅막의 재료는, 실란계 수지 및 실록산계 수지로 이루어진 군에서 선택된 적어도 하나의 수지, 및 자외선을 흡수하여 상기 코팅막에 포함된 수지를 중합시키는 광중합 개시제를 포함할 수 있다. The material of the coating film may include at least one resin selected from the group consisting of a silane-based resin and a siloxane-based resin, and a photopolymerization initiator that absorbs ultraviolet light to polymerize the resin contained in the coating film.

상기 코팅막의 재료는 유기물을 포함하지 않을 수 있다. The material of the coating film may not contain an organic substance.

또한 본 발명은, 상기 무기재 방식 코티용 필름을 제조하는 방법으로서, 제1 이형 필름의 일 측면에 액상(液狀)의 코팅제를 도포하는 코팅제 도포 단계, 가열에 의해 상기 제1 이형 필름에 도포된 코팅제에서 용제(solvent)를 증발시켜 졸(sol) 또는 겔(gel) 상태의 코팅막을 형성하는 건조 단계, 및 상기 제1 이형 필름과 대면하는 상기 코팅막의 일 측면과 반대되는, 상기 코팅막의 타 측면에 제2 이형 필름을 부착하는 제2 이형 필름 부착 단계를 구비하는 무기재 방식 코팅용 필름 제조 방법을 제공한다. Further, the present invention provides a method for producing the film for an inorganic protective coating, comprising the steps of: applying a coating agent for applying a liquid coating agent to one side of a first release film; applying the coating agent to the first release film by heating; A drying step of evaporating a solvent in the coated coating agent to form a coating film in a sol or gel state and a drying step of drying the coating film opposite to one side of the coating film facing the first release film, And a second release film attaching step of attaching a second release film to the side surface of the film.

상기 코팅제 도포 단계에서는, 슬롯 다이(slot die), 콤마 롤러(comma roller), 및 마이크로 그라비아 롤러(micro gravure roller) 중 하나를 사용하여 액상의 코팅제를 도포할 수 있다. In the coating application step, a liquid coating may be applied using one of a slot die, a comma roller, and a micro gravure roller.

상기 제2 이형 필름 부착 단계는, 상기 코팅막이 형성된 제1 이형 필름과 상기 제2 이형 필름을, 상기 코팅막과 상기 제2 이형 필름이 서로 마주보게 하고 한 쌍의 밀착된 롤러 사이를 통과시키는 단계를 포함할 수 있다. The step of attaching the second release film may include a step of allowing the first release film and the second release film, on which the coating film is formed, to pass between the pair of closely-spaced rollers, with the coating film and the second release film facing each other .

본 발명의 무기재 방식 코팅용 필름에 의하면, 기재 필름(base film) 없이 박막 형태의 코팅 물질만이 모재 표면에 부착되고 경화되므로, 모재 표면에 도포되는 코팅막의 두께가 균일하고, 코팅막으로 인한 모재의 두께 증가와 광투과성 저하가 최소화된다. According to the film for inorganic coating of the present invention, since only the thin film-like coating material is adhered to and hardened on the surface of the base material without the base film, the thickness of the coating film applied on the surface of the base material is uniform, And the decrease in light transmittance is minimized.

본 발명의 실시예와 같이 코팅막에 실란계 또는 실록산계 수지가 포함되는 경우, 모재의 표면의 경도(hardness)가 커져 표면 손상이 억제되고, 표면을 통한 수분 침투와 산소 침투가 억제되어 제품의 내구성이 향상된다. When the coating film includes a silane-based or siloxane-based resin as in the embodiment of the present invention, the hardness of the surface of the base material is increased, thereby suppressing surface damage, suppressing moisture penetration and oxygen penetration through the surface, .

또한, 모재 표면에 부착되는 코팅막이 경화되면서 수축되지 않으며 기재 필름이 구비되지 않으므로, 기재 필름과 코팅막의 변형율 차이로 인한 모재와 코팅막의 분리 및 모재의 형태 변형이 방지된다. Further, since the coating film adhering to the surface of the base material is not cured and is not shrunk and the base film is not provided, the separation of the base material and the coating film due to the difference in strain between the base film and the coating film and the shape deformation of the base material are prevented.

도 1 내지 도 3은 본 발명의 실시예에 따른 무기재 방식 코팅용 필름 제조 방법을 순차적으로 도시한 구성도이다.
도 4 내지 도 7은 본 발명의 실시예에 따른 무기재 방식 코팅용 필름을 이용하여 모재의 표면을 코팅하는 과정을 순차적으로 도시한 도면이다. FIGS. 1 to 3 are schematic views sequentially illustrating a method for producing an inorganic coating film according to an embodiment of the present invention.
FIGS. 4 to 7 are views sequentially illustrating a process of coating a surface of a base material using a film for coating with an inorganic coating according to an embodiment of the present invention.

이하, 첨부된 도면을 참조하여 본 발명의 실시예에 따른 무기재 방식 코팅용 필름 및 이의 제조 방법을 상세하게 설명한다. 본 명세서에서 사용되는 용어(terminology)들은 본 발명의 바람직한 실시예를 적절히 표현하기 위해 사용된 용어들로서, 이는 사용자 또는 운용자의 의도 또는 본 발명이 속하는 분야의 관례 등에 따라 달라질 수 있다. 따라서, 본 용어들에 대한 정의는 본 명세서 전반에 걸친 내용을 토대로 내려져야 할 것이다.Hereinafter, an inorganic coating film and a method of manufacturing the same according to an embodiment of the present invention will be described in detail with reference to the accompanying drawings. The terminology used herein is a term used to properly express the preferred embodiment of the present invention, which may vary depending on the intention of the user or operator or the custom of the field to which the present invention belongs. Therefore, the definitions of these terms should be based on the contents throughout this specification.

도 1 내지 도 3은 본 발명의 실시예에 따른 무기재 방식 코팅용 필름 제조 방법을 순차적으로 도시한 구성도이다. 도 4를 먼저 참조하면, 본 발명의 실시예에 따른 무기재 방식 코팅용 필름(1)은 코팅막(5)과 코팅막(5)의 하측면과 상측면에 각각 박리(剝離) 가능하게 적층되는 제1 이형 필름(3)과 제2 이형 필름(7)을 구비한다. 코팅막(5)은 졸(sol) 또는 젤(gel) 상태의 층(layer)으로, 자외선(UV: ultraviolet ray)이 조사(照射)되면 단단하게 경화되는 성질을 갖는다. FIGS. 1 to 3 are schematic views sequentially illustrating a method for producing an inorganic coating film according to an embodiment of the present invention. Referring to FIG. 4, a film 1 for coating with inorganic coating according to an embodiment of the present invention includes a coating layer 5 and a coating layer 5, which are laminated on the lower and upper surfaces of the coating layer 5, 1 release film (3) and a second release film (7). The coating film 5 is a layer in a sol or gel state and has a property of being hardened hardly when irradiated with ultraviolet rays.

코팅막(5)의 재료에는, 기본 수지(base resin)인 올리고머와, 반응성 희석제로서 역할을 하는 모노머와, 광중합 개시제와, 소량의 첨가제가 포함된다. 모재(30)(도 5 참조)의 표면을 충격에 강하도록 경화시키고, 모재(30) 표면의 방습성(防濕性), 발수성(撥水性), 방식성(防蝕性)이 향상되도록, 상기 올리고머 및 모노머로서는 실란계 수지(silane-based resin) 및 실록산계 수지(siloxane-based resin)로 이루어진 군(群)에서 선택된 적어도 하나의 수지가 포함된다. 예를 들어, 실란계 수지에는 이소부틸 트리메톡시 실란, 이소옥틸 트리메톡시 실란 등이 있고, 실록산계 수지에는 폴리아크릴 실록산(Polyacrylsiloxane), 폴리아크릴-우레탄 실록산(Polyacryl-uratansiloxane), 폴리에폭시 실록산(polyepoxysilxone) 등이 있다. 또한, 상기 코팅막(5)의 재료로서 유기물은 포함되지 않는다. 상기 광중합 개시제는 자외선을 흡수하여 라디칼 혹은 양이온을 생성시켜 코팅막(5)에 포함된 수지(resin)의 중합을 개시하는 역할을 한다. The material of the coating film 5 includes an oligomer as a base resin, a monomer serving as a reactive diluent, a photopolymerization initiator, and a small amount of an additive. The surface of the base material 30 (see FIG. 5) is hardened so that the surface of the base material 30 is hardened by impact, and the surface of the base material 30 is coated with the oligomer And monomers include at least one resin selected from the group consisting of silane-based resin and siloxane-based resin. Examples of the silane-based resin include isobutyltrimethoxysilane and isooctyltrimethoxysilane. Siloxane-based resins include polyacrylsiloxane, polyacryl-uratansiloxane, polyepoxysiloxane, (polyepoxysilxone). In addition, an organic material is not included as the material of the coating film 5. [ The photopolymerization initiator absorbs ultraviolet light to generate radicals or cations and initiates polymerization of the resin contained in the coating film 5.

코팅막(5)의 재료로서 실란계 수지 또는 실록산계 수지가 적용됨으로써 자외선 조사에 의해 코팅막(5)이 경화될 때 수축되지 않고 이완되는 특성이 있고, 이로 인해 모재(30)(도 6 참조)에 고착된 때 모재(30)의 변형이 방지되는 효과가 있다. 또한, 코팅막(5)의 재료로서 유기물이 포함되지 않고 무기물이 포함되므로 코팅막(5)이 경화되었을 때 경도(硬度)가 커져 모재(30)의 표면 손상 억제 효과가 향상된다. When the coating film 5 is applied with a silane-based resin or a siloxane-based resin, the coating film 5 is not shrunk and relaxed when the coating film 5 is cured by irradiation of ultraviolet rays. There is an effect that deformation of the base material 30 is prevented when it is fixed. Since the coating film 5 does not contain an organic substance but contains an inorganic substance, the hardness of the coating film 5 is increased when the coating film 5 is cured, thereby improving the effect of suppressing surface damage of the base material 30.

제1 이형 필름(3)과 제2 이형 필름(7)은, 예컨대, PET(Polyethylene phthalate)와 같은 수지로 된 플렉서블(flexible)한 필름으로, 코팅막(5)으로 모재(30)(도 5 참조) 표면을 도포할 때 제1 이형 필름(3)과 제2 이형 필름(7)이 코팅막(5)에서 쉽게 박리되도록 각 이형 필름(3, 7)의 코팅막(5)과 대면(對面)하는 측면(4, 8)에는 이형제(離形劑)가 도포되어 있다. 한 쌍의 이형 필름(3, 7) 중 하나의 이형 필름이 다른 하나의 이형 필름보다 코팅막(5)에서 더 쉽게 박리(剝離)되도록, 즉 코팅막(5)에 대한 이형력(release force)이 차이가 나도록 제1 이형 필름(3)과 제2 이형 필름(7)에는 서로 다른 이형제가 도포된다. 상기 이형력은 박리도(剝離度)라고도 한다. The first release film 3 and the second release film 7 are flexible films made of a resin such as PET (polyethylene phthalate) (5) of the release films (3, 7) so that the first release film (3) and the second release film (7) are easily peeled off from the coating film (5) (4, 8) is coated with a releasing agent. The releasing film of one of the pair of releasing films 3 and 7 is more easily peeled off from the coating film 5 than the other releasing film, Different mold release agents are applied to the first release film 3 and the second release film 7 so that the release film is formed. The releasing force is also referred to as the releasing degree.

예를 들어, 한 쌍의 이형 필름(3, 7) 중 상대적으로 쉽게 박리되는 이형 필름에는 실리콘계 수지(silicone-based resin)를 포함하는 이형제가 도포되고, 한 쌍의 이형 필름(3, 7) 중 상대적으로 어렵게 박리되는 이형 필름에는 아크릴계 수지(acrylic-based resin) 또는 플루오르계 수지(fluorine-based resin)를 포함하는 이형제가 도포된다. 여기서, 상대적으로 쉽게 박리된다는 것은 이형 필름(3, 7)을 코팅막(5)에서 박리할 때 상대적으로 작은 이형력을 가하여 박리할 수 있다는 것을 의미한다. 한편, 본 발명의 실시예에 따라서, 한 쌍의 이형 필름(3, 7) 중에 제1 이형 필름(3)이 제2 이형 필름(7)보다 더 쉽게 박리될 수도 있고, 반대로 제2 이형 필름(7)이 제1 이형 필름(3)보다 더 쉽게 박리될 수도 있다. For example, a releasing film containing a silicone-based resin is applied to a releasing film relatively easily peeled out of the pair of releasing films 3 and 7, The releasing film, which is relatively difficult to peel off, is coated with a release agent comprising an acrylic-based resin or a fluorine-based resin. Here, relatively easily peeled off means that the release films 3 and 7 can be peeled off by applying a relatively small releasing force when peeling off the coating film 5 from the coating film 5. On the other hand, according to the embodiment of the present invention, the first release film 3 may be more easily peeled off from the pair of release films 3 and 7 than the second release film 7, 7 may be more easily peeled off than the first release film 3.

도 1 내지 도 3을 함께 참조하면, 무기재 방식 코팅용 필름(1)의 제조 방법은, 코팅제 도포 단계, 건조 단계, 및 제2 이형 필름 부착 단계를 구비한다. 도 1 내지 도 3에 도시된 실시 예 에서는 롤투롤 방식(roll-to-roll type)으로 무기재 방식 코팅용 필름(1)이 생산된다. 부연하면, 제1 이형 필름 공급 롤러(11)에 권취된 제1 이형 필름(3)과, 제2 이형 필름 공급 롤러(20)에 권취된 제2 이형 필름(7)이 각각 제1 이형 필름 공급 롤러(11)와 제2 이형 필름 공급 롤러(20)에서 풀려 끊김 없이 연속적으로 공급되고, 완성된 무기재 방식 코팅용 필름(1)이 코팅용 필름 회수 롤러(27)를 통해 권취되어 회수된다. Referring to Figs. 1 to 3 together, the method for producing the film for inorganic coating (1) comprises a coating application step, a drying step, and a second release film attaching step. In the embodiment shown in FIGS. 1 to 3, a film 1 for inorganic coating is produced in a roll-to-roll type. The first release film 3 wound around the first release film feed roller 11 and the second release film 7 wound around the second release film feed roller 20 are fed to the first release film supply roller 11, The film 1 is unwound from the roller 11 and the second release film feed roller 20 continuously and seamlessly, and the completed film for inorganic coating film 1 is wound and recovered through the film recovery roller 27 for coating.

도 1을 참조하면, 상기 코팅제 도포 단계는, 제1 이형 필름 공급 롤러(11)에서 공급되는 제1 이형 필름(3)의 상측면(4)에 액상(液狀)의 코팅제(5a)를 도포하는 단계이다. 상기 코팅제는 상기 코팅막(5)의 재료인 올리고머, 모노머, 광중합 개시제, 및 소량의 첨가제가 용제(solvent)에 혼합 용융된 것으로, 액체 상태 내지 콜로이드 상태이다. 1, the applying of the coating agent is performed by applying a liquid coating agent 5a to the upper side 4 of the first release film 3 fed from the first release film feeding roller 11, . The coating agent is a liquid state or a colloid state in which an oligomer, a monomer, a photopolymerization initiator, and a small amount of an additive, which are materials of the coating film 5, are mixed and melted in a solvent.

제1 이형 필름(3)이 지지 롤러(13)에 지지되어 진행할 때 슬롯 다이(15)를 통해 제1 이형 필름(3)의 상측면에 코팅제(5a)가 도포된다. 도 1에 도시된 바와 달리 콤마 롤러(comma roller) 또는 마이크로 그라비아 롤러(micro gravure roller)를 이용하여 통해 제1 이형 필름(3)의 상측면에 코팅제(5a)를 도포할 수도 있다. 슬롯 다이(15), 콤마 롤러, 또는 마이크로 그라비아 롤러를 이용하여 코팅제(5a)를 도포하는 방법은 스프레이 코팅(spray coating), 딥 코팅(dip coating), 또는 플로우 코팅(flow coating)에 의해 코팅제(5a)를 도포하는 것보다 코팅층의 두께를 얇게 하고, 균일하게 조절하기 용이한 장점이 있다. The coating agent 5a is applied to the upper surface of the first release film 3 through the slot die 15 when the first release film 3 is supported by the support roller 13 and proceeds. The coating agent 5a may be coated on the upper surface of the first release film 3 by using a comma roller or a micro gravure roller, as shown in FIG. The method of applying the coating agent 5a using the slot die 15, the comma roller, or the microgravure roller may be performed by spray coating, dip coating, or flow coating, The thickness of the coating layer can be made thinner and uniformly adjusted.

도 2를 참조하면, 건조 단계는 열(熱)을 가하여 제1 이형 필름(3)에 도포된 코팅제(5a)(도 1 참조)에서 용제(solvent)를 증발시켜 졸(sol) 또는 겔(gel) 상태의 코팅막(5)을 형성하는 단계이다. 부연하면, 코팅제(5a)가 도포된 제1 이형 필름(3)이 건조기를 통과할 때 건조기 내에서 제1 이형 필름(3)은 가이드 롤러들(17, 18)에 지지되어 일 방향으로 진행하고, 건조기 내의 복사열(H)과 열풍(熱風)으로 솔벤트가 증발된다. 솔벤트가 증발되어 졸 또는 겔 상태가 된 코팅막(5)은 점착성과 탄성을 띄며, 제1 이형 필름(3)의 상측면(4)에 도포된 이형제에 의해 코팅막(5)은 상기 상측면(4)에 약하게 점착된다. 2, the drying step is performed by applying heat to evaporate the solvent from the coating agent 5a (see FIG. 1) applied to the first release film 3 to form a sol or a gel gel ) Coating film 5 is formed. In addition, when the first release film 3 coated with the coating agent 5a passes through the dryer, the first release film 3 is supported by the guide rollers 17 and 18 in the dryer and proceeds in one direction , The solvent is evaporated by radiant heat (H) and hot air in the dryer. The coating film 5 having a solvent or a solvent evaporated to become a sol or gel state has adhesiveness and elasticity and the coating film 5 is coated on the upper side 4 of the first release film 3 by the release agent applied to the upper side 4 of the first release film 3 ).

도 3을 참조하면, 제2 이형 필름 부착 단계는, 제1 이형 필름(3)에 적층 형성된 코팅막(5)의 상측면에 제2 이형 필름(7)을 부착하는 단계이다. 이형 필름 부착기(22)는 한 쌍의 밀착된 롤러(23, 24)를 구비한다. 건조기를 통과하여 코팅막(5)이 형성된 제1 이형 필름(3)과 제2 이형 필름 공급 롤러(20)에서 풀려 공급되는 제2 이형 필름(7)을, 코팅막(5)과 제2 이형 필름(7)이 마주보게 하고 상기 한 쌍의 밀착된 롤러(23, 24) 사이를 통과시킴으로써 제2 이형 필름(7)이 코팅막(5) 상측면에 부착된다. 제2 이형 필름(7)의 하측면(8)에 도포된 이형제에 의해 코팅막(5)은 상기 하측면(8)에 약하게 점착된다. Referring to Fig. 3, the second release film attaching step is a step of attaching the second release film 7 to the upper side of the coating film 5 formed by laminating the first release film 3 on the upper side. The release film attacher 22 has a pair of closely spaced rollers 23, 24. The first release film 3 on which the coating film 5 is formed and the second release film 7 released from the second release film supply roller 20 are passed through the dryer to form the coating film 5 and the second release film The second release film 7 is adhered to the side surface of the coating film 5 by passing the first release film 7 and the second release film 7 between the pair of the contact rollers 23 and 24 facing each other. The coating film 5 is weakly adhered to the lower side surface 8 by the releasing agent applied to the lower side surface 8 of the second release film 7.

상술한 바와 같이, 코팅막(5)에 대한 제1 이형 필름(3)의 박리성과 제2 이형 필름(7)의 박리성은 서로 다르다. 제1 이형 필름(3)에 적층된 코팅막(5)에 제2 이형 필름(7)이 부착됨으로써 무기재 방식 코팅용 필름(1)이 형성되고, 상기 무기재 방식 코팅용 필름(1)은 코팅용 필름 회수 롤러(27)에 권취되어 회수된다. As described above, the peeling property of the first release film 3 and the peeling property of the second release film 7 with respect to the coating film 5 are different from each other. The inorganic release coating film 1 is formed by attaching the second release film 7 to the coating film 5 laminated on the first release film 3, Film winding rollers 27 and is recovered.

도 4 내지 도 7은 본 발명의 실시예에 따른 무기재 방식 코팅용 필름을 이용하여 모재의 표면을 코팅하는 과정을 순차적으로 도시한 도면이다. 먼저, 도 4를 참조하면, 무기재 방식 코팅용 필름(1)의 제1 및 제2 이형 필름(3, 7) 중 하나를 코팅막(5)에서 벗겨내 제거한다. FIGS. 4 to 7 are views sequentially illustrating a process of coating a surface of a base material using a film for coating with an inorganic coating according to an embodiment of the present invention. First, referring to FIG. 4, one of the first and second release films 3 and 7 of the inorganic film coating film 1 is peeled off from the coating film 5.

만약 코팅막(5)에 대한 제1 이형 필름(3)과 제2 이형 필름(7)의 이형력이 같거나 비슷하면 제1 및 제2 이형 필름(3, 7) 중 하나의 이형 필름만 코팅막(5)에서 벗겨내기가 용이하지 않을 뿐 아니라 벗겨내는 이형 필름에 코팅막(5)의 일 부분이 붙어 떨어져 나가게 되어 코팅막(5)이 손상될 수 있다. 그러나, 본 발명의 실시예와 같이 제1 이형 필름(3)과 제2 이형 필름(7)의 이형력이 크게 차이 나는 경우에는 한 쌍의 이형 필름(3, 7) 중 이형력이 더 작은 이형 필름, 즉 더 쉽게 박리되는 이형 필름이 코팅막(5)에서 벗겨지고, 다른 하나의 이형 필름은 코팅막(5)에 부착된 상태로 유지되며 코팅막(5)에도 손상이 발생되지 않게 된다.If the first release film 3 and the second release film 7 have the same or similar releasing force to the coating film 5, only one release film of the first and second release films 3 and 7 5, it is not easy to peel off, and at the same time, a part of the coating film 5 adheres to the releasing film peeling off, so that the coating film 5 may be damaged. However, when the releasing force of the first release film 3 and the second release film 7 is greatly different from each other as in the embodiment of the present invention, the releasing force of the pair of release films 3, The film, that is, the releasing film which is more easily peeled off is peeled off from the coating film 5, the other releasing film remains attached to the coating film 5, and the coating film 5 is also not damaged.

한편, 이형 필름(3, 7)에 도포되는 이형제의 성분 함유량을 조절하여 이형 필름(3, 7)과 코팅막(5) 사이의 이형력과, 코팅막(5)의 도포성('wetting feature' 라고도 한다)을 조절할 수 있다. 예를 들어, 이형제가 실리콘계 수지를 포함하는 실리콘계 이형제인 경우에 실리콘계 수지가 10 내지 80 wt% 함유되는 것이 바람직하며, 이형제가 플루오르계 수지를 포함하는 플루오르계 이형제인 경우에 플루오르계 수지가 2 내지 20 wt% 함유되는 것이 바람직하다. On the other hand, by adjusting the component content of the releasing agent applied to the releasing films 3 and 7, the releasing force between the releasing films 3 and 7 and the coating film 5 and the coating property of the coating film 5 Can be adjusted. For example, when the releasing agent is a silicone type releasing agent containing a silicone resin, it is preferable that the silicone resin is contained in an amount of 10 to 80 wt%, and when the releasing agent is a fluorine type releasing agent containing a fluorine resin, And more preferably 20 wt%.

한편, 첨부된 도면의 실시예에서는 제1 이형 필름(3)이 제2 이형 필름(7)보다 코팅막(5)에서 더 쉽게 박리되고, 제2 이형 필름(7)보다 먼저 제1 이형 필름(3)이 박리되는 것으로 도시되어 있으나, 이는 예에 불과하며 반대의 경우도 가능하다. On the other hand, in the embodiment of the accompanying drawings, the first release film 3 is more easily peeled off from the coating film 5 than the second release film 7, and the first release film 3 ) Is shown as being peeled off, but this is merely an example, and the opposite case is also possible.

도 5를 참조하면, 모재(30)의 표면과 코팅막(5)의 노출된 측면이 마주보도록 코팅막(5)을 모재(30)의 표면에 부착한다. 도 5 내지 도 7에는 곡면형 디스플레이 패널이 모재(30)의 예로서 도시되어 있으나, 본 발명에 따른 무기재 방식 코팅용 필름(1)(도 4 참조)의 적용 대상은 이에 한정되는 것은 아니다. 도 5에 도시되진 않았으나, 고무와 같은 탄성 소재로 된 롤러(roller)나 스퀴지(squeegee)로 제2 이형 필름(7)을 모재(30)에 대해 가압하여 코팅막(5)을 모재(30)의 표면에 부착할 수 있으며, 이때 모재(30)이 표면과 코팅막(5) 사이에 기포가 생기지 않도록 유의하여야 한다. 5, the coating film 5 is attached to the surface of the base material 30 so that the surface of the base material 30 and the exposed side of the coating film 5 face each other. 5 to 7 illustrate a curved display panel as an example of the base material 30, but the application of the film 1 for inorganic coating according to the present invention (see FIG. 4) is not limited thereto. 5, the second release film 7 is pressed against the base material 30 by a roller or a squeegee made of an elastic material such as rubber, so that the coating film 5 is pressed against the base material 30 So that bubbles are not formed between the surface of the base material 30 and the coating film 5. In this case,

도 6을 참조하면, 자외선 경화기 내에 코팅막(5)이 부착된 모재(30)를 넣거나 통과시키면서 자외선(UV)을 상기 코팅막(5)에 조사한다. 그리하면 코팅막(5)이 경화되면서 모재(30)의 표면에 고착(固着)된다. Referring to FIG. 6, ultraviolet rays (UV) are irradiated onto the coating film 5 while the base material 30 with the coating film 5 is inserted or passed through the ultraviolet curing unit. Thus, the coating film 5 is hardened and fixed to the surface of the base material 30.

도 7을 참조하면, 경화된 코팅막(5) 상측면에 부착된 제2 이형 필름(7)을 벗겨내 모재(30) 표면에 경화된 코팅막(5)만 남긴다. 코팅막(5)은 이미 경화되어 있고, 모재(30) 표면에 고착되어 있으므로 제2 이형 필름(7)은 코팅막(5)에서 쉽게 벗겨지고 코팅막(5)은 손상되지 않는다. 상술한 바와 같이, 기재 필름(base film) 없이 코팅막(5)만이 모재(30) 표면에 부착되고 경화되므로, 모재(30) 표면에 도포되는 코팅막(5)의 두께가 균일하고, 코팅막(5)의 부가로 인한 모재(30)의 두께 증가와 광투과성 저하가 최소화된다. Referring to FIG. 7, the second release film 7 attached to the side of the cured coating film 5 is peeled off, leaving only the cured coating film 5 on the surface of the base material 30. Since the coating film 5 is already cured and fixed on the surface of the base material 30, the second release film 7 is easily peeled off from the coating film 5 and the coating film 5 is not damaged. Only the coating film 5 is adhered to the surface of the base material 30 and hardened without the base film so that the thickness of the coating film 5 applied to the surface of the base material 30 is uniform and the thickness of the coating film 5 is uniform, The increase of the thickness of the base material 30 and the decrease of light transmittance are minimized.

코팅막(5)에 실란계 또는 실록산계 수지가 포함되어 있으므로, 모재(30)의 표면의 경도(hardness)가 커져 표면 손상이 억제되고, 표면을 통한 수분 침투와 산소 침투가 억제되어 제품의 내구성이 향상된다. 모재(30) 표면에 부착되는 코팅막(5)이 경화되면서 수축되지 않으며 기재 필름이 구비되지 않으므로, 기재 필름과 코팅막의 변형율 차이로 인한 모재(30)와 코팅막(5)의 분리 및 모재(30)의 형태 변형이 방지된다. Since the coating film 5 contains the silane-based or siloxane-based resin, the hardness of the surface of the base material 30 is increased to suppress surface damage, and moisture penetration and oxygen penetration through the surface are suppressed, . Since the coating film 5 adhering to the surface of the base material 30 does not shrink as it is cured and the base film is not provided, the separation of the base material 30 and the coating film 5 due to the difference in strain between the base film and the coating film, Is prevented from being deformed.

본 발명은 도면에 도시된 실시예를 참고로 설명되었으나 이는 예시적인 것에 불과하며, 당해 분야에서 통상의 지식을 가진 자라면 이로부터 다양한 변형 및 균등한 타 실시예가 가능함을 이해할 수 있을 것이다. 따라서 본 발명의 진정한 보호범위는 첨부된 특허청구범위에 의해서만 정해져야 할 것이다. While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it will be understood by those skilled in the art that various changes and modifications may be made without departing from the scope of the present invention. Therefore, the true scope of protection of the present invention should be defined only by the appended claims.

1: 무기재 방식 코팅용 필름 3: 제1 이형 필름
5: 코팅막 7: 제2 이형 필름
11: 제1 이형 필름 공급 롤러 15: 슬롯 다이
20: 제2 이형 필름 공급 롤러 22: 이형 필름 부착기
27: 코팅용 필름 회수 롤러 30: 모재1: Inorganic coating film for coating 3: First release film
5: Coating film 7: Second release film
11: first release film feed roller 15: slot die
20: second release film feeding roller 22: releasing film attaching machine
27: coating film collecting roller 30: base material

Claims (9)

졸(sol) 또는 겔(gel) 상태의 코팅막; 상기 코팅막의 일 측면에 박리(剝離) 가능하게 적층되는 제1 이형 필름; 및, 상기 코팅막의 타 측면에 박리 가능하게 적층되는 제2 이형 필름;을 구비하고,
상기 졸 또는 겔 상태의 코팅막은 모재의 표면에 부착된 후 경화되어 상기 모재의 표면에 고착(固着)되고,
상기 제1 이형 필름 및 상기 제2 이형 필름 중 하나의 이형 필름은 상기 코팅막이 상기 모재의 표면에 부착되기 전에 상기 코팅막에서 박리(剝離)되고, 다른 하나의 이형 필름은 상기 코팅막이 상기 모재의 표면에 부착되고 경화된 후에 상기 코팅막에서 박리되는 것을 특징으로 하는 무기재 방식 코팅용 필름. A coating film in a sol or gel state; A first release film laminated on one side of the coating film so as to be peeled off; And a second release film which is peelably laminated on the other side of the coating film,
The sol or gel coating film is adhered to the surface of the base material and cured and fixed to the surface of the base material,
Wherein one of the first release film and the second release film is peeled off from the coating film before the coating film is adhered to the surface of the base material and the other release film is peeled off from the surface of the base material And is peeled off from the coating film after being cured. 제1 항에 있어서,
상기 제1 이형 필름과 상기 제2 이형 필름은 상기 코팅막에 대한 이형력(release force)이 서로 다른 것을 특징으로 하는 무기재 방식 코팅용 필름. The method according to claim 1,
Wherein the first release film and the second release film have different releasing forces with respect to the coating film. 제2 항에 있어서,
상기 코팅막과 대면(對面)하는 상기 하나의 이형 필름의 측면에는 실리콘계 수지(silicone-based resin)를 포함하는 이형제(離形劑)가 도포되고, 상기 코팅막과 대면하는 상기 다른 하나의 이형 필름의 측면에는 아크릴계 수지(acrylic-based resin) 또는 플루오르계 수지(fluorine-based resin)를 포함하는 이형제가 도포된 것을 특징으로 하는 무기재 방식 코팅용 필름. 3. The method of claim 2,
A releasing agent including a silicone-based resin is applied to a side surface of the one release film facing the coating film, and a side surface of the other release film facing the coating film Characterized in that the releasing agent is coated with a release agent comprising an acrylic-based resin or a fluorine-based resin. 제1 항에 있어서,
상기 코팅막은 자외선 조사(照射)에 의해 경화되는 것을 특징으로 하는 무기재 방식 코팅용 필름. The method according to claim 1,
Wherein the coating film is cured by irradiation with ultraviolet light. 제4 항에 있어서,
상기 코팅막의 재료는, 실란계 수지 및 실록산계 수지로 이루어진 군에서 선택된 적어도 하나의 수지, 및 자외선을 흡수하여 상기 코팅막에 포함된 수지를 중합시키는 광중합 개시제를 포함하는 것을 특징으로 하는 무기재 방식 코팅용 필름. 5. The method of claim 4,
Wherein the material of the coating film includes at least one resin selected from the group consisting of a silane-based resin and a siloxane-based resin, and a photopolymerization initiator that absorbs ultraviolet light to polymerize the resin contained in the coating film Film. 제5 항에 있어서,
상기 코팅막의 재료는 유기물을 포함하지 않는 것을 특징으로 하는 무기재 방식 코팅용 필름. 6. The method of claim 5,
Wherein the material of the coating film does not contain an organic substance. 제1 항 내지 제6 항 중 어느 한 항의 무기재 방식 코티용 필름을 제조하는 방법으로서,
제1 이형 필름의 일 측면에 액상(液狀)의 코팅제를 도포하는 코팅제 도포 단계; 가열에 의해 상기 제1 이형 필름에 도포된 코팅제에서 용제(solvent)를 증발시켜 졸(sol) 또는 겔(gel) 상태의 코팅막을 형성하는 건조 단계; 및, 상기 제1 이형 필름과 대면하는 상기 코팅막의 일 측면과 반대되는, 상기 코팅막의 타 측면에 제2 이형 필름을 부착하는 제2 이형 필름 부착 단계;를 구비하는 것을 특징으로 하는 무기재 방식 코팅용 필름 제조 방법. A method for producing an inorganic protective coating film according to any one of claims 1 to 6,
Applying a coating agent for applying a liquid coating agent to one side of the first release film; A drying step of evaporating a solvent in a coating agent applied to the first release film by heating to form a coating film in a sol or gel state; And a second release film attaching step of attaching a second release film to the other side of the coating film opposite to one side of the coating film facing the first release film, Film. 제7 항에 있어서,
상기 코팅제 도포 단계에서는, 슬롯 다이(slot die), 콤마 롤러(comma roller), 및 마이크로 그라비아 롤러(micro gravure roller) 중 하나를 사용하여 액상의 코팅제를 도포하는 것을 특징으로 하는 무기재 방식 코팅용 필름 제조 방법. 8. The method of claim 7,
Characterized in that in the step of applying the coating agent, a liquid coating agent is applied using one of a slot die, a comma roller, and a micro gravure roller. Gt; 제7 항에 있어서,
상기 제2 이형 필름 부착 단계는, 상기 코팅막이 형성된 제1 이형 필름과 상기 제2 이형 필름을, 상기 코팅막과 상기 제2 이형 필름이 서로 마주보게 하고 한 쌍의 밀착된 롤러 사이를 통과시키는 단계;를 포함하는 것을 특징으로 하는 무기재 방식 코팅용 필름 제조 방법. 8. The method of claim 7,
The step of attaching the second release film comprises passing the first release film and the second release film on which the coating film is formed between the pair of closely spaced rollers so that the coating film and the second release film face each other; ≪ / RTI > wherein the inorganic filler comprises at least one inorganic filler.
KR1020140187593A 2014-12-23 2014-12-23 Film for coating attached on surface without base film and method for fabricating the same KR20160077556A (en)