KR20160065309A - Composition for stabilizing asbestos and treatment method for suppressing asbestos using the same - Google Patents

Composition for stabilizing asbestos and treatment method for suppressing asbestos using the same Download PDF

Info

Publication number
KR20160065309A
KR20160065309A KR1020140168608A KR20140168608A KR20160065309A KR 20160065309 A KR20160065309 A KR 20160065309A KR 1020140168608 A KR1020140168608 A KR 1020140168608A KR 20140168608 A KR20140168608 A KR 20140168608A KR 20160065309 A KR20160065309 A KR 20160065309A
Authority
KR
South Korea
Prior art keywords
asbestos
stabilization
parts
weight
silicate
Prior art date
Application number
KR1020140168608A
Other languages
Korean (ko)
Other versions
KR101666909B1 (en
Inventor
이상명
이준철
Original Assignee
이상명
이준철
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 이상명, 이준철 filed Critical 이상명
Priority to KR1020140168608A priority Critical patent/KR101666909B1/en
Publication of KR20160065309A publication Critical patent/KR20160065309A/en
Application granted granted Critical
Publication of KR101666909B1 publication Critical patent/KR101666909B1/en

Abstract

The present invention relates to a composition of a treating agent for stabilizing asbestos by which asbestos can be chemically stabilized as it effectively penetrates into an building material containing asbestos and discharge or spattering of asbestos can be prevented even in the presence of an external impact, and a method for stabilizing asbestos using the composition. The composition of a treating agent for stabilizing asbestos according to the present invention includes: an alkali metal silicate that is selected from a group consisting of lithium silicate, sodium silicate, and potassium silicate; a silane composite that is selected from a group consisting of dimethyl dimethoxy silane, ethyl trimethoxy silane, methyl trimethoxy silane, and gamma-glicidyl oxypropyl trimethoxy silane; a polyatomic doner that is selected from a group consisting of lead titanate and a lead zirconate., and water.

Description

석면 안정화용 처리제 조성물 및 이를 이용한 석면 안정화 처리 방법 {Composition for stabilizing asbestos and treatment method for suppressing asbestos using the same}TECHNICAL FIELD The present invention relates to an asbestos stabilizing treatment composition and a method of stabilizing asbestos using the same,

본 발명은 석면함유 건축자재를 안정화하는 석면 안정화용 처리제 조성물 및 이를 이용한 석면의 안정화 처리 방법에 관한 것이다.The present invention relates to a treating composition for stabilizing asbestos-containing building materials and a method for treating asbestos using the same.

보다 구체적으로, 본 발명은 석면을 함유한 건축자재에 효과적으로 침투하여 석면을 화학적으로 안정화시킬 수 있고, 외부 충격에도 석면의 유출 또는 비산을 방지할 수 있는 석면 안정화용 처리제 조성물 및 이를 이용한 석면 안정화 처리 방법에 관한 것이다.More particularly, the present invention relates to a treatment composition for stabilizing asbestos, which can effectively stabilize the asbestos by penetrating effectively the building material containing asbestos and prevent the leakage or scattering of the asbestos against external impact, ≪ / RTI >

우리나라는 급격한 근대화 과정을 거치면서 건축에 석면이 포함된 건축자재를 다량 사용해왔다. 석면은 마그네슘과 규소를 포함하고 있는 광물질이며, 단열성, 불연성, 내구성, 절연성이 우수하고 가격도 저렴하여 오래 전부터 천정재, 보온 단열재, 방음재, 지붕재(slate) 등 건축자재로 각광을 받아왔다.Korea has been using a lot of building materials containing asbestos in its architecture during the rapid modernization process. Asbestos is a mineral containing magnesium and silicon, and has long been in the limelight as a building material such as ceiling material, insulation material, sound insulation material, slate and so on since it is excellent in heat insulation, incombustibility, durability, insulation and price.

그러나 최근에 와서 석면이 석면폐, 폐암, 악성중피종 등 많은 질병 유발의 요인이 되는 것이 밝혀졌고, 석면이 포함된 건축자재가 인체에 치명적인 해를 입힐 수 있다는 사실이 알려지면서, 석면의 사용이 규제되고 있다.However, recently, it has been found that asbestos is a cause of many diseases such as asbestosis, lung cancer, and mesothelioma, and it is known that building materials containing asbestos can cause fatal harm to the human body. have.

그러나 석면의 사용 규제 전부터 지하철과 같은 공공구조물, 주택, 빌딩 같은 건축물에 사용되어 있는 석면 함유 건축자재는 폐기 또는 해체하기가 어려운 실정이며, 이러한 건축자재에 함유된 석면은 시간이 경과하면서 유출되어 비산하는 문제점이 있다. 따라서 석면 함유 건축자재를 폐기 또는 해체하지 않고도 석면의 비산을 방지할 수 있는 석면의 안정화 방법이 필요한 실정이다.However, since asbestos-containing building materials used in public structures such as subway, housing, and buildings such as subways are difficult to dispose of or dismantle from before regulation of asbestos use, asbestos contained in such building materials is leaked out over time, . Therefore, there is a need for a method of stabilizing asbestos that can prevent the scattering of asbestos without disposing or dismantling the asbestos-containing building material.

석면의 안정화 기술과 관련된 선행기술로는 예를 들면 등록특허 제10-1364693호는 석면 폐기재를 용융로에서 용융시켜 무해화하는 처리 방법을 개시하고 있으며, 등록특허 제10-1164500호에는 석면 함유 폐기물을 분쇄하지 않고 원형 그대로 유지한 상태에서 마이크로파를 조사하여 석면을 변성시켜 무해화하는 처리 방법을 개시하고 있다. 그러나 상기 선행기술은 고가의 기기나 장치를 별도로 구비해야 하며, 처리 공정이 복잡하고 고비용이 소요되는 문제점이 있다. As a prior art related to the stabilization technology of asbestos, for example, Japanese Patent Registration No. 10-1364693 discloses a treatment method of melting asbestos waste material in a melting furnace and making it harmless. In the patent No. 10-1164500, Discloses a treatment method in which microwave is irradiated while being kept in a circular shape without being pulverized to modify the asbestos to render it harmless. However, the prior art has a disadvantage in that an expensive apparatus or device must be separately provided, and a complicated process and high cost are required.

화학물질로 제조된 처리제 조성물에 의해 석면을 안정화시키는 기술도 알려져 있으며, 예를 들어 등록특허 제10-1031861호는 4급 암모늄염이 담지된 나노 실리카 수용액을 주성분으로 포함하는 석면 비산 방지제를 개시하고 있고, 등록특허 제10-0981944호는 건축자재 표면에 수지 코팅물을 배합하여 제조한 석면 안정화 용제를 도포하고, 상기 용제의 건조 후에 건축자재 표면에 난연제를 도포하고, 상기 난연제의 건조 후에 건축자재 표면에 천연성분의 항균 탈취제를 도포하는 단계를 포함하여 석면의 비산을 방지하는 처리 방법을 개시하고 있다. A technique for stabilizing asbestos by a treating composition made of a chemical substance is also known. For example, Japanese Patent No. 10-1031861 discloses an asbestos scattering inhibitor containing a quaternary ammonium salt-supported nano-silica aqueous solution as a main component , Registration No. 10-0981944 discloses a method of coating an asbestos stabilizing solvent by applying a resin asbestos stabilizing solvent prepared by blending a resin coating on the surface of a building material, applying a flame retardant to the surface of the building material after drying the solvent, Which comprises applying a natural component antimicrobial deodorant to the surface of the asbestos.

그러나 이러한 선행기술은 어느 것도 석면의 비산 방지 효과가 충분하지 못하며, 또한 안정화 효과가 일시적이고 지속적인 석면 안정화 효과는 떨어진다는 문제점이 있다.However, none of these prior arts have the problem that the effect of preventing asbestos from scattering is not sufficient, and that the stabilizing effect is temporary and the asbestos stabilization effect is deteriorated continuously.

또한, 국내에서 주로 사용된 건축자재 중 천정재는 석면이 15~18%, 시멘트가 82~85%로 되어 있어, 표면의 조직이 매우 치밀하고 단단하여, 그 속에 존재하고 있는 석면을 처리제로 처리하기가 매우 어렵다. 따라서 이 문제를 해결하기 위한 특수한 침투제가 필요한 실정이다. Among the building materials mainly used in Korea, the ceiling material is made of 15 ~ 18% of asbestos and 82 ~ 85% of cement, so that the structure of the surface is very dense and hard, Is very difficult. Therefore, a special penetrant is needed to solve this problem.

석면 처리제를 석면 함유 건축자재에 효과적으로 침투할 수 있게 하고, 또한 석면 처리제에 의해 석면을 지속적으로 안정화시키기 위해서는, 기존에 사용된 석면의 종류 및 성분을 정확하게 파악한 후에 이를 안정화시킬 수 있는 최적의 수단을 도출할 필요가 있다.In order to effectively penetrate asbestos-containing building materials into asbestos-containing building materials and to continuously stabilize asbestos by asbestos processing agents, it is necessary to accurately determine the type and composition of asbestos used, It is necessary to derive.

석면의 종류에는 여러 가지가 있으나, 우리나라에서 주로 사용된 석면은 사문석(Serpentine)에서 채취된 크리소타일(백석면, 3MgO·2SiO2·2H2O)과 각섬석(Amphibole)에서 채취한 크로시도라이트(청석면, Na2Fe(SiO3)2FeSiO3H2O), 아모사이트(갈석면, (FeMg)SiO3)이다. 그 외에도 안소필라이트((MgFe)7Si8O22(OH)2), 트레몰라이트(Ca2Mg5Si8O22(OH)2), 악티노라이트(CaO3(MgFe)O4SiO2)가 있으나 이들은 산출량이 적고 또한 섬유가 약해서 이용 가치가 적어 거의 사용되지 않고 있다. However, asbestos is mainly used in Korea because it is composed of chrysotile (Baekseok-myeon, 3MgO · 2SiO 2 · 2H 2 O) collected from serpentine and croplandite (amphibole) collected from amphibole a cheongseokmyeon, Na 2 Fe (SiO 3) 2 FeSiO 3 H 2 O), amorphous site (galseokmyeon, (FeMg) SiO 3). (MgFe) 7 Si 8 O 22 (OH) 2 ), tremolite (Ca 2 Mg 5 Si 8 O 22 (OH) 2 ), actinolite (CaO 3 (MgFe) O 4 SiO 2 ), But they are rarely used due to their low yield and their low value due to their weak fiber.

Karl Frank, "Asbestos", Becker und Haag(1952); Dr.Myrij, C. Shaw, "Handbook of Asbestos Textiles", Asbestos Texile Institute(1961)에 기재된 내용에 따르면, 크리소타일 석면(백석면)은 SiO2 37∼44%, MgO 39∼44%, FeO 0∼6%, Fe2O3 0.1∼5.0%, Al2O3 0.2∼1.5%, H2O 12.0∼15.0%를 성분으로 포함하고 있고, 크로시도라이트 석면(청석면)은 SiO2 49∼53%, MgO 0∼3%, FeO 13∼20%, Fe2O3 17∼20%, H2O 2.5∼4.5%, Na2O 4.0∼8.5%를 성분으로 포함하고 있고, 아모사이트 석면(갈석면)은 SiO2 49∼53%, MgO 1∼7%, FeO 34∼44%, Al2O3 2∼9%, H2O 2∼5%, CaO+Na2O 0.5∼2.5%를 성분으로 포함하고 있다. 백석면은 Mg를 다량 포함하는 반면, 청석면은 Fe를 다량 포함하고, 갈석면은 Al, Fe를 상대적으로 다량 포함하고 있다. Karl Frank, "Asbestos ", Becker und Haag (1952); According to Dr.Myrij, C. Shaw, "Handbook of Asbestos Textiles" and Asbestos Texile Institute (1961), chrysotile asbestos has 37 to 44% of SiO 2, 39 to 44% of MgO, ~6%, Fe 2 O 3 0.1~5.0 %, Al 2 O 3 0.2~1.5%, H 2 O and contains 12.0~15.0% of ingredient, chroman attempt Added asbestos (cheongseokmyeon) is SiO 2 49~53% By weight, MgO 0 to 3%, FeO 13 to 20%, Fe 2 O 3 17 to 20%, H 2 O 2.5 to 4.5% and Na 2 O 4.0 to 8.5% Contains 49 to 53% of SiO 2 , 1 to 7% of MgO, 34 to 44% of FeO, 2 to 9% of Al 2 O 3 , 2 to 5% of H 2 O and 0.5 to 2.5% of CaO + Na 2 O . The whitewashed surface contains a large amount of Mg, whereas the crystalline rock surface contains a large amount of Fe, and the brick surface contains a relatively large amount of Al and Fe.

석면의 종류에 따라 함유되어 있는 성분에 차이가 있으며, 이와 같은 석면의 종류 및 성분을 고려하여 석면을 효과적으로 안정화시키고 비산을 방지할 수 있는 처리제 조성물을 개발할 필요가 있다. It is necessary to develop a treating composition capable of effectively stabilizing asbestos and preventing it from scattering in consideration of kinds and components of such asbestos.

따라서 본 발명의 과제는 석면함유 건축자재에 내재된 석면을 효과적으로 안정화시킬 수 있고, 안정화 효과가 지속적일 수 있는 석면 안정화용 처리제 조성물 및 이를 이용한 석면의 안정화 처리 방법을 제공하는 것이다. Accordingly, an object of the present invention is to provide a treatment composition for asbestos stabilization which can effectively stabilize asbestos contained in asbestos-containing building materials and can stabilize the stabilization effect, and a method for treating asbestos using the same.

본 발명자들은 실란 화합물을 알칼리금속 실리케이트와 함께 첨가함으로써 알칼리금속 실리케이트를 석면 함유 건축자재 내부로 효과적으로 침투시키고, 또한 다원자 공여체를 첨가함으로써 알칼리금속 실리케이트와 다원자 공여체의 다원자가 금속이온을 교차 결합시켜 석면 함유 건축자재를 화학적으로 안정화시키고, 또한 충진제를 첨가함으로써 석면에 부족한 이온성분을 보충하여 이들 이온 성분을 알칼리금속 실리케이트와 교차 결합시켜 석면 함유 건축자재를 화학적으로 더욱 안정화시킬 수 있다는 것을 도출하였다.The present inventors have found that by adding a silane compound together with an alkali metal silicate, the alkali metal silicate can be effectively penetrated into the asbestos containing building material, and also by cross-linking the alkali metal silicate and the polyvalent metal ion of the polyatomic donor by adding a polyatomic donor It has been found that asbestos-containing building materials can be chemically stabilized and also fillers can be added to supplement the insufficient ionic components in the asbestos and cross-link these ionic components with alkali metal silicates to chemically stabilize the asbestos-containing building materials.

본 발명의 과제를 해결하기 위한 수단으로서, 본 발명의 석면 안정화용 처리제 조성물은 리튬 실리케이트, 소듐 실리케이트, 및 포타슘 실리케이트로 이루어진 군에서 선택되는 알칼리금속 실리케이트; 디메틸 디메톡시 실란, 에틸 트리메톡시 실란, 메틸 트리메톡시 실란, 및 감마-글리시딜 옥시프로필 트리메톡시실란으로 이루어진 군에서 선택되는 실란 화합물; 납 티타네이트, 및 납 지르코네이트로 이루어진 군에서 선택되는 다원자 공여체; 및 물을 포함하여 이루어지는 것을 특징으로 한다.As means for solving the problem of the present invention, the treating composition for asbestos stabilization of the present invention is an alkali metal silicate selected from the group consisting of lithium silicate, sodium silicate, and potassium silicate; Silane compounds selected from the group consisting of dimethyldimethoxysilane, ethyltrimethoxysilane, methyltrimethoxysilane, and gamma-glycidyloxypropyltrimethoxysilane; Lead titanate, and lead zirconate; And water.

또한 본 발명의 석면 안정화용 처리제 조성물은 물 100중량부를 기준으로, 알칼리금속 실리케이트를 50 내지 80 중량부 함유하고, 실란 화합물을 8 내지 16 중량부 함유하고, 다원자 공여체를 2 내지 8 중량부 함유하는 것을 특징으로 한다.In addition, the treatment composition for asbestos stabilization according to the present invention contains 50 to 80 parts by weight of an alkali metal silicate, 8 to 16 parts by weight of a silane compound, 2 to 8 parts by weight of a polyatomic donor, .

또한 본 발명의 석면 안정화용 처리제 조성물은 규회석, 활석, 및 카올린으로 이루어진 군에서 선택되는 충진제를 더욱 포함하는 것을 특징으로 한다.Also, the treating composition for asbestos stabilization of the present invention is characterized by further comprising a filler selected from the group consisting of wollastonite, talc, and kaolin.

또한 본 발명의 석면 안정화용 처리제 조성물은 물 100중량부를 기준으로 충진제를 30 내지 60 중량부 함유하는 것을 특징으로 한다.The treatment composition for asbestos stabilization according to the present invention is characterized by containing 30 to 60 parts by weight of a filler based on 100 parts by weight of water.

또한 본 발명의 석면 안정화 처리 방법은 석면 함유 건축자재에 본 발명의 석면 안정화용 처리제 조성물을 도포 및 건조하는 제 1 단계; 석면 함유 건축자재에 실리카졸을 추가한 석면 안정화용 처리제 조성물을 도포 및 건조하는 제 2 단계; 및 석면 함유 건축자재에 무기안료와 천연의 방향성 항균탈취제를 도포 및 건조하는 제 3 단계를 포함하여 이루어지는 것을 특징으로 한다.The asbestos stabilization treatment method of the present invention includes a first step of applying and drying the treatment composition for asbestos stabilization of the present invention to an asbestos-containing building material; A second step of applying and drying an asbestos stabilizing treatment composition comprising silica sol added to an asbestos-containing building material; And a third step of applying and drying an inorganic pigment and a natural aromatic antibacterial / deodorant to asbestos-containing building materials.

본 발명의 석면 안정화용 처리제 조성물에 따르면, 실란 화합물을 알칼리금속 실리케이트와 함께 첨가함으로써 알칼리금속 실리케이트를 석면 함유 건축자재 내부로 효과적으로 침투시키고, 알칼리금속 실리케이트의 알칼리금속 이온이 석면 중의 Ca, Mg, Al 등 금속이온과 치환 반응을 일으킴으로써 석면을 화학적으로 안정화시키고 석면의 비산이나 유출을 방지할 수 있다. 또한 본 발명의 석면 안정화용 처리제 조성물에 따르면, 다원자 공여체를 첨가함으로써 알칼리금속 실리케이트와 다원자 공여체의 다원자가 금속이온을 교차 결합시켜 석면 함유 건축자재의 조직을 화학적으로 안정화시킬 수 있다.According to the treatment composition for asbestos stabilization of the present invention, the alkali metal silicate is effectively penetrated into the asbestos-containing building material by adding the silane compound together with the alkali metal silicate, and the alkali metal ions of the alkali metal silicate are contained in the asbestos Ca, Mg, Al It is possible to chemically stabilize asbestos and prevent asbestos from scattering or leaking by causing a substitution reaction with metal ions such as. In addition, according to the treatment composition for asbestos stabilization of the present invention, the structure of the asbestos-containing building material can be chemically stabilized by cross-linking the alkali metal silicate and the polyvalent metal ion of the polyatomic donor by adding the polyatomic donor.

또한 본 발명의 석면 안정화용 처리제 조성물은 충진제를 더욱 첨가함으로써 석면에 부족한 이온성분을 보충하여 이들 이온 성분을 알칼리금속 실리케이트와 교차 결합시켜 석면 함유 건축자재를 화학적으로 더욱 안정화시킬 수 있다.In addition, the treating composition for asbestos stabilization of the present invention can further stabilize the asbestos-containing building material by supplementing the insufficient ion component to the asbestos by cross-linking the ion component with the alkali metal silicate by further adding the filler.

본 발명의 석면 안정화용 처리제 조성물 및 이를 이용한 석면 안정화 처리 방법에 따르면, 건축자재에 내재된 석면을 효과적으로 안정화시킬 수 있을 뿐만 아니라, 화학적 안정화 메커니즘에 의해 석면의 안정화 효과가 지속적이다.According to the treating composition for asbestos stabilization of the present invention and the method for stabilizing asbestos using the same, not only the asbestos inherent in the building material can be effectively stabilized, but also the stabilizing effect of the asbestos is maintained by the chemical stabilization mechanism.

또한 건축자재의 조직도 더욱 견고해지게 할 수 있으며, 외부 충격에도 석면이 유출 또는 비산되지 않고, 건축자재의 수명을 연장시킬 수 있다.In addition, the structure of building materials can be made more robust, and asbestos does not leak or scatter even in an external impact, and the life of building materials can be extended.

도 1은 본 발명에 따른 석면 안정화용 처리제 조성물로 처리한 석면 함유 건축자재 시료의 전자현미경 사진이다.
도 2는 석면 안정화 처리를 거치지 않은 석면 함유 건축자재 시료의 전자현미경 사진이다.1 is an electron micrograph of an asbestos-containing building material sample treated with the treating composition for asbestos stabilization according to the present invention.
2 is an electron micrograph of a sample of building material containing asbestos that has not undergone asbestos stabilization treatment.

본 발명의 석면 안정화용 처리제 조성물은 리튬 실리케이트, 소듐 실리케이트, 및 포타슘 실리케이트로 이루어진 군에서 선택되는 알칼리금속 실리케이트; 디메틸 디메톡시 실란, 에틸 트리메톡시 실란, 메틸 트리메톡시 실란, 및 감마-글리시딜 옥시프로필 트리메톡시실란으로 이루어진 군에서 선택되는 실란 화합물; 납 티타네이트, 및 납 지르코네이트로 이루어진 군에서 선택되는 다원자 공여체; 및 물을 포함하여 이루어진다. The treating composition for asbestos stabilization of the present invention is an alkali metal silicate selected from the group consisting of lithium silicate, sodium silicate, and potassium silicate; Silane compounds selected from the group consisting of dimethyldimethoxysilane, ethyltrimethoxysilane, methyltrimethoxysilane, and gamma-glycidyloxypropyltrimethoxysilane; Lead titanate, and lead zirconate; And water.

본 발명의 석면 안정화용 처리제 조성물은 리튬 실리케이트, 소듐 실리케이트, 및 포타슘 실리케이트로 이루어진 군에서 선택되는 알칼리금속 실리케이트(M2O·SiO2; 여기서 M은 Li, Na, 또는 K)를 포함하는 것에 의해, 알칼리금속 실리케이트의 알칼리금속 이온이 석면 중의 Ca, Mg, Al 등 금속이온과 치환 반응을 일으킴으로써 석면을 화학적으로 안정화시키고 석면의 비산이나 유출을 방지할 수 있다.The treatment composition for asbestos stabilization of the present invention comprises an alkali metal silicate (M 2 O.SiO 2, wherein M is Li, Na, or K) selected from the group consisting of lithium silicate, sodium silicate, and potassium silicate , Alkali metal ions of alkali metal silicate cause substitution reaction with metal ions such as Ca, Mg and Al in the asbestos, thereby chemically stabilizing the asbestos and preventing scattering or leakage of asbestos.

알칼리금속 실리케이트는 수용액 중에서 하기와 같이 석면 중의 M2O와 반응함으로써 M2 규산염을 형성하고 알칼리성을 나타내게 된다.The alkali metal silicate reacts with M 2 O in the asbestos as follows in an aqueous solution to produce M 2 Silicate and alkaline.

M1 2SiO3 + M2O + H2O → M2SiO3 + M1OH M 1 2 SiO 3 + M 2 O + H 2 O → M 2 SiO 3 + M 1 OH

상기 반응은 금속 M1(Li, Na, K)의 이온화 경향이 M2(Ca, Mg, Al)보다 크기 때문에 이온 치환반응이 오른쪽으로 진행하는 것을 이용하고 있다 . Since the ionization tendency of the metal M 1 (Li, Na, K) is larger than M 2 (Ca, Mg, Al), the above reaction utilizes that the ion substitution reaction proceeds to the right.

M1(미해리) + M2(이온) → M1(이온) + M2(미해리) M 1 (non-dissociated) + M 2 (ion) → M 1 (ion) + M 2 (non-dissociated)

석면 안정화용 처리제 조성물 중에 알칼리금속 실리케이트는 물 100중량부를 기준으로 50 내지 80 중량부 함유되는 것이 바람직하다.The alkali metal silicate in the asbestos stabilization treating composition is preferably contained in an amount of 50 to 80 parts by weight based on 100 parts by weight of water.

알카리금속 실리케이트로서는 포타슘 실리케이트(K2O·SiO2)를 사용하는 것이 바람직하며, K2O와 SiO2의 혼합 중량비가 1:1.8 내지 1:3.5인 것이 바람직하고, 가장 바람직하게는 K2O 23.7중량%와 SiO2 76.3중량%로 이루어진 포타슘 실리케이트를 사용한다.As the alkali metal silicate, it is preferable to use potassium silicate (K 2 O.SiO 2 ), and the mixing weight ratio of K 2 O and SiO 2 is preferably 1: 1.8 to 1: 3.5, and most preferably K 2 O A potassium silicate consisting of 23.7 wt% and 76.3 wt% of SiO 2 is used.

또한 본 발명의 석면 안정화용 처리제 조성물은 알칼리금속 실리케이트를 석면 함유 건축자재에 효과적으로 침투시키기 위하여 실란 화합물을 첨가하는 것을 특징으로 한다. Further, the treating composition for asbestos stabilization of the present invention is characterized by adding a silane compound to effectively penetrate the alkali metal silicate into the building material containing asbestos.

본 발명의 석면 안정화용 처리제 조성물은 디메틸 디메톡시 실란(dimethyl dimethoxy silane), 에틸 트리메톡시 실란(ethyl trimethoxy silane) 메틸 트리메톡시 실란(methyl trimethoxy silane) 감마-그리시딜 옥시프로필 트리메톡시 실란(gama-glycidyl oxypropyl trimethoxy silane)으로 이루어진 군에서 선택되는 실란 화합물을 포함하는 것에 의해, 알칼리금속 실리케이트의 건축자재 내부로의 침투를 용이하게 할 뿐만 아니라 석면의 안정화 효과를 더욱 향상시킬 수 있다.The treatment composition for asbestos stabilization according to the present invention may contain at least one selected from the group consisting of dimethyl dimethoxy silane, ethyl trimethoxy silane, methyl trimethoxy silane gamma-glycidyloxypropyl trimethoxysilane gama-glycidyl oxypropyl trimethoxy silane), the alkali metal silicate can easily penetrate into the building material, and the stabilization effect of the asbestos can be further improved.

이들 실란 화합물은 단독으로 사용하는 것보다는 2종 이상을 혼용함으로써 알칼리금속 실리케이트의 침투 촉진, 석면의 안정화 촉진, 건축자재의 강도 강화 등 필요한 목적을 달성할 수 있다.These silane compounds may be used in combination of two or more species to achieve the purpose of promoting penetration of alkali metal silicate, promoting stabilization of asbestos, and strengthening strength of building materials.

석면 안정화용 처리제 조성물 중에 실란 화합물은 물 100중량부를 기준으로 8 내지 16 중량부 함유되는 것이 바람직하다.It is preferable that the silane compound in the treating composition for asbestos stabilization is contained in an amount of 8 to 16 parts by weight based on 100 parts by weight of water.

또한 본 발명의 석면 안정화용 처리제 조성물은 납 티타네이트, 및 납 지르코네이트로 이루어진 군에서 선택되는 다원자 공여체를 포함하는 것에 의해, 알칼리금속 실리케이트의 실리케이트와 다원자 공여체의 다원자가 가교 결합을 형성함으로써 건축자재의 강도가 높아지고 견고해져서 외부 충격에도 석면의 비산이나 탈리가 없어지므로 석면의 안정화 효과를 더욱 향상시킬 수 있다. 다원자 공여체를 포함하는 것에 의해,내수성과 내화학성도 향상시킬 수 있다. Further, the treatment composition for asbestos stabilization of the present invention comprises a polyatomic donor selected from the group consisting of lead titanate, and lead zirconate, thereby forming a polyvalent cross-linking of the silicate of the alkali metal silicate and the polyatomic donor As a result, the strength of the building material is increased and becomes strong, and the asbestos scattering and desorption are eliminated even in the external impact, so that the stabilization effect of the asbestos can be further improved. By including a polyatomic donor, water resistance and chemical resistance can be improved.

석면 안정화용 처리제 조성물 중에 다원자 공여체는 물 100중량부를 기준으로 2 내지 8 중량부 함유되는 것이 바람직하다.It is preferable that the polyatomic donor in the treating composition for asbestos stabilization is contained in an amount of 2 to 8 parts by weight based on 100 parts by weight of water.

또한 본 발명의 석면 안정화용 처리제 조성물은 규회석, 활석, 및 카올린으로 이루어진 군에서 선택되는 충진제를 더 포함할 수 있다. 규회석, 활석, 및 카올린으로 이루어진 군에서 선택되는 충진제를 포함하는 것에 의해, 석면 중에 부족한 다원자 공여체를 보충하고 충진제의 금속 이온이 더욱 다원자 공여체로 작용하여 알칼리금속 실리케이트의 실리케이트와 가교 결합을 형성함으로써 석면의 안정화 효과를 더욱 향상시킬 수 있다.In addition, the treating composition for asbestos stabilization of the present invention may further comprise a filler selected from the group consisting of wollastonite, talc, and kaolin. By incorporating a filler selected from the group consisting of wollastonite, talc, and kaolin, the metal ion of the filler acts as a more polyatomic donor to form a bridge with the silicate of the alkali metal silicate Whereby the stabilizing effect of the asbestos can be further improved.

충진제 성분인 규회석(CaSiO3), 활석(Mg3Si4O10(OH)2), 카올린(Al2Si2O5(OH)4)은 석면 중에 부족한 다원자 공여체를 보충해주는 작용을 한다. 즉, 규회석은 Ca, 활석은 Mg, 카올린은 Al을 보충할 수 있다. 상술하였듯이 청석면, 갈석면에는 MgO, Al2O3, CaO의 함량이 적고, 백석면에는 Al2O3, CaO의 함량이 적은데, 이들 금속 산화물을 추가로 첨가함으로써 다원자 공여체로 작용하게 하여 가교 결합의 형성에 의한 석면의 안정화 효과를 더욱 향상시킬 수 있다. 따라서 본 발명에서는 충진제를 첨가함으로써 석면에 부족한 공여체를 보충하여 석면의 안정화 효과를 크게 향상시킬 수 있다. CaSiO 3 , talc (Mg 3 Si 4 O 10 (OH) 2 ), and kaolin (Al 2 Si 2 O 5 (OH) 4 ) are the fillers that supplement the unsaturated polyatomic donor in the asbestos. That is, wollastonite may supplement Ca, talc may be Mg, and kaolin may be supplemented with Al. As described above, the content of MgO, Al 2 O 3 , and CaO is small in the surface of the pearlite surface and the surface of the brass, and the content of Al 2 O 3 and CaO is small in the whitewasic surface. By additionally adding these metal oxides, It is possible to further improve the stabilizing effect of the asbestos by the formation of the asbestos. Therefore, in the present invention, by adding a filler, it is possible to greatly improve the stabilization effect of asbestos by replenishing donors that are insufficient in asbestos.

석면 안정화용 처리제 조성물 중에 충진제는 물 100중량부를 기준으로 30 내지 60 중량부 함유되는 것이 바람직하다.It is preferable that the filler in the treatment composition for asbestos stabilization is contained in an amount of 30 to 60 parts by weight based on 100 parts by weight of water.

또한 본 발명의 석면 안정화용 처리제 조성물은 수성계 도료에서 일반적으로 사용되고 있는 침강 방지제, 소포제, 안정제, 난연제 등의 각종 첨가제를 더 포함할 수 있다. 석면 안정화용 처리제 조성물 중에 첨가제는 물 100중량부를 기준으로 2 내지 8 중량부 함유되는 것이 바람직하다.In addition, the treating composition for asbestos stabilization of the present invention may further contain various additives such as anti-settling agents, defoaming agents, stabilizers, and flame retardants generally used in aqueous coating materials. It is preferable that the additive in the treatment composition for asbestos stabilization is contained in an amount of 2 to 8 parts by weight based on 100 parts by weight of water.

본 발명의 석면 안정화 처리 방법은, 리튬 실리케이트, 소듐 실리케이트, 및 포타슘 실리케이트로 이루어진 군에서 선택되는 알칼리금속 실리케이트; 디메틸 디메톡시 실란, 에틸 트리메톡시 실란, 메틸 트리메톡시 실란, 및 감마-글리시딜 옥시프로필 트리메톡시실란으로 이루어진 군에서 선택되는 실란 화합물; 납 티타네이트, 및 납 지르코네이트로 이루어진 군에서 선택되는 다원자 공여체; 및 규회석, 활석, 및 카올린으로 이루어진 군에서 선택되는 충진제를 포함하는 석면 안정화용 처리제 조성물을 석면 함유 건축자재에 도포 및 건조하는 제 1 단계; 상기 석면 함유 건축자재에 실리카졸을 추가한 상기 석면 안정화용 처리제 조성물을 도포 및 건조하는 제 2 단계; 및 상기 석면 함유 건축자재에 무기안료와 천연의 방향성 항균탈취제를 도포 및 건조하는 제 3 단계를 포함하여 이루어진다.The asbestos stabilization treatment method of the present invention comprises an alkali metal silicate selected from the group consisting of lithium silicate, sodium silicate, and potassium silicate; Silane compounds selected from the group consisting of dimethyldimethoxysilane, ethyltrimethoxysilane, methyltrimethoxysilane, and gamma-glycidyloxypropyltrimethoxysilane; Lead titanate, and lead zirconate; And a filler selected from the group consisting of wollastonite, talc, and kaolin, to an asbestos-containing building material and drying the asbestos-containing building material; A second step of coating and drying the asbestos stabilizing treatment composition to which silica sol is added to the asbestos-containing building material; And a third step of applying and drying an inorganic pigment and a natural aromatic antiseptic and deodorant to the asbestos-containing building material.

상기 제 1 단계에서는 상술한 석면 안정화용 처리제 조성물을 석면 함유 건축자재에 도포함으로써, 건축자재 내부까지 처리제 조성물 성분을 깊숙히 침투시키고, 석면 내의 MgO, Al2O3, CaO, FeO, Fe2O3 등의 금속이온과 알칼리금속 실리케이트의 금속이온이 치환 반응을 일으키고, 다원자 공여체가 알칼리금속 실리케이트와 가교 결합을 형성하고, 또한 충진제의 금속 이온이 알칼리금속 실리케이트와 가교 결합을 형성함으로써, 석면을 화학적으로 안정화시키고 석면의 비산이나 유출을 방지할 수 있다.In the first step, the above-described asbestos stabilizing treating composition is applied to the asbestos-containing building material to deeply penetrate the treating agent composition component into the building material, and MgO, Al 2 O 3 , CaO, FeO, Fe 2 O 3 And the metal ion of the alkali metal silicate causes the substitution reaction, the polyatomic donor forms the crosslinking with the alkali metal silicate, and the metal ion of the filler forms the crosslinking with the alkali metal silicate, And asbestos can be prevented from scattering or leaking.

상기 제 2 단계에서는 상술한 석면 안정화용 처리제 조성물에 실리카졸을 추가한 처리제 조성물을 제 1 단계의 처리를 거친 석면 함유 건축자재에 도포함으로써, 상기 제 1 단계에서 안정화되지 않은 잔여 금속 산화물을 추가로 안정화시키면서 건축자재 내부를 견고하게 하여 석면이 유출, 비산되지 않도록 한층 더 고착 강화시킨다. 실리카졸(SiO2)를 추가함으로써 이것이 결합재로 작용하여 건축자재 내부를 더 단단히 고착시킬 수 있다. 석면 안정화용 처리제 조성물 100중량부를 기준으로 실리카졸은 25 내지 50 중량부 첨가하는 것이 바람직하다. In the second step, the treatment composition obtained by adding the silica sol to the above-mentioned asbestos stabilizing treatment composition is applied to the asbestos-containing building material subjected to the first treatment to further remove the unstabilized residual metal oxide Stabilize the inside of building materials while stabilizing, so that the asbestos does not leak or scatter further strengthened. By adding silica sol (SiO 2 ) this can act as a binder and allow the interior of the building material to be more firmly fixed. It is preferable to add 25 to 50 parts by weight of silica sol based on 100 parts by weight of the treating composition for asbestos stabilization.

상기 제 3 단계에서는 무기안료와 천연의 방향성 항균탈취제를 제 1 단계의 처리를 거친 석면 함유 건축자재에 도포함으로써, 습기가 잘 유통되게 하고 곰팡이나 세균의 번식을 막고, 나아가 미장 효과도 나타낼 수 있다.In the third step, the inorganic pigments and the natural aromatic antiseptic and deodorant are applied to the asbestos-containing building material which has undergone the first-stage treatment, thereby making it possible to distribute the moisture well, prevent the growth of fungi and bacteria, .

무기안료로서는 통상적으로 일반 페인트에서 사용하는 무기계 안료, 예를 들어 산화티타늄, 산화철 계열(흑색 황색 적갈색), 산화크롬, 군청 그 외 다수의 안료를 사용할 수 있다.As the inorganic pigment, an inorganic pigment commonly used in general paints such as titanium oxide, iron oxide series (black yellow reddish brown), chromium oxide, ultramarine blue, and many other pigments may be used.

본 발명의 석면 안정화 처리 방법에 따른 제 1 단계 ∼ 제 3 단계에 있어서 도포는 분무기, 롤러 도포기 등 공지의 도포 수단을 적의 이용하여 도포할 수 있으며, 도포 방법 및 수단에 특별한 제한은 없다.In the first to third steps of the asbestos stabilization treatment method of the present invention, the application may be carried out by using any known application means such as an atomizer or a roller applicator, and there is no particular limitation on the application method and means.

상기 제 1 단계의 도포량은 300∼400g/m2로 도포하는 것이 바람직하며, 상기 제 2 단계의 도포량은 300∼400g/m2로 도포하는 것이 바람직하며, 상기 제 3 단계의 도포량은 0.25∼0.4g/m2로 도포하는 것이 바람직하다.The coating amount of the first stage, it is preferable to apply a 300~400g / m 2, the application amount of the second step, and is preferably coated with 300~400g / m 2, the application amount of the third step is from 0.25 to 0.4 g / m < 2 >.

이하, 실시예를 통하여 본 발명에 따른 석면 안정화용 처리제 조성물 및 석면 안정화 처리 방법에 대해 보다 구체적으로 설명한다. 단, 실시예는 본 발명의 실시양태를 예시한 것이며, 본 발명의 기술 범위가 실시예에만 한정되는 것은 아니다.Hereinafter, the treatment composition for asbestos stabilization and the asbestos stabilization treatment method according to the present invention will be described in more detail with reference to examples. However, the embodiments are illustrative of the embodiments of the present invention, and the technical scope of the present invention is not limited to the embodiments.

실시예Example

물 100중량부에 알칼리금속 실리케이트로서 포타슘 실리케이트 60중량부, 실란 화합물로서 디메틸 디메톡시 실란 12중량부, 다원자 공여체로서 납 티타네이트 6중량부, 충진제로서 규회석, 활석, 및 카올린을 합계로 50중량부, 첨가제로서 폴리알카놀 아르닌 4중량부를 배합하고 교반하여 석면 안정화용 처리제 조성물을 얻었다.60 parts by weight of potassium silicate as an alkali metal silicate, 12 parts by weight of dimethyldimethoxysilane as a silane compound, 6 parts by weight of lead titanate as a polyatomic donor, wollastonite, talc and kaolin as fillers were added in a total amount of 50 parts by weight And 4 parts by weight of polyalkanol Arnine as an additive were mixed and stirred to obtain a treating composition for asbestos stabilization.

상기와 같이 얻어진 석면 안정화용 처리제 조성물을 미리 준비한 건축자재 시료에 300∼400g/m2로 1차 도포하고 건조시킨 다음, 상기 석면 안정화용 조성물에 실리카졸을 30중량부 배합한 조성물을 건축자재 시료에 300∼400g/m2로 2차 도포하고 건조시킨 다음, 산화티타늄 및 방향성 항균탈취제를 0.3g/m2로 3차 도포하고 건조시켰다.The thus obtained composition for asbestos stabilization treatment was first applied to a sample of building material prepared in advance at 300 to 400 g / m < 2 >, dried, and then 30 parts by weight of silica sol was added to the composition for asbestos stabilization. the second was coated to a 300~400g / m 2 and dried, and then, coating the titanium oxide and the third directional antimicrobial deodorant to 0.3g / m 2 and dried.

상기 단계를 거쳐 안정화 처리된 건축자재 시료를 실내공기질공정시험기준 (환경부 고시 제2010-24호)에 따라 석면 검출량에 대해 시험하였다. 시험에서는 길이 대 직경비 3:1 이상, 직경 0.25㎛ 이상, 길이 5.0㎛ 초과인 섬유만 계수하였다.The stabilized building material samples through the above steps were tested for the amount of asbestos detected according to the indoor air quality process test standard (Ministry of Environment Notice No. 2010-24). In the test, only fibers having a length to diameter ratio of 3: 1 or more, a diameter of 0.25 占 퐉 or more, and a length of 5.0 占 퐉 or more were counted.

본 발명의 석면 안정화용 처리제 조성물을 도포하지 않은 건축자재 시료를 대조군으로 하였고, 상기 3차 도포까지 끝낸 건축자재 시료 3개, 본 발명의 석면 안정화용 처리제 조성물로 1차 도포만 실시한 시료 1개에 대해 각각 시험하였다.A sample of the building material to which the asbestos stabilizing treatment composition of the present invention was not applied was used as a control group. Three samples of the building material finished to the third application were applied, and one sample of the present invention subjected to the first application with the asbestos stabilizing treatment composition Respectively.

편광현미경을 이용하여 분석하고, 성분분석기로 구성성분을 분석하였다. Analyzed with a polarizing microscope, and components were analyzed with a component analyzer.

시료 구분Sample classification 결과치 (단위: structures/cc)Results (unit: structures / cc) 무도포 시료Non-foaming sample 0.005 (백석면)0.005 (white stone surface) 3차 도포 시료 1Tertiary application sample 1 <0.002<0.002 3차 도포 시료 2Tertiary application sample 2 <0.002<0.002 3차 도포 시료 3Third Coating Sample 3 <0.002<0.002 1차 도포 시료 1Primary coating sample 1 <0.002<0.002

시험 결과, 본 발명의 석면 안정화 처리 방법에 의해 3차 도포 처리된 석면 함유 건축자재는 석면이 실질적으로 검출되지 않았다. 또한 본 발명에 따른 석면 안정화용 처리제 조성물로 1차 도포된 석면 함유 건축자재에서도 실질적으로 석면이 검출되지 않았으며, 이는 본 발명에 따른 석면 안정화용 처리제 조성물이 1회 도포에서도 현저한 효과를 나타내는 것을 입증한다. 반면에 석면 안정화용 처리제 조성물이 도포되지 않은 시료에서는 백석면의 검출이 확인되었다.As a result of the test, the asbestos-containing building material subjected to the third coating treatment by the asbestos stabilization treatment method of the present invention was not substantially detected. Also, the asbestos-containing building material primarily coated with the treating composition for asbestos stabilization according to the present invention did not substantially detect asbestos. This demonstrates that the treating composition for asbestos stabilization according to the present invention shows remarkable effects even in one application do. On the other hand, the detection of the white stone surface was confirmed in the sample to which the treating composition for asbestos stabilization was not applied.

또한 본 발명에 따른 석면 안정화용 처리제 조성물이 도포된 시료의 전자현미경 (3000배) 사진을 도 1에 나타내고, 석면 안정화용 처리제 조성물이 도포되지 않은 시료의 전자현미경 (3000배) 사진을 도 2에 나타낸다. 도 1 및 도 2를 대비하면, 본 발명에 따른 석면 안정화용 처리제 조성물로 처리함으로써, 석면 함유 건축자재의 내부가 화학적으로 안정화되고 견고하게 되는 것이 확인된다.1 shows an electron microscope (3000 times) photograph of a sample coated with the treating composition for asbestos stabilization according to the present invention, and FIG. 2 shows an electron microscope (3000 times) photograph of a sample to which the treating composition for asbestos stabilization was applied . 1 and 2, it is confirmed that the interior of the asbestos-containing building material is chemically stabilized and solidified by treating with the treating composition for asbestos stabilization according to the present invention.

석면은 미량의 비산 또는 유출로도 인체 및 환경에 치명적인 해를 끼칠 수 있으므로, 본 발명의 석면 안정화용 처리제 조성물은 석면의 안정화에 우수한 효과가 있음을 알 수 있다.Since the asbestos can cause a serious harm to the human body and the environment even in a trace amount of scattering or leakage, the treating composition for asbestos stabilization of the present invention has an excellent effect on the stabilization of asbestos.

Claims (5)

리튬 실리케이트, 소듐 실리케이트, 및 포타슘 실리케이트로 이루어진 군에서 선택되는 알칼리금속 실리케이트; 디메틸 디메톡시 실란, 에틸 트리메톡시 실란, 메틸 트리메톡시 실란, 및 감마-글리시딜 옥시프로필 트리메톡시실란으로 이루어진 군에서 선택되는 실란 화합물; 납 티타네이트, 및 납 지르코네이트로 이루어진 군에서 선택되는 다원자 공여체; 및 물을 포함하는 것을 특징으로 하는 석면 안정화용 처리제 조성물.Alkali metal silicates selected from the group consisting of lithium silicate, sodium silicate, and potassium silicate; Silane compounds selected from the group consisting of dimethyldimethoxysilane, ethyltrimethoxysilane, methyltrimethoxysilane, and gamma-glycidyloxypropyltrimethoxysilane; Lead titanate, and lead zirconate; And water. &Lt; / RTI &gt; 제 1 항에 있어서,
물 100중량부를 기준으로, 알칼리금속 실리케이트를 50 내지 80 중량부 함유하고, 실란 화합물을 8 내지 16 중량부 함유하고, 다원자 공여체를 2 내지 8 중량부 함유하는 것을 특징으로 하는 석면 안정화용 처리제 조성물.The method according to claim 1,
A treatment composition for asbestos stabilization, which comprises 50 to 80 parts by weight of an alkali metal silicate, 8 to 16 parts by weight of a silane compound, and 2 to 8 parts by weight of a polyatomic donor, based on 100 parts by weight of water . 제 1 항에 있어서,
규회석, 활석, 및 카올린으로 이루어진 군에서 선택되는 충진제를 더욱 포함하는 것을 특징으로 하는 석면 안정화용 처리제 조성물.The method according to claim 1,
Wherein the filler further comprises a filler selected from the group consisting of wollastonite, talc, and kaolin. 제 3 항에 있어서,
물 100중량부를 기준으로 충진제를 30 내지 60 중량부 함유하는 것을 특징으로 하는 석면 안정화용 처리제 조성물.The method of claim 3,
Wherein the filler is contained in an amount of 30 to 60 parts by weight based on 100 parts by weight of water. 석면 함유 건축자재에 제 1 항에 기재된 석면 안정화용 처리제 조성물을 도포 및 건조하는 제 1 단계; 석면 함유 건축자재에 실리카졸을 추가한 상기 석면 안정화용 처리제 조성물을 도포 및 건조하는 제 2 단계; 및 석면 함유 건축자재에 무기안료와 천연의 방향성 항균탈취제를 도포 및 건조하는 제 3 단계를 포함하는 것을 특징으로 하는 석면 안정화 처리 방법.A first step of applying and drying the treatment composition for asbestos stabilization according to claim 1 to a building material containing asbestos; A second step of coating and drying the asbestos stabilizing treatment composition to which silica sol is added to the asbestos-containing building material; And a third step of applying and drying an inorganic pigment and a natural aromatic aromatic deodorant to the asbestos-containing building material.
KR1020140168608A 2014-11-28 2014-11-28 Composition for stabilizing asbestos and treatment method for suppressing asbestos using the same KR101666909B1 (en)