KR20130024864A - Composition for flame resistant - Google Patents
Composition for flame resistant Download PDFInfo
- Publication number
- KR20130024864A KR20130024864A KR1020120096233A KR20120096233A KR20130024864A KR 20130024864 A KR20130024864 A KR 20130024864A KR 1020120096233 A KR1020120096233 A KR 1020120096233A KR 20120096233 A KR20120096233 A KR 20120096233A KR 20130024864 A KR20130024864 A KR 20130024864A
- Authority
- KR
- South Korea
- Prior art keywords
- flame retardant
- potassium
- acid
- weight
- ammonium
- Prior art date
Abstract
Description
본 발명은 가연성 구조로 된 목재 및 볏짚 등에 사용되는 방염 조성물에 관한 것이다. 구체적으로, 목재, 볏짚, 한지, 의류 등에 도포 또는 분사하여 화염의 전파를 억제할 수 있으며, 탄화면적, 잔염시간, 잔신시간이 우수하고, 문화재와 한국전통의 13 종 (뇌록, 양록, 장단, 군청, 삼청, 석황, 석간주, 주홍, 지당, 하엽, 다자, 육색, 먹) 단청색에 대해 백화, 박락, 얼룩 등의 유해성이 없으며, 다공성 구조의 표면 및 내·외부에 난연성을 증진시키는 동시에 구조물의 열화현상을 방지할 수 있는 실온 경화용 유무기질 결합제 방염 조성물에 관한 것이다. The present invention relates to a flame retardant composition used for wood and rice straw having a flammable structure. Specifically, it can be applied or sprayed on wood, rice straw, Korean paper, clothing, etc. to suppress the propagation of flames, and has excellent burnout, afterflame time, after-rest time, and 13 kinds of cultural assets and Korean traditions It is free from harmful effects such as whitening, peeling, and staining against the dark blue color of the Navy Blue, Samcheong, Seokwang, Seokju, Scarlet, Lactose, Lower Leaf, Multilateral, Meat Color, and Black), while improving the flame resistance on the surface of the porous structure and the inside and the outside. It relates to an organic-inorganic binder flame retardant composition for room temperature curing that can prevent deterioration.
일상생활에서 사용되는 가연성재질의 제품 및 목재류와 섬유 및 플라스틱류를 방염처리 한다는 것은 기술적으로나 경제성으로 보아 어려운 측면이 있다. 하지만 실제로 꼭 그럴 필요성이 없으므로 각 나라에서는 방화측면에서 볼 때 꼭 필요하다고 인정되는 대상물만을 방염처리 하도록 법으로 규정해 놓고 있다.Flame retardant treatment of combustible materials and woods, fibers and plastics used in daily life is difficult in terms of technology and economics. In practice, however, there is no need for this, and in each country, the law requires that only objects that are deemed necessary in terms of fire protection be treated by law.
미국 유럽 선진국과 일본의 경우를 보면 방염처리를 요구하는 대상물로는 건축 내외장재 이외에도 차량, 기차, 선박, 항공기, 등의 각종 수송체의 내외장재, 각종 전기, 전자제품의 가연성 부품, 공산품 등 어린이들의 완구류 의류 등 광범위하게 규정하고 있다.In the case of developed countries in the US, Europe, and Japan, objects that require flame retardant treatment are children's toys such as interior and exterior materials of vehicles, trains, ships, aircrafts, and other materials such as vehicles, combustible parts of electric and electronic products, and industrial products. It is regulated widely such as clothing.
한국의 경우 고층건물과 극장, 호텔, 병원 등 특수장소의 내외장재인 합판, 섬유판, 카페트, 커텐 등의 방염처리 대상이 소방법에 규정되어 있고, 목조문화재의 경우는 아직 소방법에 규정되어 있지 않지만 문화재 관리국에서 별도로 방염처리를 강력히 권장하고 있다.In Korea, fire prevention targets such as plywood, fiberboard, carpets, and curtains, which are interior and exterior materials for high-rise buildings, theaters, hotels, hospitals, and other special places, are regulated in the Fire Protection Law. Flame retardant treatment is highly recommended.
방염처리 대상물을 재료별로 보면 목재류와 섬유류, 플라스틱류 등 크게 세가지로 구분되는데 방염처리 방법은 처리대상의 종류에 따라서도 다르지만 처리대상물의 재료에 따라 크게 달라진다.In terms of materials, the materials are classified into three types, such as wood, fiber, and plastics. The method of flameproofing varies greatly depending on the type of object to be treated.
현존하는 우리나라 목조 문화재에서도 알 수 있는 바와 같이, 적절한 보존방법만 강구된다면 목재의 수명은 1,000년 이상이 되는 것으로 확인되고 있으나, 이러한 우수한 목조 문화재에 대한 보존기술은 현재까지 매우 취약하다.As can be seen from the existing Korean wooden cultural assets, if the proper preservation method is taken, the life of the wood is confirmed to be over 1,000 years, but the preservation technology for such excellent wooden cultural assets is very weak to date.
목조 문화재는 재질이 주로 나무로 되어 있어 화재에 매우 취약한 점이 있고 곰팡이, 곤충 등에 대한 저항력이 약하여 문제가 되어 왔다. 목조 문화재는 효과적인 방염, 방미, 방부, 방충처리 등을 하지 않을 경우 화재 및 생물 열화에 대한 위험성이 매우 높다.Wooden cultural properties are mainly made of wood, so they are very vulnerable to fire and have a weak resistance to mold, insects, and the like. Wooden cultural properties have a high risk of fire and biodegradation if they are not effectively flameproofed, protected, preserved, or treated.
기존의 일반적인 목재 방염약제로 수용성 무기염류계로 인산염이나, 황산염, 붕산 등이 사용되어 왔다. 수용성 무기염류는 방염효과는 비교적 우수하나 목조 문화재에 적용한 경우 건조 후 목재 표면에 결정성 분말이나 백분현상을 일으키거나, 단청 색상 중 뇌록색 등에 포함되어 있는 호분의 주된 성분인 탄산칼슘과 반응하여 황산인산칼슘 등의 불용성 염으로 변하여 백화현상 등을 일으켜, 단청의 외관을 손상시킬 뿐만 아니라 방염성도 저하시키는 결과를 가져온다. Phosphates, sulfates, boric acids, etc. have been used as water-soluble inorganic salts as conventional wood flame retardants. Water-soluble inorganic salts have excellent flame retardant effect, but when applied to wooden cultural properties, sulfuric acid reacts with calcium carbonate, which is the main component of the powder contained in cerebrum, etc. It turns into an insoluble salt such as calcium phosphate, causes whitening, and the like, which not only damages the appearance of mono, but also reduces the flame resistance.
종래 목조 건축물 등의 방염을 위해 한국공개특허 제 2010-0074444 호 및 제 2007-0103884 호와 한국등록특허 제 776377 호 등이 개시되었으나, 상기 문제들의 해결에는 미흡한 실정이다.Conventional Korean Patent Publication Nos. 2010-0074444 and 2007-0103884 and Korean Patent No. 776377 have been disclosed for the protection of wooden buildings. However, there is insufficient solution to the above problems.
본 발명의 해결과제는 다양한 다공성 건축물의 내외장자재의 방염성능을 증진시키며, 일반 건축물 및 목조 건축물, 문화재를 비롯한 각종 목조 구조물의 단청 및 단청색 13 종 (뇌록, 양록, 장단, 군청, 삼청, 석황, 석간주, 주홍, 지당, 하엽, 다자, 육색, 먹)에 백분 또는 백화 현상을 수반하지 않고, 방부, 방미, 방충 효과를 동시에 부여할 수 있으며, 다공성 건축자재 및 목구조물의 열화현상을 지속적이면서도 반영구적으로 방지하고, 건축물의 외관을 장기적으로 유지시킬 수 있으며, 우수한 내약품성을 지님은 물론, 다공성 구조물과의 결합성 및 친화성이 우수할 뿐만 아니라, 간단한 처리로 단시간에 구조물을 효과적으로 처리할 수 있는 친환경적 실온 경화용 방염제 방염 조성물을 제공하는 것을 그 목적으로 한다.The problem of the present invention is to improve the flameproofing performance of the interior and exterior materials of various porous buildings, and 13 kinds of mono and mono blue of various wooden structures, including general buildings, wooden buildings, cultural properties (Benrok, Yangnok, Jangdan, Guncheong, Samcheong, It does not involve white powder or bleaching effect of turmeric, limestone, scarlet, land sugar, lower lobe, multilateral, flesh color, ink), and it can give antiseptic, antiseptic, and insect repellent effect at the same time, and it keeps deterioration of porous building materials and wooden structures. It can prevent semipermanently and maintain the appearance of building for a long time. It not only has excellent chemical resistance, but also has excellent binding and affinity with porous structure. It is an object of the present invention to provide an environmentally friendly flame-retardant flame retardant composition for room temperature curing.
본 발명의 방염 조성물은 상술한 바와 같은 목적을 달성하기 위하여, In order to achieve the object as described above, the flame retardant composition of the present invention,
치환되지 않은 또는 프로필기 및 에톡시기로 치환된 실리카 졸 100 중량부, 100 parts by weight of a silica sol unsubstituted or substituted with a propyl group and an ethoxy group,
인산염, 황산염, 할로겐산염, 설파민산염, 붕소염, 포스폰산염 및 그 혼합물로 이루어진 군에서 선택된 방염 보조제 1 내지 600 중량부, 1 to 600 parts by weight of a flame retardant aid selected from the group consisting of phosphates, sulfates, halides, sulfamates, boron salts, phosphonates and mixtures thereof,
치환되지 않은 또는 아민으로 치환된 탄소수 1 내지 5의 알콜 10 내지 500 중량부, 및 10 to 500 parts by weight of an unsubstituted or substituted amine with 1 to 5 carbon atoms, and
물 50 내지 10000 중량부50 to 10000 parts by weight of water
를 포함하는 것을 특징으로 한다.Characterized in that it comprises a.
또한, 상기 실리카 졸의 실리카 농도는 5 내지 50 중량%일 수 있다.In addition, the silica concentration of the silica sol may be 5 to 50% by weight.
또한, 상기 인산염은 제일인산암모늄, 제이인산암모늄, 제삼인산암모늄, 제일인산나트륨, 제이인산나트륨, 제삼인산나트륨, 제일인산칼륨, 제이인산칼륨, 제삼인산칼륨, 제일인산구아니딘, 제이인산구아니딘, 축합도가 1 내지 250의 저축합 암모늄폴리포스페이트, 구아닐유레아포스페이트, 인산의 아민염 및 그 혼합물로 이루어진 군에서 선택될 수 있다.In addition, the phosphate is ammonium monophosphate, diammonium phosphate, ammonium triphosphate, sodium monophosphate, sodium diphosphate, sodium triphosphate, potassium monophosphate, potassium diphosphate, tripotassium phosphate, guanidine phosphate, guanidine diphosphate, condensation The degree can be selected from the group consisting of low condensed ammoniumpolyphosphate of 1 to 250, guanylureaureaphosphate, amine salt of phosphoric acid and mixtures thereof.
또한, 상기 황산염은 황산암모늄, 황산나트륨, 황산칼륨, 황산의 아민염 및 그 혼합물로 이루어진 군에서 선택될 수 있다.In addition, the sulfate may be selected from the group consisting of ammonium sulfate, sodium sulfate, potassium sulfate, amine salt of sulfuric acid and mixtures thereof.
또한, 상기 할로겐산염은 염화암모늄, 염화나트륨, 염화칼륨, 브롬화암모늄, 브롬화나트륨, 브롬화칼륨, 할로겐산의 아민염 및 그 혼합물로 이루어진 군에서 선택될 수 있다.In addition, the halide salt may be selected from the group consisting of ammonium chloride, sodium chloride, potassium chloride, ammonium bromide, sodium bromide, potassium bromide, amine salts of halogen acids and mixtures thereof.
또한, 상기 설파민산염은 구아니딘설파메이트, 암모늄설파메이트, 설파민산나트륨, 설파민산칼륨, 설파민산의 아민염 및 그 혼합물로 이루어진 군에서 선택될 수 있다.In addition, the sulfamate may be selected from the group consisting of guanidine sulfamate, ammonium sulfamate, sodium sulfamate, potassium sulfamate, an amine salt of sulfamic acid, and mixtures thereof.
또한, 상기 붕소염은 붕산, 붕사, 산화 붕소, 포타슘펜타보레이트(KB5O7), 포타슘테트라보레이트(K2B4O7), 소듐메타보레이트(NaBO2), 암모늄펜타보레이트[(NH4)2B10O16·8H2O], 붕산의 아민염 및 그 혼합물로 이루어진 군에서 선택될 수 있다.In addition, the boron salt is boric acid, borax, boron oxide, potassium pentaborate (KB 5 O 7 ), potassium tetraborate (K 2 B 4 O 7 ), sodium metaborate (NaBO 2 ), ammonium pentaborate [(NH 4 ) 2 B 10 O 16 · 8H 2 O], an amine salt of boric acid, and mixtures thereof.
또한, 상기 포스폰산염은 아미노트리메틸렌포스폰산, 1-하이드록시에틸렌-1,1-다이포스포폰산, 에틸렌다이아민테트라메틸렌포스폰산, 헥사메틸렌다이아민테트라메틸렌포스폰산, 다이에틸렌트리아민펜타메틸렌포스폰산, 포스폰산의 아민염 및 그 혼합물로 이루어진 군에서 선택될 수 있다.Further, the phosphonic acid salts include aminotrimethylenephosphonic acid, 1-hydroxyethylene-1,1-diphosphoic acid, ethylenediaminetetramethylenephosphonic acid, hexamethylenediaminetetramethylenephosphonic acid, and diethylenetriaminepenta. It may be selected from the group consisting of methylenephosphonic acid, amine salt of phosphonic acid and mixtures thereof.
또한, 상기 물은 나노버블수일 수 있다.In addition, the water may be nanobubble water.
또한, 상기 나노버블수의 기포 평균입경은 1 내지 500 nm일 수 있다.In addition, the average bubble diameter of the nanobubble number may be 1 to 500 nm.
또한, 상기 나노버블수의 액체 및 기체의 중량비는 액체 : 기체 = 70 내지 99.9 : 0.1 내지 30일 수 있다.In addition, the weight ratio of the liquid and the gas of the nanobubble water may be a liquid: gas = 70 to 99.9: 0.1 to 30.
또한, 상기 나노버블수를 구성하는 기체는 공기, 질소, 산소 및 그 혼합물로 이루어진 군에서 선택될 수 있다.In addition, the gas constituting the nanobubble water may be selected from the group consisting of air, nitrogen, oxygen and mixtures thereof.
본 발명에 따른 비휘발성 실온 경화용 유무기질 결합제 방염 조성물은 목재나 짚 등과 같은 다공성 구조물에 간단히 도포, 침적 또는 분사함으로써 작업이 간편하다. 이처럼 다공성 구조물에 적용된 본 발명의 조성물은 상기 다공성 구조물 내부까지 침투하여, 구조물 구축과 그 구조물의 지속적인 방염성을 유지하며, 화학생물적 열화현상 방지 효과를 얻을 수 있음은 물론, 건축물의 외관을 획기적으로 향상시킬 수 있으며, 단시간에 구조물을 효과적으로 처리할 수 있다. Non-volatile room temperature-based organic-based binder flame retardant composition according to the present invention is easy to work by simply applying, depositing or spraying on a porous structure such as wood or straw. As such, the composition of the present invention applied to the porous structure penetrates to the inside of the porous structure, maintains the structure of the structure and the continuous flame resistance of the structure, and can obtain the effect of preventing chemical and biological deterioration, as well as significantly the appearance of the building It can be improved and the structure can be effectively processed in a short time.
이와 같은 본 발명에 따른 대표적인 처리효과를 들면 다음과 같다.Representative treatment effects according to the present invention as described above are as follows.
1) 방염(난연)/내구성 증진 효과:1) Flame retardant (flame retardant) / durability enhancement effect:
본 발명에 따른 실온 경화형 방염 조성물을 다공성 구조물에 도포하면, 구조물 내·외부에 분자 결합체를 형성하기 때문에, 화염전파를 억제하여 탄화면적과 잔염시간 및 잔신시간 측면에서 우수한 난연효과를 거둘 수 있고, 구조물의 강도가 증대되며 내마모성이 향상된다. When the room temperature curable flame retardant composition according to the present invention is applied to a porous structure, since the molecular conjugate is formed inside and outside the structure, flame propagation can be suppressed to achieve excellent flame retardant effect in terms of carbon screen area, afterflame time and residual time, The strength of the structure is increased and the wear resistance is improved.
2) 화학생물적/열화 방지 효과:2) Chemical biological / degradation protection effect:
본 발명에 따른 방염 조성물은 다공성 목재 구조물 등의 생물적 열화 내지는 중성화 현상의 요인인 물, CO2, NOx, SOx 등의 진입을 차단함으로써 산성화와 그로 인한 열화를 방지할 수 있다. 그리고, 생물학적 저항성이 뛰어나 외부로부터 곤충이나 애벌레의 침투를 막아 다공성 구조물에 효과적이다.The flame retardant composition according to the present invention can prevent acidification and its deterioration by blocking the entry of water, CO 2 , NO x, SO x, etc., which are factors of biological degradation or neutralization of the porous wood structure. In addition, its excellent biological resistance prevents the penetration of insects and larvae from the outside and is effective for porous structures.
3) 내후성/동결융해 방지 효과:3) Weathering resistance / freeze thawing effect:
본 발명에 따른 방염 조성물을 다공성 구조물에 도포하면, 내후성이 향상되고 자외선에 의한 열화를 억제시킨다. 또한, 수분의 침투를 억제하여 동결/융해 사이클에 의해 발생하는 크랙을 감소시킨다.Application of the flame retardant composition according to the present invention to a porous structure improves weather resistance and suppresses deterioration by ultraviolet rays. It also inhibits the ingress of moisture to reduce cracks caused by freeze / thaw cycles.
4) 외관 향상 효과:4) Appearance Enhancement Effect:
본 발명에 따른 방염 조성물을 다공성 구조물에 도포하면, 개질 반응에 의해 재료의 표면이 봉인되어 건축물의 외관이 미려해지는 효과가 있다. 더구나, 곰팡이의 발생도 억제하는 것이 가능하다.When the flame retardant composition according to the present invention is applied to a porous structure, the surface of the material is sealed by the reforming reaction, and the appearance of the building is beautiful. In addition, it is possible to suppress the occurrence of mold.
5) 방염 향상 효과:5) Flame retardant effect:
본 발명에 따른 방염 조성물을 다공성 구조물에 도포하면, 고분자의 열분해 경로를 변경하여 가연성 기체의 양을 감소시키고 잔존 탄화물의 양을 증가시켜 난연성을 부여한다.When the flame retardant composition according to the present invention is applied to a porous structure, the pyrolysis path of the polymer is changed to reduce the amount of flammable gas and increase the amount of residual carbide to impart flame retardancy.
그리고, 연소시 고분자 표면에 막을 형성하여 가연성 기체와 공기 중 산소와의 접촉을 차단하여 연소가 일어나지 않게 하거나, 발열량을 줄일 수 있다.In addition, by forming a film on the surface of the polymer during combustion to block the contact between the combustible gas and oxygen in the air to prevent the combustion occurs or reduce the amount of heat generated.
또한, 연소 반응에 참여하는 Hㆍ, OHㆍ 와 같은 활성 라디칼을 난연제가 흡수하고, 연소과정에서 유지되어야 하는 열에너지를 소비시킴으로써 연속반응을 억제한다. In addition, the continuous reaction is suppressed by the flame retardant absorbing active radicals such as H. OH. OH. Participating in the combustion reaction, and consuming heat energy that must be maintained in the combustion process.
본 발명의 방염 조성물은 목조 문화재를 비롯한 목재류 및 볏짚류, 섬유류에 방염, 방미, 방부, 방충효과를 동시에 부여할 수 있을 뿐만 아니라 백분이나 백화현상을 발생시키지 않고, 단청의 색상 변화도 비교적 적게 나타난다. 더욱이 일액형 액체로 제공되므로 처리시간과 비용을 절약할 수 있고 사용이 간편하다.The flame retardant composition of the present invention can not only impart flame retardant, anti-fog, antiseptic, and insect repellent effects to woods, rice straws, and textiles, including wooden cultural assets, but also cause no white powder or whitening, and have a relatively small color change. . Moreover, it is available as a one-component liquid, which saves processing time and costs and is easy to use.
그리고, 목재의 탄화면적과 잔염시간 및 잔신시간 측면에서 우수하고, 목재 문화재의 13 종 단청색에 대해 백화, 박락, 얼룩 등 유해성이 없는 장점이 있다.In addition, it is excellent in terms of the surface area of burned wood, afterflame time and remaining time, and there are no harmful effects such as whitening, peeling, and staining for the 13 kinds of monochromatic colors of wood cultural properties.
이와 같은 난연 원리를 이용하여 범용 고분자 제품에 난연성을 부여하는 방법은 다음과 같다.The method of imparting flame retardancy to general-purpose polymer products using the flame retardant principle is as follows.
ㆍ분자구조 변경을 통한 난연성 고분자의 제조ㆍ Manufacture of flame retardant polymer by changing molecular structure
ㆍ반응형 난연제를 분자 구조내에 화학적으로 결합시키는 방법ㆍ How to chemically bind reactive flame retardant in molecular structure
ㆍ첨가형 난연제를 분자 내에 물리적으로 첨가시키는 방법ㆍ How to physically add additive flame retardant in molecule
이하, 본 발명의 바람직한 실시예에 대하여 상세히 설명한다. 또한, 하기의 설명에서는 구체적인 구성요소 등과 같은 많은 특정사항들이 설명되어 있는데, 이는 본 발명의 보다 전반적인 이해를 돕기 위해서 제공된 것일 뿐 이러한 특정 사항들 없이도 본 발명이 실시될 수 있음은 이 기술분야에서 통상의 지식을 가진 자에게는 자명하다 할 것이다. 그리고, 본 발명을 설명함에 있어서, 관련된 공지 기능 혹은 구성에 대한 구체적인 설명이 본 발명의 요지를 불필요하게 흐릴 수 있다고 판단되는 경우 그 상세한 설명을 생략한다.Hereinafter, preferred embodiments of the present invention will be described in detail. In the following description, numerous specific details, such as specific elements, are set forth in order to provide a thorough understanding of the present invention, and it is to be understood that the present invention may be practiced without these specific details, It will be obvious to those who have knowledge of. In the following description of the present invention, a detailed description of known functions and configurations incorporated herein will be omitted when it may make the subject matter of the present invention rather unclear.
본 발명에서 "목조 문화재"라 함은 문화재 보호법에 의해 관리되는 국보, 보물, 유형 문화재 등으로 지정된 문화재는 물론, 보존가치가 있는 여타의 모든 목조 건축물, 목조 구조물을 가리키는 것이다.In the present invention, the term "wooden cultural property" refers to all other wooden buildings and wooden structures having a preservation value, as well as cultural assets designated as national treasures, treasures, and tangible cultural properties managed by the Cultural Property Protection Act.
본 발명의 비휘발성 상온 경화용 유무기질 결합제 내외장 목재용 및 볏짚 방염액 조성물은 상술한 바와 같은 목적을 달성하기 위하여, In order to achieve the object as described above, the non-volatile room temperature curing organic-inorganic binder internal and external wood and rice straw flame retardant composition of the present invention,
치환되지 않은 또는 프로필기 및 에톡시기로 치환된 실리카 졸 100 중량부, 100 parts by weight of a silica sol unsubstituted or substituted with a propyl group and an ethoxy group,
인산염, 황산염, 할로겐산염, 설파민산염, 붕소염, 포스폰산염 및 그 혼합물로 이루어진 군에서 선택된 방염 보조제 1 내지 600 중량부, 1 to 600 parts by weight of a flame retardant aid selected from the group consisting of phosphates, sulfates, halides, sulfamates, boron salts, phosphonates and mixtures thereof,
치환되지 않은 또는 아민으로 치환된 탄소수 1 내지 5의 알콜 10 내지 500 중량부, 및 10 to 500 parts by weight of an unsubstituted or substituted amine with 1 to 5 carbon atoms, and
물 50 내지 10000 중량부50 to 10000 parts by weight of water
를 포함하는 것을 특징으로 한다.Characterized in that it comprises a.
상기 치환되지 않은 또는 프로필기 및 에톡시기로 치환된 콜로이드 실리카 졸은 상기 다양한 방염 보조제와 서로 반응하여 실리카 졸 - 방염 보조제 화합물을 형성하고 이 화합물이 방염제를 구성하는 것으로 예측된다.The unsubstituted or substituted propyl group and ethoxy group colloidal silica sol reacts with the various flame retardant aids to form a silica sol flame retardant adjuvant and the compound constitutes a flame retardant.
여기서, 상기 실리카 졸 내부의 실리카 농도는 일반적으로 5 내지 50 중량%이다.Here, the silica concentration in the silica sol is generally 5 to 50% by weight.
또한, 상기 인산염은 제일인산암모늄, 제이인산암모늄, 제삼인산암모늄, 제일인산나트륨, 제이인산나트륨, 제삼인산나트륨, 제일인산칼륨, 제이인산칼륨, 제삼인산칼륨, 제일인산구아니딘, 제이인산구아니딘, 축합도가 1 내지 250의 저축합 암모늄폴리포스페이트, 구아닐유레아포스페이트, 인산의 아민염 및 그 혼합물로 이루어진 군에서 선택될 수 있다.In addition, the phosphate is ammonium monophosphate, diammonium phosphate, ammonium triphosphate, sodium monophosphate, sodium diphosphate, sodium triphosphate, potassium monophosphate, potassium diphosphate, tripotassium phosphate, guanidine phosphate, guanidine diphosphate, condensation The degree can be selected from the group consisting of low condensed ammoniumpolyphosphate of 1 to 250, guanylureaureaphosphate, amine salt of phosphoric acid and mixtures thereof.
또한, 상기 황산염은 황산암모늄, 황산나트륨, 황산칼륨, 황산의 아민염 및 그 혼합물로 이루어진 군에서 선택될 수 있다.In addition, the sulfate may be selected from the group consisting of ammonium sulfate, sodium sulfate, potassium sulfate, amine salt of sulfuric acid and mixtures thereof.
또한, 상기 할로겐산염은 염화암모늄, 염화나트륨, 염화칼륨, 브롬화암모늄, 브롬화나트륨, 브롬화칼륨, 할로겐산의 아민염 및 그 혼합물로 이루어진 군에서 선택될 수 있다.In addition, the halide salt may be selected from the group consisting of ammonium chloride, sodium chloride, potassium chloride, ammonium bromide, sodium bromide, potassium bromide, amine salts of halogen acids and mixtures thereof.
또한, 상기 설파민산염은 구아니딘설파메이트, 암모늄설파메이트, 설파민산나트륨, 설파민산칼륨, 설파민산의 아민염 및 그 혼합물로 이루어진 군에서 선택될 수 있다.In addition, the sulfamate may be selected from the group consisting of guanidine sulfamate, ammonium sulfamate, sodium sulfamate, potassium sulfamate, an amine salt of sulfamic acid, and mixtures thereof.
또한, 상기 붕소염은 붕산, 붕사, 산화 붕소, 포타슘펜타보레이트(KB5O7), 포타슘테트라보레이트(K2B4O7), 소듐메타보레이트(NaBO2), 암모늄펜타보레이트[(NH4)2B10O16·8H2O], 붕산의 아민염 및 그 혼합물로 이루어진 군에서 선택될 수 있다.In addition, the boron salt is boric acid, borax, boron oxide, potassium pentaborate (KB 5 O 7 ), potassium tetraborate (K 2 B 4 O 7 ), sodium metaborate (NaBO 2 ), ammonium pentaborate [(NH 4 ) 2 B 10 O 16 · 8H 2 O], an amine salt of boric acid, and mixtures thereof.
또한, 상기 포스폰산염은 아미노트리메틸렌포스폰산, 1-하이드록시에틸렌-1,1-다이포스포폰산, 에틸렌다이아민테트라메틸렌포스폰산, 헥사메틸렌다이아민테트라메틸렌포스폰산, 다이에틸렌트리아민펜타메틸렌포스폰산, 포스폰산의 아민염 및 그 혼합물로 이루어진 군에서 선택될 수 있다.Further, the phosphonic acid salts include aminotrimethylenephosphonic acid, 1-hydroxyethylene-1,1-diphosphoic acid, ethylenediaminetetramethylenephosphonic acid, hexamethylenediaminetetramethylenephosphonic acid, and diethylenetriaminepenta. It may be selected from the group consisting of methylenephosphonic acid, amine salt of phosphonic acid and mixtures thereof.
상기 방염 보조제는 단독 또는 혼합의 형태로 사용할 수 있으며, 그 함량은 상기 실리카 졸 100 중량부에 대하여 1 내지 600 중량부인 것이 바람직하다. 방염 보조제의 함량이 상기 범위 미만이면 충분한 방염 성능을 거두기 어려우며, 반대로 상기 범위를 초과하면 단청에 대해 백분이나 백화 현상을 나타내거나 균일한 일액형으로 제조하기가 곤란하다.The flame retardant aid can be used alone or in a mixed form, the content of which is preferably 1 to 600 parts by weight based on 100 parts by weight of the silica sol. If the content of the flame retardant is less than the above range, it is difficult to achieve sufficient flame retardant performance. On the contrary, if the content of the flame retardant exceeds the above range, it is difficult to show white powder or whitening phenomenon to mono or to prepare a uniform one-part form.
본 발명은 특히 실리카 졸과 상기 방염 보조제가 목재 등의 공극에 깊숙이 침투하는 것을 보조하기 위해 침투 보조제를 필수성분으로 포함하는 것을 특징으로 한다.In particular, the present invention is characterized in that the silica sol and the flame retardant aid include a penetration aid as an essential ingredient to assist the deep penetration of pores such as wood.
상기 침투보조제로는 치환되지 않은 또는 아민으로 치환된 탄소수 1 내지 5의 알콜이 사용되며, 예컨대, 메탄올, 에탄올, 프로판올, 이소프로필알콜, 모노에탄올아민 등을 들 수 있다.As the penetration aid, an unsubstituted or substituted C1-C5 alcohol is used, and examples thereof include methanol, ethanol, propanol, isopropyl alcohol, monoethanolamine, and the like.
이러한 침투 보조제는 실리카 졸 100 중량부 당 10 내지 500 중량부가 사용되는 것이 바람직한데, 상기 범위 미만에서는 침투가 충분하고 신속하게 이루어지지 않아 방염성능이 떨어지고, 반대로 상기 범위를 초과하면 건조시간이 불필요하게 길어지는 단점이 있다.It is preferable that such a penetration aid is used in an amount of 10 to 500 parts by weight per 100 parts by weight of the silica sol. If the penetration is less than the above range, the penetration is insufficient and the flame retardant performance is reduced. There is a drawback to lengthening.
한편, 본 발명의 방염 조성물을 다공성 구조물의 표면에 침투시키는 방법은 상기 방염 조성물을 다공성 구조물 표면에 도포, 함침 또는 분산하거나, 다공성 물건을 본 발명의 방염 조성물에 침지시킴으로써 이루어진다.On the other hand, the method of infiltrating the flameproof composition of the present invention on the surface of the porous structure is made by applying, impregnating or dispersing the flameproof composition on the surface of the porous structure, or immersing the porous object in the flameproof composition of the present invention.
본 발명은 별도의 분산제를 사용하지 않고 용제의 결합력과 화학반응을 적절한 온도제어로 사용한 것을 특징으로 한다. 분산제는 분산질이 분산매에 잘 분산되도록 첨가하는 성분인데, 이 자체가 환경에 유해할 수 있고, 더군다나 본 발명의 경우에는 콜로이드 실리카 졸의 반응을 저해하므로 그 사용을 지양하는 것이 바람직하다. 본 발명자들은 일반적인 물 대신 나노버블수를 사용함으로써 분산제의 사용을 최소화하고 방염 보조제 등을 완전하고 안정적으로 분산시킬 수 있었으며, 이 점이 본 발명의 주요한 장점으로 기능한다.The present invention is characterized by using the bonding strength and chemical reaction of the solvent in the appropriate temperature control without using a separate dispersant. The dispersant is a component which is added to disperse the dispersant well in the dispersion medium, which itself may be harmful to the environment, and furthermore, in the case of the present invention, it is preferable to avoid its use because it inhibits the reaction of the colloidal silica sol. The present inventors were able to minimize the use of dispersant and disperse the flame retardant and the like completely and stably by using nanobubble water instead of general water, and this is a major advantage of the present invention.
최근 작은 직경을 갖는 기포(버블)에 여러가지 작용 효과가 있다는 것이 밝혀졌으며, 현재 이러한 기포를 제조하는 기술 및 그 효과에 대한 연구가 진행되고 있다. 상기 기포는 그 직경에 따라서 마이크로 버블, 마이크로 나노버블 및 나노버블로 분류할 수 있다. 구체적으로는, 마이크로 버블은 그 발생시에 있어서 10 내지 수십 ㎛의 직경을 갖는 기포이고, 마이크로 나노버블은 그 발생시에 있어서 수백 ㎚ 내지 10 ㎛의 직경을 갖는 기포이며, 나노버블은 그 발생시에 있어서 수백 ㎚ 이하의 직경을 갖는 기포이다. 또한, 마이크로 버블은 발생 후의 수축 운동에 의해 그 일부가 마이크로 나노버블로 변화되는 경우가 있다. 또, 나노버블은 장기간에 걸쳐 액체 중에 존재할 수 있다는 성질을 가지고 있다.Recently, it has been found that there are various effects on bubbles (bubbles) having a small diameter, and researches on the technology for producing such bubbles and their effects are currently underway. The bubbles can be classified into micro bubbles, micro nano bubbles and nano bubbles according to their diameters. Specifically, the microbubble is a bubble having a diameter of 10 to several tens of micrometers at the time of its generation, and the micro nanobubbles are bubbles having a diameter of several hundred nm to 10 micrometers at the time of its generation, and the nanobubbles are hundreds of microbubbles at the time of its generation. It is a bubble which has a diameter of nm or less. In addition, a part of micro bubbles may change into micro nano bubbles by the contraction motion after generation | occurrence | production. In addition, nanobubbles have the property of being present in a liquid for a long time.
본 발명은 이러한 나노버블을 함유한 나노버블수를 사용함으로써 별도의 분산제 없이도 무기물들을 용이하게 혼합시킬 수 있고, 오랜 시간 경과 후에도 상기 무기물들이 안정적으로 혼합상태를 유지할 수 있음을 가장 큰 특징으로 한다.The present invention is characterized in that the nanobubbles containing the nanobubbles can be easily mixed with inorganic materials without a separate dispersant, and the inorganic materials can be stably mixed even after a long time.
상기 나노버블수를 구성하는 기포의 평균입경은 1 내지 500 nm인 것이 바람직한데, 1 nm 미만의 나노버블을 형성시키려면 초음파를 더 많이 가하거나 펌핑 압력을 상승시켜야 하므로 불필요한 운전비용의 상승을 가져오고, 반대로 평균입경이 500 nm를 초과하면 본 발명 소기의 목적을 달성하기 곤란한 문제점이 있다.It is preferable that the average particle diameter of the bubbles constituting the nanobubble number is 1 to 500 nm. To form the nanobubble of less than 1 nm, it is necessary to apply more ultrasonic waves or to increase the pumping pressure. On the contrary, if the average particle diameter exceeds 500 nm, there is a problem that it is difficult to achieve the object of the present invention.
그리고, 상기 나노버블수를 구성하는 기체는 공기가 일반적이나, 산화력을 필요로 하는 경우에는 산소를, 반대로 산화가 문제되는 경우에는 질소를 사용하는 것이 더 바람직하며, 이들의 혼합 기체를 사용하는 것도 가능하다.In addition, the gas constituting the nanobubble water is generally air, but when oxygen requires an oxidizing power, it is more preferable to use nitrogen when oxidation is a problem, and to use a mixed gas thereof. It is possible.
상기 나노버블수를 구성하는 액체 및 기체의 중량비는 액체 : 기체 = 70 내지 99.9 : 0.1 내지 30인 것이 바람직한데, 기체가 0.1 중량비 미만인 경우 본 발명 소기의 목적을 달성하기 곤란하고, 30 중량비를 초과하는 경우 과도한 기포 주입으로 인한 운전비 상승의 문제점이 있다.The weight ratio of the liquid and the gas constituting the nanobubble water is preferably liquid: gas = 70 to 99.9: 0.1 to 30. When the gas is less than 0.1 weight ratio, it is difficult to achieve the object of the present invention, and exceeds 30 weight ratio. If there is a problem of operating cost increase due to excessive bubble injection.
본 발명의 방염 조성물을 이용한 다공성 구조물의 처리방법은, 상기 방염 조성물을 다공성 구조물, 목재류, 종이류, 의류의 표면에 도포, 침적 또는 분사하고, 상기 방염 조성물이 표면 또는 내부에 스며들어, 경화됨으로써 방염시키는 단계를 포함한다.In the method for treating a porous structure using the flame retardant composition of the present invention, the flame retardant composition is applied to a surface of a porous structure, wood, paper, or clothing, deposited or sprayed, and the flame retardant composition penetrates into the surface or inside and is cured by curing. It comprises the step of.
이렇게 공극으로 스며든 본 발명의 방염 조성물을 구성하는 화학종은 다공성 구조물 내부에 존재하는 공극에 코팅이 되어, 방염성 화합물을 생성하게 되는 것이다.The chemical species constituting the flame retardant composition of the present invention soaked into the pores are coated on the pores present in the porous structure, thereby producing a flame retardant compound.
나아가, 본 발명의 방염 조성물은 화학적 저항성이 뛰어나, 경화된 결정체는 흡수성을 감소시키고 자외선, 빛, 솔벤트, 글리즈 및 일반 화학약품에 대해 높은 내구성을 나타낸다. Furthermore, the flame retardant composition of the present invention is excellent in chemical resistance, so that the cured crystals reduce the absorbency and exhibit high durability against ultraviolet rays, light, solvents, glyces and general chemicals.
본 발명의 방염 조성물이 적용될 수 있는 분야는 다공성 건축물의 내외장재, 목재를 이용한 외부 노출 조형물 일체의 오염방지 및 방염, 벤치나 난간처럼 부드러운 촉감을 필요로 하는 목구조물 외부데크, 외부목재의 사이딩, 외부도어, 펜스, 테이블, 창문틀과 외부 몰딩, 학교 및 유치원의 목재 놀이기구, 교보제, 목조문화제, 사찰, 목제건축물, 외장용 목재 제품, 가제보, 꽃박스, 격자무늬목재, 목조주택 등을 들 수 있다. Fields to which the flame retardant composition of the present invention can be applied are interior and exterior materials of porous buildings, external pollution prevention and flame prevention of all external exposed sculptures using wood, wooden structure external decks that require a soft touch like benches or railings, siding of external wood, exterior Doors, fences, tables, window frames and exterior moldings, wooden playground equipment for schools and kindergartens, Kyoboje, wooden cultural festivals, temples, wooden buildings, exterior wooden products, gazebos, flower boxes, plaids, wooden houses, etc. have.
이하, 본 발명의 실시예에 대하여 설명한다.Hereinafter, embodiments of the present invention will be described.
실시예Example
실시예Example : 상온 Room temperature 경화용Hardening 유무기질 결합제인 내외장 목재 및 볏짚용 방염 조성물 Flame retardant composition for interior and exterior wood and rice straw
하기 표 1에 나타낸 조성비에 따라, 본 발명의 일 실시예에 따른 방염 조성물을 제조하였다.According to the composition ratio shown in Table 1, to prepare a flame retardant composition according to an embodiment of the present invention.
Item
Order of judgment
Item
Order of judgment
Item
Order of judgment
Item
Order of judgment
시험예Test Example 1 : 이화학 성능평가 1: Physical and chemical performance evaluation
1) 유기물(TVOCs) 방출1) Release of Organics (TVOCs)
상기 표 9의 실시예로부터 유기물 방출 여부를 분석한 결과를 표 10에 나타내었다. 시험은 기체 크로마토그래피/MS와 Headspace (Perkin-elmer, USA), Tarac GC/DSQⅡMS (ThermoFinnigan, USA)로 수행하였다.Table 10 shows the results of analyzing the organic material release from the Example of Table 9. Testing was performed by gas chromatography / MS, Headspace (Perkin-elmer, USA), Tarac GC / DSQIIMS (ThermoFinnigan, USA).
2) 포름알데히드 방산량2) Formaldehyde Dissipation
방염제를 시험편 (70 mm× 150 mm, 8장) 양면에 도포하여 증류수 300 mL를 넣은 데시케이터에 설치한다. 온도 23 ℃에서 24시간 동안 유지하여 증류수에 포함된 포름알데히드를 발색시켜 UV흡광광도계 (UV-1650PC, SHIMADZU)로 측정한다.A flame retardant is applied to both sides of the specimen (70 mm × 150 mm, 8 sheets) and installed in a desiccator containing 300 mL of distilled water. It is maintained at a temperature of 23 ℃ for 24 hours to form formaldehyde contained in distilled water and measured by UV absorbance photometer (UV-1650PC, SHIMADZU).
3) 중금속 함량 (Pb, Cd, Hg, Cr6+)3) Heavy metal content (Pb, Cd, Hg, Cr6 +)
방염제 용액을 ICP, AAS, UV흡광광도계를 사용하여 분석한다.Flame retardant solution is analyzed using ICP, AAS, UV absorbance photometer.
4) 수소이온농도 (pH)4) hydrogen ion concentration (pH)
방염제를 pH meter로 측정한다.Flame retardant is measured with a pH meter.
5) 비중5) Specific gravity
비중병에 방염제를 채우고 전ㆍ후 무게차를 이용하여 측정한다.Fill the pycnometer with flame retardant and measure the weight difference before and after.
실시예에 대한 유해물질 함유여부 및 기본물성 시험결과 요약은 표 10 및 표 11과 같다.Table 10 and Table 11 summarize the test results for the presence of hazardous substances and basic physical properties for the examples.
하기 표 10에서 알 수 있는 바와 같이, 본 발명의 방염 조성물은 유기물질을 전혀 방출하지 않음으로써, 환경에 무해하고 작업자에게 위생적으로 안전한 물질임을 확인할 수 있었다.As can be seen in Table 10, the flame retardant composition of the present invention did not emit any organic material, it was confirmed that the material is harmless to the environment and hygienically safe to workers.
합계
0.1 %
이하
Sum
0.1%
Below
주 1) 검출안됨 (검출한계 : 0.1 g/L 이하)Note 1) Not detected (detection limit: 0.1 g / L or less)
2) 검출안됨 (검출한계 : 0.01 mg/L 이하) 2) Not detected (detection limit: 0.01 mg / L or less)
3) 검출안됨 (검출한계 : 2.5 mg/kg 이하) 3) Not detected (detection limit: 2.5 mg / kg or less)
4) 검출안됨 (검출한계 : 1.0 mg/kg 이하) 4) Not detected (detection limit: 1.0 mg / kg or less)
5) 설계값 1.1 g/mL의 98 % ~ 105 % 범위.
5) 98% to 105% of design value 1.1 g / mL.
시험예Test Example 2 : 내후성 평가 2: weather resistance evaluation
1) 촉진내후성 시험조건1) Accelerated weathering test conditions
방염제가 도포된 시험편을 7일 이상 건조한 후 촉진내후성 시험기에 설치하여 아래의 조건으로 시험하였다.The flame retardant-coated test piece was dried for at least 7 days and then installed in an accelerated weather resistance tester, and tested under the following conditions.
- 장비명 : 촉진내후성 시험기 UV2000 (ATLAS, USA), 색차계 I-7 (McBath, UK)-Equipment Name: Accelerated Weathering Tester UV2000 (ATLAS, USA), Colorimeter I-7 (McBath, UK)
- 시험사이클 : UV 50 ℃, 4 h → 응축 40 ℃, 4 h-Test cycle: UV 50 ℃, 4 h → condensation 40 ℃, 4 h
- 사이클반복 : 25 회, 총 200 시간-Cycle repeat: 25 times, total 200 hours
- 방사조도 : 0.63 W/m2-Irradiance: 0.63 W / m2
- 램프종류 : UV-A 340 nm-Lamp type: UV-A 340 nm
2) 측정항목 2) Metric
- 겉보기 : 촉진내후성 시험 전후를 비교하여 백화, 박락, 얼룩, 광택현상을 시험자의 육안으로 판단하여 이상 유무를 확인한다.-Appearance: Compare with before and after accelerated weathering test, whitening, peeling, stain and gloss are judged visually by the tester to check for abnormalities.
- 비교색차 : 방염제를 도포한 시험편과 방염제를 도포하지 않은 공시험편을 색차계를 이용하여 시험전ㆍ후 색도를 측정하여 색차 값을 구한다. 방염제를 도포한 시험편의 색차 값과 방염제를 도포하지 않은 공시험편의 색차값의 차이는 각 시험편은 3.0 미만, 단청색상별 평균은 1.5 미만이어야 한다. 내후성의 방염처리제 처리 전후 단청 시험편의 색차 값은 표 12와 같다.-Comparative Color Difference: Measure the chromaticity before and after the test by using colorimeter for test specimen coated with flame retardant and blank test specimen without flame retardant. The difference between the color difference value of the test piece coated with the flame retardant and the blank value of the blank test piece without the flame retardant shall be less than 3.0 for each specimen, and less than 1.5 for the average for each monochromatic color. The color difference values of the mono test specimens before and after the weather resistant flame retardant treatment are shown in Table 12.
시험예Test Example 3 : 3: 방염성Flameproof 평가 evaluation
1) 방염성 평가의 시험조건 1) Test condition of flame retardancy evaluation
- 장비명 : 방염시험기 (FL-45MC, SUGA test instrument)-Equipment Name: Flameproof Tester (FL-45MC, SUGA test instrument)
- 불꽃길이 : 65 mm-Flame length: 65 mm
- 가열시간 : 2 분Heating time: 2 minutes
2) 측정항목 및 기준 2) Metrics and criteria
- 잔염시간 : 버어너의 불꽃을 제거한 때부터 불꽃을 올리며 연소하는 상태가 그칠 때까지의 시간, 10 초 이내-Afterflame time: within 10 seconds from when the burner's flame is removed until the flame burns up
- 잔신시간 : 버어너의 불꽃을 제거한 때부터 불꽃을 올리지 아니하고 연소하는 상태가 그칠 때까지의 시간, 30 초 이내-Residual time: Within 30 seconds from when the burner's flame is removed until the combustion state stops without raising the flame.
- 탄화면적 : 시험 후 시험편(목재)이 탄화된 부분의 면적, 50 cm2-Surface area: Area of carbonized part of test piece (wood) after test, 50 cm2
(측정장치 : PLANIX EX(TAMAYA technics Inc., JAPAN)) (Measurement device: PLANIX EX (TAMAYA technics Inc., JAPAN))
- 탄화길이 : 시험 후 시험편(목재)이 탄화된 부분의 길이, 20 cm-Carbonization length: The length of the carbonized part of the test piece (wood) after the test, 20 cm
상기 시험 결과 방염성 시험 결과는 표 14 내지 17과 같다.The test results The flame resistance test results are shown in Tables 14 to 17.
이상에서는 본 발명의 바람직한 실시예에 대해서 설명하였으나, 본 발명은 상술한 특정의 실시예에 한정되지 아니하며, 당해 기술분야에서 통상의 지식을 가진 자라면 본원 발명의 요지를 벗어남이 없이 다양한 변형 실시가 가능함은 물론이다. 따라서, 본 발명의 범위는 위의 실시예에 국한해서 해석되어서는 안되며, 후술하는 특허청구범위 뿐만 아니라 이 특허청구범위와 균등한 것들에 의해 정해져야 할 것이다.
While the present invention has been described in connection with what is presently considered to be practical exemplary embodiments, it is to be understood that the invention is not limited to the disclosed embodiments, but, on the contrary, Of course it is possible. Accordingly, the scope of the present invention should not be construed as being limited to the above-described embodiments, but should be determined by equivalents to the appended claims, as well as the following claims.
Claims (10)
인산염, 황산염, 할로겐산염, 설파민산염, 붕소염, 포스폰산염 및 그 혼합물로 이루어진 군에서 선택된 방염 보조제 1 내지 600 중량부,
치환되지 않은 또는 아민으로 치환된 탄소수 1 내지 5의 알콜 10 내지 500 중량부, 및
물 50 내지 10000 중량부
를 포함하는 방염 조성물.100 parts by weight of a silica sol unsubstituted or substituted with a propyl group and an ethoxy group,
1 to 600 parts by weight of a flame retardant aid selected from the group consisting of phosphates, sulfates, halides, sulfamates, boron salts, phosphonates and mixtures thereof,
10 to 500 parts by weight of an unsubstituted or substituted amine with 1 to 5 carbon atoms, and
50 to 10000 parts by weight of water
Flame retardant composition comprising a.
상기 실리카 졸의 실리카 농도는 5 내지 50 중량%인 것을 특징으로 하는 방염 조성물.The method according to claim 1,
Flame retardant composition, characterized in that the silica concentration of the silica sol is 5 to 50% by weight.
상기 인산염은 제일인산암모늄, 제이인산암모늄, 제삼인산암모늄, 제일인산나트륨, 제이인산나트륨, 제삼인산나트륨, 제일인산칼륨, 제이인산칼륨, 제삼인산칼륨, 제일인산구아니딘, 제이인산구아니딘, 축합도가 1 내지 250의 저축합 암모늄폴리포스페이트, 구아닐유레아포스페이트, 인산의 아민염 및 그 혼합물로 이루어진 군에서 선택된 것을 특징으로 하는 방염 조성물.The method according to claim 1,
The phosphate is ammonium monophosphate, diammonium phosphate, ammonium triphosphate, sodium monophosphate, sodium diphosphate, sodium triphosphate, potassium monophosphate, potassium diphosphate, potassium triphosphate, guanidine phosphate, guanidine diphosphate, condensation degree Flame-retardant composition, characterized in that selected from the group consisting of 1 to 250 low-condensation ammonium polyphosphate, guanylurea phosphate, amine salt of phosphoric acid and mixtures thereof.
상기 황산염은 황산암모늄, 황산나트륨, 황산칼륨, 황산의 아민염 및 그 혼합물로 이루어진 군에서 선택된 것을 특징으로 하는 방염 조성물.The method according to claim 1,
The sulphate is flame retardant composition, characterized in that selected from the group consisting of ammonium sulfate, sodium sulfate, potassium sulfate, amine salt of sulfuric acid and mixtures thereof.
상기 할로겐산염은 염화암모늄, 염화나트륨, 염화칼륨, 브롬화암모늄, 브롬화나트륨, 브롬화칼륨, 할로겐산의 아민염 및 그 혼합물로 이루어진 군에서 선택된 것을 특징으로 하는 방염 조성물.The method according to claim 1,
The halide salt is flame retardant composition, characterized in that selected from the group consisting of ammonium chloride, sodium chloride, potassium chloride, ammonium bromide, sodium bromide, potassium bromide, amine salts of halogen acids and mixtures thereof.
상기 설파민산염은 구아니딘설파메이트, 암모늄설파메이트, 설파민산나트륨, 설파민산칼륨, 설파민산의 아민염 및 그 혼합물로 이루어진 군에서 선택된 것을 특징으로 하는 방염 조성물.The method according to claim 1,
The sulfamate is a flame retardant composition, characterized in that selected from the group consisting of guanidine sulfamate, ammonium sulfamate, sodium sulfamate, potassium sulfamate, amine salt of sulfamic acid and mixtures thereof.
상기 붕소염은 붕산, 붕사, 산화 붕소, 포타슘펜타보레이트(KB5O7), 포타슘테트라보레이트(K2B4O7), 소듐메타보레이트(NaBO2), 암모늄펜타보레이트[(NH4)2B10O16·8H2O], 붕산의 아민염 및 그 혼합물로 이루어진 군에서 선택된 것을 특징으로 하는 방염 조성물.The method according to claim 1,
The boron salt is boric acid, borax, boron oxide, potassium pentaborate (KB 5 O 7 ), potassium tetraborate (K 2 B 4 O 7 ), sodium metaborate (NaBO 2 ), ammonium pentaborate [(NH 4 ) 2 B 10 O 16 .8H 2 O], an amine salt of boric acid and a mixture thereof.
상기 포스폰산염은 아미노트리메틸렌포스폰산, 1-하이드록시에틸렌-1,1-다이포스포폰산, 에틸렌다이아민테트라메틸렌포스폰산, 헥사메틸렌다이아민테트라메틸렌포스폰산, 다이에틸렌트리아민펜타메틸렌포스폰산, 포스폰산의 아민염 및 그 혼합물로 이루어진 군에서 선택된 것을 특징으로 하는 방염 조성물.The method according to claim 1,
The phosphonic acid salts include aminotrimethylenephosphonic acid, 1-hydroxyethylene-1,1-diphosphoic acid, ethylenediaminetetramethylenephosphonic acid, hexamethylenediaminetetramethylenephosphonic acid, and diethylenetriaminepentamethylene phosphate. Flame retardant composition, characterized in that selected from the group consisting of phosphates, amine salts of phosphonic acid and mixtures thereof.
상기 물은 나노버블수인 것을 특징으로 하는 방염 조성물.The method according to claim 1,
The water-proof composition, characterized in that the nanobubble water.
상기 나노버블수의 기포 평균입경은 1 내지 500 nm인 것을 특징으로 하는 방염 조성물.
The method according to claim 9,
Flame-proof composition, characterized in that the average bubble diameter of the nanobubble number is 1 to 500 nm.