KR20140075500A - Metal nanoparticles with enhanced anti-oxidation and method of preparation of the same - Google Patents
Metal nanoparticles with enhanced anti-oxidation and method of preparation of the same Download PDFInfo
- Publication number
- KR20140075500A KR20140075500A KR1020120143916A KR20120143916A KR20140075500A KR 20140075500 A KR20140075500 A KR 20140075500A KR 1020120143916 A KR1020120143916 A KR 1020120143916A KR 20120143916 A KR20120143916 A KR 20120143916A KR 20140075500 A KR20140075500 A KR 20140075500A
- Authority
- KR
- South Korea
- Prior art keywords
- metal
- metal nanoparticles
- reaction
- precursor
- ligand
- Prior art date
Abstract
Description
본 발명은 산화 안정성을 개선시키기 위하여 표면 처리된 금속 나노입자 및 그 제조방법에 관한 것이다.The present invention relates to metal nanoparticles surface-treated to improve oxidation stability and a method for producing the same.
투명 전도성 전극(TCEs; Transparent Conductive Electrodes)의 중요성은 터치 패널, 평판 디스플레이, 다른 광전자 소자등의 응용을 위해 그 중요성이 날로 커져가고 있다. ITO 는 유기 태양전지 등의 분야에서 현재 투명 전극으로 가장 폭넓게 사용되는 재료이지만 소성 재료라 깨지기 쉬우며 휨 변형 등에 취약하여 폴리머 기판 위에 코팅했을때 기판을 구부리면 막이 부서지는 단점이 있다. 그리고, 무엇보다 In의 희소성으로 인하여 가격이 점점 증가하고 있으며, 그 공급에 있어 문제점이 대두되고 있는 현실이다. The importance of Transparent Conductive Electrodes (TCEs) is becoming increasingly important for applications such as touch panels, flat panel displays, and other optoelectronic devices. ITO is the most widely used transparent electrode in the field of organic solar cell but it is fragile because it is fragile and is vulnerable to bending deformation. Therefore, when the substrate is coated on a polymer substrate, the film is broken. And, moreover, the price is increasing due to the scarcity of In, and there is a problem in supply.
최근 이러한 ITO의 문제점들을 해결하기 위한 방안으로 플렉서블 투명 전극이면서 ITO를 대체 할 수 있는 재료로 거론되고 있는 것들에, 전도성 폴리머 또는 나노 기술의 발달로 뛰어난 광전기적 특성을 갖게 된 탄소 나노 튜브, 그래핀, 금속 나노와이어 또는 금속 나노입자 등의 금속 나노구조가 있다. Recently, transparent transparent electrodes and ITO substitutes have been proposed as solutions for the problems of ITO. Among them, carbon nanotubes having excellent photoelectric characteristics due to the development of conductive polymers or nanotechnology, , Metal nanowires or metal nanoparticles.
금속 나노입자는 전도성 잉크의 형태로 제조되어 잉크젯 등의 공정에 의해 전극 제조에 이용된다. 이러한 금속 나노입자는 금, 은, 백금, 구리, 니켈, 철, 코발트, 아연, 크롬, 망간 등의 입자를 포함할 수 있다. 이중에서 구리, 니켈, 철, 코발트, 아연, 크롬, 망간 입자는 귀금속 나노 입자에 비하여 제조 비용이 저렴하지만, 산화 안정성이 낮다는 문제점이 있다. The metal nanoparticles are produced in the form of a conductive ink and are used for electrode production by a process such as an ink jet process. Such metal nanoparticles may include particles of gold, silver, platinum, copper, nickel, iron, cobalt, zinc, chromium, manganese and the like. Among these, copper, nickel, iron, cobalt, zinc, chromium, and manganese particles are inexpensive to manufacture compared to noble metal nanoparticles, but have a low oxidation stability.
특히 구리(Cu)는 저렴한 가격과 함께 우수한 전도성을 지니고 있다. 그러나 나노입자 상태에서는 표면이 쉽게 산화됨에 따라 전도성이 크게 저하되기 때문에 전도성 잉크로서의 사용이 어렵다. 또한 표면 산화를 방지하기 위해서 사용되는 산화방지제에 의해서도 전도성이 떨어질 수 있는 문제가 있다. 또한 현재 전도성 잉크의 나노입자로서 주로 사용되는 은(Ag)은 매우 고가이고 최근 가격이 급등함에 따라 비교적 저가이면서 높은 전기 전도성 확보가 가능한 대체 물질이 절실히 요구되고 있다. Especially copper (Cu) has good conductivity with low price. However, in the nanoparticle state, it is difficult to use it as a conductive ink because the surface is easily oxidized and the conductivity is greatly lowered. There is also a problem in that the conductivity may be lowered by an antioxidant used for preventing surface oxidation. In addition, silver (Ag), which is currently used as a nanoparticle of conductive ink, is very expensive, and as the price has recently surged, a substitute material that is relatively inexpensive and capable of ensuring high electric conductivity is desperately required.
한편 금속 나노입자의 제조에 있어서는 입자의 뭉침(aggregation)이 발생하지 않으며 균일한 크기로 입경을 제어하는 것이 관건이다. 따라서 비교적 저가의 금속 재료를 이용하면서도 이것의 입경을 제어하고 산화 안정성 및 전기적 물성이 개선된 금속 나노입자를 제공하고자 하는 노력이 계속되고 있다. On the other hand, in the production of metal nanoparticles, aggregation of particles does not occur, and it is important to control the particle size to a uniform size. Therefore, efforts have been made to provide metal nanoparticles having a reduced oxidation resistance and an improved electrical property while controlling the particle diameter thereof while using relatively inexpensive metal materials.
본 발명은 산화 안정성이 개선된 우수한 전기 전도도를 갖는 금속 나노입자를 제공하는 것을 목적으로 한다. 또한 본 발명은 비교적 저렴한 금속을 이용하며 낮은 소결 온도에서 분해되는 리간드와 결합된 형태를 제공하여, 공정상 유리한 금속 나노입자를 제공하고자 한다. 나아가 본 발명은 조절된 입경을 갖는 금속 나노입자를 제공하고자 한다. It is an object of the present invention to provide metal nanoparticles having improved oxidation stability and excellent electrical conductivity. The present invention also provides metal nano-particles that are advantageous in terms of process by using a relatively inexpensive metal and providing a form coupled with a ligand which is decomposed at a low sintering temperature. The present invention further provides metal nanoparticles having a controlled particle size.
또한 본 발명은 금속 나노입자의 제조 방법으로서 입경의 조절이 용이하고 산화 안정성이 개선되며 저온 열분해성을 갖는 금속 나노입자를 제조하는 방법을 제공하고자 한다.The present invention also provides a method for preparing metal nanoparticles having a low temperature thermal decomposition property, which can easily control the particle size, improve oxidation stability, and produce metal nanoparticles.
본 발명은 코어 금속이 극성의 리간드와 결합되고 또한 포름산에 의해 표면이 개질된 것을 특징으로 하는 금속 나노입자를 제공한다. The present invention provides metal nanoparticles characterized in that the core metal is bonded to a polar ligand and the surface is modified by formic acid.
바람직하게, 상기 코어 금속은 구리, 니켈, 철, 코발트, 아연, 크롬 또는 망간 입자이다.Preferably, the core metal is copper, nickel, iron, cobalt, zinc, chromium or manganese particles.
바람직하게, 상기 코어 금속은 하기 식으로 표현되는 금속의 전구체로부터 제조된 것이다:Preferably, the core metal is made from a precursor of a metal represented by the formula:
[식 1][Formula 1]
상기 식에서 M은 Cu, Ni, Fe, Co, Zn, Cr 또는 Mn이고, m=1~5이고, M is Cu, Ni, Fe, Co, Zn, Cr, or Mn, m is 1 to 5,
R은 
(여기서, X는 수소, 탄소수 1 내지 6의 알킬기, 또는 할로겐이며, n은 0 내지 23의 정수이다.)(Wherein X is hydrogen, an alkyl group having 1 to 6 carbon atoms, or a halogen, and n is an integer of 0 to 23.)
바람직하게, 상기 극성의 리간드는 피리딘(pyridine)이다. Preferably, the polar ligand is pyridine.
바람직하게, 상기 금속 나노입자는 표면에 형성된 금속 포메이트를 포함한다. Preferably, the metal nanoparticles comprise a metal formate formed on the surface.
바람직하게, 상기 금속 나노입자의 소결 온도는 150 내지 250 ℃이다.Preferably, the sintering temperature of the metal nanoparticles is 150 to 250 ° C.
또한 본 발명은 하기 식으로 표현되는 금속의 전구체를 캡핑화제(capping agent)에 용해시켜 반응액을 제조한 후, 이를 250 내지 350 ℃의 반응 온도에서 1 내지 4 시간 동안 반응시킴으로써 금속 나노입자를 제조하는 단계;The present invention also relates to a method for preparing metal nanoparticles by dissolving a precursor of a metal represented by the following formula in a capping agent to prepare a reaction solution and then reacting it at a reaction temperature of 250 to 350 ° C for 1 to 4 hours ;
상기 제조된 금속 나노입자를 극성의 리간드로 리간드 교환 반응시키는 단계; 및 Ligand exchange reaction of the prepared metal nanoparticles with a polar ligand; And
상기 리간드 교환된 금속 나노입자를 포름산과 반응시키는 단계를 포함하는 것을 특징으로 하는 금속 나노입자의 제조방법을 제공한다: And reacting the ligand-exchanged metal nanoparticles with formic acid to produce metal nano-particles.
[식 1][Formula 1]
상기 식에서 M은 Cu, Ni, Fe, Co, Zn, Cr 또는 Mn이고, m=1~5이고, M is Cu, Ni, Fe, Co, Zn, Cr, or Mn, m is 1 to 5,
R은 
(여기서, X는 수소, 탄소수 1 내지 6의 알킬기, 또는 할로겐이며, n은 0 내지 23의 정수이다.)(Wherein X is hydrogen, an alkyl group having 1 to 6 carbon atoms, or a halogen, and n is an integer of 0 to 23.)
바람직하게, 상기 캡핑화제(capping agent)는 탄소수 4 내지 18의 알킬기를 갖는 아민이다.Preferably, the capping agent is an amine having an alkyl group of 4 to 18 carbon atoms.
바람직하게, 상기 반응액 내 전구체의 농도는 30 내지 60 mmol이다. Preferably, the concentration of the precursor in the reaction solution is 30 to 60 mmol.
바람직하게, 상기 전구체는 구리 헥사노에이트(Copper(II) bis(2-ethylhexanoate))이다. Preferably, the precursor is copper (II) bis (2-ethylhexanoate).
바람직하게, 상기 금속 나노입자를 제조하는 단계에서의 반응은 비활성 분위기 또는 환원 분위기에서 수행된다. Preferably, the reaction in the step of preparing the metal nanoparticles is carried out in an inert atmosphere or a reducing atmosphere.
바람직하게, 상기 리간드 교환 반응은 비초음파 분무 하에서 및 비활성 분위기 또는 환원 분위기에서 진행된다. Preferably, the ligand exchange reaction is carried out under non-ultrasonic atomization and in an inert or reducing atmosphere.
본 발명에 의하면 입경이 조절된 금속 나노입자를 제조하고 이것의 표면 개질을 통해 산화 안정성을 개선함으로써, 우수한 전기적 물성을 구현할 수 있다. 또한 본 발명의 금속 나노입자는 가격적으로 비교적 저렴한 금속을 사용하며, 전극의 제조 등 그 적용에 있어 낮은 소결 온도에 의하는 것이 가능하므로 공정상 유리한 장점이 있다. 따라서 본 발명은 산화 방지를 위한 금속/금속 포메이트의 코어-쉘 구조의 나노입자 잉크 소재 개발에 이용될 수 있다. According to the present invention, excellent electrical properties can be realized by preparing metal nanoparticles having controlled particle diameters and improving the oxidation stability through surface modification thereof. The metal nanoparticles of the present invention use a relatively inexpensive metal at a cost and can be subjected to a low sintering temperature in the application of the electrode and the like, and thus, they are advantageous in terms of the process. Therefore, the present invention can be used to develop nanoparticle ink materials of core / shell structure of metal / metal formate for prevention of oxidation.
도 1은 본 발명의 금속 나노 입자의 제조 과정을 도시한 것이다.
도 2는 본 발명의 실시예에서 코어의 금속 입자 제조에 사용되는 반응기를 도시한 것이다.
도 3a는 실시예에서 제조된 입자들의 리간드 교환 반응 전후를 비교한 SEM 사진이다.
도 3b는 비교예에서 제조된 입자들의 리간드 교환 반응 전후를 비교한 SEM 사진이다.
도 4a는 실시예에서 최종적으로 수득되는 금속 나노입자의 XRD 사진이다.
도 4b는 실시예의 제조 과정 중 얻어진 코어 금속 입자의 XRD 사진이다. FIG. 1 illustrates a process for preparing metal nanoparticles of the present invention.
Figure 2 shows a reactor used in the manufacture of metal particles of a core in an embodiment of the present invention.
FIG. 3A is a SEM photograph of the particles prepared in the examples before and after the ligand exchange reaction. FIG.
FIG. 3B is a SEM photograph showing the comparison of the particles prepared in the comparative example before and after the ligand exchange reaction.
4A is an XRD photograph of metal nanoparticles finally obtained in the examples.
4B is an XRD photograph of the core metal particles obtained during the manufacturing process of the embodiment.
본 발명은 코어 금속 입자가 극성의 리간드와 결합되고 또한 포름산에 의해 표면이 개질된 것을 특징으로 하는 금속 나노입자를 제공한다. 일 실시예로 상기 금속 나노입자는 금속/금속 포메이트의 코어-쉘 구조를 갖는다. The present invention provides a metal nanoparticle characterized in that the core metal particle is bonded to a polar ligand and the surface is modified with formic acid. In one embodiment, the metal nanoparticles have a core-shell structure of metal / metal formate.
상기 코어 입자를 이루는 금속으로는 특히 산화 안정성이 낮은 구리, 니켈, 철, 코발트, 아연, 크롬, 망간 입자를 사용할 수 있다. 이들을 나노 입자로 형성하는 과정에서 먼저 극성의 리간드와 결합시킨 후, 후속적으로 포름산(formic acid)과 반응시킴으로써 표면에 금속의 포메이트(formate)가 형성된 형태로 제조한다. 즉, 산화되기 쉬운 금속 입자의 표면을 극성의 리간드 및 그것의 포메이트 형태로 둘러싸는 것에 의해 입자의 산화 안정성을 개선시키는 것이다. As the metal forming the core particles, copper, nickel, iron, cobalt, zinc, chromium, and manganese particles having low oxidation stability may be used. In the process of forming them into nanoparticles, they are first bound to a polar ligand and subsequently reacted with formic acid to form a metal formate on the surface. That is, the surface of metal particles that can be easily oxidized is surrounded by a polar ligand and a formate thereof to improve the oxidation stability of the particles.
상기 극성의 리간드는 중심(코어)의 금속 입자와 포름산과의 반응이 잘 일어나도록 유도하는 작용을 한다. 또한 비교적 작은 분자량의 것을 이용하여 저온 열분해가 가능하게 한다. 일 실시예로 본 발명에서 극성의 리간드로 사용하는 것은 도 1에 도시된 바와 같은 피리딘이다. 피리딘은 B.P가 115.2 ℃이다. 그러므로 피리딘을 사용할 경우 올레일아민 등의 리간드 (B.P 364 ℃)를 사용하는 경우에 비해 현저히 낮은 온도에서 열분해가 가능한 것이다. 이에 따라 본 발명의 금속 나노입자는 제품 적용시 150 내지 250 ℃ 온도에서의 소결에 의할 수 있다. The polar ligand acts to induce the reaction between the metal particles of the core and the formic acid. In addition, low-temperature pyrolysis is possible using a relatively small molecular weight. In one embodiment, the use of a polar ligand in the present invention is pyridine as shown in FIG. The pyridine has a B.P of 115.2 캜. Therefore, when pyridine is used, pyrolysis can be performed at a significantly lower temperature than when a ligand such as oleylamine (B.P. 364 ° C) is used. Accordingly, the metal nanoparticles of the present invention can be sintered at a temperature of 150 to 250 ° C when the product is applied.
본 발명에서는 상기 극성 리간드의 일 예로서 피리딘을 사용한다. 그러나 이에 한정되는 것이 아니며 극성의 리간드로서 금속 입자와 포름산의 반응이 용이하게 일어나게 하고 저온에서의 열분해가 가능한 것이라면 제한없이 사용될 수 있다. In the present invention, pyridine is used as an example of the polar ligand. However, the present invention is not limited thereto, and it can be used without limitation as long as it can easily react the metal particles with formic acid as a polar ligand and pyrolysis at low temperature.
본 발명에서 코어의 금속 입자를 제조하기 위해서 하기 식으로 표현되는 구조를 갖는 금속의 전구체를 사용한다:In order to prepare the metal particles of the core in the present invention, a precursor of the metal having the structure represented by the following formula is used:
[식 1][Formula 1]
상기 식에서 M은 Cu, Ni, Fe, Co, Zn, Cr 또는 Mn이고, m=1~5이고, M is Cu, Ni, Fe, Co, Zn, Cr, or Mn, m is 1 to 5,
R은 
(여기서, X는 수소, 탄소수 1 내지 6의 알킬기, 또는 할로겐이며, n은 0 내지 23의 정수이다.)(Wherein X is hydrogen, an alkyl group having 1 to 6 carbon atoms, or a halogen, and n is an integer of 0 to 23.)
상기 전구체는 사용 용매에 대해 고 용해성이라는 특징을 갖는 물질이다. 따라서 합성을 위한 반응액의 제조가 용이하다. 본 발명에서는 상기 전구체를 용매이자 캡핑화제에 용해시켜 반응액을 제조한다. 즉 별도의 용매를 사용하지 않고 상기 전구체를 캡핑화제에 바로 용해시키는 것으로 반응액의 제조를 완성한다. 상기 캡핑화제는 전구체를 환원시켜 금속의 나노입자 형태로 만들며 형성된 나노입자 주위를 감싸 입자를 안정화시키는 역할을 한다. 또한 캡핑화제는 제조된 금속 나노입자의 산화를 막는 역할을 한다. 이를 위해 캡핑화제는 적당한 체인 길이를 갖는 것이 바람직하다. 따라서 금속의 전구체에 대해 적당한 캡핑화제를 찾는 것이 관건이다. 본 발명에서는 캡핑화제로 아민을 사용한다. 상기 아민은 탄소수 4 내지 18의 알킬기를 포함하는 것이 바람직하다. 본 발명에서는 바람직하게 캡핑화제로 부틸 아민(butylamine), 옥틸 아민(octylamine), 도데실 아민(dodecylamine), 올레일 아민(Oleylamine) 등을 사용할 수 있다. 더욱 바람직하게는 캡핑화제로 올레일 아민(Oleylamine)을 사용한다. 올레일 아민은 지방산(fatty acid)인 올레산(oleic acid)의 아민이며, 상대적으로 분자량이 크기 때문에 금속 나노입자와 결합하여 입자 표면에 층을 형성할 수 있다. 그 결과, 외부의 산소가 금속 나노 입자의 코어로 확산되는 것을 방지함으로써 금속 나노 입자의 산화 안정성을 증가시킬 수 있다. 또한, 상기 금속 나노 입자와 결합한 올레인 아민은 유기 용매 내에서 나노 입자의 분산을 용이하게 할 수 있다. The precursor is a substance having a characteristic that it is highly soluble in the solvent used. Therefore, it is easy to prepare a reaction solution for synthesis. In the present invention, the precursor is dissolved in a solvent and a capping agent to prepare a reaction solution. That is, the precursor is directly dissolved in the capping agent without using a separate solvent to complete the preparation of the reaction solution. The capping agent reduces the precursor to form a nanoparticle of metal and surrounds the formed nanoparticles to stabilize the particles. The capping agent also serves to prevent the oxidation of the prepared metal nanoparticles. For this purpose, the capping agent preferably has an appropriate chain length. It is therefore important to find a suitable capping agent for the metal precursor. In the present invention, an amine is used as a capping agent. The amine preferably contains an alkyl group having 4 to 18 carbon atoms. In the present invention, as a capping agent, butylamine, octylamine, dodecylamine, oleylamine and the like may be preferably used. More preferably, oleylamine is used as a capping agent. The oleylamine is an oleic acid amine which is a fatty acid. Due to its relatively high molecular weight, it can bind to metal nanoparticles and form a layer on the surface of the particles. As a result, oxidation stability of the metal nanoparticles can be increased by preventing external oxygen from diffusing into the core of the metal nanoparticles. In addition, the olefin amine combined with the metal nanoparticles can easily disperse the nanoparticles in the organic solvent.
본 발명에서 사용하는 금속의 전구체는 캡핑화제에 대해 고 용해성을 가지므로 별도의 용매 없이 캡핑화제에 녹여 반응액을 제조하는 것은 물론 반응액 중의 전구체의 농도를 조절하여 목적으로 하는 적합한 입도의 나노입자를 제조할 수 있다. 전구체는 바람직하게 30 내지 60 mmol의 농도로 캡핑화제에 녹여 사용한다. 전구체를 30 mmol 농도 미만으로 사용할 경우 입자가 굵고 성기며 균일성도 우수하지 못하다. 반면 60 mmol을 초과하여 사용할 경우 고농도의 전구체가 한꺼번에 반응에 참가하여 입자의 응집이 일어날 가능성이 있다. 따라서 전구체의 농도가 적절한 경우 입자의 크기를 제어할 수 있을 뿐만 아니라 균일한 입도의 나노 입자를 제조할 수 있다. Since the precursor of the metal used in the present invention has high solubility in the capping agent, it is dissolved in a capping agent without any additional solvent to prepare a reaction solution, and the concentration of the precursor in the reaction solution is adjusted, Can be produced. The precursor is preferably dissolved in a capping agent at a concentration of 30 to 60 mmol. When the precursor is used at a concentration of less than 30 mmol, the particles are coarse, brittle and not uniform. On the other hand, when it is used in excess of 60 mmol, there is a possibility that the high concentration of precursor participates in the reaction at one time and the aggregation of the particles occurs. Therefore, when the concentration of the precursor is appropriate, not only the particle size can be controlled but also nanoparticles having uniform particle size can be produced.
상기 전구체는 나노입자의 획득에 있어 유리하다. 암모늄 리간드 염 등 기존의 전구체들을 사용할 때 입자의 응집(aggregation)이 발생하여 나노입자의 형태를 얻기가 곤란한 조건의 합성 방법에 있어서도 본 발명의 상기 전구체를 사용하면 응집이 일어나지 않고 입자의 형태가 유지되고 최종 생성물로서 나노입자가 수득되는 것이 확인된다.The precursor is advantageous in the acquisition of nanoparticles. Ammonium ligand salt and the like, it is difficult to obtain the nanoparticle form due to the aggregation of the particles. When the precursor of the present invention is used, aggregation does not occur and the morphology of the particles is maintained And it is confirmed that nanoparticles are obtained as a final product.
상기 전구체는 캡핑화제에 용해시켜 제조된 반응액을 일정 온도로 승온시킨 후 일정 시간 동안 반응시키는 방법으로 나노입자의 형태로 제조할 수 있다. 또한 반응 온도 또는 시간을 조절함으로써 제조되는 나노입자의 입도 및 입도의 분포를 용이하게 조절할 수 있다. 바람직하게 반응액을 250 내지 350 ℃로 까지 승온시킨 후 그 온도에서 1 내지 4 시간 동안 반응을 진행시킨다. 250 ℃ 미만의 온도에서 반응을 진행할 경우 제조되는 입자의 입도 분포가 균일하지 못하고, 반면 350 ℃를 초과하는 고온에서 반응시킬 경우 입자의 뭉침 현상(aggregation)이 발생된다. 또한 1 시간 미만의 반응 시간에 의할 경우 바람직한 사이즈 및 양의 입자 생성이 일어나지 않고, 반대로 4 시간을 초과하는 장시간의 반응에 의하면 입자의 뭉침 현상이 일어난다. 또한 반응 시간이 길어질수록 전체적인 입자의 크기가 증가하는 경향이 있다. The precursor may be prepared in the form of nanoparticles by heating the reaction solution prepared by dissolving the precursor in a capping agent to a predetermined temperature and reacting the precursor for a predetermined time. Further, the particle size and particle size distribution of the nanoparticles produced by controlling the reaction temperature or time can be easily controlled. Preferably, the temperature of the reaction solution is raised to 250 to 350 ° C, and the reaction is allowed to proceed at that temperature for 1 to 4 hours. When the reaction is carried out at a temperature lower than 250 ° C, the particle size distribution of particles produced is not uniform, whereas when the reaction is carried out at a temperature higher than 350 ° C, agglomeration of particles occurs. In addition, when the reaction time is shorter than 1 hour, particles of a desired size and amount do not occur. Conversely, when the reaction takes longer than 4 hours, aggregation of the particles occurs. The longer the reaction time, the greater the overall particle size.
한편 상기 반응 동안 반응기는 진공 분위기, 환원 분위기 또는 비활성 기체 분위기로 유지시키는 것이 바람직하다. 대기 분위기에서 합성을 진행할 경우 금속 나노입자가 산화된다. 따라서 반응 중 대기로부터 금속의 산화를 제어하고 나아가 금속의 환원을 돕기 위해 바람직하게 질소(N2) 퍼징을 유지한 상태에서 합성을 진행한다. 산화가 제어된 나노 입자는 전기적 물성이 향상되는 것이 확인된다.Meanwhile, during the reaction, the reactor is preferably maintained in a vacuum atmosphere, a reducing atmosphere or an inert gas atmosphere. When synthesized in the atmosphere, metal nanoparticles are oxidized. Therefore, synthesis is preferably carried out while nitrogen (N 2 ) purging is maintained in order to control the oxidation of the metal from the atmosphere during the reaction and further assist the reduction of the metal. It is confirmed that the nanoparticles having controlled oxidation have improved electrical properties.
상기와 같은 방법으로 입경이 제어된 입자는 일 실시예로서 도 2에 도시된 바와 같이 코어 금속이 캡핑화제로부터 유도되는 비극성의 리간드와 결합하여 둘러싸인 구조를 갖는다. The particles whose particle diameters are controlled in the above manner have a structure in which the core metal is surrounded and bound to a non-polar ligand derived from the capping agent as shown in Fig. 2 as an example.
다음으로 본 발명의 금속 나노입자를 제조하기 위하여 상기 입자를 극성의 리간드와 반응시키기 위해 도 1에 도시된 바와 같은 리간드 교환 반응(Ligand exchange reaction)을 진행한다. Next, in order to produce the metal nanoparticles of the present invention, a ligand exchange reaction as shown in FIG. 1 is performed in order to react the particles with a polar ligand.
상기 리간드 교환 반응은 바람직하게 비활성 분위기 또는 환원 분위기에서 진행된다. 이것은 반응 중에 일어날 수 있는 코어 금속의 산화를 방지하기 위함이다. 또한 반응 중에는 입자의 뭉침을 방지하기 위해 통상적으로 행해지는 초음파 분산(sonication)을 수행하지 않는 것이, 입자의 분쇄를 방지하고 금속 전구체와 캡핑화제의 반응으로부터 이미 이루어져 있는 입자의 결정성을 유지시킬 수 있어 바람직하다. The ligand exchange reaction preferably proceeds in an inert or reducing atmosphere. This is to prevent oxidation of the core metal which may occur during the reaction. Also, during the reaction, it is desirable to avoid sonication, which is conventionally done to prevent particle agglomeration, to prevent fragmentation of the particles and to maintain the crystallinity of the particles already formed from the reaction of the metal precursor and the capping agent .
리간드 교환 반응에 의해 최초로 얻어진 코어 금속의 표면을 둘러싸고 있던 비
표면 개질 반응에 사용되는 포름산은 일 실시예로서 하기 식으로 표현되는 반응 메카니즘에 따라 표면의 산화된 형태의 금속과 반응하여 금속 포메이트를 형성한다. The formic acid used in the surface modification reaction reacts with the oxidized form of the surface on the surface according to the reaction mechanism represented by the following formula to form a metal formate.
[식 2][Formula 2]
이렇게 형성된 포메이트는 내부의 금속이 산화되는 것을 방지한다. 즉 포름산에 의한 표면 개질 반응은 금속 표면에 이미 산화된 형태를 제거하는 것과 동시에 더 이상의 산화가 일어나지 못하도록 금속 입자 표면에 차단층을 형성함으로써 금속 나노입자의 산화 안정성을 개선시키는 것이다. The formate thus formed prevents the internal metal from being oxidized. That is, the surface modification reaction by formic acid improves the oxidation stability of the metal nanoparticles by removing the already oxidized form on the metal surface and forming a barrier layer on the surface of the metal particle so that further oxidation can not occur.
상기 공정을 통해 얻어진 금속 나노 입자는 캡핑화제에 의해 일차적으로 산화가 방지된 것을 리간드 교환 반응을 통해 저온 열분해성의 리간드로 교체하고 다음으로 이것을 포름산으로 표면 개질시키는 반응을 통해 표면에 금속의 포메이트가 형성되는 구조로 제조됨으로써 저온 열분해성 및 산화 안정성이라는 특성을 갖게 된다.
The metal nanoparticles obtained by the above process are replaced with a low-temperature pyrolyzable ligand through a ligand exchange reaction, which is firstly prevented from oxidation by a capping agent, and then the surface of the metal nanoparticle is reformed with formic acid to form a metal formate So that it has characteristics of low temperature thermal decomposition ability and oxidation stability.
이하 실시예를 통하여 본 발명을 구체적으로 설명한다. 그러나 이는 발명의 이해를 돕기 위한 것일 뿐 본 발명이 이에 한정되는 것으로 여겨져서는 안된다.
Hereinafter, the present invention will be described in detail with reference to examples. It should be understood, however, that the present invention is not intended to be limited thereto, as it is intended to assist the understanding of the invention.
실시예Example
(1) 코어 금속 입자의 제조(1) Production of core metal particles
도 2에 도시된 바와 같은 3-neck 둥근 플라스크의 반응기에 구리 헥사노에이트(Copper(II) 2-ethylhexanoate) 14.2 g을 계량하여 넣고, 플라스틱 시린지를 이용하여 올레일 아민(Oleylamine) 50 ml를 투입했다. 이 반응기에 스터링 바를 넣고 반응기와 3 neck 커버에 그리스를 발라 클램프로 연결하고 중간의 neck에 컨덴서를 연결하였다. 컨덴서 상부는 진공 라인(vacuum line)과 연결되어 있으며 연결 부위마다 그리스를 발라 leak를 방지하였다. 14.2 g of copper hexanoate (Copper (II) 2-ethylhexanoate) was weighed into a reactor of a 3-neck round flask as shown in FIG. 2, and 50 ml of oleylamine was introduced using a plastic syringe did. A stir bar was placed in the reactor and the reactor and 3 neck cover were greased with a clamp and a condenser was connected to the middle neck. The upper part of the condenser was connected to a vacuum line and grease was applied to each part to prevent leakage.
반응기를 핫 플레이트에 장착하고 150 ℃에서 500 rpm 으로 교반하여 반응물을 용해시켰다. 이때 반응액은 진한 청색이었다. The reactor was mounted on a hot plate and stirred at 500 rpm at 150 DEG C to dissolve the reactants. At this time, the reaction solution was dark blue.
다음으로 반응액으로부터 수분을 제거하기 위하여 상기 온도에서(핫 플레이트 상(150 ℃)에서) 30 분 동안 반응기 내부로 진공 및 질소 가스를 반복적으로 가했다. Next, vacuum and nitrogen gas were repeatedly added to the inside of the reactor at this temperature (on a hotplate (150 ° C)) for 30 minutes to remove moisture from the reaction liquid.
반응 전에 예열시켜 놓았던 히팅 맨틀(heating mantle)로 반응기를 옮겨 승온을 시작하였다. 이때 반응기를 옮기는 과정에서 호일 등으로 반응기를 감싸주어 열방출을 최대한 막아주었다. 질소 분위기 하에서 천천히 저어주면서(500 rpm) 20 분에 걸쳐 250 ℃까지 승온 시켰다. 그런 다음 반응액의 내부 온도 250 ℃에서 1 시간 동안 반응을 진행시켰다. 반응은 250 ℃에 도달 시점으로부터 1 시간 동안 진행되도록 하였다. The reactor was transferred to a heating mantle which had been preheated before the reaction to start the heating. At this time, the reactor was wrapped with a foil or the like in the process of transferring the reactor to prevent the heat emission to the maximum. The temperature was raised to 250 ° C over 20 minutes while slowly stirring (500 rpm) in a nitrogen atmosphere. Then, the reaction was allowed to proceed at an internal temperature of 250 캜 for 1 hour. The reaction was allowed to proceed for 1 hour from the point of arrival at 250 ° C.
반응이 진행됨에 따라 가스가 발생하는데 이때 발생하는 가스는 시린지를 사용하여 제거했다. 1 시간 후 반응을 종료하고 자연 냉각시켰다. 반응의 종료에 따라 반응액은 진한 갈색으로 변하였다. As the reaction proceeds, gas is generated. The gas generated at this time is removed by using a syringe. After 1 hour, the reaction was terminated and allowed to cool naturally. Upon completion of the reaction, the reaction solution turned dark brown.
반응 종료 후 반응액에 직접 헥산(Hexane) 10 ml를 투입하여 희석시키고 10 분 동안 교반하였다. 원심분리용 튜브(40ml 용량)에 상기 희석된 반응액 10 ml, 헥산 5 ml, 이소프로필알콜(Isopropyl alcohol, IPA) 20 ml를 넣고 vortex로 충분히 혼합시켜 주었다. 10000 rpm/5분 간 원심분리하여 생성물 입자를 수득하였다.
After completion of the reaction, 10 ml of hexane was directly added to the reaction solution, and the mixture was diluted and stirred for 10 minutes. 10 ml of the diluted reaction solution, 5 ml of hexane and 20 ml of isopropyl alcohol (IPA) were added to a centrifuge tube (40 ml capacity), and the mixture was sufficiently mixed with a vortex. And centrifuged at 10000 rpm for 5 minutes to obtain product particles.
(2) 리간드 교환 반응(2) Ligand exchange reaction
50 mL의 피리딘(Pyridine)과 폴리비닐피롤리돈(Polyvinylpyrrolidone, PVP) 1 g을 70 mL 바이얼에 혼합하고 80 ℃로 가열하며 300 rpm으로 교반시켰다. 이 때 PVP를 한 번에 넣게 되면 Pyridine 안에서 뭉치는 현상이 발생할 수 있으므로 소량씩 첨가하며 녹였다. 완전 용해가 확인되었을 때 Schlenk line이 장착된 3구 반응기에 제조된 상기 용액 50 ml와 Hexane 10mL를 주입했고 구리 나노입자 파우더 1 g을 첨가했다. 반응 중 산화 발생을 막기 위해 반응기 내부의 산소와 잔여 수분을 제거해야 하기 위해 8 x 10-2torr의 진공 유지(30 초 동안) 및 500 cc/분의 아르곤 가스의 주입(3 분 동안)을 각 5회 반복했다. 이 후 아르곤 가스의 유량을 500cc/분으로 고정한 상태로 80 ℃까지 가열하며 450rpm 이상의 속도로 교반하면서 반응시켰다. 80℃까지 가열 후 3시간이 지나면 자연 냉각하며 12시간 이상 더 반응시켰다. 이후 입자의 세척 및 안정적인 분산 상태의 유지를 위해 Methyl alcohol(MeOH)10 ml를 주입하고 5 분 동안 교반을 유지했다. 반응 완료 용액은 수거하여 용액 :MeOH 1 : 2를 비율을 유지하여 혼합하고 초원심분리 장치를 이용하여 입자를 회수했다. 미반응 하고 남아있는 PVP 및 제거된 OLA의 세척을 위하여 상기 과정을 총 2회 반복했다.
50 mL of pyridine and 1 g of polyvinylpyrrolidone (PVP) were mixed in a 70 mL vial, heated to 80 ° C and stirred at 300 rpm. At this time, if PVP is added at one time, it may dissolve in pyridine. When complete dissolution was confirmed, 50 ml of the solution prepared in a three-necked reactor equipped with a Schlenk line and 10 ml of hexane were introduced and 1 g of copper nanoparticle powder was added. Vacuum maintenance of 8 x 10-2 torr (for 30 seconds) and injection of argon gas (for 3 minutes) of 500 cc / min were repeated to remove oxygen and residual moisture in the reactor to prevent oxidation during the reaction. Repeated times. Thereafter, while the flow rate of the argon gas was fixed at 500 cc / min, the mixture was heated to 80 ° C and reacted at a rate of 450 rpm or more while stirring. After 3 hours of heating to 80 ℃, the reaction was allowed to cool for more than 12 hours. Afterwards, 10 ml of methyl alcohol (MeOH) was injected and the stirring was maintained for 5 minutes in order to wash the particles and maintain a stable dispersion state. The reaction-completed solution was collected, mixed with the solution: MeOH 1: 2 at a ratio, and the particles were recovered using an ultracentrifuge. The above procedure was repeated twice for washing the unreacted and remaining PVP and removed OLA.
(3) 포름산에 의한 표면 개질 반응(3) Surface modification reaction with formic acid
포메이트 쉘 형성에 사용되는 용액의 제작을 위해서 70mL vial 병에 아세토니트릴(Acetonitrile) 50mL와 포름산(Formic acid) 120 μl를 넣고 교반하여 혼합하였다. 제작된 용액을 Shlenk line이 장착된 3구 반응기에 넣고 상기 리간드 교환 반응된 입자를 1g 첨가하였다. 이후 8 x 10-2torr의 진공 유지(30 초 동안) 및 500 cc/분의 아르곤 가스의 주입(3 분 동안)을 각 5회 반복한 후 500 cc/분의 아르곤 주입을 유지한 채 30 분 동안 교반하며 반응시켰다. 이후 제작된 용액에 이소프로필알콜(Isopropyl alocohol, IPA라 명명)을 10mL 첨가하고 5 분 동안 교반 상태를 유지하였다. 이후 제작된 용액을 수거하여 용액 : IPA 1 : 2의 비율로 혼합하여 초원심 분리시켜 입자를 수득하였다. 상기 과정을 총 2회 진행하며 이를 통해 남아있는 포름산을 세척하였다. 최종적으로 평균 직경 100 nm 이하의 구형 Cu/Cu 포메이트 코어-쉘 구조의 금속 나노입자를 얻을 수 있었다.
For the preparation of the solution used for forming the formate shell, 50 mL of acetonitrile and 120 μl of formic acid were added to a 70 mL vial bottle and mixed by stirring. The prepared solution was put into a three-necked reactor equipped with a Shlenk line, and 1 g of the ligand-exchanged particles was added. Subsequently, a vacuum maintenance of 8 x 10-2 torr (for 30 seconds) and an injection of argon gas of 500 cc / min (for 3 minutes) were repeated 5 times each, followed by 30 minutes of argon injection at 500 cc / And reacted with stirring. 10 mL of isopropyl alcohol (IPA) was added to the solution, and the mixture was stirred for 5 minutes. Thereafter, the prepared solutions were collected, mixed at a ratio of 1: 2 solution: IPA, and ultracentrifuged to obtain particles. The procedure was carried out twice in total, and the remaining formic acid was washed. Finally, metal nanoparticles of spherical Cu / Cu formate core-shell structure with an average diameter of 100 nm or less were obtained.
비교예Comparative Example
실시예 (2)에서 리간드 교환 반응을 대기 분위기에서 진행시키고 초음파 처리를 수행하는 것을 제외하고 실시예와 동일한 방법으로 금속 나노입자를 제조하였다.
Metal nanoparticles were prepared in the same manner as in Example 1, except that the ligand exchange reaction in Example (2) was conducted in an atmospheric environment and ultrasonic treatment was performed.
평가evaluation
1. 리간드 교환 반응 전후 입자의 결정성 평가1. Evaluation of crystallinity of particles before and after ligand exchange reaction
실시예 (1)에서 얻어지는 코어의 금속 입자 및 (2)에서 리간드 교환 반응 후의 금속 나노입자 각각에 대하여 주사전자현미경(Scanning electron microscope, SEM)으로 촬영하였으며 도 3a와 같은 사진을 얻었다. 리간드 교환 반응 후에도 입자의 결정성이 그대로 유지되는 것을 확인할 수 있다. The metal particles of the core obtained in Example (1) and the metal nanoparticles after the ligand exchange reaction in (2) were photographed by a scanning electron microscope (SEM), and the photograph as shown in FIG. 3A was obtained. It can be confirmed that the crystallinity of the particles is maintained even after the ligand exchange reaction.
한편 비교예의 제조 과정 중 리간드 교환 반응 중 초음파 처리를 한 경우 수득된 입자에 대해 SEM 촬영을 하였고 도 3b와 같은 사진을 얻었다. 반응 중 초음파 처리를 한 경우 결정성이 훼손되었음을 확인할 수 있다.
On the other hand, in the case of the ultrasound treatment during the ligand exchange reaction in the manufacturing process of the comparative example, the obtained particles were SEM-photographed and the photograph as shown in FIG. 3B was obtained. When the ultrasonic treatment is performed during the reaction, it can be confirmed that the crystallinity is damaged.
2. 금속 나노입자의 산화 안정성 평가2. Oxidation stability evaluation of metal nanoparticles
실시예에서 최종적으로 얻어진 금속 나노입자에 대하여 XRD 로 성분 분석을 하였다. 결과를 도 4a에 나타내었다. 시료로부터 얻어진 데이터는 Cu와 동일한 패턴인 것으로 확인되었으며 산화구리(CuO)의 피크는 발견되지 않았다. 따라서 최종 수득물에서 금속의 산화가 방지된 것을 확인할 수 있다.The metal nanoparticles finally obtained in the examples were analyzed by XRD. The results are shown in FIG. 4A. The data obtained from the sample were confirmed to be the same pattern as Cu and no peak of copper oxide (CuO) was found. Therefore, it can be confirmed that oxidation of the metal is prevented in the final product.
반면, 실시예의 (1)로부터 얻어진 입자에 대해 얻어진 XRD 데이터를 보면 도 4b에서와 같이 산화 구리(CuO, Cu2O)와 같은 피크들이 부분적으로 나타나고 있음을 알 수 있다. On the other hand, the XRD data obtained for the particles obtained from the embodiment (1) shows that peaks such as copper oxide (CuO, Cu 2 O) are partially appeared as shown in FIG. 4B.
이로부터 포름산으로 표면이 개질된 입자에서 산화 안정성이 개선되었음이 확인되었다.
From this, it was confirmed that the oxidation stability was improved in the surface-modified particles of formic acid.
Claims (12)
상기 코어 금속은 구리, 니켈, 철, 코발트, 아연, 크롬 또는 망간 입자인 것을 특징으로 하는 금속 나노입자.The method of claim 1,
Wherein the core metal is copper, nickel, iron, cobalt, zinc, chromium or manganese particles.
상기 코어 금속은 하기 식으로 표현되는 금속의 전구체로부터 제조된 것을 특징으로 하는 금속 나노입자.
[식 1]
상기 식에서 M은 Cu, Ni, Fe, Co, Zn, Cr 또는 Mn이고, m=1~5이고,
R은
(여기서, X는 수소, 탄소수 1 내지 6의 알킬기, 또는 할로겐이며, n은 0 내지 23의 정수이다.)The method of claim 1,
Wherein the core metal is produced from a precursor of a metal represented by the following formula.
[Formula 1]
M is Cu, Ni, Fe, Co, Zn, Cr, or Mn, m is 1 to 5,
R is
(Wherein X is hydrogen, an alkyl group having 1 to 6 carbon atoms, or a halogen, and n is an integer of 0 to 23.)
상기 극성의 리간드는 피리딘(pyridine)인 것을 특징으로 하는 금속 나노입자.The method of claim 1,
Wherein the polar ligand is pyridine.
상기 금속 나노입자는 표면에 형성된 금속 포메이트를 포함하는 것을 특징으로 하는 금속 나노입자. The method of claim 1,
Wherein the metal nanoparticles comprise a metal formate formed on a surface thereof.
상기 금속 나노입자의 소결 온도는 150 내지 250 ℃인 것을 특징으로 하는 금속 나노입자.The method of claim 1,
Wherein the metal nanoparticles have a sintering temperature of 150 to 250 ° C.
상기 제조된 금속 나노입자를 극성의 리간드로 리간드 교환 반응시키는 단계; 및
상기 리간드 교환된 금속 나노입자를 포름산과 반응시키는 단계를 포함하는 것을 특징으로 하는 금속 나노입자의 제조방법:
[식 1]
상기 식에서 M은 Cu, Ni, Fe, Co, Zn, Cr 또는 Mn이고, m=1~5이고,
R은
(여기서, X는 수소, 탄소수 1 내지 6의 알킬기, 또는 할로겐이며, n은 0 내지 23의 정수이다.)A precursor of metal nanoparticles is prepared by dissolving a metal precursor represented by the following formula in a capping agent to prepare a reaction solution and reacting the metal nanoparticle at a reaction temperature of 250 to 350 ° C for 1 to 4 hours, ;
Ligand exchange reaction of the prepared metal nanoparticles with a polar ligand; And
And reacting the ligand-exchanged metal nanoparticles with formic acid to produce metal nanoparticles.
[Formula 1]
M is Cu, Ni, Fe, Co, Zn, Cr, or Mn, m is 1 to 5,
R is
(Wherein X is hydrogen, an alkyl group having 1 to 6 carbon atoms, or a halogen, and n is an integer of 0 to 23.)
상기 캡핑화제(capping agent)는 탄소수 4 내지 18의 알킬기를 갖는 아민인 것을 특징으로 하는 금속 나노입자의 제조방법.8. The method of claim 7,
Wherein the capping agent is an amine having an alkyl group of 4 to 18 carbon atoms.
상기 반응액 내 전구체의 농도는 30 내지 60 mmol인 것을 특징으로 하는 금속 나노입자의 제조방법. 8. The method of claim 7,
Wherein the concentration of the precursor in the reaction solution is 30 to 60 mmol.
상기 전구체는 구리 헥사노에이트(Copper(II) bis(2-ethylhexanoate))인 것을 특징으로 하는 금속 나노입자의 제조방법. 8. The method of claim 7,
Wherein the precursor is copper (II) bis (2-ethylhexanoate).
상기 금속 나노입자를 제조하는 단계에서의 반응은 비활성 분위기 또는 환원 분위기에서 수행되는 것을 특징으로 하는 금속 나노입자의 제조방법. 8. The method of claim 7,
Wherein the reaction in the step of preparing the metal nanoparticles is performed in an inert atmosphere or a reducing atmosphere.
상기 리간드 교환 반응은 비초음파 분무 하에서 및 비활성 분위기 또는 환원 분위기에서 진행되는 것을 특징으로 하는 금속 나노입자의 제조방법.
8. The method of claim 7,
Wherein the ligand exchange reaction is carried out under non-ultrasonic atomization and in an inert or reduced atmosphere.