CN1263677C - Preparation for composite material with nanometal or metal oxide distributed on surface of carbon nanotube uniformly - Google Patents
Preparation for composite material with nanometal or metal oxide distributed on surface of carbon nanotube uniformly Download PDFInfo
- Publication number
- CN1263677C CN1263677C CN 200410013069 CN200410013069A CN1263677C CN 1263677 C CN1263677 C CN 1263677C CN 200410013069 CN200410013069 CN 200410013069 CN 200410013069 A CN200410013069 A CN 200410013069A CN 1263677 C CN1263677 C CN 1263677C
- Authority
- CN
- China
- Prior art keywords
- carbon
- carbon nanotube
- composite material
- nano tube
- metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a method for preparing composite material with metals or metal oxides uniformly distributed on the surface of a carbon nanometer tube. The method is based on a precursor, the supersound treatment for a long time or / and the agitation and the standing treatment of an organic metal compound and a carbon nanometer tube treated by concentrated nitric acid are carried out, and the organic metal compound coordinately reacts with carboxyl groups and/or carbonyl groups and/or hydroxy groups on the surface of the carbon nanometer tube. Under the action of an alcohol solvent, the organic metal compound is nucleated on the tube wall of the carbon nanometer tube, and a plurality of nanometer magnitude quantum dots or tens of nanometer crystals are crystallized and grown along the growth direction of the limited priority crystal surface. Finally, nanometer metal/carbon nanometer tubes uniformly distributed and nanometer metal oxide/carbon nanometer tube composite material are formed. The composite material has application prospects for sensors, nanometer electron devices, superhigh magnetic recording multimedia, lithium batteries, solar batteries based on nanometer material and novel catalysts.
Description
Technical Field
The present invention belongs to a preparation method of a composite material with nanometer metal or metal oxide uniformly distributed on the surface of a carbon nano tube.
Background
Carbon nanotubes have attracted much attention since their discovery in 1991 due to their unique structure, specific mechanical and electrical properties. At present, carbon nanotubes can be formed into various composite materials with other materials, such as polymer composite materials, ceramic composite materials, layered composite materials, nitrogen-doped composite materials, carbon/carbon nanotube composite materials, and the like (ann. rev. mater. res.2003, 33, 419), and the composite materials have potential application prospects in the aspects of reinforcing fibers, novel catalysts and electronic nano-devices. There are two methods for preparing a composite material using carbon nanotubes as a template, one is chemical bonding (acc. chem. res.2002, 35, 1096) by functionalizing the surface of carbon nanotubes, and the other is coating a film on the surface of carbon nanotubes (langmuir.2003, 19, 7026), both of which finally use high temperature heating (calcination) to obtain bonding of inorganic compounds to carbon nanotubes. Although inorganic compound/carbon nanotube composites have been synthesized, they still lack the ability to control the distribution of inorganic compounds on the surface of carbon nanotubes and to form nanoparticles and even quantum dots.
The synthesis of various metal or metal oxide nanomaterials using alcohols as solvents is a widely used method (Angew. chem. int. Ed.2001, 40, 359), by means of which TiO is synthesized2、CoO、ZnO、Cu2O、Fe2O3、Nb2O3、Ta2O3、Al2O3And many inorganic nano materials can be prepared. In the method, the solvent alcohol not only can perform the hydrolysis function, but also some solvents can reduce the compounds in unstable valence state, even the compoundsTo reduce it to elemental metal. The main advantage of this method is the ability to control the shape, size and uniformity of particle size of the precipitated particles by varying experimental conditions (J.Mater.Chem.1996, 6, 1047; Science, 2000, 287, 1989).
Metal oxide and carbon nanotube and metal and carbon nanotube composite material. The catalyst has application prospect in the aspects of sensors, nano electronic devices, ultrahigh magnetic recording multimedia, lithium batteries, solar batteries based on nano materials and novel catalysts.
Disclosure of Invention
The invention aims to provide a preparation method of a composite material with nano metal or metal oxide uniformly distributed on the surface of a carbon nano tube.
The method of the invention utilizes the coordination bond formed between the organic metal compound and the functionalized carbonnano tube, and then hydrolyzes and/or reduces under the action of alcohol solvent to obtain the metal oxide and carbon nano tube or metal and carbon nano tube composite material with nano particles and even quantum dots uniformly distributed on the surface of the carbon nano tube.
The principle of the invention is as follows:
the carbon nanotubes with functionalized surfaces can be coordinately bonded with the metal in the organic metal compound through pretreatment, and the formula is as follows:
wherein n and m represent any number, 1 ═ 2 or 3 or 4, CNTs represent carbon nanotubes, Me represents a metal element, and R is a hydrocarbyl or a hydrocarbyl group having a carbonyl group; the expression is represented by a carboxyl group, and the expression in which a carbonyl group or a hydroxyl group participates in the reaction is similar thereto.
When the valence state of the metal is +2, the adjacent carboxyl and/or carbonyl and/or hydroxyl on one carbon nanotube or the carboxyl and/or carbonyl and/or hydroxyl on different carbon nanotubes can generate coordination with the organic metal compound; when the valence of the metal is +3 or +4, the carboxyl and/or carbonyl and/or hydroxyl on different carbon nanotubes can coordinate with the organic metal compound. Thus, the precursor and the carbon nanotube are chemically bonded together.
Under the action of alcohol solvent, the organic metal compound combined with the carbon nano tube is subjected to hydrolysis reaction, and the expression is as follows:
(R' ═ H or hydrocarbyl)
After the reaction lasts for a long time, the metal hydroxide on the surface of the carbon nanotube can generate decomposition reaction, and a metal oxide and carbon nanotube composite material is generated. When the solvent has a certain reducing capacity, the metal and carbon nanotube composite material can be finally obtained.
Generally, only carbon nanotubes that have been surface-treated and have carboxyl and/or carbonyl and/or hydroxyl groups on the surface will be coordinately bound to the organometallic compound under certain conditions. The carbon nanotubes are sufficiently dispersed by long-time ultrasound and/or stirring, and the organic metal compound has an opportunity to contact as many carbon nanotubes as possible and reach the surface of the carbon nanotubes to be bonded with functional groups thereon; the long-time standing enables the organic metal compound to be fully combined with the groups on the carbon nano tube to form coordinate bonds, and lays a foundation for the crystallization nucleation of metal oxide or metal crystals on the surface of the carbon nano tube. By selecting proper solvent and controlling the concentration, time, temperature and other methods of reaction, different metal oxides or metals can be controlled to nucleate at the place where the carbon nanotube can form coordinate bond, and grow into quantum dots with a few nanometers or particles with a few tens of nanometers along the crystal growth direction limited by the carbon nanotube.
The scheme for realizing the purpose of the invention is as follows: the preparation method of the composite material with nano metal or metal oxide uniformly distributed on the surface of the carbon nano tube is characterized in that the composite material is prepared by an alcohol solvent method according to the following two steps:
the first step of pretreatment:
(1) dissolving metal oxide or metal precursor organic metal compound in alcohol or lower ether, sulfone, tetrahydrofuran or halogenated hydrocarbon organic solvent,
(2) refluxing carbon nanotubes (purchased from market, produced by Shenzhen Nangang) with concentrated nitric acid at 15-240 ℃ for 1-2 hours to enable the surfaces of the carbon nanotubes to have carboxyl and/or carbonyl and/or hydroxyl polar groups, namely surface functionalization,
(3) putting the carbon nano tube with functionalized surface into the solution obtained in the step (1), fully performing ultrasonic treatment and/or stirring, and fully standing to enable the metal oxide or the metal organic compound to form coordination bond combination with the polar group on the surface of the carbon nano tube;
the second step is preparation: and (3) reacting the ligand bond combination obtained by the pretreatment in the first step by using alcohols and aqueous solution thereof as solvents, wherein the control conditions are as follows: reaction conjugate concentration 1X 10-7The solvent of 500g/L is reacted at 50 to 300 ℃ for 0.5 to 108 hours to obtain the composite material with the nano metal or the metal oxide uniformly distributed on the surface of the carbon nano tube.
The carbon nanotube surface evenly distributed nano metal or metal oxide composite material comprises: CuO, carbon nanotube and Cu2O and carbon nanotube, Cu and carbon nanotube, ZnO and carbon nanotubeNanotube, CdO and carbon nanotube, NiO and carbon nanotube, Ni and carbon nanotube, CoO and carbon nanotube, Co and carbon nanotube, TiO2With carbon nanotubes and Al2O3With carbon nanotubes, SiO2With carbon nanotubes, Fe2O3And carbon nanotube, Fe and carbon nanotube, Nb2O5And carbon nanotube, WO3And carbon nanotubes, V2O5With carbon nanotubes,Sb2O5With carbon nanotubes, Sb2O3With carbon nanotubes, SnO2And carbon nanotube, SnO and carbon nanotube, Sn and carbon nanotube, MoO3And carbon nanotube, MoO and carbon nanotube, Mo and carbon nanotube, Ta2O5With carbon nanotubes and Bi2O3And carbon nanotube, La2O3And carbon nanotube, Y2O3With carbon nanotubes, ZrO2Composite material of carbon nanotube, Ag and carbon nanotube, Pt and carbon nanotube, Pa and carbon nanotubeAnd (5) feeding.
The solvent for dissolving the precursor organometallic compound is alcohol (such as methanol, ethanol, isopropanol, butanol), lower ether (such as diethyl ether), sulfone (such as dimethyl sulfoxide), tetrahydrofuran, and halogenated hydrocarbon (such as chloroform, carbon tetrachloride).
In the pretreatment process for forming a coordinate bond between the carbon nanotube and the organometallic compound, the concentration of the organometallic compound in the organic solvent is 1 × 10-5-30M。
In the pretreatment process of forming coordination bond between carbon nanotube and organic metal compound, the addition amount of carbon nanotube is 1 × 10-6100g/L of solution.
In the pretreatment process of forming the coordination bond between the carbon nano tube and the organic metal compound, the time required by ultrasonic treatment and/or stirring is 0.4-10 h.
In the pretreatment process of forming the coordination bond between the carbon nano tube and the organic metal compound, the standing time after the ultrasonic and/or stirring treatment is 0.5-72 h.
In the second step of preparing the composite material, the selected alcohol and its aqueous solution are ethanol or propanol, isopropanol, ethylene glycol, glycerol, diethylene glycol, triethylene glycol, diglycerol, hexadecanediol, and polyvinyl alcohol.
In the preparation stage of the composite material, the temperature of reaction hydrolysis is 50-300 ℃.
Detailed Description
The carbon nanotubes with functionalized surfaces used in the following examples are carbon nanotubes with carboxyl and/or carbonyl and/or hydroxyl polar groups on the surfaces after refluxing of commercially available carbon nanotubes (produced by Shenzhen Nangang) with concentrated nitric acid at 150-240 ℃ for 1-2 hours.
Example 1: adding 20mg of carbon nano tube with functionalized surface and 1g of aluminium isopropoxide into 200mL of isopropanol, heating and ultrasonically dispersing for 4h, standing for 12h, then centrifugally separating the suspension, retaining black solid substances, and drying the mixture with coordination in an oven. 20mg of the mixture was taken and placed in 200mL of diethylene glycol in water (volume ratio 3: 1) and reacted at 95 ℃ for 2h, then the temperature was raised to 250 ℃ and the reaction was continued for 8h to obtain a black product.
Al observed by high resolution transmission electron microscope2O3With the carbon nano tube composite material, the surface of the carbon nano tube can be seen to have crystals with irregular shapes of about 10nm, and the crystals are distributed uniformly at intervals of 500 nm. X-ray diffraction shows Al2O3The nature of the crystal.
Example 2: 10mg of carbon nanotubes with functionalized surfaces and 300mg of copper acetate were ultrasonically dispersed in ethanol for 3 hours, left to stand for 24 hours, and then the suspension was centrifugally separated,and the precipitate was put into an oven to remove the solvent. The mixture obtained after the copper acetate had been deposited on the surface of the carbon nanotubes was placed in a closed reactor together with 200mL of glycerol solvent, and nitrogen gas was introduced. Heating to 200 deg.C under vigorous stirring, reacting for 3 hr, centrifuging the obtained suspension, washing the precipitate with distilled water for 3 times, and oven drying in a vacuum oven to obtain Cu2O and carbon nanotube composite material.
The preparation method of the metal Cu and carbon nanotube composite material is the same as that of Cu2O is similar to the carbon nanotube composite in that the reaction time is extended to over 5 hours while the temperature is increased to 250 ℃.
The preparation method of the CuO and carbon nanotube composite material is the same as that of Cu in the pretreatment stage of forming coordinate bonds between precursors and carbon nanotubes2The same as the O/carbon nanotube composite material, the hydrolysis reaction stage is as follows: and mixing the mixture of copper acetate deposited on the surface of the carbon nano tube with 200mL of water, reacting for 5h at 95 ℃, then raising the temperature to 250 ℃, and continuing to react for 10h to obtain the black CuO and carbon nano tube composite material.
The three metal oxides and metals can be uniformly distributed on the surface of the carbon nano tube under a high-resolution transmission electron microscope, the crystal particle size is 6-50nm, wherein Cu is2The quantum dots on the surface of the carbon nano tube in the O/carbon nano tube composite material are arranged one by one. XRD analysis proves the existence of three kinds of crystals。
Example 3: and ultrasonically dispersing 300mg of carbon nano tube with functionalized surface and 2g of zinc acetate in ethanol for 4 hours, standing for 24 hours, and directly putting the suspension into an oven for drying to remove the solvent. 1g of the obtained mixture in which zinc acetate is deposited on the surface of the carbon nano tube is mixed with 300mL of diethylene glycol solvent, the temperature is raised to 300 ℃ under vigorous stirring, and the hydrolysis reaction lasts for 3 hours. And centrifugally separating, washing, repeating for 3 times, and drying in an oven to obtain the dark gray ZnO and carbon nanotube composite material. According to observation of a high-resolution transmission electron microscope, ZnO of about 15-40nm is found to be distributed more uniformly on the surface of the carbon nano tube, and some nano ZnO crystals appear in the background independently. XRD detection proves that the crystal is ZnO.
The preparation process of the CdO and carbon nanotube composite material is basically the same as that described above, except that the solvent is hexadecanediol.
Example 4: 2g of tetrabutyl titanate and 500mg of carbon nanotube wire with functionalized surface are ultrasonically dispersed in 500mL of ether solvent for 1 hour, then are magnetically stirred for 12 hours, and are dried after standing for 12 hours to remove the solvent. Dispersing 500mg of the above mixture in 400mL of 2% polyvinyl alcohol solution by vigorous stirring, reacting at 100 deg.C for 10 hr, stopping reaction, centrifuging, washing, repeating for 3 times, and oven drying to obtain grey-black TiO2And carbon nanotube composite material. The observation of an electron microscope shows that titanium dioxide crystals grow on the surface of the carbon nano tube and are dispersed uniformly, but part of the titanium dioxide crystals are gathered and appear in the background. XRD analysis proves that the titanium dioxide crystals in the composite material are mainly in a sharp state, but a small amount of rutile type exists.
SiO2、SnO2、ZrO2The preparation process of the material is similar to that of the carbon nano tube composite material, except that the used hydrolysis solvents are diethylene glycol, triethylene glycol and glycerol respectively.
Example 5: ultrasonically dispersing 1g of niobium ethoxide and 10mg of carbon nano tube with functionalized surface in 300mL of chloroform for 0.5h, magnetically stirring for 2h, standing for 48h, centrifuging the suspension, and precipitatingPut into an oven to remove the solvent. Putting the obtained mixture of the niobium ethoxide deposited on the surface of the carbon nano tube and 500mL of diethylene glycol solvent into a reactor, raising the temperature to 300 ℃ under the condition of vigorous stirring, stopping the reaction after 1h, centrifugally separating the obtained suspension, washing the precipitate for 3 times by using distilled water, and drying in a vacuum oven to obtain the Nb-containing carbon nano tube2O5And carbon nanotube composite material. Electron microscopy analysis showed Nb2O5The crystals are distributed on the surface of the carbon nano tube more uniformly, the particle size is 6-10nm, and the quantum effect is good. XRD analysis shows that the granular quantum dots exist in a crystal form.
V2O5、Sb2O5、Ta2O5The method of preparing the composite material with the carbon nano tube is similar to the process.
Example 6: 0.5g of platinum acetate and 20mg of carbon nanotubes with functionalized surfaces are ultrasonically dispersed in 200mL of dimethyl sulfone solvent for 8h, and after standing for 10h, the suspension is directly dried to remove the solvent. Putting the mixture of platinum acetate and carbon nano-tubes, 300mL of 1 and 2-hexadecanediol solventinto a reactor, violently stirring, adding initiator oleic acid, heating to 200 ℃, stopping reaction after 10 hours, centrifugally separating the obtained suspension, washing precipitates for 3 times by using distilled water, and putting the precipitates into an oven for drying to obtain the Pt/carbon nano-tube composite material. Electron microscopy analysis shows that Pt crystals are relatively uniformly distributed on the surface of the carbon nanotube, and the particle size is 20 nm. XRD analysis proves that the nano particles are Pt metal simple substances.
The preparation process of the Ag and carbon nano tube and Pa/carbon nano tube composite material is basically the same as that of the Pt and carbon nano tube composite material.
Example 7: ultrasonically dispersing 2g of nickel acetate and 50mg of carbon nano tubes with functionalized surfaces in 500mL of tetrahydrofuran solvent for 3h, magnetically stirring for 10h, standing for 3h, and directly drying the suspension to remove the solvent. Putting the mixture of nickel acetate and carbon nano tubes and 300mL of diglycol solvent into a reactor, violently stirring, heating to 180 ℃, stopping reaction after 3 hours, centrifugally separating the obtained suspension, washing the precipitate with distilled water for 3 times, and drying to obtain the NiO and carbon nano tube composite material. Electron microscope analysis shows that NiO crystals are distributed on the surface of the carbon nano tube more uniformly, the particle size is 2-3nm, and the quantum effect is good. XRD analysis confirmed that the nanoparticles were nickel oxide.
Fe2O3Similar to the preparation method of the carbon nano tube, the CoO and carbon nano tube, the MoO and carbon nano tube and the NiO and carbon nano tube composite material. The preparation method of the nano metal composite material corresponding to the four metal oxides is basically consistent with the process, only the hydrolysis solvent needs to use glycerol or triethylene glycol which has three hydroxyl groups and strong reducibility, and the reaction time also needs to be prolonged to be more than 6 hours.
Example 8: 3g of tin (II) oxalate and 300mg of carbon nanotubes with functionalized surfaces were ultrasonically dispersed in 500mL of isopropanol solvent for 3h, and after standing for 8h, the suspension was directly dried to remove the solvent. And putting the mixture of the tin (II) oxalate and the carbon nano tube and 300mL of glycol solvent into a reactor, violently stirring, heating to 150 ℃, reacting for 6 hours, stopping, centrifugally separating the obtained suspension, washing the precipitate for 3 times by using distilled water, and drying to obtain the SnO and carbon nano tube composite material. Electron microscope analysis shows that SnO crystals are distributed on the surface of the carbon nano tube more uniformly, and the particle size is 15-20 nm. XRD analysis demonstrated that the nanoparticles were stannous oxide.
In the reaction process, the hydrolysis solvent is changed into triethylene glycol or glycerol, the reaction time is prolonged to 10 hours, and finally the Sn/carbon nano tube composite material is obtained.
Example 9: 1g of tungsten hexacarbonyl and 20mg of carbon nanotubes with functionalized surfaces are dispersed in 300mL of carbon tetrachloride solvent, magnetically stirred for 15h, and after standing for 8h, the solvent is removed by centrifugal separation. Putting the mixture of tungsten hexacarbonyl and carbon nano tube and 300mL of ethanol solvent into a reactor, violently stirring, heating to 120 ℃, carrying out reflux reaction for 8 hours, stopping, centrifugally separating the obtained suspension, washing the precipitate with distilled water for 3 times, and drying to obtain the WO3And carbon nanotube composite material.Analysis by electron microscope shows WO3The crystals are relatively uniformly distributed inThe diameter of the particles on the surface of the carbon nano tube is less than 50 nm. XRD analysis demonstrated that the nanoparticles were tungsten trioxide.
MoO3Preparation process of carbon nanotube composite material and WO3Similar to that of the carbon nanotube composite.
Example 10: ultrasonically dispersing 0.3g of bismuth salicylate and 10mg of carbon nano tubes with functionalized surfaces in butanol for 0.5h, magnetically stirring for 12h, and directly drying the suspension to remove the solvent. Putting the mixture of bismuth salicylate and carbon nanotube and 200mL of propanol solvent into a reactor, violently stirring, carrying out reflux reaction for 10 hours at the temperature of 150 ℃, carrying out centrifugal separation treatment on the suspension, and drying to obtain Bi2O3And carbon nanotube composite material. TEM shows Bi2O3The nano particles are uniformly distributed on the surface of the carbon nano tube. XRD analysis shows that the crystal is Bi2O3。
La2O3、Y2O and Sb2O3Preparation process of composite material with carbon nano tube and Bi2O3Similar to that of the carbon nanotube composite.
Claims (8)
1. A method for preparing a composite material with uniformly distributed nano metal or metal oxide on the surface of a carbon nano tube is characterized by comprising the following two steps of:
the first step of pretreatment:
(1) dissolving metal oxide or metal precursor organic metal compound in alcohol or lower ether, sulfone, tetrahydrofuran or halogenated hydrocarbon organic solvent,
(2) refluxing the carbon nanotube with concentrated nitric acid at 150-240 deg.C for 1-2 hr to make its surface have polar groups of carboxyl and/or carbonyl and/or hydroxyl, i.e. surface functionalization,
(3) putting the carbon nano tube with functionalized surface into the solution obtained in the step (1), fully performing ultrasonic treatment and/or stirring, and fully standing to enable the metal oxide or the metal organic compound to form coordination bond combination with the polar group on the surface of the carbon nano tube;
the second step is preparation:
and (3) reacting the ligand bond combination obtained by the pretreatment in the first step by using alcohols and aqueous solution thereof as solvents, wherein the control conditions are as follows: reaction conjugate concentration 1X 10-7The solvent of 500g/L is reacted at 50 to 300 ℃ for 0.5 to 108 hours to obtain the composite material with the nano metal or the metal oxide uniformly distributed on the surface of the carbon nano tube.
2. The method of claim 1, wherein the step of uniformly distributing the nano metal or metal oxide composite material on the surface of the carbon nanotube comprises: CuO, carbon nanotube and Cu2O and carbon nanotube, Cu and carbon nanotube, ZnO and carbon nanotube, CdO and carbon nanotube, NiO and carbon nanotube, Ni and carbon nanotube, CoO and carbon nanotube, Co and carbon nanotube, TiO2With carbon nanotubes and Al2O3With carbon nanotubes, SiO2With carbon nanotubes, Fe2O3And carbon nanotube, Fe and carbon nanotube, Nb2O5And carbon nanotube, WO3And carbon nanotubes, V2O5With carbon nanotubes,Sb2O5With carbon nanotubes, Sb2O3With carbon nanotubes, SnO2And carbon nanotube, SnO and carbon nanotube, Sn and carbon nanotube, MoO3And carbon nanotube, MoO and carbon nanotube, Mo and carbon nanotube, Ta2O5With carbon nanotubes and Bi2O3And carbon nanotube, La2O3And carbon nanotube, Y2O3With carbon nanotubes, ZrO2And carbon nano tube, Ag and carbon nano tube, Pt and carbon nano tube, Pa and carbon nano tube composite material.
3. The method according to claim 1, wherein the solvent for dissolving the precursor organometallic compound is methanol, ethanol, isopropanol, butanol, diethyl ether, dimethyl sulfoxide, tetrahydrofuran, chloroform or carbon tetrachloride.
4、The method according to claim 1, wherein the concentration of the organometallic compound in the organic solvent during the pretreatment for forming the coordinate bond between the carbon nanotube and the organometallic compound is 1X 10-5-30M。
5. The method according to claim 1, wherein the amount of the carbon nanotubes added is 1X 10 in the pretreatment for forming coordinate bonds between the carbon nanotubes and the organometallic compound-6100g/L of solution.
6. The method according to claim 1, wherein the time for the ultrasonic treatment and/or the stirring is 0.4 to 72 hours during the pretreatment for forming the coordinate bond between the carbon nanotube and the organometallic compound.
7. The method according to claim 1, wherein the standing time is 0.5 to 72 hours during the pretreatment for forming a coordinate bond between the carbon nanotube and the organometallic compound.
8. The process according to claim 1, wherein in the second preparation stage, the alcohol or its aqueous solution is selected from ethanol, propanol, isopropanol, ethylene glycol, glycerol, diethylene glycol, triethylene glycol, diglycerol, hexadecanediol, and polyvinyl alcohol.