KR20140023858A - Anodes active material containing si composite for lithium secondary batteries and its preparation method and lithium secondary batteries comprising the same - Google Patents
Anodes active material containing si composite for lithium secondary batteries and its preparation method and lithium secondary batteries comprising the same Download PDFInfo
- Publication number
- KR20140023858A KR20140023858A KR1020130093352A KR20130093352A KR20140023858A KR 20140023858 A KR20140023858 A KR 20140023858A KR 1020130093352 A KR1020130093352 A KR 1020130093352A KR 20130093352 A KR20130093352 A KR 20130093352A KR 20140023858 A KR20140023858 A KR 20140023858A
- Authority
- KR
- South Korea
- Prior art keywords
- nano
- graphene
- carbon fiber
- silicon
- fiber composite
- Prior art date
Abstract
Description
본 발명은 리튬이차전지용 실리콘 복합재 음극활물질, 이의 제조방법 및 이를 포함하는 리튬이차전지에 관한 것이다.The present invention relates to a silicon composite anode active material for a lithium secondary battery, a manufacturing method thereof, and a lithium secondary battery including the same.
리튬 이차전지용 음극 재료 중 실리콘은 탄소 재료를 대체할 수 있는 물질로 상용화된 흑연질 재료의 이론 용량보다 큰 이론 용량을 갖고 있다. 그러나 실리콘은 리튬과의 합금화(alloying) 및 비합금화(de-alloying) 과정에서 많은 부피 변화로 인하여 전극이 열화되기 때문에 용량이 급격히 감소하는 문제점이 있다.Among the negative electrode materials for lithium secondary batteries, silicon has a theoretical capacity larger than that of the graphite material commercialized as a material that can replace the carbon material. However, silicon has a problem in that its capacity decreases rapidly because the electrode deteriorates due to a large volume change in the alloying and de-alloying process with lithium.
이러한 부피 변화에 따른 전극의 퇴화를 막기 위하여 다공성 실리콘을 이용하여 부피 변화에 대한 완충 효과를 갖도록 하는 방안이 검토되고 있다. 또한, 입자의 크기를 나노 크기로 제조하여 전극의 절대적인 부피 변화를 최소화하려는 노력이 진행되고 있다. In order to prevent the deterioration of the electrode due to the volume change, a method of using a porous silicon to have a buffer effect against the volume change has been studied. In addition, efforts have been made to minimize the absolute volume change of the electrode by preparing the size of the particles to a nano size.
실리콘 산화물(SiO)은 리튬과의 반응에 의해 형성된 리튬 산화물(Li2O)과 리튬실리케이트(LiaSibOc)가 실리콘의 부피변화를 완화시키는 효과가 있어 실리콘보다는 안정한 충방전 성능을 얻을 수 있지만, 실리콘(Si)보다 용량과 전기전도도가 낮다는 문제점이 있다. 이를 해결하기 위해 SiO-카본 복합재 또는 카본 코팅된 SiO 소재를 개발하는 노력이 진행되고 있다.Silicon oxide (SiO) is a lithium oxide (Li 2 O) and lithium silicate (Li a Si b O c ) formed by the reaction with lithium has the effect of mitigating the volume change of silicon to obtain a stable charge and discharge performance than silicon However, there is a problem that capacity and electrical conductivity are lower than that of silicon (Si). In order to solve this problem, efforts are being made to develop SiO-carbon composites or carbon coated SiO materials.
상기 실리콘 나노분말을 제조하는 방법으로는 화학적 또는 전기 화학적 방법으로 실리콘 웨이퍼를 식각하는 방법이 보고된 바 있다. 또한, 나노 크기의 실리콘 입자를 합성하는 다른 방법으로 유기-금속계 전구체를 이용하여 합성하는 방법 또는 액상의 전구체를 환원하는 방법이 알려져 있다. 그러나 유기-금속계 전구체 또는 액상 전구체는 반응성이 매우 강하고 독성이 강하여 산소나 수분이 없는 조건에서 합성하여야 하는 단점이 있다.As a method of producing the silicon nano powder, a method of etching a silicon wafer by a chemical or electrochemical method has been reported. As another method for synthesizing nano-sized silicon particles, a method of synthesizing using an organo-metallic precursor or a method of reducing a liquid precursor is known. However, the organo-metallic precursor or the liquid precursor has a disadvantage in that it is highly reactive and highly toxic to synthesize in the absence of oxygen or moisture.
또한, 상기 실리콘 나노 분말의 제조방법으로는 다공성의 실리콘 입자를 초음파 처리하는 방법, 콜로이드 합성법, 진공증착법 등을 이용하여 제조하는 방법이 있으나, 상기 방법들은 비용이 높은 공정이 요구되고, 전구체 또는 식각 용액이 유독한 문제점이 있다. In addition, the method of manufacturing the silicon nanopowder includes a method of ultrasonically treating porous silicon particles, a colloid synthesis method, a vacuum deposition method, etc., but these methods require a costly process, and precursor or etching The solution is toxic.
한국공개특허 제10-2004-0082876호(특허문헌 1)에는 실리콘전구체와 알카리금속 또는 알카리 토금속을 열처리를 통해 실리콘 입자를 제조하고 이를 초음파를 이용하여 실리콘 나노입자를 제조하는 방법이 개시되어 있으나, 리튬이차전지 음극용 활물질에 적용시 부피 팽창 및 박리 등으로부터 안정성을 개선할 수는 있으나, 충방전 성능이 충분하지 못하고, 사이클 특성이 떨어지는 문제점이 있다. Korean Patent Laid-Open Publication No. 10-2004-0082876 (Patent Document 1) discloses a method for preparing silicon particles by heat treating a silicon precursor and an alkali metal or an alkaline earth metal, and using the ultrasonic waves to produce silicon nanoparticles. When applied to an active material for a lithium secondary battery negative electrode, it is possible to improve stability from volume expansion and peeling, but there is a problem in that charge and discharge performance is not sufficient and cycle characteristics are poor.
한편, 그래핀, 탄소나노튜브 등의 도전성 재료를 전지용 전극재료로서 사용하는 것에 관해 지속적으로 연구되고 있다. 한국공개특허 제10-2011-0059130호(특허문헌 2)에는 탄소나노튜브 및 그래핀이 혼합된 복합 조성물 및 이를 전극재료로 이용하는 방법에 관해 기재되어 있으나, 이는 실리콘 또는 실리콘 아산화물 나노 분말을 사용하고 있지 않으며 전극재료로서 단순히 탄소섬유, 그래핀 등의 다양한 성분들을 혼합하여 전지에 적용하는 것에 관해서만 기재되어 있어 실리콘계 나노 분말상을 포함하는 전극재료의 입자크기, 기공정도, 전기전도도 등의 물리화학적 특성을 개선시키는 데 한계가 있다. On the other hand, the use of conductive materials such as graphene and carbon nanotubes as battery electrode materials has been continuously studied. Korean Patent Publication No. 10-2011-0059130 (Patent Document 2) describes a composite composition in which carbon nanotubes and graphene are mixed and a method of using the same as an electrode material. It is described only to apply various components such as carbon fiber, graphene, etc. to the battery as an electrode material, and the physical and chemical properties such as particle size, preprocessing diagram, and electrical conductivity of the electrode material including the silicon-based nano powder phase are described. There is a limit to improving the characteristics.
따라서, 경제적으로 저렴하면서도 상온에서 간단하게 나노 실리콘계 입자를 제조하고 이에 도전성재료를 부가하여 이차전지 음극재료의 입자크기, 표면적, 기공 정도, 나노구조 등의 물리화학적 특성을 조절함으로써 활물질로서의 성능을 획기적으로 향상시킬 수 있는 방법에 대한 연구 개발이 필요한 실정이다.Therefore, it is economically inexpensive but simply manufactures nano silicon-based particles at room temperature and adds a conductive material to them to control physicochemical properties such as particle size, surface area, porosity, and nanostructure of the secondary battery anode material to breakthrough performance as an active material. Research and development on how to improve the situation is required.
본 발명은 상기와 같은 문제점을 해결하기 위하여 안출된 것으로서, 저가의 실리카를 이용하여 나노 실리콘계 화합물 분말을 합성하며, 상기 나노 실리콘계 화합물, 그래핀 및 탄소섬유를 포함함으로써 비용을 절감하면서 전극 특성을 향상시킬 수 있는 이차전지용 음극활물질을 제공하는 것을 목적으로 한다.The present invention has been made to solve the above problems, synthesizes a nano silicon-based compound powder using a low-cost silica, and improve the electrode characteristics while reducing the cost by including the nano silicon-based compound, graphene and carbon fiber It is an object of the present invention to provide a negative electrode active material for a secondary battery.
또한, 본 발명은 상기 나노 실리콘계 화합물-그래핀-탄소섬유 복합재를 포함하는 리튬이차전지용 음극활물질 및 이를 포함하는 이차전지를 제공하는 데 그 목적이 있다.In addition, an object of the present invention is to provide a negative active material for a lithium secondary battery comprising the nano-silicon compound-graphene-carbon fiber composite and a secondary battery comprising the same.
상기와 같은 목적을 달성하기 위하여, 본 발명은 나노 실리콘, 나노 실리콘 아산화물 및 이들의 혼합물 중에서 선택되는 나노 실리콘계 화합물과 그래핀 및 탄소섬유를 포함하여 제조되는 나노 실리콘계 화합물-그래핀-탄소섬유 복합재를 제공한다.In order to achieve the above object, the present invention is a nano-silicon compound-graphene-carbon fiber composites, including nano-silicon compound selected from nano silicon, nano silicon suboxide and mixtures thereof and graphene and carbon fiber To provide.
본 발명의 일 실시예에 따른 나노 실리콘계 화합물-그래핀-탄소섬유 복합재에 있어서, 상기 나노 실리콘 아산화물(SiOx)은 0 < x < 0.9, 좋게는 0 < x < 0.5, 더욱 바람직하게는 0.2 < x < 0.4일 수 있다.In the nano silicon-based compound-graphene-carbon fiber composite according to an embodiment of the present invention, the nano silicon suboxide (SiO x ) is 0 <x <0.9, preferably 0 <x <0.5, more preferably 0.2 <x <0.4.
본 발명은 나노 실리콘, 나노 실리콘 아산화물 및 이들의 혼합물 중에서 선택되는 나노 실리콘계 화합물-그래핀-탄소섬유 복합재를 포함하는 리튬이차전지용 음극활물질을 제공할 수 있다. The present invention can provide a negative electrode active material for a lithium secondary battery comprising a nano silicon-based compound-graphene-carbon fiber composite selected from nano silicon, nano silicon suboxide and mixtures thereof.
본 발명은 상기 나노 실리콘계 화합물-그래핀-탄소섬유 복합재를 함유한 음극활물질을 포함하는 리튬이차전지를 제공할 수 있다. The present invention can provide a lithium secondary battery comprising a negative electrode active material containing the nano-silicon compound-graphene-carbon fiber composite.
본 발명은 (a) 리튬 분말과 실리카 분말을 산소 교환 반응시켜, 나노 실리콘, 나노 실리콘 아산화물 및 이들의 혼합물 중에서 선택되는 나노 실리콘계 화합물 분말을 제조하는 단계 및 (b) 상기 제조된 나노 실리콘계 화합물 분말과, 그래핀 및 탄소섬유를 혼합하는 단계를 포함하는 나노 실리콘계 화합물-그래핀-탄소섬유 복합재를 제조하는 방법을 제공한다. The present invention comprises the steps of (a) oxygen-exchanging lithium powder and silica powder to produce a nano silicon-based compound powder selected from nano silicon, nano silicon suboxide and mixtures thereof, and (b) the nano silicon-based compound powder And, and provides a method for producing a nano-silicon compound-graphene-carbon fiber composite comprising the step of mixing the graphene and carbon fibers.
본 발명의 일 실시예에 따른 나노 실리콘계 화합물-그래핀-탄소섬유 복합재의 제조방법에 있어서, (a)단계는 제조된 나노 실리콘계 화합물 분말을 리튬 산화물로부터 분리 및 정제하는 단계를 더 포함할 수 있다.In the method of manufacturing a nano silicon-based compound-graphene-carbon fiber composite according to an embodiment of the present invention, step (a) may further include separating and purifying the prepared nano silicon-based compound powder from lithium oxide. .
본 발명의 일 실시예에 따른 나노 실리콘계 화합물-그래핀-탄소섬유 복합재의 제조방법에 있어서, (b)단계는 나노 실리콘계 화합물 분말과, 그래핀 및 탄소섬유를 각각 용매에 분산시킨 슬러리를 혼합한 다음 상기 용매를 제거한 후 건조하는 단계를 더 포함할 수 있다.In the method for producing a nano-silicon compound-graphene-carbon fiber composite according to an embodiment of the present invention, step (b) is a mixture of a nano silicon-based compound powder, a slurry of graphene and carbon fibers dispersed in a solvent, respectively After removing the solvent may further comprise the step of drying.
본 발명의 일 실시예에 따른 나노 실리콘계 화합물-그래핀-탄소섬유 복합재의 제조방법에 있어서, 실리카 분말은 퓸드 실리카, 마이크로포러스 실리카, 메조포러스 실리카 및 매크로포러스 실리카 중에서 선택되는 어느 하나 또는 둘 이상의 혼합물일 수 있다. In the method for producing a nano-silicon compound-graphene-carbon fiber composite according to an embodiment of the present invention, the silica powder is any one or a mixture of two or more selected from fumed silica, microporous silica, mesoporous silica and macroporous silica Can be.
본 발명의 일 실시예에 따른 나노 실리콘계 화합물-그래핀-탄소섬유 복합재의 제조방법에 있어서, 실리카 분말은 제한되지 않지만 예를 들면 직경이 2 ㎚ ~ 30 ㎛일 수 있다.In the method of manufacturing a nano silicon-based compound-graphene-carbon fiber composite according to an embodiment of the present invention, the silica powder is not limited, but may be, for example, 2 nm to 30 μm in diameter.
본 발명의 일 실시예에 따른 나노 실리콘계 화합물-그래핀-탄소섬유 복합재의 제조방법에 있어서, 그래핀은 특별히 제한되지 않지만 예를 들면 직경이 10㎚ ~ 5㎛일 수 있다.In the method of manufacturing a nano silicon-based compound-graphene-carbon fiber composite according to an embodiment of the present invention, graphene is not particularly limited, but may be, for example, 10 nm to 5 μm in diameter.
본 발명의 일 실시예에 따른 나노 실리콘계 화합물-그래핀-탄소섬유 복합재의 제조방법에 있어서, 탄소섬유는 특별히 제한되지 않지만 예를 들면 두께 1nm ~ 5㎛, 길이 50 ~ 200㎛일 수 있다.In the method of manufacturing a nano silicon-based compound-graphene-carbon fiber composite according to an embodiment of the present invention, the carbon fiber is not particularly limited, but may be, for example, 1 nm to 5 μm in thickness and 50 to 200 μm in length.
본 발명의 일 실시예에 따른 나노 실리콘계 화합물-그래핀-탄소섬유 복합재의 제조방법에 있어서, 리튬과 실리카(SiO2)의 몰비는 본 발명이 목적으로 하는 범위내에서 조절하여 사용할 수 있으며, 예를 들면 2 ~ 6 : 1일 수 있다.In the method for producing a nano silicon-based compound-graphene-carbon fiber composite according to an embodiment of the present invention, the molar ratio of lithium and silica (SiO 2 ) may be adjusted and used within the scope of the present invention. For example, it may be 2 to 6: 1.
본 발명의 일 실시예에 따른 나노 실리콘계 화합물-그래핀-탄소섬유 복합재의 제조방법에 있어서, (a)단계는 비활성 분위기 내에서 혼합한 후, 충분한 시간, 일 예를 들면, 1 ~ 20 시간동안 볼밀링을 실시하여 고상반응 할 수 있다.In the method for producing a nano-silicon compound-graphene-carbon fiber composite according to an embodiment of the present invention, step (a) is a sufficient time, for example, 1 to 20 hours after mixing in an inert atmosphere It is possible to perform solid state reaction by performing ball milling.
본 발명의 일 실시예에 따른 나노 실리콘계 화합물-그래핀-탄소섬유 복합재의 제조방법에 있어서, (a)단계의 산소 교환 반응은 교환반응이 충분히 진행될 수 있는 온도라면 제한되지 않으며, 예를 들면 0 ~ 300 ℃의 온도범위에서 실시할 수 있다.In the method for producing a nano-silicon compound-graphene-carbon fiber composite according to an embodiment of the present invention, the oxygen exchange reaction of step (a) is not limited as long as the exchange reaction can proceed sufficiently, for example 0 It can be carried out in the temperature range of ~ 300 ℃.
본 발명의 일 실시예에 따른 나노 실리콘계 화합물-그래핀-탄소섬유 복합재의 제조방법에 있어서, (b)단계의 탄소 섬유는 산처리를 통해 표면 산화된 것일 수 있다.In the method for producing a nano silicon-based compound-graphene-carbon fiber composite according to an embodiment of the present invention, the carbon fiber of step (b) may be surface oxidized through acid treatment.
본 발명의 일 실시예에 따른 나노 실리콘계 화합물-그래핀-탄소섬유 복합재의 제조방법에 있어서, (b)단계에서 나노 실리콘계 화합물 분말과, 그래핀 및 탄소 섬유의 혼합물의 중량혼합비는 크게 제한되는 것은 아니지만 좋게는 1 : 9 ~ 9 : 1일 수 있다.In the method for producing a nano silicon-based compound-graphene-carbon fiber composite according to an embodiment of the present invention, the weight mixing ratio of the nano silicon-based compound powder and the mixture of graphene and carbon fiber in step (b) is greatly limited. But preferably it may be 1: 9-9: 1.
본 발명의 일 실시예에 따른 나노 실리콘계 화합물-그래핀-탄소섬유 복합재의 제조방법에 있어서, (b)단계에서 그래핀 및 탄소 섬유는 크게 제한되는 것은 아니지만 좋게는 중량혼합비가 1 : 10 ~ 10 : 1일 수 있다. In the method for producing a nano-silicon compound-graphene-carbon fiber composite according to an embodiment of the present invention, the graphene and carbon fibers in step (b) is not significantly limited, but preferably a weight mixing ratio of 1: 10 to 10 May be one.
본 발명의 일 실시예에 따른 나노 실리콘계 화합물-그래핀-탄소섬유 복합재의 제조방법에 있어서, (b)단계는 크게 제한되지 않지만 예를 들면 0 ~ 100℃에서 실시할 수 있다.In the method for producing a nano silicon-based compound-graphene-carbon fiber composite according to an embodiment of the present invention, step (b) is not particularly limited, but may be performed at, for example, 0 to 100 ° C.
본 발명의 일 실시예에 따른 나노 실리콘계 화합물-그래핀-탄소섬유 복합재에 있어서, 탄소 섬유는 통상의 탄소섬유라면 크게 제한되지 않으며, 예를 들면 카본파이버, 단일벽 탄소나노튜브, 다중벽 탄소나노튜브 및 탄소나노와이어 중에서 선택되는 어느 하나일 수 있으며 이를 개질한 것일 수도 있다.In the nano-silicon compound-graphene-carbon fiber composite according to an embodiment of the present invention, the carbon fiber is not particularly limited as long as the conventional carbon fiber, for example, carbon fiber, single-walled carbon nanotubes, multi-walled carbon nano It may be any one selected from a tube and carbon nanowires and may be modified.
본 발명은 상기의 제조방법으로 제조되는 나노 실리콘계 화합물-그래핀-탄소섬유 복합재를 제공할 수 있다.The present invention can provide a nano-silicon compound-graphene-carbon fiber composite prepared by the above production method.
본 발명은 저가의 실리카를 이용하여 나노 실리콘계 화합물 분말을 합성하여 비용을 절감하면서 동시에 이차전지 전기화학적 특성을 향상시킬 수 있는 나노 실리콘계 화합물-그래핀-탄소섬유 복합재 및 이를 포함하는 리튬이차전지용 음극활물질을 제공할 수 있다.The present invention is a nano silicon compound-graphene-carbon fiber composite and a negative electrode active material for lithium secondary battery comprising the same to synthesize a nano silicon compound powder using a low-cost silica and at the same time reduce the cost and improve the secondary battery electrochemical properties Can be provided.
또한, 본 발명은 반응공정이 단순하여 생산성 및 경제성이 뛰어나고 환경친화적인 나노 실리콘계 화합물-그래핀-탄소섬유 복합재의 제조방법을 제공할 수 있는 이점이 있다. In addition, the present invention has the advantage of providing a method for producing a nano-silicon compound-graphene-carbon fiber composite having excellent productivity, economical efficiency and environment-friendly simple reaction process.
또한, 본 발명은 다양한 종류의 실리카를 사용할 수 있으며, 그래핀과 탄소섬유의 물리적 특성과 함량을 제어함으로써 나노 실리콘계 화합물-그래핀-탄소섬유 복합재의 입경, 기공도, 전기전도도를 이차전지용 음극에 최적화하여 적용할 수 있는 장점이 있다.In addition, the present invention can use a variety of silica, by controlling the physical properties and content of the graphene and carbon fiber to the particle size, porosity, electrical conductivity of the nano-silicon compound-graphene-carbon fiber composite to the anode for secondary batteries There is an advantage that can be optimized and applied.
도 1은 본 발명의 일 실시예에서 나노 실리카로부터 얻은 나노 실리콘 분말의 TEM 이미지와 전자회절패턴을 나타낸 것이다.
도 2는 본 발명의 일 실시예에서 나노 실리콘-그래핀-탄소섬유 복합재 분말의 TEM 이미지를 나타낸 것이다.
도 3은 본 발명의 일 실시예에 따른 나노 실리콘 복합재 음극을 포함하는 리튬이차전지의 정전압순환곡선을 나타낸 그래프이다.
도 4는 본 발명의 일 실시예에 따른 나노 실리콘- 그래핀-카본섬유 복합재 음극의 충방전 프로파일을 나타낸 그래프이다.
도 5는 본 발명의 일 실시예에 따른 나노 실리콘- 그래핀-카본섬유 복합재 음극의용량 프로파일을 나타낸 그래프이다.
도 6은 본 발명의 일 실시예에 따른 나노 실리콘-그래핀-카본섬유 복합재 음극과 실리콘 음극의 싸이클 성능 비교를 나타낸 그래프이다.
도 7은 본 발명의 일 실시예 의해 제조된 나노 실리콘 아산화물(SiO0 .37) 분말의 TEM 이미지와 elemental mapping 이미지를 나타낸 것이다.
도 8는 본 발명의 일 실시예에 따른 나노 실리콘 아산화물(SiO0 .37)- 그래핀-카본섬유 복합재 음극의 용량 프로파일을 나타낸 그래프이다.1 illustrates a TEM image and an electron diffraction pattern of a nano silicon powder obtained from nano silica in an embodiment of the present invention.
Figure 2 shows a TEM image of the nano silicon-graphene-carbon fiber composite powder in one embodiment of the present invention.
3 is a graph showing a constant voltage circulation curve of a lithium secondary battery including a nano silicon composite anode according to an embodiment of the present invention.
Figure 4 is a graph showing the charge and discharge profile of the nano silicon-graphene-carbon fiber composite anode according to an embodiment of the present invention.
Figure 5 is a graph showing the capacity profile of the nano silicon-graphene-carbon fiber composite anode according to an embodiment of the present invention.
6 is a graph showing a cycle performance comparison between the nano silicon-graphene-carbon fiber composite anode and the silicon anode according to an embodiment of the present invention.
7 shows the TEM image and elemental mapping images of the nano-silicon suboxide (SiO 0 .37) powders prepared by one example embodiment of the present invention.
Figure 8 is nano-silicon suboxide (SiO 0 .37) in accordance with one embodiment of the present invention - a graph showing the dose profile of the carbon fiber composite cathode-graphene.
이하 본 발명의 나노 실리콘계 화합물-그래핀-탄소섬유 복합재, 리튬이차전지용 음극활물질, 이의 제조방법 및 이를 포함하는 리튬이차전지를 상세히 설명한다. 다음에 소개되는 실시예들은 당업자에게 본 발명의 사상이 충분히 전달될 수 있도록 하기 위해 예로서 제공되는 것이다. 또한, 사용되는 기술 용어 및 과학 용어에 있어서 다른 정의가 없다면, 이 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 통상적으로 이해하고 있는 의미를 가지며, 하기의 설명 및 첨부 도면에서 본 발명의 요지를 불필요하게 흐릴 수 있는 공지 기능 및 구성에 대한 설명은 생략한다.Hereinafter, the nano-silicon compound-graphene-carbon fiber composite of the present invention, a negative electrode active material for a lithium secondary battery, a manufacturing method thereof, and a lithium secondary battery including the same will be described in detail. The following embodiments are provided by way of example so that those skilled in the art can fully understand the spirit of the present invention. Further, it is to be understood that, unless otherwise defined, technical terms and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs. Descriptions of known functions and configurations that may be unnecessarily blurred are omitted.
본 발명의 발명자들은 리튬이차전지용 음극활물질을 개발하기 위하여 연구한결과, 나노 실리콘, 나노 실리콘 아산화물 및 이들의 혼합물 중에서 선택되는 나노 실리콘계 화합물과 그래핀 및 탄소섬유를 포함하여 제조되는 나노 실리콘계 화합물-그래핀-탄소섬유 복합재를 제공하여, 놀랍게도 이를 포함하는 리튬이차전지용 음극활물질의 비용을 절감하면서 동시에 리튬이차전지의 전기화학적인 특성을 획기적으로 향상시킬 수 있음을 발견하여 본 발명을 완성하였다.The inventors of the present invention have studied to develop a negative electrode active material for a lithium secondary battery, and as a result, a nano silicon compound prepared from nano silicon compound selected from nano silicon, nano silicon suboxide and mixtures thereof, and graphene and carbon fiber- The present invention was completed by providing a graphene-carbon fiber composite material, surprisingly reducing the cost of a negative electrode active material for a lithium secondary battery including the same, and significantly improving the electrochemical characteristics of the lithium secondary battery.
본 발명은 나노 실리콘, 나노 실리콘 아산화물 및 이들의 혼합물 중에서 선택되는 나노 실리콘계 화합물과 그래핀 및 탄소섬유를 포함하여 제조되는 나노 실리콘계 화합물-그래핀-탄소섬유 복합재를 제공할 수 있다. 이때, 상기 나노 실리콘은 나노 크기의 실리콘(Si)이며, 나노 실리콘 아산화물은 SiOx에서 x의 범위가 0 < x < 0.9, 좋게는 0 < x < 0.5, 더욱 바람직하게는 0.2 < x < 0.4일 수 있다. 상기 범위에서는 전극의 전기전도도가 더욱 우수하고, 리튬이차전지의 충방전 가역성 및 용량이 매우 우수한 특성이 있어서 좋다. The present invention can provide a nano-silicon compound-graphene-carbon fiber composite prepared from nano silicon-based compound selected from nano silicon, nano silicon suboxide, and mixtures thereof, and graphene and carbon fiber. In this case, the nano silicon is a nano-sized silicon (Si), the nano silicon suboxide is SiO x to x in the range of 0 <x <0.9, preferably 0 <x <0.5, more preferably 0.2 <x <0.4 Can be. In the above range, there is a characteristic that the electrode has more excellent electrical conductivity, and has very excellent charge / discharge reversibility and capacity of the lithium secondary battery.
본 발명은 상기 나노 실리콘계 화합물-그래핀-탄소섬유 복합재를 포함하는 리튬이차전지용 음극활물질을 제공할 수 있다. The present invention can provide a negative electrode active material for a lithium secondary battery comprising the nano-silicon compound-graphene-carbon fiber composite.
본 발명은 상기 나노 실리콘계 화합물-그래핀-탄소섬유 복합재를 함유한 음극활물질을 포함하는 리튬이차전지를 제공할 수 있다. The present invention can provide a lithium secondary battery comprising a negative electrode active material containing the nano-silicon compound-graphene-carbon fiber composite.
본 발명은 (a) 리튬 분말과 실리카 분말을 산소 교환 반응시켜, 나노 실리콘, 나노 실리콘 아산화물 및 이들의 혼합물 중에서 선택되는 나노 실리콘계 화합물 분말을 제조하는 단계 및 (b) 상기 제조된 나노 실리콘계 화합물 분말과, 그래핀 및 탄소섬유를 혼합하는 단계를 포함하는 나노 실리콘계 화합물-그래핀-탄소섬유 복합재를 제조하는 방법을 제공한다. The present invention comprises the steps of (a) oxygen-exchanging lithium powder and silica powder to produce a nano silicon-based compound powder selected from nano silicon, nano silicon suboxide and mixtures thereof, and (b) the nano silicon-based compound powder And, and provides a method for producing a nano-silicon compound-graphene-carbon fiber composite comprising the step of mixing the graphene and carbon fibers.
구체적으로, 본 발명의 나노 실리콘계 화합물-그래핀-탄소섬유 복합재 제조방법은 리튬 분말과 실리카(SiO2) 분말을 반응시켜 실리카의 산소가 리튬으로 전달되는 산소 교환반응(single displacement)이 이루어지도록 하여 나노 실리콘계 화합물 분말을 생성하고, 이후, 생성된 나노 실리콘계 화합물 분말, 그래핀 및 탄소섬유를 균일하게 혼합하는 것을 포함할 수 있다.Specifically, the nano-silicon compound-graphene-carbon fiber composite manufacturing method of the present invention by reacting the lithium powder and silica (SiO 2 ) powder to the oxygen displacement reaction (single displacement) to transfer the oxygen of the silica to lithium The nano silicon-based compound powder may be generated, and then, the resulting nano silicon-based compound powder, graphene, and carbon fibers may be uniformly mixed.
상기 나노 실리콘계 화합물 분말은 나노 실리콘, 나노 실리콘 아산화물 및 이들의 혼합물 중에서 선택되는 어느 하나일 수 있다. The nano silicon-based compound powder may be any one selected from nano silicon, nano silicon suboxide, and mixtures thereof.
상기 나노 실리콘계 화합물-그래핀-탄소섬유 복합재 제조방법에 있어서, 나노 실리콘계 화합물 분말이 나노 실리콘(Si)일 경우 반응식은 하기 반응식 1과 같다.
In the nano-silicon compound-graphene-carbon fiber composite manufacturing method, when the nano-silicon compound powder is nano silicon (Si), the reaction scheme is shown in
4 Li + SiO2 → Si + 2Li2O (반응식 1)
4 Li + SiO 2 → Si + 2Li 2 O (Scheme 1)
즉, 상기 나노 실리콘은 리튬 금속 분말이 산화리튬으로 산화되면서 실리카를 환원시켜 생성된다. That is, the nano silicon is produced by reducing silica while lithium metal powder is oxidized to lithium oxide.
상기 나노 실리콘계 화합물-그래핀-탄소섬유 복합재 제조방법에 있어서, 나노 실리콘계 화합물 분말이 나노 실리콘 아산화물(SiOx)일 경우 반응식은 하기 반응식 2와 같다. In the nano-silicon compound-graphene-carbon fiber composite manufacturing method, when the nano-silicon compound powder is nano silicon suboxide (SiO x ), the reaction scheme is shown in
이때, 나노 실리콘 아산화물(SiOx) 분말은 실리카가 불완전 환원되어 형성되는 것으로, 상기 실리콘 아산화물(SiOx)에서 x는 0 < x < 0.9, 좋게는 0 < x < 0.5, 더욱 바람직하게는 0.2 < x < 0.4일 수 있다. 상기 실리콘 아산화물 나노 분말은 리튬 분말과 실리카 분말의 산소 교환반응 시간이나 리튬과 실리카의 몰비를 조절하여 환원이 충분히 이루어지지 않게 함으로써 일부 산소가 잔류하여 아산화물이 형성될 수 있다. 일예로, 리튬 분말과 실리카 분말의 볼밀 공정을 3시간 이내로 하거나, 실리카와 반응하는 리튬이 4몰 이하인 경우에 실리카 환원이 충분히 이루어지지 않아 아산화물을 형성할 수 있다.
In this case, the nano silicon suboxide (SiO x ) powder is formed by incomplete reduction of silica, x in the silicon suboxide (SiO x ) is 0 <x <0.9, preferably 0 <x <0.5, more preferably 0.2 <x <0.4. The silicon nitrous nanopowder may be partially formed by remaining oxygen by adjusting the oxygen exchange reaction time of the lithium powder and the silica powder or by reducing the molar ratio of the lithium and silica so that some oxygen remains. For example, when the ball mill process of the lithium powder and the silica powder is within 3 hours, or when lithium reacted with silica is 4 mol or less, silica reduction may not be sufficiently performed to form a suboxide.
(4-2x) Li + SiO2 → (2-x) Li2O + SiOx (반응식 2)
(4-2x) Li + SiO 2 → (2-x) Li 2 O + SiO x (Scheme 2)
본 발명에서 사용되는 실리카(SiO2) 분말은 퓸드 실리카(fumed silica), 마이크로포러스 실리카(microporous silica), 메조포러스 실리카(mesoporous silica) 및 매크로포러스 실리카(macroporous silica) 중에서 선택되는 어느 하나 또는 둘 이상의 혼합물일 수 있으며, 실리카의 종류, 크기 또는 기공 크기에 제한되지 않고 사용될 수 있다. The silica (SiO 2 ) powder used in the present invention is any one or two or more selected from fumed silica, microporous silica, mesoporous silica and macroporous silica. It can be a mixture, and can be used without being limited to the type, size or pore size of silica.
상기 실리카 분말은 바람직하게는 2 ㎚ ~ 30 ㎛의 직경인 것을 사용할 수 있으며, 더욱 바람직하게는 10 ㎚ ~ 100 ㎚인 것을 사용할 수 있다. 실리카 분말의 입경이 상기 범위를 초과하면 리튬확산이 용이하지 않을 수 있으며, 미만이면 높은 비표면적과 표면에너지로 인해 입자 뭉침 현상이 일어나 음극 제조시 요구되는 입자 분산력이 떨어질 수 있다. Preferably, the silica powder may be used having a diameter of 2 nm to 30 μm, and more preferably 10 nm to 100 nm. If the particle diameter of the silica powder exceeds the above range, lithium diffusion may not be easy. If the particle diameter is smaller than the particle size, the particle dispersing force required for the production of the negative electrode may be reduced due to the high specific surface area and surface energy.
상기 그래핀은 직경이 10 ㎚ ~ 5 ㎛인 것을 사용할 수 있으며, 상기 탄소섬유는 두께가 1nm ~ 5㎛, 길이 50 ~ 200 ㎛인 것을 사용할 수 있다. 또한 상기 탄소 섬유는 카본 파이버(carbon fiber), 단일벽 탄소 나노튜브(SWCNT), 다중벽 탄소 나노튜브(MWCNT) 및 탄소 나노와이어(carbon nanowire) 중에서 선택되는 어느 하나일 수 있다. The graphene may be used having a diameter of 10 nm ~ 5 ㎛, the carbon fiber may be used having a thickness of 1 nm ~ 5 ㎛, length 50 ~ 200 ㎛. In addition, the carbon fiber may be any one selected from carbon fiber, single-walled carbon nanotubes (SWCNT), multi-walled carbon nanotubes (MWCNT), and carbon nanowires.
상기 리튬과 실리카(SiO2)의 몰비는 2 ~ 6 : 1 일 수 있으며, 리튬이 6보다 큰 비율을 가지게 되면 반응 후 남는 리튬을 제거하기 위해 사용되는 산의 양 증가와 폐수 증가 결과를 얻을 수 있고, 2보다 작은 비율일 경우 산소 함량이 높은 산화물 (SiOy, 1<y<2)이 얻어져 리튬이차전지의 충방전 가역성 및 용량이 감소하는 결과를 얻을 수 있다. The molar ratio of the lithium and silica (SiO 2 ) may be 2 to 6: 1, and when lithium has a ratio greater than 6, an increase in the amount of acid used to remove lithium remaining after the reaction and an increase in wastewater may be obtained. In addition, when the ratio is less than 2, an oxide having a high oxygen content (SiO y , 1 <y <2) is obtained, thereby reducing the charge and discharge reversibility and capacity of the lithium secondary battery.
상기 나노 실리콘계 화합물 분말을 형성하는 단계는 일예로, 리튬 분말과 실리카 분말을 글러브 박스 내에서 혼합한 후 1 내지 20시간동안 볼밀링을 수행하여 실시할 수 있다. 이때, 글러브박스는 질소 또는 아르곤과 같은 비활성 기체 분위기일 수 있으며, 상기 리튬과 실리카의 볼밀을 통한 산소 교환반응 온도는 0 ~ 300℃일 수 있다. 상기 반응온도가 300℃ 초과이면 입자크기가 크고 작은 불균일한 입자들이 얻어질 수 있어 바람직하지 않으며, 0℃ 미만이면 산소의 교환반응속도가 낮아질 수 있다. The forming of the nano silicon-based compound powder may be performed by, for example, mixing the lithium powder and the silica powder in a glove box and performing ball milling for 1 to 20 hours. At this time, the glove box may be an inert gas atmosphere such as nitrogen or argon, the oxygen exchange reaction temperature through the ball mill of the lithium and silica may be 0 ~ 300 ℃. If the reaction temperature is more than 300 ℃ non-uniform particles of large and small particle size can be obtained is not preferable, if less than 0 ℃ the exchange reaction rate of oxygen can be lowered.
본 발명에서 상기 나노 실리콘계 화합물 분말을 제조하는 단계 이후에, 제조된 나노 실리콘계 화합물 분말을 리튬 산화물로부터 분리 및 정제하는 공정을 더 포함할 수 있다. After the step of preparing the nano-silicon compound powder in the present invention, the prepared nano-silicon compound powder may further comprise the step of separating and purifying from the lithium oxide.
상기 분리 및 정제 공정은 산처리를 통해 부반응물인 리튬산화물을 제거하는 단계를 포함할 수 있다. 얻어진 리튬산화물은 하기 반응식 3 및 4과 같이 산과 반응하여 염화리튬(LiCl)이 생성된다.
The separation and purification process may include the step of removing the lithium oxide as a side reaction through acid treatment. The obtained lithium oxide is reacted with an acid as in Schemes 3 and 4 to produce lithium chloride (LiCl).
Li2O + H2O → 2LiOH (반응식 3)Li 2 O + H 2 O → 2LiOH (Scheme 3)
Li2O + 2HCl → 2LiCl + H2O (반응식 4)
Li 2 O + 2HCl → 2LiCl + H 2 O (Scheme 4)
산처리 공정에서 사용되는 산의 종류는 황산, 염산, 질산, 인산 등 무기산이 사용될 수 있으며, 이에 제한되지 않는다. The acid used in the acid treatment process may be inorganic acids such as sulfuric acid, hydrochloric acid, nitric acid, phosphoric acid, and the like.
상기 산처리 후 물, 에탄올, 이소프로판올 및 이들의 혼합 용매로 산처리 후의 생성물을 수차례 세척하여 최종적으로 얻어지는 나노 실리콘계 화합물 분말을 건조한다. After the acid treatment, the product obtained after the acid treatment is washed several times with water, ethanol, isopropanol and a mixed solvent thereof to finally dry the nano silicon-based compound powder.
본 발명에서 상기 나노 실리콘계 화합물 분말, 그래핀 및 탄소섬유를 혼합하는 공정은 나노 실리콘계 화합물 분말과, 그래핀 및 탄소섬유를 각각 용매에 분산시킨 슬러리를 혼합한 다음 상기 용매를 제거하고 이를 건조하는 공정을 추가로 포함할 수 있다. In the present invention, the process of mixing the nano silicon-based compound powder, graphene and carbon fiber is a process of mixing the nano silicon-based compound powder, a slurry of graphene and carbon fibers dispersed in a solvent and then removing the solvent and drying it It may further include.
상기 용매는 나노 실리콘계 화합물 분말, 그래핀 및 탄소섬유를 균일하게 분산시킬 수 있는 것이면 어느 것을 사용해도 좋으며, 바람직하게는 탄소수 1 ~ 5의 알코올, 물 또는 이들의 혼합물 중에서 선택되는 어느 하나일 수 있다. The solvent may be any one as long as it can uniformly disperse the nano silicon-based compound powder, graphene and carbon fiber, and preferably may be any one selected from alcohols having 1 to 5 carbon atoms, water or mixtures thereof. .
상기 탄소 섬유는 산 처리를 통해 표면산화를 유도하여 분산성을 향상시킬 수 있다. 이때, 산은 황산, 염산, 질산, 인산 등 무기산 또는 카르복실기를 가진 유기산을 사용할 수 있다.The carbon fiber may improve surface dispersibility by inducing surface oxidation through acid treatment. At this time, the acid may be an inorganic acid such as sulfuric acid, hydrochloric acid, nitric acid, phosphoric acid or an organic acid having a carboxyl group.
상기 산처리 후 물, 에탄올, 이소프로판올 및 이들의 혼합 용매로 산처리 후의 생성물을 수차례 세하여 건조하는 단계를 더 포함할 수 있다.After the acid treatment, water, ethanol, isopropanol and a mixed solvent thereof may further comprise the step of drying the product after the acid treatment several times.
본 발명에서 나노 실리콘계 화합물 분말과 그래핀 및 탄소섬유의 혼합 중량비는 1/9 ~ 9/1 일수 있다. 상기 범위 초과이면 나노 실리콘계 화합물 분말에 그래핀과 탄소섬유를 혼합한 효과가 미미하며, 미만이면 전기화학적 활성을 가지는 실리콘 함량이 낮아지고 용량이 떨어질 수 있다. In the present invention, the mixed weight ratio of the nano silicon-based compound powder and graphene and carbon fiber may be 1/9 to 9/1. If the range is greater than the above range, the effect of mixing graphene and carbon fiber in the nano silicon-based compound powder is insignificant, and if less, the silicon content having electrochemical activity may be lowered and the capacity may be decreased.
상기 그래핀 및 탄소섬유의 중량혼합비는 1/10 ~ 10/1일 수 있으며, 나노 실리콘계 화합물 분말과 그래핀 및 탄소섬유를 균일하게 혼합하고 분산시키는 단계는 0 ~ 100 ℃에서 실시될 수 있다. The weight mixing ratio of the graphene and carbon fibers may be 1/10 to 10/1, and uniformly mixing and dispersing the nano silicon-based compound powder and graphene and carbon fibers may be performed at 0 to 100 ° C.
본 발명은 상기 제조방법에 의해 얻어지는, 나노 실리콘계 화합물-그래핀-탄소섬유 복합재 및 이를 음극활물질로서 포함하는 리튬이차전지를 제공할 수 있다.The present invention can provide a nano-silicon compound-graphene-carbon fiber composite material obtained by the above production method and a lithium secondary battery comprising the same as a negative electrode active material.
본 발명에 따른 리튬이차전지의 일 양태로서, 양극활물질은 Li(Mn, Ni, Co)O2계, LiMn2 - xMxO4 (M=Li, Al, Zn, Zr, Cr, Co, Ni, Fe) 스피넬계, LiMPO4 (M=Fe, Mn, Co, Ni) 중에서 선택되는 어느 하나를 포함하며, 전해질로서 LiPF6 리튬염과 비수용성 카보네이트계 용매를 포함할 수 있다. In one embodiment of the lithium secondary battery according to the present invention, the positive electrode active material is Li (Mn, Ni, Co) O 2 system, LiMn 2 - x M x O 4 (M = Li, Al, Zn, Zr, Cr, Co, Ni, Fe) spinel-based, LiMPO 4 (M = Fe, Mn, Co, Ni) containing any one selected from, may include LiPF 6 lithium salt and a water-insoluble carbonate solvent.
본 발명은 양극, 음극 및 분리막을 포함하는 리튬 이차 전지에 있어서, 상기 음극은 (ⅰ) 금속재질의 집전체; 및 (ⅱ) 상기 집전체에 도포되는 음극 활물질로서 상기 나노 실리콘계 화합물-그래핀-탄소섬유 복합재를 포함하는 리튬 이차 전지를 제공할 수 있다.
The present invention provides a lithium secondary battery comprising a positive electrode, a negative electrode and a separator, wherein the negative electrode comprises: (i) a current collector made of metal; And (ii) it can provide a lithium secondary battery comprising the nano-silicon compound-graphene-carbon fiber composite as a negative electrode active material applied to the current collector.
이하 본 발명에 따른 나노 실리콘계 화합물-그래핀-탄소섬유 복합재의 제조방법을 바람직한 일 실시예를 통해 설명하고자 한다.
Hereinafter, a method for preparing a nano-silicon compound-graphene-carbon fiber composite according to the present invention will be described through a preferred embodiment.
(실시예 1) 산소 치환 고상반응에 의한 나노 실리카로부터 나노 실리콘 분말의 제조와 나노 실리콘-그 래핀 -카본섬유 복합재 제조 Example 1 Preparation of Nano Silicon Powders and Nano Silicon- Graphene -Carbon Fiber Composites from Nano Silica by Oxygen Substitution Solid Phase Reaction
실리카(SiO2, 평균입경 15㎚) 분말과 리튬 금속 분말(평균입경 25㎛)을 1 : 4 몰비로 아르곤 분위기, 상온(25℃)에서 혼합한 후, 상온에서 6시간동안 볼밀링하며 고상(solid-state) 반응시켜 산소 치환반응을 유도하였다. Silica (SiO 2 , 15 nm average particle diameter) powder and lithium metal powder (average particle diameter 25 μm) were mixed in an argon atmosphere at room temperature (25 ° C.) in a 1: 4 molar ratio, and then ball milled at room temperature for 6 hours to obtain a solid phase ( solid-state reaction to induce oxygen substitution.
부반응물인 리튬산화물과 합성된 실리콘 분말을 분리하기 위해 리튬산화물을 0.5M 염산 용액으로 세척하고, 에탄올과 1M HCl 수용액의 혼합용액(에탄올과 1M HCl 수용액의 혼합비율 1:1)으로 순차적으로 씻어냈다.Lithium oxide was washed with 0.5 M hydrochloric acid solution to separate side reactions of lithium oxide and synthesized silicon powder, and sequentially washed with a mixed solution of ethanol and 1M HCl solution (mixture ratio of ethanol and 1M HCl solution 1: 1). Paid.
상기 공정으로, 하기 식 1 및 2와 같이 산과 리튬산화물이 반응하여 물에 용해하기 쉬운 LiCl 염이 생성되었다. In the above process, LiCl salt, which is easily soluble in water, was formed by reacting acid and lithium oxide as shown in
이후, 물로 수차례 세척하여 LiCl을 제거한 다음, 최종적으로 수득한 짙은 갈색의 나노 실리콘 분말(SiO, 평균입경 50 nm)을 진공오븐에서 건조하였다.After washing several times with water to remove LiCl, the finally obtained dark brown nano silicon powder (SiO, average particle diameter: 50 nm) was dried in a vacuum oven.
도 1은 본 발명의 나노 실리카로부터 얻은 나노 실리콘(SiO) 분말의 TEM 이미지와 전자회절패턴을 나타낸 것이다. 약 50 nm의 직경을 가지는 구상형의 나노 실리콘 분말의 1차 입자가 관찰되며, 전자회절패턴에서 특정 링(ring) 모양 또는 규칙적인 전자배열이 관찰되지 않으므로, 제조된 실리콘 분말은 비정질임을 확인할 수 있었다. Figure 1 shows the TEM image and electron diffraction pattern of the nano silicon (SiO) powder obtained from the nano-silica of the present invention. Primary particles of spherical nano silicon powder having a diameter of about 50 nm are observed, and since no specific ring shape or regular electron arrangement is observed in the electron diffraction pattern, it can be confirmed that the manufactured silicon powder is amorphous. there was.
상기 제조된 나노 실리콘 분말 100mg을 물 100㎖에 균일하게 분산하고, 그래핀 분말(평균입경 2.5㎛) 50mg 및 카본섬유 분말(두께 100nm) 50mg을 물 200㎖에 분산시킨 슬러리를 상기 물에 분산된 나노 실리콘 분말 용액과 혼합한 후. 초음파를 이용해 분산하여 복합재 분산용액을 제조하였다. 이때, 복합재 분산용액은 50 : 25 : 25 wt% 비율을 가지는 나노 실리콘-그래핀-카본섬유 복합재를 포함한다. 즉, 나노 실리콘/(그래핀+탄소섬유) 무게비가 1/1이며, 그래핀/카본섬유 무게비도 1/1인 분말액을 제조한다. 다음으로, 원심분리를 통하여 물을 제거하고 진공오븐에서 건조시킴으로써 실리콘 복합재 음극활물질을 얻었다. The slurry of 100 mg of the prepared nano silicon powder was uniformly dispersed in 100 ml of water, and 50 mg of graphene powder (average particle diameter: 2.5 μm) and 50 mg of carbon fiber powder (thickness of 100 nm) were dispersed in 200 ml of water. After mixing with nano silicon powder solution. Dispersion was performed using ultrasonic waves to prepare a composite dispersion solution. At this time, the composite dispersion solution includes a nano silicon-graphene-carbon fiber composite having a ratio of 50:25:25 wt%. That is, the nano silicon / (graphene + carbon fiber) weight ratio is 1/1, and the graphene / carbon fiber weight ratio is 1/1 to prepare a powder solution. Next, water was removed through centrifugation and dried in a vacuum oven to obtain a silicon composite anode active material.
도 2는 나노 실리콘-그래핀-카본섬유 복합재 분말의 TEM 이미지를 나타낸 것이다. 실리콘 복합재 음극활물질을 이루고 있는 세가지 성분이 균일하게 혼합되어 있고 입자간 접촉이 양호함을 확인할 수 있었다.
Figure 2 shows a TEM image of the nano silicon-graphene-carbon fiber composite powder. Three components constituting the silicon composite anode active material were uniformly mixed and good contact between particles was confirmed.
(실시예 2) 실시예 1의 나노 실리콘- 그래핀 -카본섬유 음극활물질로 이루어진 음극을 포함하는 리튬이차전지의 전기화학적 특성 조사 Example 2 Investigation of electrochemical characteristics of a lithium secondary battery including a negative electrode made of the nano silicon- graphene -carbon fiber negative electrode active material of Example 1
실시예 1에서 나노 실리카로부터 제조한 나노 실리콘-그래핀-카본섬유 복합재 음극활물질 : 카본 도전재(super P) : 폴리아크릴산(polyacrylic acid) 바인더의 중량비를 75 : 15 : 10 (wt%)로 혼합하여 음극을 제조하였다. 이때, 폴리아크릴산을 NMP(N-methyl pyrrolidinone)에 용해하여 바인더 용액을 준비한 후, 여기에 실리콘 복합재 음극활물질 및 카본 도전재(super P)를 넣어 음극 코팅용 슬러리를 제조하였다. 상기 슬러리를 구리 집전체 포일위에 통상의 방법으로 코팅하였다. 다음으로, 진공 오븐을 이용하여 110℃에서 12시간 동안 건조하였다. 건조 후 40 kg/㎠의 압력이 유지되는 롤 프레스(roll press)에 통과시켜 음극을 제작하였다. Nano silicon-graphene-carbon fiber composite material prepared from nano silica in Example 1 negative electrode active material: carbon conductive material (super P): polyacrylic acid (polyacrylic acid) binder in a weight ratio of 75: 15: 10 (wt%) To prepare a negative electrode. In this case, after preparing a binder solution by dissolving polyacrylic acid in NMP (N-methyl pyrrolidinone), a silicon composite negative electrode active material and a carbon conductive material (super P) were added thereto to prepare a slurry for negative electrode coating. The slurry was coated on a copper current collector foil in a conventional manner. Next, it was dried for 12 hours at 110 ℃ using a vacuum oven. After drying, a negative electrode was prepared by passing through a roll press maintained at a pressure of 40 kg /
리튬셀은 리튬 메탈을 상대전극 및 기준전극으로 하고, 제조된 실리콘 음극을 작업 전극으로 사용하였다. 전해액으로 1M LiPF6이 녹아 있는 에틸렌 카보네이트 (EC) 및 에틸메틸 카보네이트 (EMC)의 혼합용액(혼합액 비율 3:7)에 실란 첨가제(tris(2-mehtoxyethoxy) vinylsilane) 5wt%이 되도록 하여 제작하였다. The lithium cell used lithium metal as a counter electrode and a reference electrode, and the prepared silicon anode was used as a working electrode. The silane additive (tris (2-mehtoxyethoxy) vinylsilane) was added in a mixed solution (mixture ratio 3: 7) of ethylene carbonate (EC) and ethylmethyl carbonate (EMC) in which 1M LiPF 6 was dissolved as an electrolyte.
나노 실리콘-그래핀-카본섬유 복합재를 함유한 음극을 포함하는 리튬이차전지의 정전압순환곡선을 0.05 ~ 1.5 vs. Li/Li+ 전위구간에서 0.1 mV/s sweep rate로 측정하여 도 3에 나타내었다. The constant voltage cycling curve of a lithium secondary battery including a negative electrode containing a nano silicon-graphene-carbon fiber composite was 0.05 to 1.5 vs. It is shown in Figure 3 by measuring at 0.1 mV / s sweep rate in the Li / Li + potential range.
Cathodic process(충전, 리튬삽입)에서 관찰되는 약 0.2 V의 피크는 비정질 실리콘으로 리튬삽입이 일어나는 프로세스이고, anodic process(방전, 리튬탈착)에서 관찰되는 약 0.3 V의 피크는 LixSi 비정질 실리콘으로부터 리튬 탈착에 의한 것이고, 약 0.5 V의 피크는 Li15Si4 상으로부터 리튬이 탈착되어 실리콘이 재생성되는 프로세스에 의한 것이다. 본 발명의 일 실시예에 따른 나노 실리콘-그래핀-카본섬유 복합재가 리튬셀에서 전기화학적으로 활성을 보이며 가역적으로 리튬의 삽입-탈착이 일어남을 알 수 있다. The peak of about 0.2 V observed in the cathodic process is the process of lithium insertion into amorphous silicon and the peak of about 0.3 V observed in the anodic process (discharge, lithium desorption) is from Li x Si amorphous silicon. This is due to lithium desorption and the peak of about 0.5 V is due to the process in which lithium is desorbed from the Li 15 Si 4 phase to regenerate the silicon. Nano silicon-graphene-carbon fiber composite according to an embodiment of the present invention shows an electrochemical activity in the lithium cell, it can be seen that the insertion-desorption of lithium reversibly.
다음으로, 나노 실리콘-그래핀-카본섬유 복합재 음극의 충방전 프로파일을 살펴보면, 150 ㎂/㎠ 전류밀도 (약 0.02C 에 해당)로 0.1 - 1.5 V vs. Li/Li+ 구간에서 정전류-정전압 (CC-CV) 방식으로 충전과 방전을 실시하였다. 도 4는 이에 따른 충방전 프로파일을 나타낸 것으로서, 비정질 실리콘으로의 리튬 삽입, 탈착 반응에 의한 LixSi 형성에 의한 평탄면을 확인할 수 있었다. Next, looking at the charge-discharge profile of the nano silicon-graphene-carbon fiber composite anode, 0.1-1.5 V vs. 150 ㎂ / ㎠ current density (corresponding to about 0.02C). Charge / discharge was performed in a constant current-constant voltage (CC-CV) manner in the Li / Li + region . Figure 4 shows the charge and discharge profile accordingly, it was confirmed that the flat surface by the Li x Si formation by lithium insertion, desorption reaction into amorphous silicon.
또한, 음극의 용량 (capacity)을 무게당 용량 (specific gravimetric capacity)으로 환산한 결과를 도 5에 나타내었다. In addition, the results of converting the capacity (catacity) of the negative electrode into a specific gravimetric capacity is shown in FIG.
본 발명의 일 실시예에 따른 나노 실리콘-그래핀-카본섬유 복합재를 포함하는 음극은 초기 충전(리튬 삽입) 용량은 1700 mAh/g, 초기 방전(리튬 탈착) 용량은 606 mAh/g로서, 초기 효율은 약 36 %이나, 5회 이후 20 싸이클까지 734 ~ 635 mAh/g의 방전용량과 약 95 % 이상의 효율을 유지하였다. The negative electrode including the nano silicon-graphene-carbon fiber composite according to an embodiment of the present invention has an initial charge (lithium insertion) capacity of 1700 mAh / g, an initial discharge (lithium desorption) capacity of 606 mAh / g, The efficiency was about 36%, but the discharge capacity of 734 to 635 mAh / g was maintained up to 20 cycles after 5 cycles, and the efficiency was about 95% or more.
또한, 리튬삽입-탈착 중 일어나는 입자 부서짐 현상에 의해 실리콘 입자의 표면적(전해질과 접하는 계면적)이 증가하게 되고, 이로써 전해질 환원분해가 활발히 일어나 추가적인 충전 용량이 발생함으로써 높은 초기 충전 용량을 얻을 수 있었다. In addition, the particle breakage phenomenon during lithium insertion-desorption increases the surface area of the silicon particles (interface contacting with the electrolyte), thereby actively reductively decomposing the electrolyte and generating additional charge capacity, thereby obtaining a high initial charge capacity. .
또한, 그래핀 입자의 표면에 리튬이온이 비가역적으로 흡착되어 충전 용량만을 증가시킬 수 있다. In addition, lithium ions are irreversibly adsorbed on the surface of the graphene particles to increase only the charge capacity.
도 6은 본 발명의 일 실시예에 따른 나노 실리콘-그래핀-카본섬유 복합재 음극과, 실리콘 음극의 싸이클 성능을 비교한 것으로서, 나노 실리콘 분말만으로 제조된 음극에서는 3회 싸이클 이후 급격히 방전용량이 감소하였다. 이는 상기 나노 나노 실리콘계 화합물-그래핀-탄소섬유 복합재 음극의 그래핀과 탄소섬유가 리튬과의 반응시 발생하는 실리콘의 부피변화를 수용(accomodate)하고 음극의 전기전도도를 증가시킴으로써 싸이클 성능을 상당히 향상됨을 확인할 수 있다.
6 is a comparison of the cycle performance of the nano silicon-graphene-carbon fiber composite anode and the silicon anode according to an embodiment of the present invention, in the anode made of nano silicon powder only after three cycles, the discharge capacity is sharply reduced It was. This significantly improves cycle performance by accommodating the volume change of silicon generated when the graphene and carbon fiber of the nano-nano-silicon compound-graphene-carbon fiber composite anode react with lithium and increasing the electrical conductivity of the cathode. can confirm.
(실시예 3) 산소 치환 고상반응에 의한 나노 실리카로부터 나노 실리콘 아산화물( SiOx ) 분말의 제조와 나노 실리콘 아산화물- 그래핀 -카본섬유 복합재 제조 Example 3 Preparation of Nano Silicon Suboxide ( SiOx ) Powder from Nano Silica by Oxygen Substitution Solid Phase Reaction and Preparation of Nano Silicon Suboxide- Graphene -Carbon Fiber Composites
실리카(SiO2, 평균입경 15㎚) 분말과 리튬 금속 분말(평균입경 25㎛)을 1 : 4 몰비로 아르곤 분위기, 상온(25℃)에서 혼합한 후, 상온에서 3시간동안 볼밀링하며 고상(solid-state) 반응시켜 산소 치환반응을 유도하였다. Silica (SiO 2 , 15 nm average particle diameter) powder and lithium metal powder (average particle diameter 25 μm) were mixed in an argon atmosphere at room temperature (25 ° C.) in a 1: 4 molar ratio, and then ball milled at room temperature for 3 hours. solid-state reaction to induce oxygen substitution.
(4-2x) Li + SiO2 → (2-x) Li2O + SiOx (반응식 4)(4-2x) Li + SiO 2 → (2-x) Li 2 O + SiO x (Scheme 4)
실시예 1과 동일한 방법으로 부반응물인 리튬산화물과 합성된 실리콘 아산화물 분말을 분리하기 위해 리튬산화물을 0.5M 염산 용액으로 세척하고, 에탄올과 1M HCl 수용액의 혼합용액(에탄올과 1M HCl 수용액의 혼합비율 1:1)으로 순차적으로 씻어냈다. LiCl을 제거한 후, 최종적으로 갈색의 나노 실리콘 아산화물 분말(SiO0.37, 평균입경 50 nm)을 얻은 후 진공오븐에서 건조하였다. Lithium oxide was washed with 0.5M hydrochloric acid solution to separate the lithium reactant and the synthesized silicon suboxide powder in the same manner as in Example 1, and a mixed solution of ethanol and 1M HCl aqueous solution (ethanol and 1M HCl aqueous solution was mixed). The ratio was washed sequentially with 1: 1). After removing LiCl, a brown nano silicon nitrite powder (SiO 0.37 , average particle diameter: 50 nm) was obtained and dried in a vacuum oven.
도 7은 본 발명의 일 실시예에 따른 나노 실리카로부터 얻은 나노 실리콘 아산화물 분말의 TEM 이미지와 elemental mapping 이미지를 나타낸 것이다. 약 50 nm의 직경을 가지는 실리콘 아산화물의 약 200 ~ 300nm 직경의 2차 입자를 확인할 수 있었다. elemental mapping 분석에 의해 얻은 Si : O = 1 : 0.37 비로부터, 제조된 실리콘 아산화물의 화학식이 SiO0.37 임을 알 수 있다. Figure 7 shows a TEM image and elemental mapping image of the nano silicon dioxide powder obtained from nano silica according to an embodiment of the present invention. Secondary particles having a diameter of about 200 to 300 nm of silicon suboxide having a diameter of about 50 nm could be identified. From the Si: O = 1: 0.37 ratio obtained by elemental mapping analysis, it can be seen that the chemical formula of the prepared silicon suboxide is SiO 0.37 .
실시예 1과 동일한 방법으로 나노 실리콘 아산화물(SiO0.37) 분말 100mg을 물 100㎖에 균일하게 분산하고, 그래핀 분말(평균입경 2.5㎛) 12.5mg 및 카본섬유 분말(두께 100nm) 12.5mg을 물 50㎖에 분산시킨 슬러리를 상기 물에 분산된 나노 실리콘 아산화물 분말 용액과 혼합한 후, 초음파를 이용해 분산하여 복합재 분산용액을 제조하였다. 이때, 복합재 분산용액은 80 : 10 : 10 wt% 비율을 가지는 나노 실리콘 아산화물(SiO0.37)-그래핀-카본섬유 복합재를 포함한다. 즉, 나노 실리콘 아산화물/(그래핀+탄소섬유) 무게비가 4/1이며, 그래핀/카본섬유 무게비도 1/1인 분말액을 제조한다. 다음으로, 원심분리를 통하여 물을 제거하고 진공오븐에서 건조시킴으로써 실리콘 복합재 음극활물질을 얻었다.
In the same manner as in Example 1, 100 mg of nano silicon suboxide (SiO 0.37 ) powder was uniformly dispersed in 100 ml of water, 12.5 mg of graphene powder (average particle diameter: 2.5 μm) and 12.5 mg of carbon fiber powder (100 nm thick) were prepared. The slurry dispersed in 50 ml was mixed with the nano silicon nitrite powder solution dispersed in the water, and then dispersed using ultrasonic waves to prepare a composite dispersion solution. At this time, the composite dispersion solution comprises a nano silicon suboxide (SiO 0.37 ) -graphene -carbon fiber composite having a ratio of 80:10:10 wt%. That is, a powder solution having a nano silicon suboxide / (graphene + carbon fiber) weight ratio of 4/1 and a graphene / carbon fiber weight ratio of 1/1 is prepared. Next, water was removed through centrifugation and dried in a vacuum oven to obtain a silicon composite anode active material.
(실시예 4) 실시예 3의 나노 실리콘 아산화물( SiO 0 .37 )- 그래핀 -카본섬유 음극활물질로 이루어진 음극을 포함하는 리튬이차전지의 전기화학적 특성 조사 (Example 4) Example 3 nano silicon suboxide (SiO 0 .37) of the-graphene-electrochemical properties of the lithium secondary battery comprising a negative electrode made of a carbon fiber anode active material irradiated
실시예 3에서 나노실리카로부터 제조한 나노 실리콘 아산화물(SiO0 .37)-그래핀-카본섬유 음극활물질 : 카본 도전재(super P) : 바인더의 중량비를 75 : 10 : 15 (wt%)로 혼합하여 음극을 제조하였다. 이때, 나트륨 카르복시 메틸 셀룰로오스(sodium carboxymethyl cellulose) 및 폴리아크릴산(polyacrylic acid)을 1 : 1 중량혼합비 로 혼합하여 물에 용해한 바인더 용액을 준비한 후, 여기에 실리콘 복합재 음극활물질 및 카본 도전재(super P)를 넣어 음극 코팅용 슬러리를 제조하였다. 상기 슬러리를 구리 집전체 포일위에 통상의 방법으로 코팅하였다. 다음으로, 진공 오븐을 이용하여 110℃에서 12시간 동안 건조하였다. 건조 후 40 kg/㎠의 압력이 유지되는 롤 프레스(roll press)에 통과시켜 음극을 제작하였다. Exemplary nano silicon suboxide produced from nanosilica in Example 3 (SiO 0 .37) - graphene-carbon fiber cathode active material: a 15 (wt%): carbon conductive agent (super P): the weight ratio of the binder is 75: 10 The negative electrode was prepared by mixing. At this time, sodium carboxymethyl cellulose and polyacrylic acid are mixed in a 1: 1 weight ratio to prepare a binder solution dissolved in water, and then a silicon composite anode active material and a carbon conductive material (super P) are added thereto. Was prepared to prepare a slurry for negative electrode coating. The slurry was coated on a copper current collector foil in a conventional manner. Next, it was dried for 12 hours at 110 ℃ using a vacuum oven. After drying, a negative electrode was prepared by passing through a roll press maintained at a pressure of 40 kg /
리튬셀은 리튬 메탈을 상대전극 및 기준전극으로 하고, 제조된 실리콘 음극을 작업전극으로 사용하고, 전해액으로 1M LiPF6이 녹아 있는 풀루오로 에틸렌 카보네이트 (FEC)와 디에틸 카보네이트 (DEC)의 혼합용액(혼합액 비율 5:5)를 사용하여 제작되었다. 약 0.2C로 0.05 ~ 1.5 V 전압구간에서 정전류-정전압 (CC-CV) 방식으로 충전과 방전을 실시하였다. 상기 나노 실리콘 아산화물(SiO0 .37)-그래핀-카본섬유 복합재를 포함하는 리튬이차전지의 음극용량 (capacity)을 무게당 용량 (specific gravimetric capacity)으로 환산한 결과를 도 8에 나타내였다. Lithium cells use lithium metal as a counter electrode and a reference electrode, and a prepared silicon cathode as a working electrode, and a mixture of fluoro ethylene carbonate (FEC) and diethyl carbonate (DEC) in which 1M LiPF 6 is dissolved as an electrolyte. It produced using the solution (mixture ratio 5: 5). Charging and discharging were performed in a constant current-constant voltage (CC-CV) method at a voltage range of 0.05 to 1.5 V at about 0.2C. The nano-silicon suboxide (SiO 0 .37) - graphene - was expressed in terms of the effect of the negative electrode capacity of the lithium secondary battery comprising the carbon fiber composite material (capacity) in a dose (specific gravimetric capacity) per weight in Fig.
본 발명의 일 실시예에 따른 나노 실리콘 아산화물(SiO0 .37)-그래핀-카본섬유 복합재를 포함하는 음극은 초기 충전(리튬 삽입) 용량은 1965 mAh/g, 초기 방전(리튬 탈착) 용량은 1579 mAh/g로서, 초기 쿨롱효율은 약 80 %이나, 2회 이후 쿨롱효율이 97 % 이상으로 증가하였으며, 50 싸이클까지의 용량유지율은 80 %이였다. Nano-silicon suboxide according to one embodiment of the present invention (SiO 0 .37) - graphene-anode including a carbon fiber composite material is initially charged (lithium insertion) capacity is 1965 mAh / g, an initial discharge (lithium desorption) Capacity Was 1579 mAh / g, the initial coulombic efficiency was about 80%, but after two cycles, the coulombic efficiency increased to more than 97%, and the capacity retention up to 50 cycles was 80%.
이는 실시예 2의 나노실리콘 복합재로 제조된 음극에서보다 충방전 성능이 향상된 것이다. 이는 실리콘 아산화물(SiO0 .37)에서의 산소가 초기 충전 중 Li2O, 리튬실리케이트를 형성하여 실리콘의 부피변화 수용력(accomodate)이 향상되었고 나노 실리콘 아산화물(SiO0 .37)-그래핀-카본섬유 복합재 음극을 부반응 억제효과가 있다고 알려져 있는 FEC:DEC로 이루어진 전해액에서 충방전시킴으로써 전해액과의 계면반응이 억제되었기 때문이다.
This is an improved charge and discharge performance than the negative electrode made of the nanosilicon composite of Example 2. This silicon suboxide (SiO 0 .37) oxygen of the initial charge Li 2 O, to form a lithium silicate improved the volume change of the silicon capacity (accomodate) nano silicon suboxide in (SiO 0 .37) - graphene This is because the interfacial reaction with the electrolyte was suppressed by charging and discharging the carbon fiber composite anode in an electrolyte consisting of FEC: DEC, which is known to have a side reaction inhibitory effect.
이상과 같이 본 발명에서는 한정된 실시예에 의해 설명되었으나 이는 본 발명의 보다 전반적인 이해를 돕기 위해서 제공된 것일 뿐, 본 발명은 상기의 실시예에 한정되는 것은 아니며, 본 발명이 속하는 분야에서 통상의 지식을 가진 자라면 이러한 기재로부터 다양한 수정 및 변형이 가능하다. While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is to be understood that the invention is not limited to the disclosed embodiments, but, on the contrary, Various modifications and variations are possible in light of the above teachings.
따라서, 본 발명의 사상은 설명된 실시예에 국한되어 정해져서는 아니되며, 후술하는 특허청구범위뿐 아니라 이 특허청구범위와 균등하거나 등가적 변형이 있는 모든 것들은 본 발명 사상의 범주에 속한다고 할 것이다.
Accordingly, the spirit of the present invention should not be construed as being limited to the embodiments described, and all of the equivalents or equivalents of the claims, as well as the following claims, belong to the scope of the present invention .
Claims (19)
Nano-silicon compound-graphene-carbon fiber composites, including nano-silicon compound selected from nano silicon, nano silicon suboxide and mixtures thereof and graphene and carbon fiber.
상기 나노 실리콘 아산화물은 SiOx(0 < x < 0.5)인 나노 실리콘계 화합물-그래핀-탄소섬유 복합재.
The method of claim 1,
The nano silicon suboxide is SiO x (0 <x <0.5) nano silicon compound-graphene-carbon fiber composite.
The negative electrode active material for a lithium secondary battery comprising the nano-silicon compound-graphene-carbon fiber composite of any one of claims 1 and 2.
A lithium secondary battery comprising the negative electrode active material for lithium secondary battery of claim 3.
(b) 상기 제조된 나노 실리콘계 화합물 분말과, 그래핀 및 탄소섬유를 혼합하는 단계를 포함하는 나노 실리콘계 화합물-그래핀-탄소섬유 복합재를 제조하는 방법.
(a) oxygen-reacting lithium powder and silica powder to prepare a nano silicon-based compound powder selected from nano silicon, nano silicon suboxide, and mixtures thereof; and
(B) a method for producing a nano-silicon compound-graphene-carbon fiber composite comprising the step of mixing the nano-silicon compound powder prepared above, graphene and carbon fibers.
상기 (a)단계는 제조된 나노 실리콘계 화합물 분말을 리튬 산화물로부터 분리 및 정제하는 단계를 더 포함하는 나노 실리콘계 화합물-그래핀-탄소섬유 복합재를 제조하는 방법.
The method of claim 5,
The step (a) is a method for producing a nano-silicon compound-graphene-carbon fiber composite further comprising the step of separating and purifying the prepared nano-silicon compound powder from lithium oxide.
상기 (b)단계는 나노 실리콘계 화합물 분말과, 그래핀 및 탄소섬유를 각각 용매에 분산시킨 슬러리를 혼합한 다음 상기 용매를 제거한 후 건조하는 단계를 더 포함하는 나노 실리콘계 화합물-그래핀-탄소섬유 복합재를 제조하는 방법.
The method of claim 5,
The step (b) is a nano silicon compound-graphene-carbon fiber composites further comprising the step of mixing the nano-silicon compound powder, a slurry in which graphene and carbon fibers dispersed in a solvent, and then removing the solvent and drying How to prepare.
상기 실리카 분말은 퓸드 실리카, 마이크로포러스 실리카, 메조포러스 실리카 및 매크로포러스 실리카 중에서 선택되는 어느 하나 또는 둘 이상의 혼합물인 나노 실리콘계 화합물-그래핀-탄소섬유 복합재를 제조하는 방법.
The method of claim 5,
The silica powder is any one or a mixture of two or more selected from fumed silica, microporous silica, mesoporous silica and macroporous silica nano-silicon compound-graphene-carbon fiber composite manufacturing method.
상기 실리카 분말은 직경이 2 ㎚ ~ 30 ㎛인 나노 실리콘계 화합물-그래핀-탄소섬유 복합재를 제조하는 방법.
The method of claim 5,
The silica powder is a method for producing a nano-silicon compound-graphene-carbon fiber composite having a diameter of 2 nm ~ 30 ㎛.
상기 그래핀은 직경이 10㎚ ~ 5㎛인 나노 실리콘계 화합물-그래핀-탄소섬유 복합재를 제조하는 방법.
The method of claim 5,
The graphene is a method for producing a nano-silicon compound-graphene-carbon fiber composite having a diameter of 10nm ~ 5㎛.
상기 탄소섬유는 두께 1nm ~ 5㎛, 길이 50 ~ 200㎛인 나노 실리콘계 화합물-그래핀-탄소섬유 복합재를 제조하는 방법.
The method of claim 5,
The carbon fiber is a method for producing a nano-silicon compound-graphene-carbon fiber composite material having a thickness of 1nm ~ 5㎛, 50 ~ 200㎛.
상기 리튬과 실리카(SiO2)의 몰비는 2 ~ 6 : 1인 나노 실리콘계 화합물-그래핀-탄소섬유 복합재를 제조하는 방법.
The method of claim 5,
The molar ratio of the lithium and silica (SiO 2 ) is 2 to 6: 1 method of manufacturing a nano silicon-based compound-graphene-carbon fiber composite.
상기 (a)단계는 비활성 분위기 내에서 혼합한 후, 1 ~ 20 시간동안 볼밀링 공정으로 실시하는 것인 나노 실리콘계 화합물-그래핀-탄소섬유 복합재를 제조하는 방법.
The method of claim 5,
The step (a) is a method for producing a nano-silicon compound-graphene-carbon fiber composite material which is carried out by a ball milling process for 1 to 20 hours after mixing in an inert atmosphere.
상기 (a)단계의 산소 교환 반응은 0 ~ 300 ℃의 온도범위에서 실시하는 것인 나노 실리콘계 화합물-그래핀-탄소섬유 복합재를 제조하는 방법.
The method of claim 5,
Oxygen exchange reaction of the step (a) is a method for producing a nano-silicon compound-graphene-carbon fiber composite that is carried out at a temperature range of 0 ~ 300 ℃.
상기 (b)단계의 탄소 섬유는 산처리를 통해 표면 산화된 것인 나노 실리콘계 화합물-그래핀-탄소섬유 복합재를 제조하는 방법.
The method of claim 5,
The carbon fiber of step (b) is a method of producing a nano silicon-based compound-graphene-carbon fiber composite that is surface oxidized through acid treatment.
상기 (b)단계에서 나노 실리콘계 화합물 분말과, 그래핀 및 탄소 섬유의 혼합물의 중량혼합비는 1 : 9 ~ 9 : 1인 나노 실리콘계 화합물-그래핀-탄소섬유 복합재를 제조하는 방법.
The method of claim 5,
The method for producing a nano-silicon compound-graphene-carbon fiber composite having a weight mixing ratio of the nano-silicon compound powder and the mixture of graphene and carbon fiber in step (b) is 1: 9 to 9: 1.
상기 (b)단계에서 그래핀 및 탄소 섬유는 중량혼합비가 1 : 10 ~ 10 : 1인 나노 실리콘계 화합물-그래핀-탄소섬유 복합재를 제조하는 방법.
The method of claim 5,
Graphene and carbon fibers in the step (b) is a method of producing a nano silicon compound-graphene-carbon fiber composite material having a weight mixing ratio of 1:10 to 10: 1.
상기 (b)단계는 0 ~ 100℃에서 실시되는 나노 실리콘계 화합물-그래핀-탄소섬유 복합재를 제조하는 방법.
The method of claim 5,
Step (b) is a method for producing a nano-silicon compound-graphene-carbon fiber composite is carried out at 0 ~ 100 ℃.
상기 탄소 섬유는 카본파이버, 단일벽 탄소나노튜브, 다중벽 탄소나노튜브 및 탄소나노와이어 중에서 선택되는 어느 하나인 나노 실리콘계 화합물-그래핀-탄소섬유 복합재를 제조하는 방법.The method of claim 5,
The carbon fiber is any one selected from carbon fiber, single-wall carbon nanotubes, multi-walled carbon nanotubes and carbon nanowires.