KR20140000060U - Film for mobile equipment with fragrance diffusion - Google Patents

Film for mobile equipment with fragrance diffusion Download PDF

Info

Publication number
KR20140000060U
KR20140000060U KR2020120005477U KR20120005477U KR20140000060U KR 20140000060 U KR20140000060 U KR 20140000060U KR 2020120005477 U KR2020120005477 U KR 2020120005477U KR 20120005477 U KR20120005477 U KR 20120005477U KR 20140000060 U KR20140000060 U KR 20140000060U
Authority
KR
South Korea
Prior art keywords
film
layer
mobile device
base film
hard coating
Prior art date
Application number
KR2020120005477U
Other languages
Korean (ko)
Other versions
KR200474976Y1 (en
Inventor
신형철
Original Assignee
주식회사 유엠티랩스
주식회사 유엠티랩스
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 유엠티랩스, 주식회사 유엠티랩스 filed Critical 주식회사 유엠티랩스
Priority to KR2020120005477U priority Critical patent/KR200474976Y1/en
Publication of KR20140000060U publication Critical patent/KR20140000060U/en
Application granted granted Critical
Publication of KR200474976Y1 publication Critical patent/KR200474976Y1/en

Abstract

향기 발산 효과가 있어, 모바일 기기 사용시 기분 전환이나 심신을 안정시킬 수 있는 모바일 기기용 필름에 대하여 개시한다.
본 고안에 따른 모바일 기기용 필름은 기재필름; 상기 기재필름 상부에 형성된 하드코팅층; 상기 하드코팅층 상에 형성된 방오층; 및 상기 기재필름 하부에 형성된 점착층;을 포함하고, 상기 하드코팅층 및 방오층 중에서 하나 이상의 층에 방향성 물질이 포함되어 있는 것을 특징으로 한다. And a film for mobile devices capable of stabilizing the mind and body when the mobile device is used.
The film for a mobile device according to the present invention comprises a substrate film; A hard coating layer formed on the base film; An antifouling layer formed on the hard coating layer; And an adhesive layer formed on the bottom of the base film, wherein at least one of the hard coat layer and the anti-scattering layer contains a directional material.

Description

향기 발산 효과가 있는 모바일 기기용 필름 {FILM FOR MOBILE EQUIPMENT WITH FRAGRANCE DIFFUSION}FIELD FOR MOBILE EQUIPMENT WITH FRAGRANCE DIFFUSION [0002]

본 고안은 휴대폰, 태블릿 PC 등과 같은 모바일 기기의 표면에 부착되는 필름에 관한 것으로, 보다 상세하게는 향기 발산 효과가 있는 모바일 기기용 필름에 관한 것이다.
The present invention relates to a film adhered to a surface of a mobile device such as a mobile phone or a tablet PC, and more particularly to a film for a mobile device having a flavor-emitting effect.

휴대폰, 태블릿 PC 등과 같은 모바일 기기는 휴대가 가능하다. Mobile devices such as mobile phones and tablet PCs are portable.

모바일 기기는 통상 터치 스크린 방식이 적용된다. 터치 스크린은 일반적으로 강화유리를 필수적으로 포함하고 있다. The mobile device is generally applied to the touch screen method. The touch screen generally includes tempered glass essentially.

그리고, 강화유리 표면에는 스크래치 방지, 지문 방지 등 각종 기능성 필름이 부착되어 있다. On the surface of the tempered glass, various functional films such as scratch prevention and fingerprint prevention are attached.

그런데, 특히 휴대폰의 경우, 사용자가 모바일 기기를 사용할 경우, 얼굴의 화장품, 땀 등이 휴대폰 표면에 묻게 되고, 휴대폰 표면에 묻은 화장품, 땀이 고착될 경우, 악취를 낼 수 있다.
In particular, in the case of a mobile phone, when a user uses a mobile device, cosmetics and sweat of the face are buried on the surface of the mobile phone, and when the cosmetics and perspiration adhered to the surface of the mobile phone are fixed, odors can be generated.

본 고안과 관련된 배경기술로는 대한민국 공개특허공보 제10-2005-0106536호(2005.11.10. 공개)가 있으며, 상기 문헌에는 향기를 부여하는 방향성 물질이 포함된 밀봉 필름이 기재되어 있다.
A background art related to the present invention is Korean Patent Laid-Open Publication No. 10-2005-0106536 (published on November 10, 2005), which discloses a sealing film containing a fragrance-imparting aromatic substance.

본 고안의 하나의 목적은 향기 발산 기능이 있어, 사용자로 하여금 모바일 기기 사용시 기분 전환 효과 또는 심신 안정 효과를 부여할 수 있는 모바일 기기용 필름을 제공하는 것이다.One object of the present invention is to provide a film for a mobile device which has a fragrance dissipating function and can give a user a mood stabilizing effect or a mind and body stabilizing effect when using a mobile device.

본 고안의 다른 목적은 상기의 향기 발산 효과와 더불어 충격 흡수 기능이 있어, 향기를 발산할 수 있으며, 아울러 모바일 기기에 가해지는 충격을 최소화함으로써 강화유리와 같은 부품이 파손되는 것을 방지할 수 있는 모바일 기기용 필름을 제공하는 것이다.
Another object of the present invention is to provide a mobile phone capable of preventing a component such as a tempered glass from being damaged by minimizing a shock applied to a mobile device, And to provide a film for a device.

상기 목적을 달성하기 위한 본 고안의 실시예에 따른 모바일 기기용 필름은 기재필름; 상기 기재필름 상부에 형성된 하드코팅층; 상기 하드코팅층 상에 형성된 방오층; 및 상기 기재필름 하부에 형성된 점착층;을 포함하고, 상기 하드코팅층 및 방오층 중에서 하나 이상의 층에 방향성 물질이 포함되어 있는 것을 특징으로 한다. According to an aspect of the present invention, there is provided a film for a mobile device comprising: a base film; A hard coating layer formed on the base film; An antifouling layer formed on the hard coat layer; And an adhesive layer formed on the bottom of the base film, wherein at least one of the hard coat layer and the anti-scattering layer contains a directional material.

이때, 상기 방향성 물질은 상기 하드코팅층 및 방오층을 형성하기 위한 하드코팅 조성물 및 방오 조성물 전체 100 중량부에 대하여 2~5중량부로 첨가되는 것이 보다 바람직하다.
It is more preferable that the aromatic material is added in an amount of 2 to 5 parts by weight based on 100 parts by weight of the hard coating composition and the antifouling composition for forming the hard coating layer and the antifouling layer.

상기 다른 목적을 달성하기 위한 본 고안의 실시예에 따른 모바일 기기용 필름은 제1기재필름; 상기 제1기재필름 상부에 형성된 충격흡수층; 상기 충격흡수층 상부에 형성된 제2기재필름; 상기 제2기재필름 상부에 형성된 하드코팅층; 상기 하드코팅층 상부에 형성된 방오층; 및 상기 제1기재필름 하부에 형성된 점착층;을 포함하고, 상기 하드코팅층 및 방오층 중에서 하나 이상의 층에 방향성 물질이 포함되어 있는 것을 특징으로 한다. According to another aspect of the present invention, there is provided a film for a mobile device comprising: a first base film; An impact absorbing layer formed on the first base film; A second base film formed on the impact absorbing layer; A hard coating layer formed on the second base film; An antifouling layer formed on the hard coating layer; And an adhesive layer formed under the first base film, wherein at least one of the hard coat layer and the anti-scattering layer contains a directional material.

이때, 상기 제1기재필름 및 제2기재필름의 재질은 폴리에틸렌테레프탈레이트(PET), 폴리카보네이트(PC) 및 연신 폴리프로필렌(OPP) 중에서 1종 이상을 포함하는 것이 바람직하다. At this time, it is preferable that the first base film and the second base film include at least one material selected from the group consisting of polyethylene terephthalate (PET), polycarbonate (PC), and stretched polypropylene (OPP).

또한, 상기 충격흡수층의 재질은 투명 실리콘 고무, 투명 열가소성 폴리우레탄(TPU) 및 투명 겔(gel) 중에서 1종 이상을 포함하고, 상기 충격흡수층의 두께는 50~200㎛인 것이 바람직하다.
The material of the shock absorbing layer may include at least one of transparent silicone rubber, transparent thermoplastic polyurethane (TPU) and transparent gel, and the thickness of the impact absorbing layer is preferably 50 to 200 mu m.

상기 다른 목적을 달성하기 위한 본 고안의 다른 실시예에 따른 모바일 기기용 필름은 3장 이상의 기재 필름들; 상기 기재 필름들 사이마다 형성된 2이상의 충격흡수층들; 상기 기재필름들 중 최상부 기재필름의 상부에 형성된 하드코팅층; 상기 하드코팅층 상부에 형성된 방오층; 및 상기 기재필름들 중 최하부 기재필름의 하부에 형성된 점착층;을 포함하고, 상기 하드코팅층 및 방오층 중에서 하나 이상의 층에 방향성 물질이 포함되어 있는 것을 특징으로 한다. According to another aspect of the present invention, there is provided a film for a mobile device comprising at least three base films; At least two shock absorbing layers formed between the base films; A hard coat layer formed on the uppermost one of the base films; An antifouling layer formed on the hard coating layer; And an adhesive layer formed on a lower portion of the substrate film among the substrate films, wherein at least one of the hard coating layer and the anti-scattering layer contains a directional substance.

이때, 상기 충격흡수층들의 재질은 투명 실리콘 고무, 투명 열가소성 폴리우레탄(TPU) 및 투명 겔 중에서 1종 이상을 포함하고, 상기 충격흡수층들 각각의 두께는 10~100㎛인 것을 특징으로 한다.
At this time, the material of the shock absorbing layers includes at least one of transparent silicone rubber, transparent thermoplastic polyurethane (TPU) and transparent gel, and each of the shock absorbing layers has a thickness of 10 to 100 탆.

본 고안에 따른 모바일 기기용 필름에 의하면, 하드코팅층과 방오층이 형성됨으로써 스크래치 방지 및 지문 방지 효과를 얻을 수 있으며, 아울러 이들 층에 방향성 물질이 포함됨으로써, 모바일 기기에서 향기가 발산되므로, 기분 전환 효과 혹은 심신안정 효과를 제공할 수 있다. According to the film for mobile devices according to the present invention, the hard coating layer and the antifouling layer are formed to prevent scratches and prevent fingerprints, and the fragrance is emitted from the mobile device because the fragrance material is contained in these layers. Effect or mind-body stabilization effect.

또한, 본 고안에 따른 모바일 기기용 필름의 경우, 향기 발산 기능과 함께 충격흡수 기능이 있어, 외부 충격에 대하여 강화유리와 같은 부품의 파손을 방지할 수 있다.
Further, in the case of the film for a mobile device according to the present invention, since it has a function of absorbing a shock and a function of absorbing a shock, it is possible to prevent breakage of a component such as tempered glass against an external impact.

도 1은 본 고안의 실시예에 따른 모바일 기기용 필름의 단면을 개략적으로 나타낸 것이다.
도 2는 본 고안의 다른 실시예에 따른 모바일 기기용 필름의 단면을 개략적으로 나타낸 것이다.
도 3은 본 고안의 또 다른 실시예에 따른 모바일 기기용 필름의 단면을 개략적으로 나타낸 것이다.
1 schematically shows a cross section of a film for a mobile device according to an embodiment of the present invention.
2 schematically shows a cross section of a film for a mobile device according to another embodiment of the present invention.
3 schematically shows a cross section of a film for a mobile device according to another embodiment of the present invention.

본 고안의 이점 및 특징, 그리고 그것들을 달성하는 방법은 상세하게 후술되어 있는 실시예들을 참조하면 명확해질 것이다. 그러나, 본 고안은 이하에서 개시되는 실시예들에 한정되는 것이 아니라 서로 다른 다양한 형태로 구현될 것이며, 단지 본 실시예들은 본 고안의 개시가 완전하도록 하며, 본 고안이 속하는 기술 분야에서 통상의 지식을 가진 자에게 고안의 범주를 완전하게 알려주기 위해 제공되는 것이며, 본 고안은 청구항의 범주에 의해 정의될 뿐이다.The advantages and features of the present invention, and how to accomplish them, will become apparent with reference to the embodiments described in detail below. It should be understood, however, that the present invention is not limited to the disclosed embodiments, but may be embodied in many different forms and should not be construed as limited to the embodiments set forth herein, To the person having the invention, and this invention is only defined by the scope of the claims.

이하, 첨부된 도면을 참조하여, 본 고안에 따른 향기 발산 효과가 있는 모바일 기기용 필름에 대하여 상세히 설명하기로 한다.
Hereinafter, a film for a mobile device having a flavor-emitting effect according to the present invention will be described in detail with reference to the accompanying drawings.

도 1은 본 고안의 실시예에 따른 모바일 기기용 필름의 단면을 개략적으로 나타낸 것이다.1 schematically shows a cross section of a film for a mobile device according to an embodiment of the present invention.

도 1을 참조하면, 도시된 모바일 기기용 필름의 경우, 기재필름(110), 하드코팅층(120), 방오층(130) 및 점착층(140)을 포함한다. Referring to FIG. 1, the illustrated film for a mobile device includes a base film 110, a hard coating layer 120, an antifouling layer 130, and an adhesive layer 140.

기재필름(110)은 투명한 고분자 필름으로서, 폴리에틸렌테레프탈레이트(PET), 폴리카보네이트(PC), 폴리에틸렌(PE), 연신 폴리프로필렌(OPP), 폴리염화비닐(PVC) 등의 재질로 형성될 수 있다.The base film 110 is a transparent polymer film and may be formed of a material such as polyethylene terephthalate (PET), polycarbonate (PC), polyethylene (PE), stretched polypropylene (OPP), polyvinyl chloride .

하드코팅층(120)은 기재필름(110) 상부에 형성되어, 필름의 내스크래치성을 향상시키는 역할을 한다. 상기 하드코팅층(120)은 공지의 하드코팅 조성물의 도포 및 경화 공정을 통하여 형성될 수 있다. The hard coating layer 120 is formed on the base film 110 to improve the scratch resistance of the film. The hard coating layer 120 may be formed by applying and curing a known hard coating composition.

방오층(130)은 하드코팅층(120) 상부에 형성되어, 필름에 지문 방지 혹은 오염 방지 기능을 부여한다. 상기 방오층(130)은 공지의 방오 조성물의 도포 및 경화 공정을 통하여 형성될 수 있다. The antifouling layer (130) is formed on the hard coat layer (120) to provide a fingerprint prevention function or a dirt prevention function to the film. The antifouling layer 130 may be formed through application and curing of a known antifouling composition.

상기의 하드코팅 조성물과 방오 조성물의 경우, 경화에 의한 막 형성 후 투명하고, 각각의 기능을 발휘할 수 있는 것이라면 제한없이 이용할 수 있으며, 물질, 두께 등에 특별한 한정이 있는 것은 아니다. The above-mentioned hard coating composition and antifouling composition can be used without limitation as long as they are transparent after film formation by curing and can exhibit their respective functions, and there is no particular limitation on the material, thickness, and the like.

이때, 본 발명의 경우, 상기 하드코팅층(120) 및 방오층(130) 중에서 하나 이상의 층에 방향성 물질이 포함되어 있다. 이러한 방향성 물질은 하드코팅층(120)을 형성하기 위한 하드코팅 조성물 혹은 방오층(130)을 형성하기 위한 방오 조성물에 포함될 수 있다. At this time, in the present invention, at least one layer among the hard coating layer 120 and the antifouling layer 130 includes a directional material. Such a directional substance may be included in the hard coating composition for forming the hard coating layer 120 or in the antifouling composition for forming the antifouling layer 130.

방향성 물질은 정해진 향기를 발산함으로써 모바일 기기 사용시 사용자의 기분 전환을 시켜주거나 또는 널리 알려진 바와 같이 부교감 신경을 자극함으로써 심신을 안정시킬 수 있는 효과를 제공한다. The aromatic substance emits a predetermined scent, thereby changing the user's mood when using the mobile device or stimulating the parasympathetic nerve as is widely known, thereby providing a stable effect on the mind and body.

방향성 물질은 송유, 정향 추출액, 쑥 농축액, 에틸 바닐린, 아이소유제닐 아세테이트, 헬리오트로핀 다이에틸 아세탈, 헬리오날, 캐시메란, 피페로닐 아세톤, 메틸 베타-나프틸 케톤, 메틸 다이하이드로자스모네이트, 라이랄 등이 제시될 수 있으나, 반드시 이에 제한되는 것은 아니다. Aromatic substances include pine oil, clove extract, mugwort concentrate, ethyl vanillin, isoeugenyl acetate, heliotropin diethyl acetal, helional, cashmeran, piperonyl acetone, methyl beta-naphthyl ketone, methyl dihydrozasmo Nate, Lyral and the like can be presented, but are not necessarily limited thereto.

이러한 방향성 물질은 하드코팅층(120)을 형성하기 위한 하드코팅 조성물 및 방오층(130)을 형성하기 위한 방오 조성물을 합한 중량 100 중량부에 대하여 2~5중량부로 포함되는 것이 보다 바람직하다. 방향성 물질의 첨가량이 2중량부 미만일 경우, 향기 발산 효과가 불충분하다. 반대로, 방향성 물질의 첨가량이 5중량부를 초과하는 경우, 필름의 투명성을 저하하는 등 물성 저하를 가져올 수 있다.More preferably, the aromatic material is included in an amount of 2 to 5 parts by weight based on 100 parts by weight of the total of the hard coating composition for forming the hard coat layer 120 and the antifouling composition for forming the antifouling layer 130. When the addition amount of the aromatic substance is less than 2 parts by weight, the aroma-releasing effect is insufficient. On the contrary, when the addition amount of the aromatic substance is more than 5 parts by weight, the transparency of the film may be deteriorated and the physical properties may be deteriorated.

점착층(140)은 본 발명에 따른 필름을 모바일 기기에 부착하기 위한 것이다. 점착층(140)의 보호를 위하여, 점착층(140) 하부에는 이형지(미도시)가 부착되어 있을 수 있다.
The adhesive layer 140 is for attaching the film according to the present invention to a mobile device. In order to protect the adhesive layer 140, a releasing paper (not shown) may be attached to the lower side of the adhesive layer 140.

도 2는 본 고안의 다른 실시예에 따른 모바일 기기용 필름의 단면을 개략적으로 나타낸 것이다.2 schematically shows a cross section of a film for a mobile device according to another embodiment of the present invention.

도 2를 참조하면, 도시된 모바일 기기용 필름의 경우, 제1기재필름(210a), 충격흡수층(220), 제2기재필름(210b), 점착층(230), 하드코팅층(240), 방오층(250)을 포함한다. Referring to FIG. 2, in the case of the film for a mobile device, the first base film 210a, the impact absorbing layer 220, the second base film 210b, the adhesive layer 230, the hard coat layer 240, And a pentagonal layer 250.

제1기재필름(210a)과 제2기재필름(210b)은 투명한 고분자 필름으로서, 폴리에틸렌테레프탈레이트(PET), 폴리카보네이트(PC), 폴리에틸렌(PE), 연신 폴리프로필렌(OPP), 폴리염화비닐(PVC) 등의 재질로 형성될 수 있다. The first base film 210a and the second base film 210b may be transparent polymer films such as polyethylene terephthalate (PET), polycarbonate (PC), polyethylene (PE), stretched polypropylene (OPP) PVC) or the like.

특히, 제1기재필름(210a)와 제2기재필름(210b)은 강도, 내후성 등의 기계적 물성이 우수하고, 충격흡수층(220)과의 부착력이 우수한 폴리에틸렌테레프탈레이트(PET), 폴리카보네이트(PC) 및 연신 폴리프로필렌(OPP) 중에서 1종 이상을 포함하는 재질로 형성되는 것이 보다 바람직하다. Particularly, the first base film 210a and the second base film 210b are made of polyethylene terephthalate (PET), polycarbonate (PC) having excellent mechanical properties such as strength and weather resistance and excellent adhesion to the impact absorbing layer 220 ) And stretched polypropylene (OPP).

충격흡수층(220)은 외부 충격을 흡수하여, 모바일 기기로 가해지는 충격을 감소시키는 역할을 한다. The shock absorbing layer 220 absorbs an external impact, thereby reducing the impact applied to the mobile device.

이러한 충격흡수층(220)은 투명성을 가지면서도 충격흡수능이 우수한 투명 실리콘 고무, 투명 열가소성 폴리우레탄(TPU) 및 투명 겔(gel) 중에서 1종 이상을 포함하는 재질로 형성될 수 있다. 이들 투명 실리콘 고무 또는 투명 열가소성 폴리우레탄 재질의 충격흡수층의 경우, 액상의 투명 실리콘 고무 또는 투명 열가소성 폴리우레탄을 제1기재필름(210a) 상에 도포한 후, 경화시키는 과정을 통하여 형성할 수 있다. 투명 겔의 경우, 실리콘 겔과 같은 공지의 투명한 겔, 보다 바람직하게는 고화된 겔을 제1기재필름 상에 적층한 후 제2기재필름(110b)을 적층할 수 있다. The shock absorbing layer 220 may be formed of a material containing at least one of transparent silicone rubber, transparent thermoplastic polyurethane (TPU), and transparent gel having transparency and excellent shock absorbing ability. In the case of the transparent silicone rubber or the transparent thermoplastic polyurethane shock absorbing layer, the liquid transparent silicone rubber or the transparent thermoplastic polyurethane may be coated on the first base film 210a and then cured. In the case of the transparent gel, a known transparent gel such as a silicone gel, more preferably a solidified gel may be laminated on the first base film, and then the second base film 110b may be laminated.

본 고안에서는 제1기재필름(210a)와 제2기재필름(210b) 사이에 충격흡수층(220)이 형성되어 있는 구조를 갖는다. The present invention has a structure in which an impact absorbing layer 220 is formed between the first base film 210a and the second base film 210b.

충격흡수층(220) 하부에만 제1기재필름(210a)이 형성되어 있고, 충격흡수층(220) 상부에 제2기재필름(210b)이 존재하지 않는 경우, 모바일 기기 사용시 충격흡수층(220)의 일부분, 특히 충격흡수층(220)의 상부 부분이 필름의 측면쪽으로 이탈될 수 있다. 그러나, 충격흡수층(220) 상부에 제2기재필름(210b)까지 형성되어 있는 경우, 제1기재필름(210a)이 충격흡수층(220)을 아래쪽에서 붙잡고, 제2기재필름(210b)이 충격흡수층(220)을 위쪽에서 붙잡고 있는 형태가 되어, 충격흡수층의 미끄러짐을 방지함으로써 충격흡수층(220)의 일부분의 측면 이탈을 억제할 수 있다. When the first base film 210a is formed only on the lower portion of the impact absorbing layer 220 and the second base film 210b does not exist on the impact absorbing layer 220, a portion of the impact absorbing layer 220, In particular, the upper portion of the impact absorbing layer 220 may be released toward the side of the film. However, when the second base film 210b is formed on the top of the impact absorbing layer 220, the first base film 210a catches the impact absorbing layer 220 from below, and the second base film 210b catches the impact absorbing layer 220. [ The side surface of the impact absorbing layer 220 can be prevented from slipping off by preventing the impact absorbing layer from slipping.

상기 충격흡수층(220)의 두께는 50~200㎛인 것이 보다 바람직하다. 충격흡수층의 두께가 50㎛ 미만일 경우에는 충격흡수능이 불충분할 수 있다. 반대로, 충격흡수층의 두께가 200㎛를 초과하는 경우, 더 이상의 충격흡수 효과 향상없이 필름의 두께만 증대시킬 수 있다.
The thickness of the impact absorbing layer 220 is more preferably 50 to 200 占 퐉. When the thickness of the shock absorbing layer is less than 50 µm, the shock absorbing ability may be insufficient. On the contrary, when the thickness of the shock absorbing layer exceeds 200 µm, only the thickness of the film may be increased without further improving the shock absorbing effect.

점착층(230)은 제1기재필름(210a) 하부에 형성되며, 모바일 기기에 필름이 부착될 수 있도록 한다.The adhesive layer 230 is formed under the first base film 210a so that the film can be attached to the mobile device.

하드코팅층(240)은 필름에 내스크래치성을 부여하며, 방오층(250)은 필름이 오염되거나, 지문이 남는 것을 방지한다. 이러한 하드코팅층(240)과 방오층(250) 각각은 공지된 하드코팅 조성물, 방오 조성물을 이용하여 형성할 수 있다. 이때, 본 발명에 따른 필름의 경우, 하드코팅층 및 방오층 중에서 하나 이상의 층에 방향성 물질이 포함되어 있어, 향기 발산 효과를 제공한다. 이러한 향기 발산 효과에 대하여는 도 1에 도시된 예에서 전술한 바와 동일하므로, 그 상세한 설명은 생략하기로 한다.
The hard coat layer 240 imparts scratch resistance to the film, and the antifouling layer 250 prevents the film from being contaminated or leaving fingerprints. Each of the hard coat layer 240 and the antifouling layer 250 may be formed using a known hard coating composition and antifouling composition. At this time, in the case of the film according to the present invention, at least one layer among the hard coating layer and the anti-scattering layer contains a directional substance, thereby providing a perfume emitting effect. Such a flavor emanating effect is the same as that described above in the example shown in Fig. 1, and thus a detailed description thereof will be omitted.

도 3은 본 고안의 또 다른 실시예에 따른 모바일 기기용 필름의 단면을 개략적으로 나타낸 것이다.3 schematically shows a cross section of a film for a mobile device according to another embodiment of the present invention.

도 3을 참조하면, 도시된 모바일 기기용 필름은 제1기재필름(310a), 제1충격흡수층(320a), 제2기재필름(310b), 제2충격흡수층(320b), 제3기재필름(310c), 점착층(330), 하드코팅층(340) 및 방오층(350)을 포함한다.3, the illustrated film for a mobile device includes a first base film 310a, a first impact absorbing layer 320a, a second base film 310b, a second impact absorbing layer 320b, a third base film An adhesive layer 330, a hard coating layer 340,

기재필름들(310a, 310b, 310c) 각각은 투명한 고분자 필름으로서, 전술한 바와 같이 폴리에틸렌테레프탈레이트(PET), 폴리카보네이트(PC) 및 연신 폴리프로필렌(OPP) 중에서 1종 이상을 포함하는 재질로 형성되는 것이 보다 바람직하다. Each of the base films 310a, 310b and 310c is a transparent polymer film formed of a material containing at least one of polyethylene terephthalate (PET), polycarbonate (PC) and stretched polypropylene (OPP) .

또한, 충격흡수층들(320a, 320b)은 투명 실리콘 고무, 투명 열가소성 폴리우레탄(TPU) 및 투명 겔 중에서 1종 이상을 포함하는 재질로 형성될 수 있다. In addition, the impact absorbing layers 320a and 320b may be formed of a material including at least one of transparent silicone rubber, transparent thermoplastic polyurethane (TPU), and transparent gel.

또한, 점착층(330)은 제1기재필름(310a), 즉 최하부 기재필름 하부에 형성되며, 모바일 기기에 필름이 부착될 수 있도록 한다. In addition, the adhesive layer 330 is formed on the first base film 310a, that is, under the lowermost base film, so that the film can be attached to the mobile device.

또한, 하드코팅층(340) 및 방오층(350) 중에서 하나 이상의 층에 방향성 물질이 포함되어 있어, 향기 발산 효과를 제공한다. In addition, at least one of the hard coat layer 340 and the antifouling layer 350 includes a directional material, thereby providing a perfume emitting effect.

도 2에 도시된 모바일 기기용 필름의 경우, 단층의 충격흡수층이 형성되어 있다. 반면, 도 3에 도시된 모바일 기기용 필름의 경우, 다층의 충격흡수층(320a, 320b)이 형성되어 있으며, 아울러 충격흡수층(320a, 320b) 상부 및 하부 각각에 기재필름(310a, 310b, 310c)이 형성되어 있는 라멜라 구조(Lamella Structure)를 갖는다. In the case of the film for mobile devices shown in Fig. 2, a single-layered shock absorbing layer is formed. In the case of the film for mobile devices shown in FIG. 3, the multi-layered shock absorbing layers 320a and 320b are formed, and the base films 310a, 310b, and 310c are formed on the upper and lower portions of the impact absorbing layers 320a and 320b, respectively. And a lamella structure in which the lamella structure is formed.

이와 같이, 기재필름과 충격흡수층이 라멜라 구조를 갖는 경우, 외부 충격을 충격흡수층들(320a, 320b)이 순차적으로 분산시킬 수 있어서, 모바일 기기에 가해지는 충격을 보다 감소시킬 수 있다. In this way, when the base film and the impact absorbing layer have a lamellar structure, the impact absorbing layers 320a and 320b can sequentially disperse an external impact, so that the impact applied to the mobile device can be further reduced.

이때, 충격흡수층들(320a, 320b) 각각의 두께는 10~100㎛인 것이 보다 바람직하다. 충격흡수층들(320a, 320b) 각각의 두께가 10㎛ 미만일 경우, 충격흡수능이 불충분할 수 있다. 반대로, 충격흡수층들(320a, 320b)의 두께가 100㎛를 초과하는 경우, 더 이상의 충격흡수능 향상없이 필름의 두께만 증가할 수 있다.
At this time, the thickness of each of the shock absorbing layers 320a and 320b is more preferably 10 to 100 占 퐉. When the thickness of each of the shock absorbing layers 320a and 320b is less than 10 mu m, the impact absorbing ability may be insufficient. Conversely, when the thickness of the shock absorbing layers 320a and 320b exceeds 100 mu m, the thickness of the film can be increased without further improving the shock absorbing ability.

실시예Example

이하, 본 고안의 바람직한 실시예를 통해 본 고안의 구성 및 작용을 더욱 상세히 설명하기로 한다. 다만, 이는 본 고안의 바람직한 예시로 제시된 것이며 어떠한 의미로도 이에 의해 본 고안이 제한되는 것으로 해석될 수는 없다. Hereinafter, the structure and operation of the present invention will be described in more detail through preferred embodiments of the present invention. It should be understood, however, that this is a preferred embodiment of the present invention and should not be construed as limiting the present invention in any way.

여기에 기재되지 않은 내용은 이 기술 분야에서 숙련된 자이면 충분히 기술적으로 유추할 수 있는 것이므로 그 설명을 생략하기로 한다.
Details that are not described herein will be omitted since those skilled in the art can sufficiently infer technically.

1. 필름의 제조1. Manufacture of film

실시예 1Example 1

제1기재필름, 충격흡수층, 제2기재필름이 순차로 적층된 형태의 필름을 제조하였다. A film in which the first base film, the impact absorbing layer, and the second base film were sequentially laminated was produced.

제1기재필름 및 제2기재필름으로 40㎛ 두께의 PET 필름(SH86, SKC 제조)을 사용하였으며, 충격흡수층은 액상 투명 실리콘(KE-441, 신에츠 제조)을 이용하여 100㎛ 두께로 형성하였다.
A PET film (manufactured by SH86, SKC) having a thickness of 40 mu m was used as the first base film and a second base film, and a 100 mu m thick shock absorbing layer was formed using liquid transparent silicone (KE-441, Shin-Etsu).

실시예 2Example 2

충격흡수층으로 액상 TPU(CU87AS, 창민 제조)로 사용한 것을 제외하고는 실시예 1과 동일한 조건으로 필름을 제조하였다.
A film was prepared under the same conditions as in Example 1 except that the liquid absorbing layer was used as a liquid TPU (CU87AS, Changmin).

실시예 3Example 3

제1기재필름, 제1충격흡수층, 제2기재필름, 제2충격흡수층, 제3기재필름이 순차로 적층된 형태의 필름을 제조하였다. A film in which the first base film, the first impact-absorbing layer, the second base film, the second impact-absorbing layer, and the third base film were sequentially laminated was produced.

제1기재필름, 제2기재필름 및 제3기재필름으로 40㎛ 두께의 PET 필름(SH86, SKC 제조)을 사용하였으며, 제1충격흡수층 및 제2충격흡수층 각각은 액상 투명 실리콘(KE-441, 신에츠 제조)을 이용하여 40㎛ 두께로 형성하였다.
40 μm thick PET film (manufactured by SH86, SKC) was used as the first base film, the second base film and the third base film, and each of the first and second impact absorbing layers was made of liquid transparent silicon (KE-441, Manufactured by Shin-Etsu Co., Ltd.).

실시예 4Example 4

제1충격흡수층 및 제2충격흡수층으로 액상 TPU(CU87AS, 창민 제조)로 사용한 것을 제외하고는 실시예 3과 동일한 조건으로 필름을 제조하였다.
A film was prepared under the same conditions as in Example 3, except that the first and second impact-absorbing layers were used as liquid TPU (CU87AS, Changmin).

비교예 1Comparative Example 1

충격흡수층을 형성하지 않았으며, 40㎛ 두께의 PET 필름(SH86, SKC 제조)을 합지하였다.
A shock absorbing layer was not formed, and a 40 μm-thick PET film (SH86, manufactured by SKC) was laminated.

2. 특성 평가2. Characterization

실시예 1~4 및 비교예 1에 따른 필름 하면에 아크릴 점착층을 형성한 후, 두께 1.3mm의 강화유리(삼성테크로글라스 제조)에 부착한 후, 투명성 평가 및 충격흡수 평가를 수행하였다. Acrylic adhesive layers were formed on the back surfaces of the films according to Examples 1 to 4 and Comparative Example 1 and then attached to tempered glass having a thickness of 1.3 mm (manufactured by Samsung Techoglass), and transparency evaluation and impact absorption evaluation were carried out.

(1) 투명성 평가 방법(1) transparency evaluation method

피사체가 정상적으로 인식되는지를 육안으로 확인하였다. It was visually confirmed whether the subject was recognized normally.

투명성 평가 결과, 실시예 1~4 및 비교예 1에 따른 필름이 부착된 강화유리 모두가 양호한 투명성을 나타내었다. As a result of the transparency evaluation, both the tempered glass with the film according to Examples 1 to 4 and Comparative Example 1 showed good transparency.

(2) 충격흡수 평가 방법(2) Impact absorption evaluation method

1.04kg의 강구를 사용하여 1.5m 및 2m 높이에서 자유낙하시켜 강화유리의 파손 여부를 확인하였으며, 각 시편에 대하여 30회씩 평가하여, 파손 회수를 나타내었으며, 그 결과를 표 1에 나타내었다. Using 1.04kg steel balls, free fall was confirmed at 1.5m and 2m heights to confirm the breakage of tempered glass, and the number of breakages was evaluated 30 times for each specimen, and the results are shown in Table 1 below.

[표 1][Table 1]

Figure utm00001
Figure utm00001

표 1을 참조하면, 충격흡수층이 형성된 실시예 1~4에 따른 필름이 부착된 강화유리 시편의 경우, 파손 회수가 현저히 낮은 것을 볼 수 있다. Referring to Table 1, in the case of the reinforced glass specimen with the film according to Examples 1 to 4 in which the impact absorbing layer is formed, the number of breakages is considerably low.

특히, 기재필름과 충격흡수층이 라멜라 구조로 형성된 실시예 2 및 실시예 4에 따른 필름이 부착된 강화유리 시편의 경우, 전체 충격흡수층 두께가 더 얇음에도 불구하고 충격흡수능력이 더 우수함을 나타내었다.
Particularly, in the case of the tempered glass specimen with the film according to Examples 2 and 4, in which the base film and the impact absorbing layer were formed in a lamellar structure, the impact absorbing capacity was superior even though the entire impact absorbing layer thickness was thinner .

본 고안은 실시예를 참고로 하여 설명되었으나, 이는 예시적인 것에 불과하며, 당해 기술이 속하는 분야에서 통상의 지식을 가진 자라면 이로부터 다양한 변형 및 균등한 타 실시예가 가능하다는 점을 이해할 것이다. 따라서, 본 고안의 진정한 기술적 보호범위는 실용신안등록청구범위에 의해서 정하여져야 할 것이다.
While the present invention has been described with reference to exemplary embodiments, it is to be understood that the invention is not limited to the disclosed exemplary embodiments, but, on the contrary, is intended to cover various modifications and equivalent arrangements included within the spirit and scope of the appended claims. Therefore, the true scope of technical protection of this invention should be determined by the utility model registration claim scope.

110 : 기재필름 120 : 하드코팅층
130 : 방오층 140 : 점착층
210a : 제1기재필름 210b : 제2기재필름
220 : 충격흡수층 230 : 점착층
240 : 하드코팅층 250 : 방오층
310a : 제1기재필름 310b : 제2기재필름
310c : 제3기재필름 320a : 제1충격흡수층
320b : 제2충격흡수층 330 : 점착층
340 : 하드코팅층 350 : 방오층110: base film 120: hard coating layer
130: antifouling layer 140: adhesive layer
210a: first base film 210b: second base film
220: shock absorbing layer 230: adhesive layer
240: hard coating layer 250: antifouling layer
310a: first base film 310b: second base film
310c: third base film 320a: first shock absorbing layer
320b: second shock absorbing layer 330: adhesive layer
340: hard coating layer 350: antifouling layer

Claims (10)

기재필름;
상기 기재필름 상부에 형성된 하드코팅층;
상기 하드코팅층 상에 형성된 방오층; 및
상기 기재필름 하부에 형성된 점착층;을 포함하고,
상기 하드코팅층 및 방오층 중에서 하나 이상의 층에 방향성 물질이 포함되어 있는 것을 특징으로 하는 모바일 기기용 필름.
A base film;
A hard coating layer formed on the base film;
An antifouling layer formed on the hard coating layer; And
And a pressure-sensitive adhesive layer formed under the base film.
Film for a mobile device, characterized in that the aromatic coating is contained in at least one of the hard coating layer and the antifouling layer.
제1항에 있어서,
상기 방향성 물질은
상기 하드코팅층 및 방오층을 형성하기 위한 하드코팅 조성물 및 방오 조성물 전체 100 중량부에 대하여 2~5중량부로 첨가되는 것을 특징으로 하는 모바일 기기용 필름.
The method of claim 1,
The aromatic material is
Mobile hard film and the anti-fouling layer for forming the anti-fouling layer for the mobile device film, characterized in that added to 2 to 5 parts by weight based on 100 parts by weight of the total.
제1기재필름;
상기 제1기재필름 상부에 형성된 충격흡수층;
상기 충격흡수층 상부에 형성된 제2기재필름;
상기 제2기재필름 상부에 형성된 하드코팅층;
상기 하드코팅층 상부에 형성된 방오층; 및
상기 제1기재필름 하부에 형성된 점착층;을 포함하고,
상기 하드코팅층 및 방오층 중에서 하나 이상의 층에 방향성 물질이 포함되어 있는 것을 특징으로 하는 모바일 기기용 필름.
First substrate film;
An impact absorbing layer formed on the first base film;
A second base film formed on the impact absorbing layer;
A hard coating layer formed on the second base film;
An antifouling layer formed on the hard coating layer; And
And an adhesive layer formed under the first base film,
Film for a mobile device, characterized in that the aromatic coating is contained in at least one of the hard coating layer and the antifouling layer.
제3항에 있어서,
상기 방향성 물질은
상기 하드코팅층 및 방오층을 형성하기 위한 하드코팅 조성물 및 방오 조성물 전체 100 중량부에 대하여 2~5중량부로 첨가되는 것을 특징으로 하는 모바일 기기용 필름.
The method of claim 3,
The aromatic material is
Mobile hard film and the anti-fouling layer for forming the anti-fouling layer for the mobile device film, characterized in that added to 2 to 5 parts by weight based on 100 parts by weight of the total.
제3항에 있어서,
상기 제1기재필름 및 제2기재필름의 재질은
폴리에틸렌테레프탈레이트(PET), 폴리카보네이트(PC) 및 연신 폴리프로필렌(OPP) 중에서 1종 이상을 포함하는 것을 특징으로 하는 모바일 기기용 필름.
The method of claim 3,
The material of the first substrate film and the second substrate film is
A film for mobile devices comprising at least one of polyethylene terephthalate (PET), polycarbonate (PC) and oriented polypropylene (OPP).
제3항에 있어서,
상기 충격흡수층의 재질은 투명 실리콘 고무, 투명 열가소성 폴리우레탄(TPU) 및 투명 겔 중에서 1종 이상을 포함하고,
상기 충격흡수층의 두께는 50~200㎛인 것을 특징으로 하는 모바일 기기용 필름.
The method of claim 3,
The material of the shock absorbing layer comprises at least one of transparent silicone rubber, transparent thermoplastic polyurethane (TPU) and transparent gel,
The thickness of the shock absorbing layer is a film for a mobile device, characterized in that 50 ~ 200㎛.
3장 이상의 기재 필름들;
상기 기재 필름들 사이마다 형성된 2이상의 충격흡수층들;
상기 기재필름들 중 최상부 기재필름의 상부에 형성된 하드코팅층;
상기 하드코팅층 상부에 형성된 방오층; 및
상기 기재필름들 중 최하부 기재필름의 하부에 형성된 점착층;을 포함하고,
상기 하드코팅층 및 방오층 중에서 하나 이상의 층에 방향성 물질이 포함되어 있는 것을 특징으로 하는 모바일 기기용 필름.
Three or more base films;
Two or more shock absorbing layers formed between the base films;
A hard coat layer formed on the uppermost one of the base films;
An antifouling layer formed on the hard coating layer; And
And an adhesive layer formed on a lower portion of the lowermost base film among the base films,
Film for a mobile device, characterized in that the aromatic coating is contained in at least one of the hard coating layer and the antifouling layer.
제7항에 있어서,
상기 제1기재필름 및 제2기재필름의 재질은
폴리에틸렌테레프탈레이트(PET), 폴리카보네이트(PC) 및 연신 폴리프로필렌(OPP) 중에서 1종 이상을 포함하는 것을 특징으로 하는 모바일 기기용 필름.
The method of claim 7, wherein
The material of the first substrate film and the second substrate film is
A film for mobile devices comprising at least one of polyethylene terephthalate (PET), polycarbonate (PC) and oriented polypropylene (OPP).
제8항에 있어서,
상기 방향성 물질은
상기 하드코팅층 및 방오층을 형성하기 위한 하드코팅 조성물 및 방오 조성물 전체 100 중량부에 대하여 2~5중량부로 첨가되는 것을 특징으로 하는 모바일 기기용 필름.
9. The method of claim 8,
The aromatic material is
Mobile hard film and the anti-fouling layer for forming the anti-fouling layer for the mobile device film, characterized in that added to 2 to 5 parts by weight based on 100 parts by weight of the total.
제8항에 있어서,
상기 충격흡수층들의 재질은 투명 실리콘 고무, 투명 열가소성 폴리우레탄(TPU) 및 투명 겔 중에서 1종 이상을 포함하고,
상기 충격흡수층들 각각의 두께는 10~100㎛인 것을 특징으로 하는 모바일 기기용 필름. 9. The method of claim 8,
The material of the shock absorbing layer comprises at least one of transparent silicone rubber, transparent thermoplastic polyurethane (TPU) and transparent gel,
The thickness of each of the shock absorbing layer is a film for a mobile device, characterized in that 10 ~ 100㎛.
KR2020120005477U 2012-06-26 2012-06-26 Film for mobile equipment with fragrance diffusion KR200474976Y1 (en)